JP5958244B2 - Color filter substrate and manufacturing method thereof - Google Patents

Description

  The present invention relates to a color filter substrate used in a flat display, for example, an electroluminescence display device, and a manufacturing method thereof.

At present, it can be said that the central presence in flat displays is a liquid crystal display, but as a flat display based on a display principle different from a liquid crystal display, an organic or inorganic electroluminescence (hereinafter abbreviated as EL) display device. Development of plasma display panels, light-emitting diode display devices, fluorescent display tube display devices, field emission displays, and the like has also been actively conducted.
These new flat displays are all called self-luminous displays, which consume less power, have better contrast, have almost no viewing angle dependency, and have faster response times and video afterimage problems compared to liquid crystal displays. It has excellent characteristics such as no occurrence. Recently, among these, EL display devices have been put into practical use mainly in mobile products such as in-vehicle navigation, mobile phones, and digital cameras. Mobile products are used in various environments due to their portability, and are particularly frequently used outdoors. However, when used outdoors, there is a problem that the display quality deteriorates due to the decrease in contrast and the occurrence of color mixing due to the influence of external light such as sunlight.
In order to suppress the influence of such external light, a circularly polarizing plate is provided on the front plate of the EL display device (Patent Document 1), and a colored layer is provided instead of the circularly polarizing plate (Patent Document 2). Proposing a light scattering layer containing fine particles (Patent Document 3) has been proposed.

JP 2004-205849 A JP 2005-317271 A JP 2007-287597 A

However, when a circularly polarizing plate is used, the light use efficiency from the EL element is poor, the luminance of the EL display device is insufficient, the cost of the circularly polarizing plate is high, and the manufacturing cost of the color filter substrate is reduced. There was a problem that there was a limit.
When a colored layer is used instead of the circularly polarizing plate, there is a problem in that although the use efficiency of light from the EL element is high, the color quality of the EL display device is affected and the display quality is lowered.
In addition, when the external light is appropriately scattered by the light scattering layer to suppress the reflected light, the light scattering efficiency is good, but the back scattering light is generated by the light scattering layer and the display becomes white. There has been a problem that the display quality is deteriorated. In addition, if the dispersibility of the fine particles contained in the light scattering layer is poor, appropriate scattering of external light cannot be obtained, and thus there is a problem that process management of the light scattering layer is complicated.
The present invention has been made in view of such circumstances, and suppresses the influence of white dust caused by external light and enables a high-contrast, high-brightness display and such a color filter substrate. It aims at providing the manufacturing method of.

  In order to solve such a problem, the present invention is a color filter substrate including a transparent substrate and a colored layer on the transparent substrate, and the colored layer includes a red colored layer, a green colored layer, and a blue colored layer. And a white colored layer, at least in the region where the white colored layer is located, there is a light scattering functional layer having a haze value in the range of 10 to 70. The light scattering functional layer comprises an organic film and a high refractive index film. And the organic film side is located on the transparent substrate side, the organic film has an uneven surface with the high refractive index film, and the refractive index of the organic film is the high refractive index The refractive index is smaller than the refractive index of the refractive index film.

  Moreover, the present invention is a color filter substrate comprising a transparent substrate and a colored layer on the transparent substrate, the colored layer having a red colored layer, a green colored layer, a blue colored layer and a white colored layer, The white colored layer is composed of a light scattering functional layer, the light scattering functional layer is formed by laminating an organic film and a high refractive index film, and the haze value is in the range of 10 to 70, and the organic film side is located on the transparent substrate side. The organic film has an uneven surface at the interface with the high refractive index film, and the refractive index of the organic film is smaller than the refractive index of the high refractive index film.

As another aspect of the present invention, the light scattering functional layer is configured to exist also in a region where the red colored layer, the green colored layer, and the blue colored layer are located.
As another aspect of the present invention, the high refractive index film is formed of silicon oxide, silicon nitride, silicon oxynitride, silicon carbide, titanium oxide, niobium oxide, indium oxide, zinc oxide, tin oxide or tantalum oxide, gallium, cerium. In addition, one or more materials selected from the group doped with any of aluminum, carbon, tin, and boron are included.
As another aspect of the present invention, the maximum roughness (Rmax) of the irregular surface of the organic film is 10 μm or less.
As another aspect of the present invention, a planarization layer is provided on the high refractive index film of the light scattering functional layer.
In another embodiment of the present invention, the organic film has a thickness in the range of 0.1 to 10 μm.
As another aspect of the present invention, the difference between the refractive index of the high refractive index film and the refractive index of the organic film is 0.4 or more.

  The present invention also relates to a light scattering function present in a transparent substrate, a colored layer having a red colored layer, a green colored layer, a blue colored layer and a white colored layer on the transparent substrate, and at least a region where the white colored layer is located. A method of manufacturing a color filter substrate comprising a layer, wherein after forming an organic resin layer for forming an organic film, a high refractive index film is formed on the organic resin layer, and then subjected to heat treatment to form the organic resin layer. The light which is a laminate of the organic film and the high refractive index film and the organic film side is located on the transparent substrate side by contracting the resin layer to generate an uneven surface at the interface with the high refractive index film It was set as the structure which has the process of forming a scattering function layer.

The present invention also includes a transparent substrate and a colored layer having a red colored layer, a green colored layer, a blue colored layer and a white colored layer on the transparent substrate, and the white colored layer is a color filter comprising a light scattering functional layer. A method for manufacturing a substrate, wherein after forming an organic resin layer for forming an organic film, a high refractive index film is formed on the organic resin layer, and then heat treatment is performed to shrink the organic resin layer. By forming an uneven surface at the interface with the high refractive index film, the light scattering function layer is formed by laminating the organic film and the high refractive index film and the organic film side is located on the transparent substrate side. It was set as the structure which has a process to do.
The electroluminescence display device of the present invention includes a color filter substrate and an electroluminescence element side substrate, and the color filter substrate is any one of the color filter substrates described above.

In the color filter substrate of the present invention, external light incident from the transparent substrate side is moderately scattered by the light scattering functional layer, so that generation of external light regular reflection light and backscattered light is suppressed, thereby causing external light. The generation of white dust is suppressed, and the haze value of the light-scattering functional layer is set to an appropriate range, so the light utilization efficiency from the light emitter is good, and high-contrast and high-luminance display is possible. It can be.
In the method for producing a color filter substrate of the present invention, an expensive circularly polarizing plate is unnecessary, and complicated process management for forming a light scattering layer in which fine particles are uniformly dispersed is unnecessary. The manufacturing cost can be reduced. In addition, since the uneven surface is formed at the interface with the high refractive index film using the stress generated by the difference in thermal shrinkage behavior between the organic resin layer and the high refractive index film, the uneven surface can be easily formed.

FIG. 1 is a cross-sectional view showing an embodiment of a color filter substrate of the present invention. FIG. 2 is a cross-sectional view showing another embodiment of the color filter substrate of the present invention. FIG. 3 is a cross-sectional view showing another embodiment of the color filter substrate of the present invention. FIG. 4 is a process diagram for explaining an embodiment of a method for producing a color filter substrate of the present invention. FIG. 5 is a schematic configuration diagram showing an embodiment of an EL display device of the present invention.

  Hereinafter, embodiments of the present invention will be described with reference to the drawings. Note that the drawings are schematic or conceptual, and the dimensions of each member, the ratio of sizes between the members, etc. are not necessarily the same as the actual ones, and represent the same members. However, in some cases, the dimensions and ratios may be different depending on the drawing.

