JP2003276342A - 光記録媒体 - Google Patents

光記録媒体

Info

Publication number
JP2003276342A
JP2003276342A JP2002085993A JP2002085993A JP2003276342A JP 2003276342 A JP2003276342 A JP 2003276342A JP 2002085993 A JP2002085993 A JP 2002085993A JP 2002085993 A JP2002085993 A JP 2002085993A JP 2003276342 A JP2003276342 A JP 2003276342A
Authority
JP
Japan
Prior art keywords
dye
recording medium
optical recording
wavelength
recording
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2002085993A
Other languages
English (en)
Inventor
Takashi Doi
高志 洞井
Hiroyuki Arioka
博之 有岡
Shigetoshi Fukuzawa
成敏 福澤
Shuji Tsukamoto
修司 塚本
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TDK Corp
Original Assignee
TDK Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TDK Corp filed Critical TDK Corp
Priority to JP2002085993A priority Critical patent/JP2003276342A/ja
Priority to US10/394,257 priority patent/US20030190448A1/en
Priority to TW092106486A priority patent/TWI238407B/zh
Priority to EP03006746A priority patent/EP1349159A1/en
Priority to CNB031076920A priority patent/CN1213420C/zh
Publication of JP2003276342A publication Critical patent/JP2003276342A/ja
Priority to US11/014,855 priority patent/US7022393B2/en
Pending legal-status Critical Current

Abstract

(57)【要約】 【課題】 高耐光性や良好な反射率を維持しつつ１０ｍ
／ｓ以上の高速な線速度で記録を行い得る光記録媒体を
提供する。 【解決手段】 薄膜状態での極大吸収波長が４５０ｎｍ
以上６００ｎｍ以下の第１色素を主成分として含有する
記録層２２を基材２１上に設けて構成された光記録媒体
１０であって、記録層２２は、記録波長における消衰係
数が０．５以上の第２色素を含んで形成されている。こ
の場合、第２色素は、薄膜状態での極大吸収波長が６０
０ｎｍ以上７５０ｎｍ以下であるのが好ましい。

Description

【発明の詳細な説明】
【０００１】
【発明の属する技術分野】本発明は、記録層に色素を用
いた光記録媒体に関し、特に高速記録が可能な光記録媒
体に関するものである。
【０００２】
【従来の技術】現在、ディジタル記録が可能な光記録媒
体として大容量追記型コンパクトディスク（ＤＶＤ−
Ｒ）の商品化が行われている。このＤＶＤ−Ｒは、光透
過性基材上に、記録層、反射層、保護層が順次積層され
た構造を備え、波長が６３０〜６８０ｎｍのレーザーで
記録および再生が可能なメディアとして規格化されてい
