KR20160124395A - Polycarbonate-glass laminated sheet and method for manufacturing of the same - Google Patents
Polycarbonate-glass laminated sheet and method for manufacturing of the same Download PDFInfo
- Publication number
- KR20160124395A KR20160124395A KR1020150054865A KR20150054865A KR20160124395A KR 20160124395 A KR20160124395 A KR 20160124395A KR 1020150054865 A KR1020150054865 A KR 1020150054865A KR 20150054865 A KR20150054865 A KR 20150054865A KR 20160124395 A KR20160124395 A KR 20160124395A
- Authority
- KR
- South Korea
- Prior art keywords
- polycarbonate
- glass
- sheet
- bonding
- bonded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
본 발명은 폴리카보네이트 기재시트, 상기 폴리카보네이트 기재시트의 양면에 적층되는 자외선 차단 공압출층을 포함하는 폴리카보네이트 적층시트에 유리 플레이트를 양면으로 접합한 유리-폴리카보네이트-유리 접합시트와 상기 폴리카보네이트 적층시트 및 상기 유리 플레이트를 접합하기 위한 접합기재를 포함하는 유리-폴리카보네이트-유리 접합시트에 관한 것이다.
상술한 바와 같이, 본 발명의 실시예에 따른 폴리카보네이트-유리 접합시트는 하드코팅층을 포함하지 않아 추가적인 공정 및 비용을 절감하면서 경량화된 접합시트를 제공한다.The present invention relates to a glass-polycarbonate-glass bonded sheet obtained by bonding a glass plate to both sides of a polycarbonate laminated sheet including a polycarbonate-based sheet, an ultraviolet shielding coextruded layer laminated on both sides of the polycarbonate-based sheet, A glass-polycarbonate-glass bonded sheet comprising a laminated sheet and a bonded substrate for bonding the glass plate.
As described above, the polycarbonate-glass bonded sheet according to the embodiment of the present invention does not include a hard coating layer, thereby providing a lightened bonded sheet while saving additional processing and costs.
Description
본 기술은 폴리카보네이트 및 유리를 접합한 접합시트에 관한 것이다.The present invention relates to a bonded sheet obtained by bonding polycarbonate and glass.
일반적으로 유리는 건축, 산업 등 다양한 분야의 재료로서 일상 생활에 사용되고 있다. 특히 자동차의 전면 유리에는 접합유리가 사용되어 왔다(도 1 참조). 접합유리로서는, 유리판과 유리판을 접합하거나(도 1에서 도면 부호 11 및 12가 모두 유리인 경우), 유리판과 수지 필름을 접착 수지층(13)을 통하여 접착된 강화유리(도 1에서 도면 부호 11 또는 12 중 하나만 유리인 경우) 등이 사용되고 있다.Generally, glass is used in everyday life as a material in various fields such as architecture and industry. Particularly, a laminated glass has been used for a front glass of an automobile (see Fig. 1). As the laminated glass, a glass plate and a glass plate may be joined (in the case where all of the
상기 종래의 기술의 접합유리는 자연재해 또는 인위적인 이유로 파괴되는 것을 막기 위하여 일반 판유리 또는 강화 유리를 2장 이상 접합하여 안전유리를 사용하거나 유리 안쪽 면에 유리비산방지용 필름이나 외부 침입을 지연시키는 필름을 부착하여 사용한다. 종래의 유리 접합 방법은 접착성 물질의 기계적 및 물리적 특성의 한계성과 유리 간의 접합으로 외부 충격에 의한 저항성이 낮고, 유리의 전체 두께가 두꺼워지고 무게가 증가하는 등 복합적인 추가 비용 발생으로 경제적이지 못하다. 이는 유리의 두께 증가에 의한 부피와 하중 때문에 건축물이나 자동차에 적용할 시 유리 하중에 견딜 수 있는 구조를 갖추기 위해 추가적인 원자재 비용이 발생하고, 복잡한 추가 설계가 필요하게 되며, 운송과 설치 과정에서의 원가상승 및 복합비용 발생하여 결국 경제적 손실로 이어지게 된다.In order to prevent natural glass disruption or destruction due to artificial reasons, the above-mentioned prior art glass laminated glass is bonded with two or more sheets of general glass or tempered glass to use a safety glass, or a film for preventing glass scattering or a film for delaying external penetration It is used by attaching. Conventional glass bonding methods are not economical because of the limitations of the mechanical and physical properties of the adhesive material and the low cost of resistance due to external impact due to the bonding between the glasses and the increase in the total thickness of the glass and the increase in weight, . This is because, due to the volume and the load due to the increase in the thickness of the glass, additional raw material costs are incurred in order to have a structure capable of withstanding the glass load when applied to buildings or automobiles, and further complicated designs are required. Rise and compound costs resulting in economic losses.
