RU2002783C1 - Adhesive composition for sticky bands and films - Google Patents
Adhesive composition for sticky bands and filmsInfo
- Publication number
- RU2002783C1 RU2002783C1 SU4947576A RU2002783C1 RU 2002783 C1 RU2002783 C1 RU 2002783C1 SU 4947576 A SU4947576 A SU 4947576A RU 2002783 C1 RU2002783 C1 RU 2002783C1
- Authority
- RU
- Russia
- Prior art keywords
- acrylate
- adhesive
- rubber
- ethyl acetate
- adhesive tapes
- Prior art date
Abstract
Использование: получение клеевых композиций дл липких лент и пленок, эксплуатируемых при температуре от - 60 до -ь 160°,С. Сущность изобретени : клеева композици дл липких лент и пл енок содержит акрилатный каучук - сополимер бутилакрилата, этоксиэтилакрилата и метилвинил- пиридина (СКБЭВП) при массовом соотношении мономеров 45 - 70 : 25 - 50 : 3 - 5 - 100 мас . низкомолекул рный акрилатный каучук на основе этоксиэтилакрилата и акриловой кислоты (СКА - РЭТОКС) со статически распределением либо концевыми карбоксильными группами с функциональность не более 3,5 и моамассой 3000 - 5000 - 40 - 60 мас , диэлоксидный олигомер на основе ди-. фенилолпропана или тетрабромдифенилпропана с содержанием эпоксидных групп не более 13% 5 - 35 мас.4, зтилацетат 200 - 500 маем. Каучук СКТЭВП раствор ют в этипацетате, добавл ют жидкий каучук СКА - РЭТОКС, перемешивают и добавл ют раствор эпоксидной смолы в этилацета- те. Характеристики липких лент: прочность при отслаивании при 20° С от алюминиевого сплава на СТФ-подпожке 0.9 кг/см, на лавсане - 0,85 кг/см, стойкость к действию статического напр жени сдвига при температуре от - 60 до + 160° С 6000 мин 2таблUsage: preparation of adhesive compositions for adhesive tapes and films operated at a temperature of from -60 to-160 ° C. SUMMARY OF THE INVENTION: the adhesive composition for adhesive tapes and films contains acrylate rubber - a copolymer of butyl acrylate, ethoxyethyl acrylate and methyl vinyl pyridine (SCBEP) with a weight ratio of monomers of 45 - 70: 25 - 50: 3 - 5 - 100 wt. low molecular weight acrylate rubber based on ethoxyethyl acrylate and acrylic acid (SKA - RETOX) with a statically distributed or terminal carboxyl group with a functionality of not more than 3.5 and a moamass of 3000 - 5000 - 40 - 60 wt., di-based oxide oligomer. phenylolpropane or tetrabromodiphenylpropane with an epoxy content of not more than 13% 5 to 35 wt. 4, ethyl acetate 200 to 500 may. SKTEVP rubber is dissolved in ethyl acetate, SKA-RETOX liquid rubber is added, mixed and a solution of epoxy resin in ethyl acetate is added. Characteristics of adhesive tapes: peeling strength at 20 ° C from the aluminum alloy on the STF support, 0.9 kg / cm, on the lavsan - 0.85 kg / cm, resistance to static shear stress at a temperature of from -60 to + 160 ° C; C 6000 min 2tables
Description
Изобретение относитс к области клеевых композиций и может быть использовано дл липких лент и пленок, предназначенных дл длительной эксплуатации при температуре от-60 до И60°С. Подложками дл таких липких лент могут быть различные полимерные пленки, ткани, также материалы с инер- тными поверхност ми, например фторлакоткани.The invention relates to the field of adhesive compositions and can be used for adhesive tapes and films intended for long-term operation at temperatures from -60 to 60 ° C. The substrates for such adhesive tapes can be various polymer films, fabrics, and also materials with inert surfaces, for example fluorinated fabrics.
Клеева композици может использоватьс в виде переносного липкого сло на бумаге с ангиадгезионным покрытием.The adhesive composition can be used in the form of a portable sticky layer on an anti-adhesive paper.