る。この場合、このＤＶＤ−Ｒでは、レーザーで情報を
記録するために必要なグルーブと呼ばれる案内溝が光透
過性基材上に形成されており、この案内溝の形状は、各
々の記録再生特性やサーボ信号特性などを含めた総合的
な信号品質を考慮して最適化されている。一例として、
この案内溝は、０．６μｍ〜０．７μｍ程度のピッチで
形成されている。一方、記録層は、各種の記録材料で形
成されており、一例として、下記の一般式（Ｉ）で示さ
れる色素と金属とのキレート化合物（含金属アゾ色素）
で形成されている。
【化３】 なお、この一般式（Ｉ）中において、Ａは、それが結合
している炭素原子および窒素原子と一緒になって複素環
を形成する残基を表し、Ｂは、それが結合している二つ
の炭素原子と一緒になって芳香環または複素環を形成す
る残基を表し、Ｘは、ヒドロキシル基、カルボキシル
基、スルホン酸誘導体基、または（ＮＳＯ ２Ｑ）−を表
し、このＱはハロゲン原子で置換されてもよい炭素数１
〜６のアルキル基を表す。
【０００３】この場合、この含金属アゾ色素に限定され
るものではないが、ＤＶＤ−Ｒで用いられる色素（例え
ば含金属アゾ色素やシアニン色素）は、図１の特性Ｗで
示すように、薄膜状態での極大吸収波長が記録再生用レ
ーザー波長（６３０ｎｍ以上６８０ｎｍ以下）よりも短
波長側の４５０ｎｍ〜６００ｎｍであって、記録再生用
レーザー波長における消衰係数が約０．０１〜０．０３
となる特性を有している。したがって、この含金属アゾ
色素を含む前述の色素を１００％使用して構成した記録
層も同様の特性を有するため、記録再生用レーザー波長
において十分な反射率が確保されている。中でも、含金
属アゾ色素は高耐光性を有しているため、記録層も同様
にして高い耐光性を有している。
【０００４】
【発明が解決しようとする課題】ところが、含金属アゾ
色素を含む前述の色素１００％で記録層を構成した光記
録媒体には、以下の改善すべき点がある。すなわち、Ｄ
ＶＤ−Ｒの基本仕様における線速度は３．４９ｍ／ｓ
（１倍速）に規定されており、この光記録媒体もこの線
速度で記録可能に設計されている。また、より高速な２
倍速での記録も可能なこともこの光記録媒体で確認され
ている。しかしながら、最近では、１０ｍ／ｓ以上のさ
らに高速な線速度（例えば４倍速）での記録がＤＶＤ−
Ｒに望まれるようになってきており、発明者の実験によ
れば、現状出力の記録用レーザーを使用して記録する場
合、記録層の感度が不足するため、この光記録媒体に１
０ｍ／ｓ以上の線速度で記録するのが困難であることが
確認された。一方、記録用レーザーの出力を高めて記録
層の感度不足を補ったり、記録層の組成を変えて感度を
高めたりする等の手法を採用することによって４倍速で
記録し得ることも実験で確認されている。しかしなが
ら、記録用レーザーの出力に限界があるため、その耐久
性等を考慮した場合、記録用レーザーとしては、その出
力が所定のレベル以下であるのが好ましい。したがっ
て、記録用レーザーの出力を高めて記録層の感度不足を
補う手法は現実的ではない。一方、記録層の組成を大き
く変える手法は、前述したＤＶＤ−Ｒ用の色素で構成し
た記録層の電気特性（高耐光性や良好な反射率）を確保
するのが困難でエラー率の増加や反射率の低下等の原因
となるため、これも現実的ではない。したがって、現状
の光記録媒体には、高耐光性や良好な反射率を維持しつ
つ高速な線速度で記録を行うのが困難であるという課題
がある。
【０００５】本発明は、かかる改善すべき点に鑑みてな
されたものであり、高耐光性や良好な反射率を維持しつ
つ１０ｍ／ｓ以上の高速な線速度で記録を行い得る光記
録媒体を提供することを主目的とする。
【０００６】
【課題を解決するための手段】上記目的を達成すべく本
発明に係る光記録媒体は、薄膜状態での極大吸収波長が
４５０ｎｍ以上６００ｎｍ以下の第１色素を主成分とし
て含有する記録層を基材上に設けて構成された光記録媒
体であって、前記記録層は、記録波長における消衰係数
