RU2597603C1 - Pyrotechnic composition of screening smoke - Google Patents
Pyrotechnic composition of screening smoke Download PDFInfo
- Publication number
- RU2597603C1 RU2597603C1 RU2015112748/05A RU2015112748A RU2597603C1 RU 2597603 C1 RU2597603 C1 RU 2597603C1 RU 2015112748/05 A RU2015112748/05 A RU 2015112748/05A RU 2015112748 A RU2015112748 A RU 2015112748A RU 2597603 C1 RU2597603 C1 RU 2597603C1
- Authority
- RU
- Russia
- Prior art keywords
- smoke
- composition
- pyrotechnic
- pyrotechnic composition
- masking
- Prior art date
Abstract
Description
Изобретение относится к области пиротехники, а более конкретно к составам для образования при горении дымовых маскирующих завес.The invention relates to the field of pyrotechnics, and more particularly to compositions for the formation of smoke masking during burning.
Уровень данной области техники характеризует металлохлоридный пиротехнический состав, описанный в патенте RU 2369589 С2, C06D 3/00; С06В 33/12, 2009 г., который включает гексахлорэтан, окись цинка, алюминиевый порошок и технологическую добавку - фторкаучук, при следующем соотношении компонентов (мас. %):The level of this technical field is characterized by the metal chloride pyrotechnic composition described in patent RU 2369589 C2, C06D 3/00; СВВ 33/12, 2009, which includes hexachloroethane, zinc oxide, aluminum powder and a technological additive - fluororubber, in the following ratio of components (wt.%):
Фторкаучук марки СКФ-32 в роли технологической добавки обеспечивает пригодность металлохлоридного состава для серийного производства, требуемую механическую прочность и физико-химическую стабильность дымообразующего заряда в условиях эксплуатации, обеспечив при этом низкую чувствительность к механическим воздействиям.SKF-32 grade fluororubber as a technological additive ensures the suitability of the metal chloride composition for mass production, the required mechanical strength and physico-chemical stability of the smoke-forming charge under operating conditions, while ensuring low sensitivity to mechanical stress.
Недостатком этого пиротехнического состава является неустойчивое (пульсирующее) горение из-за малого содержания металлического горючего - алюминиевого порошка и низкая скорость генерирования дыма, что снижает мобильность постановки маскирующей завесы при обнаружении средств нападения противника.The disadvantage of this pyrotechnic composition is unstable (pulsating) combustion due to the low content of metal fuel - aluminum powder and low smoke generation rate, which reduces the mobility of setting a masking curtain when detecting enemy attack means.
Отмеченные недостатки устранены в пиротехническом составе по патенту RU 23553606 С1, C06D 3/00; С06В 33/12, 2009 г., который по технической сущности и числу совпадающих признаков выбран в качестве наиболее близкого аналога предложенному составу.The noted disadvantages are eliminated in the pyrotechnic composition according to patent RU 23553606 C1, C06D 3/00; С06В 33/12, 2009, which, according to the technical nature and the number of matching features, was chosen as the closest analogue to the proposed composition.
Известный металлохлоридный дымообразующий состав включает гексахлорэтан, перхлорат калия, алюминиевый порошок и технологические добавки: хлорнаирит, пластифицированный дибутилсебацианатом и аэросил при следующем соотношении компонентов, мас. %:Known metal chloride smoke-forming composition includes hexachloroethane, potassium perchlorate, aluminum powder and processing aids: chlornairite, plasticized dibutyl sebacyanate and aerosil in the following ratio, wt. %:
Известный пиротехнический состав характеризуется повышенными технологическими свойствами в промышленной переработке, а также улучшенными показателями назначения - повышенной маскирующей способностью более контрастного белого дыма, который дополнительно отражает лазерное облучение на длине волны 1,06 мкм, на которой функционируют средства обнаружения и наведения противника.The well-known pyrotechnic composition is characterized by enhanced technological properties in industrial processing, as well as improved destination indicators - increased masking ability of more contrasting white smoke, which additionally reflects laser irradiation at a wavelength of 1.06 μm, at which the enemy’s detection and guidance tools function.
