Abstract

FIELD: building materials.

SUBSTANCE: invention is related to production of dry building mixtures, and can be used for insulating and corrosion-protective coatings for external and internal finishing of buildings and structures for various purposes. The dry building mixture contains, wt.%: Portland cement 15.2-45.7, quartz sand with M_S equal to 2.0-2.5 48.6-81.7, wollastonite with particle sizes from 2 to 60 microns 1.5-4.9, a complex additive including superplasticizer powder C-3 0.1-0.5 and calcium or zinc stearate 0.1-0.3.

EFFECT: production of a dry construction mixture of high density, increasing the strength, water resistance, resistance to the effects of low-mineralized waters and chlorine-containing solutions of the coating made using the building mixture.

1 cl

Description

Изобретение относится к области строительных материалов, а именно к производству сухих строительных смесей, и может быть использовано для изоляционных и коррозионно-защитных покрытий для наружной и внутренней отделки зданий и сооружений различного назначения. The invention relates to the field of building materials, namely to the production of dry building mixtures, and can be used for insulating and corrosion-protective coatings for external and internal finishing of buildings and structures for various purposes.

Известна сухая строительная смесь, включающая цемент, песок и комплексную добавку с пластификатором на основе метилцеллюлозы и известковой смеси для приготовления водонепроницаемого раствора (Патент РФ № 2119467). Введение комплексной добавки обеспечивает хорошую пластичность раствора, высокую морозостойкость и водонепроницаемость. Однако такая сухая строительная смесь имеет повышенный расход цемента и недостаточно высокую коррозионную стойкость.A dry construction mixture is known, including cement, sand and a complex additive with a plasticizer based on methylcellulose and a lime mixture for the preparation of a waterproof mortar (RF Patent No. 2119467). The introduction of a complex additive ensures good plasticity of the solution, high frost resistance and water resistance. However, such a dry construction mixture has an increased consumption of cement and insufficiently high corrosion resistance.

Известна сухая строительная смесь, включающая, мас.%: цемент 10-25, песок 50-80 и комплексную добавку 10-25, которая содержит, мас.%: порошок С-3 1-3, гипс 18-28, доломит 2-7, вулканическую породу 40-60 и микрокремнезем - остальное (Патент РФ 2079462). Использование сухой комплексной добавки облегчает ее приготовление и введение в строительную смесь, однако не обеспечивает высокую прочность и коррозионную стойкость.A dry construction mixture is known, including, wt.%: cement 10-25, sand 50-80 and a complex additive 10-25, which contains, wt.%: C-3 powder 1-3, gypsum 18-28, dolomite 2- 7, volcanic rock 40-60 and microsilica - the rest (RF Patent 2079462). The use of a dry complex additive makes it easier to prepare and introduce into the building mixture, but does not provide high strength and corrosion resistance.

Наиболее близким по технической сущности и достигаемому результату является сухая строительная смесь (Патент РФ № 2214376), состоящая из цемента, песка и комплексной добавки, включающей порошок пластификатора С-3, причем указанная добавка дополнительно содержит стеарат кальция или стеарат цинка при следующем соотношении компонентов, мас.%: цемент 14,2 - 49,9, песок 49,6 - 85,6, С-3 0,04 - 0,50, стеарат кальция или стеарат цинка 0,10 - 0,3. Недостатком данной сухой строительной смеси являются невысокая прочность и коррозионная стойкость, что значительно ограничивает сферу ее применения.The closest in technical essence and achieved result is a dry construction mixture (RF Patent No. 2214376), consisting of cement, sand and a complex additive including C-3 plasticizer powder, and this additive additionally contains calcium stearate or zinc stearate in the following ratio of components, wt.%: cement 14.2 - 49.9, sand 49.6 - 85.6, C-3 0.04 - 0.50, calcium stearate or zinc stearate 0.10 - 0.3. The disadvantage of this dry construction mixture is its low strength and corrosion resistance, which significantly limits its scope of application.

Техническая задача, положенная в основу заявляемого изобретения, состоит в получении сухой строительной смеси высокой плотности, а покрытие, выполненное с использованием заявленной строительной смеси, обладает прочностью, водонепроницаемостью и стойкостью к воздействию слабоминерализованных вод и хлорсодержащих растворов.The technical problem underlying the claimed invention is to obtain a dry building mixture of high density, and the coating made using the claimed building mixture is durable, waterproof and resistant to the effects of low-mineralized waters and chlorine-containing solutions.

Поставленная задача решается таким образом, что сухая строительная смесь, состоящая из портландцемента, кварцевого песка и комплексной добавки, включающей порошок суперпластификатора С-3 и стеарат кальция или цинка, содержит кварцевый песок с М_кр. равным 2,0-2,5, и дополнительно – мелкодисперсный волластонит с размерами частиц от 2 до 60 мкм, при следующем соотношении компонентов, мас.%: портландцемент – 15,2-45,7, кварцевый песок с модулем крупности М_кр. равным 2,0-2,5 – 48,6-81,7, суперпластификатор С-3 – 0,1-0,5, стеарат кальция или стеарат цинка – 0,1-0,3, мелкодисперсный волластонит – 1,5-4,9.The problem is solved in such a way that a dry construction mixture consisting of Portland cement, quartz sand and a complex additive, including C-3 superplasticizer powder and calcium or zinc stearate, contains quartz sand with M _cr. equal to 2.0-2.5, and additionally - finely dispersed wollastonite with particle sizes from 2 to 60 microns, with the following ratio of components, wt.%: Portland cement - 15.2-45.7, quartz sand with a particle size modulus M _cr. equal to 2.0-2.5 - 48.6-81.7, superplasticizer C-3 - 0.1-0.5, calcium stearate or zinc stearate - 0.1-0.3, fine wollastonite - 1.5 -4.9.

