RU2136782C1 - Inhibitor "reacor-21" for corrosion protection of building steels in hydrogen sulfide-containing mineralized media - Google Patents
Inhibitor "reacor-21" for corrosion protection of building steels in hydrogen sulfide-containing mineralized media Download PDFInfo
- Publication number
- RU2136782C1 RU2136782C1 RU97107790A RU97107790A RU2136782C1 RU 2136782 C1 RU2136782 C1 RU 2136782C1 RU 97107790 A RU97107790 A RU 97107790A RU 97107790 A RU97107790 A RU 97107790A RU 2136782 C1 RU2136782 C1 RU 2136782C1
- Authority
- RU
- Russia
- Prior art keywords
- hydrogen sulfide
- inhibitor
- corrosion
- corrosion protection
- reacor
- Prior art date
Abstract
Description
Изобретение относится к защите металлов от сероводородной коррозии в сероводородсодержащих минерализованных средах. The invention relates to the protection of metals from hydrogen sulfide corrosion in hydrogen sulfide-containing mineralized environments.
Среди наиболее близких по назначению ингибиторов (аналог), защищенных в последнее время патентами РФ, известно, например, применение триалкилбензилметиламмония хлористого или фтористого, или йодистого, дополнительно содержащего октидециламин, хинолин или его производные в качестве ингибитора сероводородной коррозии и наводороживания стали [1]. Among the closest to the intended purpose inhibitors (analogue), recently protected by RF patents, it is known, for example, the use of trialkylbenzylmethylammonium chloride or fluoride, or iodide, additionally containing octidecylamine, quinoline or its derivatives as an inhibitor of hydrogen sulfide corrosion and hydrogenation of steel [1].
Недостатком аналога является его высокая стоимость и невысокая степень защиты при низком содержании сероводорода в минерализованной воде. The disadvantage of the analogue is its high cost and low degree of protection with a low content of hydrogen sulfide in mineralized water.
К заявляемому ингибитору близок по составу (прототип) ингибитор коррозии на основе эпоксидной смолы [2]. The claimed inhibitor is similar in composition (prototype) to a corrosion inhibitor based on epoxy resin [2].
Недостатком прототипа является:
1) Высокая стоимость ингибитора по сравнению с заявляемым.The disadvantage of the prototype is:
1) The high cost of the inhibitor compared with the claimed.
Целями данного изобретения являются:
1) разработка высокоэффективного ингибитора сероводородной коррозии строительных сталей при транспортировании обводненной нефти в системе нефтесбора и пластовых вод в системе поддержания пластового давления,
2) утилизация отходов производства алифатических спиртов (C8-C12),
3) снижение стоимости реагентов для интенсификации добычи нефти,
4) расширение ассортимента применяемых ингибиторов.The objectives of this invention are:
1) the development of a highly effective inhibitor of hydrogen sulfide corrosion of structural steels during the transportation of flooded oil in the oil gathering system and produced water in the reservoir pressure maintenance system,
2) disposal of waste from the production of aliphatic alcohols (C 8 -C 12 ),
3) reducing the cost of reagents for the intensification of oil production,
4) expanding the range of inhibitors used.
Поставленная цель достигается тем, что в качестве ингибитора сероводородной коррозии строительных сталей применяют 5-20%-ный раствор диеновой эпоксидной смолы в отходах производства алифатических спиртов (C8-C12).This goal is achieved in that a 5-20% solution of diene epoxy resin in waste from the production of aliphatic alcohols (C 8 -C 12 ) is used as an inhibitor of hydrogen sulfide corrosion of building steels.
Диеновая эпоксидная смола широко применяется для создания полимерных покрытий [3]. Отходы производства спиртов в настоящее время используются в качестве котельного топлива. Diene epoxy resin is widely used to create polymer coatings [3]. Alcohol production wastes are currently used as boiler fuel.
Использование указанного раствора в качестве ингибитора для защиты металлов от коррозии в литературе не описано. The use of this solution as an inhibitor for protecting metals from corrosion is not described in the literature.
Исследования по определению ингибирующей эффективности соединений проводили на образцах из стали 20, широко используемой в настоящее время при строительстве газонефтепроводов. Studies to determine the inhibitory effectiveness of compounds were carried out on samples of steel 20, which is currently widely used in the construction of gas and oil pipelines.
