KR20190037412A - Method of manufacturing composite polymer electrolyte membrane and fuel cell - Google Patents
Method of manufacturing composite polymer electrolyte membrane and fuel cell Download PDFInfo
- Publication number
- KR20190037412A KR20190037412A KR1020170126693A KR20170126693A KR20190037412A KR 20190037412 A KR20190037412 A KR 20190037412A KR 1020170126693 A KR1020170126693 A KR 1020170126693A KR 20170126693 A KR20170126693 A KR 20170126693A KR 20190037412 A KR20190037412 A KR 20190037412A
- Authority
- KR
- South Korea
- Prior art keywords
- solution
- electrolyte membrane
- polymer electrolyte
- acid group
- ionic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
본 발명은 복합 고분자 전해질막 제조방법 및 연료전지에 관한 것으로, 더욱 상세하게는 저가습 또는 무가습 조건에서도 사용 가능한 복합 고분자 전해질막 제조방법 및 연료전지에 관한 것이다.The present invention relates to a method for producing a composite polymer electrolyte membrane and a fuel cell, and more particularly, to a method for producing a composite polymer electrolyte membrane and a fuel cell that can be used under low humidity or no humidification conditions.
연료전지는 연료의 화학에너지가 전기화학반응에 의해 전기에너지로 직접 변화하는 기술을 이용하는 발전장치로서, 수소와 공기 중의 산소를 각각 고분자 전해질막 양측에 제공되는 연료극과 공기극에 공급하여 연속적으로 전기를 생산하는 전기화학적 발전장치이다. A fuel cell is a power generation device that utilizes a technique in which the chemical energy of a fuel is directly changed into electrical energy by an electrochemical reaction and supplies hydrogen and oxygen in the air to the fuel and air electrodes provided on both sides of the polymer electrolyte membrane, It is an electrochemical power generation device that produces electricity.
연료전지의 고분자 전해질막은 수소이온의 이동과 함께 연료극과 공기극을 분리시키는 중요한 역할을 하며, 이를 위하여 높은 수소이온 전도, 낮은 연료 투과도 및 물의 이동 등의 특성을 가져야한다. 일반적으로 사용되는 고분자 전해질막으로는 퍼플루오르술폰산을 사용한 나피온 막이 있는데, 종래의 나피온 막은 물을 매개체로 하여 이온 전도를 유지하기 때문에 연료전지 작동 온도가 90℃ 이하에서만 사용 가능하다는 문제가 있으며, 특히 100℃ 이상의 온도와 50% 이하의 낮은 가습 조건에서 기계적 및 열적 안정성, 수소 이온 전도도 등의 특성 감소로 인하여 연료전지의 성능이 급격하게 저하되는 문제점이 있다.The polymer electrolyte membrane of the fuel cell plays an important role in separating the fuel electrode and the air electrode together with the movement of the hydrogen ion. For this purpose, the polymer electrolyte membrane should have high hydrogen ion conductivity, low fuel permeability, and water migration. As a polymer electrolyte membrane commonly used, there is a Nafion membrane using perfluorosulfonic acid. The conventional Nafion membrane retains ion conduction by using water as a medium, so that the fuel cell operating temperature can be used only at 90 ° C or lower The performance of the fuel cell is drastically deteriorated due to the reduction of the characteristics such as mechanical and thermal stability and proton conductivity at a temperature of 100 ° C or higher and a low humidification condition of 50% or lower.
나피온 막의 수소이온의 전도성을 유지하기 위해서는 가습으로 인한 수분 공급 및 유지가 필수적이며, 일반적인 연료전지 시스템에서는 수분 공급 및 나피온 막의 습도를 유지하기 위해 연료가스가 수분을 포함한 상태로 연료극에 공급되도록 별도의 가습기를 구비하고 있다. 하지만, 가습기의 설치 및 가습기에 필요한 주변부품으로 인해 연료전지의 규격이 커지면서 구조가 복합해지고 제작 및 유지 보수 비용이 증가하게 되는 문제점이 존재하게 된다.In order to maintain the conductivity of the hydrogen ion of the Nafion membrane, moisture supply and maintenance due to humidification are essential. In a typical fuel cell system, in order to maintain the humidity of the water supply and Nafion membrane, the fuel gas is supplied to the fuel electrode And a separate humidifier is provided. However, due to the installation of the humidifier and the surrounding components required for the humidifier, the size of the fuel cell is increased and the structure becomes complicated and the manufacturing and maintenance costs increase.
본 발명은 저가습 또는 무가습 조건에서도 사용 가능한 복합 고분자 전해질막 제조방법 및 연료전지를 제공한다.The present invention provides a method for producing a composite polymer electrolyte membrane and a fuel cell which can be used under low humidity or no humidification conditions.
본 발명의 실시예에 따른 복합 고분자 전해질막 제조방법은 인산기를 포함하는 이온성 용액을 제조하는 과정; 상기 이온성 용액에 술폰산기를 갖는 용액을 첨가한 후 교반하여 혼합용액을 제조하는 과정; 및 상기 혼합용액을 주조한 후 건조시키는 과정을 포함할 수 있다.A method for preparing a composite polymer electrolyte membrane according to an embodiment of the present invention includes the steps of preparing an ionic solution containing a phosphoric acid group; Adding a solution having a sulfonic acid group to the ionic solution, and then stirring to prepare a mixed solution; And casting and drying the mixed solution.
상기 건조시키는 과정 이전에, 상기 혼합용액에 상기 복합 고분자 전해질막에 기계적 물성을 부여하는 고분자 용액을 추가하는 과정을 더 포함할 수 있다.The method may further include a step of adding a polymer solution for imparting mechanical properties to the mixed polymer electrolyte membrane before the drying process.
