SU5377A1

SU5377A1 - The method of manufacture of dentures

Info

Publication number: SU5377A1
Application number: SU6687A
Authority: SU
Inventors: Бэрлин А.Л.
Original assignee: Л.Б. Хольман; Ш. Лейсестер
Priority date: 1926-02-13
Filing date: 1926-02-13
Publication date: 1928-05-31

Description

fe зубных протезах, СоедйнйтёльНУё части дл зубов обычно изготовл ютс из благородных металлов и вулканизированного каучука (вулканита). Попытки применени взамен них различных композиций из Нитроцеллюлогзы оказались неудачными и выйСнйли их неприменимоёть на практике. С другой стороны , вулканизированный каучуК (вулканит), наиболее широко пр мен ющийс в производстве зубных протезов, имеет р д недостатков , как например, хрупкость и свойство, раздражать десны при долгом употреблении.Feet prostheses, joints for teeth are usually made of noble metals and vulcanized rubber (volcanic). Attempts to use various compositions of Nitrocellulose to replace them were unsuccessful and failed to be applied in practice. On the other hand, vulcanized rubber (vulcanite), which is most widely used in the manufacture of dental prostheses, has a number of drawbacks, such as fragility and the ability to irritate the gums with long-term use.

Дл устранени этих недостатков дл протезов, примен емых в дентиатрии , предлагаетс употребл ть способные формоватьс нерастворимые в воде органические производные целлюлозы, в том числе органические сложные эфиры целлюлозы и нерастворимые в воде простые эфиры целлюлозы.To eliminate these drawbacks, dentures used in dentures are suggested to use water-soluble, organic water-insoluble organic derivatives of cellulose, including organic cellulose esters and water-insoluble cellulose ethers.

Нормально эти материалы прй мен ютс в соединении с вёществаНи , придающими ий йластичносгь или в зкость, и в некоторых слу ча х с летучими pacrвopиtert миlNormally, these materials vary in conjunction with substances that impart elasticity or viscosity, and in some cases with volatile chemicals.

Примен емые дл §тих Целей еёщества не должны иметь ни вкуси ни запаха, если они хот бы частично остаютс в rotoBoM изделии; Одним из таких веществ, как про изводное целлюлозы, может витьсй например, уксуснокисла соль целлюлозы , ацетил-целлюлоза. При применении последней или какой либо другой производной целлкЗло зы, согласно предлагаемому изобретению , К ней добавл етс какое либо вещество, придающее массё пластичность, в количестве, дающей возможность производить |;формование в нагретом состо нии без летучих растворителей.The substances used for their purpose should have no taste or odor if they remain at least partially in the rotoBoM product; One of such substances as cellulose derivative can be, for example, acetic acid cellulose salt, cellulose acetyl. When using the latter or any other derivative of cellulose according to the present invention, a substance is added to it, giving the mass plasticity, in an amount that makes it possible to produce a hot, non-volatile solvent.

По предлагаемому способу помещаютс основанием вверх в составе из пластичной массы, содержащейс в одной половинке формьг; satfei fryfla -ввод т композицию целлюлозы , соедин ют обе половинки формы и; сжав их вместе, пбдвергают нагрев нию до температуры, достаточной дл уплотнени состава и приобретени им требуемой пластичности . Композици сложного эфира целлюлозы может примен тьс в виде пластинок или листо| ,..или же в виде кусков с шероховатой поверхностью, имеющих форму готовых пластинок дл протезов , или наконец, в зернистой или порошкообразной форме. Дл придани композиции требуемого цвета можно примен ть пигменты, свдержащие титан или киноварь или же другие, дающие нужную окраску. При изготовлении протезов из веществ, примен емых по данному иробретенинэ восковой слепок челюсти с зу бати-кладетс в фоёму обратной стороной чем та, которой он кладете при изготовлении их из ВУЛК ЙНИЙ, f.-e. зубы помещаютс ,в гипс кусающей стороной .In the proposed method, the base is placed upwards in a composition of plastic mass contained in one half of the molds; satfei fryfla-enter the cellulose composition, combine both halves of the form and; squeezing them together, pbd is heated to a temperature sufficient to compact the composition and acquire the required ductility. The composition of the cellulose ester can be applied in the form of plates or sheets | , .. or in the form of pieces with a rough surface, having the form of ready-made plates for prostheses, or finally, in a granular or powdered form. To impart a composition of a desired color, pigments withheld titanium or cinnabar or others that give the desired color can be used. In the manufacture of prostheses from substances used in this ibrebretenine a wax cast of the jaw with a bati-in the form of a bati-back in the form of the back side than that which he put in the manufacture of them from WULC YNI, f.-e. the teeth are placed in the plaster by the biting side.

Форма изготовл етс обычным образом и открываетс тогда, когда гипс отвердеет, при чем воск удал етс обычный образом. После этого об ; ш лввинки формы подогр1| а ,19те и разнимаютс , и в полэвинку , содержащую зубы, вводитс композици сложного эфира целлюлозы в виде грубо формованных пластинок, листов, зерен или т. п., затем форма подвергаетс нагреву под давлением до температуры , при которой происходит п| оцесс уплотнени производной целлюлозы. Когда температура дойдет .до 160° (она не должна превысить 200°) или несколько выше , давление постепенно увеличиваетс .The mold is made in the usual way and opens when the plaster hardens, and the wax is removed in the usual manner. After that, about; w wvwinki forms heated | a, 19 and are separated, and a pulp ester composition in the form of coarsely molded plates, sheets, grains or the like is introduced into a polynx containing teeth, then the mold is heated under pressure to a temperature at which n | consolidation process of a cellulose derivative. When the temperature reaches up to 160 ° (it should not exceed 200 °) or slightly higher, the pressure gradually increases.

Г|ока форма не закроетс соверiiggHHo . Эта операци , продолжаетс оцоло 15 минут. Когда форма совсем закроетс , она отнимаетс вместе с прессом от нагревател и помещаетс в холодную воду, где оставл етс до полного охлаждени . После этого форма открываетс , протез вынимаетс ,, удал етс излишний материал, и изделие подвергаетс обычной дальнейшей -обработке . При применении материала , согласно изобретению, допускаетс исправление поврежденных протезов обычным путемThe form is not closed by perfectgHHo. This operation lasts 15 minutes. When the mold is completely closed, it is taken away with the press from the heater and placed in cold water, where it is left until it is completely cooled. Thereafter, the mold is opened, the prosthesis is removed, the excess material is removed, and the product is subjected to normal further processing. When using the material according to the invention, it is possible to repair damaged prostheses in the usual way.

Предмет патента.The subject of the patent.

Claims

1. A method of making dental irotheses, characterized by the use of non-soluble as a molding material, 1 in organic water

the production of cellulose, in the form of its esters or ethers (for example, acetyl cellulose) with an admixture of substances that impart the necessary plasticity and viscosity to the mass.

2. Making dentures according to the method specified in claim 1, characterized in that the molding material (jaws and teeth) is molded in the form of sheets, plates, grains or powder to form prostheses (molds and teeth) and heated under pressure at a temperature of 160 ° C. to 200 ° C, followed by complete cooling of the form, after which the form is separated and the products are subjected to further processing by conventional methods.

3. In the method according to claim 1, for implanting the desired color to the prostheses, titanium white with a variety of colored pigments