Известны клеи дл липких лент, работоспособные при повышенных температурах. Например, клей на основе акриловых полимеров с добавками в качестве сшивающего агента - изофталамина, и катализатора - гетрабутилтитаната или октата хрома. Сшивание происходит в процессе удалени растворител при сушке кле .Adhesives for adhesive tapes which are operable at elevated temperatures are known. For example, an adhesive based on acrylic polymers with additives as a crosslinking agent - isophthalamine, and a catalyst - hetrabutyl titanate or chromium octate. Crosslinking occurs during the removal of the solvent by drying the glue.
Известна также клеева композици на основе сополимера октилакрилатов и акриловой кислоты с использованием в качестве латентного отвердител алкоксилиров анно- го аминоформальдсгидного конденсата. Однако указанные выше клем и липкие ленты с их использованием работоспособны при температуре не выше+70°С,A glue composition based on a copolymer of octyl acrylates and acrylic acid is also known, using an amine formaldehyde condensate as a latent hardener of alkoxylates. However, the above clems and adhesive tapes with their use are operable at a temperature not exceeding + 70 ° C,
В качестве прототипа выбрана клеева композици следуюа его состава, мае. ч.:A glue composition of the following composition was selected as a prototype in May. hours:
Хлорвинилова Khlorvinilova
смола ПСХ-ЛС100,0resin PSX-LS100,0
Пластификатор фосфатный158 ,0-164.0Phosphate plasticizer158, 0-164.0
Канифоль27,0Rosin27.0
Клеева композици используетс в липкой пленке марки ЛИГ (ТУ-17-7Й-85) на подложке из фторлакоткани. Липка лента Примен етс в отечественном самолетостроении дл длительной эксплуатации при температуре от -60 до +60°С. Недостатками липкой лепты ЛНГ вл ютс низка когези- онна прочность (стойкость к длительному действию статического напр жени сдвига), особенно при температуре выше -t-60°C, так как клеева композици содержит б своем составе низкомолекул рный фосфатный пластификатор, что определ ет его низкие когезионные и адгезионные свойства при температуре свыше +60°С.The glue composition is used in a LIG adhesive film (TU-17-7Y-85) on a fluorocarbon substrate. Adhesive tape Used in domestic aircraft manufacturing for long-term operation at temperatures from -60 to + 60 ° C. The disadvantages of sticky mite of LNG are low cohesive strength (resistance to long-term action of static shear stress), especially at temperatures above -t -60 ° C, since the adhesive composition contains a low molecular weight phosphate plasticizer, which determines it low cohesive and adhesive properties at temperatures above + 60 ° C.
Целью изобретени вл етс повышение когезионной прочности композиции при температуре от -60 до +160°С, а также адгезии к различным Субстратам.The aim of the invention is to increase the cohesive strength of the composition at a temperature of from -60 to + 160 ° C, as well as adhesion to various substrates.
Указанна цель достигаетс составом композиции, включающей полимерную основу и растворитель - этилацетат, отличающийс тем. что, с целью повышени когезионной прочности и адгезии к различным субстратам при температуре от -60 доThis goal is achieved by the composition comprising a polymer base and a solvent of ethyl acetate, characterized in that. that, in order to increase cohesive strength and adhesion to various substrates at temperatures from -60 to
-М60°С, она содержит в качестве полимерной основы акрилатный каучук - сополимер бутилакрилата, зтоксиэтилакрилата и ме- тилвинилпиридина при массовом соотно- шении мономеров 45-70:25-50:3-5 и дополнительно низкомолекул рный акрилатный каучук на основе этоксиэтилакрила- та и акриловой кислоты со статистически распределенными либо концевыми карбок- сильными группами с функциональностью не более 3.5 и мол. массой 3000-5000 и диэпоксидный олигомер на основе дифени- лолпропана или тетрабромдифенилолпро- пана с содержанием эпоксидных групп не более 13 мае. % при следующем соотношении компонентов, мае. ч.:-M60 ° C, it contains acrylate rubber as a polymer base - a copolymer of butyl acrylate, ztoxyethyl acrylate and methyl vinyl pyridine with a mass ratio of monomers 45-70: 25-50: 3-5 and additionally low molecular weight acrylate rubber based on ethoxyethyl acrylate and acrylic acid with statistically distributed or terminal carboxylic acid groups with a functionality of not more than 3.5 mol%. weighing 3000-5000 and a diepoxide oligomer based on diphenylolpropane or tetrabromodiphenylolpropane with an epoxy content of not more than 13 May. % at the following ratio of components, May. hours:
Акрилатный каучук сополимер бутилакрилата.Acrylate rubber butyl acrylate copolymer.
