RU2188980C1 - Method of protecting underground pipelines and metal structures from corrosion - Google Patents
Method of protecting underground pipelines and metal structures from corrosion Download PDFInfo
- Publication number
- RU2188980C1 RU2188980C1 RU2001114740/06A RU2001114740A RU2188980C1 RU 2188980 C1 RU2188980 C1 RU 2188980C1 RU 2001114740/06 A RU2001114740/06 A RU 2001114740/06A RU 2001114740 A RU2001114740 A RU 2001114740A RU 2188980 C1 RU2188980 C1 RU 2188980C1
- Authority
- RU
- Russia
- Prior art keywords
- corrosion
- underground pipelines
- metal structures
- primer
- bitumen
- Prior art date
Abstract
Description
Изобретение относится к защите подземных трубопроводов и подземных металлоконструкций от коррозии. The invention relates to the protection of underground pipelines and underground metal structures from corrosion.
Преимущественная область использования изобретения - наложение защитных покрытий на поверхность подземных трубопроводов и металлических конструкций. The preferred area of use of the invention is the application of protective coatings to the surface of underground pipelines and metal structures.
Известен способ защиты оборудования от водородного растрескивания (статья Иванова С.С. Ингибирование водородного растрескивания лакокрасочными покрытиями. //Защита от коррозии и охрана окружающей среды. - 1994 г. - 7. - с. 11-12), заключающийся в нанесении грунтовки на поверхность оборудования и наложения по ней ингибированного лакокрасочного покрытия. There is a method of protecting equipment from hydrogen cracking (article by S. Ivanov, Inhibition of hydrogen cracking by coatings. // Corrosion protection and environmental protection. - 1994. - 7. - S. 11-12), which consists in applying a primer to equipment surface and application of inhibited paintwork over it.
Недостатком известного способа является то, что в грунтовых условиях лакокрасочное покрытие быстро разрушается. The disadvantage of this method is that in soil conditions, the paintwork quickly collapses.
Прототипом изобретения является способ защиты от коррозии подземных трубопроводов (ГОСТ P51164-98. Трубопроводы стальные магистральные. Общие требования к защите oт коррозии. М.: Госстандарт России. - 1998. - 42 с.), в котором предусматривается нанесение на трубопровод грунтовки, на которую накладывается защитное покрытие, и применение катодной защиты. The prototype of the invention is a method of corrosion protection of underground pipelines (GOST P51164-98. Steel main pipelines. General requirements for corrosion protection. M: Gosstandart of Russia. - 1998. - 42 pp.), Which provides for the application of a primer on the pipeline, which a protective coating is applied, and the use of cathodic protection.
Недостатком прототипа является то, что в процессе эксплуатации с течением времени на некоторых участках трубопровода вследствие плохой адгезии с металлом или катодного отслаивания между изоляцией и грунтовкой оказывается влага, приводящая к коррозии трубопровода. Применение катодной защиты увеличивает приток влаги к трубопроводу за счет влияния сил элекроосмоса в местах, характеризующихся частичным или полным разрушением защитного покрытия. В результате процесс коррозии интенсивно продолжается, приводя к образованию коррозионных разрушений. The disadvantage of the prototype is that during operation over time, in some sections of the pipeline due to poor adhesion to metal or cathodic peeling between the insulation and the primer, moisture appears, leading to corrosion of the pipeline. The use of cathodic protection increases the flow of moisture to the pipeline due to the influence of electroosmosis forces in places characterized by partial or complete destruction of the protective coating. As a result, the corrosion process continues intensively, leading to the formation of corrosion damage.
Техническая задача, решаемая изобретением, заключается в повышении эффективности способа за счет торможения факторов, вызывающих коррозию на поверхности трубопровода. The technical problem solved by the invention is to increase the efficiency of the method by inhibiting factors that cause corrosion on the surface of the pipeline.
