RU2694049C1 - High-penetrating oil composition - Google Patents
High-penetrating oil composition Download PDFInfo
- Publication number
- RU2694049C1 RU2694049C1 RU2018120337A RU2018120337A RU2694049C1 RU 2694049 C1 RU2694049 C1 RU 2694049C1 RU 2018120337 A RU2018120337 A RU 2018120337A RU 2018120337 A RU2018120337 A RU 2018120337A RU 2694049 C1 RU2694049 C1 RU 2694049C1
- Authority
- RU
- Russia
- Prior art keywords
- mass
- weight
- mixture
- composition
- oil
- Prior art date
Abstract
Description
Область техники, к которой относится изобретениеThe technical field to which the invention relates.
Настоящее изобретение относится к композициям, содержащим высокопроникающее масло. Композиции по изобретению могут применяться для чистки стволов оружия, а также для облегчения движения застарелых и заржавелых петель, шкивов, болтов, подшипников, других металлических деталей и механизмов, и растворения засохших масляных и жирных загрязнений. Композиция по настоящему изобретению характеризуется содержанием смеси органических растворителей – нефтяных дистиллятов, кислородсодержащих органических соединений (низкомолекулярных спиртов и кетонов), скипидара, антикоррозионных добавок и добавок, улучшающих проникающую способность.The present invention relates to compositions containing high-penetrating oil. The compositions according to the invention can be used to clean the barrel of a weapon, as well as to facilitate the movement of old and rusty hinges, pulleys, bolts, bearings, other metal parts and mechanisms, and to dissolve dried oily and greasy dirt. The composition of the present invention is characterized by the content of a mixture of organic solvents - petroleum distillates, oxygen-containing organic compounds (low molecular weight alcohols and ketones), turpentine, anti-corrosion additives and additives that improve penetration.
Уровень техникиThe level of technology
Из US 3623983 известно проникающее масло (композиция), в своем составе содержащее минеральное масло, растворитель из ряда легких дистиллятов нефти, смесь углеводородного сульфоната металла и алифатической карбоновой кислоты, полученной окислением углеводородного воска, эфиры фосфорной кислоты и углеводородного спирта, содержащего не менее 12 атомов углерода в молекуле. Действие этого проникающего масла основано на частичном растворении окислов железа и проникновении в образующееся пространство для облегчения движения приржавевших деталей. Однако, композиция, известная из US 3623983 обладает низкой способностью очистки отложений меди и других металлов в стволах огнестрельного оружия, так как она не обладает достаточной проникающей способностью под эти отложения и не способна их растворить.From US 3623983 known penetrating oil (composition), in its composition containing mineral oil, a solvent from a number of light distillates of oil, a mixture of hydrocarbon metal sulfonate and aliphatic carboxylic acid, obtained by oxidation of hydrocarbon wax, ethers of phosphoric acid and hydrocarbon alcohol containing at least 12 atoms carbon in the molecule. The effect of this penetrating oil is based on the partial dissolution of iron oxides and penetration into the resulting space to facilitate the movement of rusted parts. However, the composition known from US 3,623,983 has a low ability to clean deposits of copper and other metals in the trunks of a firearm, as it does not have sufficient penetrating power under these deposits and is not able to dissolve them.
Из US 1895374 известно проникающее масло (композиция), в своем составе содержащее легкие нефтяные дистилляты низкой вязкости, насыщенные карбоновые кислоты, содержащие от 4 до 12 атомов углерода в молекуле. Композиция может применяться для ослабления усилия движения приржавевших болтов, шпилек и других деталей. Однако, в композиции отсутствуют кислородсодержащие органические растворители (спирты и кетоны), которые снижают вязкость композиции и придают лучшие проникающие свойства, ввиду чего данная композиция обладает большей вязкостью и меньшей проникающей способностьюFrom US 1895374 known penetrating oil (composition), in its composition containing light oil distillates of low viscosity, saturated carboxylic acids containing from 4 to 12 carbon atoms in the molecule. The composition can be used to reduce the movement force of rusted bolts, studs and other parts. However, in the composition there are no oxygen-containing organic solvents (alcohols and ketones), which reduce the viscosity of the composition and impart better penetrating properties, which means that this composition has a higher viscosity and less penetration.