[Color filter substrate]
FIG. 1 is a cross-sectional view showing an embodiment of a color filter substrate of the present invention. In FIG. 1, the color filter substrate 1 includes a transparent substrate 2, a colored layer 3 disposed on the transparent substrate 2, and a light scattering functional layer 5 laminated so as to cover the colored layer 3. Yes. The colored layer 3 has a red colored layer 3R, a green colored layer 3G, a blue colored layer 3B, and a white colored layer 3W, and a light shielding layer is provided at the boundary between the colored layers 3R, 3G, 3B, 3W of the respective colors. 4 is located.
FIG. 2 is a cross-sectional view showing another embodiment of the color filter substrate of the present invention. In FIG. 2, the color filter substrate 1 ′ is a transparent substrate 2, a light scattering functional layer 5 positioned on the transparent substrate 2, and a color disposed on the light scattering functional layer 5 via the planarization layer 8. Layer 3. The color filter substrate 1 ′ is different from the color filter substrate 1 described above in that the position of the colored layer 3 in the layer configuration is on the opposite side of the transparent substrate 2 with the light scattering functional layer 5 interposed therebetween. The same members as those constituting the substrate 1 are denoted by the same member numbers.
In the present invention, the haze value of the light scattering functional layer 5 constituting the color filter substrate 1, 1 'is in the range of 10 to 70, preferably 20 to 60. This light scattering functional layer 5 is formed by laminating an organic film 6 and a high refractive index film 7, and the organic film 6 side is located on the transparent substrate 2 side. The organic film 6 constituting the light scattering functional layer 5 has an uneven surface 6 a at the interface with the high refractive index film 6, and the refractive index of the organic film 6 is smaller than the refractive index of the high refractive index film 7. It is.

  In the illustrated example, the light scattering functional layer 5 is disposed in a region where the colored layers 3R, 3G, 3B, 3W constituting the colored layer 3 are located. However, the color filter substrate of the present invention is colored at least white. It is necessary that the light scattering functional layer 5 is disposed in a region where the layer 3W is located. This is because generation of white dust due to external light in the white colored layer 3W is more noticeable than in the colored layers 3R, 3G, 3B. Therefore, the light scattering functional layer 5 may be disposed only in the region where the white colored layer 3W is located. 3, the color filter substrate 1 ″ in which the white colored layer 3W also serves as the light scattering functional layer 5 may be used. In this case, the light scattering function is also provided on the colored layers 3R, 3G, and 3B. A layer 5 may be provided.

Next, each configuration of the color filter substrate of the present invention will be described.
<Transparent substrate>
The transparent substrate 2 is not particularly limited as long as it is a substrate transparent to visible light, and the same transparent substrate used for a general color filter can be used. Specifically, a rigid material such as quartz glass, Pyrex (registered trademark) glass, or synthetic quartz, or a transparent flexible material having flexibility such as a transparent resin film or an optical resin plate can be used.
In the present invention, the term “transparent” means that the total light transmittance in the sample is 99% or more.

<Colored layer>
As described above, the colored layer 3 includes the red colored layer 3R, the green colored layer 3G, the blue colored layer 3B, and the white colored layer 3W, and is located in the pixel region. Such colored layers 3R, 3G, 3B, 3W are arranged in a pattern. This pattern arrangement is not particularly limited to that shown in the figure, and can be a known arrangement such as a stripe type, a mosaic type, a triangle type, or a four-pixel arrangement type. The ratio can be arbitrarily set.
Such a colored layer 3 may contain, for example, a colorant or the like in a binder resin, and a material generally used for a color filter is used as a forming material for the binder resin and the colorant. Can do. Examples of the colorant used in the red coloring layer 3R include perylene pigments, lake pigments, azo pigments, quinacridone pigments, anthraquinone pigments, anthracene pigments, isoindoline pigments, and the like. You may use individually or in mixture of 2 or more types. The colorant used for the green colored layer 3G includes phthalocyanine pigments such as halogen polysubstituted phthalocyanine pigments or halogen polysubstituted copper phthalocyanine pigments, triphenylmethane basic dyes, isoindoline pigments, and isoindolinone. These pigments or dyes may be used alone or in admixture of two or more. Further, examples of the colorant used for the blue colored layer 3B include copper phthalocyanine pigments, anthraquinone pigments, indanthrene pigments, indophenol pigments, cyanine pigments, dioxazine pigments, and the like. You may use individually or in mixture of 2 or more types. Further, the white colored layer 3W may be made of a binder resin used for the red colored layer 3R, the green colored layer 3G, and the blue colored layer 3B, and in the binder resin for the purpose of adjusting the white chromaticity. In addition, a color material such as a purple color material or a blue color material may be contained.

<Light shielding layer>
The light-shielding layer 4 is located in the non-pixel region, and is, for example, a stripe shape or a lattice shape parallel to each other, a material containing a black pigment in a binder resin, a material made of a metal thin film such as chromium, etc. It may be.

<Light scattering functional layer>
The light scattering functional layer 5 is a layer for appropriately scattering light incident on the color filter substrate 1 from the transparent substrate 2 side to suppress the generation of externally reflected light and backscattered light toward the transparent substrate 2 side. As described above, the haze value is in the range of 10 to 70, preferably 20 to 60. If the haze value of the light scattering functional layer 5 is less than 10, the light scattering function by the light scattering functional layer 5 is insufficient, and if it exceeds 70, the light emitter when the color filter substrate is used in a display device The utilization efficiency of light from is low, and the luminance is insufficient, which is not preferable. Here, the haze value is obtained by (diffuse light transmittance / total light transmittance) × 100, and can be measured using a haze meter (HM-150 type) manufactured by Murakami Color Research Laboratory. it can.
As described above, the light scattering functional layer 5 is formed by laminating the organic film 6 and the high refractive index film 7, and the organic film 6 side is located on the transparent substrate 2 side. The organic film 6 constituting the light scattering functional layer 5 has an uneven surface 6 a at the interface with the high refractive index film 7, and the refractive index of the organic film 6 is higher than the refractive index of the high refractive index film 7. Is also small. Here, the refractive index can be measured by a spectroscopic ellipsometer (UVISEL manufactured by Joban-Evon).

  The organic film 6 constituting the light scattering functional layer 5 can be formed using a transparent resin having a refractive index smaller than the refractive index of the high refractive index film 7. Examples of the transparent resin include acrylic resins, epoxy resins, polyvinyl alcohol resins, polyimide resins, vinyl ether resins, benzyl methacrylate: styrene: acrylic acid: 2-hydroxyethyl methacrylate copolymer, polycarbonate resin, polyurethane. Resins, polyester resins, maleic acid resins, polyamide resins and the like can be used alone or in combination of two or more. The transparent resin forming the organic film 6 may be the same resin material as the binder resin of the colored layer 3 described above. For example, in the above-described color filter substrate 1 ″, the same resin as the binder resin of the white colored layer 3W is used. An organic film 6 is formed using a material.

