RU2808465C1 - Universal tinting paste - Google Patents
Universal tinting paste Download PDFInfo
- Publication number
- RU2808465C1 RU2808465C1 RU2023125256A RU2023125256A RU2808465C1 RU 2808465 C1 RU2808465 C1 RU 2808465C1 RU 2023125256 A RU2023125256 A RU 2023125256A RU 2023125256 A RU2023125256 A RU 2023125256A RU 2808465 C1 RU2808465 C1 RU 2808465C1
- Authority
- RU
- Russia
- Prior art keywords
- pigment
- wetting
- pigments
- molecular weight
- resin
- Prior art date
Abstract
Description
Изобретение относится к колеровочным пастам, предназначенным для использования в готовых базовых лакокрасочных материалах (ЛКМ). The invention relates to tinting pastes intended for use in ready-made base paints and varnishes.
Из уровня техники известна колеровочная композиция для окрасочных продуктов (патент RU 2157395 опубликовано: 10.10.2000 Бюл. № 28), содержащая 2-75 мас. % пигментного компонента (А), состоящего из одного или более органических и/или неорганических пигментов и, возможно пигментов-наполнителей, 10-60 мас. % компонента-разбавителя (Б), состоящего из одного или более органических растворителей, ни один из которых не является алифатическим спиртом или ароматическим углеводородом, и 10-50 мас.% (в расчете на 100% нелетучей части) компонента - пленкообразующего (В), состоящего из одного или более пленкообразующих, растворимых в компоненте-разбавителе (Б). Она отличается тем, что 20-100% от общей массы компонента-разбавителя (Б) составляет биодеградирующий эфир молочной кислоты и С1-С10 спирта, а 70-100% от общей массы компонента-пленкообразующего (В) составляют кетональдегидная смола, кетонная смола и/или альдегидная смола, которые по меньшей мере частично растворимы в растворителях окрасочных продуктов, включая алифатические углеводороды. A tinting composition for painting products is known from the prior art (patent RU 2157395 published: 10.10.2000 Bulletin No. 28), containing 2-75 wt. % pigment component (A), consisting of one or more organic and/or inorganic pigments and possibly filler pigments, 10-60 wt. % diluent component (B), consisting of one or more organic solvents, none of which is an aliphatic alcohol or aromatic hydrocarbon, and 10-50 wt.% (based on 100% non-volatile portion) film-forming component (B) , consisting of one or more film-forming agents, soluble in the diluent component (B). It differs in that 20-100% of the total mass of the diluent component (B) is a biodegradable ester of lactic acid and C1-C10 alcohol, and 70-100% of the total mass of the film-forming component (B) is ketonaldehyde resin, ketone resin and /or aldehyde resin that is at least partially soluble in paint product solvents, including aliphatic hydrocarbons.
Известна универсальная пигментная колеровочная паста (патент на изобретение RU 2320691, опубликовано: 27.03.2008 Бюл. № 9), содержащая пигмент, пленкообразующее, диспергатор, загуститель, органический растворитель. В качестве пленкообразующего используют алкидную глифталевую смолу на основе льняного масла, глицерина и фталевого ангидрида в соотношении, мас.%: 45-47:17-19:34-38, с вязкостью 60 с, измеренной при температуре (20,0±0,5)°С по вискозиметру ВЗ-246, в виде 50%-ного раствора смолы в ксилоле с кислотным числом 17-19 мгКОН/г, в качестве загустителя используют загуститель Clayton AF, в качестве органического растворителя используют ксилол, при следующем соотношении компонентов, мас.%: указанный 50%-ный раствор алкидной глифталевой смолы 30-40, ксилол 34-45, диспергатор 0,9-2, загуститель Clayton AF 0,3-0,5, пигмент - остальное. A universal pigment tinting paste is known (invention patent RU 2320691, published: March 27, 2008 Bulletin No. 9), containing pigment, film-forming agent, dispersant, thickener, and organic solvent. Alkyd glypthal resin based on linseed oil, glycerin and phthalic anhydride is used as a film-forming agent in the ratio, wt.%: 45-47:17-19:34-38, with a viscosity of 60 s, measured at a temperature of (20.0±0. 5)°C according to the VZ-246 viscometer, in the form of a 50% solution of resin in xylene with an acid number of 17-19 mgKOH/g, Clayton AF thickener is used as a thickener, xylene is used as an organic solvent, with the following ratio of components, wt.%: the specified 50% solution of alkyd glyphthalic resin 30-40, xylene 34-45, dispersant 0.9-2, Clayton AF thickener 0.3-0.5, pigment - the rest.
