KR20020055567A - Sheet for repair and reinforcement of concrete structure and method thereof - Google Patents
Sheet for repair and reinforcement of concrete structure and method thereof Download PDFInfo
- Publication number
- KR20020055567A KR20020055567A KR1020010017148A KR20010017148A KR20020055567A KR 20020055567 A KR20020055567 A KR 20020055567A KR 1020010017148 A KR1020010017148 A KR 1020010017148A KR 20010017148 A KR20010017148 A KR 20010017148A KR 20020055567 A KR20020055567 A KR 20020055567A
- Authority
- KR
- South Korea
- Prior art keywords
- adhesive
- concrete structure
- fibers
- repair
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
본 발명은 콘크리트 구조물의 보수 및 보강, 더욱 상술하면, 콘크리트 구조물의 콘크리트가 콜드조인트나 중성화, 염해(鹽害) 등에 의해 철근의 부식이나 골재의 팽창, 혹은 시공불량 등에 의해 콘크리트편으로서 박리낙하하는 것을 방지하고, 상기의 요인에 의해 박리나 들뜸이 발생하고 보수한 부분이 박리낙하하는 것을 방지하는 시트 및 콘크리트 구조물의 보수·보강방법에 관한 것이다.The present invention is to repair and reinforce the concrete structure, more specifically, the concrete of the concrete structure peeled and dropped as a concrete piece due to the corrosion of the rebar, expansion of aggregate, or poor construction due to cold joints, neutralization, salting, etc. The present invention relates to a method for repairing and reinforcing a sheet and a concrete structure, which prevents the peeling and falling of the repaired portion from occurring due to the above factors.
콘크리트 구조물은 장기에 걸쳐서 내구성이 있다고 생각된 시기도 있었으나, 근년, 년월을 경과한 콘크리트 구조물의 콘크리트가 콜드조인트나 중성화, 알칼리골재반응, 동해(凍害), 염해 혹은 시공불량 등 여러가지 이유에 의해 콘크리트편으로서의 박리낙하나 균열에 의해 누수를 초래하고, 사회문제로 되었다.There were times when concrete structures were considered to be durable over a long period of time, but in recent years, concrete in concrete structures that have passed over the years may be damaged due to various reasons such as cold joints, neutralization, alkali aggregate reaction, east sea, salt damage or poor construction. Peeling and cracking as a piece caused water leakage due to cracks, and became a social problem.
종래는 콘크리트 박리낙하의 염려가 있는 경우, 먼저 콘크리트 표면을 깨끗이 청정하고, 이어서 콘크리트 열화의 정도에 의해, 함침재, 철근방청재, 단면수복재, 균열 주입재 등을 필요에 따라 시공하고, 하도재를 도포한 후에 퍼티 등 하지조정재를 사용하여 평활화 등의 처리를 시행하고, 1차 마무리를 행한다. 다음에 표면피복재로서 각종 도료, 건축마무리 도장재, 도막방수재, 성형판 등으로 2차 마무리를 행하든지, 혹은 1차 마무리의 후에 접착제를 도포하고, 그 위에 보수나 보강을 위하여 직포(織布)나 편포(編布)를 부착하고, 더욱이 접착제를 도포하여 굳히고, 건조고화후에 다시 하도재를 도포하고, 그 위에 내후성(耐候性)을 갖는 도료를 도포하고, 2차 마무리를 행하고 있었다.Conventionally, if there is a concern of falling concrete peeling, first clean the concrete surface, and then the impregnating material, the reinforcing bar rusting material, the cross-sectional restoring material, the crack injection material, etc. are constructed as needed by the degree of concrete deterioration. After application | coating, the process of smoothing etc. is performed using the base adjustment materials, such as a putty, and 1st finishing is performed. Next, as the surface coating material, secondary finishing is done with various paints, building finishing coating materials, waterproofing films, and molding plates, or an adhesive is applied after the primary finishing, and a woven cloth or A knitted fabric was attached, and an adhesive was further applied to harden it, and after drying and solidifying, the undercoating material was again applied, the coating material which has weather resistance was applied, and the secondary finishing was performed.
접착제로서는 에폭시계 등, 도료로서는 아크릴계수지, 우레탄수지, 불소계수지 또는 같은 고무 등이 사용된다. 건축 마무리재로서는, 시멘트, 규산질, 아크릴수지 등, 성형판으로서는, GRC, 알루미늄판, PIC판 등이 사용되고 있다.As the adhesive, an epoxy resin, an acrylic resin, a urethane resin, a fluorine resin or the like rubber is used. As a building finishing material, GRC, an aluminum board, a PIC board, etc. are used as molded boards, such as cement, silicic acid, and an acrylic resin.
이들의 작업은 고소작업이기 때문에 중노동이라는 것, 경화나 양생 등이 필요하고 시공공기도 길게 되므로 공사코스트가 높게 되는 것, 시공현장의 조건에 따라서는, 품질관리가 어려운 점이 있고, 소정의 품질을 확보하기위해서 과잉의 사양설계로 되는 것 등의 문제를 가지고 있었다.Since these works are high-level work, heavy labor, hardening and curing are required, and construction time is long, so construction cost is high and quality control is difficult depending on the construction site conditions. In order to secure it, there were problems such as excessive specification design.