이를 보완하기 위해 폴리카보네이트 시트를 이용하여 유리를 일부 대체함으로써 경량화와 충격강도의 향상을 꾀할 수 있으나, 폴리카보네이트는 표면 경도가 낮기 때문에 표면에 하드코팅을 해야 하는 추가공정과 비용이 발생하는 문제점이 있다.In order to compensate for this, a part of the glass is replaced by a polycarbonate sheet to improve the light weight and the impact strength. However, since the polycarbonate has a low surface hardness, have.
이와 관련하여 특허문헌 1에는 유리나 합성수지로 이루어진 시트를 적층하거나, 여기에 접합필름을 더 포함하고, 무기입자를 이용하는 접합시트에 대해서 개시를 하고 있으나, 본 발명과는 차이가 있다.In this connection, Patent Document 1 discloses a laminated sheet made of glass or a synthetic resin, or a laminated sheet further comprising a laminated film thereon, and a laminated sheet using inorganic particles. However, this is different from the present invention.
상기 문제점을 해결하기 위해, 본 발명은 폴리카보네이트 기재시트, 상기 폴리카보네이트 기재시트의 양면에 적층되는 자외선 차단 공압출층을 포함하는 폴리카보네이트 적층시트; 상기 폴리카보네이트 적층시트의 양면에 접합되는 유리 플레이트; 및 상기 폴리카보네이트 적층시트 및 상기 유리 플레이트를 접합하기 위한 접합기재를 포함하는 폴리카보네이트-유리 접합시트에 관한 것으로, 하드코팅이 필요없는 접합시트를 제공할 수 있다.In order to solve the above problems, the present invention provides a polycarbonate laminated sheet comprising a polycarbonate base sheet, an ultraviolet barrier coextruded layer laminated on both sides of the polycarbonate base sheet, A glass plate bonded to both sides of the polycarbonate laminated sheet; And a polycarbonate-glass bonded sheet comprising the polycarbonate-laminated sheet and a bonded substrate for bonding the glass plate, wherein a bonded sheet without hard coating is provided.
상기한 바와 같은 목적을 달성하기 위한 본 발명의 특징에 따르면, 본 발명은 폴리카보네이트 기재시트, 상기 폴리카보네이트 기재시트의 양면에 적층되는 자외선 차단 공압출층을 포함하는 폴리카보네이트 적층시트; 상기 폴리카보네이트 적층시트의 양면에 접합되는 유리 플레이트; 및 상기 폴리카보네이트 적층시트 및 상기 유리 플레이트를 접합하기 위한 접합기재;를 포함하는 폴리카보네이트-유리 접합시트에 관한 것이다.According to an aspect of the present invention, a polycarbonate-laminated sheet includes a polycarbonate-based sheet, and an ultraviolet shielding coextruded layer laminated on both sides of the polycarbonate-based sheet. A glass plate bonded to both sides of the polycarbonate laminated sheet; And a bonding substrate for bonding the polycarbonate-laminated sheet and the glass plate to each other, and a polycarbonate-glass bonded sheet including the bonded substrate.