Недостатком данного состава является ограниченное применение данных концентратов. The disadvantage of this composition is the limited use of these concentrates.
Наиболее близким к предлагаемому техническому решению является цветная паста для растворяющих красок (патент CN101085888, опубл. 12.12.2007). Она состоит из пигментов плюс альдегидных и кетоновых смол с отличной совместимостью с различными смолами, растворителями и добавками, экологически чистыми ацетатными растворителями, высокомолекулярными супердиспергаторами и средствами для обработки поверхности. Ее особенностью является то, что ее массовое содержание составляет: пигмент 25-80%, альдегидная и кетоновая смолы 5-32%, сложноэфирный растворитель 10-40%, диспергатор А составляет 1-9% или диспергатор В составляет 1-6%, средство для обработки поверхности 0-5%. The closest to the proposed technical solution is a colored paste for solvent paints (patent CN101085888, published 12/12/2007). It consists of pigments plus aldehyde and ketone resins with excellent compatibility with a variety of resins, solvents and additives, environmentally friendly acetate solvents, high molecular weight superdispersants and surface treatments. Its peculiarity is that its mass content is: pigment 25-80%, aldehyde and ketone resins 5-32%, ester solvent 10-40%, dispersant A is 1-9% or dispersant B is 1-6%, the product for surface treatment 0-5%.
Недостатком данной пасты является содержание растворителя, что может повлиять на флокуляцию пигментов в каком-либо из типов связующих базовых красок, так как растворитель меняет полярность системы. The disadvantage of this paste is that it contains solvent, which can affect the flocculation of pigments in any type of base paint binder, since the solvent changes the polarity of the system.
Задачей, на решение которой направлено заявляемое изобретение, является разработка универсальной колеровочной пигментной пасты, без содержания растворителей в систему, которые могут пагубно повлиять на процессы стабилизации пигментов. The problem to be solved by the claimed invention is the development of a universal tinting pigment paste, without containing solvents in the system, which can adversely affect the processes of pigment stabilization.
Данная задача решается тем, что универсальная колеровочная паста, содержит кетональдегидную смолу, смачивающий и диспергирующий агент и пигментный компонент, в качестве смачивающего и диспергирующего агента использован высокомолекулярный полимерный гипердисперсант с молекулярным весом ≥5000 г/моль, основанный на технологии контролируемой полимеризации акрилатов, с группой сродства к пигментам, а в качестве пигментов использован органический или неорганический пигмент, при следующем соотношении ингредиентов, в масс.% кетональдегидная смола – 42- 80, смачивающий и диспергирующий агент – 5-8, - пигментный компонент 15-50. This problem is solved by the fact that the universal tinting paste contains a ketonaldehyde resin, a wetting and dispersing agent and a pigment component; a high molecular weight polymer hyperdispersant with a molecular weight of ≥5000 g/mol is used as a wetting and dispersing agent, based on the technology of controlled polymerization of acrylates, with a group affinity for pigments, and organic or inorganic pigment is used as pigments, with the following ratio of ingredients, in wt.% ketonaldehyde resin - 42-80, wetting and dispersing agent - 5-8, - pigment component 15-50.
Техническим результатом, достигаемым предлагаемым составом, является универсальность колеровочной пасты, подходящей для всех известных баз, в том числе эпоксидных, акриловых, алкидных, полиуретановых и т.д. The technical result achieved by the proposed composition is the versatility of the tinting paste, suitable for all known bases, including epoxy, acrylic, alkyd, polyurethane, etc.
Колеровочная паста применяется для придания цвета в лакокрасочных материалах. Tinting paste is used to add color to paints and varnishes.
Колеровочная паста для получения желтого, зеленого или синего цвета имеет следующий состав, масс.%: The tinting paste for obtaining yellow, green or blue has the following composition, wt.%:
- кетональдегидная смола – 42- 80 - ketonaldehyde resin – 42-80
- смачивающий и диспергирующий агент – 5-8 - wetting and dispersing agent – 5-8
- пигментный компонент, состоящий из органического или неорганического пигмента - 15-50. - pigment component consisting of organic or inorganic pigment - 15-50.