が０．５以上の第２色素を含んで形成されている。な
お、本発明における「薄膜状態での極大吸収波長」と
は、有機色素膜を記録層として成膜した状態での極大吸
収波長を意味する。この場合、薄膜状態での極大吸収ス
ペクトルは、色素を溶媒に溶かした溶液状態における極
大吸収スペクトルとは挙動が異なる。この薄膜状態での
極大吸収スペクトルは、例えば、以下のようにして測定
することができるが、これに限定されるものではない。
すなわち、一般的には、まず、対象となる色素を１〜２
０重量％の濃度で有機溶媒に溶解し、スピンコートに
て、グループまたはピット等のないＰＣ平板上に特定の
配向性を有しないようにして６０〜２００ｎｍ程度の膜
厚として、５０℃〜７０℃で乾燥して成膜する。有機溶
媒は、色素を溶解させることができ、かつ大気中におけ
る沸点が５０℃〜１５０℃であるようなものを選択する
のが好ましい。スピンコート時の溶媒揮発の際に色素が
著しい結晶化、あるいは会合を起こしてしまうような場
合には、別の溶媒を選択する。成膜後、分光光度計を使
用して、作製した色素薄膜付きＰＣ平板の透過吸収スペ
クトルを測定する。また、消衰係数（光学定数）も上記
の測定方法に準じて測定することが可能である。つま
り、例えば、上記の色素薄膜付きＰＣ平板を作製すると
共に、同様の色素薄膜付きＰＣ平板上に金の反射膜を形
成したものを作製する。次いで、分光光度計を使用し
て、色素薄膜付きＰＣ平板を測定対象体として、必要と
する波長における透過率を測定し、金の反射膜を形成し
たＰＣ平板を測定対象体として、必要とする波長におけ
る反射率を測定する。その後、測定した透過率および反
射率から消衰係数を演算する。
【０００７】この場合、前記第２色素は、薄膜状態での
極大吸収波長が６００ｎｍ以上７５０ｎｍ以下であるの
が好ましい。
【０００８】さらに、前記記録層は、波長６６０ｎｍに
おける薄膜状態での消衰係数が０．０３以上０．１以下
であるのが好ましい。
【０００９】さらに、前記記録層は、０．５以上５以下
の重量％で前記第２色素を含んで形成されているのが好
ましい。
【００１０】また、この光記録媒体は、６３０ｎｍ以上
６８０ｎｍ以下の波長のレーザーで前記記録層に情報が
記録されるのが好ましい。
【００１１】また、この光記録媒体は、１０ｍ／ｓ以上
の線速度で前記記録層に情報を記録可能に構成されてい
る。
【００１２】さらに、この光記録媒体は、前記第１色素
が、下記の一般式（Ｉ）で示される色素と金属とのキレ
ート化合物（含金属アゾ色素）の中から選ばれる１種ま
たは２種以上で構成されている。
【化４】 式中、Ａは、それが結合している炭素原子および窒素原
子と一緒になって複素環を形成する残基を表し、Ｂは、
それが結合している二つの炭素原子と一緒になって芳香
環または複素環を形成する残基を表し、Ｘは、ヒドロキ
シル基、カルボキシル基、スルホン酸誘導体基、または
（ＮＳＯ２Ｑ）−を表し、当該Ｑは、ハロゲン原子で置
換されていてもよい炭素数１〜６のアルキル基を表す。
【００１３】また、この光記録媒体は、前記第２色素
が、下記の一般式（ＩＩ）で示されるペンタメチンシア
ニン色素で構成されている。
【化５】 式中、Ｒ１，Ｒ２は、それぞれ独立に、置換もしくは非
置換の炭素原子数１〜６のアルキル基、置換もしくは非
置換の炭素原子数１〜６のアルケニル基を表し、Ｚ１，
Ｚ２は、それぞれ独立に、５員もしくは６員の複素環、
または５員もしくは６員の複素環を含む縮合環を形成す
る原子団を表し、Ｙは、一価のアニオンを表す。
【００１４】
【発明の実施の形態】以下、添付図面を参照して、本発
明に係る光記録媒体の好適な実施の形態について説明す
る。
【００１５】本発明に係る光記録媒体（ＤＶＤ−Ｒ）
は、少なくとも、第１色素を主成分として含有する記録
層を基材上に設けると共に、この記録層上に反射層を設
けて構成された光記録媒体であって、この記録層中の色
素全量に対して０．５以上５以下の重量％で第２色素が
配合されている。
【００１６】この場合、第１色素は、記録層の主たる特
