JP2003247210A - Weatherproof protection method for waterproof layer - Google Patents
Weatherproof protection method for waterproof layerInfo
- Publication number
- JP2003247210A JP2003247210A JP2002045864A JP2002045864A JP2003247210A JP 2003247210 A JP2003247210 A JP 2003247210A JP 2002045864 A JP2002045864 A JP 2002045864A JP 2002045864 A JP2002045864 A JP 2002045864A JP 2003247210 A JP2003247210 A JP 2003247210A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- waterproof layer
- resistant
- weather
- waterproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】
【課題】 橋梁等の防水層を有するコンクリート構造物
において、該防水層を保護して直射日光等に晒されても
長期耐久性を確保することのでき、且つ施工が容易な耐
候性の保護方法及び、その上を人が歩くような長期の使
用に耐える構造物を提供する。
【解決手段】 少なくとも、耐候性フィルム層（Ａ）、
耐熱高強度フィルム層（Ｂ）からなる多層シートを、接
着剤層（Ｃ）を介するか、又は特定の接着剤によりコン
クリート表面に形成されている防水層（Ｄ）の外表面に
貼付する防水層の耐候性保護方法。（Ａ）層としてはフ
ッ化ビニリデン系樹脂フィルム、（Ｂ）層としては、ポ
リカーボネート等の延伸フィルムが好ましい。(57) [Problem] In a concrete structure having a waterproof layer such as a bridge, the waterproof layer can be protected and long-term durability can be ensured even when exposed to direct sunlight, and construction is easy. The present invention provides a method for protecting a weatherproof device and a structure capable of withstanding long-term use such as walking on a person. SOLUTION: At least a weather-resistant film layer (A),
A waterproof layer in which a multilayer sheet composed of a heat-resistant high-strength film layer (B) is adhered to an outer surface of a waterproof layer (D) formed on a concrete surface via an adhesive layer (C) or a specific adhesive. Weatherproof protection method. The (A) layer is preferably a vinylidene fluoride resin film, and the (B) layer is preferably a stretched film of polycarbonate or the like.
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、防水層を有するコ
ンクリート構造物からなる橋梁等の防水材の耐候性を保
護する工法に関する。尚、本発明で耐候性フィルム層等
の樹脂組成を示す「％」等の単位は、特に断らない限
り、樹脂成分の合計を１００としたときの質量基準の値
で表す。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for protecting the weather resistance of a waterproof material such as a bridge made of a concrete structure having a waterproof layer. In the present invention, units such as “%” indicating the resin composition of the weather resistant film layer and the like are represented by mass-based values when the total of the resin components is 100, unless otherwise specified.
【０００２】[0002]
【従来の技術】コンクリート構造物からなる橋梁は、コ
ンクリートが長期に渡って雨水に晒され劣化するのを防
止する目的で、コンクリートの表面に防水材からなる防
水層を設けている。この防水層としては、例えばアスフ
ァルト系、アクリル系、又はウレタン系接着剤、もしく
は、各種ゴム等からなるシートが用いられている。これ
らのシートは防水効果は有するものの、クロロプレンゴ
ムシートのような特殊なものを除いて、直射の日光に対
する耐候性が不十分であり、従来は、この防水層に直射
日光が当たらないような施工方法が採られていた。2. Description of the Related Art In a bridge made of a concrete structure, a waterproof layer made of a waterproof material is provided on the surface of the concrete for the purpose of preventing the concrete from being deteriorated by being exposed to rainwater for a long period of time. As the waterproof layer, a sheet made of, for example, an asphalt-based, acrylic-based, or urethane-based adhesive, or various rubbers is used. Although these sheets have a waterproof effect, except for special ones such as chloroprene rubber sheets, they have insufficient weather resistance to direct sunlight, and in the past, this waterproof layer was constructed so that it would not be exposed to direct sunlight. The method was adopted.
【０００３】しかしながら、この方法では橋梁の防水構
造が大きく制約を受ける。近年透水性のアスファルト舗
装の普及により、橋梁の端部が直射日光に晒される構造
が提案されており、そのような長期使用に十分耐える防
水層の耐候性保護方法が求められていた。この目的で一
部でアクリル樹脂系の耐候性塗料が使用されているが、
その耐久性は１０年以下であり、十分満足できるもので
はなかった。However, this method greatly restricts the waterproof structure of the bridge. With the recent widespread use of water-permeable asphalt pavement, a structure has been proposed in which the ends of the bridge are exposed to direct sunlight, and there has been a demand for a weatherproof protection method for the waterproof layer that can withstand such long-term use. For this purpose, acrylic resin-based weather resistant paint is used in some parts,
The durability was 10 years or less, and was not sufficiently satisfactory.
【０００４】[0004]
【発明が解決しようとする課題】本発明の目的は、橋梁
等のコンクリート構造物の防水層の耐候性を向上させる
ことに有る。即ち、橋梁等の防水層を有するコンクリー
ト構造物において、該防水層を保護して直射日光等に晒
されても長期耐久性を確保することのでき、且つ施工が
容易な耐候性の保護方法及び、その上を人が歩くような
使用でも、長期に渡ってそれに耐える強度の耐候性保護
層を有する構造物を提供することを課題とする。An object of the present invention is to improve the weather resistance of a waterproof layer of a concrete structure such as a bridge. That is, in a concrete structure having a waterproof layer such as a bridge, it is possible to secure long-term durability even when exposed to direct sunlight by protecting the waterproof layer, and a weatherproof protection method that is easy to construct and An object of the present invention is to provide a structure having a weather-resistant protective layer that has strength enough to withstand a long walk even when a person walks on it.
