RU2730341C1 - Rubber mixture for sealing layer of cargo solid metal cord tires - Google Patents
Rubber mixture for sealing layer of cargo solid metal cord tires Download PDFInfo
- Publication number
- RU2730341C1 RU2730341C1 RU2019113610A RU2019113610A RU2730341C1 RU 2730341 C1 RU2730341 C1 RU 2730341C1 RU 2019113610 A RU2019113610 A RU 2019113610A RU 2019113610 A RU2019113610 A RU 2019113610A RU 2730341 C1 RU2730341 C1 RU 2730341C1
- Authority
- RU
- Russia
- Prior art keywords
- rubber
- sealing layer
- solid metal
- metal cord
- cargo
- Prior art date
Abstract
Description
Изобретение относится к резиновой смеси для герметизирующего слоя шины на основе комбинации галогенированного хлорбутилкаучука и небольшой доли натурального каучука, которая может быть использована в шинной промышленности при разработке рецептуры резин для грузовых цельнометаллокордных шин (далее - ЦМК шин).The invention relates to a rubber compound for the sealing layer of a tire based on a combination of halogenated chlorobutyl rubber and a small proportion of natural rubber, which can be used in the tire industry when developing a rubber formulation for all-steel truck tires (hereinafter - SSC tires).
Известно техническое решение, являющееся прототипом к настоящему изобретению и раскрытое в патенте SU №1707025, опубл. от 23.01.1992 г., относящиеся к резиновым смесям для герметизирующего слоя на основе комбинации хлорбутилкаучука и бутилкаучука. Резиновая смесь по данному решению (раскрытая во 2 варианте примеров исполнения решения), содержит хлорбутилкаучук при следующем соотношении компонентов в массовых частях на 100 массовых частей полимеров:Known technical solution, which is a prototype to the present invention and disclosed in the patent SU No. 1707025, publ. from 23.01.1992, relating to rubber compounds for a sealing layer based on a combination of chlorobutyl rubber and butyl rubber. The rubber mixture according to this solution (disclosed in the 2nd version of the examples of the solution execution) contains chlorobutyl rubber with the following ratio of components in mass parts per 100 mass parts of polymers:
Но резиновые смеси на основе комбинации хлорбутилкаучука и бутилкаучука и резиновая смесь прототипа обладают рядом недостатков: по технологическим свойствам при сборке шин на сборочном станке отмечены низкие технологические свойства резиновой смеси при формовании на станке, наблюдался разрыв резиновой смеси гермослоя по стыкам в 3-х местах, так как известная резиновая смесь не обеспечивает достаточную эластичность, сопротивление раздиру, конфекционные свойства, и наблюдаются низкие технические свойства.But rubber compounds based on a combination of chlorobutyl rubber and butyl rubber and a rubber compound of the prototype have a number of disadvantages: in terms of technological properties when assembling tires on an assembly machine, low technological properties of the rubber compound when molded on a machine were noted, a rupture of the rubber compound of the hermetic layer at the joints in 3 places was observed, since the known rubber compound does not provide sufficient elasticity, tear resistance, confection properties, and poor technical properties are observed.
Техническим результатом настоящего изобретения является разработка рецептуры резиновой смеси для герметизирующего слоя грузовых цельнометаллокордных шин, обеспечивающей газопроницаемость, повышенную эластичность, сопротивление раздиру, конфекционные свойства, улучшенные технические свойства невулканизованных смесей и вулканизатов по сравнению с известными резиновыми смесями для герметизирующего слоя грузовых цельнометаллокордных шин.The technical result of the present invention is the development of a rubber compound for the sealing layer of all-steel truck tires, providing gas permeability, increased elasticity, tear resistance, confection properties, improved technical properties of uncured mixtures and vulcanizates in comparison with known rubber compounds for the sealing layer of all-steel truck tires.