性を決定する色素として機能し、図１の特性Ｗに示すよ
うに、薄膜状態での極大吸収波長領域が記録再生用レー
ザー波長（以下、「記録波長」または「再生波長」とも
いう。具体的には６３０ｎｍ以上６８０ｎｍ以下の波
長）よりも短波長側の４５０ｎｍ〜６００ｎｍであっ
て、記録再生用レーザー波長における消衰係数が約０．
０１〜０．０３となる特性を有している。具体的には、
第１色素は、下記一般式（Ｉ）で示される色素（アゾ系
有機色素）と金属とのキレート化合物（含金属アゾ色
素）の中から選ばれる１種または２種以上で構成されて
いる。
【化６】 式中、Ａは、それが結合している炭素原子および窒素原
子と一緒になって複素環を形成する残基を表し、Ｂは、
それが結合している二つの炭素原子と一緒になって芳香
環または複素環を形成する残基を表し、Ｘは、ヒドロキ
シル基、カルボキシル基、スルホン酸誘導体基、または
（ＮＳＯ２Ｑ）−を表し、当該Ｑは、ハロゲン原子で置
換されていてもよい炭素数１〜６のアルキル基を表す。
【００１７】第２色素は、線速度１０ｍ／ｓ以上（例え
ば４倍速）で記録可能に記録層の記録感度を高めるため
に配合（添加）される色素であって、図１の特性Ｘに示
すように、薄膜状態での極大吸収波長が６００ｎｍ以上
７５０ｎｍ以下であって、薄膜状態での記録再生用レー
ザー波長における消衰係数が０．５以上となる特性を有
している。具体的には、第２色素としては、下記一般式
（ＩＩ）で示される色素が好ましく、さらに具体的に
は、下記式（ＩＩＩ）で示されるペンタメチンシアニン
色素を採用することができる。
【化７】 なお、この式（ＩＩ）中、Ｒ１，Ｒ２は、それぞれ独立
に、置換もしくは非置換の炭素原子数１〜６のアルキル
基、置換もしくは非置換の炭素原子数１〜６のアルケニ
ル基を表し、Ｚ１，Ｚ２は、それぞれ独立に、５員もし
くは６員の複素環、または５員もしくは６員の複素環を
含む縮合環を形成する原子団を表し、Ｙは、一価のアニ
オンを表す。
【化８】 また、ペンタメチンシアニン色素以外にも、下記式（Ｉ
Ｖ）で示されるトリメチンシアニン色素や、下記式
（Ｖ）で示されるヘプタメチンシアニン色素等を第２色
素として採用することができる。
【化９】
【化１０】
【００１８】また、上記の構成により、記録層は、記録
再生用レーザー波長（一例として６６０ｎｍ）における
薄膜状態での消衰係数が０．０３以上０．１以上となる
特性を有している。
【００１９】この光記録媒体では、含金属アゾ色素を主
成分として構成された記録層に、薄膜状態での記録再生
用レーザー波長における消衰係数が高い（０．５以上の
消衰係数）色素、例えばペンタメチンシアニン色素が第
２色素として配合されている。このため、この記録層
は、含金属アゾ色素を１００％で構成した記録層と同等
の高耐光性と、記録再生用レーザー波長における良好な
反射率とを確保しつつ、配合したペンタメチンシアニン
色素によって記録再生用レーザー波長に対する吸収率を
高めることができる結果、記録再生用レーザー波長での
記録感度が高められている。つまり、この光記録媒体で
は、高耐光性および良好な反射率を維持しつつ、１０ｍ
／ｓ以上の線速度（４倍速：１４ｍ／ｓ）での情報の記
録が可能となっている。ここで、消衰係数が０．５未満
である色素を第２色素として採用した場合、目標とする
記録感度を得るためには配合量を多くする必要がある
が、第２色素の配合量を多くすると第１色素の配合量が
少なくなるため、エラー率の増加、屈折率の低下による
変調度の低下、および反射率の低下を招いて、ＤＶＤ−
Ｒとしての再生特性および高速記録特性を満足できなく
なる。一方、消衰係数が０．５以上の色素を第２色素と
して採用した場合、第２色素の配合量を５重量％以下に
抑えることができるため、第１色素の配合量を十分に確
保することができる結果、ＤＶＤ−Ｒとしての再生特性
および高速記録特性を十分に満足させることができる。
なお、第２色素として使用できる色素の消衰係数には理
論上の上限はないが、少量で大きい効果があるものを配