Формируемая при горении состава дымовая завеса понижает светопроницаемость за счет поглощения и рассеяния его аэрозольными частицами значительной части оптического излучения видимого спектра, чем обеспечивается маскировка техники и личного состава.The smoke screen formed during the combustion of the composition reduces light transmission due to the absorption and scattering of aerosol particles of a significant part of the optical radiation of the visible spectrum, which provides masking of equipment and personnel.
Повышенная масса алюминиевого порошка (металлического горючего) в совокупности с дополнительным активным окислителем - перхлоратом калия (дымообразователем) обеспечили высокие температуру и скорость горения металлохлоридного состава, при полном выгорании сажевых частиц, что способствует мобильному получению маскирующей завесы контрастного белого дыма.The increased mass of aluminum powder (metal fuel) in combination with an additional active oxidizing agent - potassium perchlorate (smoke generator) ensured high temperature and burning rate of the metal chloride composition, with the soot particles completely burning out, which contributes to the mobile production of a masking curtain of contrasting white smoke.
Хлорнаирит, пластифицированный дибутилсебацинатом, увеличивает плотность и прочность формируемых из пиротехнического состава зарядов, дополнительно выполняя функции окислителя и органического горючего в композиции.Chlornaairite, plasticized by dibutyl sebacinate, increases the density and strength of charges formed from the pyrotechnic composition, additionally performing the functions of an oxidizing agent and organic fuel in the composition.
Дибутилсебацинат при этом служит в качестве регулятора скорости горения смеси.Dibutyl sebacinate in this case serves as a regulator of the burning rate of the mixture.
Технологическая добавка - аэросил обеспечивает сыпучесть состава для автоматического дозирования смеси.Technological additive - Aerosil provides flowability of the composition for automatic dosing of the mixture.
Однако продолжением отмеченных достоинств являются присущие недостатки:However, a continuation of these advantages are inherent disadvantages:
- смесь компонентов при перемешивании пылит, что небезопасно, а при дозировании комкуется, не обеспечивая технологичности промышленному производству дымообразующих зарядов из пиротехнического состава;- a mixture of components when mixing dusts, which is unsafe, and when dosing crumbles, not ensuring the manufacturability of the industrial production of smoke-forming charges from a pyrotechnic composition;
- хлорнаирит в России не производится и является дефицитным импортным материалом, ограничивающим спецпроизводство, при этом для его введения в композицию требуется дополнительное пластифицирование дибутилсебацинатом, который снижает температуру горения состава и увеличивает вынос в маскирующее облако сажи;- chlornairite is not produced in Russia and is a scarce imported material that limits special production, and its introduction into the composition requires additional plasticization with dibutylsebacinate, which reduces the combustion temperature of the composition and increases the removal of soot into a masking cloud;
- при избытке пластификатора происходит недопустимая его экссудация на поверхность уплотняемого функционального заряда;- with an excess of plasticizer, its inadmissible exudation to the surface of the compacted functional charge occurs;
- несбалансированность содержания в известном составе перхлората калия приводит к пламенному горению, в результате чего падает насыщенность генерируемого дыма белым цветом, то есть снижается функциональность по назначению.- imbalance in the content in the known composition of potassium perchlorate leads to flame burning, resulting in a decrease in the saturation of the generated smoke in white, that is, the functionality decreases as intended.
Технической задачей, на решение которой направлено настоящее изобретение, является повышение функциональности дымообразующего металлохлоридного состава, технология приготовления которого пригодна для промышленного производства простым смешиванием компонентов.The technical problem to which the present invention is directed is to increase the functionality of a smoke-forming metal chloride composition, the preparation technology of which is suitable for industrial production by simple mixing of the components.