상기 고분자 용액은 폴리이미드계 고분자, 폴리에테르계 고분자, 폴리아릴렌계 고분자 및 폴리페닐렌계 고분자 중 적어도 어느 하나를 포함할 수 있다.The polymer solution may include at least one of a polyimide-based polymer, a polyether-based polymer, a polyarylene-based polymer, and a polyphenylene-based polymer.
상기 술폰산기를 갖는 용액은 퍼플루오로설폰산 용액일 수 있다.The solution containing the sulfonic acid group may be a perfluorosulfonic acid solution.
상기 인산기를 포함하는 이온성 용액을 제조하는 과정은, 1,2-디메틸이미다졸과 1-브로모부탄을 교반한 후 건조시켜 생성물을 형성하는 과정; 상기 생성물을 아세토아니트릴과 인산 용액에 용해시킨 후 교반시키는 과정; 및 상기 아세토아니트릴을 휘발시키는 과정을 포함할 수 있다.The process for preparing an ionic solution containing the phosphoric acid group comprises the steps of stirring 1,2-dimethylimidazole and 1-bromobutane and drying to form a product; Dissolving the product in an acetonitrile and a phosphoric acid solution, and stirring the resultant; And a step of volatilizing the acetanthrityl.
상기 인산기를 포함하는 이온성 용액은 DMBulmH2PO4 이온성 용액일 수 있다.The ionic solution containing the phosphate group may be a DMBulmH 2 PO 4 ionic solution.
상기 1,2-디메틸이미다졸과 1-브로모부탄을 교반하는 과정 및 상기 생성물을 용해시킨 후 교반시키는 과정은 상온 및 불활성 가스 분위기에서 수행될 수 있다.The process of stirring the 1,2-dimethylimidazole and 1-bromobutane, and dissolving and stirring the product may be performed at room temperature and in an inert gas atmosphere.
본 발명의 다른 실시예에 따른 연료전지는 연료가스를 공급받고, 수소의 산화반응이 이루어지는 연료극; 상기 연료극과 대응되며 산소의 환원반응이 이루어지는 공기극; 및 인산기와 술폰산기를 동시에 가지는 수소이온 전도성 고분자 및 기계적 물성을 부여하는 고분자를 포함하고, 상기 연료극과 공기극 사이에 배치되어 상기 연료극으로부터 공기극으로 수소 이온이 이동하는 복합 고분자 전해질막을 포함할 수 있다.According to another aspect of the present invention, there is provided a fuel cell comprising: a fuel electrode to which a fuel gas is supplied and an oxidation reaction of hydrogen is performed; An air electrode corresponding to the fuel electrode and performing a reduction reaction of oxygen; And a composite polymer electrolyte membrane including a hydrogen-ion conductive polymer having both a phosphoric acid group and a sulfonic acid group, and a polymer imparting mechanical properties, and disposed between the fuel electrode and the air electrode and moving hydrogen ions from the fuel electrode to the air electrode.
상기 복합 고분자 전해질막은 인산기를 포함하는 이온성 용액, 술폰산기를 갖는 용액 및 고분자 용액을 혼합한 혼합용액을 주조 및 건조시켜 형성될 수 있다.The composite polymer electrolyte membrane may be formed by casting and drying a mixed solution obtained by mixing an ionic solution containing a phosphate group, a solution having a sulfonic acid group, and a polymer solution.
상기 연료가스는 상기 연료극에 수분을 공급하기 위한 추가 가습 없이 상기 연료극에 공급될 수 있다.The fuel gas may be supplied to the fuel electrode without further humidification for supplying moisture to the fuel electrode.
상기 복합 고분자 전해질막은 상온 내지 200℃의 온도 범위에서 사용될 수 있다.The composite polymer electrolyte membrane may be used at a temperature ranging from room temperature to 200 ° C.
상기 수소 이온은 상기 복합 고분자 전해질막에 의해 저가습 또는 무가습 조건에서도 이동할 수 있다.The hydrogen ions can move under the low humidification condition or the no humidification condition by the composite polyelectrolyte membrane.
상기 복합 고분자 전해질막은 150μm 내지 250μm의 두께를 가질 수 있다.The composite polymer electrolyte membrane may have a thickness of 150 탆 to 250 탆.
본 발명에서는 술폰산기와 인산기를 동시에 가지는 복합 고분자 전해질막을 제조함으로써 100℃ 이상의 온도와 무가습 또는 저가습 조건에서도 술폰산기 및 인산기를 통한 양이온 교환 전달이 매우 용이해질 수 있다. 이온 전도를 위한 메커니즘이 물에 의존하지 않으므로 별도의 가습기가 필요하지 않으며 이에 단순한 연료전지 시스템 구성이 가능해질 수 있다.In the present invention, by preparing a composite polymer electrolyte membrane having both a sulfonic acid group and a phosphoric acid group at the same time, the exchange of the cation exchange through the sulfonic acid group and the phosphoric acid group can be facilitated even at a temperature of 100 ° C or higher and no humidification or low humidity. Since the mechanism for ion conduction does not depend on water, a separate humidifier is not necessary and a simple fuel cell system configuration can be made possible.
또한, 복합 고분자 전해질막을 100℃ 이상의 온도에서도 사용할 수 있음으로써 연료전지의 작동 온도를 높여 더 높은 연료 효율로 인한 연료전지의 출력값을 높일 수 있다. Also, since the composite polymer electrolyte membrane can be used at a temperature of 100 ° C or higher, the operating temperature of the fuel cell can be increased to increase the output value of the fuel cell due to higher fuel efficiency.