  The organic film 6 may be a transparent resin containing a desired color material. As the color material, a black color material or a colored color material can be appropriately used. The black color material has a function of adjusting the transmittance of the organic film 6, and when backscattered light is generated in the light scattering of external light at the interface between the uneven surface 6 a of the organic film 6 and the high refractive index film 7, For example, carbon black, titanium black, titanium nitride, titanium nitride oxide, and titanium carbide can be used. Further, as the coloring color material, for example, backscattered light is generated in the light scattering of the external light at the interface between the uneven surface 6a of the organic film 6 and the high refractive index film 7, and a yellowish color shift occurs. In this case, yellowing can be suppressed by using a blue color material. Therefore, the light scattering function layer 5 can be provided with the function of adjusting the color shift caused by the external light by containing the desired coloring material in the organic film 6. As such a coloring material, in addition to a blue coloring material, a green coloring material, a red coloring material, a yellow coloring material, a purple coloring material, and the like can be given, and these coloring coloring materials are used in combination. be able to.

  The uneven surface 6a of the organic film 6 is provided in order to appropriately scatter external light incident from the transparent substrate 2 side at the interface between the organic film 6 and the high refractive index film 7, and the maximum roughness of the uneven surface 6a. The thickness (Rmax) is 10 μm or less, preferably in the range of 0.5 to 8 μm. If the maximum roughness (Rmax) of the concavo-convex surface 6a exceeds 10 μm, the effect of suppressing the occurrence of externally reflected light is insufficient, which is not preferable. Here, the maximum roughness (Rmax) of the concavo-convex surface 6a is an atomic force microscope (AS-7B-M, manufactured by Takano Co., Ltd.) and a stylus type film thickness meter (P-15, manufactured by KLA-Tencor Japan Co., Ltd.). (Atomic force microscope is used when Rmax is less than 1 μm, and a stylus thickness meter is used when Rmax is 1 μm or more). Further, when the thickness variation of the high refractive index film 7 is 0.1 μm or less, it is considered that the shape of the uneven surface 6 a of the organic film 6 is reflected on the surface of the high refractive index film 7. The maximum roughness (Rmax) of the rate film 7 can be measured to obtain the maximum roughness (Rmax) of the uneven surface 6a. In addition, the thickness of the high refractive index film | membrane 7 can be measured using a stylus-type film thickness meter (P-15 by KLA-Tencor Japan Co., Ltd.).

The thickness of the organic film 6 is in the range of 0.1 to 10 μm, preferably 1 to 8 μm. The thickness of the organic film 6 is, for example, the average thickness from the interface with the colored layer 3 to the uneven surface 6a in the color filter substrate 1, and the uneven surface 6a from the interface with the transparent substrate 2 in the color filter substrate 1 ′. It is the average of thickness until. The thickness of such an organic film 6 can be measured using a stylus type film thickness meter (P-15 manufactured by KLA-Tencor Japan Co., Ltd.). If the thickness of the organic film 6 is less than 0.1 μm, the formation of the uneven surface becomes insufficient, so that the influence of external light cannot be reduced and sufficient display quality cannot be obtained. On the other hand, when the thickness exceeds 10 μm, the luminance is lowered and the display quality may be deteriorated.
The high refractive index film 7 constituting the light scattering functional layer 5 is provided to appropriately scatter external light incident from the transparent substrate 2 side at the interface with the organic film 6. Such a high refractive index film 7 includes a material having a refractive index larger than the refractive index of the organic film 6. The material may be any of an inorganic material, an organic material, and an inorganic-organic composite material. Good. Examples of the inorganic material include silicon oxide, silicon nitride, silicon oxynitride, silicon carbide, titanium oxide, niobium oxide, indium oxide, zinc oxide, tin oxide or tantalum oxide, gallium, cerium, aluminum, carbon, tin and boron. One or more inorganic materials selected from the group doped with any of the above can be mentioned, and the high refractive index film 7 can be formed by a vacuum film formation method such as a sputtering method, a chemical vapor deposition method, or the like. .
The difference between the refractive index of the high refractive index film 7 and the refractive index of the organic film 6 is 0.3 or more, preferably 0.4 or more, and the difference in refractive index between the two is less than 0.3. Further, light scattering at the interface between the high refractive index film 7 and the uneven surface 6a of the organic film 6 is not preferable. The thickness of the high refractive index film 7 is not particularly limited, and the high refractive index film 7 formed by a vacuum film forming method is formed by, for example, a chemical vapor deposition method in a range of 0.01 to 0.5 μm. In the high refractive index film | membrane 7, it can set suitably in the range of 1-10 micrometers, for example.

<Planarization layer>
The flattening layer 8 constituting the color filter substrate 1 ′ is provided in order to form the colored layer 3 with high accuracy on the light scattering function layer 5 having an uneven shape. For example, the planarizing layer 8 is formed by appropriately selecting from the resin materials mentioned as the transparent resin constituting the organic film 6 of the light scattering functional layer 5 or the resin material used as the binder resin of the colored layer 3. Can do. And the refractive index of the planarization layer 8 is smaller than the refractive index of the high refractive index film 7, and the difference between the refractive index of the planarization layer 8 and the refractive index of the organic film 6 is ± 0.3 or less, The difference is preferably zero.
The thickness of the flattening layer 8 can be appropriately set as long as the surface on which the colored layer 3 is located is a flat surface, and is not particularly limited.

  In such a color filter substrate of the present invention, the external light incident from the transparent substrate 2 side is moderately scattered by the light scattering functional layer 5, so that the external light regular reflection light and the backscattered light are suppressed. As a result, when the color filter substrate of the present invention is used in a display device, the occurrence of white dust due to external light is suppressed, and the haze value of the light scattering function layer 5 is set to an appropriate range. Therefore, the utilization efficiency of light from the light emitter is good, and display with high contrast and high luminance can be made possible.

The above-described embodiment of the color filter substrate is an example, and the present invention is not limited to such an embodiment. For example, the color filter substrate of the present invention may not have a light shielding layer. Further, on the light scattering functional layer 5 in the color filter substrate 1, on the colored layer 3 in the color filter substrate 1 ', 1 ", any one of a planarization layer, a gas barrier layer, a transparent electrode layer, etc., or two or more kinds In the color filter substrate 1, the planarizing layer absorbs the uneven shape of the light scattering functional layer 5 to expose the planarized surface, and the color filter substrate 1 ′, 1 ″. Then, the uneven | corrugated shape in the colored layer 3 is absorbed and a planarization surface is exposed, and it can be the same as that of the above-mentioned planarization layer 8. The gas barrier layer prevents the light emitting layer from being deteriorated by the gas generated from the constituent layers of the color filter substrate when the color filter substrate of the present invention is used in an EL display device. It may be made of a material such as silicon nitride or silicon oxynitride.
The above-described color filter substrate of the present invention is used for EL display devices, plasma display panels, light emitting diode display devices, fluorescent display tube display devices, self-luminous display devices such as field emission displays, and liquid crystal displays. can do.

[Color filter substrate manufacturing method]
FIG. 4 is a process diagram for explaining an embodiment of the method for producing a color filter substrate of the present invention, and illustrates the above-described color filter substrate 1 of the present invention as an example.
In FIG. 4, first, the light shielding part 4 is formed on the transparent substrate 2, and then the colored layer 3 having the red colored layer 3R, the green colored layer 3G, the blue colored layer 3B, and the white colored layer 3W is formed ( FIG. 4 (A)).
The light shielding part 4 can be formed by a method for forming a light shielding part in a general color filter. For example, a thin film can be formed by a vacuum film forming method using a metal material, and this thin film can be formed by pattern etching. Moreover, the light-shielding part 4 can also be formed by the vacuum film-forming method through a mask. Furthermore, it can be formed by applying a coating liquid containing light-shielding particles such as black pigment in the binder resin, and then pattern etching, and using the above-mentioned photosensitive coating liquid It can also be formed by photolithography.
The colored layer 3 can be formed using a method for forming a colored layer in a general color filter, for example, a photolithography method, an inkjet method, a printing method, an electrodeposition method, or the like. In addition, as materials for forming the colored layer 3 such as a binder resin and a colorant, materials generally used for color filters can be used.