этоксиэтилакрилата и метилвинилпиридина,ethoxyethyl acrylate and methyl vinyl pyridine,
марки СКБЭВЦbrand SKBEVC
(ТУ 38.403.605.89)100,0(TU 38.403.605.89) 100.0
Низкомолекул рныйLow molecular weight
акрилатный каучук наacrylate rubber on
основе отоксиэтилакрилатаotoxyethyl acrylate based
и акриловой кислоты,and acrylic acid,
марки СКА-РэтоксSKA-Ratox brands
(ТУ 38.403.664-90)40,0-60,0(TU 38.403.664-90) 40.0-60.0
Диэпоксидный олигомер 0 на основеDiepoxy Oligomer 0 Based
дифенилолпропанаdiphenylolpropane
ЗД-8, ЭД-10ZD-8, ED-10
(ГОСТ 10587-84)(GOST 10587-84)
или на основе 5 тетрабромдифенилолпропана ФОУ-8 . ТУ 38-УССР215-8-805 ,0-35,0or based on 5 tetrabromodiphenylolpropane FOU-8. TU 38-Ukrainian SSR215-8-805, 0-35.0
ЭтилацетатEthyl acetate
(ГОСТ 89981)- 200,0-500.0(GOST 89981) - 200.0-500.0
0 Новизна данного технического решени заключаетс в том, что авторами предлагаетс клеева композици , позвол юща без введени в нее специальных отвердите- лей получать частично сшиваемый липкий 5 клей, чем достигаетс его работоспособность в интервале температур от -60 до +160°С при сохранении баланса адгезионных и когезионных свойств. Существенным преимуществом предлагаемого решени в- 0 л етс возможность в случае необходимости варьировать баланс адгезионных и когезионных свойств путем изменени соотношени низкомолекул рного каучука с карбоксильными группами и эпоксидной 5 смолы в составе композиции.0 The novelty of this technical solution lies in the fact that the authors propose a glue composition that allows, without introducing special hardeners, to obtain a partially crosslinkable sticky 5 glue, which ensures its performance in the temperature range from -60 to + 160 ° C while maintaining the balance adhesive and cohesive properties. A significant advantage of the proposed solution is the possibility, if necessary, to vary the balance of adhesive and cohesive properties by changing the ratio of low molecular weight rubber with carboxyl groups and epoxy 5 resin in the composition.
Примеры приготовлени клеевых композиций . Готов т клеевые композиции 1-12, составы которых приведены в таблице.Examples of the preparation of adhesive compositions. Adhesive compositions 1-12 are prepared, the compositions of which are shown in the table.
Пример 1. 100 г каучука СКБЭВЦ раствор ют в 200 г этилацетата, затем до5 олчют 50 г жидкого каучука СКА-Р ив основе эгоксиэтилакрилспэ, пеосг-н им- влют и добавл ют 15 г эпоксидно CNVfti ФОУ-8 в пиде 1 %-ного раствора в кпз- цетате Клеевую массу перемешиваю до получени однородною раствора,Example 1. 100 g of rubber SKBEC is dissolved in 200 g of ethyl acetate, then 50 g of liquid rubber SKA-P based on ehoxyethyl acrylpe are added, peg-n is present and 15 g of epoxy CNVfti FOU-8 are added in 1% pid solution in cepsetate I mix the glue mass until a homogeneous solution is obtained,
Оцеьку свойств кле производили н липких летах, Липкие ленты полу- ли на подложке из фторлакоткан СТФ (ТУ 1-92- 32-83) или лавсановой пленки методом пол- ива кле на фильеры. Сушку липких лент производили на воздухе при гемперагуре 85-95°С в течение 15 мин.The properties of adhesives were evaluated on sticky years. Adhesive tapes were woven on a substrate of STF fluorocarcotane (TU 1-92-32-83) or dacron film by pouring glue onto spinnerets. Adhesive tapes were dried in air at a hemisphere of 85-95 ° C for 15 minutes.