본 발명은 상기와 같은 문제점을 해결하기 위해 이루어진 것으로, 현장에서의 접착제나 도료의 도포작업공정의 간소화, 시공의 용이화 및 미리 품질관리가 용이한 환경하에서 부재를 제조하여 두고 프리패브화를 도모하는 것으로, 중노동을 저감시키고, 시공공기를 단축화하고, 품질을 안정시키는 것을 목적으로 하는 것이다.The present invention has been made in order to solve the above problems, to simplify the application process of the adhesive or paint in the field, to facilitate the construction and to prepare the member in an environment where quality control is easy in advance to achieve prefabrication It aims at reducing heavy labor, shortening construction air, and stabilizing quality.
도 1은 본 발명에 관한 콘크리트 구조물의 보수·보강용 시트의 일실시의 형태를 도시하는 단면도이다.BRIEF DESCRIPTION OF THE DRAWINGS It is sectional drawing which shows one Embodiment of the sheet | seat for repair and reinforcement of the concrete structure which concerns on this invention.
도 2는 본 발명에 관한 콘크리트 구조물의 보수·보강용 시트를 콘크리트 구조물의 표면에 시공한 일실시의 형태를 도시하는 단면도이다.It is sectional drawing which shows one Embodiment which constructed the sheet for repair and reinforcement of the concrete structure which concerns on this invention on the surface of a concrete structure.
도 3은 본 발명에 관한 콘크리트 구조물의 보수·보강용 시트의 다른 실시의 형태를 도시하는 단면도이다.It is sectional drawing which shows other embodiment of the sheet | seat for repair and reinforcement of the concrete structure which concerns on this invention.
도 4는 본 발명에 관한 콘크리트 구조물의 보수·보강용 시트를 콘크리트 구조물의 표면에 시공한 다른 실시의 형태를 도시하는 단면도이다.It is sectional drawing which shows other embodiment which constructed the sheet for repair and reinforcement of the concrete structure which concerns on this invention on the surface of a concrete structure.
"도면의 주요부분에 대한 부호의 설명""Description of Symbols for Major Parts of Drawings"
1; 폴리불화비닐 필름2; 우레탄계 접착제One; Polyvinyl fluoride film 2; Urethane Adhesive
3; 비니론 3축메시4; 폴리에스테르섬유 부직포3; Biniron triaxial mesh 4; Polyester Fiber Nonwoven
5; 에폭시수지 접착제6; 콘크리트 구조물5; Epoxy resin adhesives 6; Concrete structure
본 발명자들은, 상기 목적을 달성하기위해서 예의 검토한 결과, 콘크리트 구조물의 보수·보강공법에 있어서, 콘크리트 구조물의 표면피복으로서 접착제 혹은 도료를 사용하여 반복하여 도장을 행하는 대신에, 내후성, 방오성(防汚性)이나 방수성 등을 가지는 보호층으로서의 외층재료와 콘크리트면과의 접착을 용이하게 하기위한 부착층으로서의 내층재료를 미리 적층가공을 행하는 적층체로서 하고, 그 적층체를 현장에서 부착하는 것으로, 콘크리트 박리낙하를 방지하기위한 보수나 보강의 작업을 경감·단축화를 할 수 있다는 깨달음을 얻어서 본 발명을 이루게 되었다.MEANS TO SOLVE THE PROBLEM As a result of earnestly examining in order to achieve the said objective, in the repair and reinforcement method of a concrete structure, instead of repeating application | coating using adhesive or a paint as surface coating of a concrete structure, it is a weather-resistant and antifouling property. By making a laminate in advance by laminating the outer layer material as a protective layer having a protective property, water resistance, etc., and the inner layer material as an adhesion layer for facilitating adhesion between concrete surfaces, and attaching the laminate in situ, The present invention has been achieved by realizing that the work of repair or reinforcement to prevent peeling of concrete can be reduced and shortened.
본 발명은, (1) 보호층과 부착층과의 적층체로서 형성되는 것을 특징으로 하는 콘크리트 구조물의 보수·보강용 시트, 및 (2) 이 보수·보강용 시트를 콘크리트 구조물에, 이 시트의 부착층과 이 콘크리트 구조물의 표면을 접착제를 사용하여 부착하는 것을 특징으로 하는 콘크리트 구조물의 보수·보강방법을 제공한다.The present invention provides (1) a sheet for repair and reinforcement of a concrete structure, and (2) a sheet for repair and reinforcement of a concrete structure, which is formed as a laminate of a protective layer and an adhesion layer. It provides a repair and reinforcement method for a concrete structure, characterized in that the adhesive layer is attached to the surface of the concrete structure using an adhesive.
즉, 본 발명의 콘크리트구조물의 보수·보강용 시트는, 보호층과 부착층을 미리 적층가공을 행하여 적층체로서 놓아두는 것이다.That is, the sheet for repair and reinforcement of the concrete structure of this invention is laminated | stacked beforehand and a protective layer and an adhesion layer are put as a laminated body.