도 1은 본 발명의 실시예에 따른 복합 고분자 전해질막의 제조방법을 나타내는 순서도.
도 2는 본 발명의 실시예에 따른 복합 고분자 전해질막의 온도에 따른 이온 전도도를 나타내는 그래프.
도 3은 본 발명의 실시예에 따른 복합 고분자 전해질막의 전류 밀도에 따른 전압 및 출력 밀도를 나타내는 그래프.
도 4는 본 발명의 실시예에 따른 인산기를 포함하는 이온성 용액의 함량에 따른 복합 고분자 전해질막의 온도 대 이온 전도도를 나타내는 그래프.
도 5는 본 발명의 실시예에 따른 인산기를 포함하는 이온성 용액의 함량에 따른 복합 고분자 전해질막의 전류 밀도 대 전압 및 출력 밀도를 나타내는 그래프.1 is a flow chart showing a method of manufacturing a composite polymer electrolyte membrane according to an embodiment of the present invention.
2 is a graph showing ionic conductivity of a composite polymer electrolyte membrane according to an embodiment of the present invention.
3 is a graph showing voltage and power density according to current density of a composite polymer electrolyte membrane according to an embodiment of the present invention.
4 is a graph showing the temperature versus ionic conductivity of a composite polymer electrolyte membrane according to the content of an ionic solution containing a phosphate group according to an embodiment of the present invention.
5 is a graph showing current density versus voltage and power density of a composite polymer electrolyte membrane according to the content of an ionic solution including a phosphate group according to an embodiment of the present invention.
이하, 첨부된 도면을 참조하여 본 발명의 실시 예를 더욱 상세히 설명하기로 한다. 그러나 본 발명은 이하에서 개시되는 실시 예에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시 예들은 본 발명의 개시가 완전하도록 하며, 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이다. 발명을 상세하게 설명하기 위해 도면은 과장될 수 있고, 도면상에서 동일 부호는 동일한 요소를 지칭한다.Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings. It will be apparent to those skilled in the art that the present invention may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, It is provided to let you know. To illustrate the invention in detail, the drawings may be exaggerated and the same reference numbers refer to the same elements in the figures.
도 1은 본 발명의 실시예에 따른 복합 고분자 전해질막의 제조방법을 나타내는 순서도이다.1 is a flowchart showing a method for producing a composite polymer electrolyte membrane according to an embodiment of the present invention.
도 1을 참조하면, 본 발명의 실시예에 따른 복합 고분자 전해질막 제조방법은 인산기를 포함하는 이온성 용액을 제조하는 과정; 상기 이온성 용액에 술폰산기를 갖는 용액을 첨가한 후 교반하여 혼합용액을 제조하는 과정; 및 상기 혼합용액을 주조한 후 건조시키는 과정을 포함할 수 있다.Referring to FIG. 1, a method for fabricating a composite polymer electrolyte membrane according to an embodiment of the present invention includes the steps of preparing an ionic solution containing a phosphoric acid group; Adding a solution having a sulfonic acid group to the ionic solution, and then stirring to prepare a mixed solution; And casting and drying the mixed solution.
본 발명에서는 이온 전도를 위한 메커니즘이 물에 의존하지 않고, 100℃ 이상의 온도와 저가습 또는 무가습 조건에서도 이온 전도가 가능한 고분자 전해질막을 제조하기 위하여 인산기를 포함하는 이온성 용액 및 술폰산기를 갖는 용액을 사용하여 100℃ 이상에서 물이 존재하지 않은 환경에서도 양이온 교환 전달을 가능하게 할 수 있는 복합 고분자 전해질막을 제조하였다.In the present invention, in order to produce a polymer electrolyte membrane which does not depend on water for ion conduction and which can conduct ions even at a temperature of 100 ° C or higher and under a low humidity or no humidification condition, a solution containing a phosphoric acid group and a solution containing a sulfonic acid group A composite polymer electrolyte membrane capable of allowing cation exchange exchange even in an environment where water is not present at 100 ° C or higher was prepared.
먼저, 복합 고분자 전해질막을 제조하기 위해 인산기를 포함하는 이온성 용액을 제조할 수 있다(S100). 이때, 인산기를 포함하는 이온성 용액을 제조하는 과정은 1,2-디메틸이미다졸과 1-브로모부탄을 교반한 후 건조시켜 생성물을 형성하는 과정; 상기 생성물을 아세토아니트릴과 인산 용액에 용해시킨 후 교반시키는 과정; 및 상기 아세토아니트릴을 휘발시키는 과정을 포함할 수 있다.First, an ionic solution containing a phosphate group may be prepared to prepare a composite polymer electrolyte membrane (S100). At this time, the process for preparing an ionic solution containing a phosphoric acid group is a process in which 1,2-dimethylimidazole and 1-bromobutane are stirred and dried to form a product; Dissolving the product in an acetonitrile and a phosphoric acid solution, and stirring the resultant; And a step of volatilizing the acetanthrityl.
보다 자세히 살펴보면, 상온 및 불활성 가스 예를 들어, 아르곤 가스 분위기에서 1,2-디케틸이미다졸과 1-브로모부탄을 1:1로 리플럭스 및 교반을 12시간 진행하였으며, 교반이 완료되면 세척 및 건조시켜 생성물을 형성하였다. 건조에 의해 생성된 생성물을 아세토아니트릴과 인산 용액에 용해시킨 후 상온 및 아르곤 가스 분위기에서 48시간 교반을 진행하였으며, 교반이 완료되면 용매인 아세토아니트릴을 휘발시켜 인산기가 포함된 DMBulmH2PO4 이온성 용액을 제조하였다.More specifically, reflux and stirring were carried out for 1 hour at room temperature and an inert gas such as argon gas atmosphere in 1,2-dicetylimidazole and 1-bromobutane for 12 hours, Washed and dried to form the product. The product produced by drying was dissolved in acetonitrile and a phosphoric acid solution, and stirred at room temperature and argon gas atmosphere for 48 hours. When the stirring was completed, acetonitrile as a solvent was volatilized and DMBulmH 2 PO 4 Ionic solution.
