KR20090083633A

KR20090083633A - Plastic file coating composition

Info

Publication number: KR20090083633A
Application number: KR1020080009552A
Authority: KR
Inventors: 이은미
Original assignee: 이은미
Priority date: 2008-01-30
Filing date: 2008-01-30
Publication date: 2009-08-04

Abstract

플라스틱 줄에 우수한 유연성, 탄성, 윤활성과 분무 특성을 나타내는 플라스틱 줄 코팅제 조성물에 관한 것으로 플라스틱 줄을 오랫동안 사용할 경우 표면의 오일이 제거되어 탄력과 유연성이 없어지며 마찰이 발생하여 쉽게 닳고 소음이 발생하는 문제가 생겨 사용하는데 불편한 점이 많다. 본 발명은 분사 후 플라스틱 줄에 끈적거리는 느낌이 없어 언제나 새 줄 같이 윤기가 나 사용감을 우수하게 하는 플라스틱 줄 코팅제 조성물을 제공한다.This is a plastic file coating composition that shows excellent flexibility, elasticity, lubricity, and spraying properties on plastic wires. When plastic wires are used for a long time, the oil on the surface is removed, causing elasticity and flexibility to be lost, and friction causes easy wear and noise. There are many inconveniences to use. The present invention provides a plastic file coating composition which does not feel sticky to the plastic file after spraying and thus always has a shiny and usable feeling like a new file.

구성 성분으로서 메틸알코올 28 내지 35중량%, 에틸 알코올 25 내지 32중량%, 동점도가 40℃에서 6.00 내지 11.00 cSt인 액체 파라핀 오일 25 내지 30중량%, 폴리에테르 변성실리콘 6.75 내지 8.85중량%, 점도가 25℃에서 100 내지 100,000 cSt인 디메틸실리콘오일 4.5 내지 5.15중량% 및 올레인산 0.5 내지 1.5중량%를 포함하는 플라스틱 줄 코팅제를 제공한다.As components, 28 to 35% by weight methyl alcohol, 25 to 32% by weight ethyl alcohol, 25 to 30% by weight liquid paraffin oil having a kinematic viscosity of 6.00 to 11.00 cSt at 40 ° C, 6.75 to 8.85% by weight polyether modified silicone, viscosity Provided is a plastic file coating comprising 4.5 to 5.15 weight percent dimethylsilicone oil and 0.5 to 1.5 weight percent oleic acid at 25 ° C. at 100 to 100,000 cSt.

본 발명의 식물잎 플라스틱 줄 코팅제를 액화석유가스를 추진제로 한 에어로졸(Aerosol) 스프레이 형태로 제작하여 사용하면, 각종 플라스틱 줄 또는 플라스틱류의 사용 과정에서 발생하는 처음 사용시와는 달리 탄성, 유연성이 떨어지는 문제를 해결할 수 있으며 또한 줄, 또는 플라스틱 간의 마찰 계수를 줄여 줌 음으로서 오랫동안 소음 없이 유연성과 탄력성을 유지한 채 사용할 수 있게 한다.When the plant leaf plastic file coating of the present invention is manufactured and used in the form of an aerosol spray using liquefied petroleum gas as a propellant, it is inferior in elasticity and flexibility, unlike the first use that occurs during the use of various plastic files or plastics. It also solves the problem and also reduces the coefficient of friction between strings or plastics, making it possible to maintain flexibility and elasticity for a long time without noise.

Description

Coating compositions for plastic strings

본 발명은 플라스틱 줄 코팅제 조성물에 관한 것으로 더욱 상세하게는 플라스틱 줄을 오랫동안 사용할 경우 표면의 오일이 제거되어 탄력과 유연성이 없어지며 마찰이 발생하여 쉽게 닳는 문제가 생겨 사용하는데 불편한 점을 본 발명품을 분사하여 사용하면 플라스틱 줄에 끈적거리는 느낌이 없어 언제나 새 줄 같이 윤기가 나 사용감을 우수하게 하는 플라스틱 줄 코팅제에 관한 것이다.The present invention relates to a plastic file coating composition, and more particularly, when the plastic file is used for a long time, the oil on the surface is removed to lose elasticity and flexibility, and friction occurs easily, causing wear problems. It is a plastic file coating which gives a good feeling of feeling and feel like a new file without any sticky feeling.