여기서, 본 발명의 콘크리트 구조물의 보수·보강용 시트는, 보호층과 부착층이외에, 보강층을 더 적층하여도 좋다. 그리고, 보강층이 직포, 편포, 부직포 및 적층포중에서 선택되는 1종 또는 2종 이상의 섬유기재로 이루어지는 것이 바람직하고, 그와같은 섬유기재로서는, 폴리에스테르섬유, 폴리아미드섬유, 비니론섬유, 카본섬유, 유리섬유 또는 폴리오레핀섬유로 이루어지는 군 중에서 선택되는 1종 또는 2종이상의 섬유로 이루어지는 것이 보다 바람직하다.Here, in the repair / reinforcement sheet of the concrete structure of the present invention, a reinforcing layer may be further laminated in addition to the protective layer and the adhesion layer. And, it is preferable that the reinforcing layer is made of one or two or more types of fiber base material selected from woven fabric, knitted fabric, nonwoven fabric and laminated fabric, and as such a fiber base material, polyester fiber, polyamide fiber, Vinyron fiber, carbon fiber It is more preferable that it consists of 1 type, or 2 or more types of fiber chosen from the group which consists of glass fiber or a polyolefin pin fiber.
상기 설명한 적층체에 있어서, 보호층은 불소계수지, 아크릴계수지, 아크릴실리콘계수지, 아크릴불소계수지, 실리콘계수지, 우레탄계수지 및 염소계수지로 이루어지는 군 중에서 선택되는 1종 또는 2종 이상의 합성수지로 이루어지는 합성수지층인 것이 바람직하고. 상기 보호층이 그 표면에 광촉매층을 갖는 것이 바람직하다.In the laminate described above, the protective layer is a synthetic resin layer composed of one or two or more synthetic resins selected from the group consisting of fluorine resin, acrylic resin, acrylic silicone resin, acrylic fluorine resin, silicone resin, urethane resin and chlorine resin. Is preferable. It is preferable that the said protective layer has a photocatalyst layer on the surface.
더욱이, 상기 설명한 적층체에 있어서, 부착층은, 직포, 편포, 부직포, 적층포 및 종이로 이루어지는 군에서 선택되는 1종 또는 2종 이상의 섬유기재로 이루어지는 것이 바람직하고, 그와 같은 섬유기재로서 폴리에스테르섬유, 폴리아미드섬유, 비니론섬유, 카본섬유, 유리섬유 및 폴리오레핀섬유로 이루어지는 군 중에서 선택되는 1종 또는 2종이상의 섬유기재인 것이 보다 바람직하다.Furthermore, in the laminate described above, the adhesive layer is preferably made of one or two or more types of fiber base materials selected from the group consisting of woven fabrics, knitted fabrics, nonwoven fabrics, laminated fabrics, and papers. It is more preferable that it is 1 type, or 2 or more types of fiber base material chosen from the group which consists of ester fiber, polyamide fiber, Vinyron fiber, carbon fiber, glass fiber, and polyolefin fiber.
그리고, 본 발명의 콘크리트 구조물의 보수·보강방법은 (1)에 기재된 콘크리트 구조물의 보수·보강용 시트를 콘크리트 구조물에, 이 시트의 부착층과 이 콘크리트 구조물의 표면을 접착제를 사용하여 부착하는 것을 특징으로 하는 콘크리트 구조물의 보수·보강방법이다.The repair and reinforcement method of the concrete structure according to the present invention is to attach the sheet for repair and reinforcement of the concrete structure described in (1) to the concrete structure, and to attach the adhesive layer of the sheet and the surface of the concrete structure with an adhesive. It is a repair and reinforcement method of concrete structure.
여기서, 부착층과 콘크리트 구조물의 표면을 접착하는 접착제는, 에폭시계 접착제, 우레탄계 접착제, 실리콘계 접착제, 고무계 접착제, 비닐에스테르계 접착제, 폴리에스테르계 접착제, 폴리머시멘트계 접착제, 아크릴계 접착제 및 폴리올레핀계 접착제로 이루어지는 군 중에서 선택되는 1종 또는 2종 이상의 접착제로 이루어지는 것이 바람직하다.Here, the adhesive for bonding the adhesive layer to the surface of the concrete structure is composed of an epoxy adhesive, a urethane adhesive, a silicone adhesive, a rubber adhesive, a vinyl ester adhesive, a polyester adhesive, a polymer cement adhesive, an acrylic adhesive, and a polyolefin adhesive. It is preferable that it consists of 1 type, or 2 or more types of adhesives chosen from group.
이하, 본 발명을 보다 상세히 설명한다.Hereinafter, the present invention will be described in more detail.