【０００５】[0005]
【課題を解決するための手段】本発明者は、これらの課
題を鋭意検討した結果、少なくとも耐候性フィルム層及
び耐熱高強度フィルム層を含む多層シートを、直射日光
に晒される橋梁の端部の防水層の表面に貼付することに
より、防水層の耐候性が改善されることを見出した。
又、前記多層シートに、防水性を有する接着剤層を形成
し、直接コンクリート表面に貼付することも可能であっ
た。更にこれ等の多層シートは、実用上の十分な耐久性
を有しており、施工も容易であることを見出し本発明に
到達した。Means for Solving the Problems As a result of diligent studies on these problems, the present inventor has found that a multilayer sheet containing at least a weather resistant film layer and a heat resistant high strength film layer can be applied to an end portion of a bridge exposed to direct sunlight. It was found that the weather resistance of the waterproof layer is improved by sticking it on the surface of the waterproof layer.
It was also possible to form a waterproof adhesive layer on the multilayer sheet and directly attach it to the concrete surface. Further, they have arrived at the present invention by finding that these multilayer sheets have practically sufficient durability and are easy to apply.
【０００６】即ち、本発明は、耐候性フィルム層
（Ａ）、耐熱高強度フィルム層（Ｂ）及び接着剤層
（Ｃ）からなる多層シートを、コンクリート表面に形成
されている防水層（Ｄ）の外表面に貼付する防水層の耐
候性保護方法であり、又、耐候性フィルム層（Ａ）、耐
熱高強度フィルム層（Ｂ）及び接着剤層（Ｃ）からな
り、防水層を形成する接着剤層（Ｃ）からなる多層シー
トを、コンクリート表面に貼付する耐候性保護方法、又
は、耐候性フィルム層（Ａ）及び耐熱高強度フィルム層
（Ｂ）からなる多層シートを、アクリル系接着剤を用い
てコンクリート表面上に形成されている防水層（Ｄ）の
外表面に貼付する防水層の耐候性保護方法である。耐候
性フィルム層（Ａ）はフッ化ビニル系樹脂又はフッ化ビ
ニリデン系樹脂であることが好ましく、耐候性フィルム
層（Ａ）は、フッ化ビニリデン系樹脂６０％以上、及び
メタクリル酸エステル系樹脂を含有する表層（Ａ１）
と、メタクリル酸エステル系樹脂５０％以上及びフッ化
ビニリデン系樹脂を含有する裏面層（Ａ２）で構成され
ていることがより好ましい。一方で、耐熱高強度フィル
ム層（Ｂ）は、ポリカーボネート、ポリエチレンテレフ
タレート又はポリプロピレンからなるフィルム、もしく
は、ビニロン繊維又はアラミド繊維からなるメッシュの
うちから選択した１種又は２種以上であることが好まし
く、更に接着剤層（Ｃ）は、ゴムアスファルト又はアク
リル系接着剤のいずれかであることが好ましい。又、本
発明は、以上の手段を用いて橋梁端部の防水層の耐候性
を保護したコンクリート橋梁を含む。That is, according to the present invention, a waterproof sheet (D) formed on a concrete surface is a multilayer sheet comprising a weather resistant film layer (A), a heat resistant and high strength film layer (B) and an adhesive layer (C). Is a method for protecting the weather resistance of a waterproof layer to be attached to the outer surface of the film, and also comprises a weather resistant film layer (A), a heat-resistant and high-strength film layer (B) and an adhesive layer (C) to form a waterproof layer. A weather-resistant protection method in which a multi-layer sheet comprising the agent layer (C) is applied to the concrete surface, or a multi-layer sheet comprising the weather-resistant film layer (A) and the heat-resistant and high-strength film layer (B) is replaced with an acrylic adhesive. It is a method for protecting the weather resistance of a waterproof layer which is attached to the outer surface of the waterproof layer (D) formed on the surface of concrete. The weather resistant film layer (A) is preferably a vinyl fluoride resin or a vinylidene fluoride resin, and the weather resistant film layer (A) comprises a vinylidene fluoride resin of 60% or more and a methacrylic acid ester resin. Surface layer contained (A1)
And a back surface layer (A2) containing 50% or more of a methacrylic acid ester resin and a vinylidene fluoride resin. On the other hand, the heat-resistant and high-strength film layer (B) is preferably one or more selected from a film made of polycarbonate, polyethylene terephthalate or polypropylene, or a mesh made of vinylon fiber or aramid fiber, Further, the adhesive layer (C) is preferably either rubber asphalt or acrylic adhesive. Further, the present invention includes a concrete bridge in which the weather resistance of the waterproof layer at the bridge end is protected by using the above means.
【０００７】[0007]
【発明の実施の形態】以下、本発明を詳細に説明する。
本発明は、前記のように耐候性フィルム層（Ａ）、耐熱
高強度フィルム層（Ｂ）、及び接着剤層（Ｃ）からなる
多層シート、又は耐候性フィルム層（Ａ）、耐熱高強度
フィルム層（Ｂ）からなる多層シートを、接着剤にてコ
ンクリート表面上に形成された防水層の表面に貼付する
ことにより、防水層を直射日光から保護するものであ
る。特に橋梁の端部が直射日光に晒される施工方法によ
る工事において、その橋梁の端部の保護に有用である。BEST MODE FOR CARRYING OUT THE INVENTION The present invention will be described in detail below.
As described above, the present invention provides a multilayer sheet comprising a weather resistant film layer (A), a heat resistant high strength film layer (B), and an adhesive layer (C), or a weather resistant film layer (A), a heat resistant high strength film. The multi-layer sheet comprising the layer (B) is attached to the surface of the waterproof layer formed on the concrete surface with an adhesive to protect the waterproof layer from direct sunlight. Especially, it is useful for protecting the end of the bridge in the construction by the construction method in which the end of the bridge is exposed to direct sunlight.