В US 20060194701 раскрывается оружейное масло (композиция), содержащее в своем составе 2-15%масс. изопропанола, до 60%масс. гептана или другого нефтяного дистиллята, 3-20%масс. регуляторов вязкости, антиоксидантов и восстанавливающих агентов. Композиция может применяться для смазывания различных механизмов оружия, но не обладает проникающим эффектом для эффективной чистки различных отложений (нагар, омеднение, освинцовка и др.).In US 20060194701 disclosed gun oil (composition), containing in its composition 2-15% of the mass. isopropanol, up to 60% of the mass. heptane or other petroleum distillate, 3-20% of the mass. viscosity regulators, antioxidants and reducing agents. The composition can be used to lubricate various mechanisms of weapons, but does not have a penetrating effect for the effective cleaning of various sediments (carbon, copper-plating, leaded, etc.).
В RU 2132365 раскрывается защитный смазочный материал, содержащий церезин, синтетическую смолу на основе фенола и органический растворитель, отличающийся тем, что он дополнительно содержит экстракт нефтяной, полиэтилен высокого давления и может содержать петролатум. Раскрытое изобретения содержит в своем составе полиэтилен высокого давления, следы которого могут остаться в стволе после чистки огнестрельного оружия и негативно повлиять на качество дальнейшей стрельбы. RU 2132365 discloses a protective lubricant containing ceresin, a phenol-based synthetic resin and an organic solvent, characterized in that it additionally contains an extract of petroleum, high-pressure polyethylene and may contain petrolatum. The disclosed invention contains in its composition high-pressure polyethylene, traces of which may remain in the barrel after cleaning a firearm and adversely affect the quality of further firing.
Кроме того, известны коммерческие проникающие масла Kano Kroil и WD-40. Однако указанные составы обладают большим значением поверхностного натяжения и меньшей проникающей способностью .In addition, the commercial penetrating oils Kano Kroil and WD-40 are known. However, these compositions have a large surface tension and less penetrating power.
В то же время композиция по настоящему изобретению за счет низкого поверхностного натяжения проникает в мельчайшие (размером в миллионные доли сантиметра) щели и трещины, и отшелушиват отложения, образующиеся в стволах огнестрельного оружия – медь, свинец, томпак, нагар и т.д.At the same time, the composition of the present invention penetrates into the smallest (millionths of a centimeter in size) gaps and cracks due to the low surface tension and peels deposits formed in the trunks of a firearm - copper, lead, tompac, carbon deposits, etc.
Краткое описание чертежейBrief Description of the Drawings
На Фиг. 1 представлены результаты очистки внутренней поверхности стволов с помощью известных композиций и композиций по изобретению.FIG. 1 shows the results of cleaning the inner surface of the trunks using known compositions and compositions according to the invention.
Раскрытие изобретенияDISCLOSURE OF INVENTION
Заявленная в настоящем изобретении композиция проникающего масла может включать следующие компоненты: The penetrating oil composition claimed in the present invention may include the following components:
- минеральные гидроочищенные (CAS №№: 64741-89-5, 64742-55-8, 64742-54-7, 64742-53-6, 64742-52-5, 72623-87-1, 72623-86-0) или депарафинированные масла (CAS №№: 64742-56-9, 64742-70-7, 64742-71-8, 64742-65-0) или их смесь (0-50% по массе);- mineral hydrotreated (CAS №№: 64741-89-5, 64742-55-8, 64742-54-7, 64742-53-6, 64742-52-5, 72623-87-1, 72623-86-0) or dewaxed oils (CAS №№: 64742-56-9, 64742-70-7, 64742-71-8, 64742-65-0) or their mixture (0-50% by weight);
