Abstract

FIELD: building materials industry, methods of sheet decorating materials production in particular. SUBSTANCE: method provides for application on base of pattern, of several layers of different pigments and drying. In the case after application of first layer of pigment on base surface it is subjected to drying under room temperature for one hour and then painted surface is subjected to pattern embossing. Then the surface is once more covered by layer of other color pigment with following its removal from protrusions. Then the sheet is dried under room temperature till full drying. To increase polychromy and polypattern, cycle of painted surface embossing by new pattern and covering it with other color pigment is repeated several times between drying stages. Due to the operations method of decorating sheet material allows to simplify and to make cheaper production process. EFFECT: decreased costs and simplified production process. 2 cl

Description

Изобретение относится к строительным материалам и покрытиям, в частности к изготовлению листового декоративного материала. The invention relates to building materials and coatings, in particular to the manufacture of sheet decorative material.

Известен способ получения декоративного рулонного материала [1] заключающийся в одновременном разматывании с рулонов полотен бумаги-основы, пропитки их смолой, предварительном соединении их по плоскостям между собой и одновременном удалении избытков смолы горячим прессованием путем пропускания полотен между бесконечной лентой и вращающимся обогреваемым барабаном, в сматывании спрессованного полотна в рулон с последующей выдержкой, отличающийся тем, что с целью повышения качества и производительности труда, прессование осуществляют при t 100-140^oC, удельном давлении 1,6-4,0 кГ/см² и скорости вращения барабана 0,5-3,0 об/мин, при этом выдержка осуществляется посредством помещения готового рулонного материала в термокамеру при t 80-120^oC в течение 0,5-1,0 ч.There is a method of producing decorative roll material [1] which consists in simultaneously unwinding the base paper from the rolls, impregnating them with resin, pre-connecting them on planes with each other and simultaneously removing excess resin by hot pressing by passing the canvases between an endless ribbon and a rotating heated drum, in winding the pressed web into a roll with subsequent exposure, characterized in that in order to improve the quality and productivity, pressing is carried out at t 100-140 ^o C, specific pressure 1.6-4.0 kg / cm ² and drum rotation speed 0.5-3.0 rpm, while exposure is carried out by placing the finished roll material in a heat chamber at t 80 -120 ^o C for 0.5-1.0 hours

Недостатком такого способа является сложность и относительная высокая стоимость процесса производства вследствии использования в процессе дорогой смолы и необходимости осуществления подогрева при температуре много большей комнатной. The disadvantage of this method is the complexity and the relatively high cost of the production process due to the use of expensive resin in the process and the need for heating at a temperature much higher than room temperature.

Известен такой способ художественной отделки изделий из древесины [2] заключающийся в подготовке поверхности изделия, нанесении рисунка через трафарет на изделие посредством перемещения последнего в поперечном направлении относительно вращающихся красящих валков с эластичным покрытием и последующим удалении трафарета с поверхности изделия. There is such a method of artistic decoration of wood products [2] consisting in preparing the surface of the product, applying a picture through a stencil to the product by moving the latter in the transverse direction relative to the rotating painting rolls with an elastic coating and then removing the stencil from the surface of the product.

Недостатком такого способа является сложность отделки и низкое качество покрытия вследствие необходимости в последующем после окраски удалять трафарет, что не исключает подтеков красителя. The disadvantage of this method is the complexity of the finish and poor quality of the coating due to the need to subsequently remove the stencil after painting, which does not exclude smudges of the dye.

Известен также способ изготовления декоративного материала [3] принятый за прототип, заключающийся в том, что на материал наносят предварительный слой краски или покрытия одного цвета, полностью просушивают, после чего наносят слой покрытия другого цвета и пропускают материал через тиснильный валок с осуществленным узором. Рисунок тиснения, имеющийся на валике, дает повторяющийся рисунок на покрытии. Видимый в местах контакта с приподнятыми участками предварительный слой дает контрастный цвет. Меняя скорость вращения валика во время тиснения, можно менять повторяющуюся длину рисунка. Затем покрытие высушивают. Недостатком данного способа является удорожание материала вследствие необходимости полной просушки материала после первого покрытия. There is also a known method of manufacturing a decorative material [3] adopted as a prototype, which consists in the fact that a preliminary layer of paint or coating of one color is applied to the material, completely dried, after which a coating layer of a different color is applied and the material is passed through an embossing roller with a pattern. The embossing pattern available on the roller gives a repeating pattern on the coating. The preliminary layer visible at the points of contact with elevated areas gives a contrasting color. By changing the speed of rotation of the roller during stamping, you can change the repeating length of the pattern. Then the coating is dried. The disadvantage of this method is the cost of material due to the need for complete drying of the material after the first coating.