【０００８】耐候性フィルム層（Ａ）としては、直射日
光に耐える耐候性や実用上の強度を有するフィルムであ
れば特に制限はないが、特にフッ化ビニル系樹脂又はフ
ッ化ビニリデン系樹脂フィルムが好ましく、押出成形し
やすい点で更に好ましくはフッ化ビニリデン系樹脂であ
る。本発明でいうフッ化ビニリデン系樹脂とは、フッ化
ビニリデンの単独重合体、フッ化ビニリデン単位を主な
構成成分とする共重合体、及びそれらの重合体を主成分
とし、耐候性を損なわない範囲でメタクリル酸エステル
系樹脂等を混合した組成物をいう。又、同様にフッ化ビ
ニル系樹脂とは、フッ化ビニルの単独重合体、前記と同
様の共重合体、及びそれらにメタクリル酸エステル系樹
脂を混合物した組成物である。これらの樹脂は、耐候性
が優れるとともに、大気中の粉塵や自動車排気ガス等に
よる汚れを減少出来る。The weather resistant film layer (A) is not particularly limited as long as it is a film having weather resistance to withstand direct sunlight and practical strength, but a vinyl fluoride resin or vinylidene fluoride resin film is particularly preferable. A vinylidene fluoride-based resin is more preferable because it is easily extruded. The vinylidene fluoride-based resin referred to in the present invention is a homopolymer of vinylidene fluoride, a copolymer having vinylidene fluoride units as a main constituent, and those polymers as a main component, which do not impair the weather resistance. A composition in which a methacrylic acid ester resin or the like is mixed in the range. Similarly, the vinyl fluoride resin is a homopolymer of vinyl fluoride, a copolymer similar to the above, and a composition in which a methacrylic acid ester resin is mixed. These resins have excellent weather resistance and can reduce dirt due to dust in the atmosphere, automobile exhaust gas, and the like.
【０００９】本発明でフッ化ビニリデン系樹脂との配合
に用いられるメタクリル酸エステル系樹脂とは、メタク
リル酸メチルの単独重合体、又はメタクリル酸メチルと
共重合可能な単量体との共重合体をいう。共重合可能な
単量体としては、炭素数２〜４のメタクリル酸エステ
ル、アクリル酸メチル、アクリル酸ブチルをはじめとす
る炭素数１〜８のアクリル酸エステル、スチレン、α−
メチルスチレン、アクリロニトリル、アクリル酸及び、
その他のエチレン性不飽和モノマー等がある。好ましく
は、メタクリル酸メチルと炭素数１〜８のアクリル酸エ
ステルの共重合体であり、さらに好ましくはアクリル酸
ブチルやアクリル酸メチルをコモノマーとするメタクリ
ル酸メチル共重合体である。The methacrylate ester resin used in the present invention for blending with the vinylidene fluoride resin is a homopolymer of methyl methacrylate or a copolymer of a monomer copolymerizable with methyl methacrylate. Say. Examples of the copolymerizable monomer include methacrylic acid esters having 2 to 4 carbon atoms, acrylic acid esters having 1 to 8 carbon atoms such as methyl acrylate and butyl acrylate, styrene, α-
Methylstyrene, acrylonitrile, acrylic acid and
Other examples include ethylenically unsaturated monomers. A copolymer of methyl methacrylate and an acrylate ester having 1 to 8 carbon atoms is preferable, and a methyl methacrylate copolymer having butyl acrylate or methyl acrylate as a comonomer is more preferable.
【００１０】耐候性フィルム層（Ａ）には、耐候性をさ
らに向上させるために、耐候性フィルム層（Ａ）に用い
たフッ化ビニリデン系樹脂等と相溶性のある紫外線吸収
剤を添加しても良く、必要に応じて顔料、酸化防止剤、
及び充填剤等を添加しても良く、印刷により模様をつけ
ても良い。To the weather-resistant film layer (A), an ultraviolet absorber compatible with the vinylidene fluoride resin used for the weather-resistant film layer (A) is added in order to further improve the weather resistance. Also good, if necessary, pigment, antioxidant,
Also, a filler or the like may be added, and a pattern may be formed by printing.
【００１１】さらに、耐候性フィルム層（Ａ）として
は、フッ化ビニリデン系樹脂を好ましくは６０％以上、
更に好ましくは７５％以上及びメタクリル酸エステル系
樹脂を含有した組成物からなる層を表層とし、この表層
に、メタクリル酸エステル系樹脂を５０％以上、及びフ
ッ化ビニリデン系樹脂を含有する組成物からなる裏面層
を積層した多層フィルムを用いることが好ましい。この
裏面層を有するフィルムを用いると、耐熱高強度フィル
ム（Ｂ）との接着が容易となる。表層のフッ化ビニリデ
ン系樹脂が６０％未満では、本発明の目的である直射日
光に晒される用途での使用では、耐候性の保護効果が十
分得られない場合がある。又、裏面層のメタクリル酸エ
ステル系樹脂が５０％未満では、前記の耐熱高強度フィ
ルム（Ｂ）との接着が難しくなる場合がある。Further, as the weather resistant film layer (A), vinylidene fluoride resin is preferably contained in an amount of 60% or more,
More preferably, a layer composed of a composition containing 75% or more and a methacrylic acid ester resin is used as a surface layer, and the surface layer is formed from a composition containing 50% or more of a methacrylic acid ester resin and a vinylidene fluoride resin. It is preferable to use a multilayer film in which the following back surface layer is laminated. Use of the film having this back surface layer facilitates adhesion with the heat-resistant and high-strength film (B). When the vinylidene fluoride-based resin in the surface layer is less than 60%, the weather resistance protective effect may not be sufficiently obtained in use for the purpose of the present invention where the resin is exposed to direct sunlight. If the amount of the methacrylic acid ester resin in the back surface layer is less than 50%, the adhesion with the heat resistant and high strength film (B) may be difficult.