- средние нефтяные дистилляты, в частности авиационный, технический или осветительный керосины, а также уайт-спирит или их смеси (0-50% по массе);- medium oil distillates, in particular, aviation, technical or lighting kerosene, as well as white spirit or mixtures thereof (0-50% by weight);
- насыщенные спирты нормального и разветвленного строения, содержащие в структуре молекулы от 2 до 10, в частности от 2 до 9, от 2 до 8, от 2 до 7, от 2 до 6 или от 2 до 5 атомов углерода (0-50% по массе);- saturated alcohols of normal and branched structure, containing in the structure of the molecule from 2 to 10, in particular from 2 to 9, from 2 to 8, from 2 to 7, from 2 to 6 or from 2 to 5 carbon atoms (0-50% by weight);
- кетоны, содержащие в структуре молекулы от 3 до 10, в частности от 3 до 9, от 3 до 8, от 3 до 7 или от 3 до 6 атомов углерода (0-50% по массе);- ketones containing from 3 to 10 in the structure of the molecule, in particular from 3 to 9, from 3 to 8, from 3 to 7 or from 3 to 6 carbon atoms (0-50% by weight);
- смесь терпеновых углеводородов, в частности живичный, экстракционный или сульфатный скипидары и т.п. (0-50% по массе);- a mixture of terpene hydrocarbons, in particular gum, extraction or sulphate turpentine, etc. (0-50% by weight);
- антикоррозионные добавки, в частности фенольные, аминные, серосодержащие или другие (0-5% по массе);- anti-corrosion additives, in particular phenolic, amine, sulfur-containing or other (0-5% by weight);
- добавки, улучшающие проникающую способность композиции (0,1-5% по массе). В качестве таких добавок могут выступать: полидиметилсилоксаны с концевыми гидроксильными группами (кинематическая вязкость до 200 сСт), галогенсодержащие органические вещества ClFmCln, где l = 2-6, (m+n) = (2l+2).- additives that improve the penetrating ability of the composition (0.1-5% by weight). As such additives can be: polydimethylsiloxanes with terminal hydroxyl groups (kinematic viscosity up to 200 cSt), halogen-containing organic substances C l F m Cl n , where l = 2-6, (m + n) = (2 l + 2).
Композиция по настоящему изобретению может содержать минеральные гидроочищенные или депарафинированные масла или их смесь. Указанные масла, в частности включают CAS №№: 64741-89-5, 64742-55-8, 64742-54-7, 64742-53-6, 64742-52-5, 72623-87-1, 72623-86-0, CAS №№: 64742-56-9, 64742-70-7, 64742-71-8, 64742-65-0. Содержание указанных масел в композиции составляет приблизительно от 0 до 50 % масс, в частности приблизительно 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49 или 50% масс. или любой диапазон в пределах указанных значений. Наиболее предпочтительное количество составляет 5-45% масс., еще более предпочтительное количество составляет 15-35% масс., в частности 25%. Указанные гидроочищенные и депарафинизированные масла могут быть смешаны в любом соотношении, в частности от 1:10 до 10:1 соответственно, наиболее предпочтительно – в равных долях.The composition of the present invention may contain mineral hydrotreated or dewaxed oils or a mixture thereof. These oils, in particular, include CAS №№: 64741-89-5, 64742-55-8, 64742-54-7, 64742-53-6, 64742-52-5, 72623-87-1, 72623-86- 0, CAS №№: 64742-56-9, 64742-70-7, 64742-71-8, 64742-65-0. The content of these oils in the composition is from about 0 to 50% by weight, in particular about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17 , 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42 , 43, 44, 45, 46, 47, 48, 49 or 50% of the mass. or any range within the specified values. The most preferred amount is 5-45% by weight, an even more preferred amount is 15-35% by weight, in particular 25%. Said hydrotreated and dewaxed oils can be mixed in any ratio, in particular from 1:10 to 10: 1, respectively, and most preferably in equal proportions.
