RU2122376C1 - Method of manufacturing metalloceramic dental prostheses - Google Patents
Method of manufacturing metalloceramic dental prostheses Download PDFInfo
- Publication number
- RU2122376C1 RU2122376C1 RU97100346A RU97100346A RU2122376C1 RU 2122376 C1 RU2122376 C1 RU 2122376C1 RU 97100346 A RU97100346 A RU 97100346A RU 97100346 A RU97100346 A RU 97100346A RU 2122376 C1 RU2122376 C1 RU 2122376C1
- Authority
- RU
- Russia
- Prior art keywords
- prosthesis
- manufacturing
- ceramic coating
- metalloceramic
- dental prostheses
- Prior art date
Abstract
Description
Изобретение относится к медицине, а именно к ортопедической стоматологии при изготовлении металлокерамических зубных протезов. The invention relates to medicine, namely to orthopedic dentistry in the manufacture of cermet dentures.
Известен способ изготовления металлокерамических зубных протезов, включающий изготовление металлической основы-каркаса из сплава КХС, его шлифовку, очистку, нанесение керамического покрытия на торцовую и внутреннюю поверхности каркаса и спекание с последующим глазурованием протеза [1]. A known method of manufacturing a ceramic-metal dentures, including the manufacture of a metal base frame of the KHS alloy, grinding, cleaning, applying a ceramic coating to the end and inner surfaces of the frame and sintering followed by glazing of the prosthesis [1].
Недостатком известного способа является то, что он не обеспечивает высокого качества протеза. The disadvantage of this method is that it does not provide high quality prosthesis.
Наиболее близким техническим решением является способ изготовления металлокерамических зубных протезов, включающий отливку металлической основы, ее очистку, повторную термообработку в течение 10 - 15 минут при температуре 1110 - 1150oC, удаление образовавшейся окисной пленки, обезжиривание спиртом, высушивание заготовки изделия и последующего керамического покрытия [2] .The closest technical solution is a method of manufacturing a ceramic-metal dentures, including casting a metal base, cleaning it, repeated heat treatment for 10 - 15 minutes at a temperature of 1110 - 1150 o C, removing the formed oxide film, degreasing with alcohol, drying the workpiece and subsequent ceramic coating [2].
Недостатком известного способа является низкое качество протеза из-за непрочной химической связи сплава КХС с керамическим покрытием. The disadvantage of this method is the low quality of the prosthesis due to the fragile chemical bond of the KHS alloy with a ceramic coating.
Задачей изобретения является повышение качества протеза и обеспечение полной индеферентности его к тканям полости рта. The objective of the invention is to improve the quality of the prosthesis and ensure its complete inference to the tissues of the oral cavity.
Поставленная задача достигается путем отливки металлической основы из сплава никелида титана, удаления окисного слоя, последующего нанесения керамического покрытия и спекания протеза при температуре 850-870oC.The task is achieved by casting a metal base from an alloy of titanium nickelide, removing the oxide layer, then applying a ceramic coating and sintering the prosthesis at a temperature of 850-870 o C.
Никелид титана образует прочную химическую связь с керамическим покрытием вследствие взаимной диффузии ионов керамики и сплава, а также являясь сверхэластичным сплавом, снижает пластическую деформацию металлокерамическим протезам, что предотвращает их от образования микротрещин и сколов в керамическом покрытии. Titanium nickelide forms a strong chemical bond with the ceramic coating due to the mutual diffusion of ceramic and alloy ions, and as a superelastic alloy, it reduces plastic deformation of cermet prostheses, which prevents them from microcracks and chips in the ceramic coating.
Способ осуществляют следующим образом. The method is as follows.
На гипсовой модели челюстей моделируют восковую конструкцию металлического каркаса традиционным способом. Каркас из никелида титана отливают в вакуумной печи при температуре 1200-1250oC, затем кюветы охлаждают, извлекают изделие, очищают его в пескоструйном аппарате, обрабатывают и припасовывают на модели челюсти и в полости рта пациента в клинике. После примерки металлического каркаса - основы его обрабатывают раствором, состоящим из 1 части - плавиковой кислоты, 2 частей - серной кислоты, 6 частей - дистиллированной воды, затем промывают в дистиллированной воде, сушат и наносят керамическое покрытие. Протез спекают в печи при температуре 850-870oC. Температура спекания не должна превышать 880oC, так как более высокая температура приводит к деструктурированию сплава никелида титана и нарушению химической связи металл-керамика.On the plaster model of the jaws, the wax structure of the metal frame is modeled in the traditional way. The titanium nickelide framework is cast in a vacuum oven at a temperature of 1200-1250 o C, then the cuvettes are cooled, the product is removed, cleaned in a sandblasting apparatus, processed and fitted on the model of the jaw and in the patient's oral cavity in the clinic. After trying the metal frame - the base, it is treated with a solution consisting of 1 part - hydrofluoric acid, 2 parts - sulfuric acid, 6 parts - distilled water, then washed in distilled water, dried and coated with a ceramic coating. The prosthesis is sintered in an oven at a temperature of 850-870 o C. The sintering temperature should not exceed 880 o C, since a higher temperature leads to the destruction of the titanium nickelide alloy and the breaking of the metal-ceramic chemical bond.
Предлагаемый способ позволяет изготовить зубные протезы из полностью индиферентных материалов для полости рта и повысить качество протезов, исключив возможные сколы керамического покрытия от металлического каркаса. The proposed method allows the manufacture of dentures from completely indifferent materials for the oral cavity and to improve the quality of prostheses, eliminating possible chips of ceramic coating from a metal frame.
Claims (1)