Требуемый технический результат достигается тем, что известный пиротехнический состав маскирующего дыма, включающий гексаэлорэтан, перхлорат калия, окись цинка, алюминиевый порошок, пластификатор и технологическую добавку, согласно изобретению, дополнительно содержит тиомочевину, а в качестве технологической добавки - графит пиротехнический и в качестве пластификатора - хлорпарафин жидкий ХП-470, при следующем соотношении компонентов, мас. %:The required technical result is achieved by the fact that the known pyrotechnic composition of masking smoke, including hexaloroethane, potassium perchlorate, zinc oxide, aluminum powder, a plasticizer and a technological additive, according to the invention, additionally contains thiourea, and pyrotechnic graphite as a technological additive, and as a plasticizer, liquid chloroparaffin HP-470, in the following ratio, wt. %:
Отличительные признаки предложенного технического решения обеспечили новое, дополнительное к оптической непрозрачности формируемой дымовой завесы (для электромагнитного излучения видимого диапазона частот) качество: поглощение и рассеяние электромагнитного излучения в диапазоне инфракрасных волн, что позволяет маскировать передвижение техники за счет создания экрана с фоновым уровнем теплового излучения от работающих двигателей.Distinctive features of the proposed technical solution provided a new, additional to the optical opacity of the formed smoke screen (for electromagnetic radiation of the visible frequency range) quality: absorption and scattering of electromagnetic radiation in the infrared wavelength range, which allows masking the movement of equipment by creating a screen with a background level of thermal radiation from working engines.
Оптимизация массового соотношения окислитель/металлическое горючее в количестве 1,2 против 0,8 по прототипу повысила полноту сгорания компонентов состава, при том, что достаточное количество алюминиевого порошка обеспечивает глубину взаимодействия окиси цинка с углеродом, снижая содержание сажи в генерируемых аэрозольных продуктах горения. В результате этого достигается контрастность дыма яркого белого цвета.Optimization of the mass ratio of oxidizer / metal fuel in an amount of 1.2 versus 0.8 according to the prototype increased the completeness of combustion of the components of the composition, while a sufficient amount of aluminum powder provides a depth of interaction of zinc oxide with carbon, reducing the soot content in the generated aerosol combustion products. As a result, a bright white smoke contrast is achieved.
Предложенный пиротехнический металлохлоридный состав характеризуется технологичностью в приготовлении простым смешиванием компонентов, так как в качестве пластификатора используется готовый промышленно выпускаемый продукт - жидкий хлорпарафин ХП-470, широко применяемый в пиротехническом производстве.The proposed pyrotechnic metal chloride composition is characterized by manufacturability in the preparation by simple mixing of the components, since a ready-made commercially available product is used as a plasticizer - liquid chlorine paraffin HP-470, which is widely used in pyrotechnic production.
Введение в пиротехнический состав серосодержащей тиомочевины, которая служит газообразователем для выноса генерируемого при горении аэрозоля и активатором горения состава, обеспечило формирование сульфидов в соединении с металлами (ZnS, AlS) - твердых частиц, которые частично поглощают инфракрасное излучение, а именно, от работающих двигателей техники, и хаотично отражают его во всех направлениях пространства. Таким образом, дисперсная фаза аэрозоля функционирует в качестве распределенных источников вторичного излучения, формируя фононный уровень инфракрасного излучения дымовой завесы, представляющей по существу защитный экран маскируемых объектов техники с работающими двигателями, концентрированно излучающими тепловую энергию.The introduction of sulfur-containing thiourea into the pyrotechnic composition, which serves as a gasifier for the removal of the aerosol generated during combustion and the combustion activator, ensured the formation of sulfides in combination with metals (ZnS, AlS) - solid particles that partially absorb infrared radiation, namely, from working engines , and randomly reflect it in all directions of space. Thus, the dispersed phase of the aerosol functions as distributed sources of secondary radiation, forming the phonon level of the infrared radiation of the smoke curtain, which is essentially a protective screen for masked objects of technology with working engines that concentrate emitting thermal energy.
Использование в качестве технологической добавки дымообразующего состава графита пиротехнического (марки «П»), взамен аэросила по прототипу, направлено на исключение пыления сухих компонентов при смешивании, которые при этом более равномерно распределяются в объеме, и обеспечение прессуемости состава в уплотненные заряды.The use of pyrotechnic graphite graphite (grade “P”) as a technological additive, instead of aerosil according to the prototype, is aimed at eliminating dusting of dry components during mixing, which are more evenly distributed in volume, and ensuring the compressibility of the composition into sealed charges.