Сущность изобретения заключается в том, что в известном способе защиты подземных трубопроводов и металлоконструкций, включающем нанесение на трубопровод грунтовки с последующих нанесением защитного покрытия, согласно изобретению перед нанесением защитного покрытия в грунтовку предварительно вводят ингибитор коррозии "Тревис" на основе алкилпиридинов в количестве 1: 500 по массе. The essence of the invention lies in the fact that in the known method of protecting underground pipelines and metal structures, including applying a primer to the pipeline, followed by applying a protective coating, according to the invention, before applying a protective coating, the “Travis” corrosion inhibitor based on alkylpyridines in an amount of 1: 500 by weight.
Способ осуществляют следующим образом. В грунтовку добавляют ингибитор коррозии "Тревис". Смесь перемешивается до создания однородной массы, затем после очистки трубопровода грунтовка наносится на него, а далее накладывается изоляция в установленном порядке. The method is as follows. The Travis corrosion inhibitor is added to the primer. The mixture is mixed until a homogeneous mass is created, then after cleaning the pipeline, a primer is applied to it, and then insulation is applied in the prescribed manner.
Способ был осуществлен в лабораторных условиях, испытанию были подвергнуты два образца:
1. Стальная пластина 60х15х1 покрывалась битумной грунтовкой, представляющей собой битум, растворенный в бензине в пропорции 3:1.The method was carried out in laboratory conditions, two samples were tested:
1. The steel plate 60x15x1 was coated with a bitumen primer, which is bitumen, dissolved in gasoline in a 3: 1 ratio.
2. Стальная пластина 60х15х1 покрывалась грунтовкой, представляющей собой композицию в пропорции: на 50 г битумной грунтовки добавлено 0,1 ингибитора коррозии "Тревис" на основе алкилпиридинов. В качестве коррозионной среды использован 3%-ный раствор NaCl. 2. The 60x15x1 steel plate was coated with a primer, which is a composition in proportion: 0.1 g of Travis corrosion inhibitor based on alkylpyridines was added to 50 g of bitumen primer. A 3% NaCl solution was used as a corrosive medium.
Были проведены электрохимические исследования скорости коррозии образцов. По полученным данным были построены поляризационные кривые. Согласно Тафелевским уравнениям экстраполяции была рассчитана скорость коррозии, для первого образца она составила 2,7•10-3 мм/год, а для второго образца - 0,618•10-3 мм/год. Кроме того, образцы были испытаны в условиях, приближенных к реальным.Electrochemical studies of the corrosion rate of samples were carried out. Based on the data obtained, polarization curves were constructed. According to the Tafel equations of extrapolation, the corrosion rate was calculated, for the first sample it was 2.7 • 10 -3 mm / year, and for the second sample it was 0.618 • 10 -3 mm / year. In addition, the samples were tested under conditions close to real ones.
Образцы поочередно помещали в емкость с электролитом, служащим катодом, а емкость - анодом. Для протекания электрохимических процессов к установке подключали источник постоянного тока. Потенциал "образец-электролит" поддерживали (-0,65) В по ХЭC. The samples were alternately placed in a container with an electrolyte serving as a cathode, and a container - an anode. For electrochemical processes to occur, a direct current source was connected to the installation. The sample-electrolyte potential was maintained at (-0.65) V by HES.
Время проведения экспериментов для каждого образца 30 мин. По окончании экспериментов значение защитного тока для первого образа составило (-0,34) мА, а для второго - (-0,13) мА. The experiment time for each sample is 30 minutes. At the end of the experiments, the protective current for the first image was (-0.34) mA, and for the second - (-0.13) mA.
Проведенные эксперименты показали, что изобретение способствует улучшению защиты от коррозии. Experiments have shown that the invention improves corrosion protection.
Положительный эффект по сравнению с прототипом заключается в том, что в предлагаемом изобретении предложенная композиция хорошо защищает в грунтовых условиях. Это повышает эффективность способа защиты и снижает аварийность. The positive effect compared with the prototype is that in the proposed invention, the proposed composition protects well in soil conditions. This increases the efficiency of the protection method and reduces the accident rate.
Claims (1)