Кетональдегидная смола не способна к пленкообразованию. Смола является производным алкил циклогексанона с карбонильными и гидроксильными функциональными группами. За счет своей химической природы данный тип смолы не омыляется, за счет чего сохраняется стабильность полученной пасты, обладает устойчивостью к пожелтению, что важно для колеровочных паст. Благодаря функциональным группам дает возможность получения паст с высокой интенсивностью цвета (возможность высокой загрузки пигментов), обеспечивает низкую вязкость пигментных концентратов и хорошую совместимость пигментных паст. Ketonaldehyde resin is not capable of film formation. The resin is an alkyl cyclohexanone derivative with carbonyl and hydroxyl functional groups. Due to its chemical nature, this type of resin does not saponify, due to which the stability of the resulting paste is maintained and is resistant to yellowing, which is important for tinting pastes. Thanks to the functional groups, it makes it possible to obtain pastes with high color intensity (the possibility of high loading of pigments), ensures low viscosity of pigment concentrates and good compatibility of pigment pastes.
Смачиватель - диспергатор высокомолекулярный подбирали исходя из его эффективных свойств, а именно высокий молекулярный вес, хорошие реологические свойства системы, так как смачиватель – диспергатор имеет влияние на реологические свойства и смачивание пигмента, от чего зависит количество пигмента в колеровочной пасте. В качестве смачивающего и диспергирующего агента используют добавки, которые содержат в себе группы, обладающие сродством к пигменту, содержащие нейтрализованные группы «кислота и основание». The wetting agent - high molecular weight dispersant was selected based on its effective properties, namely high molecular weight, good rheological properties of the system, since the wetting agent - dispersant has an effect on the rheological properties and wetting of the pigment, which determines the amount of pigment in the tinting paste. As a wetting and dispersing agent, additives are used that contain groups that have an affinity for the pigment, containing neutralized acid and base groups.
Высокомолекулярные смачивающие- диспергирующие добавки — это добавки с молекулярным весом ≥5000 г/моль, основаны на технологии контролируемой полимеризации акрилатов. Данная технология подразумевает структурированное распределение мономеров. Якорные группы создают молекулярное звено полиакрилата (контролируемой полимеризацией) и расположены в определенных (упорядоченных) местах. High-molecular wetting-dispersing additives are additives with a molecular weight of ≥5000 g/mol, based on the technology of controlled polymerization of acrylates. This technology involves a structured distribution of monomers. The anchor groups create the molecular unit of the polyacrylate (by controlled polymerization) and are located in specific (ordered) locations.
Смачивающий и диспергирующий агент за счет своей молекулярной структуры позволяет ускорить процесс дробления (диспергирования) пигментов, обеспечивают получение стабильной суспензии. The wetting and dispersing agent, due to its molecular structure, allows you to speed up the process of crushing (dispersing) pigments and ensure the production of a stable suspension.
В качестве диспергирующего агента используются амфифильные соединения, они гидрофильны и липофильны. Органические пигменты содержат в основном ароматические группы, поэтому применены добавки с содержанием фенильных и нафтильных групп. Для более лучшей эффективности применены добавки с несколькими функциональными группами для предотвращения процесса флокуляции пигмента. Химическая природа добавок представляет собой высокомолекулярные полимеры с группами, имеющие сродство к пигменту. Amphiphilic compounds are used as dispersing agents; they are hydrophilic and lipophilic. Organic pigments contain mainly aromatic groups, so additives containing phenyl and naphthyl groups are used. For better efficiency, additives with several functional groups are used to prevent the pigment flocculation process. The chemical nature of the additives is high molecular weight polymers with groups that have an affinity for the pigment.
Смачивание частиц пигмента важно для их равномерного распределения в жидкости, частица пигмента должна быть полностью окружена жидкой средой, что дает хорошо диспергироваться пигменту в диспергирующей смоле. Диспергирующие добавки должны снижать поверхностное натяжение жидкости. Для смачивания твердого тела жидкостью поверхностное натяжение жидкости должно быть ниже поверхностного натяжения твердого тела. Жидкость с меньшим поверхностным натяжением лучше смачивает пигменты, чем жидкость с высоким поверхностным натяжением. Следовательно, добавка, улучшающая смачивание, должна в первую очередь снижать поверхностное натяжение жидкости. Если этого не происходит, пигмент не смачивается или плохо смачивается в диспергирующей среде. Wetting of the pigment particles is important for their uniform distribution in the liquid; the pigment particle must be completely surrounded by the liquid medium, which allows the pigment to be well dispersed in the dispersing resin. Dispersing additives should reduce the surface tension of the liquid. For a solid to be wetted by a liquid, the surface tension of the liquid must be lower than the surface tension of the solid. A liquid with a lower surface tension wets pigments better than a liquid with a high surface tension. Therefore, a wetting additive must primarily reduce the surface tension of the liquid. If this does not happen, the pigment is not wetted or is poorly wetted in the dispersing medium.