Особенностью приготовления предложенного пиротехнического состава является содержание комплекса технологических добавок: графита П и хлорпарафина жидкого ХП-470 в оптимизированном соотношении на границах диапазонов их содержания, соответственно: 1:2=0,5 и 2:3≈0,7.A feature of the preparation of the proposed pyrotechnic composition is the content of a complex of technological additives: graphite P and chlorine paraffin liquid ХП-470 in an optimized ratio at the boundaries of their content ranges, respectively: 1: 2 = 0.5 and 2: 3≈0.7.
При введении в пиротехническую смесь графита П и хлорпарафина жидкого ХП-470 в массовом соотношении меньше 0,5 не исключается пыление, а уплотненные заряды характеризуются неудовлетворительной пластичностью и могут крошиться.When graphite P and chloroparaffin are introduced into the pyrotechnic mixture in a mass ratio of less than 0.5, dusting is not ruled out, and the compacted charges are characterized by poor ductility and may crumble.
При введении в пиротехническую смесь графита П и хлорпарафина жидкого ХП-470 в массовом соотношении больше 0,7 не отмечается улучшения технологических свойств состава: равномерности распределения компонентов, снижения пыления и улучшения прессуемости зарядов.When graphite P and chloroparaffin are introduced into the pyrotechnic mixture in liquid mass HP-470 in a mass ratio of more than 0.7, there is no improvement in the technological properties of the composition: uniform distribution of components, reduced dusting and improved compressibility of charges.
При введении в пиротехнический состав графита П меньше 1 мвс. % его сыпучесть неудовлетворительна для автоматического дозирования компонентов по изобретению, а его содержание больше 2 мас. % является балластным, так как не сопровождается заметным улучшением технологичности.When graphite P is introduced into the pyrotechnic composition, it is less than 1 msec. % its flowability is unsatisfactory for automatic dosing of the components according to the invention, and its content is more than 2 wt. % is ballast, as it is not accompanied by a noticeable improvement in manufacturability.
При введении в пиротехнический состав хлорпарафина жидкого ХП-470 меньше 2 мас. % возможно пыление на операции смешивания компонентов, что взрывоопасно для высокочувствительной смеси в производственном помещении.When introducing into the pyrotechnic composition of chloroparaffin liquid CP-470 less than 2 wt. % dusting is possible during component mixing operations, which is explosive for a highly sensitive mixture in a production room.
При содержании в пиротехническом составе хлорпарафина жидкого ХП-470 больше 3 мас. % происходит недопустимая его экссудация на поверхности формируемых зарядов при уплотнении состава.When the content in the pyrotechnic composition of chloroparaffin liquid CP-470 is more than 3 wt. % its unacceptable exudation occurs on the surface of the formed charges during compaction of the composition.
При содержании в дымообразующем пиротехническом составе гексахлорэтана больше 29 мас. % снижается количественное образование оксида алюминия, в результате чего падает контрастность белого цвета генерируемого при горении дыма, снижая маскирующую способность формируемой завесы.When the content in the smoke-forming pyrotechnic composition of hexachloroethane is more than 29 wt. % the quantitative formation of aluminum oxide is reduced, as a result of which the contrast of the white color of the smoke generated during combustion decreases, reducing the masking ability of the formed curtain.
При содержании в дымообразующем пиротехническом составе гексахлорэтана меньше 24 мас. % падает хлорирование цинка, что сильно снижает оптическую плотность маскирующей завесы.When the content in the smoke-forming pyrotechnic composition of hexachloroethane is less than 24 wt. % zinc chlorination decreases, which greatly reduces the optical density of the masking curtain.
При содержании в составе по изобретению перхлората калия меньше 16 мас. % скорость горения и генерирования дыма не удовлетворяет технические требования по постановке маскирующей завесы для оперативной передислокации техники.When the content in the composition according to the invention, potassium perchlorate is less than 16 wt. % The rate of burning and smoke generation does not satisfy the technical requirements for the installation of a masking curtain for the rapid relocation of equipment.