Для достижения технического результата проведены исследовательские работы, подобрана усовершенствованная рецептура резиновой смеси, опытным путем установлено содержание ингредиентов, а именно резиновая смесь для герметизирующего слоя грузовых цельнометаллокордных шин по настоящему изобретению содержит хлорбутилкаучук, натуральный каучук, наполнители в виде комбинации технического углерода полуактивной марки N660 и природного светлого наполнителя, пластификаторы, вулканизующий агент в виде нерастворимой серы, ускоритель вулканизации в виде бензотиазол-2-третбутилсульфенамида, активаторы, противостарители, при следующем соотношении компонентов в массовых частях на 100 массовых частей полимеров:To achieve the technical result, research work was carried out, an improved formulation of the rubber mixture was selected, the content of ingredients was experimentally established, namely, the rubber mixture for the sealing layer of all-steel truck tires according to the present invention contains chlorobutyl rubber, natural rubber, fillers in the form of a combination of carbon black of semi-active grade N660 and natural light filler, plasticizers, vulcanizing agent in the form of insoluble sulfur, vulcanization accelerator in the form of benzothiazole-2-tert-butylsulfenamide, activators, antioxidants, with the following ratio of components in mass parts per 100 mass parts of polymers:
Изготовлены опытные образцы резиновых смесей по настоящему изобретению и прототипа, проведены испытания свойств невулканизованных смесей и вулканизатов, сравнительные свойства резиновых смесей приведены в таблице 1.Prototypes of rubber compounds according to the present invention and prototype were made, the properties of uncured mixtures and vulcanizates were tested, comparative properties of rubber compounds are shown in Table 1.
Резиновая смесь по настоящему изобретению удовлетворительно прошла промышленные испытания. Отмечено, что подобранная резиновая смесь обеспечивает заявленные свойства, эластична, наблюдается высокое сопротивление раздиру, при сборке шин смесь не рвется и сохраняет газонепроницаемость.The rubber composition of the present invention has passed industrial tests satisfactorily. It is noted that the selected rubber compound provides the declared properties, is elastic, high tear resistance is observed, during tire assembly, the compound does not break and remains gas-tight.
Это достигнуто частичным введением в состав резиновой смеси натурального каучука, что позволяет сохранить эластичность, повысить сопротивление раздиру. А хлорбутилкаучук марки ХБК-139 сохраняет сопротивление газопроницаемости.This is achieved by the partial introduction of natural rubber into the rubber compound, which allows you to maintain elasticity and increase tear resistance. Chlorobutyl rubber of the KhBK-139 brand retains its resistance to gas permeability.
Замена технического углерода марки П-514 на комбинацию технического углерода марки N660 и природного светлого наполнителя, а также увеличение дозировки технического углерода марки N660 позволяет стабилизировать технические свойства резиновой смеси.Replacement of P-514 grade carbon black with a combination of N660 grade carbon black and natural light filler, as well as increasing the N660 grade carbon black dosage allow stabilizing the technical properties of the rubber compound.
Замена ускорителя N-циклогексил-2-бензотиазилсульфенамида на ускоритель замедленного действия бензотиазол-2-третбутилсульфенамид дает равномерное распределение скорости вулканизации.Replacing the N-cyclohexyl-2-benzothiazylsulfenamide accelerator with the delayed-action benzothiazole-2-tert-butylsulfenamide accelerator gives a uniform distribution of the vulcanization rate.
Замена растворимой серы на нерастворимую серу показывает основное преимущество, это сохранение конфекционной клейкости невулканизованных заготовок за счет исключения выцветания серы при хранении резиновых смесей и полуфабрикатов.Replacing soluble sulfur with insoluble sulfur shows the main advantage, this is the preservation of the confection stickiness of unvulcanized blanks due to the elimination of sulfur fading during storage of rubber mixtures and semi-finished products.
Резиновая смесь по настоящему изобретению может быть изготовлена на стандартном оборудовании шинной промышленности с применением стандартных технологий.The rubber composition of the present invention can be manufactured on standard equipment in the tire industry using standard technologies.
Результаты проведенных испытаний резиновых смесей по настоящему изобретению и прототипа подтверждают достижение разработанной резиновой смеси заявленного технического результата, а именно необходимой газопроницаемости, повышенной эластичности, сопротивления раздиру, конфекционных свойств, улучшенных технических свойств невулканизованных смесей и вулканизатов, удовлетворяет технологическим требованиям при сборке шин по сравнению с известными и ранее применяемыми резиновыми смесями для герметизирующего слоя грузовых цельнометаллокордных шин.The results of the tests carried out on the rubber compounds according to the present invention and the prototype confirm the achievement of the developed rubber compound of the claimed technical result, namely, the necessary gas permeability, increased elasticity, tear resistance, confection properties, improved technical properties of uncured mixtures and vulcanizates, satisfies the technological requirements for tire assembly compared to known and previously used rubber compounds for the sealing layer of cargo all-steel cord tires.
Claims (2)