본 발명의 콘크리트 구조물의 보수·보강용 시트는, 콘크리트 구조물의 보수·보강공법에 있어서, 콘크리트 구조물의 표면피복으로서 접착제 혹은 도료를 사용하여 반복하여 도장을 행하는 대신에, 내후성, 방오성, 방수성이나 방염성 등을 갖는 보호층으로서의 외층재료와 콘크리트면과의 접착을 용이하게 하기위한 부착층으로서의 내층재료를 미리 적층가공을 행하여 적층체로 하여 두고, 그 적층체를 현장에서 부착함으로써, 콘크리트 박리낙하를 방지하기위한 보수나 보강작업을 경감·단축화, 및 품질의 안정화를 이룰 수 있는 것이다.The sheet for repair and reinforcement of the concrete structure of the present invention is weatherproof, antifouling, waterproof or flame retardant in the repair and reinforcement method of the concrete structure, instead of repeatedly applying the coating using an adhesive or paint as the surface coating of the concrete structure. In order to prevent the peeling of concrete, the inner layer material serving as an adhesion layer for facilitating adhesion between the outer layer material serving as a protective layer and the concrete surface having the back and the like is laminated in advance, and the laminated body is adhered in the field to prevent the peeling of concrete. It can reduce and shorten repair and reinforcement work and stabilize quality.
본 발명에 있어서는, 이와같이 하여 이루어지는 적층체에 있어서, 보호층과 부착층의 사이에 보강층을 개재시킨 적층체로 해도 좋다.In this invention, it is good also as a laminated body which interposed a reinforcement layer between a protective layer and an adhesion layer in the laminated body comprised in this way.
이 보강층은, 본 발명의 콘크리트 구조물의 보수·보강용 시트의 파단을 방지하기위해 물리적 강도를 높이는 것을 목적으로 하여 적층되고, 그 물리적 강도는 보호층 및 부착층과 적층된 때에, 콘크리트편이 박리한 경우의 무게에 견디는 정도의 강도가 있는 층형상의 것이면 특히 제한은 없고, 합성수지, 무기물이나 천연물의 섬유로 이루어지는 직포, 편포, 부직포, 적층포 등의 섬유기재, 합성수지나 금속의 시트 등이 채용될 수 있다.This reinforcement layer is laminated for the purpose of increasing physical strength in order to prevent breakage of the repair / reinforcement sheet of the concrete structure of the present invention. There is no restriction in particular as long as it is a layered material having strength to withstand the weight of the case, and textile materials such as woven fabrics, knitted fabrics, nonwoven fabrics, laminated fabrics made of synthetic resins, inorganic or natural fibers, synthetic resins and metal sheets, etc. may be employed. Can be.
그리고, 보강층은 직포, 편포, 부직포 및 적층포 중에서 선택되는 1종 또는 2종 이상의 섬유기재로 이루어지는 것이 바람직하고, 그와 같은 섬유기재로서는, 폴리에스테르섬유, 폴리아미드섬유, 비니론섬유, 카본섬유, 유리섬유 또는 폴리올레핀섬유로 이루어지는 군 중에서 선택되는 1종 또는 2종 이상의 섬유로 이루어지는 것이 보다 바람직하다.The reinforcing layer is preferably composed of one or two or more fiber bases selected from woven fabrics, knitted fabrics, nonwoven fabrics, and laminated fabrics, and such fiber bases include polyester fibers, polyamide fibers, bininiron fibers, and carbon fibers. It is more preferable that it consists of 1 type, or 2 or more types of fiber chosen from the group which consists of glass fiber or a polyolefin fiber.
이들 중에서도 가볍고 강도가 우수한 것이므로, 폴리에스테르섬유, 폴리아미드섬유, 비니론섬유, 및 폴리올레핀섬유가 특히 바람직하다. 이들의 섬유는 혼방되어 있어도 좋고, 종사(縱絲), 횡사(橫絲)로 나누어 사용해도 좋고, 다층으로 적층되어도 좋다. 또 합성수지층과 적층되어도 좋다.Among them, polyester fibers, polyamide fibers, biniron fibers, and polyolefin fibers are particularly preferable because they are light and excellent in strength. These fibers may be mixed, or may be divided into solid and horizontal yarns, or may be laminated in multiple layers. It may also be laminated with a synthetic resin layer.
섬유기재의 형태로서는, 직포, 편포, 부직포 혹은 적층포 등이 바람직하다. 구체적으로는, 스펀본드, 멜트프론이나 니들펀치 등으로 제작된 부직포, 장섬유의 모노필라멘트나 멀티필라멘트 혹은 단섬유의 방사(紡絲)를 짯거나 엮은 직포나 편포, 3개의 실을 사용하여 교점을 접착시킨 3축 메시나 종횡의 섬유를 접착시킨 와리브(日石化學(株)의 등록상표), 2축 직교 적층포 등의 2개 이상의 실을 사용하여 교점을 접착시킨 적층포를 들 수 있다.As a form of a fiber base material, a woven fabric, a knitted fabric, a nonwoven fabric, a laminated fabric, etc. are preferable. Specifically, non-woven fabrics made of spunbond, melt-pron, needle punch, etc., monofilaments of long fibers or multifilaments, or woven fabrics or knitted fabrics woven or woven with woven yarns of short fibers, the intersections using three threads And laminated fabrics bonded to each other using two or more yarns, such as a triaxial mesh bonded to the surface, a warrib (registered trademark of 石 石 學), and a biaxially orthogonal laminated fabric. .
