RU2002104580A - Способ и состав для антикоррозионной обработки металлической подложки, предварительно защищенной слоем покрытия на основе цинка - Google Patents
Способ и состав для антикоррозионной обработки металлической подложки, предварительно защищенной слоем покрытия на основе цинкаInfo
- Publication number
- RU2002104580A RU2002104580A RU2002104580/02A RU2002104580A RU2002104580A RU 2002104580 A RU2002104580 A RU 2002104580A RU 2002104580/02 A RU2002104580/02 A RU 2002104580/02A RU 2002104580 A RU2002104580 A RU 2002104580A RU 2002104580 A RU2002104580 A RU 2002104580A
- Authority
- RU
- Russia
- Prior art keywords
- silane
- composition according
- layer
- paragraphs
- organic paint
- Prior art date
Links
- 239000000203 mixture Substances 0.000 title claims 17
- 238000000034 method Methods 0.000 title claims 14
- 239000000758 substrate Substances 0.000 title claims 10
- 239000011247 coating layer Substances 0.000 title claims 4
- 238000005260 corrosion Methods 0.000 title claims 3
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims 14
- NBIIXXVUZAFLBC-UHFFFAOYSA-N Phosphoric acid Chemical compound OP(O)(O)=O NBIIXXVUZAFLBC-UHFFFAOYSA-N 0.000 claims 12
- BLRPTPMANUNPDV-UHFFFAOYSA-N Silane Chemical compound [SiH4] BLRPTPMANUNPDV-UHFFFAOYSA-N 0.000 claims 12
- 229910000077 silane Inorganic materials 0.000 claims 12
- 239000010410 layer Substances 0.000 claims 11
- 239000003973 paint Substances 0.000 claims 10
- 229910052751 metal Inorganic materials 0.000 claims 9
- 239000002184 metal Substances 0.000 claims 9
- 239000000377 silicon dioxide Substances 0.000 claims 7
- 229910000147 aluminium phosphate Inorganic materials 0.000 claims 6
- KGBXLFKZBHKPEV-UHFFFAOYSA-N boric acid Chemical compound OB(O)O KGBXLFKZBHKPEV-UHFFFAOYSA-N 0.000 claims 6
- 239000004327 boric acid Substances 0.000 claims 6
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 claims 5
- 239000007864 aqueous solution Substances 0.000 claims 5
- 235000012239 silicon dioxide Nutrition 0.000 claims 5
- 239000011701 zinc Substances 0.000 claims 5
- 229910052725 zinc Inorganic materials 0.000 claims 5
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims 4
- 239000000080 wetting agent Substances 0.000 claims 4
- 238000005246 galvanizing Methods 0.000 claims 3
- 238000004073 vulcanization Methods 0.000 claims 3
- IGFHQQFPSIBGKE-UHFFFAOYSA-N 4-nonylphenol Polymers CCCCCCCCCC1=CC=C(O)C=C1 IGFHQQFPSIBGKE-UHFFFAOYSA-N 0.000 claims 2
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 claims 2
- PWHULOQIROXLJO-UHFFFAOYSA-N Manganese Chemical compound [Mn] PWHULOQIROXLJO-UHFFFAOYSA-N 0.000 claims 2
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 claims 2
- 239000004721 Polyphenylene oxide Substances 0.000 claims 2
- 239000011248 coating agent Substances 0.000 claims 2
- 238000000576 coating method Methods 0.000 claims 2
- 230000007797 corrosion Effects 0.000 claims 2
- 238000004070 electrodeposition Methods 0.000 claims 2
- -1 epoxysilanes Chemical class 0.000 claims 2
- 238000010438 heat treatment Methods 0.000 claims 2
- 229910052748 manganese Inorganic materials 0.000 claims 2
- 239000011572 manganese Substances 0.000 claims 2
- SNQQPOLDUKLAAF-UHFFFAOYSA-N nonylphenol Polymers CCCCCCCCCC1=CC=CC=C1O SNQQPOLDUKLAAF-UHFFFAOYSA-N 0.000 claims 2
- 229920000570 polyether Polymers 0.000 claims 2
- 230000005855 radiation Effects 0.000 claims 2
- 229910002016 Aerosil® 200 Inorganic materials 0.000 claims 1