合した場合、配合量の微妙な違いで記録感度がばらつく
ことにつながり、安定した生産を行うことが困難とな
る。したがって、光記録媒体用色素としては、消衰係数
が２以下のものを使用して、配合量を０．５重量％以上
にするのが好ましい。
【００２０】
【実施例】次に、実施例を挙げて本発明を詳細に説明す
る。
【００２１】最初に、本実施例で使用した光記録媒体の
基本構成について、図２を参照して説明する。光記録媒
体１０は、ＤＶＤ−Ｒ規格に対応した光記録媒体であっ
て、記録可能に構成されたディスク２０とディスク３０
（ダミー基板）を接着剤４０で貼り合わすことによって
構成されている。この場合、ディスク２０は、グルーブ
ＧＲが形成された基材（通常、ポリカーボネート樹脂を
用いて０．６ｍｍ程度の厚みに形成されている）２１上
に、記録層２２、反射層２３および保護層２４が順次積
層されて構成されている。ディスク３０は、例えば基材
２１と同様の材料を用いて構成されている。接着剤４０
は、紫外線硬化性樹脂や熱硬化性樹脂などの任意の材料
を選択することができ、この接着剤４０による接着層は
１０μｍ〜２００μｍ程度の厚みに形成されている。
【００２２】基材２１は、ディスク状に形成されて、裏
面側からの記録および再生を可能とするために、記録再
生用レーザー光（波長６３０ｎｍ〜６８０ｎｍ程度）に
対して、実質的に透明（好ましくは透過率８８％以上）
な樹脂あるいはガラスを材料として形成されている。こ
の場合、樹脂としては、ポリカーボネート樹脂、アクリ
ル樹脂、アモルファスポリオレフィン、ＴＰＸ、ポリス
チレン系樹脂等の各種熱可塑性樹脂を採用することがで
きる。
【００２３】記録層２２は、３０ｎｍ〜３００ｎｍの厚
みに形成されている。反射層２３は、Ａｕ、Ｃｕ、Ａ
ｌ、Ａｇ、ＡｇＣｕ等の高反射率金属または合金を材料
として形成されている。また、反射層２３は、その厚み
が５０ｎｍ以上であるのが好ましく、蒸着、スパッタ等
によって形成されている。保護層２４は、例えば紫外線
硬化樹脂等の各種樹脂材料を用いて、０．５μｍ〜１０
０μｍ程度の厚さに形成されている。
【００２４】この光記録媒体１０に情報を記録または追
記する際には、記録再生用レーザー光を基材２１を通し
てパルス状に照射する。この結果、記録層２２の照射部
位における光反射率が変化して、情報が記録される。
【００２５】次に、本実施例で採用した試験方法および
評価方法を説明する。なお、試験に先立ち、評価機「Ｄ
ＤＵ−１０００」（パルステック社製。波長６６１ｎ
ｍ。ＮＡ０．６０）を使用して、線速度３．４９ｍ／ｓ
および線速度１４．０ｍ／ｓにて、レーザーピックアッ
プの記録レーザーパワーを順次上げつつ記録層に情報を
記録した。
【００２６】＜最適記録パワー＞最適記録パワーは、
「ＤＤＵ−１０００」（パルステック社製。波長６５０
ｎｍ。ＮＡ０．６０）を使用して、上記した線速度１
４．０ｍ／ｓで記録した情報を線速度３．４９ｍ／ｓで
再生した際におけるジッター値が最小となるときの記録
レーザーパワーの出力値であり、この最適記録パワーに
ついては、下記の評価基準にて評価した。 （評価基準） ○：最適記録パワーが２４ｍＷ以下 ×：最適記録パワーが２４ｍＷを超える
【００２７】＜ジッター＞ジッターについては、線速度
３．４９ｍ／ｓおよび線速度１４．０ｍ／ｓの両記録線
速度で記録した情報を、「ＤＤＵ−１０００」（パルス
テック社製。波長６５０ｎｍ。ＮＡ０．６０）を使用し
て、線速度３．４９ｍ／ｓで再生し、下記の評価基準に
基づいて評価した。 （評価基準） ○：線速度３．４９ｍ／ｓ，１４．０ｍ／ｓのどちらで
も総合ジッター値が８％以下 ×：いずれかの線速度で総合ジッター値が８％を超える
【００２８】＜反射率＞反射率については、線速度３．
４９ｍ／ｓおよび線速度１４．０ｍ／ｓの両記録線速度
で記録した情報を、「ＤＤＵ−１０００」（パルステッ
ク社製。波長６５０ｎｍ。ＮＡ０．６０）を使用して、
線速度３．４９ｍ／ｓで再生し、下記の評価基準に基づ