인산기를 포함하는 이온성 용액이 최종적으로 제조되면, 이온성 용액을 이용한 복합 고분자 전해질막을 제조하기 위해 이온성 용액에 유기용매 예를들어 DMF 용매를 분산시켜 24시간 교반하였으며, 교반이 완료되면 술폰산기를 갖는 용액을 첨가하여 24시간 교반을 추가로 진행하여 혼합용액을 제조하였다(S200). 이때, 술폰산기를 갖는 용액은 퍼플루오로술폰산 용액일 수 있다. 인산기를 포함하는 이온성 용액에 퍼플루오로술폰산 용액이 첨가되어 제조된 혼합용액에는 수소 이온 교환기인 인산기와 술폰산기가 동시에 존재하게 되는데, 술폰산기는 가습 등으로 인한 물이 존재할 시 친수성의 술폰산기(또는 황산기)에 존재하는 복합 이온이라 불리는 친수성 부분을 통해 수소 이온 등의 양이온 교환 전달이 일어날 수 있다. When an ionic solution containing a phosphoric acid group is finally prepared, an organic solvent such as DMF solvent is dispersed in an ionic solution to prepare a composite polymer electrolyte membrane using an ionic solution, and the mixture is stirred for 24 hours. When stirring is completed, Was added, followed by further stirring for 24 hours to prepare a mixed solution (S200). At this time, the solution having a sulfonic acid group may be a perfluorosulfonic acid solution. In the mixed solution prepared by adding the perfluorosulfonic acid solution to the ionic solution containing the phosphoric acid group, the hydrogen ion exchanger phosphoric acid group and the sulfonic acid group are simultaneously present. When water due to humidification or the like is present, the sulfonic acid group Cation exchange exchange of hydrogen ions or the like can occur through a hydrophilic moiety called a complex ion present in the sulfate group.
하지만, 친수성의 술폰산기만을 가지는 나피온 막이 연료전지의 고분자 전해질막으로 사용될 경우 나피온 막은 물을 매개체로 하여 이온 전도를 유지하기 때문에 연료전지 작동 온도가 90℃ 이하에서만 사용가능하다는 문제가 있으며, 특히 100℃ 이상의 온도와 50% 이하의 낮은 가습 조건에서 기계적 및 열적 안정성, 수소 이온 전도도 등의 특성 감소로 인하여 연료전지의 성능이 급격하게 저하되는 문제점이 존재하게 된다. 100℃ 이상의 온도와 저가습 또는 무가습 조건에서 수소이온의 전도성을 유지하기 위해 수분 공급 및 나피온 막의 습도 유지는 필수적이며 이를 위해 연료가스가 수분을 포함한 상태로 연료극에 공급되도록 별도의 가습기를 구비하게 된다. 하지만, 가습기의 설치 및 가습기에 필요한 주변부품으로 인해 연료전지의 부피 및 무게 증가에 따른 불편함이 발생하는 문제점이 발생한다.However, when a Nafion membrane having only a hydrophilic sulfonic acid group is used as a polymer electrolyte membrane of a fuel cell, the Nafion membrane maintains ion conduction by using water as a medium. Therefore, there is a problem that the fuel cell operating temperature can be used only at 90 ° C or less, Particularly, there is a problem that the performance of the fuel cell is drastically deteriorated due to the decrease in characteristics such as mechanical and thermal stability and hydrogen ion conductivity at a temperature of 100 ° C or higher and a low humidification condition of 50% or lower. In order to maintain the conductivity of the hydrogen ion at a temperature of 100 ° C or more and low humidification or no humidification, it is essential to maintain the humidity of the Nafion membrane. To this end, a separate humidifier is provided to supply the fuel gas to the fuel electrode . However, there arises a problem that inconvenience arises due to the volume and weight increase of the fuel cell due to the installation of the humidifier and peripheral parts required for the humidifier.
본 발명에서는 술폰산기 뿐만 아니라 인산기를 동시에 가지는 복합 고분자 전해질막을 제조하기 위해서 열적 및 전기화학적 성질, 이온 전도 등이 가능하여 높은 전해질 특성을 나타낼 수 있는 인산기를 포함하는 이온성 용액을 제조한 뒤 퍼플루오로술폰산 용액에 혼합하여 복합 고분자 전해질막을 형성하였으며, 이로부터 이온성 용액의 인산기와 퍼플루오로설폰산 용액의 술폰산기가 이온의 이동에 관여하게 되어 100℃ 이상의 온도 및 저가습 또는 무가습 조건에서도 높은 이온 전도를 나타낼 수 있게 된다.In the present invention, in order to produce a composite polymer electrolyte membrane having both a sulfonic acid group and a phosphoric acid group at the same time, an ionic solution containing a phosphate group capable of exhibiting thermal and electrochemical properties, ion conduction, The sulfonic acid group of the ionic solution and the sulfonic acid group of the perfluorosulfonic acid solution are involved in the movement of the ions, so that the ionic solution of the ionic solution and the high Ion conduction can be expressed.