Next, an organic resin layer 6 'for forming an organic film is formed on the colored layer 3, and then a high refractive index film 7 is formed on the organic resin layer 6' (FIG. 4B). The resin material used for forming the organic resin layer 6 ′ is glass among the resin materials mentioned as the transparent resin constituting the organic film 6 of the light scattering function layer 5 in the description of the color filter substrate of the present invention. A resin material having a relatively low transition temperature (Tg), for example, a Tg of 150 ° C. or lower can be used. When the material of the high refractive index film 7 is an organic material, an organic resin is used by using a resin material having a Tg lower than that of the organic material contained in the high refractive index film 7, for example, a Tg of 10 ° C. or lower. Layer 6 'is formed. The organic resin layer 6 ′ can be formed by applying a coating solution for forming an organic film by a general application means such as a spin coating method, a die coating method, or an ink jet method. The thickness of the organic resin layer 6 ′ can be set in the range of 1 to 10 μm, preferably 1.5 to 10 μm, in order to facilitate the formation of the uneven surface by shrinkage in the process described later.
Moreover, in this invention, you may use the material used for formation of organic resin layer 6 'for formation of the above-mentioned white colored layer 3W. In this case, the light scattering functional layer 5 can be formed as the white colored layer 3W as in the above-described color filter substrate 1 ″.

  Further, the high refractive index film 7 is an inorganic material, an organic material, or an inorganic organic composite material that is cited as the material constituting the high refractive index film 7 of the light scattering function layer 5 in the description of the color filter substrate of the present invention. Any of them may be formed. Among these materials, an inorganic material can be particularly preferably used in order to facilitate formation of an uneven surface due to the shrinkage of the organic resin layer 6 ′ in a process described later, and a high refractive index can be obtained by a vacuum film forming method such as a sputtering method. A film 7 can be formed. The thickness of the high refractive index film 7 to be formed is a thickness that does not hinder formation of the uneven surface due to the shrinkage of the organic resin layer 6 ′ in the process described later. For example, the high refractive index film using indium tin oxide (ITO) 7 can be set in the range of 0.01 to 0.6 μm, preferably 0.01 to 0.5 μm, and the thickness of the high refractive index film 7 can be appropriately set according to the material used.

  Next, heat treatment is performed to shrink the organic resin layer 6 ′ to form an uneven surface 6 a at the interface with the high refractive index film 7, and a light scattering functional layer that is a laminate of the organic film 6 and the high refractive index film 7. 5 is formed (FIG. 4C). The temperature of the heat treatment is a temperature equal to or higher than the Tg of the organic resin layer 6 ′, and preferably about 20 to 80 ° C. higher than the Tg. By this heat treatment, the uneven surface 6a is formed at the interface with the high refractive index film 7 by using the stress generated by the difference in thermal contraction behavior between the organic resin layer 6 'and the high refractive index film 7.

In such a method for producing a color filter substrate of the present invention, an expensive circularly polarizing plate is unnecessary, and complicated process management for forming a light scattering layer in which fine particles are uniformly dispersed is unnecessary, The manufacturing cost of the color filter substrate can be reduced. Further, the uneven surface 6a is formed at the interface with the high refractive index film 7 by utilizing the stress generated by the difference in heat shrinkage between the organic resin layer 6 'and the high refractive index film 7, so that the uneven surface can be easily formed. It is. In particular, for example, when the high refractive index film 7 is formed of indium tin oxide, a heat treatment for causing the organic resin layer 6 ′ to shrink and generating an uneven surface 6 a at the interface with the high refractive index film 7, The heat treatment for improving the transparency of indium tin oxide can be performed, and the process can be simplified.
Further, in the color filter substrate 1 ″ shown in FIG. 3, the organic resin layer 6 ′ and the high refractive index film 7 are formed in the region where the white colored layer is formed in the same manner as described above, and then heat treatment is performed. The organic resin layer 6 ′ is contracted to form an uneven surface 6 a at the interface with the high refractive index film 7, and the light scattering function layer 5, which is a laminate of the organic film 6 and the high refractive index film 7, is formed. It can be set as the colored layer 3W.
The above-described embodiment of the method for manufacturing a color filter substrate is an exemplification, and the present invention is not limited to this embodiment.

Moreover, as formation of the organic film 6 provided with the uneven surface 6a, the organic resin layer 6 'for organic film formation is formed using a photocurable resin composition, and the difference part of exposure amount arises after that. Examples thereof include a method of performing exposure such as patterning by photolithography, multistage exposure, gradation exposure, etc., and then developing.
In addition, an organic resin layer 6 'for forming an organic film is formed using a resin composition in which a photo-curable resin and a non-curable resin are mixed non-uniformly, and thereafter, exposure and development are performed to form an uneven surface. The organic film 6 provided with 6a can be formed.
In addition, a droplet of a photocurable resin is supplied to a predetermined location on the transparent substrate 2 by an ink jet method to form an organic resin layer 6 ', and an uneven shape due to the droplet remains on the surface of the organic resin layer 6'. In this state, the organic film 6 having the uneven surface 6a can be formed by performing exposure and development.
Furthermore, a laminate film having an organic film 6 having an uneven surface 6a on a resin base material may be bonded to the transparent substrate 2.

[EL display device]
Hereinafter, the EL display device of the present invention using the color filter substrate of the present invention will be described.
FIG. 5 is a schematic configuration diagram showing an embodiment of an EL display device of the present invention. In FIG. 5, an EL display device 11 is obtained by bonding and integrating the above-described color filter substrate 1 of the present invention and the electroluminescence element side substrate 21.
The color filter substrate 1 constituting the EL display device 11 is provided with a planarizing layer 9 on the light scattering functional layer 5.

The EL element side substrate 21 constituting the EL display device 11 includes a substrate 22 and a thin film transistor (TFT) 23 arranged on the substrate 22 for each pixel. The thin film transistor 23 controls the current flowing through the EL element 31 constituting the pixel to drive the EL element 31 by an active driving method. Normally, a circuit of each thin film transistor includes a gate line and a signal line (not shown). The power line is connected. A method of forming such a thin film transistor 23 can follow a known method. An insulating layer 24 is provided on the thin film transistor 23, and an EL element 31 is provided on the insulating layer 24. The EL element 31 has a light emitting layer 33 sandwiched between a lower electrode layer 32 and an upper electrode layer 34. The lower electrode layer 32 is connected to a corresponding thin film transistor 23 and corresponds to each pixel. An insulating layer (partition wall) 25 is disposed around the light emitting layer 33 positioned above to prevent a short circuit between the lower electrode layer 32 and the upper electrode layer 34. Further, a gas barrier layer 27 for mainly protecting the light emitting layer 33 is formed on the upper transparent electrode layer 34 so as to cover the entire element. As a forming material of each member constituting such an EL element side substrate 21, a material applied to a known EL element side substrate can be used.
After the EL element side substrate 21 and the color filter substrate 1 are arranged to face each other and aligned, an adhesive layer 29 formed by filling the gap between the EL element side substrate 21 and the color filter substrate 1 is used. 1 is joined and integrated to form an EL display device 11.