Смачивающие диспергирующие добавки снижают вязкость колеровочных паст, что позволяет ввести максимальное количество пигмента в систему. Процесс диспергирования можно разделить на две стадии - смачивание, непосредственно диспергирование. Чтобы частицы пигмента были равномерно распределены в жидкой среде, они должны ею смочиться. Воздух, который содержится в пигментном порошке, должен быть полностью замещен, а частицы пигмента полностью окружены жидкостью. Процесс смачивания описывается уравнением Юнга. Смачивание пигмента зависит от поверхностного натяжения поверхностей. Добавка должна снижать поверхностное натяжение. Жидкость, имеющая поверхностное натяжение ниже лучше смачивает частицы пигмента (чем меньше угол смачивания, тем лучше смачивается поверхность частиц пигмента). Процесс диспергирования происходит более качественно, если частицы хорошо смочены диспергирующей фазой. Когда частицы пигмента уже достаточно смочены раствором пленкообразователя, то их поверхность покрыта добавкой, которая ослабляет взаимодействие между частицами пигмента и таким образом снижает вязкость пигментной пасты, что позволяет увеличить загрузку пигмента и процесс диспергирования (дробления) происходит быстрее, т.е. агломераты разрушаются до первичных или до меньших пигментных агрегатов. Оптимальное смачивание происходит, когда угол смачивания равен нулю. Таким образом, процесс диспергирования невозможен без процесса смачивания, так как разделить агломераты, если частицы не смочились жидкостью невозможно, эти функции выполняют добавки смачиватели-диспергаторы. Wetting dispersants reduce the viscosity of tinting pastes, which allows the maximum amount of pigment to be introduced into the system. The dispersion process can be divided into two stages - wetting and direct dispersion. In order for the pigment particles to be evenly distributed in the liquid medium, they must be moistened with it. The air contained in the pigment powder must be completely replaced, and the pigment particles are completely surrounded by liquid. The wetting process is described by Young's equation. Pigment wetting depends on the surface tension of the surfaces. The additive should reduce surface tension. A liquid with a lower surface tension better wets the pigment particles (the smaller the contact angle, the better the surface of the pigment particles is wetted). The dispersion process occurs more efficiently if the particles are well wetted with the dispersing phase. When the pigment particles are already sufficiently wetted with the film-forming solution, their surface is coated with an additive that weakens the interaction between the pigment particles and thus reduces the viscosity of the pigment paste, which allows the pigment loading to be increased and the dispersion (crushing) process occurs faster, i.e. agglomerates are destroyed to primary or smaller pigment aggregates. Optimal wetting occurs when the contact angle is zero. Thus, the dispersion process is impossible without the wetting process, since it is impossible to separate agglomerates if the particles are not wetted with liquid; these functions are performed by wetting-dispersant additives.
В качестве пигментов используют следующие пигменты: фталоцианиновый пигмент – пигмент синий с колор индексом 15:3 (Sinco Blue 4382-331); фталоцианиновый пигмент зеленый с колор индексом PG7 (Green 7), неорганический желтый пигмент с колор индексом PY 42 (S 920). The following pigments are used as pigments: phthalocyanine pigment – blue pigment with color index 15:3 (Sinco Blue 4382-331); phthalocyanine pigment green with color index PG7 (Green 7), inorganic yellow pigment with color index PY 42 (S 920).
Пигменты выбраны по определенным Колор-Индексам для того, чтобы из набора паст возможно было создание сборных цветов по понтонам. При выборе пигментов руководствовались высокими показателями свето- и атмосферостойкости. Пигмент желтый PY 42 является неорганическим оксидом железа, что дает желтый цвет и стойкость к внешним факторам, пигмент синий органический Pb 15:3, пигмент зеленый PG7 — это синтезированный пигмент, который в зависимости от способа получения имеет различные оттенки. Они созданы на основе фталоцианина и металлов комплексообразователей меди, получая синий, и хлорированием фталоцианина меди приводит к зеленому, эти пигменты обладают химической стойкостью и высокими свойствами к воздействию свето-погоды, имеют насыщенные яркие синий и зеленый цвета. Атмосферостойкость не ниже 4 баллов, светостойкость не ниже 7. The pigments are selected according to certain Color Indexes so that from a set of pastes it is possible to create prefabricated colors for pontoons. When choosing pigments, we were guided by high levels of light and weather resistance. Yellow pigment PY 42 is an inorganic iron oxide, which gives a yellow color and resistance to external factors, blue organic pigment Pb 15:3, green pigment PG7 is a synthesized pigment, which, depending on the production method, has different shades. They are created on the basis of phthalocyanine and metal complexing agents of copper, producing blue, and chlorination of copper phthalocyanine leads to green, these pigments have chemical resistance and high properties to the effects of light and weather, and have rich, bright blue and green colors. Weather resistance not lower than 4 points, light fastness not lower than 7.