인산기를 포함하는 이온성 용액, 술폰산기를 갖는 용액이 혼합된 혼합용액을 제조한 뒤, 복합 고분자 전해질막을 형성할 때 구조적으로 막을 형성하고, 전해질막에 기계적 물성을 부여하여 형성된 막이 높은 기계적 강도를 가질 수 있도록 혼합용액에 고분자 용액을 추가하였고, 고분자 용액은 폴리이미드계 고분자, 폴리에테르계 고분자, 폴리아릴렌계 고분자 및 폴리페닐렌계 고분자 중 적어도 어느 하나를 포함할 수 있다. An ionic solution containing a phosphoric acid group or a solution having a sulfonic acid group is prepared and then a membrane is structurally formed when a composite polymer electrolyte membrane is formed and a membrane formed by imparting mechanical properties to an electrolyte membrane has a high mechanical strength And the polymer solution may include at least one of a polyimide-based polymer, a polyether-based polymer, a polyarylene-based polymer, and a polyphenylene-based polymer.
인산기를 포함하는 이온성 용액, 술폰산기를 갖는 용액 및 고분자 용액을 혼합한 혼합용액을 제조한 뒤, 혼합용액을 유리 페트리 접시에 주조한 후 건조하면(S300) 최종적으로 본 발명의 실시예에 따른 복합 고분자 전해질막이 제조될 수 있다. 제조된 용액을 주조한 후 건조하는 용액-주조 방식은 통상의 방식에 따라 이루어지는 바, 별도의 설명은 생략하기로 한다.A mixed solution obtained by mixing an ionic solution containing a phosphoric acid group, a solution having a sulfonic acid group, and a polymer solution is prepared, and then the mixed solution is cast in a glass Petri dish and dried (S300). Finally, A polymer electrolyte membrane can be produced. The solution-casting method of casting and drying the prepared solution is performed according to a conventional method, and a separate explanation will be omitted.
본 발명의 다른 실시예에 따른 연료전지는 연료가스를 공급받고, 수소의 산화반응이 이루어지는 연료극; 상기 연료극과 대응되며 산소의 환원반응이 이루어지는 공기극; 및 인산기와 술폰산기를 동시에 가지는 수소이온 전도성 고분자 및 기계적 물성을 부여하는 고분자를 포함하고, 상기 연료극과 공기극 사이에 배치되어 상기 연료극으로부터 공기극으로 수소 이온이 이동하는 복합 고분자 전해질막을 포함할 수 있다.According to another aspect of the present invention, there is provided a fuel cell comprising: a fuel electrode to which a fuel gas is supplied and an oxidation reaction of hydrogen is performed; An air electrode corresponding to the fuel electrode and performing a reduction reaction of oxygen; And a composite polymer electrolyte membrane including a hydrogen-ion conductive polymer having both a phosphoric acid group and a sulfonic acid group, and a polymer imparting mechanical properties, and disposed between the fuel electrode and the air electrode and moving hydrogen ions from the fuel electrode to the air electrode.
연료전지는 크게 연료극, 공기극 및 연료극과 공기극 사이에 복합 고분자 전해질막을 구비하는 구조로 이루어져 있으며, 연료전지에 구비되는 복합 고분자 전해질막은 인산기를 포함하는 이온성 용액, 술폰산기를 갖는 용액 및 고분자 용액을 혼합한 혼합용액을 주조 및 건조시켜 형성되는 복합 고분자 전해질막일 수 있다. 또한, 복합 고분자 전해질막은 150μm 내지 250μm 두께를 가질 수 있는데, 복합 고분자 전해질막의 두께가 150μm 미만이면 수소 이온 이외에 연료가 전해질막을 투과하는 기체 크로스오버 현상이 발생할 수 있고, 250μm을 초과하면 우수한 양이온 전도도 특성 발현이 어려울 수 있다. The fuel cell comprises a fuel electrode, an air electrode, and a composite polymer electrolyte membrane between the fuel electrode and the air electrode. The composite polymer electrolyte membrane of the fuel cell is prepared by mixing an ionic solution containing sulfonic acid group, And may be a composite polymer electrolyte membrane formed by casting and drying one mixed solution. If the thickness of the composite polymer electrolyte membrane is less than 150 탆, a gas cross-over phenomenon may occur in which the fuel permeates through the electrolyte membrane in addition to hydrogen ions. When the thickness is more than 250 탆, the composite electrolyte membrane may have a good cation conductivity Expression may be difficult.
연료극은 연료극으로 공급되는 연료가스에 포함된 수소를 산화 반응시켜 수소 이온과 전자로 변환시키는 기능을 하며, 복합 고분자 전해질막은 연료극에서 생성된 수소 이온을 공기극으로 이동시키는 이온 교환의 기능을 하고, 공기극은 수소 이온과 산소를 환원 반응시켜 소정 온도의 열과 물을 발생시키는 기능을 한다. 이러한 구조를 가지는 연료전지의 원활한 작동을 위해서는 가습으로 인한 수분 공급 및 고분자 전해질막의 습도 유지가 필수적이며, 이를 위해 일반적인 연료전지 시스템에는 가습을 위한 가습기가 구비되어 있다. 즉, 연료극으로 공급되는 연료가스는 가습기를 거쳐 수분을 포함한 상태로 연료극으로 공급되기 때문에 기존에 사용되는 연료전지용 고분자 전해질막은 가습 조건에서 우수한 전지 성능을 나타내지만 가습기 및 가습기에 필요한 주변부품으로 인해 연료전지의 규격이 커지면서 구조가 복합해지고 제작 및 유지 보수 비용이 증가하게 되는 문제가 있다.The fuel electrode has a function of converting hydrogen contained in the fuel gas supplied to the fuel electrode into hydrogen ions and electrons and converting the hydrogen into hydrogen ions and electrons. The composite polymer electrolyte membrane has a function of ion exchange for moving the hydrogen ions generated in the fuel electrode to the air electrode, Reacts with hydrogen ions and oxygen to generate heat at a predetermined temperature and water. In order to smoothly operate the fuel cell having such a structure, it is necessary to supply moisture due to humidification and to maintain the humidity of the polymer electrolyte membrane. For this purpose, a general fuel cell system is provided with a humidifier for humidification. That is, since the fuel gas supplied to the fuel electrode is supplied to the fuel electrode in a state containing water via the humidifier, the polymer electrolyte membrane for fuel cell, which is used conventionally, exhibits excellent battery performance under humidifying conditions. However, due to the peripheral parts required for the humidifier and the humidifier, There is a problem that the size of the battery becomes large and the structure becomes complex and the manufacturing and maintenance cost increases.
