SU1641841A1 - Polyvinyl chloride coating plastic - Google Patents
Polyvinyl chloride coating plastic Download PDFInfo
- Publication number
- SU1641841A1 SU1641841A1 SU894667371A SU4667371A SU1641841A1 SU 1641841 A1 SU1641841 A1 SU 1641841A1 SU 894667371 A SU894667371 A SU 894667371A SU 4667371 A SU4667371 A SU 4667371A SU 1641841 A1 SU1641841 A1 SU 1641841A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- pvc
- dichlorophenyl
- polymethyl
- polyvinyl chloride
- siloxane
- Prior art date
Abstract
Изобретение касаетс поливинил- хлоридньпс (ПВХ) пластизолей, примен емых дл нанесени на жест ные крышки, алюминиевые колпачки, покрытые адгезионным лаком, дл герметизации стекл нных банок и бутылок с продуктами детского питани и позвол ет снизить момент отвинчивани и увеличить твердость при сохранении физико-механических свойств пластизольного покрыти . Это достигаетеq за счет содержани в композиции в качестве кремний- органической жидкости 0,5-5,0 мае.ч, полиметил(дихлорфенил)силоксана на 100 мае.ч. ПВХ. Композици также содержит (мае.ч.) 60.0-85,0 пластификатора , 1,0-30,0 неорганического наполнител и 0,3-1,1 стабилизатора. 1 табл.The invention relates to polyvinyl chloride (PVC) plastisols used for coating rigid covers, aluminum caps coated with adhesive varnish for sealing glass jars and bottles of baby food and reduces the unscrewing moment and increases the hardness while maintaining physical mechanical properties of the plastisol coating. This is achieved due to the content in the composition as a silicon-organic liquid between 0.5 and 5.0 mash, polymethyl (dichlorophenyl) siloxane per 100 mash. PVC The composition also contains (by weight) 60.0-85.0 plasticizer, 1.0-30.0 inorganic filler and 0.3-1.1 stabilizer. 1 tab.
Description
Изобретение относитс к поливинил- хлоридным (ПВХ) пластизол м, примен емым дл нанесени на жест ные крышки , алюминиевые голпачки, покрытые адгезионным лаком, с целью гермети- 1 зации стекл нных банок и бутылок с продуктами детского питани .The invention relates to polyvinyl chloride (PVC) plastisols used for coating hard covers, aluminum caps coated with adhesive varnish, in order to seal glass jars and bottles of baby food.
Цель изобретени - снижение момента отвинчивани и увеличени твердости при сохранении физико-механических свойств пластизольного покрыти при вскрытии банок, укупоренных крышками с применением пластизоль- ных прокладок,а также увеличени твердости последних при сохранении физико-механических свойств пластизольного покрыти (прочность, относительное удлинение) .The purpose of the invention is to reduce the time of unscrewing and increase the hardness while maintaining the physicomechanical properties of the plastisol coating when opening the cans sealed with lids using plastisol gaskets, as well as increasing the hardness of the latter while maintaining the physical and mechanical properties of the plastisol coating (strength, relative elongation).
Композици содержит в качестве ПВХ смесь ПВХ МС 6602С или ПВХ ЕП 6602С с ПВХ С-6402Н; в качестве пластификаторов - сложноэфирные пластификаторы - диоктиловый эфир фталевой кислоты (ДОФ), эфиры эпоксидирован- ных жирных кислот - эпоксидировэнное растительное масло (ЭРМ), а также полиэфирные пластификаторы - дибути- ловый эфир полипропиленгликольади- ан (ППА-4); в качестве стабилизаторов - смесь металлосодержащих соединений - стеаратов кальци , цинка ч или смесь металлосодержащих соединений с фосфорсодержащими соединени ми - три(алкил)фенилфосфат (фосфит НФ); в качестве наполнителей - сернокислый барий ч.д.а., двуокись титана, углекислый кальций (мел);The composition contains as PVC a mixture of PVC MS 6602С or PVC EP 6602С with PVC С-6402Н; as plasticizers, ester plasticizers — phthalic acid dioctyl ester (DOP), epoxidized fatty acid esters — epoxidized vegetable oil (EPM), and polyether plasticizers — polypropylene glycol diene ether (PPA-4); as stabilizers, a mixture of metal-containing compounds — calcium stearate, zinc h, or a mixture of metal-containing compounds with phosphorus-containing compounds — tri (alkyl) phenyl phosphate (phosphite NF); as fillers, barium sulphate, analytical grade, titanium dioxide, calcium carbonate (chalk);
Дополнительно состав пластизол может содержать азодикарбонамид (порофор ЧХЗ-21).Additionally, the composition of the plastisol may contain azodicarbonamide (porophore CHZ-21).