いて評価した。 （評価基準） ○：線速度３．４９ｍ／ｓ，１４．０ｍ／ｓのどちらで
も反射率が４５％以上×：いずれかの線速度で反射率が
４５％未満
【００２９】＜変調度＞変調度については、線速度３．
４９ｍ／ｓおよび線速度１４．０ｍ／ｓの両記録線速度
で記録した情報を、「ＤＤＵ−１０００」（パルステッ
ク社製。波長６５０ｎｍ。ＮＡ０．６０）を使用して、
線速度３．４９ｍ／ｓで再生し、下記の評価基準に基づ
いて評価した。 （評価基準） ○：線速度３．４９ｍ／ｓ，１４．０ｍ／ｓのどちらで
も変調度が６０％以上×：いずれかの線速度で変調度が
６０％未満
【００３０】＜エラー＞エラーについては、線速度３．
４９ｍ／ｓおよび線速度１４．０ｍ／ｓの両記録線速度
で記録した情報を、「ＤＤＵ−１０００」（パルステッ
ク社製。波長６５０ｎｍ。ＮＡ０．６０）を使用して、
線速度３．４９ｍ／ｓで再生し、ＤＶＤデコーダー「Ｄ
Ｒ−３３４０」（ケンウッド社製）を用いて下記の評価
基準に基づいて評価した。 （評価基準） ○：線速度３．４９ｍ／ｓ，１４．０ｍ／ｓのどちらで
も８ＥＣＣブロックの最大ＰＩエラーのエラーカウント
数が２８０以下 ×：いずれかの線速度で８ＥＣＣブロックの最大ＰＩエ
ラーのエラーカウント数が２８０を超える
【００３１】（実施例１）下記の式（ＶＩ）に示す含金
属アゾ色素と上記の式（ＩＩＩ）に示すペンタメチンシ
アニン色素（記録波長６６０ｎｍにおける消衰係数：
１．２９）とを、それぞれ９８：２の重量比で混合した
後に、スピンコート法で塗布乾燥することによって記録
層２２を形成した。また、反射層２３としては、スパッ
タ法によりＡｇ反射層を形成した。さらに、保護層２４
は、紫外線硬化型アクリル樹脂「ダイキュアクリアＳＤ
３１８」（大日本インキ化学工業社製）を材料として形
成した。また、接着剤４０は、遅効性カチオン重合接着
剤「ＳＫ７０００」（ソニーケミカル社製）を使用し
た。
【化１１】
【００３２】（実施例２）上記の式（ＶＩ）に示す含金
属アゾ色素と上記の式（ＩＶ）に示すトリメチンシアニ
ン色素（記録波長６６０ｎｍにおける消衰係数：０．８
１５）とを、それぞれ９７：３の重量比で混合した以外
は、実施例１と同様にして光記録媒体を作製した。
【００３３】（実施例３）上記の式（ＶＩ）に示す含金
属アゾ色素と上記の式（Ｖ）に示すヘプタメチンシアニ
ン色素（記録波長６６０ｎｍにおける消衰係数：０．
５）とを、それぞれ９５：５の重量比で混合した以外
は、実施例１と同様にして光記録媒体を作製した。
【００３４】（比較例１）上記の式（ＶＩ）に示す含金
属アゾ色素と、下記の式（ＶＩＩ）に示すペンタメチン
シアニン色素とベンゼンジチオール金属錯体との塩形成
色素（記録波長６６０ｎｍにおける消衰係数：０．４）
とを、記録感度を満足するように（最適記録パワー２４
ｍＷ以下で記録できるように）混合した以外は、実施例
１と同様にして光記録媒体を作製した。この場合、第１
色素および第２色素をそれぞれ９０：１０の重量比で混
合した。
【化１２】
【００３５】（比較例２）上記の式（ＶＩ）に示す含金
属アゾ色素と下記の式（ＶＩＩＩ）に示すホルマザン色
素（記録波長６６０ｎｍにおける消衰係数：０．４５）
とを使用して、比較例１と同様にして光記録媒体を作製
した。この場合、第１色素および第２色素をそれぞれ９
２：８の重量比で混合した。
【化１３】
【００３６】（比較例３）上記の式（ＶＩ）に示す含金
属アゾ色素と下記の式（ＩＸ）に示すビスイミニウム塩
（記録波長６６０ｎｍにおける消衰係数：０．１）とを
使用して、比較例１と同様にして光記録媒体を作製し
た。この場合、第１色素および第２色素をそれぞれ８
０：２０の重量比で混合した。
【化１４】
【００３７】上記実施例１〜３で作製した光記録媒体、
および比較例１〜３で作製した光記録媒体を、上記の方
法に従い、各々の最適記録パワー、ジッター、変調度、
反射率およびエラー（エラー率）についての電気特性を
評価した。この評価結果を表１に示す。
【表１】
