SU1342906A1 - Coating for fire-proof deck structures - Google Patents

Coating for fire-proof deck structures Download PDF

Info

Publication number
SU1342906A1
SU1342906A1 SU853973414A SU3973414A SU1342906A1 SU 1342906 A1 SU1342906 A1 SU 1342906A1 SU 853973414 A SU853973414 A SU 853973414A SU 3973414 A SU3973414 A SU 3973414A SU 1342906 A1 SU1342906 A1 SU 1342906A1
Authority
SU
USSR - Soviet Union
Prior art keywords
coating
composition
deck
omp
water
Prior art date
Application number
SU853973414A
Other languages
Russian (ru)
Inventor
Николай Алексеевич Озеров
Владимир Игоревич Сомов
Сергей Васильевич Сычев
Лариса Алексеевна Яковлева
Татьяна Юрьевна Короткова
Original Assignee
Ленинградский филиал Всесоюзного научно-исследовательского института противопожарной обороны
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ленинградский филиал Всесоюзного научно-исследовательского института противопожарной обороны filed Critical Ленинградский филиал Всесоюзного научно-исследовательского института противопожарной обороны
Priority to SU853973414A priority Critical patent/SU1342906A1/en
Application granted granted Critical
Publication of SU1342906A1 publication Critical patent/SU1342906A1/en

Abstract

Изобретение относитс  к магнитным палубным покрыти м (ОМЛ) и предназначено дл  применени  в судовых противопожарн 11х конструкци х. Целью изобретени   вл етс  повышение огнестойкости палубных конструкций. Пель достигаетс  тем, что основн(1й слой ОМЛ, содержащий асбест, портландцемент , вспученньй вермикулит и поду, дополнительно содержит су;:1 фат алюмини  Al2( при следующем соотношении компонентов, мас.%: асбест 1,0- 4,0; портландцемент 43,0-57,0; вспученный вермикулит 10,0-15,0; сульфат алюмини  0,5-4,5; вода 30,0-35,0. 1 табл. с (Л го The invention relates to magnetic deck coatings (AML) and is intended for use in shipboard fire protection 11x designs. The aim of the invention is to increase the fire resistance of deck structures. Pel is achieved by the fact that the main layer (1st layer of AML, containing asbestos, portland cement, expanded vermiculite and hearth, additionally contains su;: 1 veil of Al2 aluminum (in the following ratio of components, wt.%: Asbestos 1.0-4.0; portland 43.0-57.0; exfoliated vermiculite 10.0-15.0; aluminum sulfate 0.5-4.5; water 30.0-35.0. 1 table s (L of

Description

Изобретение относитс  к мастичным палубным покрыти м и предназначено дл  применени  в судовых против опо- жарных конструкци х.The invention relates to mastic deck coatings and is intended for use in ship against fouling structures.

Цель изобретени  - повышение огнестойкости палубных конструкций.The purpose of the invention is to increase the fire resistance of deck structures.

Пример. В состав покрыти  вход т, мас.%:Example. The composition of the coating includes, wt.%:

Асбест0,5Asbestos 0.5

Портландцемент 47,5 Вспученный вермикулит15 ,0 Вода 33,5 Сульфат алюмини  3,6 Состав готов т путем смешени  всех сухих компонентов. Затем сульфат алюмини  раствор ют в воде и полученный раствор добавл ют в смесь сухих компонентов и перемешивают до получени  однородной массы.Portland cement 47.5 Expanded vermiculite15, 0 Water 33.5 Aluminum sulphate 3.6 Composition prepared by mixing all the dry components. Aluminum sulphate is then dissolved in water and the resulting solution is added to the mixture of dry ingredients and stirred until a homogeneous mass is obtained.