В качестве модельной коррозионной среды (КС) применяли модели сероводородсодержащих пластовых вод различных месторождений Республики Башкортостан, содержание сероводорода от 50 до 200 мг/л. As a model corrosion medium (CS), we used models of hydrogen sulfide-containing formation waters of various deposits of the Republic of Bashkortostan, the content of hydrogen sulfide from 50 to 200 mg / l.
Защитный эффект против сероводородной коррозии определяли в соответствии с [4]. The protective effect against hydrogen sulfide corrosion was determined in accordance with [4].
Эффективность защиты от общей коррозии (ОК) оценивали по поляризационным кривым следующим образом. The effectiveness of protection against general corrosion (OK) was evaluated by polarization curves as follows.
Экстраполировали тафелевы участки анодной и катодной поляризационных кривых до значения потенциала коррозии и получали величину тока коррозии в сероводородной КС. Сравнивая ход поляризационных кривых в ингибированной и неингибированной КС получаем значения токов коррозии в ингибированной (i) и неингибированной (i0) КС.The Tafel sections of the anodic and cathodic polarization curves were extrapolated to the value of the corrosion potential and the value of the corrosion current in the hydrogen sulfide CS was obtained. Comparing the course of the polarization curves in the inhibited and non-inhibited CS, we obtain the values of the corrosion currents in the inhibited (i) and non-inhibited (i 0 ) CS.
Степень защиты от ОК определяется по формуле [4], Z = (i0-i)/i0•100%.The degree of protection against OK is determined by the formula [4], Z = (i 0 -i) / i 0 • 100%.
Из таблицы видно, что предлагаемый ингибитор сероводородной коррозии строительных сталей 5-20%-ный раствор диеновой эпоксидной смолы обладает высокой степенью защиты от общей коррозии, в примененных коррозионных средах. Использование предлагаемого ингибитора позволит эффективно защищать внутреннюю поверхность оборудования нефтяных и газовых промыслов при добыче обводненной нефти, утилизировать отходы производства спиртов. The table shows that the proposed inhibitor of hydrogen sulfide corrosion of structural steels 5-20% solution of diene epoxy resin has a high degree of protection against general corrosion in corrosive environments. The use of the proposed inhibitor will effectively protect the inner surface of the equipment of oil and gas fields during the production of waterlogged oil, and utilize the waste from the production of alcohols.
Список использованных источников
1. Патент SU N 1719462 A1 от 15.03.93.List of sources used
1. Patent SU N 1719462 A1 dated 03/15/93.
2. Патент США N 3223626, кл. 252.25, 1965 г., 3 л. 2. US patent N 3223626, cl. 252.25, 1965, 3 l.
3. А.А.Герасименко. Защита от коррозии, старения и биоповреждений машин, оборудования и сооружений. Справочник в 2-х томах, М.: Машиностроение. 1987, - Т 1, - 869 с. 3. A.A. Gerasimenko. Protection against corrosion, aging and biodeterioration of machinery, equipment and structures. Handbook in 2 volumes, M .: Mechanical Engineering. 1987, - T 1, - 869 s.
4. РД 39-0147103-324-88 "Методика определения степени защиты сталей ингибиторами от коррозионно-механического разрушения в сероводородсодержащих минерализованных средах". Уфа: ВНИИСПТнефть, 1989. - 39 с. 4. RD 39-0147103-324-88 "Methodology for determining the degree of protection of steel by inhibitors from mechanical corrosion in hydrogen sulfide-containing mineralized environments." Ufa: VNIISPTneft, 1989 .-- 39 p.
Claims (1)
Диеновая эпоксидная смола - 5 - 20
Отходы производства алифатических спиртов фракций C8 - C12 - ОстальноеReakor-21 inhibitor for protection against corrosion of building steels in hydrogen sulfide mineralized environments based on epoxy resin, characterized in that it additionally contains waste from the production of aliphatic alcohols of fractions C 8 - C 12 , and as an epoxy resin - diene epoxy resin in the following the ratio of components, vol.%:
Diene Epoxy - 5 - 20
Wastes from the production of aliphatic alcohols fractions C 8 - C 12 - Else