Пигменты – это красящие вещества, которые используются для придания окраски другим материалам, в данном случае для получения цветных ЛКМ. Они влияют на механические характеристики покрытий, улучшают коррозионную стойкость и атмосферостойкость. Органические синтетические пигменты характеризуются входящими в них ароматическими группами, органические синтезированные пигменты имеют яркие цвета. Неорганические природные пигменты имеют в своем составе оксиды, сульфиды и др. и имеют цвета, соответствующие данным соединениям - тусклые, грязноватые оттенки. И те, и другие необходимы для создания полной необходимой палитры цветов. Также пигменты и синтетические, и неорганические нерастворимы в воде, функция у них одна – придание цвета. Pigments are coloring substances that are used to impart color to other materials, in this case to produce colored paints and varnishes. They affect the mechanical characteristics of coatings, improve corrosion resistance and weather resistance. Organic synthetic pigments are characterized by the aromatic groups they contain; organic synthetic pigments have bright colors. Inorganic natural pigments contain oxides, sulfides, etc. and have colors corresponding to these compounds - dull, dirty shades. Both are necessary to create the full required color palette. Also, both synthetic and inorganic pigments are insoluble in water; they have one function - giving color.
Изготовление колеровочной пигментной пасты осуществляется по следующему технологическому процессу: The production of tinting pigment paste is carried out according to the following technological process:
1. Приготовление смеси диспергирующей смолы, пигментов и добавки. Первым этапом загружается в дежу смола весь объем), сразу после загрузки смолы вводится смачиватель-диспергатор (весь объем). Осуществляется перемешивание до однородной массы. После чего порционно загружается пигмент, порция зависит от плотности пигмента – легкий пигмент смачивается сложнее, синий и зеленый пигменты ~ 5% до полного смачивания в жидкости, желтый - по ~ 10%. Перемешивается до полного его смачивания на средних оборотах диссольвера. 1. Preparation of a mixture of dispersing resin, pigments and additives. The first step is to load the entire volume of resin into the bowl); immediately after loading the resin, a wetting agent-dispersant (the entire volume) is introduced. Mixing is carried out until a homogeneous mass. After which the pigment is loaded in portions, the portion depends on the density of the pigment - light pigment is more difficult to wet, blue and green pigments ~ 5% until completely wetted in the liquid, yellow - ~ 10% each. Stir until it is completely wetted at medium speed of the dissolver.
2. Приготовленный пигментный концентрат переходит в стадию диспергирования с помощью бисерной мельницы. Процесс диспергирования проводится с контролем температуры процесса не выше 35°С. Процесс диспергирования завершается при достижении степени перетира 7 мкм. Степень перетира измеряется с помощью лабораторного прибора - гриндометра. 2. The prepared pigment concentrate goes into the dispersion stage using a bead mill. The dispersion process is carried out with process temperature control not exceeding 35°C. The dispersion process is completed when the degree of grinding reaches 7 microns. The degree of grinding is measured using a laboratory device - a grindometer.
3. Осуществление контроля качества полученного продукта – измерение вязкости, плотности и цветовых характеристик. 3. Carrying out quality control of the resulting product - measuring viscosity, density and color characteristics.
Ниже приведены примеры осуществления заявленного изобретения. Below are examples of implementation of the claimed invention.
Пример 1. Example 1.
Паста зеленая, имеющая состав, масс.%: Green paste, having the composition, wt.%:
- кетональдегидная смола – 75,0 - ketonaldehyde resin – 75.0
- пигмент фталоцианиновый зеленый– 20,0 - phthalocyanine green pigment – 20.0
- смачиватель - диспергатор высокомолекулярный W&D ВС 2152 – 5,0. - wetting agent - high molecular weight dispersant W&D BC 2152 – 5.0.
Результаты совместимости указаны в таблице №1. Compatibility results are shown in Table No. 1.
Пример 2. Example 2.