Покрытие нанос т на стальную палубу , что обеспечивает противопожарную защиту помещени  при пожаре в нижерасположенном помещении. Характеристи-,, струкций, в качестве покрыти  котокой конструкций с такими покрыти ми  вл етс  врем  достижени  предельно допустимого среднего превышени  первоначальной температуры на необогреваемой поверхности, которое принимаетс  равным . Толщина испытываемых образцов 28 мм. Изменение времени достижени  предела огнестойкости и Ьредела прочности при сжатии в зависимости от состава покрыти  приведены в таблице.The coating is applied to the steel deck, which provides fire protection for the room during a fire in the downstream room. Characteristics, as a coating for such constructions with such coatings, is the time to reach the maximum permissible average excess temperature on the unheated surface, which is assumed to be equal. The thickness of the test specimens is 28 mm. The change in the time to reach the fire resistance and the limit of compressive strength depending on the composition of the coating are given in the table.

Из табицы видно, что составы 1-10, изготовленные согласно описанным рецептурам , не удовлетвор ют поставленным требовани м как по времени дости- жени  предела огнестойкости, так и по пределу прочности. В том случае, если ввести в состав менее 1% сульфата алюмини  Al2(S04), улучшени  огнестойкости по сравнению с ОМП не наблюдаетс  (состав 9). Введение в состав более 5% сульфата алюмини  Alj(SO)j (состав 10) нецелесообразно, так как не удаетс  намного превысить среднее врем  достижени  предела огнестойкости предлагаемого состава при сохранении его физико-механических свойств. В случае, если процентное соотноще- ние ингредиентов не соответствует предлагаемому составу, то, как показано в таблице, такие составы не удовлетвор ют требовани м достижени  необходи юсти предела прочности при сжатии. При этом наблюдаетс  усадка.From the table it can be seen that compounds 1-10, made according to the described recipes, do not satisfy the set requirements both in terms of time to reach the fire resistance limit and in terms of strength. In that case, if less than 1% aluminum sulphate Al2 is introduced into the composition (S04), there is no improvement in fire resistance compared to OMP (composition 9). Introduction to the composition of more than 5% aluminum sulfate Alj (SO) j (composition 10) is impractical, since it is not possible to significantly exceed the average time to reach the fire resistance limit of the proposed composition while maintaining its physical and mechanical properties. In case the percentage ratio of ingredients does not correspond to the proposed composition, then, as shown in the table, such compositions do not meet the requirements of achieving the required compressive strength. Shrinkage is observed.

30thirty

3535

4040

4545

5050

5555

рых может быть использован предлагае мый состав. Предел прочности при сжатии этих образцов также несколько выше (приблизительно на 8%).The proposed composition may be used. The compressive strength of these specimens is also somewhat higher (approximately 8%).

Claims (1)