【００１２】耐候性フィルム層（Ａ）の厚さは、２０〜
２００μｍが好ましい。２０μｍ未満だと耐候性が得ら
れないおそれがあり、２００μｍを越えると耐候性フィ
ルム層（Ａ）が厚くなり過ぎてコストが高くなるばかり
でなく、コンクリート表面への施工が難しくなるおそれ
がある。The thickness of the weather resistant film layer (A) is 20 to 20.
200 μm is preferable. If it is less than 20 μm, the weather resistance may not be obtained, and if it exceeds 200 μm, not only the weather resistant film layer (A) becomes too thick to increase the cost, but also it may be difficult to apply it to the concrete surface.
【００１３】本発明においては、耐候性フィルム層
（Ａ）の強度を補強する目的で、耐熱高強度フィルム層
（Ｂ）を積層する必要が有る。このフィルム層を積層す
ることにより、多層シートの強度が高くなり、長期の使
用における耐久性が向上し、かつ、耐熱性が大きくなる
ために夏場の直射日光による温度上昇があっても多層シ
ートが収縮することがなくなる。In the present invention, it is necessary to laminate a heat resistant and high strength film layer (B) for the purpose of reinforcing the strength of the weather resistant film layer (A). By laminating this film layer, the strength of the multi-layer sheet is increased, the durability in long-term use is improved, and the heat resistance is increased, so that the multi-layer sheet can be formed even if the temperature rises due to direct sunlight in summer. It will not shrink.
【００１４】耐熱高強度フィルム層（Ｂ）としては、耐
熱性と高強度を有するものであれば特に制限はないが、
耐熱性と強度が大きい点で、ポリカーボネート、ポリエ
チレンテレフタレート、ポリプロピレンからなるフィル
ム、もしくはビニロン繊維又はアラミドからなるメッシ
ュ等も好ましく、これらのうちから１種もしくは２種以
上を選択して用いることができる。更に、ポリカーボネ
ート又はポリエチレンテレフタレートの延伸フィルム
が、フィルムのどの部分でも大きな強度改良効果が得ら
れる点でより好ましい。The heat-resistant and high-strength film layer (B) is not particularly limited as long as it has heat resistance and high strength.
From the viewpoint of high heat resistance and strength, a film made of polycarbonate, polyethylene terephthalate, polypropylene, a mesh made of vinylon fiber or aramid, and the like are also preferable, and one or more of them can be selected and used. Furthermore, a stretched film of polycarbonate or polyethylene terephthalate is more preferable in that a large strength improving effect can be obtained in any part of the film.
【００１５】耐熱高強度フィルム層（Ｂ）のフィルム又
はメッシュには、それ自体の十分な耐候性を確保するた
めに、紫外線吸収剤を添加しても良く、又、必要に応じ
て顔料、酸化防止剤、充填剤、可塑剤等を添加しても良
い。An ultraviolet absorber may be added to the film or mesh of the heat-resistant and high-strength film layer (B) in order to secure sufficient weather resistance of itself, and if necessary, a pigment or an oxidant may be added. You may add an inhibitor, a filler, a plasticizer, etc.
【００１６】耐熱高強度フィルム層（Ｂ）の厚さは、強
度と施工性から決められるが、３０〜３００μｍが好ま
しい。３０μｍ未満だと耐熱高強度フィルム層の強度が
十分でないおそれがあり、３００μｍを越えると耐熱高
強度フィルム層が硬くなり過ぎてコンクリートコーナー
表面への施工が難しくなるおそれがある。The thickness of the heat-resistant and high-strength film layer (B) is determined depending on the strength and workability, but is preferably 30 to 300 μm. If it is less than 30 μm, the strength of the heat-resistant and high-strength film layer may not be sufficient, and if it exceeds 300 μm, the heat-resistant and high-strength film layer may be too hard and it may be difficult to apply it to the concrete corner surface.
【００１７】耐候性フィルム層（Ａ）と耐熱高強度フィ
ルム層（Ｂ）を積層するには、ウレタン系、エポキシ
系、又はアクリル系等公知の接着剤を使用できるが、接
着性の点でウレタン系のものが好ましく、一般的にはフ
ィルムをドライラミネート法により積層する。積層によ
って得られた（Ａ）層と（Ｂ）層からなる多層シートの
厚さは、各層の組成や厚さにより異なるが、防水層
（Ｄ）に貼付する施工性の観点から、一般的には４００
μｍ以下が好ましい。To laminate the weather-resistant film layer (A) and the heat-resistant and high-strength film layer (B), known adhesives such as urethane-based, epoxy-based or acrylic-based adhesives can be used. A type is preferable, and generally, films are laminated by a dry laminating method. The thickness of the multilayer sheet composed of the (A) layer and the (B) layer obtained by laminating varies depending on the composition and thickness of each layer, but is generally from the viewpoint of workability of sticking to the waterproof layer (D). Is 400
μm or less is preferable.