상기 접합기재는, 폴리비닐부티랄(PolyVinyl Butyral, PVB), 에틸비닐아세테이트(Ethyl VinylAcetate, EVA), 폴리올레핀 엘라스토머(polyolefin elastomer, POE), 폴리우레탄(PolyUrethane, PU), 및 에틸렌-아크릴공중합체수지막으로 이루어진 군으로부터 선택되는 접합필름 또는 접합액인 것을 특징으로 하고, 상기 폴리카보네이트 적층시트, 상기 유리 플레이트 및 상기 접합기재의 두께는 각각 1㎜ 내지 3㎜, 2㎜ 내지 3㎜ 및 0.4㎜ 내지 2㎜인 것을 특징으로 한다.The bonded substrate may be formed of at least one of polyvinyl butyral (PVB), ethyl vinyl acetate (EVA), polyolefin elastomer (POE), polyurethane (PU), and ethylene- Wherein the thickness of the polycarbonate laminated sheet, the glass plate, and the bonded substrate is 1 mm to 3 mm, 2 mm to 3 mm, and 0.4 mm to 3 mm, respectively, 2 mm.
상술한 바와 같이, 본 발명으로 인한 실시예에 따른 폴리카보네이트-유리 접합시트는 폴리카보네이트 면으로 표면 경도를 상승시키시 위한 하드코팅 작업이 필요 없어지기 때문에 추가적인 공정 및 비용이 발생하지 않는 효과가 있다.As described above, the polycarbonate-glass bonded sheet according to the embodiment of the present invention has no polycarbonate surface and hard coating operation for raising the surface hardness is not necessary, so that there is no additional process and cost.
또한, 종래의 유리-유리 접합시트와 비교하여 폴리카보네이트 시트를 사용하여 내충격성을 향상시킬 수 있고, 광투과율의 감소 없이 경량화하는 효과가 있다.Further, the impact resistance can be improved by using the polycarbonate sheet as compared with the conventional glass-glass bonded sheet, and the effect of reducing the light transmittance without decreasing the light transmittance is achieved.
도 1은 종래의 접합유리를 개략적으로 도시한 개념도이다.
도 2는 본 발명의 일 실시예에 따른 폴리카보네이트-유리 접합시트를 개략적으로 도시한 단면도이다.
도 3은 본 발명의 일 실시예에 따른 유리-폴리카보네이트-유리로 접합한 적층시트를 개략적으로 도시한 단면도이다.
도 4는 본 발명의 일 실시예에 따른 폴리카보네이트-유리 접합시트를 제조하
는 방법 중 진공백 방식으로 탈기하는 모습을 개략적으로 도시한 개념도이다.
도 5는 본 발명의 일 실시예에 따른 폴리카보네이트-유리 접합시트를 제조하는 방법 중 접합필름을 시트 사이에 삽입한 후에 프레스 등을 이용하여 압착 방식으로 접착하는 것을 개략적으로 도시한 개념도이다.
도 6은 본 발명의 일 실시예에 따른 폴리카보네이트-유리 접합시트를 제조하는 방법 중 액상의 접착제를 시트 사이에 주입하는 방법을 개략적으로 도시한 개념도이다.1 is a conceptual view schematically showing a conventional laminated glass.
2 is a schematic cross-sectional view of a polycarbonate-glass bonded sheet according to an embodiment of the present invention.
3 is a cross-sectional view schematically showing a laminated sheet bonded by glass-polycarbonate-glass according to an embodiment of the present invention.
4 is a cross-sectional view of a polycarbonate-glass bonded sheet according to an embodiment of the present invention.
Is a conceptual diagram schematically showing a manner of degassing in a vacuum method in the method.
FIG. 5 is a conceptual view schematically showing a method of manufacturing a polycarbonate-glass bonded sheet according to an embodiment of the present invention, in which a bonded film is inserted between sheets and then bonded by a press method or the like.