이들의 보강층은, 본 발명의 보수·보강용 시트 전체로서의 강도가 콘크리트 구조물의 일부가 박리된 경우에 박리된 콘크리트편을 지지할 수 있는 강도가 확보될 수 있을 정도이면 보강층자체의 강도에 제한은 없는데, 일본도로공단이 규정하는 압발(押拔)시험에 있어서, 압발력이 1500N 이상으로 된 시점에서 10mm이상의 변위를 유지하는 것이 바람직하고, 보호층과 부착층만의 적층체로 상기 보강범위가 만족되는 경우는, 보강층을 설치할 필요는 없다. 또한, 본 명세서에서 시트라고 칭하는 것은 두께나 강성에 제한되는 것은 아니고 얇고 유연성이 풍부한 필름이나 비교적 강성이 높은 판형상의 것도 포함되는 것이다.These reinforcement layers are not limited to the strength of the reinforcement layer itself as long as the strength of the repair / reinforcement sheet of the present invention is sufficient to secure the strength of the peeled concrete piece when a part of the concrete structure is peeled off. In the compression test prescribed by the Japan Highway Corporation, it is desirable to maintain a displacement of 10 mm or more at the time when the pressing force becomes 1500 N or more, and the reinforcement range is satisfied by the laminate of the protective layer and the adhesive layer only. In this case, it is not necessary to provide a reinforcing layer. In addition, what is called a sheet in this specification is not restrict | limited to thickness and rigidity, A thin and flexible film and a plate-shaped thing with comparatively high rigidity are included.
상기 설명한 적층체에 있어서, 보호층은 내후성, 방오성, 방수성이나 차염성 등의 기능을 부여하는 외층이고, 불소계수지, 아크릴계수지, 아크릴실리콘계수지, 아크릴불소계수지, 실리콘계수지, 우레탄계수지 및 염소계수지로 이루어지는 군 중에서 선택되는 1종 또는 2종 이상의 합성수지로 이루어지는 합성수지층인 것이 바람직하다. 이들의 합성수지층의 형성은 적층시에 수지를 용융압출하여도 좋지만, 미리 필름으로 성형된 것을 사용하면 보강층이나 부착층의 적층작업이 용이하게 되어 바람직하다. 이들의 합성수지층은 복수의 합성수지가 혼합되어도 좋고, 다층으로 적층되어도 좋다. 그리고, 오염부착방지의 관점에서는, 상기 보호층이 산화티타늄 등의 금속산화물로 이루어지는 광촉매층을 그 표면에 설치하고, 자기세정기능을부여하는 것이 바람직하다.In the laminate described above, the protective layer is an outer layer that provides functions such as weather resistance, antifouling property, waterproofness, or flame retardancy, and includes fluorine resin, acrylic resin, acrylic silicone resin, acrylic fluorine resin, silicone resin, urethane resin, and chlorine resin. It is preferable that it is a synthetic resin layer which consists of 1 type, or 2 or more types of synthetic resin chosen from the group which consists of. Although the formation of these synthetic resin layers may melt-extrude resin at the time of lamination | stacking, it is preferable to use the thing shape | molded previously with the film by making it easy to laminate | stack a reinforcement layer and an adhesion layer. These synthetic resin layers may be mixed with a plurality of synthetic resins or may be laminated in multiple layers. From the standpoint of prevention of contamination adhesion, it is preferable that the protective layer is provided with a photocatalyst layer made of a metal oxide such as titanium oxide on the surface thereof to impart a self-cleaning function.
콘크리트 구조물의 보수·보강용 시트는 시공작업중에 표면이 오염되거나, 파손, 상처가 생길 수 있으므로, 보호층의 외면에, 그들을 방지하기위해 폴리에틸렌테레프탈레이트(PET) 등의 폴리에스테르필름, 6나일론 등의 폴리아미드필름이나 폴리에틸렌이나 폴리플로필렌 등의 폴리올레핀계 필름에 아크릴계 혹은 고무계 등의 점착제로 미(微)점착가공된 박리가능한 마스킹필름을 피복하여 두는 것이 바람직하다. 특히, 보수·보강용 시트를 시공할 때, 가열롤러를 사용하여 압착하는 경우가 있으므로, 내열성 및 강도가 우수한 PET필름이 바람직하다.Repair and reinforcement sheets of concrete structures may be contaminated, damaged or damaged during construction work, so to prevent them on the outer surface of the protective layer, polyester films such as polyethylene terephthalate (PET), 6 nylon, etc. It is preferable to coat a peelable masking film which is microadhesive processed with an adhesive such as acrylic or rubber on a polyamide film or a polyolefin film such as polyethylene or polyflopropylene. Especially when constructing a sheet for repair and reinforcement, since it may be crimped | bonded using a heating roller, PET film excellent in heat resistance and strength is preferable.
박리가능한 마스킹필름의 점착층은, 마스킹필름을 적층하는 것으로 보수·보강용 시트가 딱딱하게 되어 시공시에 굴곡부로의 추종성이 저하하는 것을 방지하기위함과, 시공후에 마스킹필름의 박리개시를 용이하게 하기위해서, 부분접착, 예를들면 메시형상, 점형상, 힘줄형상 등의 형태로 설치하는 것이 바람직하다.The adhesive layer of the peelable masking film is a lamination of the masking film to prevent the repair and reinforcement sheet from becoming hard and to prevent the followability to the bent portion during construction, and to easily start peeling off of the masking film after construction. For the sake of clarity, it is preferable to install in the form of partial bonding, for example, mesh, point, tendon, or the like.