При содержании в дымообразующем пиротехническом составе перхлората калия больше 20 мас. % растет температура горения, сопровождающаяся пламеобразованием, которое приводит к резкому снижению маскирующей способности завесы.When the content in the smoke-forming pyrotechnic composition of potassium perchlorate is more than 20 wt. % the combustion temperature increases, accompanied by flame formation, which leads to a sharp decrease in the masking ability of the curtain.
При введении в дымообразующий пиротехнический состав алюминиевого порошка меньше 20 мас. % температура и скорость горения не обеспечивают заданной интенсивности постановки маскирующей завесы.When introduced into the smoke-forming pyrotechnic composition of aluminum powder is less than 20 wt. % the temperature and the burning rate do not provide the specified intensity for setting the masking curtain.
При введении в пиротехнический состав алюминиевого порошка больше 25 мас. % заметно повышается температура горения, при которой падает маскирующая способность дымовой завесы из-за выгорания структурных компонентов состава.When introduced into the pyrotechnic composition of aluminum powder more than 25 wt. % the combustion temperature rises markedly, at which the masking ability of the smoke screen decreases due to the burning out of the structural components of the composition.
При введении в пиротехнический состав окиси цинка меньше 20 мас. % в генерируемом аэрозоле образуется дефицит хлорида цинка, снижающий насыщенность дыма белым цветом, недостаточная контрастность которого ухудшает маскировку в оптическом диапазоне.When introduced into the pyrotechnic composition of zinc oxide is less than 20 wt. % in the generated aerosol, a deficiency of zinc chloride is formed, which reduces the saturation of smoke with white color, the lack of contrast of which worsens the masking in the optical range.
При введении в пиротехнический состав окиси цинка больше 30 мас. % происходит неполная его возгонка, то есть функциональность маскирующей завесы не улучшается.When introduced into the pyrotechnic composition of zinc oxide is more than 30 wt. % its incomplete sublimation occurs, that is, the functionality of the masking curtain does not improve.
Следовательно, каждый существенный признак необходим, а их совокупность является достаточной для достижения новизны качества, неприсущего признакам в разобщенности, то есть поставленная в полезной модели техническая задача решена не суммой эффектов, а новым сверхэффектом суммы признаков.Consequently, each essential feature is necessary, and their combination is sufficient to achieve the novelty of a quality that is not inherent in signs of disunity, that is, the technical problem posed in the utility model is not solved by the sum of the effects, but by a new super-effect of the sum of the attributes.
Количественное соотношение компонентов предложенного дымообразующего пиротехнического состава было рассчитано по математической модели планирования эксперимента и подтверждено результатами экспериментальной проверки функционирования опытных образцов зарядов по назначению, которые показали достижение улучшенных характеристик по максимальной маскирующей способности и оптической плотности аэродисперсного образования при горении состава, компоненты которого содержатся в пределах оптимизированных диапазонов.The quantitative ratio of the components of the proposed smoke-forming pyrotechnic composition was calculated according to the mathematical model of the experimental design and confirmed by the results of experimental verification of the functioning of the prototype charges for their intended purpose, which showed the achievement of improved characteristics for maximum masking ability and optical density of the aerodisperse formation during combustion of the composition, the components of which are contained within the optimized ranges.
Приготавливается предложенный дымообразующий металлохлоридный пиротехнический состав механическим смешиванием компонентов, которые вносятся в вышеуказанном оптимальном массовом соотношении, в лопастном смесителе, например, марки СНД-100, в следующем порядке, при загрузке компонентов мерными дозами (мас. %):The proposed smoke-forming metal chloride pyrotechnic composition is prepared by mechanical mixing of the components, which are introduced in the above optimal weight ratio, in a paddle mixer, for example, brand SND-100, in the following order, when loading the components in measured doses (wt.%):
- 18±2 алюминиевый порошок и 2,5±0,5 хлорпарафин жидкий ХП-470, которые перемешивают в течение 7-10 минут;- 18 ± 2 aluminum powder and 2.5 ± 0.5 chloroparaffin liquid KP-470, which are mixed for 7-10 minutes;
- затем в смеситель вводят остальные порошкообразные компоненты: 26,5±2,5 гексахлорэтан, 18±2 перхлорат калия, 25±5 окись цинка (цинковые белила), 4±1 тиомочевину, и 1,5±0,5 графит П, которые перемешивают в течение 10-15 минут до равномерного распределения компонентов в объеме.- then the remaining powder components are introduced into the mixer: 26.5 ± 2.5 hexachloroethane, 18 ± 2 potassium perchlorate, 25 ± 5 zinc oxide (zinc white), 4 ± 1 thiourea, and 1.5 ± 0.5 graphite P, which are mixed for 10-15 minutes until the components are evenly distributed in the volume.