Композиция по настоящему изобретению может содержать средние нефтяные дистилляты. Указанные нефтяные дистилляты, в частности включают авиационный, технический или осветительный керосины, а также уайт-спирит или их смеси. Содержание указанных нефтяных дистиллятов в композиции составляет приблизительно от 0 до 50 % масс, в частности приблизительно 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49 или 50% масс. или любой диапазон в пределах указанных значений. Предпочтительным является количество от 5 до 45 % масс., в частности от 20 масс. % до 30 масс. %.The composition of the present invention may contain middle oil distillates. These petroleum distillates, in particular, include aviation, technical or lighting kerosene, as well as white spirit or mixtures thereof. The content of these petroleum distillates in the composition is from about 0 to 50% by weight, in particular about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49 or 50% of the mass. or any range within the specified values. Preferred is an amount of from 5 to 45 wt.%, In particular from 20 mass. % up to 30 wt. %
Композиция по настоящему изобретению может содержать насыщенные спирты нормального и разветвленного строения. В частности, указанные спирты содержат в структуре молекулы от 2 до 10, в частности от 2 до 9, от 2 до 8, от 2 до 7, от 2 до 6 или от 2 до 5 атомов углерода, т.е. 2, 3, 4, 5, 6, 7, 8, 9 или 10 атомов углерода. Примерами таких спиртов являются этанол, пропанол, изопропанол, н-бутанол, 2-бутанол (втор-бутанол), 2-метил-1-пропанол (изобутанол), 2-метил-2-пропанол (трет-бутанол), пентанол и т.д. Содержание указанных спиртов в композиции составляет приблизительно от 0 до 50 % масс, в частности приблизительно 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49 или 50% масс. или любой диапазон в пределах указанных значений.The composition of the present invention may contain saturated alcohols of normal and branched structure. In particular, these alcohols contain from 2 to 10 in the structure of the molecule, in particular from 2 to 9, from 2 to 8, from 2 to 7, from 2 to 6 or from 2 to 5 carbon atoms, i.e. 2, 3, 4, 5, 6, 7, 8, 9, or 10 carbon atoms. Examples of such alcohols are ethanol, propanol, isopropanol, n-butanol, 2-butanol (sec-butanol), 2-methyl-1-propanol (isobutanol), 2-methyl-2-propanol (tert-butanol), pentanol and t .d The content of these alcohols in the composition is from about 0 to 50% by weight, in particular about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17 , 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42 , 43, 44, 45, 46, 47, 48, 49 or 50% of the mass. or any range within the specified values.
Композиция по настоящему изобретению может содержать кетоны. В частности, указанные кетоны содержат в структуре молекулы от 3 до 10, в частности от 3 до 9, от 3 до 8, от 3 до 7 или от 3 до 6 атомов углерода, т.е. 3, 4, 5, 6, 7, 8, 9 или 10 атомов углерода. Примерами таких кетонов являются метилэтилкетон, диметилкетон и т.п. Содержание указанных кетонов в композиции составляет приблизительно от 0 до 50 % масс, в частности приблизительно 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49 или 50% масс. или любой диапазон в пределах указанных значений.The composition of the present invention may contain ketones. In particular, these ketones contain from 3 to 10 in the structure of the molecule, in particular from 3 to 9, from 3 to 8, from 3 to 7, or from 3 to 6 carbon atoms, i.e. 3, 4, 5, 6, 7, 8, 9 or 10 carbon atoms. Examples of such ketones are methyl ethyl ketone, dimethyl ketone, and the like. The content of these ketones in the composition is from about 0 to 50% by weight, in particular about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17 , 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42 , 43, 44, 45, 46, 47, 48, 49 or 50% of the mass. or any range within the specified values.
Композиция по настоящему изобретению может содержать смесь терпеновых углеводородов. В частности, указанные терпеновые углеводороды включают живичный, экстракционный или сульфатный скипидары и т.п. Содержание указанных терпеновых углеводородов в композиции составляет приблизительно от 0 до 50 % масс, в частности приблизительно 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49 или 50% масс. или любой диапазон в пределах указанных значений.The composition of the present invention may contain a mixture of terpene hydrocarbons. In particular, said terpene hydrocarbons include gum, extraction or sulphate turpentine, and the like. The content of said terpenic hydrocarbons in the composition is from about 0 to 50% by weight, in particular about 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19, 20, 21, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33, 34, 35, 36, 37, 38, 39, 40, 41, 42, 43, 44, 45, 46, 47, 48, 49 or 50% of the mass. or any range within the specified values.