【００１８】本発明の耐候性保護に適用されるコンクリ
ートは、雨水等によるコンクリートの浸食を抑制する目
的で、通常その表面に防水層が設けられている。その防
水層（Ｄ）としては、アスファルト系、アクリル系、又
はウレタン系接着剤、もしくは各種ゴムからなるシート
等が用いられている。本発明の接着剤層（Ｃ）は、一般
的には前記の耐候性フィルム層（Ａ）と耐熱高強度フィ
ルム層（Ｂ）を積層した多層シート、及び該防水層
（Ｄ）、又はコンクリート表面に接着でき、長期の接着
耐久性を有するものであれば良い。但し、夏場の温度で
軟化して粘着力が低下しない為には、６５℃以上の実用
耐熱温度を有するものが好ましい。The concrete applied to the weather resistance protection of the present invention is usually provided with a waterproof layer on the surface thereof for the purpose of suppressing erosion of the concrete by rainwater or the like. As the waterproof layer (D), a sheet made of an asphalt-based, acrylic-based, or urethane-based adhesive, or various kinds of rubber is used. The adhesive layer (C) of the present invention is generally a multilayer sheet obtained by laminating the weather resistant film layer (A) and the heat resistant and high strength film layer (B), and the waterproof layer (D), or a concrete surface. Any material that can be adhered to and has long-term adhesion durability may be used. However, those having a practical heat resistance temperature of 65 ° C. or higher are preferable in order to prevent the adhesive force from being lowered by softening at the temperature in summer.
【００１９】接着剤層（Ｃ）に用いられる接着剤として
は、ゴムアスファルト系、アクリル系、又はエポキシ系
の接着剤が使用できる。これらの接着剤は、施工の際に
前記の耐候性フィルム層（Ａ）と耐熱高強度フィルム層
（Ｂ）を積層した積層シート、もしくは後述の防水層
（Ｄ）の表面に塗布して用いても良いが、ゴムアスファ
ルト系接着剤は、予め前記の積層シートにコーティング
して接着剤層（Ｃ）を設けた「耐候性保護シート」と
し、施工現場で防水層（Ｄ）表面に常温で圧着するだけ
で貼付できるという点で、施工性及び取り扱い性の面か
ら好ましい。又、ゴムアスファルト系接着剤は、それ自
体が防水性を有するので、前記耐候性保護シートをコン
クリート表面に直接貼付して用いることもできる。その
場合接着剤が防水層（Ｄ）の役割を果たす。As the adhesive used in the adhesive layer (C), a rubber asphalt-based, acrylic-based or epoxy-based adhesive can be used. These adhesives are used by applying to the surface of a laminated sheet in which the weather resistant film layer (A) and the heat resistant and high strength film layer (B) are laminated at the time of construction, or the waterproof layer (D) described later. The rubber asphalt adhesive can be used as a "weatherproof protective sheet" by coating the above-mentioned laminated sheet with the adhesive layer (C) in advance, and pressure-bonding it to the surface of the waterproof layer (D) at room temperature at the construction site. From the viewpoint of workability and handleability, it can be attached simply by Further, since the rubber asphalt adhesive itself has a waterproof property, the weather resistant protective sheet can be used by directly pasting it on the concrete surface. In that case, the adhesive plays the role of the waterproof layer (D).
【００２０】本発明において、ゴムアスファルト系接着
剤とは、アスファルトにゴムを添加して改質した、自着
性を有するゴムアスファルトであり、使用されるゴム
は、スチレン・ブタジエン系ゴム（ブロック共重合体及
びそれらの水添物を含む）、クロロプレンゴム等各種の
ゴムが使用できるが、自着性や耐熱性が大きい点で、ス
チレン・ブタジエン系ゴムが好ましい。In the present invention, the rubber asphalt adhesive is a rubber asphalt having self-adhesive property obtained by modifying rubber by adding rubber to the asphalt, and the rubber used is a styrene-butadiene rubber (block copolymer). Various rubbers such as polymers and their hydrogenated products) and chloroprene rubber can be used, but styrene-butadiene rubbers are preferable from the viewpoint of high self-adhesiveness and heat resistance.
【００２１】接着剤層（Ｃ）の厚さは、前記の接着剤層
としての機能を満たす範囲であれば、特に限定されるも
のではないが、接着剤層（Ｃ）がゴムアスファルト層の
場合は、作業性、性能、接着面の凹凸追従性、及びコス
トの点で、１．０〜３.０ｍｍが好ましい。The thickness of the adhesive layer (C) is not particularly limited as long as it satisfies the function as the above-mentioned adhesive layer, but when the adhesive layer (C) is a rubber asphalt layer. Is preferably 1.0 to 3.0 mm in terms of workability, performance, conformability to unevenness of the adhesive surface, and cost.
【００２２】次に、本発明の施工方法について述べる。
一般的には前記の耐候性フィルム層（Ａ）、耐熱高強度
フィルム層（Ｂ）を積層した多層シートの耐熱高強度フ
ィルム層（Ｂ）の表面、防水層（Ｄ）表面、又はコンク
リート表面に、前記の接着剤を塗布して該多層シートを
貼付する。一方で接着剤層（Ｃ）としてゴムアスファル
ト層を設けた「耐候性保護シート」は、ゴムアスファル
ト層自体が優れた防水性を有しているので、プライマー
を介して直接コンクリート表面に貼付することで、防水
層の機能を合わせ持ったシートとして用いることができ
る。例えば、アスファルト系プライマーをコンクリート
表面にローラー等で塗布、乾燥後、プライマー上に多層
シートを空気が巻き込まない様に貼り付けるとよい。貼
り付けの際にはゴムアスファルト層とコンクリート表面
のプライマー層が接する様にする。尚、プライマーの選
択により湿潤コンクリート面への施工も可能となる。Next, the construction method of the present invention will be described.