Полиметил(дихлорфенил)силоксан (жидкость 162-70) предназначен дл получени термостойких масел и жидкости марки ХС-2-1БВ (полиметил(ди- хлорфенил)силоксанова жидкость), получаема при высоком вакууме.Polymethyl (dichlorophenyl) siloxane (liquid 162-70) is intended for the production of heat-resistant oils and liquids of mark XC-2-1BV (polymethyl (dichlorophenyl) siloxane liquid) obtained under high vacuum.
Изобретение иллюстрируетс следующими примерамиThe invention is illustrated by the following examples.
Пример 1 (предлагаемый).Example 1 (proposed).
15 мас.ч, сернокислого бари , 27 мае.ч эпоксидированного соевого масла смешивают и перетирают на пастотерке до дисперсности 50-60 мкм, 0917 мас.ч стеарата цинка, 0,13 мае.ч. стеарата кальци смешивают с 1 мае.ч эпокси- дированного соевого масла, перетирают на пастотерке до дисперсности 50 мкм.15 parts by weight of barium sulphate, 27 parts of epoxidized soybean oil are mixed and ground on a pasteur to a dispersion of 50-60 microns, 0917 parts by weight of zinc stearate, 0.13 parts by weight Calcium stearate is mixed with 1 mAh of epoxidized soybean oil, ground on a pasteur to a dispersion of 50 microns.
В планетарный лопастной смеситель загружают 44 мас.ч, эпоксидированного соевого масла, пасту сернокислого бари и пасту стеарата кальци и стеарата цинка, перемешивают содержимое смесител 5 мин, добавл ют 0,5 мае.ч. полиметил(дихлорфенил)силоксанау пе- ремекивают 1 мин. Загружают 40 мае.ч. ПВХ МС 6602С, перемешивают 1 мин, добавл ют 40 мае,4. ПВХ МС 6602С, перемешивают 2мин, добавл ют 20 мас,ч„ ПВХ C-6402HS перемешивают 8 мин9 ва- куумируют. Пластизоль оставл ют на вызреваете на 24 ч.44 parts by weight of the epoxidized soybean oil, barium sulphate paste and calcium stearate and zinc stearate are loaded into the planetary paddle mixer, the contents of the mixer are mixed for 5 minutes, 0.5 wt.h. polymethyl (dichlorophenyl) siloxane is spiked for 1 min. Download 40 mah. PVC MS 6602C, stirred for 1 min, add 40 May, 4. PVC MS 6602C, stirred for 2 min, 20 wt. Added, h „PVC C-6402HS stirred for 8 min9 was evacuated. Plastisol is left to mature for 24 hours.
Твердость пластизольной пленки определ ют следующим образом,The hardness of the plastisol film is determined as follows.
Пластизоль нанос т на пластинуPlastisol is applied to the plate.
из жести таким образом, чтобы уровень был заведомо выше зазора, установленного на ноже Гарднера. Избыток пласти зол снимают с помощью ножа Гарднера, отрегулированного на 1,27 мм. Сразу же после нанесени пластину с пласти- золем помещают в термошкаф, нагретый до температуры 20512°С, и выдерживают при этой температуре 3,5 мин. Пластину извлекают из термошкафа, охлаждают до комнатной температуры и снимаfrom the tin so that the level was obviously above the gap set on the Gardner knife. Excess plasticity is removed with a Gardner knife, adjusted to 1.27 mm. Immediately after the application, the plate with plastisol is placed in a heating cabinet heated to a temperature of 20512 ° C and kept at this temperature for 3.5 minutes. The plate is removed from the oven, cooled to room temperature and removed.
ют гщенку с пластины. Из пленки вырубают три диска диаметром J«,1 мм. Измерение твердости провод т на пакете из 2-3 образцов твердомером типа Шор А.They are fed from the plate. Three discs with a diameter of J “, 1 mm are cut out of the film. The hardness measurement is carried out on a package of 2-3 samples with a Shore A. hardness meter.
Момент отвинчивани определ ют прибором Торк Тестер на банках, укупоренных крышками, покрытыми плас- тизолем. Желатинизацию пластиэол на крышках провод т при 220-240°С в течение 60 с. Состав пластизол , момент отвинчивани крышки и твердость пластизольной пленки указаны в таблице.The moment of unscrewing is determined with a Tork Tester device on cans corked with lids covered with plastisol. The gelatinization of the plastiol on the caps is carried out at 220-240 ° C for 60 s. The composition of the plastisol, the moment the cap is unscrewed, and the hardness of the plastisol film are shown in the table.
Примеры 1-12 осуществл ют по предлагаемому способу,Examples 1-12 are carried out according to the proposed method
пример 13- по известному.example 13 is known.
Свойства и составы готастизолей приведены в таблице. Композиции получают и испытывают, как указано в примере 1.The properties and compositions of gotiztisols are given in the table. The compositions receive and test, as indicated in example 1.
Claims (1)