더욱이, 상기 설명한 적층체에 있어서, 부착층으로서는, 콘크리트 구조물과 접착하기위한 접착제와 일체화하여 접착제층의 일부로 되는 것이므로, 층이 벌어지거나 층간박리하거나 하는 일이 없도록 시공시에 사용하는 접착제와 익숙해지기 좋고, 접착제를 층전체에 함침시키기 쉬운 것이 바람직하다. 이 관점에서는, 직포, 편포, 부직포, 적층포 및 종이 중에서 선택되는 섬유기재로 이루어지는 것이 바람직하고, 섬유기재로서는 펄프나 면, 모시 등의 천연섬유, 폴리에스테르섬유, 폴리아미드섬유, 비니론섬유, 카본섬유, 유리섬유 및 폴리오레핀섬유로 이루어지는 군 중에서 선택되는 1종 또는 2종 이상의 섬유로 이루어지는 것이 바람직하다. 이들의 섬유는 혼방되어도 좋고, 종사, 횡사로 나누어 사용되어도 좋고, 다층으로 적층되어도 좋다. 종이는 코루게이트가공되어도 좋다.Furthermore, in the laminate described above, the adhesive layer is integrally formed with the adhesive for bonding with the concrete structure to be part of the adhesive layer, so that the adhesive layer is used with the adhesive used during construction so that the layer does not open or peel off. It is preferable that it is good and it is easy to impregnate an adhesive agent whole layer. From this point of view, it is preferable that the fiber base material is selected from woven fabrics, knitted fabrics, nonwoven fabrics, laminated fabrics, and paper. As the fiber base material, natural fibers such as pulp, cotton, and ramie, polyester fibers, polyamide fibers, Vinyron fibers, It is preferable that it consists of 1 type, or 2 or more types of fiber chosen from the group which consists of carbon fiber, glass fiber, and polyolefin fiber. These fibers may be mixed, may be divided into solid and horizontal yarns, and may be laminated in multiple layers. The paper may be corrugated.
이들중에서도 접착제가 침투, 함침되는 정도로 눈이 거칠고, 얇은 형상이 바람직하고, 건식부직포, 스펀본드타입, 멜트프론타입 등의 얇은 부직포나 직포, 적층포 등이 특히 바람직하다. 그리고, 상기 설명한 보강층과 동일한 섬유기재도 사용될 수 있다. 보강층과 동일한 섬유기재를 사용하면, 부착층이 보강층의 일부 또는 전부를 겸할 수 있고, 보수·보강용 시트를 얇고, 유연한 것으로 할 수 있으므로 바람직하다.Among these, an eye is rough enough to penetrate and impregnate an adhesive, and a thin shape is preferable, and thin nonwoven fabrics, such as a dry nonwoven fabric, a spun bond type, and a melt front type, a woven fabric, a laminated fabric, etc. are especially preferable. In addition, the same fiber base as the above-described reinforcing layer may be used. It is preferable to use the same fiber base as the reinforcing layer because the adhesive layer can serve as part or all of the reinforcing layer, and the sheet for repair and reinforcement can be made thin and flexible.
그리고, 더욱이, 본 발명은, 상기 설명한 콘크리트 구조물의 보수·보강용 시트를 콘크리트 구조물의 표면에 접착제를 통해서 부착하는 것을 특징으로 하는 콘크리트 구조물의 보수·보강방법을 제공한다.Moreover, this invention provides the repair and reinforcement method of the concrete structure characterized by attaching the above-mentioned repairing and reinforcing sheet of the concrete structure to the surface of the concrete structure through an adhesive agent.
본 발명의 콘크리트 구조물의 보수·보강방법은, 상기 설명한 콘크리트 구조물의 보수·보강용 시트의 부착층을, 접착제층을 통해서, 콘크리트 구조물에 부착한다.The repair and reinforcement method of the concrete structure of this invention attaches the adhesion layer of the sheet | seat for repair and reinforcement of the concrete structure mentioned above to a concrete structure through an adhesive bond layer.
여기서, 접착제층으로서는, 에폭시계 접착제, 우레탄계 접착제, 실리콘계 접착제, 고무계 접착제, 아크릴계 접착제, 폴리머시멘트계 접착제, 비닐에스테르계 접착제, 폴리에스테르계 접착제 및 폴리올레핀계 접착제로 이루어지는 군에서 선택되는 1종 또는 2종 이상의 접착제로 이루어지는 접착제층인 것이 바람직하다.Here, the adhesive layer may be one or two selected from the group consisting of an epoxy adhesive, a urethane adhesive, a silicone adhesive, a rubber adhesive, an acrylic adhesive, a polymer cement adhesive, a vinyl ester adhesive, a polyester adhesive, and a polyolefin adhesive. It is preferable that it is an adhesive bond layer which consists of above adhesive agents.