Таким образом, при одинаковой огнестойкости конструкций, изготовленных с покрытием согласно предлагаемо рецептуре с ОМП, толщина предлагаемо го покрыти , как показывают эксперименты , может быть на 25% меньше, чем толщина основного сло  покрыти  ОМП. С учетом того, что расход основного сло  покрыти  ОМП на 100 м палубы составл ет 4990 кг, уменьшение толщины основного сло  на 25% позвол ет уменьшить расход материала почти на 1250 кг.. Формула изобретени Thus, with the same fire resistance of structures made with the coating according to the proposed formulation with OMP, the thickness of the proposed coating, as shown by experiments, can be 25% less than the thickness of the main layer of the OMP coating. Taking into account the fact that the consumption of the main layer of the coating of OMP per 100 m of the deck is 4,990 kg, reducing the thickness of the main layer by 25% reduces the consumption of material by almost 1,250 kg. Покрытие дл  огнестойких палубных конструкций, содержащее асбест, порт ландцемент, вспученный вермикулит и воду, отличающеес  тем что, с целью повьш1ени  огнестойкости палубных конструкций, оно дополнительно содержит сульфат алюмини  Al(SO) при следующем (гоотношении компонентов, мас.%:Coating for fire-resistant deck structures containing asbestos, port of cement, expanded vermiculite and water, characterized in that, in order to increase the fire resistance of deck structures, it also contains aluminum sulfate Al (SO) with the following (ratio of components, wt.%: Асбест1,0-4,0Asbestos1.0-4.0 Портландцемент 43,0-57,0 Вспученный вермикулит10 ,0-13,0 Сульфат алюмини  0,5-4,5 Вода 30,0-35,0Portland cement 43.0-57.0 Expanded vermiculite10, 0-13.0 Aluminum sulfate 0.5-4.5 Water 30.0-35.0 5five 00 трещинообразование (составы 1 и 3), быстрое затвердение (составы 2 и 4). Состав 5 не обеспечивает теплоизолирующих свойств (из-за недостаточного количества вермикулита), а состав 6 - достаточной механической прочности . В том случае, если в составе присутствует недостаточное количество воды (состав 7), состав становитс  нетехнологичным (неудобоукладываемым). А при избытке воды (состав 8) наблюдаютс  увеличение растекаемости усадка и мала  механическа  прочность.cracking (compounds 1 and 3), rapid hardening (compounds 2 and 4). Composition 5 does not provide insulating properties (due to an insufficient amount of vermiculite), and composition 6 does not provide sufficient mechanical strength. In the event that there is an insufficient amount of water in the composition (composition 7), the composition becomes non-technological (non-composable). And with an excess of water (composition 8), an increase in the flowability of shrinkage and low mechanical strength are observed. Результаты испытаний образцов покрытий , изготовленных согласно рецептуре составов 11-21, показывают, что все одиннадцать образцов при испытани х превьппают врем  достижени  предельно допустимого превьш1ени  первоначальной температуры на необогреваемой поверхности на 20% (по сравнению с образцом ОМП) что подтверждает хорошую огнестойкость палубных кон0The results of testing samples of coatings made according to the formulation of compositions 11-21 show that all eleven samples during testing exceed the time to reach the maximum allowable prevailing of the initial temperature on the unheated surface by 20% (compared to the sample of MLE), which confirms good fire resistance of deck cones 5five 00 5five 00 5five рых может быть использован предлагаемый состав. Предел прочности при сжатии этих образцов также несколько выше (приблизительно на 8%).The proposed composition can be used. The compressive strength of these specimens is also somewhat higher (approximately 8%). Таким образом, при одинаковой огнестойкости конструкций, изготовленных с покрытием согласно предлагаемой рецептуре с ОМП, толщина предлагаемого покрыти , как показывают эксперименты , может быть на 25% меньше, чем толщина основного сло  покрыти  ОМП. С учетом того, что расход основного сло  покрыти  ОМП на 100 м палубы составл ет 4990 кг, уменьшение толщины основного сло  на 25% позвол ет уменьшить расход материала почти на 1250 кг.. Формула изобретени Thus, with the same fire resistance of structures made with the coating according to the proposed formulation with OMP, the thickness of the proposed coating, as shown by experiments, can be 25% less than the thickness of the main layer of the coating of OMP. Taking into account the fact that the consumption of the main layer of the coating of OMP per 100 m of the deck is 4,990 kg, reducing the thickness of the main layer by 25% reduces the consumption of material by almost 1,250 kg. Покрытие дл  огнестойких палубных конструкций, содержащее асбест, портландцемент , вспученный вермикулит и воду, отличающеес  тем, что, с целью повьш1ени  огнестойкости палубных конструкций, оно дополнительно содержит сульфат алюмини  Al(SO) при следующем (гоотношении компонентов, мас.%:Coating for fire-resistant deck structures containing asbestos, Portland cement, expanded vermiculite and water, characterized in that, in order to increase the fire resistance of the deck structures, it also contains aluminum sulfate Al (SO) with the following (component ratio, wt.%: Асбест1,0-4,0Asbestos1.0-4.0 Портландцемент 43,0-57,0 Вспученный вермикулит10 ,0-13,0 Сульфат алюмини  0,5-4,5 Вода 30,0-35,0Portland cement 43.0-57.0 Expanded vermiculite10, 0-13.0 Aluminum sulfate 0.5-4.5 Water 30.0-35.0
SU853973414A 1985-10-28 1985-10-28 Coating for fire-proof deck structures SU1342906A1 (en)