RU2192539C1

RU2192539C1 - Expanding low-density plugging material

Info

Publication number: RU2192539C1
Application number: RU2001115563/03A
Authority: RU
Inventors: В.Н. Мартынов; Т.В. Кузнецова; Ю.Р. Кривобородов; В.И. Самсоненко; Н.В. Самсоненко
Original assignee: Закрытое акционерное общество НПАК "РАНКО"
Priority date: 2001-06-08
Filing date: 2001-06-08
Publication date: 2002-11-10

Abstract

FIELD: compositions of expanding plugging materials. SUBSTANCE: expanding low-density plugging material has the following ratio of components, mas. pts: portland cement, 100; expanding additive, 5-7; commercial lignosulfonates, 0.01-0.25; triethanolamine, 0.01-0.06; neutralized air-entraining resin, 0.005-0.1; gypsum, 0-6. Expanding plugging material may contain expanding additive in the form of at least one component from group including alumina cement, alumocalcium slag, calcium sulfoaluminates, calcium sulfoferrites. EFFECT: increased sedimentation stability, adhesive and bending strength. 2 cl, 2 tbl

Description

Настоящее изобретение относится к расширяющемуся тампонажному материалу пониженной плотности и может найти применение в нефтяной и газовой промышленности для крепления скважин. The present invention relates to expanding cementing material of low density and may find application in the oil and gas industry for fastening wells.

Известен расширяющийся облегченный тампонажный раствор для крепления скважин, содержащий портландцемент, расширяющуюся добавку - НРС-1, алюминиевую пудру, анионное поверхностно-активное вещество и воду (см. RU 2082872, Е 21 В 33/138, опубл. 27.06.1997). Known expanding lightweight cement slurry for fixing wells, containing Portland cement, an expanding additive - NRS-1, aluminum powder, anionic surfactant and water (see RU 2082872, E 21 B 33/138, publ. 06/27/1997).

Наиболее близким из аналогов является расширяющийся тампонажый материал пониженной плотности, содержащий портландцемент, дизельное топливо или газоконденсат, расширяющуюся добавку - алюмокальциевый шлак, буру, технические лигносульфонаты и воду (см. SU 961407, Е 21 В 33/138, опубл. 20.04.1999). The closest of the analogues is expanding grouting material of low density, containing Portland cement, diesel fuel or gas condensate, an expanding additive - calcium-aluminum slag, borax, technical lignosulfonates and water (see SU 961407, E 21 B 33/138, publ. 04/20/1999) .

Целью настоящего изобретения являются повышение седиментационной устойчивости, адгезионной прочности и прочности при изгибе. The aim of the present invention is to increase sedimentation stability, adhesive strength and flexural strength.

Поставленная цель достигается за счет того, что расширяющийся тампонажный материал пониженной плотности, включающий портландцемент, расширяющуюся добавку, технические лигносульфонаты - ЛСТ дополнительно содержит гипс, смолу нейтрализованную воздухововлекающую и триэтаноламин при следующем соотношении, мас. ч.:
Портландцемент - 100
Расширяющаяся добавка - 5-7
Технические лигносульфонаты ЛСТ - 0,01-0,25
Триэтаноламин - 0,01-0,6
Смола нейтрализованная воздухововлекающая - 0,005-0,1
Гипс - 0-6
Причем в качестве расширяющейся добавки может быть использован по крайней мере один компонент из группы: глиноземистый цемент, алюмокальциевый шлак, сульфоалюминаты кальция, сульфоферриты кальция.This goal is achieved due to the fact that expanding grouting material of low density, including Portland cement, an expanding additive, technical lignosulfonates - LST additionally contains gypsum, neutralized air-entraining resin and triethanolamine in the following ratio, wt. hours:
Portland cement - 100
Expanding Additive - 5-7
Technical lignosulfonates LST - 0.01-0.25
Triethanolamine - 0.01-0.6
Neutralized air-entraining resin - 0.005-0.1
Gypsum - 0-6
Moreover, at least one component from the group can be used as an expanding additive: alumina cement, calcium-aluminum slag, calcium sulfoaluminates, calcium sulfoferrites.

Пример осуществления изобретения. An example embodiment of the invention.

Для приготовления тампонажного материала используют портландцемент марки 500, лигносульфонаты технические ЛСТ, расширяющуюся добавку, смолу нейтрализованную воздухововлекающую СНВ, триэтаноламин. Указанные компоненты перемешивают с водой в соотношении тампонажный материал:вода от 1:0,5 до 1:0,7 перед началом цементирования скважин. For the preparation of grouting material, Portland cement of grade 500, technical lignosulfonates LST, an expanding additive, neutralized air-entraining START resin, triethanolamine are used. These components are mixed with water in the ratio of grouting material: water from 1: 0.5 to 1: 0.7 before starting cementing wells.

Составы тампонажных растворов и их свойства приведены в табл. 1 и 2. The compositions of cement slurries and their properties are given in table. 1 and 2.

Как следует из таблицы, полученный по изобретению тампонажный материал имеет высокую седиментационную устойчивость, повышенную адгезионную прочность и высокую прочность при изгибающих нагрузках. As follows from the table, the grouting material obtained according to the invention has a high sedimentation stability, increased adhesive strength and high strength under bending loads.

Claims

1. Expanding cementing material of low density, including Portland cement, an expanding additive and technical lignosulfonates LST, characterized in that it additionally contains gypsum, neutralized air-entraining resin (-CHB) and triethanolamine in the following ratio of components, wt. hours:
Portland cement - 100
Expanding Additive - 5-7
Technical lignosulfonates - 0.01-0.25
Triethanolamine - 0.01-0.06
Neutralized air-entraining resin - 0.005-0.1
Gypsum - 0-6
2. The expanding grouting material according to claim 1, characterized in that it contains at least one component from the group as an expanding additive: alumina cement, calcium-aluminum slag, calcium sulfoaluminates, calcium sulfoferrites.