Generally, on the surface of the heat-resistant and high-strength film layer (B), the waterproof layer (D) surface, or the concrete surface of the multilayer sheet in which the weather resistant film layer (A) and the heat-resistant and high-strength film layer (B) are laminated. Then, the above-mentioned adhesive is applied and the multilayer sheet is attached. On the other hand, the "weatherproof protective sheet" provided with the rubber asphalt layer as the adhesive layer (C) has excellent waterproofness as the rubber asphalt layer itself, so it should be directly applied to the concrete surface via a primer. Thus, it can be used as a sheet that also has the function of a waterproof layer. For example, it is advisable to apply an asphalt-based primer to the surface of concrete with a roller or the like, dry it, and then attach a multilayer sheet onto the primer so that air will not be trapped therein. When applying, make sure that the rubber asphalt layer and the primer layer on the concrete surface are in contact with each other. It should be noted that it is possible to apply it to wet concrete surface by selecting the primer.
【００２３】又、この耐候性保護シート同士を繋ぐに
は、接着剤層（Ｃ）を介して耐候性保護シート同士を重
ね合わせる事で接着する。また 繋ぎ合わせ端部は接着
剤、シーラー及び耐候性塗料で処理する。又、より好ま
しくは耐候性保護シートの端部をアンカーピン等で機械
的に止め、その後にアンカーピン頭部を覆うように多層
シートを貼ると防水性が完全に保たれる。この保護シー
トを、適当な間隔でアンカーピン等で止めると、更に安
全になる。前記のようにこの耐候性保護シートは自着性
なので、施工性及び取り扱い性が良好である。Further, in order to connect the weather-resistant protective sheets to each other, the weather-resistant protective sheets are superposed on each other via the adhesive layer (C) so as to be bonded. Also, the joined ends are treated with an adhesive, a sealer and a weather resistant paint. Further, more preferably, the waterproof property is completely maintained by mechanically stopping the end portion of the weather resistant protective sheet with an anchor pin or the like and then laminating a multilayer sheet so as to cover the head of the anchor pin. It becomes safer if this protective sheet is fixed with anchor pins or the like at appropriate intervals. As described above, since this weather resistant protective sheet is self-adhesive, it has good workability and handleability.
【００２４】端部処理に用いるシーラーとしては、シリ
コンゴム系、ゴムアスファルト系、ウレタンアスファル
ト系、又はアクリル系が使用できるが、耐候性も良好で
あることから、シリコンゴム系又はアクリル系が適して
いる。又、端部処理に用いる耐候性塗料としては、フッ
素系又はアクリル系等の通常使用されるもの用いること
ができる。Silicone rubber, rubber asphalt, urethane asphalt, or acrylic can be used as the sealer for edge treatment, but silicone rubber or acrylic is suitable because of its good weather resistance. There is. Further, as the weather resistant coating used for the edge treatment, a commonly used one such as fluorine type or acrylic type can be used.
【００２５】[0025]
【実施例】以下に実施例に基づき本発明を説明する。EXAMPLES The present invention will be described below based on examples.
【００２６】（実施例１）フッ化ビニリデン樹脂９０
％、メチルメタクリレート樹脂１０％からなる表層と、
フッ化ビニリデン樹脂３０％とメチルメタクリレート樹
脂７０％からなる裏面層とを共押出することにより、４
０μｍ厚（表層３２μｍ、裏面層８μｍ）の２層フィル
ムからなるフッ素系樹脂を作製し、耐候性フィルム層と
した。耐候性フィルム層中の裏面層の上に、ポリカーボ
ネート樹脂からなる厚さ１００μｍのフィルムを、ウレ
タン系接着剤により積層し、耐熱高強度フィルム層とし
た。耐熱高強度フィルム層の上に、厚さ１．４ｍｍのゴ
ムアスファルト（実用耐熱温度７０℃以上、ゴムとして
スチレン・ブタジエンゴム使用）の接着剤層をコーティ
ングし、耐候性保護シートを作製した。(Example 1) Vinylidene fluoride resin 90
%, A surface layer made of methylmethacrylate resin 10%,
By coextruding a backside layer composed of 30% of vinylidene fluoride resin and 70% of methyl methacrylate resin, 4
A fluorine-based resin composed of a two-layer film having a thickness of 0 μm (front layer 32 μm, back surface layer 8 μm) was prepared as a weather resistant film layer. A 100 μm-thick film made of a polycarbonate resin was laminated on the back surface layer of the weather resistant film layer with a urethane adhesive to form a heat resistant and high strength film layer. A 1.4 mm thick rubber asphalt (practical heat resistant temperature of 70 ° C. or higher, using styrene / butadiene rubber as a rubber) adhesive layer was coated on the heat resistant and high strength film layer to prepare a weather resistant protective sheet.
【００２７】一方で、コンクリート試験板にアスファル
ト系プライマーをローラーで約１００ｇ／ｍ2塗布し、
手で触ってタックがなくなった事を確認後（約３０分
後）、アスファルト系防水層を貼った後に、前記の耐候
性保護シートを空気が巻き込まれない様にして、耐候性
保護シートのゴムアスファルト層と防水層が接する様に
貼りつけた。また 同様にコンクリート表面のプライマ
ー層が乾燥後、前記保護シートのゴムアスファルト層と
プライマーが接する様に貼り付けた。これらを供試体と
し、接着強度、耐候性、及び施工時間を測定した。On the other hand, a concrete test plate is coated with an asphalt-based primer by a roller at about 100 g / m 2 ,
After confirming that the tack has been eliminated by touching with your hands (after about 30 minutes), attach the asphalt-based waterproof layer, and then prevent the air from getting caught in the weatherproof protective sheet, and then use the rubber of the weatherproof protective sheet. I stuck it so that the asphalt layer and the waterproof layer were in contact. Similarly, after the primer layer on the concrete surface was dried, it was attached so that the rubber asphalt layer of the protective sheet was in contact with the primer. These were used as test pieces, and the adhesive strength, weather resistance, and construction time were measured.