Приготовленный пластифицированный пиротехнический состав направляют на прессование дымообразующих зарядов.The prepared plasticized pyrotechnic composition is directed to the compression of smoke-forming charges.
Ниже приведены характерные примеры из числа опытных составов, которые были испытаны при отработке и оптимизации различных количественных соотношений содержания структурных компонентов по настоящему изобретению.The following are typical examples from among the experimental compositions that were tested during testing and optimization of various quantitative ratios of the content of structural components of the present invention.
В Таблице приведены составы с содержанием компонентов внутри оптимизированных диапазонов содержания, на границах этих диапазонов и за их границами.The table shows the compositions with the content of the components within the optimized ranges of contents, at the boundaries of these ranges and beyond.
По технологичности, функциональным характеристикам, достигнутым в результате проведенных испытаний, физико-химическим показателям приготовленных составов и зарядов из них составы 2-4, компоненты которых содержатся в заявленных диапазонах массового соотношения, заметно превышают соответствующие показатели назначения известных аналогов:In terms of manufacturability, functional characteristics achieved as a result of the tests, physicochemical parameters of the prepared compositions and charges of them, compositions 2-4, the components of which are contained in the declared ranges of the mass ratio, significantly exceed the corresponding destination values of the known analogues:
- цвет дыма яркий, контрастно белый, при скорости горения зарядов 1,7-1,9 мм/с и дымообразующей способности 97-98%;- the color of the smoke is bright, contrasting white, with a burning speed of charges of 1.7-1.9 mm / s and smoke-generating ability of 97-98%;
- маскирующая способность 4,3-5,2 м2/г;- masking ability of 4.3-5.2 m 2 / g;
- содержание шлаков 2-3%, что полностью исключает фильтрацию;- slag content of 2-3%, which completely eliminates filtration;
- коэффициент рассеяния инфракрасного излучения - 0,8.- the scattering coefficient of infrared radiation is 0.8.
Состав №1 характеризуется низкой скоростью горения, неприемлемой для оперативной постановки маскирующей дымовой завесы.Composition No. 1 is characterized by a low burning rate, unacceptable for the operational setting of a masking smoke screen.
Горение зарядов из состава №5 происходило с образованием пламени, генерируемый дым имеет низкую контрастность, маскирующая завеса оптически прозрачна, при этом состав комкуется при смешивании компонентов и пылит, а уплотненные заряды крошатся из-за низкой пластичности.The combustion of charges from composition No. 5 occurred with the formation of a flame, the smoke generated has low contrast, the masking curtain is optically transparent, while the composition crumbles when mixing the components and dusts, and the compacted charges crumble due to low ductility.
Сравнение предложенного технического решения с ближайшими аналогами уровня техники не выявило идентичного совпадения совокупности существенных признаков изобретения.Comparison of the proposed technical solution with the closest prior art analogues did not reveal an identical match of the totality of the essential features of the invention.
Предложенные отличия состава маскирующего дыма, которые прямо не следуют из постановки технической задачи, не являются очевидными для специалиста по пиротехнике.The proposed differences in the composition of masking smoke, which do not directly follow from the statement of the technical problem, are not obvious to a specialist in pyrotechnics.
Изготовление предложенного пиротехнического дымообразующего состава возможно осуществлять в серийном производстве на действующем оборудовании.The manufacture of the proposed pyrotechnic smoke-generating composition can be carried out in serial production on existing equipment.
Из вышесказанного можно сделать вывод о соответствии изобретения условиям патентоспособности.From the foregoing, we can conclude that the invention meets the conditions of patentability.
Claims (1)