RU2015149048A - A method of producing castings from high-strength alloy based on aluminum - Google Patents

A method of producing castings from high-strength alloy based on aluminum Download PDF

Info

Publication number
RU2015149048A
RU2015149048A RU2015149048A RU2015149048A RU2015149048A RU 2015149048 A RU2015149048 A RU 2015149048A RU 2015149048 A RU2015149048 A RU 2015149048A RU 2015149048 A RU2015149048 A RU 2015149048A RU 2015149048 A RU2015149048 A RU 2015149048A
Authority
RU
Russia
Prior art keywords
aluminum
castings
producing castings
casting
heat treatment
Prior art date
Application number
RU2015149048A
Other languages
Russian (ru)
Other versions
RU2621499C2 (en
Inventor
Николай Александрович Белов
Александр Николаевич Алабин
Торгом Кароевич Акопян
Сергей Сергеевич Мишуров
Original Assignee
Федеральное государственное автономное образовательное учреждение высшего образования "Национальный исследовательский технологический университет "МИСиС"
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Федеральное государственное автономное образовательное учреждение высшего образования "Национальный исследовательский технологический университет "МИСиС" filed Critical Федеральное государственное автономное образовательное учреждение высшего образования "Национальный исследовательский технологический университет "МИСиС"
Priority to RU2015149048A priority Critical patent/RU2621499C2/en
Publication of RU2015149048A publication Critical patent/RU2015149048A/en
Application granted granted Critical
Publication of RU2621499C2 publication Critical patent/RU2621499C2/en

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C21/00—Alloys based on aluminium
    • C22C21/10—Alloys based on aluminium with zinc as the next major constituent

Landscapes

  • Continuous Casting (AREA)
  • Forging (AREA)

Claims (9)

1. Способ получения отливок из высокопрочного сплава на основе алюминия, включающий приготовление расплава, содержащего цинк, магний, медь, никель и железо, термообработку отливок, приводящую к формированию структуры, состоящей из дисперсионно упрочненной алюминиевой матрицы и компактных частиц фазы Al9FeNi, отличающийся тем, что расплав готовят на основе алюминия, содержащего железо, производимого по технологии электролиза с инертным анодом, при этом концентрацию легирующих элементов, режимы литья отливок и термообработки выбирают так, чтобы получить в отливке структуру с размером дендритной ячейки алюминиевой матрицы не более 30 мкм и ее микротвердостью не менее 170 HV.1. A method of producing castings from a high-strength alloy based on aluminum, including the preparation of a melt containing zinc, magnesium, copper, nickel and iron, heat treatment of castings, leading to the formation of a structure consisting of dispersion-hardened aluminum matrix and compact particles of the Al 9 FeNi phase, characterized the fact that the melt is prepared on the basis of aluminum containing iron produced by electrolysis with an inert anode, while the concentration of alloying elements, casting and heat treatment modes are chosen so that in order to obtain a structure with a dendritic cell size of the aluminum matrix of not more than 30 μm and its microhardness of at least 170 HV. 2. Способ получения отливок по п. 1, отличающийся тем, что отливки получают литьем в кокиль, затем их гомогенизируют, подвергают горячему изостатическому прессованию (ГИП) и упрочняющей термообработке, включающей закалку и старение, со следующими свойствами на растяжение: временное сопротивление (σв) - не менее 500 МПа, предел текучести (σ0,2) - не менее 450 МПа, относительное удлинение (δ) - не менее 5%.2. A method for producing castings according to claim 1, characterized in that the castings are obtained by casting in a chill mold, then they are homogenized, subjected to hot isostatic pressing (HIP) and hardening heat treatment, including hardening and aging, with the following tensile properties: temporary resistance (σ c ) - not less than 500 MPa, yield strength (σ 0.2 ) - not less than 450 MPa, elongation (δ) - not less than 5%. 3. Способ получения отливок по п. 1, отличающийся тем, что отливки получают методом литья с кристаллизацией под давлением3. The method of producing castings according to claim 1, characterized in that the castings are obtained by casting with crystallization under pressure 4. Способ получения отливок по п. 1, отличающийся тем, что концентрация легирующих элементов сплава на основе алюминия, произведенного по технологии электролиза с инертным анодом принадлежит следующим диапазонам, мас. %:4. The method of producing castings according to claim 1, characterized in that the concentration of alloying elements of an aluminum-based alloy produced by an inert anode electrolysis technology belongs to the following ranges, wt. %: Цинк - 6,3-7,5,Zinc - 6.3-7.5, Магний-2,1-2,8,Magnesium 2.1-2.8, Медь - 0,2-0,35,Copper - 0.2-0.35, Никель - 0,6-0,8,Nickel - 0.6-0.8, Железо - 0,50-0,70.Iron - 0.50-0.70.
RU2015149048A 2015-11-17 2015-11-17 Method for producing castings of high-strength aluminium-based alloys RU2621499C2 (en)