【００３８】表１によれば、第２色素として記録波長６
６０ｎｍにおける消衰係数が０．５以上の色素を配合し
た光記録媒体が明らかに良好な電気特性を示すことを確
認できた。その一方、第２色素として記録波長６６０ｎ
ｍにおける消衰係数が０．５未満の色素を配合した光記
録媒体では、第１色素と第２色素との配合比をどのよう
に変えたとしても、各評価項目をすべて満足させること
ができないことを確認できた。
【００３９】（実施例４）上記の式（ＶＩ）に示す含金
属アゾ色素と上記の式（ＩＩＩ）に示すペンタメチンシ
アニン色素とを、それぞれ９９．５：０．５の重量比で
混合して、記録層２２自体の消衰係数を０．０４１とし
た以外は、実施例１と同様にして光記録媒体を作製し
た。なお、この場合の消衰係数は、記録波長６６０ｎｍ
における薄膜状態での値である（以下、実施例５〜比較
例６まで同様）。
【００４０】（実施例５）上記の式（ＶＩ）に示す含金
属アゾ色素と上記の式（ＩＩＩ）に示すペンタメチンシ
アニン色素とを、それぞれ９８：２の重量比で混合して
記録層２２自体の消衰係数を０．０６６とした以外は、
実施例１と同様にして光記録媒体を作製した。
【００４１】（実施例６）上記の式（ＶＩ）に示す含金
属アゾ色素と上記の式（ＩＩＩ）に示すペンタメチンシ
アニン色素とを、それぞれ９５：５の重量比で混合して
記録層２２自体の消衰係数を０．１０とした以外は、実
施例１と同様にして光記録媒体を作製した。
【００４２】（比較例４）上記の式（ＶＩ）に示す含金
属アゾ色素と上記の式（ＩＩＩ）に示すペンタメチンシ
アニン色素とを、それぞれ１００：０の重量比で混合し
て記録層２２自体の消衰係数を０．０２とした以外は、
実施例１と同様にして光記録媒体を作製した。
【００４３】（比較例５）上記の式（ＶＩ）に示す含金
属アゾ色素と上記の式（ＩＩＩ）に示すペンタメチンシ
アニン色素とを、それぞれ９２：８の重量比で混合して
記録層２２自体の消衰係数を０．１３とした以外は、実
施例１と同様にして光記録媒体を作製した。
【００４４】（比較例６）上記の式（ＶＩ）に示す含金
属アゾ色素と上記の式（ＩＩＩ）に示すペンタメチンシ
アニン色素とを、それぞれ９９．８：０．２の重量比で
混合して記録層２２自体の消衰係数を０．０２８とした
以外は、実施例１と同様にして光記録媒体を作製した。
【００４５】上記実施例４〜６で作製した光記録媒体、
および比較例４〜６で作製した光記録媒体を、上記の方
法に従い、各々の最適記録パワー、ジッター、反射率お
よびエラー（エラー率）についての電気特性を評価し
た。この評価結果を表２に示す。
【表２】
【００４６】表２によれば、記録層２２の消衰係数が
０．０３以上０．１以下の光記録媒体が明らかに良好な
電気特性を示すことを確認できた。また、この結果か
ら、第２色素の配合量が全色素重量に対して０．５重量
％以上５重量％以下の記録層２２を有する光記録媒体が
明らかに良好な電気特性を示すことも確認できた。
【００４７】なお、本発明は上記した本発明の実施の形
態に限定されない。例えば、本発明における第１色素と
して下記式（Ｘ）の含金属アゾ色素を採用することもで
きる。
【化１５】
【００４８】また、本発明における第１色素としてキレ
ート化合物を１種類のみ使用した例について説明した
が、２種以上のキレート化合物を使用してもよい。ま
た、本発明における第２色素として、薄膜状態での極大
吸収波長が６００ｎｍ以上７５０ｎｍ以下であって、記
録用レーザー波長での消衰係数が０．７以上となる特性
を有している色素を使用した例について説明したが、こ
れに限定されず、少なくとも記録用レーザー波長におけ
る消衰係数が０．５以上の色素であればよい。
【００４９】また、本発明に係る光記録媒体は、記録層
および反射層を各々形成して貼り合わせたいわゆる両面
の光記録媒体にも適用できるのは勿論である。
【００５０】
【発明の効果】以上のように、本発明における光記録媒
体によれば、記録波長における消衰係数が０．５以上の