6 is a conceptual diagram schematically showing a method of injecting a liquid adhesive between sheets in a method of manufacturing a polycarbonate-glass bonded sheet according to an embodiment of the present invention.
이하에서는 본 발명에 따른 폴리카보네이트-유리 접합시트에 대한 바람직한 실시예를 첨부된 도면을 참조하여 상세히 설명하기로 한다. Hereinafter, preferred embodiments of the polycarbonate-glass bonded sheet according to the present invention will be described in detail with reference to the accompanying drawings.
이에 앞서, 본 명세서 및 청구범위에서 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정되어서는 아니되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. Prior to this, terms and words used in the present specification and claims should not be construed as being limited to ordinary or dictionary terms, and the inventor should appropriately define the concept of the term to describe its invention in the best way The present invention should be construed in accordance with the meaning and concept consistent with the technical idea of the present invention.
따라서, 본 명세서에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 실시예에 불과할 뿐이고 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.Therefore, the embodiments described in the present specification and the configurations shown in the drawings are merely the most preferred embodiments of the present invention and are not intended to represent all of the technical ideas of the present invention. Therefore, various equivalents It should be understood that water and variations may be present.
본 발명에서는 특히, 상기 폴리카보네이트 적층시트(110)의 양면에 유리 플레이트(120)를 접합시키는 것이 특징이다. 이와 같은 구조를 통해서 유리의 일부를 폴리카보네이트로 교체하면서도 하드코팅이 필요없는 경량화시트를 제작할 수 있는 장점이 있다.In particular, the present invention is characterized in that the
유리 플레이트(120)은 종래에 자동차, 방음벽, 건물외벽 등에 사용되는 유리라면 크게 제한이 없다. 폴리카보네이트 적층시트(110), 유리 플레이트(120) 및 접합기재(130)의 두께는 각각 각각 1㎜ 내지 3㎜, 2㎜ 내지 3㎜ 및 0.4㎜ 내지 2㎜인 일 수 있다.The
본 발명에서는 특히, 상기 폴리카보네이트 적층시트(110)의 양면에 유리 플레이트(120)를 접합시키는 것이 특징이다. 이와 같은 구조를 통해서 유리의 일부를 폴리카보네이트로 교체하면서도 하드코팅이 필요없는 경량화시트를 제작할 수 있는 장점이 있다.In particular, the present invention is characterized in that the
?유리 플레이트(120)은 종래에 자동차, 방음벽, 건물외벽 등에 사용되는 유리라면 크게 제한이 없다. 폴리카보네이트 적층시트(110), 유리 플레이트(120) 및 접합기재(130)의 두께는 각각 각각 1㎜ 내지 3㎜, 2㎜ 내지 3㎜ 및 0.4㎜ 내지 2㎜인 일 수 있다.The
도 3은 본 발명의 폴리카보네이트-유리 접합시트(100)의 폴리카보네이트 적층시트(110)를 개략적으로 도시한 단면도이다.3 is a cross-sectional view schematically showing a polycarbonate laminated