Паста синяя, имеющая состав, масс.%: Blue paste, having the composition, wt.%:
- кетональдегидная смола – 80,0 - ketonaldehyde resin – 80.0
- пигмент фталоцианиновый синий – 15,0 - phthalocyanine blue pigment – 15.0
- смачиватель - диспергатор высокомолекулярный W&D ВС 2152 – 5,0. - wetting agent - high molecular weight dispersant W&D BC 2152 – 5.0.
Результаты совместимости указаны в таблице №1. Compatibility results are shown in Table No. 1.
Пример 3. Example 3.
Паста желтая, имеющая состав, масс.%: Yellow paste, having the composition, wt.%:
- кетональдегидная смола – 42,0 - ketonaldehyde resin – 42.0
- пигмент неорганический желтый с колор индексом PY 42 (S 920) – 50,0 - inorganic yellow pigment with color index PY 42 (S 920) – 50.0
- смачиватель - диспергатор высокомолекулярный - W&D ВС 163 – 8,0. - wetting agent - high molecular weight dispersant - W&D BC 163 – 8.0.
Результаты совместимости указаны в таблице №1. Compatibility results are shown in Table No. 1.
Заявленный состав имеет ряд преимуществ: не содержит растворителей в системе, имеет универсальные свойства по совместимости с различными типами связующих. Универсальность применения колеровочных паст, т. е. применение их с различными типами связующих ЛКМ, объясняется оригинальностью состава, которая достигнута с помощью изучения и применения добавок для смачивания диспергирования, созданных по технологии контролируемой полимеризации, что позволяет более широкий спектр их применения за счет узкого молекулярно-массового распределения, это обеспечивает более широкую совместимость, что доказано практически. The declared composition has a number of advantages: it does not contain solvents in the system, and has universal properties for compatibility with various types of binders. The versatility of the use of tinting pastes, i.e. their use with various types of paint and varnish binders, is explained by the originality of the composition, which was achieved through the study and use of additives for wetting dispersion, created using controlled polymerization technology, which allows a wider range of their use due to the narrow molecular -mass distribution, this ensures wider compatibility, which has been proven practically.
Важным аспектом для конечного потребителя является «универсальность» колеровочных паст, т.е. применение в различных типах связующих. Добиться совместимости колеровочной пасты и базы под колеровку достаточно сложный процесс, который требует множества вариантов проб, поэтому одной из задач стояло сделать такие колоранты, которые требуют минимальной адаптации применения их в базовых красках. Состав колорантов был подобран таким образом, чтобы свойства краски не подвергались значительным изменениям даже при максимальном количестве добавляемого колоранта. Термин «несовместимость» используется для обозначения различных типов проблем, например: ухудшение глянца, увеличение времени высыхания или потеря определенных свойств текучести краски. Совместимость в отношении окрашивания краски колорантом называется цветосоответствием. Это означает, что в противном случае, колорант не может развить свою полную цветосилу в краске. An important aspect for the end consumer is the “versatility” of tinting pastes, i.e. application in various types of binders. Achieving compatibility between the tinting paste and the base for tinting is a rather complex process that requires many sample options, so one of the tasks was to make colorants that require minimal adaptation of their use in base paints. The composition of the colorants was selected in such a way that the properties of the paint were not subject to significant changes even with the maximum amount of colorant added. The term "incompatibility" is used to describe different types of problems, such as decreased gloss, increased drying time, or loss of certain paint flow properties. Compatibility with respect to the coloration of paint by colorant is called color matching. This means that otherwise, the colorant cannot develop its full intensity in the paint.
Основным свойством изобретения является универсальное применение колеровочных паст, которое определяется с помощью rub-out теста с цветовым различием Δ E<1,0. Для проверки на совместимость брали 3% пасты с различными типами связующих, наносили спиральным аппликатором толщиной 300 мкм. Смесь наносится на контрастный картон для проведения rub-out теста - разница в цвете между стертой и нестертой краской. Допустимое значение цветового различия - Δ E≤1,0. The main property of the invention is the universal use of tinting pastes, which is determined using a rub-out test with a color difference Δ E<1.0. To check for compatibility, 3% paste with various types of binders was taken and applied with a spiral applicator with a thickness of 300 microns. The mixture is applied to contrasting cardboard to perform a rub-out test - the difference in color between erased and unerased paint. The permissible value of color difference is Δ E≤1.0.
Результаты теста паст, полученных согласно заявляемого изобретения и известных аналогов, представлены в таблице 1. The test results of pastes obtained according to the claimed invention and known analogues are presented in Table 1.
Claims (6)