- JOYRKODLDBILNP-UHFFFAOYSA-N Ethyl urethane Chemical compound CCOC(N)=O JOYRKODLDBILNP-UHFFFAOYSA-N 0.000 claims 1
- 229920000877 Melamine resin Polymers 0.000 claims 1
- 229910000831 Steel Inorganic materials 0.000 claims 1
- NIXOWILDQLNWCW-UHFFFAOYSA-N acrylic acid group Chemical group C(C=C)(=O)O NIXOWILDQLNWCW-UHFFFAOYSA-N 0.000 claims 1
- 239000000654 additive Substances 0.000 claims 1
- 239000000956 alloy Substances 0.000 claims 1
- 229910045601 alloy Inorganic materials 0.000 claims 1
- 238000005275 alloying Methods 0.000 claims 1
- 229910052782 aluminium Inorganic materials 0.000 claims 1
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims 1
- 238000005119 centrifugation Methods 0.000 claims 1
- 238000004132 cross linking Methods 0.000 claims 1
- 239000008367 deionised water Substances 0.000 claims 1
- 229910021641 deionized water Inorganic materials 0.000 claims 1
- 238000009792 diffusion process Methods 0.000 claims 1
- 238000007598 dipping method Methods 0.000 claims 1
- 238000001035 drying Methods 0.000 claims 1
- 238000001962 electrophoresis Methods 0.000 claims 1
- 230000006698 induction Effects 0.000 claims 1
- 238000005342 ion exchange Methods 0.000 claims 1
- 229910052742 iron Inorganic materials 0.000 claims 1
- VAKIVKMUBMZANL-UHFFFAOYSA-N iron phosphide Chemical compound P.[Fe].[Fe].[Fe] VAKIVKMUBMZANL-UHFFFAOYSA-N 0.000 claims 1
- 229910052759 nickel Inorganic materials 0.000 claims 1
- 239000002736 nonionic surfactant Substances 0.000 claims 1
- 125000000951 phenoxy group Chemical group [H]C1=C([H])C([H])=C(O*)C([H])=C1[H] 0.000 claims 1
- 229920002635 polyurethane Polymers 0.000 claims 1
- 239000004814 polyurethane Substances 0.000 claims 1
- 230000001681 protective effect Effects 0.000 claims 1
- 230000001698 pyrogenic effect Effects 0.000 claims 1
- 229920005989 resin Polymers 0.000 claims 1
- 239000011347 resin Substances 0.000 claims 1
- FZHAPNGMFPVSLP-UHFFFAOYSA-N silanamine Chemical class [SiH3]N FZHAPNGMFPVSLP-UHFFFAOYSA-N 0.000 claims 1
- WIJVUKXVPNVPAQ-UHFFFAOYSA-N silyl 2-methylprop-2-enoate Chemical class CC(=C)C(=O)O[SiH3] WIJVUKXVPNVPAQ-UHFFFAOYSA-N 0.000 claims 1
- 238000005507 spraying Methods 0.000 claims 1
- 239000010959 steel Substances 0.000 claims 1
- 239000004094 surface-active agent Substances 0.000 claims 1
- BPSIOYPQMFLKFR-UHFFFAOYSA-N trimethoxy-[3-(oxiran-2-ylmethoxy)propyl]silane Chemical group CO[Si](OC)(OC)CCCOCC1CO1 BPSIOYPQMFLKFR-UHFFFAOYSA-N 0.000 claims 1
- GPRLSGONYQIRFK-MNYXATJNSA-N triton Chemical compound [3H+] GPRLSGONYQIRFK-MNYXATJNSA-N 0.000 claims 1
- UKRDPEFKFJNXQM-UHFFFAOYSA-N vinylsilane Chemical class [SiH3]C=C UKRDPEFKFJNXQM-UHFFFAOYSA-N 0.000 claims 1
- LRXTYHSAJDENHV-UHFFFAOYSA-H zinc phosphate Chemical compound [Zn+2].[Zn+2].[Zn+2].[O-]P([O-])([O-])=O.[O-]P([O-])([O-])=O LRXTYHSAJDENHV-UHFFFAOYSA-H 0.000 claims 1
- 229910000165 zinc phosphate Inorganic materials 0.000 claims 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
- C23C28/32—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer
- C23C28/322—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer only coatings of metal elements only
- C23C28/3225—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer only coatings of metal elements only with at least one zinc-based layer
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
- C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
- C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
- C23C22/07—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing phosphates