  The above-described embodiment of the EL display device is an exemplification, and the present invention is not limited to such an embodiment. For example, although the EL display device 11 is top emission, an EL element side substrate having a configuration in which the sealing layer 27 of the EL element side substrate 21 and the substrate 22 are reversed is used to cover the sealing layer 27 side. As described above, a bottom emission EL display device that is bonded to and integrated with the color filter substrate 1 by the adhesive layer 29 may be used. Further, the color filter substrate to be used may be any of the color filter substrates of the present invention including the above-described color filter substrates 1 ′ and 1 ″. Furthermore, the EL element may be either an organic EL element or an inorganic EL element. Alternatively, an EL display device in which a gas layer such as air is interposed between the color filter substrate 1 and the EL element side substrate 21 may be used.

Next, the present invention will be described in more detail with specific examples.
[Example 1]
<Preparation of color filter substrate>
As a substrate, a glass substrate (Corning 1737 glass) having a plane size of 100 mm × 100 mm and a thickness of 0.7 mm was prepared.

Next, the light shielding part was formed as follows.
First, curable resin composition A was prepared. That is, 63 parts by weight of methyl methacrylate (MMA), 12 parts by weight of acrylic acid (AA), 6 parts by weight of 2-hydroxyethyl methacrylate (HEMA), and 88 parts by weight of diethylene glycol dimethyl ether (DMDG) in the polymerization tank. After partly charged, stirred and dissolved, 7 parts by weight of 2,2′-azobis (2-methylbutyronitrile) was added and dissolved uniformly. Then, it stirred at 85 degreeC under nitrogen stream for 2 hours, and also was made to react at 100 degreeC for 1 hour. 7 parts by weight of glycidyl methacrylate (GMA), 0.4 parts by weight of triethylamine, and 0.2 parts by weight of hydroquinone were added to the resulting solution, and the mixture was stirred at 100 ° C. for 5 hours to obtain a copolymer resin solution ( A solid content of 50%) was obtained. Next, each material with the following composition was stirred and mixed at room temperature to obtain a curable resin composition A.
(Curable resin composition A)
-Copolymer resin composition (solid content 50%)-16 parts by weight-Dipentaerythritol pentaacrylate-24 parts by weight (SR399, manufactured by Sartomer)
・ Orthocresol novolac type epoxy resin: 4 parts by weight (Epicoat 180S70 manufactured by Yuka Shell Epoxy Co., Ltd.)
2-methyl-1- (4-methylthiophenyl) -2-morpholinopropane
1-one: 4 parts by weight Diethylene glycol dimethyl ether: 52 parts by weight

Subsequently, each material was mixed with the following composition, it fully disperse | distributed with the bead mill, and the black pigment dispersion liquid A was prepared.
(Black pigment dispersion A)
-Resin-coated carbon black: 20 parts by weight (Mitsubishi Chemical Corporation MS18E, average particle size 25 nm)
-Polymer dispersant: 5 parts by weight (Diaperbyk 163, manufactured by Big Chemie Japan Co., Ltd.)
・ Solvent (diethylene glycol dimethyl ether): 75 parts by weight

Next, each material was sufficiently mixed with the following composition, and the composition for light shielding parts was prepared.
(Composition for shading part)
Black pigment dispersion A: 43 parts by weight Curable resin composition A: 19 parts by weight Diethylene glycol dimethyl ether: 38 parts by weight

  The composition for light-shielding layer thus prepared was applied onto the glass substrate with a spin coater and dried at 100 ° C. for 3 minutes to form a light-shielding resin layer. A photomask is placed at a distance of 100 μm from this light-shielding resin layer, and after proximity exposure with a 2.0 kW ultrahigh pressure mercury lamp by a proximity aligner, development is performed with a 0.05 wt% aqueous potassium hydroxide solution. Thereafter, the glass substrate was left to stand in an atmosphere of 230 ° C. for 30 minutes to perform heat treatment, thereby forming a light shielding part (thickness: 1.3 μm). This light-shielding part had a shape in which openings of 39 μm × 39 μm were arranged in a matrix at a pitch of 45 μm in both the vertical and horizontal directions.

Next, negative photosensitive resin compositions for a red colored layer, a green colored layer, a blue colored layer, and a white colored layer shown below were prepared.
(Negative photosensitive resin composition for red colored layer)
・ Red pigment: 2.0 parts by weight (Chromophthal Red A2B, manufactured by Ciba Specialty Chemicals)
・ Red pigment: 1.0 part by weight (Chromophthal Red BP manufactured by Ciba Specialty Chemicals)
-Dispersant (Disperbic 161 manufactured by Big Chemie) ... 1.5 parts by weight-Monomer (SR399 manufactured by Sartomer)-4.0 parts by weight-Polymer I-5.0 parts by weight-Initiator: 1.4 parts by weight ( (Irgacure 907, manufactured by Ciba Specialty Chemicals)
・ Initiator: 0.6 parts by weight (2,2′-bis (o-chlorophenyl) -4,5,4 ′, 5′-
Tetraphenyl-1,2'-biimidazole)
・ Solvent: 80.0 parts by weight (propylene glycol monomethyl ether acetate)

(Negative photosensitive resin composition for green colored layer)
Green pigment (Dainic Seika Co., Ltd. Cyanine Green 5370) ... 1.2 parts by weight Green pigment (Daiichi Seika Co., Ltd. Cyanine Green 2GN) ... 1.6 parts by weight Yellow pigment ... 1.2 parts by weight (Lanxess) Byplast Yellow 5GN01)
・ Dispersant (Disperbic 161, manufactured by BYK-Chemie Corporation) 2.0 parts by weight Monomer (SR399, manufactured by Sartomer) 4.0 parts by weight Polymer I 5.0 parts by weight Initiator 1.4 parts by weight ( (Irgacure 907, manufactured by Ciba Specialty Chemicals)
・ Initiator: 0.6 parts by weight (2,2′-bis (o-chlorophenyl) -4,5,4 ′, 5′-
Tetraphenyl-1,2'-biimidazole)
・ Solvent: 80.0 parts by weight (propylene glycol monomethyl ether acetate)

(Negative photosensitive resin composition for blue colored layer)
・ Purple pigment: 0.6 parts by weight (Clariant Novotex Violet BL-PC VP2429)
Blue pigment (BASF Heliogen Blue L6700F) 1.4 parts by weight Pigment derivative (Abyssia Solsperse 5000) ... 0.2 parts by weight Dispersant (Bic Chemie Dispersic 161) 0.8 weight Part ・ Monomer (SR399 manufactured by Sartomer Co., Ltd.) 4.0 parts by weight Polymer I 5.0 parts by weight Initiator 1.4 parts by weight (Irgacure 907 manufactured by Ciba Specialty Chemicals)
・ Initiator: 0.6 parts by weight (2,2′-bis (o-chlorophenyl) -4,5,4 ′, 5′-
Tetraphenyl-1,2'-biimidazole)
・ Solvent: 80.0 parts by weight (propylene glycol monomethyl ether acetate)