반면에, 본 발명에서는 인산기와 술폰산기를 동시에 포함하는 수소이온 전도성 고분자 및 기계적 물성을 부여하는 고분자를 포함하는 복합 고분자 전해질막을 연료전지에 제공함으로써 인산기와 황산기가 수소 이온의 이동에 관여하게 되어 상온 내지 200℃의 온도 범위, 보다 바람직하게는 물이 존재하지 않는 100℃ 이상의 온도에서도 인산기 및 황산기를 통해 양이온 교환 전달이 매우 용이해질 수 있다. 다시 말해, 100℃ 이상에서는 물이 존재하지 않아 양이온 교환 전달이 어려운 일반적인 고분자 전해질막과 달리 본 발명의 실시예에 따른 복합 고분자 전해질막은 이온 전도를 위한 메커니즘이 물에 의존하지 않으므로 상온 내지 200℃의 온도 범위에서 다양하게 사용할 수 있으며, 이로부터 연료가스는 연료극에 수분을 공급하기 위한 추가 가습 없이 연료극에 바로 공급되어 가습기가 구비되지 않은 단순한 연료전지 시스템 구성이 가능해질 수 있다. On the other hand, in the present invention, by providing the fuel cell with a composite polymer electrolyte membrane including a hydrogen ion conductive polymer containing both a phosphoric acid group and a sulfonic acid group and a polymer imparting mechanical properties, a phosphate group and a sulfate group are involved in the movement of hydrogen ions, Cation exchange exchange through the phosphate group and the sulfate group can be made very easy even at a temperature of 200 ° C, more preferably at a temperature of 100 ° C or more in the absence of water. In other words, since the polymer electrolyte membrane according to the embodiment of the present invention does not depend on water for the mechanism of ion conduction, unlike a general polymer electrolyte membrane in which water is not present at 100 ° C or higher and cation exchange is difficult to transfer, Temperature range, from which the fuel gas can be supplied directly to the fuel electrode without additional humidification to supply water to the fuel electrode, thus making it possible to construct a simple fuel cell system without a humidifier.
도 2는 본 발명의 실시예에 따른 복합 고분자 전해질막의 온도에 따른 이온 전도도를 나타내는 그래프이고, 도 3은 본 발명의 실시예에 따른 복합 고분자 전해질막의 전류 밀도에 따른 전압 및 출력 밀도를 나타내는 그래프이다. FIG. 2 is a graph showing ionic conductivity according to temperature of a composite polymer electrolyte membrane according to an embodiment of the present invention, and FIG. 3 is a graph showing voltage and power density according to current density of a composite polymer electrolyte membrane according to an embodiment of the present invention .
도 2를 참조하면, 본 발명의 복합 고분자 전해질막(실시예1)이 100℃ 이상의 고온에서는 술폰산기에 비해 인산기인 H2PO4 - 수 증가에 따라 이온 전도도가 급격히 향상되어 일반적인 고분자 전해질막(비교예)의 이온 전도도보다 고온에서 더욱 높은 이온 전도도를 나타내었고, 특히 110℃의 온도에서는 0.055S/cm의 우수한 이온 전도도를 나타내었다. 도 3은 110℃의 온도 및 무가습 조건에서 측정된 출력 밀도를 나타낸 데이터로서 전류 밀도의 함수로 실시예1의 전압과 출력 밀도의 변화를 측정하여 연료전지 특성을 확인하였다. 도 3에서 보는 바와 같이 본원 발명에 의해 제조된 복합 고분자 전해질막을 연료전지용으로 사용할 경우 0.002W/cm2의 최대 출력 밀도를 가지는 비교예과는 달리 0.011W/cm2 이상의 최대 출력 밀도를 보이는 것을 확인할 수 있다. 기존 고분자 전해질막(비교예)에 비해 출력 밀도가 약 5배에 달하는 우수한 출력 밀도를 얻을 수 있음으로써 연료전지의 효율을 향상시킬 수 있다.2, the ionic conductivity of the composite polymer electrolyte membrane of the present invention (Example 1) increased sharply with increasing H 2 PO 4 - , which is a phosphoric acid group, at a high temperature of 100 ° C or higher, The higher ionic conductivity was shown at higher temperature than the ionic conductivity of Example 1, and especially at 110 ℃, the ionic conductivity was 0.055 S / cm. Fig. 3 shows fuel cell characteristics by measuring the change in voltage and power density of Example 1 as a function of current density as data showing the power density measured at a temperature of 110 deg. C and no humidification condition. As shown in Figure 3 can determine what seems a composite polymer electrolyte membrane when used as a fuel cell, compared to the Pre-contrast with the maximum power density of 0.002W / cm 2 0.011W / cm 2 or more maximum power density produced by the present invention have. The efficiency of the fuel cell can be improved by obtaining an excellent power density of about 5 times the power density as compared with the conventional polymer electrolyte membrane (comparative example).