본 발명은 플라스틱 줄 코팅제 조성물에 관한 것으로 더욱 상세하게는 플라스틱 줄에 분사하면 줄에 끈적거리는 느낌이 없어 언제나 새 줄 같이 윤기가 나 사용감을 우수하게 하는 플라스틱 줄 코팅제에 관한 것이다. The present invention relates to a plastic file coating composition, and more particularly, to a plastic file coating, which sprays on a plastic file, does not feel sticky to the file and always provides a shiny and comfortable feeling like a new file.

테니스 배드민턴 등의 스포츠 용품은 플라스틱 줄을 라켓에 묶어 조립하여 사용하고, 또한 기타 등의 현악기도 아름다운 소리를 내기 위해 여러 가지 합성 플라스틱 줄을 악기에 조립하여 사용하고 있다. 이러한 플라스틱 줄이 조립된 스포츠 용품 또는 악기를 오랫동안 사용하다 보면 플라스틱 표면의 오일이 증발 또는 사용중에 신체의 일부 또는 다른 물질에 닿아 제거되어 플라스틱 줄 표면이 거칠게 되어 플라스틱끼리 마찰에 의한 소음이 발생하며 또한 플라스틱의 탄성과 유연성이 처음과 는 달리 많이 감소하여 사용중 플라스틱 줄을 정렬해야하는 번거로움과 악기인 경우에는 음 조절을 위해 튜닝을 계속해서 해야하는 어려움이 있으며 또한 이러한 불편한 점으로 인해 새 플라스틱 줄을 구입해야 한다. Sports goods such as tennis badminton are used by assembling plastic strings tied to a racket, and string instruments such as guitars are also assembled by using various synthetic plastic strings in musical instruments. Long-term use of sporting goods or musical instruments assembled with such plastic strings causes oils on the plastic surface to come into contact with parts or other substances of the body during evaporation or use, resulting in a rough surface of the plastic strings, which may generate noise due to friction between the plastics. The elasticity and flexibility of plastics has decreased significantly from the beginning, and the hassle and alignment of plastic strings during use has made it difficult to continue tuning to adjust the pitch. do.

상기의 사용중 불편함은 물론 많은 시간과 경비로 인한 과다한 낭비를 초래되는 문제점을 보완하기 위해 이것을 간편하게 해결할 수 있는 간단히 플라스틱 줄에 발라 주거나 분사해주면 새 플라스틱 같은 느낌이 들게 하는 코팅제 물질을 필요로 하게 되었다.In order to compensate for the inconvenience of using the above, as well as the excessive waste caused by a lot of time and expense, it is necessary to apply a coating material that simply feels like a new plastic when applied or sprayed onto a plastic file that can be easily solved. .

본 발명은 스포츠 또는 현악기에 사용되는 플라스틱 줄 코팅제 조성물에 관한 것으로 스포츠 용품 또는 현악기의 플라스틱 줄에 분사하여 사용하면 새 줄 같이 탄성, 유연성이 증가하며 마찰 계수가 줄어들어 사용중 소음 발생이 없게 하는 플라스틱 줄 코팅제에 관한 것이다. The present invention relates to a plastic file coating composition used for sports or stringed instruments, when sprayed onto a plastic file of sporting goods or stringed instruments, such as a new file elasticity, flexibility is increased and the coefficient of friction is reduced to reduce the noise during use of the plastic file coating It is about.

대부분 플라스틱 줄을 사용하는 스포츠용품과 기타 등의 악기에 사용되는 플라스틱 줄은 열 경화성 수지로 계속해서 사용하다 보면 강도가 증가하여 딱딱한 느낌을 주고 플라스틱끼리 마찰이 자주 발생하여 소음이 발생한다. 대부분의 사용자는 당연한 결과로 인식하고 불편한 점을 감수하고 사용하고 있는 실정이거나 새로 줄을 교환하는 정도이다. 간혹, 일부 사용자들은 오일을 바르거나 분사하여 사용하는 경우도 있는데 이때 기름이 표면에 남아있어 사용중 손등의 신체 또는 의복에 오염되는 문제와 사용되는 오일 또한 냄새와 독성 등의 불편한 점이 많아, 오일을 바르는 꺼리고 있는 실정이다. Plastic cords, which are mostly used for sporting goods and other musical instruments that use plastic strings, are heat-curable resins, which continue to increase in strength, give a hard feeling, and often cause friction between plastics. Most users recognize the result as a natural result and accept the inconvenience and use a new line. Occasionally, some users apply oil or spray it, and the oil remains on the surface, which contaminates the body or clothing of the back of the hand and the oil used has many inconveniences such as smell and toxicity. I'm reluctant.