이들의 접착제는 높은 접착강도가 얻어지므로 경화형의 접착제가 바람직하다. 경화형의 접착제라면 상온경화형, 가열경화형, 전자선경화형이라도 좋고, 경화방법에는 특히 제한되지 않는다. 이들의 접착제층은 2종류 이상을 적층해도 좋다. 이들의 접착제중에서도, 접착강도가 높고, 내후성이 우수하므로 에폭시계 접착제가 바람직하고, 2액(液)경화형 에폭시계 접착제가 특히 바람직하다.Since these adhesives have a high adhesive strength, a curable adhesive is preferable. The curing adhesive may be a room temperature curing type, a heat curing type, or an electron beam curing type, and the curing method is not particularly limited. You may laminate | stack two or more types of these adhesive bond layers. Among these adhesives, epoxy adhesives are preferable because of their high adhesive strength and excellent weather resistance, and two-component curing type epoxy adhesives are particularly preferred.
(발명의 실시의 형태)(Embodiment of invention)
다음에 본 발명의 실시의 형태를 도면에 근거하여 설명한다.EMBODIMENT OF THE INVENTION Next, embodiment of this invention is described based on drawing.
도 1은, 본 발명에 관한 콘크리트 구조물의 보수·보강용 시트의 1실시형태를 도시하는 단면도이다.BRIEF DESCRIPTION OF THE DRAWINGS It is sectional drawing which shows one Embodiment of the sheet | seat for repair and reinforcement of the concrete structure which concerns on this invention.
이 시트는 다음의 수순으로 적층된다.This sheet is laminated in the following procedure.
먼저, 보호층인 폴리불화비닐필름(1)에 우레탄계 2액경화형 접착제(2)를 도포·건조하고, 보강층인 비니론 3축 메시(3)와 부착층인 폴리에스테르섬유로 이루어지는 스펀본드부직포(4)를 겹쳐서 드라이라미네이트로 하여, 전체로서 콘크리트 구조물의 보수·보강용 시트가 형성된다.First, a urethane-based two-liquid curable adhesive 2 is applied and dried on a polyvinyl fluoride film 1 as a protective layer, and a spunbond nonwoven fabric comprising a Viniron triaxial mesh 3 as a reinforcing layer and polyester fiber as an adhesive layer ( By laminating 4) as a dry laminate, the sheet for repair and reinforcement of a concrete structure is formed as a whole.
여기서 사용되는 보호층으로 되는 합성섬유층은 보강층이나 부착층의 위에 용융압출 등의 방법으로 형성되어도 좋은데, 필름에 성형된 것을 드라이 라미네이트나 압출샌드 라미네이트, 히트 라미네이트 등의 방법으로 보강층이나 부착층에 적층해도 좋다.The synthetic fiber layer used as the protective layer used herein may be formed by a method such as melt extrusion on the reinforcing layer or the adhesion layer, and the molded product is laminated on the reinforcement layer or the adhesion layer by a method such as dry laminate, extrusion sand laminate, or heat laminate. You may also
도 2는, 상기 설명한 콘크리트 구조물의 보수·보강용 시트를 콘크리트 구조물의 표면에 시공한 1실시형태를 도시한다. 이 보수·보강시공은 다음의 수순으로 시공된다.FIG. 2 shows an embodiment in which the repair / reinforcement sheet of the concrete structure described above is constructed on the surface of the concrete structure. This repair and reinforcement construction is constructed in the following procedure.
먼저, 콘크리트 구조물(6)의 표면을 디스크샌더 등에 의해 레이턴스처리 및기복수정을 시행한 후, 프라이머제를 도포, 건조후, 이 표면에 에폭시수지 접착제(5)를 도포한다. 이 표면에, 상기 설명한 콘크리트 구조물의 보수·보강용 시트의 부직포(4)로 이루어지는 부착층을 통해서 부착한다. 접착제(5)는 부직포(4)로 이루어지는 부착층에 함침되고, 콘크리트 구조물의 보수·보강용 시트는 콘크리트 구조물(6)의 표면에 견고히 접착된다.First, the surface of the concrete structure 6 is subjected to a latent treatment and relief modification with a disk sander or the like, and then a primer is applied and dried, and then the epoxy resin adhesive 5 is applied to the surface. It adheres to this surface through the adhesion layer which consists of the nonwoven fabric 4 of the sheet | seat for repair and reinforcement of the concrete structure demonstrated above. The adhesive agent 5 is impregnated into an adhesive layer made of the nonwoven fabric 4, and the sheet for repair and reinforcement of the concrete structure is firmly adhered to the surface of the concrete structure 6.
도 3은 본 발명에 관한 콘크리트 구조물의 보수·보강용 시트의 다른 실시의 형태를 도시하는 단면도이다.It is sectional drawing which shows other embodiment of the sheet | seat for repair and reinforcement of the concrete structure which concerns on this invention.
이 시트는 다음의 수순으로 적층된다.This sheet is laminated in the following procedure.