第２色素を含ませて記録層を形成したことにより、高耐
光性や良好な反射率を維持しつつ１０ｍ／ｓ以上の高速
な線速度での記録が可能な光記録媒体を提供することが
できる。
【図面の簡単な説明】
【図１】本発明の実施の形態に係る光記録媒体１０に使
用される含金属アゾ色素およびペンタメチンシアニン色
素各々のレーザ波長と消衰係数との関係を示す特性図で
ある。
【図２】ＤＶＤ−Ｒの構成を示す部分断面図である。
【符号の説明】
１０ 光記録媒体（ＤＶＤ−Ｒ） ２０ ディスク ２１ 基材 ２２ 記録層 ２３ 反射層 ２４ 保護層 ３０ ダミー基板 ４０ 接着剤
───────────────────────────────────────────────────── フロントページの続き (72)発明者 福澤 成敏 東京都中央区日本橋一丁目13番１号 ティ ーディーケイ株式会社内 (72)発明者 塚本 修司 東京都中央区日本橋一丁目13番１号 ティ ーディーケイ株式会社内 Ｆターム(参考） 2H111 EA03 EA12 EA33 EA43 FB42 FB43 5D029 JA04 JB45 JC01 5D090 AA01 BB05 CC01 CC14 KK06

Claims (8)

    【特許請求の範囲】
  1. 【請求項１】 薄膜状態での極大吸収波長が４５０ｎｍ
    以上６００ｎｍ以下の第１色素を主成分として含有する
    記録層を基材上に設けて構成された光記録媒体であっ
    て、 前記記録層は、記録波長における消衰係数が０．５以上
    の第２色素を含んで形成されている光記録媒体。
  2. 【請求項２】 前記第２色素は、薄膜状態での極大吸収
    波長が６００ｎｍ以上７５０ｎｍ以下である請求項１記
    載の光記録媒体。
  3. 【請求項３】 前記記録層は、波長６６０ｎｍにおける
    薄膜状態での消衰係数が０．０３以上０．１以下である
    請求項１または２記載の光記録媒体。
  4. 【請求項４】 前記記録層は、０．５以上５以下の重量
    ％で前記第２色素を含んで形成されている請求項１から
    ３のいずれかに記載の光記録媒体。
  5. 【請求項５】 ６３０ｎｍ以上６８０ｎｍ以下の波長の
    レーザーで前記記録層に情報が記録される請求項１から
    ４のいずれかに記載の光記録媒体。
  6. 【請求項６】 １０ｍ／ｓ以上の線速度で前記記録層に
    情報が記録される請求項１から５のいずれかに記載の光
    記録媒体。
  7. 【請求項７】 前記第１色素は、下記一般式（Ｉ）で示
    される色素と金属とのキレート化合物（含金属アゾ色
    素）の中から選ばれる１種または２種以上で構成されて
    いる請求項１から６のいずれかに記載の光記録媒体。 【化１】 式中、Ａは、それが結合している炭素原子および窒素原
    子と一緒になって複素環を形成する残基を表し、Ｂは、
    それが結合している二つの炭素原子と一緒になって芳香
    環または複素環を形成する残基を表し、Ｘは、ヒドロキ
    シル基、カルボキシル基、スルホン酸誘導体基、または
    （ＮＳＯ２Ｑ）−を表し、当該Ｑは、ハロゲン原子で置
    換されていてもよい炭素数１〜６のアルキル基を表す。
  8. 【請求項８】 前記第２色素は、下記一般式（ＩＩ）で
    示されるペンタメチンシアニン色素で構成されている請
    求項１から７のいずれかに記載の光記録媒体。 【化２】 式中、Ｒ１，Ｒ２は、それぞれ独立に、置換もしくは非
    置換の炭素原子数１〜６のアルキル基、置換もしくは非
    置換の炭素原子数１〜６のアルケニル基を表し、Ｚ１，
    Ｚ２は、それぞれ独立に、５員もしくは６員の複素環、
    または５員もしくは６員の複素環を含む縮合環を形成す
    る原子団を表し、Ｙは、一価のアニオンを表す。
JP2002085993A 2002-03-26 2002-03-26 光記録媒体 Pending JP2003276342A (ja)