- C23C22/08—Orthophosphates
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
- C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
- C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
- C23C22/48—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 not containing phosphates, hexavalent chromium compounds, fluorides or complex fluorides, molybdates, tungstates, vanadates or oxalates
- C23C22/53—Treatment of zinc or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
- C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
- C23C22/68—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous solutions with pH between 6 and 8
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
- C23C28/34—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates
- C23C28/345—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates with at least one oxide layer
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2222/00—Aspects relating to chemical surface treatment of metallic material by reaction of the surface with a reactive medium
- C23C2222/20—Use of solutions containing silanes
Landscapes
- Chemical & Material Sciences (AREA)
- Metallurgy (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Organic Chemistry (AREA)
- Inorganic Chemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Application Of Or Painting With Fluid Materials (AREA)
- Paints Or Removers (AREA)
- Laminated Bodies (AREA)
- Chemical Treatment Of Metals (AREA)
- Other Surface Treatments For Metallic Materials (AREA)
Claims (23)
1. Состав для антикоррозионной обработки металлической подложки, предварительно защищенной слоем покрытия на основе цинка, отличающийся тем, что он находится в форме водного раствора, содержащего, мас.%:
Вода 72 - 95
Силан 0,5 - 10
Борная кислота 0,5 - 3
Фосфорная кислота 0 - 3
Тонкоизмельченный диоксид кремни 1 - 10
Смачиватель 0,09 - 3
при условии, что сумма процентных содержаний борной кислоты и фосфорной кислоты не превосходит 5 мас.%.
2. Состав по п.1, отличающийся тем, что водный раствор на основе силана содержит, мас.%:
Вода 82 - 95
Силан 1 - 6
Борная кислота 0,5 - 3
Фосфорная кислота 0 - 3
Тонкоизмельченный диоксид кремния 2 - 6
Смачиватель 0,1 - 1
при условии, что сумма процентных содержаний борной кислоты и фосфорной кислоты не превосходит 5 мас.%.
3. Состав по любому из пп.1 и 2, отличающийся тем, что водный раствор на основе силана содержит, мас.%:
Вода 90
Силан 1 - 4
Борная кислота и/или фосфорная кислота 2,5
Тонкоизмельченный диоксид кремния 5
Смачиватель 0,1
4. Состав по любому из пп.1-3, отличающийся тем, что силан выбран среди аминосиланов, эпоксисиланов, винилсиланов, тиосиланов, метакрилоксисиланов, а также их смесей.
5. Состав по любому из пп.1-4, отличающийся тем, что силан представляет собой гамма-глицидоксипропилтриметоксисилан.
6. Состав по любому из пп.1-5, отличающийся тем, что тонкоизмельченный диоксид кремния представляет собой пирогенный или осажденный диоксид кремния.
7. Состав по любому из пп.1-6, отличающийся тем, что смачиватель представляет собой поверхностно-активное вещество неионного типа.
8. Состав по п.7, отличающийся тем, что неионное поверхностно-активное вещество представляет собой поверхностно-активный полиоксиэтилинированный нонилфенол.
9. Состав по любому из пп.1-8, отличающийся тем, что его рН доведен - величины, находящейся в интервале от 2 - 8.
10. Состав по п.9, отличающийся тем, что его рН доведен - величины, находящейся в интервале от 2 - 5.