또한, 도 4는 본 발명의 실시예에 따른 인산기를 포함하는 이온성 용액의 함량에 따른 복합 고분자 전해질막의 온도 대 이온 전도도를 나타내는 그래프이고, 도 5는 본 발명의 실시예에 따른 인산기를 포함하는 이온성 용액의 함량에 따른 복합 고분자 전해질막의 전류 밀도 대 전압 및 출력 밀도를 나타내는 그래프이다.4 is a graph showing the temperature versus ionic conductivity of the composite polymer electrolyte membrane according to the content of the ionic solution including the phosphoric acid group according to the embodiment of the present invention. A graph showing the current density vs. voltage and the output density of the composite polymer electrolyte membrane according to the content of the ionic solution.
도 4를 참조하면, 실시예1은 인산기를 포함하는 이온성 용액이 술폰산기를 갖는 용액과 1:1의 함량으로 첨가되었을 때 온도에 따른 이온 전도도를 나타내는 그래프이고, 실시예2는 인산기를 포함하는 이온성 용액이 술폰산기를 갖는 용액보다 적은 함량으로 첨가되었을 때 온도에 따른 이온 전도도를 나타내는 그래프이며, 실시예3은 인산기를 포함하는 이온성 용액이 술폰산기를 갖는 용액보다 많은 함량으로 첨가되었을 때 온도에 따른 이온 전도도를 나타내는 그래프이다. 도 4에서 보는 바와 같이 이온성 용액이 술폰산기를 갖는 용액과 같은 함량이거나 더 많은 함량으로 첨가되었을 경우 즉, 술폰산기에 비해 인산기의 수가 더 많아지게 되면 이온 전도도가 향상될 수 있다.Referring to FIG. 4, Example 1 is a graph showing ionic conductivity according to temperature when an ionic solution containing a phosphoric acid group is added in a 1: 1 ratio with a solution having a sulfonic acid group. Example 3 is a graph showing the ionic conductivity when the ionic solution is added at a lower content than that of the solution having the sulfonic acid group. Fig. As shown in FIG. 4, when the ionic solution is added at a content equal to or greater than that of a solution having a sulfonic acid group, that is, when the number of phosphate groups is larger than that of a sulfonic acid group, the ionic conductivity can be improved.
도 5는 도 3과 마찬가지로 110℃의 온도 및 무가습 조건에서 측정된 출력 밀도를 나타낸 데이터로서 이온성 용액의 함량에 따른 전압과 출력 밀도의 변화를 측정하여 연료전지 특성을 확인하였다. 도 5에서 보는 바와 같이 이온성 용액의 함량이 높을수록 제조된 복합 고분자 전해질막의 출력 밀도가 더 증가하는 경향성을 나타내었으며, 이에 술폰산기에 비해 인산기의 수가 증가할수록 높은 출력 밀도를 가져 연료전지의 효율이 향상될 수 있다.FIG. 5 is a graph showing power densities measured at a temperature of 110.degree. C. and no humidification condition in the same manner as FIG. 3, and the characteristics of the fuel cell were confirmed by measuring changes in voltage and power density depending on the content of the ionic solution. As shown in FIG. 5, the higher the ionic solution content, the more the output density of the composite polymer electrolyte membrane was increased. As the number of phosphate groups increased, the efficiency of the fuel cell was increased Can be improved.
상기 살펴본 바와 같이, 본 발명의 실시예에 따른 복합 고분자 전해질막이 연료전지에 사용될 경우 인산기와 술폰산기가 수소 이온의 이동에 동시에 관여하게 되어 물이 존재하지 않는 100℃ 이상 및 저가습 또는 무가습 조건에서도 높은 이온 전도도를 나타내어 상온 내지 90℃의 온도 뿐만 아니라 100℃ 이상의 고온에서도 사용할 수 있고, 이에 연료극에서 생성되는 수소 이온은 복합 고분자 전해질막에 의해 저가습 또는 무가습 조건에서도 복합 고분자 전해질막을 통해 공기극으로 이동할 수 있다. 뿐만 아니라, 기존 고분자 전해질막(비교예)에 비해 출력 밀도가 약 5배에 달하는 우수한 출력 밀도를 얻을 수 있음으로써 연료전지의 효율을 향상시킬 수 있다. 더욱이, 복합 고분자 전해질막은 이온 전도를 위한 메커니즘이 물에 크게 의존하지 않으므로 연료전지는 연료극 또는 공기극으로 공급되는 가스를 가습시켜 수분을 공급하는 가습기가 필요하지 않게 되며, 이에 단순한 연료전지 시스템 구성이 가능해질 수 있다.As described above, when the composite polymer electrolyte membrane according to the embodiment of the present invention is used in a fuel cell, phosphate and sulfonic acid groups are simultaneously involved in the movement of hydrogen ions, It can be used not only at a temperature of room temperature to 90 deg. C but also at a high temperature of 100 deg. C or more. Hence, hydrogen ions generated in the fuel electrode can be supplied to the air electrode through the composite polyelectrolyte membrane Can be moved. In addition, compared to the conventional polymer electrolyte membrane (comparative example), the power density of the fuel cell can be improved by about 5 times that of the conventional polymer electrolyte membrane. Furthermore, because the mechanism for ion conduction is not highly dependent on water, the fuel cell does not need a humidifier to humidify the gas supplied to the fuel electrode or the air electrode to supply water, and thus a simple fuel cell system configuration is possible .