Композиция по настоящему изобретению может содержать антикорозионные добавки. В частности, указанные антикорозионные добавки включают фенольные, аминные, серосодержащие или другие антикорозионные добавки. Например, диалкилдитиофосфат цинка, бис(нонилфениламин), диалкилдитиофосфат цинка, модифицированный бором. Содержание указанных антикорозионных добавок в композиции составляет приблизительно от 0 до 5 % масс, в частности приблизительно 0,1, 0,2, 0,3, 0,4, 0,5, 0,6, 0,7, 0,8, 0,9, 1, 1,1, 1,2, 1,3, 1,4, 1,5, 1,6, 1,7, 1,8, 1,9, 2, 2,1, 2,2, 2,3, 2,4, 2,5, 2,6, 2,7, 2,8, 2,9, 3, 3,1, 3,2, 3,3, 3,4, 3,5, 3,6, 3,7, 3,8, 3,9, 4, 4,1, 4,2, 4,3, 4,4, 4,5, 4,6, 4,7, 4,8, 4,9 или 5 % масс или любой диапазон в пределах указанных значений. The composition of the present invention may contain anti-corrosion additives. In particular, said anti-corrosion additives include phenolic, amine, sulfur-containing or other anti-corrosion additives. For example, dialkyldithiophosphate zinc, bis (nonylphenylamine), dialkyldithiophosphate zinc, modified with boron. The content of these anti-corrosion additives in the composition is from about 0 to 5% by weight, in particular about 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1, 1.1, 1.2, 1.3, 1.4, 1.5, 1.6, 1.7, 1.8, 1.9, 2, 2.1, 2, 2, 2.3, 2.4, 2.5, 2.6, 2.7, 2.8, 2.9, 3, 3.1, 3.2, 3.3, 3.4, 3, 5, 3.6, 3.7, 3.8, 3.9, 4, 4.1, 4.2, 4.3, 4.4, 4.5, 4.6, 4.7, 4, 8, 4.9 or 5% of the mass or any range within the specified values.
Композиция по настоящему изобретению может содержать добавки улучшающие проникающую способность композиции. В частности, указанные добавки включают полидиметилсилоксаны с концевыми гидроксильными группами (кинематическая вязкость до 200 сСт), галогенсодержащие органические вещества ClFmCln, где l = 2-6, (m+n) = (2l+2), например, 1,2,2-трифтортрихлорэтан.The composition of the present invention may contain penetration enhancing additives of the composition. In particular, these additives include hydroxyl-terminated polydimethylsiloxanes (kinematic viscosity up to 200 cSt), halogen-containing organic substances C l F m Cl n , where l = 2-6, (m + n) = (2l + 2), for example, 1,2,2-trifluorotrichloroethane.
Осуществление изобретенияThe implementation of the invention
Далее приводятся конкретные примеры осуществления настоящего изобретения. Указанные примеры служат исключительно в иллюстративных целях и не предназначены для ограничения объема настоящего изобретения.The following are specific embodiments of the present invention. These examples are for illustrative purposes only and are not intended to limit the scope of the present invention.
Пример 1. Композиция следующего состава: Example 1. A composition of the following composition:
- смесь гидроочищенного (CAS № 64742-55-8) и депарафинированного (CAS № 64742-65-0) масел в равной пропорции – 25%масс., - a mixture of hydrotreated (CAS No. 64742-55-8) and dewaxed (CAS No. 64742-65-0) oils in an equal proportion - 25% by weight,
- авиационный керосин ТС-1 – 30%масс., - aviation kerosene TS-1 - 30% of the mass.,
- изопропанол – 4%масс., - isopropanol - 4% of the mass.,
- метилэтилкетон – 20%масс., - methyl ethyl ketone - 20% of the mass.,
- живичный скипидар – 20%масс., - gum turpentine - 20% of the mass.,
- диалкилдитиофосфат цинка – 1%масс.- dialkyldithiophosphate zinc - 1% of the mass.