11. Состав по любому из пп.1-10, отличающийся тем, что он содержит, мас.%:
Вода деионизованная 91,12
Борная кислота 2,09
Силан (Эпоксисилан) 1,89
Диоксид кремния Aerosil® 200 4,69
Фосфорная кислота 0,12
Полиэтоксилированный нонилфенол
Triton® CF 54 (NP) 0,09
12. Способ антикоррозионной обработки металлической подложки, предварительно защищенной слоем покрытия на основе цинка, отличающийся тем, что на поверхность вышеупомянутой подложки наносят состав по любому из пп.1-11, а затем вышеупомянутую подложку с нанесенным составом сушат и/или вулканизируют при помощи конвективного нагрева, индукционного нагрева или инфракрасного излучения.
13. Способ по п.12, отличающийся тем, что нанесение состава по любому из пп.1-10 осуществляется во время первой стадии обработки, которая сопровождается второй стадией окончательной обработки, заключающейся в нанесении слоя органической краски, обладающей специфическими свойствами.
14. Способ по любому из пп.12 и 13, отличающийся тем, что водный раствор на основе силана применяют путем нанесения на вышеупомянутую подложку покрытия в холодном состоянии, в частности, распылением, путем нанесения валиком или, в случае необходимости, путем окунания с последующим центрифугированием или без него.
15. Способ по п.12, отличающийся тем, что температура сушки и/или вулканизации больше приблизительно 100°С и, предпочтительно, находится в интервале от 220 - 260°С.
16. Способ по п.15, отличающийся тем, что операция вулканизации, предназначенная для обеспечения сшивания силана, содержащегося в водном растворе на основе силана, применяемом на первой стадии обработки, производится во время второй стадии вулканизации слоя органической краски для окончательной отделки.
17. Способ по любому из пп.13-16, отличающийся тем, что слой органической краски, наносимый во время второй стадии, получают при помощи краски на основе смолы, выбираемой среди акриловых, полиуретановых, полиэфируретановых, эпоксиуретановых, феноксильных, полиэфирмеламиновых смол, а также их смесей.
18. Способ по любому из пп.13-17, отличающийся тем, что слой органической краски выбирают таким образом, чтобы металлическая подложка приобрела такие свойства, как пригодность для придания формы, повышенная коррозионная стойкость, свариваемость, пригодность для склеивания, пригодность для повторного лакирования, способность к восприятию слоя краски, наносимой методом электроосаждения, в частности, методом катафореза, повышенная устойчивость к действию ультрафиолетового излучения, улучшенные свойства с точки зрения цвета и глянца.
19. Способ по любому из пп.13-18, отличающийся тем, что между слоем покрытия на основе силана и отделочным слоем органической краски интеркалируют грунтовочный слой, предназначенный для улучшения адгезионных свойств и/или коррозионной стойкости металлической подложки.
20. Способ по п.19, отличающийся тем, что отделочный слой органической краски и/или интеркалированный грунтовочный слой содержат добавки, улучшающие антикоррозионные свойства, в частности, фосфат цинка (в известных случаях модифицированный) и/или функционализованные диоксиды кремния с ионообменными свойствами.
21. Способ по любому из пп.13-20, отличающийся тем, что для улучшения антикоррозионных свойств в отделочный слой органической краски добавлен цинк и/или марганец.
22. Способ по п.21, отличающийся тем, что для обеспечения свариваемости металлических подложек, обработанных данным способом, отделочный слой органической краски содержит фосфид железа.
23. Способ по любому из пп.13-22, отличающийся тем, что металлическая подложка представляет собой высокопрочную сталь или высокопрочный сплав, в частности, листовой металл, подвергнутый предварительной защитной обработке чистым цинком методом электролитического цинкования или горячего цинкования, или цинком, легированным другим металлом, выбранным среди железа, никеля, марганца и алюминия, методом электроосаждения или горячего цинкования с диффузией вышеупомянутого другого легирующего металла.