(Negative photosensitive resin composition for white colored layer)
・ Purple pigment: 0.3 parts by weight (Clariant Novotex Violet BL-PC VP2429)
Blue pigment (BASF Heliogen Blue L6700F) 0.3 parts by weight Pigment derivative (Abyssia Solsperse 5000 ... 0.04 parts by weight Dispersant (Bicchemy Dispersic 161) 0.2 parts by weight・ Monomer (SR399, manufactured by Sartomer): 4.0 parts by weight Polymer I: 5.0 parts by weight ・ Initiator: 1.4 parts by weight (Irgacure 907, manufactured by Ciba Specialty Chemicals)
・ Initiator: 0.6 parts by weight (2,2′-bis (o-chlorophenyl) -4,5,4 ′, 5′-
Tetraphenyl-1,2'-biimidazole)
・ Solvent: 50.0 parts by weight (propylene glycol monomethyl ether acetate)

The polymer I is based on 100 mol% of a copolymer of benzyl methacrylate: styrene: acrylic acid: 2-hydroxyethyl methacrylate = 15.6: 37.0: 30.5: 16.9 (molar ratio). 2-methacryloyloxyethyl isocyanate was added at 16.9 mol%, and the weight average molecular weight was 42500.
Next, the negative photosensitive resin composition for the red colored layer is applied on the glass substrate by a spin coating method so as to cover the light-shielding portion, and prebaked, and then exposed through a photomask for the red colored layer, Development was performed to form a 45 μm × 45 μm island-shaped red colored layer (thickness 2.0 μm) so as to cover a predetermined opening of the light-shielding part. Next, a green colored layer, a blue colored layer, and a white colored layer were formed by the same operation as that for forming the red colored layer.

Next, as a photocurable coating liquid for forming an organic film, the same composition as the above-described negative photosensitive resin composition for the white colored layer was used, and the red colored layer formed as described above, green It is applied by spin coating so as to cover a colored layer consisting of a colored layer, a blue colored layer, and a white colored layer, pre-baked, then exposed through a predetermined photomask, developed, and developed on the white colored layer. An organic resin layer (thickness: 4.0 μm) for forming an organic film was formed only on the substrate. (Sample 1)
In addition, as a result of measuring the refractive index after hardening of this photocurable coating liquid with a spectroscopic ellipsometer (UVISEL made by Joban Yvon), it was about 1.5.

Moreover, the organic resin layer for organic film formation was formed like the said sample 1 except having changed the thickness of the organic resin layer as follows. (Samples 2-7)
(Thickness of organic resin layer)
Sample 2: 4.6 μm
Sample 3: 5.0 μm
Sample 4: 2.0 μm
Sample 5: 1.7 μm
Sample 6: 1.0 μm
Sample 7: 7.8 μm

  Next, a thin film (thickness: 0.15 μm) of indium tin oxide was formed on the organic resin layer of the sample 1 by a mask film formation by a sputtering method to obtain a high refractive index film. The high refractive index film was directly formed on a 0.7 mm thick glass substrate (Corning 1737 glass) in the same manner as this high refractive index film forming operation, and the refractive index of this high refractive index film was determined. It was about 2.0 as a result of measuring like the above. Moreover, as a result of measuring the thickness of this high refractive index film | membrane using a stylus type film thickness meter (P-15 by KLA-Tencor Japan Co., Ltd.), it is 0.15 micrometer and thickness variation is 0.1 micrometer or less. It was a uniform thin film.

Moreover, the high refractive index film | membrane of the following thickness was formed on the organic resin layer of said samples 2-7 similarly to said sample 1. (Samples 2-7)
(High refractive index film thickness)
Sample 2: 0.2 μm
Sample 3: 0.3 μm
Sample 4: 0.08 μm
Sample 5: 0.02 μm
Sample 6: 0.01 μm
Sample 7: 0.4 μm

  Subsequently, it was left in an oven at 150 ° C. for 30 minutes for heat treatment. As a result, the organic resin layer shrinks, an organic film having an uneven surface at the interface with the high refractive index film is formed, and a light scattering functional layer (samples 1 to 7) that is a laminate of the organic film and the high refractive index film. ) Was formed on the white colored layer of the colored layer.

The maximum roughness (Rmax) of the surface of the high refractive index film of this light scattering functional layer (Samples 1 to 7) is measured using a stylus type film thickness meter (P-15 manufactured by KLA-Tencor Japan Co., Ltd.). Thus, the maximum roughness (Rmax) of the uneven surface of the organic film was obtained, and the measurement results were as follows. The thickness of the organic film was slightly thinner than the thickness of the organic resin layer due to shrinkage after the heat treatment.
(Maximum roughness (Rmax) of the surface of the high refractive index film of the light scattering functional layer)
Sample 1: 4.0 μm
Sample 2: 4.6 μm
Sample 3: 5.0 μm
Sample 4: 2.0 μm
Sample 5: 1.6 μm
Sample 6: 1.0 μm
Sample 7: 5.9 μm

  The light scattering functional layer is directly formed on a 0.7 mm thick glass substrate (Corning 1737 glass) in the same manner as the light scattering functional layer (samples 1 to 7). The haze value was measured using a haze meter (HM-150 type) manufactured by Murakami Color Research Laboratory, and the results are shown in Table 1 below.

Next, a coating for a flattening layer having the following composition so as to cover the light scattering functional layer formed as described above and the exposed colored layer (red colored layer, green colored layer, blue colored layer). The liquid was applied by spin coating, prebaked, then exposed through a photomask and developed to form a planarization layer.
(Coating liquid for flattening layer)
・ Methyl methacrylate-styrene-acrylic acid copolymer: 32 parts by weight ・ Epicoat 180S70: 18 parts by weight (manufactured by Japan Epoxy Resin Co., Ltd.)
Dipentaerythritol pentaacrylate: 42 parts by weight Initiator: 8 parts by weight (Irgacure 907 manufactured by Ciba Specialty Chemicals)
-3-methoxybutyl acetate ... 300 weight part In addition, as a result of measuring the refractive index after hardening of the coating liquid for this planarization layer similarly to the above, it was about 1.5.
Color filter substrates (Sample 1 to Sample 7) were prepared by the above operation.

For comparison, a color filter substrate (sample 8) was produced as follows.
First, a coating solution for forming a light scattering layer containing fine particles was prepared. That is, 63 parts by weight of methyl methacrylate (MMA), 12 parts by weight of acrylic acid (AA), 6 parts by weight of 2-hydroxyethyl methacrylate (HEMA), and 88 parts by weight of diethylene glycol dimethyl ether (DMDG) in the polymerization tank. After partly charged, stirred and dissolved, 7 parts by weight of 2,2′-azobis (2-methylbutyronitrile) was added and dissolved uniformly. Then, it stirred at 85 degreeC under nitrogen stream for 2 hours, and also was made to react at 100 degreeC for 1 hour. 7 parts by weight of glycidyl methacrylate (GMA), 0.4 parts by weight of triethylamine, and 0.2 parts by weight of hydroquinone are added to the resulting solution, and the mixture is stirred at 100 ° C. for 5 hours to obtain a curable resin composition. B (solid content 50%) was obtained. Next, each material was mixed with the following composition, and it stirred at room temperature, and obtained the coating liquid for light-scattering layer formation.
(Coating liquid for forming light scattering layer)
Curable resin composition B (solid content 50%) 16 parts by weight Dipentaerythritol pentaacrylate 24 parts by weight (SR399 manufactured by Sartomer)
・ Orthocresol novolac type epoxy resin: 4 parts by weight (Epicoat 180S70 manufactured by Yuka Shell Epoxy Co., Ltd.)
2-methyl-1- (4-methylthiophenyl) -2-morpholinopropane
1-one: 4 parts by weight Diethylene glycol dimethyl ether: 52 parts by weight Melamine-based resin beads (average particle size: 1.2 μm) 5 parts by weight Melamine-based resin beads (average particle size: 0.9 μm) 5 parts by weight

