RU2170757C2 - Protective lubricant for metal components - Google Patents
Protective lubricant for metal components Download PDFInfo
- Publication number
- RU2170757C2 RU2170757C2 RU99118208A RU99118208A RU2170757C2 RU 2170757 C2 RU2170757 C2 RU 2170757C2 RU 99118208 A RU99118208 A RU 99118208A RU 99118208 A RU99118208 A RU 99118208A RU 2170757 C2 RU2170757 C2 RU 2170757C2
- Authority
- RU
- Russia
- Prior art keywords
- oil
- metal components
- lubricant
- water
- pitch
- Prior art date
Abstract
Description
Изобретение относится к смазкам, используемым в качестве защитных покрытий металлических деталей, в частности при хранении сельскохозяйственной техники на открытых площадках. The invention relates to lubricants used as protective coatings for metal parts, in particular when storing agricultural machinery in open areas.
Для защиты деталей от атмосферной коррозии применяются различные консервационные масла и смазки высоковязких минеральных масел и твердых углеводородов. Многие смазки содержат различные присадки, улучшающие их защитные свойства. Механизм действия большинства защитных смазок сводится к созданию на поверхности детали слоя, который препятствует проникновению атмосферной влаги к поверхности металла. To protect parts from atmospheric corrosion, various preservation oils and lubricants of high-viscosity mineral oils and solid hydrocarbons are used. Many lubricants contain various additives that improve their protective properties. The mechanism of action of most protective lubricants is reduced to the creation of a layer on the surface of the part, which prevents the penetration of atmospheric moisture to the metal surface.
Наиболее близким техническим решением, выбранным в качестве прототипа, являются консервационные масла и смазки, полученные на базе отработанных моторных масел, используемые для межсезонной защиты от коррозии сельскохозяйственной техники, запасных частей и т.д. /"Нефтепереработка и нефтехимия", М., 1982, N 2, с. 16-18/. The closest technical solution, selected as a prototype, are preservation oils and greases obtained on the basis of used motor oils used for off-season corrosion protection of agricultural machinery, spare parts, etc. / "Oil refining and petrochemistry", M., 1982,
Недостатком таких смазок является то, что отработанные моторные масла не обладают достаточной липкостью с покрываемой поверхностью детали /адгезией/ и поэтому легко смываются атмосферными осадками в период хранения машин на открытых площадках. The disadvantage of such lubricants is that used motor oils do not have sufficient stickiness with the coated surface of the part / adhesion / and therefore are easily washed off by atmospheric precipitation during the storage of machines in open areas.
Задача изобретения - повышение коррозийной стойкости металлических деталей сельскохозяйственной техники при хранении на открытых площадках, использование отработанных моторных масел автотракторных двигателей. The objective of the invention is to increase the corrosion resistance of metal parts of agricultural machinery when stored in open areas, the use of used motor oils of automotive engines.
Указанная задача достигается тем, что предлагаемая смазка, включающая отработанное моторное масло, эмульгатор, добавку и воду, содержит в качестве эмульгатора омыленный талловый пек, в качестве добавки - кальцинированную соду при следующем соотношении компонентов, мас.%:
Отработанное моторное масло - 20-30
Омыленный талловый пек - 2,0-3,0
Кальцинированная сода - 0,3-0,9
Вода - Остальное
Для приготовления смазки использовали отработанное моторное масло, омыленный талловый пек /ОТП/ - отход сульфатно-целлюлозного производства Братского ЛПК /ОСТ-130-145-82/, являющийся поверхностно-активным веществом. Введение /ОТП/ в состав смазки обеспечивает получение стабильной эмульсии за счет наличия в составе пека смоляных и жирных кислот. В результате реакций компонентов омыленного таллового пека с отработанным моторным маслом и кальцинированной содой образуются натриевые мыла, которые являются гидрофильными эмульгаторами и дают эмульсию типа "масло в воде".This problem is achieved by the fact that the proposed lubricant, including used motor oil, emulsifier, additive and water, contains saponified tall pitch as an emulsifier, soda ash as an additive in the following ratio, wt.%:
Used engine oil - 20-30
Saponified Tall Pitch - 2.0-3.0
Soda ash - 0.3-0.9
Water - Else
For the preparation of the lubricant used spent engine oil, saponified tall pitch / OTP / - waste sulfate-cellulose production Bratsk LPK / OST-130-145-82 /, which is a surface-active substance. Introduction / OTP / into the composition of the lubricant provides a stable emulsion due to the presence of tar and fatty acids in the pitch. As a result of the reactions of saponified tall oil pitch components with used motor oil and soda ash, sodium soaps are formed, which are hydrophilic emulsifiers and give an oil-in-water emulsion.
Смазку готовили путем эмульгирования расчетных компонентов в отработанном масле, при комнатной температуре механическим перемешиванием в лопастном смесителе до получения однородной пасты, ориентировочно продолжительность составляет 10-20 минут. Смазка на основе отработанных моторных масел по консистенции представляет собой пасту серовато-желтого цвета, легко наносимую на поверхность металлических деталей кистью или разбрызгиванием под давлением. Смазка обладает высокой адгезией к поверхности металлических деталей и обеспечивает нанесение смазки равномерным тонким слоем, как в холодном, так и в горячем состояниях. Lubrication was prepared by emulsification of the calculated components in the used oil, at room temperature by mechanical stirring in a paddle mixer to obtain a homogeneous paste, approximately 10-20 minutes. Consistency-based lubrication grease is a greyish-yellow paste that is easily applied to the surface of metal parts with a brush or spray under pressure. The grease has high adhesion to the surface of metal parts and ensures that the grease is applied in a uniform thin layer, both in cold and in hot conditions.