Пример 2. Композиция следующего состава: Example 2. The composition of the following composition:
- смесь гидроочищенного (CAS № 64742-54-7) и депарафинированного (CAS № 64742-71-8) масел в равной пропорции – 25%масс., - a mixture of hydrotreated (CAS No. 64742-54-7) and dewaxed (CAS No. 64742-71-8) oils in an equal proportion - 25% by weight,
- авиационный керосин ТС-1 – 20%масс., - aviation kerosene TS-1 - 20% of the mass.,
- уайт-спирит – 14%масс.,- white spirit - 14% of the mass.,
- диметилкетон – 20%масс., - dimethyl ketone - 20% of the mass.,
- живичный скипидар – 20%масс., - gum turpentine - 20% of the mass.,
- бис(нонилфениламин) – 1%масс.- bis (nonylphenylamine) - 1% of the mass.
Пример 3. Композиция следующего состава: Example 3. The composition of the following composition:
- смесь гидроочищенного (CAS № 64742-52-5) и депарафинированного (CAS № 64742-65-0) масел в равной пропорции – 25%масс., - a mixture of hydrotreated (CAS No. 64742-52-5) and dewaxed (CAS No. 64742-65-0) oils in an equal proportion - 25% by weight,
- осветительный керосин КО – 20%масс., - lighting kerosene KO - 20% by weight,
- уайт-спирит – 14%масс.,- white spirit - 14% of the mass.,
- диметилкетон – 20%масс., - dimethyl ketone - 20% of the mass.,
- живичный скипидар – 15%масс., - gum turpentine - 15% of the mass.,
- диалкилдитиофосфат цинка, модифицированный бором – 1%масс.,- dialkyl dithiophosphate zinc, modified with boron - 1% by weight,
- 1,2,2-трифтортрихлорэтан – 5%масс.- 1,2,2-trifluorotrichloroethane - 5% of the mass.
Пример 4. Оценка проникающей способности композиций.Example 4. Evaluation of the penetrating power of the compositions.
Проникающая способность предложенных составов, по сравнению с аналогами – Kano Kroil и WD-40, исследовалась по значению поверхностного натяжения (σ) – уменьшение которого свидетельствует о лучшей проникающей способности.The penetrating ability of the proposed formulations, compared with analogues - Kano Kroil and WD-40, was investigated by the value of surface tension (σ) - a decrease which indicates the best penetrating ability.
Были получены следующие значения для исследуемых композиций:The following values were obtained for the studied compositions:
Таблица 1Table 1
Пример 5. Оценка чистящей способности композиций.Example 5. Evaluation of the cleaning ability of the compositions.
Для сравнения чистящей способности композиций проникающих масел провели чистку стволов карабина Сайга-9. Количество выстрелов перед чисткой каждого из карабинов равно 200. Сравнивали количество патчей, которое требуется для достижения одинаковой степени чистоты при однократном прохождении патча через ствол. Считали, что ствол становится чистым при выходе из ствола патча с незначительными следами грязи при том, что чистота крайнего патча одинакова для всех образцов. Меньшее количество патчей свидетельствует о более быстром достижении чистоты ствола оружия. Результаты сравнения приведены в таблице 2.To compare the cleaning ability of penetrating oil compositions, they cleaned Saiga-9 carbine barrels. The number of shots before cleaning each of the carbines is 200. They compared the number of patches that are required to achieve the same degree of purity with a single pass of the patch through the barrel. It was believed that the barrel becomes clean when exiting the stem of the patch with slight traces of dirt, while the purity of the outermost patch is the same for all samples. Fewer patches indicate a faster achievement of the purity of the barrel. The results of the comparison are shown in table 2.
Таблица 2table 2
Пример 6. Оценка эффективности композиций.Example 6. Evaluation of the effectiveness of the compositions.
Эффективность чистки сравнивали следующим образом: после предыдущей чистки смочили патч маслом Kano Kroil и пятью возвратно-поступательными движениями на всю длину прочистили внутреннюю поверхность каждого ствола. Результаты представлены на Фиг. 1. Как видно в процессе первоначальной чистки предлагаемые композиции более эффективно удалили загрязнения.The cleaning efficiency was compared as follows: after the previous cleaning, they moistened the patch with Kano Kroil oil and cleaned the inner surface of each barrel with five reciprocating movements for the entire length. The results are presented in FIG. 1. As seen in the initial cleaning process, the proposed compositions more effectively remove contaminants.
Claims (39)