In the same manner as described above, a light shielding part and a colored layer are formed on a glass substrate, and the light scattering layer forming coating solution is applied by a spin coating method so as to cover these light shielding part and the colored layer. After that, exposure was performed through a predetermined photomask, development, and post-baking were performed to form a light scattering layer (thickness 2.0 μm) only on the white colored layer of the colored layer. Thereafter, a planarizing layer was formed in the same manner as described above, and a color filter substrate (sample 8) was produced.
The light scattering layer is directly formed on a 0.7 mm thick glass substrate (Corning 1737 glass) in the same manner as the light scattering layer forming operation, and the haze value of the light scattering layer is the same as described above. The results are shown in Table 1 below.
For comparison, a color filter substrate (Sample 9) was prepared in the same manner as Sample 1 except that the light scattering functional layer was not formed.
Further, as a comparison, a circularly polarizing plate (BPCT-HC56-243HCSC manufactured by Sanlitz Co., Ltd.) was provided on the surface of the glass substrate constituting the sample 9 to prepare a color filter substrate (sample 10).

<Production of organic EL display device>
An organic EL element side substrate including a white light-emitting light source was manufactured as follows as an EL element side substrate for manufacturing an organic EL display device facing the color filter substrate.
First, a glass substrate (Corning 1737 glass) having a size of 100 mm × 100 mm and a thickness of 0.7 mm was prepared as a substrate. A thin film transistor circuit was produced on this substrate according to a conventional method.
On this, a lower electrode layer made of aluminum was formed so as to correspond to the colored layers of each color of the color filter substrate, and an insulating layer (partition wall) made of polyimide was formed in the gap between these lower electrode layers. Next, a white light emitting organic EL element (laminated structure of a hole injection layer, a white light emitting layer, and an electron injection layer) is formed in the gap between the insulating layers (partition walls), and indium tin oxide (ITO) is formed thereon. An upper transparent electrode layer was formed. A gas barrier layer made of silicon oxide was formed on the upper transparent electrode layer, and an organic EL element side substrate was produced.
The organic EL element side substrate thus prepared and each of the color filter substrates (samples 1 to 10) described above were bonded with an adhesive (NT-01UV manufactured by Nitto Denko Corporation) as shown in FIG. Thus, organic EL display devices (Sample 1 to Sample 10) were produced.

<Evaluation>
(Transmission efficiency)
The transmittance was measured over the entire color filter substrate of each sample, the transmission efficiency was evaluated according to the following criteria, and the results are shown in Table 1 below. In the measurement, the transmittance (total light transmittance measured using an integrating sphere) is measured using a haze meter (HM-150 type) manufactured by Murakami Color Research Laboratory Co., Ltd. and has a light scattering functional layer. The transmittance of a non-color filter substrate (sample 9) was calculated as 100.
(Evaluation criteria)
A: The transmittance is in the range of 85 to 100, and the transmission efficiency is extremely good. ○: The transmittance is in the range of less than 41 to 85 and can be used practically. ×: The transmittance is less than 41, and can be used in practical use. Absent

(Prevention of externally reflected light)
The color filter substrate of each organic EL display device is irradiated with light from a light source (xenon lamp) at an incident angle of 45 °, and a variable angle photometer (GCMS-11, manufactured by Murakami Color Research Laboratory Co., Ltd.) is used. Is used to perform variable reflection spectroscopic measurement (variable angle 0 degree), and the reflection intensity of the external light regular reflection light of the color filter substrate (sample 9) having no light scattering function layer is 100, and the external light regular reflection is performed according to the following criteria. The light prevention property was evaluated, and the results are shown in Table 1 below.
(Evaluation criteria)
◎: Reflection intensity is 33 or less, extremely good ○: Reflection intensity is in the range of greater than 33 to 70 or less, and can be used practically ×: Reflection intensity is greater than 70, cannot be used practically

(Visibility under the bright room)
With the respective organic EL display devices turned off, the degree of black closure under a standard light source (6500k fluorescent lamp) was visually evaluated. This evaluation is for judging the prevention of backscattering, and the evaluation was performed according to the following criteria. The results are shown in Table 1 below.
(Evaluation criteria)
○: When it appears to sink black ×: When it appears to be white and does not appear to sink black

表１で＊印を付した試料は比較例を示す。

Samples marked with * in Table 1 represent comparative examples.

[Example 2]
<Preparation of color filter substrate>
In the same manner as in Example 1, a light shielding portion and a colored layer were formed on a glass substrate (Corning 1737 glass).
Next, the same photocurable coating solution for forming an organic film as that of Sample 1 of Example 1 was used, and it was applied by spin coating so as to cover the colored layer, prebaked, and then subjected to a predetermined photo Exposure through a mask, development, and post-baking were performed to form an organic resin layer (thickness 6 μm) so as to cover the entire colored layer. Thereafter, in the same manner as in Example 1, a high refractive index film was formed on the organic resin layer and subjected to heat treatment. As a result, shrinkage occurs in the organic resin layer, an uneven surface is formed at the interface with the high refractive index film, and the light scattering functional layer that is a laminate of the organic film and the high refractive index film is formed to cover the colored layer. It was done.

The maximum roughness (Rmax) of the surface of the high refractive index film of this light scattering functional layer was measured in the same manner as described above to obtain the maximum roughness (Rmax) of the uneven surface of the organic film. The result of this measurement was 4 μm. The thickness of the organic film was slightly smaller than the thickness of the organic resin layer (6 μm) due to shrinkage after the heat treatment.
Next, in the same manner as in Example 1, a planarizing layer was formed so as to cover the light scattering functional layer.
A color filter substrate was produced by the above operation.
<Production of organic EL display device>
Using the above color filter substrate, an organic EL display device was produced in the same manner as in Example 1.
<Evaluation>
The organic EL display device was evaluated in the same manner as in Example 1 for transmission efficiency, prevention of regular reflection of external light, and visibility under a bright room. As a result, the result was the same as that of Sample 1 in Example 1.

[Example 3]
<Preparation of color filter substrate>
In the same manner as in Example 1, a light shielding portion and a colored layer were formed on a glass substrate (Corning 1737 glass).
Next, the same photocurable coating liquid for forming an organic film as that of Sample 1 of Example 1 was used, and it was applied by spin coating so as to cover the colored layer, followed by prebaking, and then a circular opening. Was exposed through a photomask arranged in a face-centered shape with a pitch of 9 μm, and then the entire surface was exposed, developed, and post-baked to form an organic film so as to cover the entire colored layer. This organic film had an uneven surface, and the maximum roughness (Rmax) of the uneven surface was measured in the same manner as described above, and was 2 μm. Moreover, it was 5 micrometers as a result of measuring the thickness of an organic film similarly to the above.
Next, a high refractive index film is formed on the organic film in the same manner as in Example 1, and a light scattering functional layer that is a laminate of the organic film and the high refractive index film is formed so as to cover the colored layer. did.
A color filter substrate (sample A) was produced by the above operation.
A color filter substrate (sample B) was prepared in the same manner as described above except that the high refractive index film was not formed.