?도 3을 참조하면, 폴리카보네이트 적층시트(110)는 3층 구조로 이루어진다. 우선, 중심이 되는 폴리카보네이트 기재 시트(112)의 일면 또는 양면에 자외선 차단 코팅층(114a, 114b)이 형성된다. 도 2 및 도 3에는 폴리카보네이트 적층시트(110)를 3층 구조로 도시하였지만, 이와는 다르게 두 층으로 구성된 자외선 차단 코팅층(114a, 114b) 중 한 층을 생략하거나 층의 두께를 변경하여 특성을 조절할 수 있다. 자외선 차단 코팅층(114a, 114b)은 폴리카보네이트 또는 폴리메틸아크릴산 메틸 등의 적어도 1종의 수지일 수 있다. 자외선 차단 코팅층(114a, 114b)은 자외선 차단의 특성을 갖는 수지로서 폴리카보네이트와의 공압출 또는 도포가 가능한 수지라면 크게 제한되지 않는다. 자외선 차단 코팅층(114a, 114b)의 두께는 폴리카보네이트 기재시트(112)에 대하여 0.1% 내지 2% 정도의 비율로 형성하는 것이 바람직하다. 자외선 차단 코팅층(114a, 114b)의 두께가 상대적으로 두꺼워지면, 광투과성이 떨어질 우려가 있다. 반면, 두께가 얇아질 경우, 자외선 차단의 효과를 충분히 얻을 수 없다.3, the polycarbonate laminated
폴리카보네이트 적층시트(110)의 형성방법에 대해서는 추후 자세하게 설명하기로 한다.The method of forming the polycarbonate laminated
접합기재(130)로는 폴리비닐부티랄(PolyVinyl Butyral, PVB), 에틸비닐아세테이트(Ethyl Vinyl Acetate, EVA), 폴리올레핀 엘라스토머(polyolefin Elastomer,POE), 폴리우레탄(PolyUrethane, PU), 또는 에틸렌-아크릴 공중합체 중에서 선택된 접합필름 또는 접합액을 사용할 수 있다. 상기 폴리비닐부티랄은 표면에 엠보싱이 있어, 접착 후 초기 탈기 시에 공기의 배출이 용이하다. 또한, 무독성, 무취이며 신축성유연소재로서 내관통성이 우수하고 방음효과가 우수하다. 상기 에틸비닐아세테이트는 태양광모듈에 주로 사용되는 접합필름으로 흐름성이 좋아 복잡한 형상구조에서 충진이 용이하다. 접합기재(130)로서는 필름 또는 액상의 수지인 것을 사용할 수 있다.The
본 발명의 다른 실시예에 따른 폴리카보네이트 적층시트 및 유리 플레이트를 접합하여 폴리카보네이트-유리 접합시트를 제조하는 방법은 상기 폴리카보네이트 적층시트 및 상기 유리 플레이트 사이에 접합기재를 개재하여 적층한 적층체를 후 탈기(de-airing)하는 제1 접합단계; 및 상기 적층체를 10내지 15bar의 압력 및 80℃ 내지 160℃의 온도에서 10분 내지 50분간 가열하는 제2접합단계를 포함한다.A method for producing a polycarbonate-glass bonded sheet by bonding a polycarbonate laminated sheet and a glass plate according to another embodiment of the present invention is a laminate obtained by laminating the polycarbonate laminated sheet and the glass plate with a bonding substrate interposed therebetween A first bonding step of de-airing; And a second bonding step of heating the laminate at a pressure of 10 to 15 bar and a temperature of 80 to 160 캜 for 10 to 50 minutes.
상기 폴리카보네이트 적층시트는 상술한 바와 같이 폴리카보네이트 기재 시트, 자외선 차단 코팅층으로 이루어진 다층구조이다. 상기 각각의 층을 공압출 또는 도포의 방법을 이용하여 다층구조를 형성한다. 이때 도포의 방법은 플로우 코팅(flow coating), 스프레이 코팅(spray coating), 딥 코팅(dipcoating) 등 종래의 방법을 사용할 수 있다.The above polycarbonate laminated sheet is a multilayer structure composed of a polycarbonate base sheet and an ultraviolet barrier coating layer as described above. Each layer is co-extruded or coated to form a multi-layer structure. In this case, conventional methods such as flow coating, spray coating and dip coating can be used as the coating method.
상기 제1 접합단계를 수행하기 전에, 우선 상기 폴리카보네이트 적층시트, 상기 접합기재 및 상기 유리 플레이트를 차례로 적층하여 적층체를 준비한다. 이때, 상기 접합기재는 필름형태의 접착제를 부착하여 사용할 수 있다.Before the first bonding step, the polycarbonate laminated sheet, the bonded substrate, and the glass plate are laminated in order to prepare a laminate. At this time, the bonded substrate may be used with a film-type adhesive attached thereto.