Целью изобретения является удешевление способа изготовления декоративного материала и расширение гаммы используемых узоров и цветов. The aim of the invention is to reduce the cost of manufacturing a decorative material and expanding the range of patterns and colors used.

Цель достигается тем, что тиснение заданного декоративного узора выполнят после нанесения первого слоя краски заданной цветности и предварительного выдерживания его до неполного высыхания при комнатной температуре, а после нанесения краски другого цвета осуществляют ее снятие с поверхности выступов узора перед окончательной сушкой. Для увеличения узорчатости и многоцветья до выполнения окончательной сушки операции тиснения дополнительных узоров и покрытия слоями различных цветов со снятием их с поверхностей выступов циклически повторяют. The goal is achieved by embossing a given decorative pattern after applying the first layer of paint of a given color and pre-curing it until it dries partially at room temperature, and after applying a different color paint, it is removed from the surface of the protrusions of the pattern before final drying. To increase the patterning and multicolor before performing the final drying, the operations of embossing additional patterns and coating with layers of various colors with their removal from the surfaces of the protrusions are cyclically repeated.

Способ осуществляется следующим образом. The method is as follows.

Для основы берется лист каландрированного картона толщиной 3-5 мм, шириной равной длине узорчатых вальцев станка, например, 1,0-1,5 м. Затем на поверхность листа наносят пульверизатором или кистью первый слой краски, например, эмали НЦ-251 светлого оттенка толщиной не более 1,5 мм. Окрашенную поверхность просушивают при комнатной температуре до неполного высыхания, например, при 18-20^oC в течение 1 ч.For the base, a sheet of calendared cardboard with a thickness of 3-5 mm, a width equal to the length of the patterned rollers of the machine, for example, 1.0-1.5 m, is taken. Then, the first paint coat, for example, NTs-251 enamel of light shade, is sprayed or brushed on the sheet surface. no more than 1.5 mm thick. The painted surface is dried at room temperature until incomplete drying, for example, at 18-20 ^o C for 1 hour

Затем лист размещают окрашенной поверхностью к вальцу с узором. Поверхность листа с нанесенным узором после вальцевания покрывают такой же краской (эмаль НЦ-251) другого цвета, например коричневого и скребком снижают слой нанесенной краски на глубину открытия выступов узора от первого тиснения. После этого лист укладывают на стеллаж и просушивают до полного высыхания красителей при комнатной температуре. Для увеличения узорчатости и многоцветья рисунка, лист окрашенный вторым цветом, после снятия этой краски с выступов первого узора просушивают в течение часа и затем пропускают через вальцы станка с другим узором, покрывают краской третьего цвета и снимают излишки с новых выступов. Затем либо высушивают лист до полного высыхания либо цикл повторяют с новым узором на вальце и другим цветом краски. Все просушки осуществляют при комнатной температуре 18-20^oC.Then the sheet is placed with a painted surface to the roll with a pattern. After rolling, the surface of the sheet with the printed pattern is coated with the same paint (NTs-251 enamel) of a different color, for example brown and the layer of applied paint is reduced to the depth of opening of the protrusions of the pattern from the first embossing. After that, the sheet is laid on a shelf and dried until the dyes completely dry at room temperature. To increase the patterning and multi-color of the pattern, the sheet painted in the second color, after removing this paint from the protrusions of the first pattern, is dried for an hour and then passed through the rollers of a machine with a different pattern, covered with a third color of paint and the excess is removed from the new protrusions. Then, either dry the sheet to dry completely or repeat the cycle with a new pattern on the roller and a different color of paint. All drying is carried out at room temperature 18-20 ^o C.

Таким образом создается многоцветная и многоузорчатая поверхность декоративного листового материал и за счет улучшения потребительских качеств и сокращения цикла просушки происходит удешевление материала. Thus, a multicolor and multicolored surface of the decorative sheet material is created, and due to the improvement of consumer qualities and the reduction of the drying cycle, the material is cheaper.

Claims

1. A method of manufacturing a decorative sheet material, which consists in applying two layers of paint of various colors with interlayer and final drying to the base surface and embossing a given decorative pattern, characterized in that the embossing is carried out after applying the first paint layer, previously keeping it until incomplete drying room temperature, and after applying a paint of a different color, it is removed from the surface of the protrusions of the pattern before final drying.

2. The method according to claim 1, characterized in that until the final drying operation, the embossing of additional patterns and coating layers of paints of various colors with their removal from the surfaces of the protrusions is cyclically repeated.