<Production of organic EL display device>
In the same manner as in Example 1, an organic EL element side substrate was produced.
The organic EL element side substrate and each of the color filter substrates (sample A and sample B) were bonded to each other at the peripheral portion via an adhesive (NT-01UV manufactured by Nitto Denko Corporation). Thus, organic EL display devices (sample A and sample B) having a structure in which an air layer is interposed between the color filter substrate and the EL element side substrate were manufactured.
<Evaluation>
The organic EL display device was evaluated in the same manner as in Example 1 for its transmission efficiency, the ability to prevent regular reflection of external light, and the visibility under a bright room. The results are shown in Table 2 below.

表２で＊印を付した試料は比較例を示す。

Samples marked with * in Table 2 represent comparative examples.

[Example 4]
<Preparation of color filter substrate>
In the same manner as in Example 1, a light shielding portion, a red colored layer, a green colored layer, and a blue colored layer are formed on a glass substrate (Corning 1737 glass), and a region where the white colored layer is formed remains unformed. did.
Next, the same photocurable coating solution for forming an organic film as that of Sample 1 of Example 1 was used, and it was applied by spin coating so as to cover the colored layer, prebaked, and then subjected to a predetermined photo It exposed through the mask, developed, and post-baked, and formed the organic resin layer (thickness 6 micrometers) only in the area | region which forms a white colored layer. Thereafter, in the same manner as in Example 1, a high refractive index film was formed on the organic resin layer and subjected to heat treatment. As a result, the organic resin layer contracted to form an uneven surface at the interface with the high refractive index film, and the light scattering functional layer, which is a laminate of the organic film and the high refractive index film, was formed as a white colored layer ( (See FIG. 3).

The maximum roughness (Rmax) of the surface of the high refractive index film of the white colored layer that also serves as the light scattering function layer was measured in the same manner as described above to obtain the maximum roughness (Rmax) of the uneven surface of the organic film. The result of this measurement was 4 μm. The thickness of the organic film was slightly smaller than the thickness of the organic resin layer (6 μm) due to shrinkage after the heat treatment.
Next, in the same manner as in Example 1, a flattening layer was formed so as to cover a red colored layer, a green colored layer, a blue colored layer, and a colored layer having a white colored layer that also serves as a light scattering functional layer.
A color filter substrate was produced by the above operation.

<Production of organic EL display device>
Using the above color filter substrate, an organic EL display device was produced in the same manner as in Example 1.
<Evaluation>
The organic EL display device was evaluated in the same manner as in Example 1 for transmission efficiency, prevention of regular reflection of external light, and visibility under a bright room. As a result, the result was the same as that of Sample 1 in Example 1.

[Example 5]
<Preparation of color filter substrate>
A color filter substrate was fabricated in the same manner as Sample 1 in Example 1 except that the high refractive index film formed on the organic resin layer was replaced with a thin film of silicon nitride instead of the thin film of indium tin oxide. The light scattering functional layer was directly formed on a 0.7 mm thick glass substrate (Corning 1737 glass) in the same manner as the light scattering functional layer forming operation, and the haze value of this light scattering functional layer was determined. As a result of measurement in the same manner as in Example 1, the haze value was 40.

<Production of organic EL display device>
Using the above color filter substrate, an organic EL display device was produced in the same manner as in Example 1.
<Evaluation>
The organic EL display device was evaluated in the same manner as in Example 1 for transmission efficiency, prevention of regular reflection of external light, and visibility under a bright room. As a result, the result was the same as that of Sample 1 in Example 1.

  It can be widely used in the electronics industry including various flat displays.

1, 1 ', 1 "... color filter substrate 2 ... transparent substrate 3 ... colored layer 3R ... red colored layer 3G ... green colored layer 3B ... blue colored layer 3W ... white colored layer 4 ... light shielding layer 5 ... light scattering functional layer 6 ... Organic film 6a ... Uneven surface 7 ... High refractive index film 8, 9 ... Planarization layer 11 ... Electroluminescence display device 21 ... Electroluminescence element side substrate

Claims (11)

In a color filter substrate comprising a transparent substrate and a colored layer on the transparent substrate,
The colored layer has a red colored layer, a green colored layer, a blue colored layer and a white colored layer,
At least in the region where the white colored layer is located, there is a light scattering functional layer having a haze value of 10 to 70, and the light scattering functional layer is a laminate of an organic film and a high refractive index film. The organic film side is located on the transparent substrate side, the organic film has an uneven surface at the interface with the high refractive index film, and the refractive index of the organic film is smaller than the refractive index of the high refractive index film A color filter substrate characterized by the above. In a color filter substrate comprising a transparent substrate and a colored layer on the transparent substrate,
The colored layer has a red colored layer, a green colored layer, a blue colored layer and a white colored layer,
The white colored layer is composed of a light scattering functional layer, the light scattering functional layer is formed by laminating an organic film and a high refractive index film, and the haze value is in the range of 10 to 70, and the organic film side is located on the transparent substrate side. The organic film has an uneven surface at the interface with the high refractive index film, and the refractive index of the organic film is smaller than the refractive index of the high refractive index film.   The color filter substrate according to claim 2, wherein the light scattering functional layer is also present in a region where the red colored layer, the green colored layer, and the blue colored layer are located.   The high refractive index film includes silicon oxide, silicon nitride, silicon oxynitride, silicon carbide, titanium oxide, niobium oxide, indium oxide, zinc oxide, tin oxide or tantalum oxide, gallium, cerium, aluminum, carbon, tin and boron. The color filter substrate according to any one of claims 1 to 3, comprising at least one material selected from the group doped with any of the above.   The color filter substrate according to claim 1, wherein a maximum roughness (Rmax) of the uneven surface of the organic film is 10 μm or less.   The color filter substrate according to claim 1, further comprising a planarizing layer on the high refractive index film of the light scattering functional layer.   The color filter substrate according to claim 1, wherein the organic film has a thickness in a range of 0.1 to 10 μm.   The color filter substrate according to any one of claims 1 to 7, wherein a difference between a refractive index of the high refractive index film and a refractive index of the organic film is 0.4 or more. Color filter substrate comprising a transparent substrate, a colored layer having a red colored layer, a green colored layer, a blue colored layer and a white colored layer on the transparent substrate, and a light scattering functional layer present at least in the region where the white colored layer is located In the manufacturing method of
After forming an organic resin layer for forming an organic film, a high refractive index film is formed on the organic resin layer, and then heat treatment is performed to shrink the organic resin layer to form the high refractive index film. A step of forming the light scattering functional layer, which is a laminate of the organic film and the high refractive index film and the organic film side is located on the transparent substrate side, by forming an uneven surface at the interface, A method for manufacturing a color filter substrate. In the method for producing a color filter substrate comprising a transparent substrate and a colored layer having a red colored layer, a green colored layer, a blue colored layer and a white colored layer on the transparent substrate, the white colored layer comprising a light scattering functional layer,
After forming an organic resin layer for forming an organic film, a high refractive index film is formed on the organic resin layer, and then heat treatment is performed to shrink the organic resin layer to form the high refractive index film. A step of forming the light scattering functional layer, which is a laminate of the organic film and the high refractive index film and the organic film side is located on the transparent substrate side, by forming an uneven surface at the interface, A method for manufacturing a color filter substrate.   An electroluminescence display device comprising a color filter substrate and an electroluminescence element side substrate, wherein the color filter substrate is the color filter substrate according to any one of claims 1 to 8.