Примеры вариантов смазки, позволяющие исключить коррозию на металлических деталях сельскохозяйственной технике при хранении на открытых площадках, при следующем соотношении компонентов:
Отработанное моторное масло 20,0; 25,0; 30,0 мас.%
Омыленный талловый пек 2,0; 2,5; 3,0 мас.%
Кальцинированная сода 0,3; 0,6; 0,9 мас.%
Вода Остальное.Examples of lubrication options to eliminate corrosion on metal parts of agricultural machinery when stored in open areas, with the following ratio of components:
Spent engine oil 20.0; 25.0; 30.0 wt.%
Saponified tall pitch 2.0; 2.5; 3.0 wt.%
Soda ash 0.3; 0.6; 0.9 wt.%
Water The rest.
Все компоненты, кроме отработанного масла, используются в виде водных растворов. All components except used oil are used as aqueous solutions.
При изготовлении смазки рекомендуется следующая последовательность загрузки составляющих компонентов: отработанное моторное масло + омыленный талловый пек + кальцинированная сода вводятся с расчетным количеством воды. In the manufacture of grease, the following sequence of loading of the components is recommended: waste engine oil + saponified tall oil pitch + soda ash are introduced with the estimated amount of water.
Для ускорения растворения омыленного таллового пека воду рекомендуется подогреть до 30-40oC.To accelerate the dissolution of saponified tall oil pitch, it is recommended to heat the water to 30-40 o C.
После длительного хранения смазки желательно кратковременное перемешивание в течение 1 мин. After prolonged storage of the lubricant, short-term mixing for 1 minute is desirable.
Перед проведением производственных испытаний смазки были проведены лабораторные испытания. Исследование защитных свойств смазок проводилось в везерометре, где образцы подвергались циклическому воздействию искусственных факторов, имеющих место при длительном хранении машин на открытых площадках. Для выбора эффективных средств были приняты следующие смазки: 1. отработанное моторное масло; 2. смазка К-17; смазка НГ-204; отработанное моторное масло + омыленный талловый пек + кальцинированная сода + вода, на поверхность образцов /сталь 10/ смазки наносили тонким слоем. Результаты ускоренных испытаний защитных свойств смазок приведены в таблице. Before conducting production tests of the lubricant, laboratory tests were conducted. The study of the protective properties of lubricants was carried out in a vesometer, where the samples were subjected to cyclic exposure to artificial factors that occur during prolonged storage of machines in open areas. The following lubricants were used to select effective agents: 1. used engine oil; 2. grease K-17; lubricant NG-204; used motor oil + saponified tall oil pitch + soda ash + water, a thin layer of grease was applied to the surface of the samples / steel 10 /. The results of accelerated tests of the protective properties of lubricants are given in the table.
Для оценки защитной способности различных консервационных масел в условиях хранения сельскохозяйственной техники были проведены испытания. Проведенные испытания по выявлению защитной способности отработанных моторных масел, которые очень широко используют хозяйства как средство защиты от коррозии при постановке сельскохозяйственной техники на хранение, показали невысокие результаты. Коэффициент защитной способности отработанного моторного масла K = 0,12 - 0,35 /см. таблицу/. Состав смазки данного состава, имеющий коэффициент защитной способности K = 0,92-0,96 /см. таблицу/, может быть рекомендован и использован для защиты от коррозии наружных поверхностей деталей сельскохозяйственной техники при хранении на открытых площадках. To assess the protective ability of various preservation oils in storage conditions of agricultural machinery, tests were conducted. Tests conducted to identify the protective ability of used motor oils, which are very widely used by farms as a means of corrosion protection when storing agricultural machinery for storage, showed poor results. The coefficient of protective ability of used engine oil K = 0.12 - 0.35 / cm. table. The composition of the lubricant of this composition having a coefficient of protective ability K = 0.92-0.96 / cm table /, can be recommended and used to protect the external surfaces of agricultural machinery parts from corrosion during storage in open areas.
Процессом торможения электродного механизма коррозии является введение в отработанное масло пассивирующих веществ. В предлагаемом составе смазки в качестве пассивирующего вещества используется омыленный талловый пек. The process of braking the electrode mechanism of corrosion is the introduction of passivating substances into the used oil. In the proposed lubricant composition, saponified tall oil pitch is used as a passivating agent.
Использование смазки данного состава позволит исключить коррозию металлических деталей сельскохозяйственной техники при хранении на открытых площадках за счет высокой адгезии к поверхности металлических деталей. Данная смазка не требует подогрева. Использование отработанных моторных масел позволит отказаться от применения для смазок дорогостоящих масляных нефтяных соединений. The use of a lubricant of this composition will eliminate the corrosion of metal parts of agricultural machinery when stored in open areas due to the high adhesion to the surface of metal parts. This grease does not require heating. The use of used motor oils will make it possible to abandon the use of expensive oil-based petroleum compounds for lubricants.
Claims (1)
Отработанное моторное масло - 20 - 30
Омыленный талловый пек - 2,0 - 3,0
Кальцинированная сода - 0,3 - 0,9
Вода - ОстальноеиProtective lubricant for metal parts during storage of agricultural machinery, including used motor oil, characterized in that it further contains saponified tall tar pitch, soda ash and water in the following ratio, wt.%:
Used engine oil - 20 - 30
Saponified Tall Pitch - 2.0 - 3.0
Soda ash - 0.3 - 0.9
Water - Rest