【００２８】（試験方法）
（１）防水層との接着性
前記保護シートを２３℃で４８時間で養生し、その防水
層と保護シート間、コンクリート試験板と保護シート間
の接着強度を以下の条件で測定した。
試験機； テンシロン
剥離角度；１８０度のピィーリング
剥離速度；１００ｍｍ／ｍｉｎサンフ゜ル
巾；３５ｍｍ
（２） 耐候試験
JIS Z9117に準拠してデューサイクル式サンシャインカ
ーボン促進耐候試験機を用いて、ブラックパネル温６３
℃、水噴霧の照射／結露サイクルを１時間／１時間の条
件下で、前記供試体の保護シート側を曝露し、サンプル
とした。そのサンプルの暴露表面の目視による外観評価
及び、光電色彩計（Ｃ光源使用）により、ΔＥを測定し
た。
（３）施工性
コンクリート製高架橋に立設した高欄に、作成した保護
シート１０ｍ2を貼り付け、貼り付けが終わるまでの施
工時間を測定した。(Test method) (1) Adhesiveness with waterproof layer The protective sheet was aged at 23 ° C. for 48 hours, and the adhesive strength between the waterproof layer and the protective sheet and between the concrete test plate and the protective sheet was as follows. It was measured under the conditions. Testing machine; Tensilon peeling angle; 180 degree peeling peeling speed; 100 mm / min sample width; 35 mm (2) Weather resistance test In accordance with JIS Z9117, a black panel temperature of 63 using a dew cycle type sunshine carbon accelerated weathering tester.
Under the condition of irradiation cycle of water spray / condensation of water spray for 1 hour / 1 hour, the protective sheet side of the specimen was exposed to obtain a sample. ΔE was measured by visual evaluation of the exposed surface of the sample and by a photoelectric colorimeter (using a C light source). (3) Workability The prepared protective sheet 10 m 2 was attached to the railing erected on the concrete viaduct, and the construction time until the attachment was completed was measured.
【００２９】（実施例２）耐熱高強度フィルム層とし
て、厚さ１００μｍのポリエチレンテレフタレートの2
軸延伸フィルムを使用した以外は、実施例１と同様に行
い、評価の結果を表１に示した。Example 2 As a heat-resistant and high-strength film layer, a polyethylene terephthalate film having a thickness of 100 μm was used.
Example 1 was repeated except that the axially stretched film was used, and the evaluation results are shown in Table 1.
【００３０】（実施例３）フッ化ビニリデン樹脂９０
％、メチルメタクリレート樹脂１０％からなる表層と、
フッ化ビニリデン樹脂４０％とメチルメタクリレート樹
脂６０％からなる裏面層とを共押出することにより、４
０μｍ厚（表層３２μｍ、裏面層８μｍ）の２層フィル
ムからなるフッ素系樹脂を作製し、耐候性フィルム層と
した。耐候性フィルム層中の裏面層の上に、ポリカーボ
ネート樹脂からなる厚さ１００μｍのフィルムを、ウレ
タン系接着剤により積層し、耐熱高強度フィルム層とし
た。Example 3 Vinylidene fluoride resin 90
%, A surface layer made of methylmethacrylate resin 10%,
By coextruding a backside layer composed of 40% vinylidene fluoride resin and 60% methyl methacrylate resin, 4
A fluorine-based resin composed of a two-layer film having a thickness of 0 μm (front layer 32 μm, back surface layer 8 μm) was prepared as a weather resistant film layer. A 100 μm-thick film made of a polycarbonate resin was laminated on the back surface layer of the weather resistant film layer with a urethane adhesive to form a heat resistant and high strength film layer.
【００３１】一方で、コンクリート板上にアスファルト
シート系防水材［電化ビチューシン５０００］をアスフ
ァルト系プライマーを１００g／m2程度塗布後貼りつけ
防水層とした。その上にアクリル系接着剤（ハードロッ
クII、電気化学工業製）を塗布し接着剤層とし、上記多
層フィルムのポリカーボネート面が該接着剤層に接する
様に貼りつけたものを供試体とし、試験方法（１）と同
様に試験評価した。On the other hand, a waterproof layer was prepared by applying an asphalt sheet waterproof material [Electronic Bitchucin 5000] on a concrete plate after applying an asphalt primer of about 100 g / m 2 thereon. An acrylic adhesive (Hard Rock II, manufactured by Denki Kagaku Kogyo Co., Ltd.) was applied thereon to form an adhesive layer, which was attached so that the polycarbonate surface of the above-mentioned multilayer film was in contact with the adhesive layer. The test evaluation was performed in the same manner as the method (1).
【００３２】（比較例1）通常の橋面防水のアスファル
ト系シート防水で採用される端部処理方法に準じて、コ
ンクリート板上に加熱熔融したゴムアスファルトコンパ
ウンドを塗布後、メッシュを貼り付け、更に加熱熔融し
たゴムアスファルトコンパウンドを塗布したものを防水
材の供試体とし、試験方法（１）と同様に試験評価し
た。尚、本比較例では、耐候性保護材は使用していない
ので、試験方法（３）の「耐候試験」において、ひび割
れが発生し防水材としての性能が失われた。(Comparative Example 1) A rubber asphalt compound which was heated and melted was applied onto a concrete plate in accordance with an end treatment method adopted for a normal bridge surface waterproofing asphalt sheet waterproofing. A test piece of a waterproof material was obtained by applying a heat-melted rubber asphalt compound, and was tested and evaluated in the same manner as in Test Method (1). In addition, in this comparative example, since the weather resistance protective material was not used, in the "weather resistance test" of the test method (3), cracking occurred and the performance as the waterproof material was lost.