Предлагаемая сухая строительная смесь отличается от известной качественным и количественным составом.The proposed dry construction mixture differs from the known one in its qualitative and quantitative composition.

Получение сухой строительной смеси высокой плотности, а также изделий на ее основе с высокой прочностью, водонепроницаемостью и стойкостью к воздействию слабоминерализованных вод и хлорсодержащих растворов обеспечивается за счет применения комплекса рационально подобранных компонентов, а именно портландцемента, кварцевого песка с М_кр. 2,0-2,5, суперпластификатора С-3, стеарат кальция или стеарат цинка и микродисперсного волластонита.The production of high-density dry building mixture, as well as products based on it with high strength, water resistance and resistance to the effects of low-mineralized waters and chlorine-containing solutions is ensured through the use of a complex of rationally selected components, namely Portland cement, quartz sand with M _cr. 2.0-2.5, superplasticizer C-3, calcium stearate or zinc stearate and microdispersed wollastonite.

Волластонит, химического состава: CaO 45÷48%, SiO₂ 50÷53%, Fe₂O₃ 0,05÷0,2%, Al₂O₃ 0,1÷0,3%, MgO 0,4÷1% и др. с размерами частиц от 2 до 60 мкм с медианным диаметром 6 мкм, являясь микрозаполнителем, заполняет пустоты между частицами более крупных фракций, обеспечивает высокую плотность и соответственно прочность и водонепроницаемость. Кроме того, волластонит в комплексе с гидрофобной добавкой стеарата кальция или стеарата цинка повышает водонепроницаемость, коррозионную стойкость к воздействию слабоминерализованных вод и хлорсодержащих растворов, так как является устойчивым к воздействию этих агрессивных сред.Wollastonite, chemical composition: CaO 45÷48%, SiO ₂ 50÷53%, Fe ₂ O ₃ 0.05÷0.2%, Al ₂ O ₃ 0.1÷0.3%, MgO 0.4÷1 %, etc. with particle sizes from 2 to 60 microns with a median diameter of 6 microns, being a micro-filler, fills the voids between particles of larger fractions, provides high density and, accordingly, strength and water resistance. In addition, wollastonite in combination with the hydrophobic additive of calcium stearate or zinc stearate increases water resistance and corrosion resistance to the effects of low-mineralized waters and chlorine-containing solutions, since it is resistant to these aggressive environments.

Для приготовления сухой строительной смеси используются портландцемент ЦЕМ I 42,5Н, ЦЕМ III/А 42,5Н по ГОСТ 31108-2020, песок кварцевый с М_кр.= 2,0-2,5 по ГОСТ 8736-2014; суперпластификатор С-3, порошок, по ТУ 6-36-0204229-625-90; стеарат кальция по ТУ 6-09-17-317-96 или стеарат цинка по ТУ 6-09-17-257-88 и волластонит марки МИВОЛ 05-97 по ТУ 5777-006-40705684-2003.To prepare the dry building mixture, Portland cement CEM I 42.5N, CEM III/A 42.5N in accordance with GOST 31108-2020, quartz sand with M _cr. = 2.0-2.5 according to GOST 8736-2014; superplasticizer S-3, powder, according to TU 6-36-0204229-625-90; calcium stearate according to TU 6-09-17-317-96 or zinc stearate according to TU 6-09-17-257-88 and wollastonite grade MIVOL 05-97 according to TU 5777-006-40705684-2003.

Сухую строительную смесь получают следующим образом: портландцемент, кварцевый песок с модулем крупности М_кр.2,0-2,5, суперпластификатор С-3, стеарат кальция или стеарат цинка и волластонит дозируются и перемешиваются в течение 15-20 минут. Готовую смесь подают на расфасовку.The dry construction mixture is prepared as follows: Portland cement, quartz sand with a particle size modulus M _cr. 2.0-2.5, superplasticizer C-3, calcium stearate or zinc stearate and wollastonite are dosed and mixed for 15-20 minutes. The finished mixture is served for packaging.

Сухая строительная смесь может использоваться для производства наружной и внутренней отделки зданий различного назначения, для ремонтных работ, изоляционных и коррозионно-защитных покрытий и др.Dry construction mixture can be used for the production of external and internal finishing of buildings for various purposes, for repair work, insulating and corrosion-protective coatings, etc.

Claims

A dry construction mixture consisting of Portland cement, quartz sand and a complex additive including C-3 superplasticizer powder and calcium or zinc stearate, characterized in that quartz sand is used with M _cr. equal to 2.0-2.5, and additionally the mixture contains finely dispersed wollastonite with particle sizes from 2 to 60 microns, with the following component ratio, wt.%:

Portland cement 15.2-45.7

Quartz sand 48.6-81.7

Superplasticizer S-3 0.1-0.5

Calcium stearate or

zinc stearate 0.1-0.3

Fine wollastonite 1.5-4.9