RU2011140398A - Способ нанесения покрытий на металлические поверхности в многостадийном способе - Google Patents
Способ нанесения покрытий на металлические поверхности в многостадийном способе Download PDFInfo
- Publication number
- RU2011140398A RU2011140398A RU2011140398/02A RU2011140398A RU2011140398A RU 2011140398 A RU2011140398 A RU 2011140398A RU 2011140398/02 A RU2011140398/02 A RU 2011140398/02A RU 2011140398 A RU2011140398 A RU 2011140398A RU 2011140398 A RU2011140398 A RU 2011140398A
- Authority
- RU
- Russia
- Prior art keywords
- silane
- aqueous composition
- silanol
- siloxane
- polysiloxane
- Prior art date
Abstract
1. Способ нанесения покрытий на металлические поверхности, особенно поверхности колесных дисков из алюминиевого сплава, в многостадийном способе, отличающийся тем, что металлические поверхности сначала контактируют с водной композицией, содержащей значительное количество силана/силанола/силоксана/полисилоксана, а затем с водной композицией, преимущественно содержащей по меньшей мере одно фосфоновое соединение, причем по меньшей мере 80% всех содержащихся в этой композиции фосфоновых соединений выбраны из группы, включающей соединения формулы XYZ,причем Y независимо друг от друга означают неразветвленную алкильную группу с 8-16 атомами углерода или алкильную группу с 8-16 атомами углерода, до 20% атомов углерода алкильной цепи которой среднестатистически имеют функциональную группу,Х означает ОН-, NH-, NHR'-, CH=CH-, CONHOH- или COOR'-группу, группу амида акриловой кислоты, эпокси-, CH=CR"-COO-, СООН-, HSO-, (ОН)РО-, (ОН)PO-, (OH)(OR')PO-, (OH)(OR')PO- или Si(ОН)-группу,Z означает (ОН)РО-, (ОН)PO-, (OH)(OR')PO- или (OH)(OR')PO-группу,причем R' означает алкильную группу с 1-4 атомами углерода,причем R" означает атом водорода или алкильную группу с 1-4 атомами углерода,причем группы Х и Z соответственно присоединены к концу группы Y,и причем прежде чем снабдить металлические поверхности по меньшей мере одним лаковым слоем или/и по меньшей мере одним клеевым слоем, последовательно формируют сначала силановое покрытие, а затем фосфонатное покрытие.2. Способ по п.1, отличающийся тем, что общее содержание силана/силанола/силоксана/полисилоксана в содержащей силан/силанол/силоксан/полисилоксан водной композиции составляет от 0,003 до 10 г/л.3. Способ по п.1, отличающийся тем, что содержащ
Claims (29)
1. Способ нанесения покрытий на металлические поверхности, особенно поверхности колесных дисков из алюминиевого сплава, в многостадийном способе, отличающийся тем, что металлические поверхности сначала контактируют с водной композицией, содержащей значительное количество силана/силанола/силоксана/полисилоксана, а затем с водной композицией, преимущественно содержащей по меньшей мере одно фосфоновое соединение, причем по меньшей мере 80% всех содержащихся в этой композиции фосфоновых соединений выбраны из группы, включающей соединения формулы XYZ,
причем Y независимо друг от друга означают неразветвленную алкильную группу с 8-16 атомами углерода или алкильную группу с 8-16 атомами углерода, до 20% атомов углерода алкильной цепи которой среднестатистически имеют функциональную группу,
Х означает ОН-, NH2-, NHR'-, CH=CH2-, CONHOH- или COOR'-группу, группу амида акриловой кислоты, эпокси-, CH2=CR"-COO-, СООН-, HSO4-, (ОН)2РО-, (ОН)2PO2-, (OH)(OR')PO-, (OH)(OR')PO2- или Si(ОН)3-группу,
Z означает (ОН)2РО-, (ОН)2PO2-, (OH)(OR')PO- или (OH)(OR')PO2-группу,
причем R' означает алкильную группу с 1-4 атомами углерода,
причем R" означает атом водорода или алкильную группу с 1-4 атомами углерода,
причем группы Х и Z соответственно присоединены к концу группы Y,
и причем прежде чем снабдить металлические поверхности по меньшей мере одним лаковым слоем или/и по меньшей мере одним клеевым слоем, последовательно формируют сначала силановое покрытие, а затем фосфонатное покрытие.
2. Способ по п.1, отличающийся тем, что общее содержание силана/силанола/силоксана/полисилоксана в содержащей силан/силанол/силоксан/полисилоксан водной композиции составляет от 0,003 до 10 г/л.
3. Способ по п.1, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция содержит по меньшей мере один моносилан, по меньшей мере один биссилилсилан или/и по меньшей мере один триссилилсилан.
4. Способ по п.1, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция содержит по меньшей мере один алкоксисилан, по меньшей мере один аминосилан, по меньшей мере один эпоксисилан или/и по меньшей мере один винилсилан или смесь по меньшей мере двух разных аминосиланов.
5. Способ по п.1, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция содержит по меньшей мере один моноаминосилан, по меньшей мере один диаминосилан, по меньшей мере один диалкоксисилан или/и по меньшей мере один триалкоксисилан.
6. Способ по п.1, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция содержит а) по меньшей мере одно соединение, выбранное из группы, включающей силаны, силанолы, силоксаны и полисилоксаны, и b) по меньшей мере одно соединение, содержащее титан, гафний или/и цирконий.