【００３３】実施例１〜３及び比較例１の評価結果を表
１に纏めた。The evaluation results of Examples 1 to 3 and Comparative Example 1 are summarized in Table 1.
【００３４】[0034]
【表１】 [Table 1]
【００３５】[0035]
【発明の効果】本発明の耐候性保護方法により、橋梁等
の防水層を有するコンクリート構造物において、該防水
層を保護して直射日光等に晒されても長期耐久性を確保
することができ、且つ施工が容易な耐候性の保護方法及
び、長期の使用に耐える強度を有する耐候性保護層を有
する構造物を提供することができる。According to the weather resistance protection method of the present invention, in a concrete structure having a waterproof layer such as a bridge, the waterproof layer can be protected to ensure long-term durability even when exposed to direct sunlight. Further, it is possible to provide a weather resistant protection method that is easy to apply and a structure having a weather resistant protective layer having strength that can withstand long-term use.
フロントページの続き Ｆターム(参考） 2D059 AA14 BB39 GG01 GG55 4F100 AJ20G AK07B AK17A AK19A AK19E AK21B AK25A AK25E AK25G AK42B AK45B AK47B AL05A AL05E AN00G AR00A AR00B AR00C AR00E BA04 BA05 BA07 BA10A BA10D DG01B DG12B DG13B GB90 JD05C JJ03B JK01B JL09 JL09A JL09E YY00E Continued front page F-term (reference) 2D059 AA14 BB39 GG01 GG55 4F100 AJ20G AK07B AK17A AK19A AK19E AK21B AK25A AK25E AK25G AK42B AK45B AK47B AL05A AL05E AN00G AR00A AR00B AR00C AR00E BA04 BA05 BA07 BA10A BA10D DG01B DG12B DG13B GB90 JD05C JJ03B JK01B JL09 JL09A JL09E YY00E
Claims (8)
ィルム層（Ｂ）及び接着剤層（Ｃ）からなる多層シート
を、コンクリート表面の防水層（Ｄ）の外表面に貼付す
る防水層の耐候性保護方法。1. A waterproof layer in which a multilayer sheet comprising a weather resistant film layer (A), a heat resistant and high strength film layer (B) and an adhesive layer (C) is attached to the outer surface of a waterproof layer (D) on a concrete surface. Weather protection method.
ィルム層（Ｂ）及び防水層を形成する接着剤層（Ｃ）か
らなる多層シートを、コンクリート表面に貼付する防水
層の耐候性保護方法。2. A weatherproof protection for a waterproof layer in which a multi-layer sheet comprising a weatherproof film layer (A), a heat-resistant and high-strength film layer (B) and an adhesive layer (C) forming a waterproof layer is attached to a concrete surface. Method.
はアクリル系接着剤である、請求項１又は請求項２に記
載の防水層の耐候性保護方法。3. The method for protecting weather resistance of a waterproof layer according to claim 1 or 2, wherein the adhesive layer (C) is a rubber asphalt or an acrylic adhesive.
フィルム層（Ｂ）からなる多層シートを、アクリル系接
着剤を用いてコンクリート表面上に形成されている防水
層（Ｄ）の外表面に貼付する防水層の耐候性保護方法。4. An outer surface of a waterproof layer (D), which comprises a multi-layer sheet comprising a weather resistant film layer (A) and a heat resistant and high strength film layer (B) formed on a concrete surface using an acrylic adhesive. A method for protecting the weather resistance of the waterproof layer attached to.
系樹脂又はフッ化ビニリデン系樹脂からなる請求項１〜
４のいずれか１項に記載の防水層の耐候性保護方法。5. The weather resistant film layer (A) is made of vinyl fluoride resin or vinylidene fluoride resin.
4. The method for protecting weather resistance of a waterproof layer according to any one of 4 above.
リデン系樹脂６０％以上、及びメタクリル酸エステル系
樹脂を含有する表層（Ａ１）と、メタクリル酸エステル
系樹脂５０％以上及びフッ化ビニリデン系樹脂を含有す
る裏面層（Ａ２）で構成されている、請求項５に記載の
防水層の耐候性保護方法。6. A surface layer (A1) in which the weather resistant film layer (A) contains 60% or more of vinylidene fluoride resin and a methacrylic acid ester resin, and 50% or more of methacrylic acid ester resin and vinylidene fluoride. The weather resistance protecting method for a waterproof layer according to claim 5, wherein the waterproof layer is composed of a back surface layer (A2) containing a resin.
ーボネート、ポリエチレンテレフタレート又はポリプロ
ピレンからなるフィルム、もしくは、ビニロン繊維又は
アラミド繊維からなるメッシュのうちから選択した１種
又は２種以上である、請求項１〜６のいずれか１項に記
載の防水層の耐候性保護方法。7. The heat-resistant and high-strength film layer (B) is one or more selected from a film made of polycarbonate, polyethylene terephthalate or polypropylene, or a mesh made of vinylon fiber or aramid fiber. Item 7. A method for protecting a waterproof layer from weathering according to any one of Items 1 to 6.
法で、橋梁端部の防水層の耐候性を保護したコンクリー
ト橋梁。8. A concrete bridge in which the weather resistance of the waterproof layer at the bridge end is protected by the method according to any one of claims 1 to 7.