Адгезию липких лент оценивали по стойкости к действию статической кагоузки при сдвиге клеевых соединений липкой ленты , склеенной с фторлз: он-.. Площадь склеивани равмз 6 см .Adhesion of adhesive tapes was assessed by their resistance to the action of static kicking during shear of adhesive joints of adhesive tape glued to fluoride: it is .. The bonding area is 6 cm.
Склеенные образцы подвергали действию статической нагрузки раоной 0,3 кг в термошчаЛу npii заданной температура. Затем отмечали врем до полного разрушени клеевого соединени в минутахThe glued samples were subjected to a static load of 0.3 kg in a temperature range of npii. Then noted the time until the complete destruction of the adhesive in minutes
Свойства липких лент, полученных на основе составов 1-12, а также протошпа приведены в таблице.The properties of adhesive tapes obtained on the basis of compositions 1-12, as well as protoshpa are given in the table.
Данные, представленные в таблице, показывают сущее таенные преимущества предлагаемых составов липких Knees5, по сравнению с прототипом. Так, например, клеевыегсоединени липких лент на основе предлагаемых композиций выдерживают статическую нагрузку сдвига при темпераThe data presented in the table show the sheer secret advantages of the proposed sticky formulations Knees5, compared with the prototype. So, for example, adhesive joints of adhesive tapes based on the proposed compositions withstand static shear at temperature
5 5
0 0
5 5
5 5
0 0
00
туре +160°С без разрушени более ПООО мин, в то врем как образцы прототипа рушаютс точение 10-20 мич.round + 160 ° C without destroying more than POOO min, while the prototype samples were destroyed by turning 10-20 mich.
При этом адгези липких лент, определ ема как сопротивление отслаиванию, превышает адгезию прототипа (составы 1-5).Moreover, the adhesion of adhesive tapes, defined as peeling resistance, exceeds the adhesion of the prototype (compositions 1-5).
При необходимости, возможно регулирование Свойств клеч в зависимости от состава . Например, введение в состав клеевой композиции максимального количества жидкого каучука приводит к повышению ее адгезионных свойств (состав 5). Напротив, максимальное содержание эпоксидной смолы (состав 3} обеспечивает высокие когези- онные свойства. Предпочтительным вариантом вл етс композици состава 1, так как обладает комплексом оптимальных адгезионных и когезионных свойств.If necessary, it is possible to adjust the properties of the cures depending on the composition. For example, the introduction of the maximum amount of liquid rubber into the adhesive composition leads to an increase in its adhesive properties (composition 5). On the contrary, the maximum content of epoxy resin (composition 3} provides high cohesive properties. A preferred composition is composition 1, since it has a combination of optimal adhesive and cohesive properties.
Композиции составов 6-12 неэффективны , по сравнению с прототипом и предлагаемым композици ми составов 1-5, так как г.седение в композицию жидкого каучука и зпогчСидной смолы в количествах менее 40 и более 00 мае, ч. и менее 5 и более 35 мае. ч. соответственно, а также раздельное использование одного из перечисленных компонентов (жидкого каучука или эпоксидной смолы) не позвол ет получить липкие ком- полиции с одновременно высокими адгезионными и когезио ными свойствами,Compositions of compositions 6-12 are ineffective in comparison with the prototype and the proposed compositions of compositions 1-5, since the sitting in the composition of liquid rubber and svogsidnogo resin in quantities of less than 40 and more than 00 may, hours and less than 5 and more than 35 may . including, respectively, as well as the separate use of one of the listed components (liquid rubber or epoxy), it is not possible to obtain sticky polices with simultaneously high adhesive and cohesive properties,
(56) Клейка лента ТУ-17-794-85.(56) Adhesive tape TU-17-794-85.
Остаоы и cstit -TiD лиг -.«х чт ссчозе п едлагаемь х композиции контрольных и про-отипйOstoa and cstit-TiD leagues -. “Thu sschose n we offer x composition control and prototype
Продолжение таблицыTable continuation
Продолжение таблицыTable continuation
Claims (1)