먼저, 폴리불화비닐필름(11)과 저밀도 폴리에틸렌필름(13)을 접착제(12)로 드라이 라미네이트하고, 보호층을 형성한다. 이어서, 이 보호층과 보강층으로서의 비니론 3축 메시(15)를 저밀도 폴리에틸렌(14)으로 압출 라미네이트함과 동시에 부착층으로서의 폴리에스테르섬유로 이루어지는 스펀본드 부직포(17)를 저밀도 폴리에틸렌(16)으로 압출 라미네이트하여, 전체로서 콘크리트 구조물의 보수·보강용 시트가 형성된다.First, the polyvinyl fluoride film 11 and the low density polyethylene film 13 are dry laminated with the adhesive 12, and a protective layer is formed. Subsequently, the protective layer and the Vininone triaxial mesh 15 as a reinforcing layer were extruded and laminated with the low density polyethylene 14, and the spunbonded nonwoven fabric 17 made of polyester fiber as the adhesion layer was extruded with the low density polyethylene 16. It laminates and the sheet | seat for repair and reinforcement of a concrete structure is formed as a whole.
도 4는 도 3의 콘크리트 구조물의 보수·보강용 시트를 콘크리트 구조물의 표면에 시공한 단면도이다.4 is a cross-sectional view of the repair and reinforcement sheet of the concrete structure of FIG. 3 constructed on the surface of the concrete structure.
도 1 내지 도 4에 도시한 본 발명에 의한 보수·보강용 시트 및 이들을 이용한 보수·보강방법은, 콘크리트 구조물의 표면에 에폭시수지 접착제를 도포하고, 섬유기재를 부착하고, 더욱이 접착제를 도포하여 굳히고, 건조고화후에 하도제, 내후성도료를 도포하는 종래법에 의한 보수·보강공법에 비하여 손색은 없었다.In the repair and reinforcement sheet and the repair and reinforcement method using the same according to the present invention shown in Figs. 1 to 4, an epoxy resin adhesive is applied to the surface of a concrete structure, a fiber base is attached, and the adhesive is further applied to harden it. Compared with the conventional method of repair and reinforcement by the conventional method of applying a primer and weather resistant paint after drying and solidification, there is no inferiority.
또한, 본 발명은 상기 구성에 한정되는 것은 아니고, 예를 들면, 본 발명의 보수·보강용 시트는 상기 이외에도,In addition, this invention is not limited to the said structure, For example, in addition to the above, the sheet | seat for repair and reinforcement of this invention,
·폴리불화비닐필름/접착제/방향족 폴리아미드메시/PET부직포Polyvinyl fluoride film / adhesive / aromatic polyamide mesh / PET nonwoven fabric
·폴리불화비닐필름/접착제/저밀도 폴리에틸렌필름/압출 폴리에틸렌/비니론메시/PET부직포Polyvinyl fluoride film / Adhesive / Low density polyethylene film / Extruded polyethylene / Vinyron mesh / PET nonwoven fabric
·폴리불화비닐필름/접착제/저밀도 폴리에틸렌필름/압출 폴리에틸렌/폴리에틸렌메시/압출 폴리에틸렌/PET부직포Polyvinyl fluoride film / adhesive / low density polyethylene film / extruded polyethylene / polyethylene mesh / extruded polyethylene / PET nonwoven fabric
·폴리불화비닐필름/접착제/방향족 폴리아미드부직포Polyvinyl fluoride film / adhesive / aromatic polyamide nonwoven fabric
·폴리불화비닐필름/접착제/저밀도 폴리에틸렌필름/압출 폴리에틸렌/PET부직포Polyvinyl fluoride film / adhesive / low density polyethylene film / extruded polyethylene / PET nonwoven fabric
·폴리불화비닐필름/접착제/PET부직포Polyvinyl fluoride film / adhesive / PET nonwoven fabric
·폴리불화비닐필름/접착제/PET직포Polyvinylidene fluoride film / adhesive / PET fabric
·폴리불화비닐필름/접착제/비니론직포Polyvinylidene fluoride film / adhesive / beanie cloth
등의 구성으로 할 수도 있다.It can also be set as the configuration.
본 발명에 관한 콘크리트 구조물의 보수·보강용 시트는 미리 가공하여 두므로, 충분한 품질관리를 행할 수 있고, 안정한 품질의 보수·보강용 시트를 제공할 수 있다. 또한, 본 발명에 관한 콘크리트 보수·보강방법은, 본 발명에 관한 콘크리트 구조물의 보수·보강용 시트를 시공현장에서 부착하므로써 행해지므로, 현장작업을 경감화할 수 있고, 공기를 단축화할 수 있어 공사코스트를 절감시키면서,종래와 동등 내지는 그 이상의 품질의 보수·보강방법을 제공할 수 있다.Since the sheet for repair and reinforcement of the concrete structure according to the present invention is processed in advance, sufficient quality control can be performed and a sheet for repair and reinforcement of stable quality can be provided. In addition, the repair and reinforcement method of the concrete according to the present invention is performed by attaching the repair and reinforcement sheet of the concrete structure according to the present invention at a construction site, whereby the field work can be reduced and the air can be shortened. It is possible to provide a repair and reinforcement method having a quality equivalent to or higher than that of conventional ones.
Claims (10)