이에 본 발명에서는 간단히 플라스틱 줄 표면에 간단히 살짝 분사만 해주면 줄 표면 오일의 흔적이 없이 코팅되어 마치 새 줄을 매었을 때의 느낌을 나타내게 하는 기술을 개발하게 되었다.Therefore, the present invention has been developed a technology that can be expressed as if a new string is simply coated by simply spraying on the surface of the plastic string simply without a trace of oil on the surface of the string.

따라서, 본 발명의 목적은 상술한 종래의 문제점을 해결하기 위한 것으로, 특별한 노력이나 시간의 낭비 없이 누구나 간단히 스포츠 경기도중에 또는 악기 연주중 또는 틈새 시간에 딱딱 해지거나 유연성, 탄성이 부족해진 플라스틱 줄에 분사하여 발라 줌으로 간단히 스포츠용품과 악기 등의 플라스틱 줄이 새 줄 같이 소음 없이 부드럽고, 탄력을 부여할 수 있는 신규한 플라스틱 줄 코팅제를 제공하는 것이다.Accordingly, an object of the present invention is to solve the above-mentioned conventional problems, without anyone having to waste any special effort or time, simply by anyone during sports competitions, playing musical instruments, or niche time in plastic strings that are hard or flexible, lacking elasticity By spraying, it is simply to provide a new plastic file coating that can soften and give elasticity without any noise like a new file.

이상에서 상술한 바와 같이, 본 발명의 플라스틱 줄 코팅제는 플라스틱 줄을 오랫동안 사용하는 데에 따른 줄이 딱딱해져서 유연성이 부족하고 탄력이 줄어 스포츠용품이나 현 악기 등의 사용시에 촉감 또는 타구감이 좋지 않으며 또한 플라스틱 줄 끼리 부딪히는 경우에 소음이 발생에 따른 문제를 제거하고 새 줄같이 유연성과 탄성을 부여하여 사용자들에게 즐거운 연주나 운동경기가 되게 함은 물론 새 줄로 교체하는데 낭비되는 시간과 경비를 절감시키며 사용이 간편하여 손쉬운 방법으로 본 코팅제를 분사함으로써 스포츠 용품의 플라스틱 줄에 운동경기중 흙 또는 테니스공의 부직포 털 등이 줄에 묻는 문제와 현악기의 플라스틱 줄에도 먼지 등의 먼지 등이 쌓이는 것을 억제하는 효과도 있다.As described above, the plastic file coating agent of the present invention has a hard line due to the long use of the plastic file, the flexibility is insufficient, the elasticity is reduced and the feel or feel at the time of use, such as sporting goods or string instruments are not good When plastic strings collide with each other, it eliminates the problems caused by noise and gives flexibility and elasticity like new strings to make users enjoy playing or playing sports, as well as reducing the time and expense of wasting new strings. This simple and easy method of spraying the coating on the plastic rope of sporting goods causes dirt or tennis balls on the rope during sports and the effect of suppressing the accumulation of dust such as dust on the string of plastic strings. There is also.

상기한 목적을 달성하기 위한 본 발명의 플라스틱 줄 코팅제는 구성 성분으로서 메틸 알코올 28 내지 35중량%, 에틸 알코올 25 내지 32중량%, 동점도가 40℃에서 6.00 내지 11.00 cSt인 액체 파라핀 오일 25 내지 30중량%, 폴리에테르 변성실리콘 6.75 내지 8.85중량%, 점도가 25℃에서 100 내지 100,000 cSt인 디메틸실리콘오 일 4.5 내지 5.15중량% 및 올레인산 0.5 내지 1.5중량%를 포함한다.Plastic string coating agent of the present invention for achieving the above object 25 to 30% by weight of the liquid paraffin oil of 28 to 35% by weight methyl alcohol, 25 to 32% by weight ethyl alcohol, kinematic viscosity 6.00 to 11.00 cSt at 40 ℃ %, 6.75 to 8.85 weight percent polyether modified silicone, 4.5 to 5.15 weight percent dimethylsilicone oil having a viscosity of 100 to 100,000 cSt at 25 ° C and 0.5 to 1.5 weight percent oleic acid.