이상에서 본 발명의 바람직한 실시예에 대하여 도시하고 설명하였으나, 본 발명은 상기한 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 것이다. 따라서, 본 발명의 기술적 보호범위는 아래의 특허청구범위에 의해서 정하여져야 할 것이다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is clearly understood that the same is by way of illustration and example only and is not to be construed as limited to the embodiments set forth herein. Those skilled in the art will appreciate that various modifications and equivalent embodiments may be possible. Accordingly, the technical scope of the present invention should be defined by the following claims.
Claims (13)
상기 이온성 용액에 술폰산기를 갖는 용액을 첨가한 후 교반하여 혼합용액을 제조하는 과정; 및
상기 혼합용액을 주조한 후 건조시키는 과정을 포함하는 복합 고분자 전해질막 제조방법.
A process for preparing an ionic solution containing a phosphoric acid group;
Adding a solution having a sulfonic acid group to the ionic solution, and then stirring to prepare a mixed solution; And
And a step of casting the mixed solution and drying the mixed solution.
상기 건조시키는 과정 이전에,
상기 혼합용액에 상기 복합 고분자 전해질막에 기계적 물성을 부여하는 고분자 용액을 추가하는 과정을 더 포함하는 복합 고분자 전해질막 제조방법.
The method according to claim 1,
Before the drying process,
And adding a polymer solution for imparting mechanical properties to the mixed polymer electrolyte membrane to the mixed solution.
상기 고분자 용액은 폴리이미드계 고분자, 폴리에테르계 고분자, 폴리아릴렌계 고분자 및 폴리페닐렌계 고분자 중 적어도 어느 하나를 포함하는 복합 고분자 전해질막 제조방법.
The method of claim 2,
Wherein the polymer solution comprises at least one of a polyimide-based polymer, a polyether-based polymer, a polyarylene-based polymer, and a polyphenylene-based polymer.
상기 술폰산기를 갖는 용액은 퍼플루오로설폰산 용액인 복합 고분자 전해질막 제조방법.
The method according to claim 1,
Wherein the sulfonic acid group-containing solution is a perfluorosulfonic acid solution.
상기 인산기를 포함하는 이온성 용액을 제조하는 과정은,
1,2-디메틸이미다졸과 1-브로모부탄을 교반한 후 건조시켜 생성물을 형성하는 과정;
상기 생성물을 아세토아니트릴과 인산 용액에 용해시킨 후 교반시키는 과정; 및
상기 아세토아니트릴을 휘발시키는 과정을 포함하는 복합 고분자 전해질막 제조방법.
The method according to claim 1,
The process for preparing an ionic solution containing a phosphoric acid group includes:
Stirring the 1,2-dimethylimidazole and 1-bromobutane, and then drying to form a product;
Dissolving the product in an acetonitrile and a phosphoric acid solution, and stirring the resultant; And
And a step of volatilizing the acetanithrile.
상기 인산기를 포함하는 이온성 용액은 DMBulmH2PO4 이온성 용액인 복합 고분자 전해질막 제조방법.
The method according to claim 1,
Wherein the ionic solution containing the phosphate group is a DMBulmH 2 PO 4 ionic solution.
상기 1,2-디메틸이미다졸과 1-브로모부탄을 교반하는 과정 및 상기 생성물을 용해시킨 후 교반시키는 과정은 상온 및 불활성 가스 분위기에서 수행되는 복합 고분자 전해질막 제조방법.
The method of claim 5,
Wherein the process of stirring the 1,2-dimethylimidazole and 1-bromobutane, and dissolving and stirring the product are performed at room temperature and in an inert gas atmosphere.
상기 연료극과 대응되며 산소의 환원반응이 이루어지는 공기극; 및
인산기와 술폰산기를 동시에 가지는 수소이온 전도성 고분자 및 기계적 물성을 부여하는 고분자를 포함하고, 상기 연료극과 공기극 사이에 배치되어 상기 연료극으로부터 공기극으로 수소 이온이 이동하는 복합 고분자 전해질막을 포함하는 연료전지.
A fuel electrode which receives a fuel gas and performs an oxidation reaction of hydrogen;
An air electrode corresponding to the fuel electrode and performing a reduction reaction of oxygen; And
A fuel cell comprising a composite polymer electrolyte membrane including a hydrogen-ion conductive polymer having a phosphate group and a sulfonic acid group at the same time, and a polymer for imparting mechanical properties, wherein hydrogen ions move from the fuel electrode to the air electrode.
상기 복합 고분자 전해질막은 인산기를 포함하는 이온성 용액, 술폰산기를 갖는 용액 및 고분자 용액을 혼합한 혼합용액을 주조 및 건조시켜 형성되는 연료전지.
The method of claim 8,
Wherein the composite polymer electrolyte membrane is formed by casting and drying a mixed solution obtained by mixing an ionic solution containing a phosphate group, a solution containing a sulfonic acid group, and a polymer solution.
상기 연료가스는 상기 연료극에 수분을 공급하기 위한 가습 없이 상기 연료극에 공급되는 연료전지.
The method of claim 8,
Wherein the fuel gas is supplied to the fuel electrode without humidification for supplying moisture to the fuel electrode.
상기 복합 고분자 전해질막은 상온 내지 200℃의 온도 범위에서 사용되는 연료전지.
The method of claim 8,
Wherein the composite polyelectrolyte membrane is used at a temperature ranging from room temperature to 200 캜.
상기 수소 이온은 상기 복합 고분자 전해질막에 의해 저가습 또는 무가습 조건에서도 이동하는 연료전지.
The method of claim 8,
Wherein the hydrogen ions move by the composite polymer electrolyte membrane under low humidification or no humidification conditions.
상기 복합 고분자 전해질막은 150μm 내지 250μm의 두께를 가지는 연료전지.The method of claim 8,
Wherein the composite polymer electrolyte membrane has a thickness of 150 탆 to 250 탆.