상기 제1 접합단계는 예비 접합단계로서 상기 폴리카보네이트 적층시트 및 상기 유리 플레이트의 접합면에 채워진 공기를 빼주는 탈기 공정을 수행한다. 상기 폴리카보네이트 적층시트, 상기 접합기재 및 상기 유리 플레이트를 차례로 적층된 상기 적층체를 가압 롤러에 통과시켜 탈기하는 가압 롤러방식으로 진공을 형성하거나, 진공백 또는 진공링을 부착하여 상기 적층체의 각각의 접촉면을 진공상태를 형성하는 방법을 사용할 수 있다. 도 4는 본 발명의 일 실시예에 따른 폴리카보네이트-유리 접합시트를 제조하는 방법 중 탈기하는 단계를 개략적으로 도시한 개념도이다. 도 4를 참조하면, 상기 적층체(10, 폴리카보네이트-유리 접합시트)의 테두리 부분에 진공펌프와 연결되는 진공링(V)을 부착시켜 탈기한다. 상기 탈기는 20℃ 내지 30℃에서 20분 내지 30분간 수행될 수 있다. 상기 제1 접합단계가 완료된 후, 상온이 될 때까지 방치하여 냉각한다.The first bonding step is a preliminary bonding step of performing a degassing process of removing the air filled in the bonding surfaces of the polycarbonate laminated sheet and the glass plate. A vacuum is formed by a pressurizing roller method in which the laminated body of the polycarbonate laminated sheet, the bonded substrate, and the glass plate laminated in this order are passed through a pressure roller and is degassed, or a vacuum blank or a vacuum ring is attached to each of the laminated bodies May be used to form a vacuum state. FIG. 4 is a conceptual view schematically showing a step of degassing in a method of manufacturing a polycarbonate-glass bonded sheet according to an embodiment of the present invention. Referring to FIG. 4, a vacuum ring (V) connected to a vacuum pump is attached to the rim of the laminate (10, polycarbonate-glass bonded sheet) to degas. The degassing may be performed at 20 캜 to 30 캜 for 20 minutes to 30 minutes. After the first bonding step is completed, the substrate is allowed to stand until it is cooled to room temperature.
상기 제1 접합단계에서 탈기로 인하여 예비접합이 수행된 상기 적층체는, 상기 제2 접합단계에서 가온 및 가압하여 상기 접합기재를 경화시켜 상기 유리 플레이트와 상기 폴리카보네이트 적층시트를 결합시킨다. 상기 제2 접합단계에서는 상기 적층체를 10bar 내지 15bar의 압력하에서 80℃ 내지 160℃에서 10분 내지 50분간 가열한다. 이때, 상온에서부터 80℃ 내지 160℃의 온도가 될 때까지 10 내지 30분간 승온한 후, 10분 내지 50분간 유지하며 가열한다. 이후, 압력을 제거하여 가열을 멈춰 냉각시킨다.The laminate subjected to the preliminary bonding by the degassing in the first bonding step is heated and pressed in the second bonding step to cure the bonding substrate to bond the glass plate and the polycarbonate laminated sheet. In the second bonding step, the laminate is heated at a temperature of 80 to 160 ° C for 10 minutes to 50 minutes under a pressure of 10 bar to 15 bar. At this time, the temperature is raised from room temperature to 80 to 160 ° C for 10 to 30 minutes, and then the mixture is heated and maintained for 10 minutes to 50 minutes. Thereafter, the pressure is removed to stop the heating and cool down.