본 발명의 플라스틱 줄 코팅제 조성물에서 메칠 알코올과 에틸 알코올은 용제 및 침투제로서 상기의 오일들이 잘 혼합되게 하며 액체 파라핀 오일(liquid parafin oil)은 점성 조절 역할을 한다. 폴리에테르 변성실리콘(modified organopolysiloxane)은 플라스틱 줄의 탄성 증가시키고 디메틸 실리콘 오일(dimethyl silicon oil)은 슬립제 역할을 올레인산은 플라스틱 줄의 유연성을 증가한다.Methyl alcohol and ethyl alcohol in the plastic file coating composition of the present invention is a solvent and a penetrating agent to make the above oils well mixed, liquid parafin oil (liquid parafin oil) plays a role of viscosity control. Polyether-modified organopolysiloxane increases the elasticity of the plastic cord and dimethyl silicon oil acts as a slip agent and oleic acid increases the flexibility of the plastic cord.

본 발명에서 각 성분의 조성은 수차례의 실험을 통하여 최적의 조성범위를 결정한 것이며, 메틸 알코올 및 에틸 알코올은 액체 파라핀 오일 및 디메틸실리콘오일의 용해성을 고려하여 상기 성분들의 점도를 한정하는 것이 바람직하다. 본 발명의 플라스틱 줄 코팅제는 원액을 그대로 또는 희석하여 사용할 수도 있으나 사용하기 간편하도록 바람직하게는 스프레이 형태로 제작한다. 스프레이는 통상의 캔 스프레이로 제작하며, 필요에 따라 스프레이 건으로도 제작할 수 있다. 충전가스는 특별히 제한되지 않으며, 예를 들면 액화석유가스(LPG)를 사용할 수 있다.In the present invention, the composition of each component is determined through several experiments to determine the optimum composition range, methyl alcohol and ethyl alcohol is preferably limited in consideration of the solubility of liquid paraffin oil and dimethyl silicone oil to limit the viscosity of the components. . Plastic filament coating of the present invention may be used as it is or diluting the stock solution, but is preferably manufactured in a spray form so as to be easy to use. The spray is produced by a conventional can spray, and can also be produced by a spray gun, if necessary. The filling gas is not particularly limited, and for example, liquefied petroleum gas (LPG) can be used.

본 발명의 플라스틱 줄 코팅제는 윤활 유연 성분을 포함하여 플라스틱 줄에 존재하는 오물이나 얼룩자국을 제거하면서 광택을 부여하며, 또한 발수성분을 포함하여 빗물 등의 수분이 플라스틱 줄에 침투하는 것을 방지하는 부가적인 효과가 있다. 이하 첨부된 도면을 참조하여 본 발명의 플라스틱 줄 코팅제를 제조하는 과정을 상세히 설명한다.The plastic file coating agent of the present invention includes a lubricating softening component to add gloss while removing dirt or stains present on the plastic file, and further includes a water repellent component to prevent moisture such as rainwater from penetrating the plastic file. Has an effect. Hereinafter, a process of manufacturing the plastic file coating of the present invention will be described in detail with reference to the accompanying drawings.

첫 번째, 메틸 알코올 29g을 반응기에 투입하고 휘저음 하면서 동점도가 40℃에서 6.00내지 11.00 cSt인 액체 파라핀 오일 28.5g과, 폴리에테르 변성실리콘 7.5g을 First, 29 g of methyl alcohol was added to the reactor and stirred, and 28.5 g of liquid paraffin oil having a kinematic viscosity of 6.00 to 11.00 cSt at 40 ° C and 7.5 g of polyether modified silicone were added.