7. Способ по п.6, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция дополнительно содержит с) катионы по меньшей мере одного типа, выбранные из группы, включающей катионы металлов от 1-й до 3-й и от 5-й до 8-й побочных групп, в том числе лантаниды, и 2-й главной группы периодической системы элементов или/и по меньшей мере одно соответствующее соединение.
8. Способ по п.6, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция дополнительно содержит по меньшей мере одно вещество d), выбранное из группы, включающей d1) не содержащие кремния соединения соответственно по меньшей мере с одной амино-, карбамидо- (=уреидо-), имидо- или/и имино-группой, d2) анионы нитрита или/и соединения по меньшей мере с одной нитрогруппой, d3) соединения на основе пероксида и d4) фосфорсодержащие соединения, анионы по меньшей мере одного фосфата или/и анионы по меньшей мере одного фосфоната, а также содержит е) воду.
9. Способ по п.7, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция дополнительно содержит по меньшей мере одно вещество d), выбранное из группы, включающей d1) не содержащие кремния соединения соответственно по меньшей мере с одной амино-, карбамидо- (=уреидо-), имидо- или/и имино-группой, d2) анионы нитрита или/и соединения по меньшей мере с одной нитрогруппой, d3) соединения на основе пероксида и d4) фосфорсодержащие соединения, анионы по меньшей мере одного фосфата или/и анионы по меньшей мере одного фосфоната, а также содержит е) воду.
10. Способ по п.6, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция дополнительно содержит f) по меньшей мере один органический растворитель.
11. Способ по п.7, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция дополнительно содержит f) по меньшей мере один органический растворитель.
12. Способ по п.8, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция дополнительно содержит f) по меньшей мере один органический растворитель.
13. Способ по п.9, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция дополнительно содержит f) по меньшей мере один органический растворитель.
14. Способ по п.1, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция содержит соответственно по меньшей мере один органический олигомер или/и органический полимер, по меньшей мере один амин, по меньшей мере одно основание, по меньшей мере один комлексообразователь, по меньшей мере одно поверхностно-активное вещество, неорганические частицы по меньшей мере одного типа или/и соответственно по меньшей мере одну неорганическую или/и органическую кислоту или/и по меньшей мере одно ее производное.
15. Способ по п.1, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция имеет показатель рН, находящийся в диапазоне от 3 до 11.
16. Способ по п.1, отличающийся тем, что содержащая силан/силанол/силоксан/полисилоксан водная композиция при контактировании имеет температуру в диапазоне от 5 до 80°С.
17. Способ по п.1, отличающийся тем, что содержащую силан/силанол/силоксан/полисилоксан водную композицию наносят напылением или погружением.
18. Способ по п.1, отличающийся тем, что общее содержание фосфонового(-ых) соединения(-й) в содержащей по меньшей мере одно фосфоновое соединение водной композиции составляет от 0,001 до 10 г/л.
19. Способ по п.1, отличающийся тем, что содержащая по меньшей мере одно фосфоновое соединение водная композиция содержит по меньшей мере одно фосфоновое соединение на основе фосфоновой кислоты, дифосфоновой кислоты, их сложного эфира или/и их соли.
20. Способ по п.1, отличающийся тем, что содержащая по меньшей мере одно фосфоновое соединение водная композиция кроме воды или смеси воды с растворителем и кроме по меньшей мере одного соединения формулы XYZ содержит биоцид, деэмульгатор, отдушку, эмульгатор, антивспениватель, гидротропный солюбилизатор, поверхностно-активное вещество, средство для установления показателя рН, средство для установления электрической проводимости, другие добавки, соответственно по меньшей мере один органический олигомер или/и органический полимер, по меньшей мере один амин или/и по меньшей мере один комплексообразователь.
21. Способ по п.1, отличающийся тем, что показатель рН содержащей по меньшей мере одно фосфоновое соединение водной композиции находится в интервале от 1,5 до 9,0.
22. Способ по п.1, отличающийся тем, что содержащая по меньшей мере одно фосфоновое соединение водная композиции при контактировании с металлической поверхностью имеет температуру от 5 до 80°С.
23. Способ по п.1, отличающийся тем, что содержащую по меньшей мере одно фосфоновое соединение водную композицию наносят погружением, орошением, разбрызгиванием или распылением.
24. Способ по п.1, отличающийся тем, что металлические поверхности перед контактированием с содержащей силан/силанол/силоксан/полисилоксан водной композицией подвергают очистке, обезжириванию или/и травлению.
25. Способ по п.1, отличающийся тем, что металлические поверхности до или/и после контактирования с содержащей силан/силанол/силоксан/полисилоксан водной композицией или/и до или/и после контактирования с содержащей по меньшей мере одно фосфоновое соединение водной композицией промывают водой.
26. Способ по п.1, отличающийся тем, что фосфонатное покрытие наносят не на высушенное, а на влажное или подсушенное силановое покрытие.
27. Способ по п.1, отличающийся тем, что перед нанесением фосфонатного покрытия силановое покрытие подвергают тщательной сушке.
28. Способ по п.1, отличающийся тем, что фосфонатное покрытие снабжают по меньшей мере одним слоем праймера, лака или/и клея.
29. Способ по одному из пп.1-28, отличающийся тем, что обработке подвергают металлические поверхности на основе алюминия, магния, железа, стали, титана, цинка, олова или/и их сплава(-ов).