본 발명의 또 다른 실시예에 따른 폴리카보네이트 적층시트 및 유리 플레이트를 접합하여 폴리카보네이트-유리 접합시트를 제조하는 방법은 상기 폴리카보네이트 적층시트 및 상기 유리 플레이트 사이에 접합기재를 도포 또는 주입하는 단계; 및 상기 접합기재가 도포 또는 주입된 상기 폴리카보네이트 적층시트 및 상기 유리 플레이트를 광량 1000 내지 1500mJ로 10초 내지 20초간UV를 조사하여 건조하는 단계를 포함한다.A method of producing a polycarbonate-glass bonded sheet by bonding a polycarbonate-laminated sheet and a glass plate according to another embodiment of the present invention comprises the steps of: applying or injecting a bonding substrate between the polycarbonate-laminated sheet and the glass plate; And drying and irradiating the polycarbonate-laminated sheet coated with the bonding substrate or the glass plate with UV light for 10 seconds to 20 seconds at a light quantity of 1000 to 1500 mJ.
도 5 및 도 6은 본 발명의 일 실시예에 따른 폴리카보네이트-유리 접합시트(100)를 제조하는 방법 중 액상의 접착기재(130)를 이용한 방법을 개략적으로 도시한 개념도이다. 액상의 접착기재(130)를 사용할 경우, 도 5와 같이 유리 플레이트(120) 또는 폴리카보네이트 적층시트(110) 상에 상기 액상 접착기재(130)를 도포하여 접합한 후, 프레스 또는 롤러(P)로 가압하고 UV 건조기로 건조할 수 있다.5 and 6 are conceptual diagrams schematically showing a method of using a liquid
또한, 유리 플레이트(120) 및 폴리카보네이트 적층시트(120)를 양면테이프등으로 1차 접착한 후에 접착액(액상의 접착기재)을 주입(I)하여 UV 건조기로 건조하여 접착시킬 수 있다.Further, after the
본 발명에 따른 접합시트의 배열과 접합방법에 따른 표면경도에 대한 실시예는 하기 표 1과 같다.Examples of the surface hardness according to the arrangement and bonding method of the bonding sheet according to the present invention are shown in Table 1 below.
이상에서 설명한 것은 본 발명에 따른 폴리카보네이트-유리 접합시트를 실시하기 위한 실시예에 불과한 것으로서, 본 발명은 상기한 실시예에 한정되지 아니하고, 이하의 특허 청구 범위에서 청구하는 바와 같이 본 발명의 요지를 벗어남이 없이 당해 발명이 속하는 분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변경 실시가 가능한 범위까지 본 발명의 기술적 사상이 있다고 할 것이다.It is to be understood that the present invention is not limited to the above-described embodiment, but may be modified in various ways within the scope and spirit of the present invention as set forth in the claims below. It will be understood by those skilled in the art that various changes in form and details may be made therein without departing from the spirit and scope of the present invention as defined by the appended claims.
이상 본 발명자에 의해서 이루어진 발명을 상기 실시 예에 따라 구체적으로 설명하였지만, 본 발명은 상기 실시 예에 한정되는 것은 아니고 그 요지를 이탈하지 않는 범위에서 여러 가지로 변경 가능한 것은 물론이다.Although the present invention has been described in detail with reference to the above embodiments, it is needless to say that the present invention is not limited to the above-described embodiments, and various modifications may be made without departing from the spirit of the present invention.
100: 폴리카보네이트-유리 접합시트
110: 폴리카보네이트 기재시트
120: 유리 플레이트
130: 접합기재100: Polycarbonate-glass bonding sheet
110: Polycarbonate substrate sheet
120: glass plate
130: bonded substrate
Claims (3)
A glass-polycarbonate-glass bonded sheet obtained by adhering a glass plate to both sides of a polycarbonate laminated sheet including an ultraviolet shielding coextruded layer laminated on both sides of a polycarbonate substrate sheet.
The bonding substrate according to claim 1, wherein the bonding substrate is at least one of polyvinyl butyral (PVB), ethyl vinyl acetate (EVA), polyolefin elastomer (POE), polyurethane An ethylene-acrylic copolymer resin film, and a glass-polycarbonate-glass bonding sheet characterized by being a bonding film or a bonding liquid.