드로핑 판넬(Dropping funnel)에 넣고 40 ℃에서 서서히 투입하면서 교반하여 A액을 제조하였다(도 1 참조). 두 번째, A액 제조와 비슷한 방법으로 에틸알코올 29 g을 반응기에 투입하고 점도가 25℃ 에서 100 내지 100,000 cSt인 디메틸실리콘오일 5 g과 올레인산 1 g을 각각의 드로핑 펀넬을 통해 40℃에서 서서히 투입하면서 혼합하여 B액을 제조하였다(도 2 참조).세 번째, 상기에서 제조한 A액과 B액을 다시 각각의 드로핑 펀넬을 통해 서서히 투입하여 반응기에서 휘저음 하여 본 발명의 플라스틱 줄 코팅제 원액 100g을 제조하였다(도 3 참조).A solution was prepared by dropping into a dropping panel and slowly stirring at 40 ° C. (see FIG. 1). Second, 29 g of ethyl alcohol was added to the reactor in a similar manner to the preparation of liquid A. 5 g of dimethylsilicone oil having a viscosity of 100 to 100,000 cSt and 1 g of oleic acid were slowly added at 40 ° C. through respective dropping funnels. The liquid B was prepared by mixing while adding (see FIG. 2). Third, the liquid A and the liquid B prepared above were gradually added again through each of the dropping funnels, and stirred in a reactor to give a plastic rope coating of the present invention. 100 g of the stock solution was prepared (see FIG. 3).

상기의 배합비율에서 가장 양호한 효과를 얻었으나, 각 성분의 양을 ±5% 범위 내에서 변경하여도 거의 동일한 효과를 얻을 수 있었다.The best effect was obtained in the above blending ratio, but the same effect was obtained even if the amount of each component was changed within the range of ± 5%.

최종적으로, 상기에서 제조한 플라스틱 줄 코팅제 원액을 에어로졸 캔에 넣고 밀봉한 후 주입구를 통하여 액화석유가스를 충전하여 에어로졸 캔 스프레이를 제작하였다 (도 4 참조). 이와 같이 제조한 플라스틱 줄 코팅제 스프레이를 스포츠용 플라스틱 줄과 현 악기의 플라스틱 줄에 살포한 결과, 줄에 끈적 그림 없이 새 줄을 묶었을 때처럼 탄성과 유연성이 우수하며 줄 끼리 마찰 계수가 줄어들어 부딪치며 나타 나는 잡음과 줄 끼리 엉키는 문제가 없이 언제나 새 줄 같이 윤기가 나 신선한 사용감을 주며 특히, 줄의 수명도 상당 기간 연장되었다Finally, the plastic cord coating solution prepared above was placed in an aerosol can and sealed, and then filled with liquefied petroleum gas through an inlet to prepare an aerosol can spray (see FIG. 4). As a result of spraying the plastic file coating spray thus manufactured on the plastic file for sports and the plastic file of the string instrument, it has excellent elasticity and flexibility as when a new file is tied without a sticky figure on the file, and the friction coefficient between the wires is reduced and it appears. I always have a shiny and fresh feel like a new one without noise and tangling problems, especially the life of the string has been extended for a long time.

도 1은 메틸 알코올과 액체 파라핀 오일 및 폴리에테르 변성실리콘을 배합 반응기에서 혼합하는 과정을 나타낸 도면,1 is a diagram illustrating a process of mixing methyl alcohol, liquid paraffin oil, and polyether modified silicone in a compounding reactor;

도 2는 에틸 알코올과 디메틸실리콘 오일 및 올레인산을 배합 반응기에서 혼합하는 과정을 나타낸 도면, 2 is a diagram illustrating a process of mixing ethyl alcohol, dimethylsilicone oil, and oleic acid in a blending reactor;

도 3은 도 1 및 2에서 제조한 두 용액을 다시 혼합하여 플라스틱 줄 코팅제 원액을 제조하는 과정을 나타낸 도면,3 is a view showing a process of preparing a plastic filed coating stock solution by mixing two solutions prepared in FIGS. 1 and 2 again;

도 4는 도 3의 플라스틱 줄 코팅제 원액을 에어로졸 캔에 주입하고 봉합한 후 주입구를 통하여 액화석유가스를 주입하여 플라스틱 줄 코팅제 에어로졸을 완성하는 과정을 나타낸 도면이다.FIG. 4 is a view illustrating a process of completing the plastic file coating aerosol by injecting the raw liquid solution of the plastic file coating material of FIG. 3 into the aerosol can and then sealing the liquid petroleum gas through the injection hole.

Claims

28 to 35% by weight methyl alcohol, 25 to 32% by weight ethyl alcohol, 25 to 30% by weight liquid paraffin oil having a kinematic viscosity of 6.00 to 11.00 cSt at 40 ° C, 6.75 to 8.85% by weight polyether modified silicone, viscosity at 25 ° C Plastic line coating composition comprising 4.5 to 5.15% by weight of dimethyl silicone oil of 100 to 100,000 cSt and 0.5 to 1.5% by weight of oleic acid.