HK40089250B - Briquettes - Google Patents

Description

The present invention relates to the production of briquettes, for example from coal, metal or metal ores. Typically, the briquettes are formed from powdered material and utilised binders such as at least partially saponified polyvinyl alcohol (PVA) and an alkali metal alkyl siliconate or polyalkylsilicic acid; formaldehyde resins, polyacrylamide; and styrene acrylic emulsions. The briquettes are typically cold cured but are still capable of being used in blast furnaces.

There are a considerable quantity of powdered minerals worldwide. These wastes result from mining manufacturing and power generation processes and represent considerable potential resource for energy or metal manufacturing. One potential problem of such powdered materials is that they are extremely difficult to transport in the powder form and, for example, coal dust in a powdered form represents a potential explosion hazard.

Additional problems with such materials include that simply adding the powder materials to a combustion chamber or, for example, a blast furnace or direct reduced iron (DRI), results in the consumption of the material before it reaches the optimum part of the combustion chamber or furnace.

There is therefore a need to be able to bind the powder material together to allow it to be successfully transported or to allow it to be utilised within, for example, blast furnaces.

The use of, for example, saponified PVA in combination with molasses, has been used to assist in the production of coal and coke briquettes comprising calcium carbonate ( DE 3335241 ). The use of other additives to the PVA, such as starch, has also been described ( EP 0252332 ) and also other variations of utilising PVA as a binder ( US 4,586,936 and EP 0284252 ).

Additionally, it is also known to utilise other binders, such as phenol formaldehyde resins ( JP 2011047006 ) or sodium silicate ( US 4,169,711 ) with such particulate material. Such silicates may be used in concentrations as high as 30% wt.

Metal briquettes can also be formed by sintering metal dust or finings. However, this takes a large amount of energy to sinter such material.

Problems associated with such binding agents include that the resistance of the briquettes to moisture, for example from rainfall falling on the finished briquettes, is often limited. Moreover, it is desirable for the briquette to have the ability to resist damage during transport, for example, by being dropped from conveyor belts or other transport systems. The briquette must retain its integrity as it passes through the furnace into the melting furnace, otherwise its performance in, for example, blast furnaces or DRI plants, can be adversely affected. Typically in the art, cement or clay-type binders are used for this purpose. However, the yield of the furnaces reduced due to the volume of the briquette that is lost due to the replacement of some of the coal by cement or clay. Moreover the presence of the cement of clay increases the amount of silica in the iron and the slag produced at the end of the process.

There are other more practical problems associated with other binders, such as the use of starches in the process as, for example, starches are typically expensive or hard to come by in the large quantities required for the large amounts of particulate materials that are available to be used with such processes.

The current invention is directed to the identification that mixing a variety of different binders can produce briquettes having excellent structural properties that lend themselves to be able to be used in, for example, blast furnaces and for the use in the production of power.

Described is a briquette comprising:

1. (i) a particulate material; and
2. (ii) a binder, the binder comprising (a) at least partially saponified polyvinyl alcohol (PVA) and (b) an alkali metal alkyl siliconate or polyalkylsilicic acid;

wherein the particulate material is selected from a carbonaceous material, metal, metal ore, mineral waste or a mixture thereof.

The carbonaceous material may, for example, be coke, graphite, carbon black, peat or coal. Coal may be any grade of coal, including lignites, sub-bituminous coal, bituminous coal, steam coal or anthracite.

Mineral wastes include mill scale, mill sludges, fines from ores or metal containing wastes.

The metal may be, or the metal ore mineral waste, may contain iron, zinc, nickel, copper, chromium, manganese, gold, platinum, silver, titanium, tin, lead, vanadium, cadmium, beryllium, molybdenum, uranium or mixtures thereof or elemental metal or in the form of, for example, oxides or silicates.

Polyvinyl alcohol is typically commercially formed from polyvinyl acetate by replacing the acetic acid radical of acetate with a hydroxyl radical by reacting the polyvinyl acetate with sodium hydroxide in a process called saponification. Partially saponified means that some of the acetate groups have been replaced by hydroxyl groups and thereby forming at least a partially saponified polyvinyl alcohol containing vinyl alcohol residues.

Typically, the PVA has a degree of saponification of at least 80%, typically at least 85%, at least 90%, at least 95%, 98%, 99% or 100% saponification. PVA may be obtained commercially from for example, Kuraray Europe GmbH of Frankfurt Am Main, Germany.

Typically it is utilised as a solution in water. The PVA may be modified to include a sodium hydroxide content.

Typically the PVA binder has an active polymer content of 12-13% and a pH in the range 4-6 when in solution.

Typically the briquette contains 0.01-0.8% by weight of PVA. More typically it contains 0.5% by weight or 0.4% or 0.3% by weight PVA.

The alkali metal alkyl siliconate may be an alkali metal C₁ to C₄ alkyl siliconate, such as an alkali metal methyl siliconate. Alternatively, the methyl group moiety may be replaced by an ethyl, propyl or butyl moiety.

Typically the alkali metal is a sodium or potassium, most typically potassium.

Most typically potassium methyl siliconate is used, for example, sold under the trade names Silres by Wacker Chemie GmbH. This has been found to create briquettes with better drop resistance or lignin sulphate. Moreover, it produces surprisingly heat stable briquettes with briquettes capable of substantially maintaining their shape in a reducing atmosphere of UP TO 1200°C.

Alkali metal alkyl siliconates typically react with carbon dioxide during a curing process to produce the equivalent polyalkylsilicic acid, such as a poly C₁ to C₄ alkyl silicic acid, such as poly methyl silicic acid. They are conventionally used as masonry waterproofing agents.

Typically 0.01% of the alkali metal alkyl siliconate or polyalkylsilicic acid, more typically 0.5% or 0.2% by weight of the material is used.

The applicant has also found that the addition of up to 15% by weight, typically 8% or 5% by weight of a metal ore or mineral waste, improves the strength of the briquette further. Typically the metal ore is, for example, and iron-containing ore, such as ferrous or ferric oxide.

The applicant has identified that using the specific siliconate or polysilicic acid, improves the strength of the material. That is, for example, it improves the green strength of the material and allows the briquette that is formed to survive drops and knocks during transportation processes and also to survive the heat of a furnace to allow it to progress into the melting zone of, for example, a blast furnace.

An aspect of the invention provides a briquette comprising:

1. (i) particulate metal ore, and
2. (ii) a binder comprising partially saponified polyvinyl alcohol and 0.5 to 1.5 wt % phenol formaldehyde resin.

This has been found to be particularly successful at producing iron-ore containing briquettes, such as from iron ore finings, meeting BS 4696-2 static reduction disintegration index, and compressive strength tests.

Phenol formaldehyde resins are generally known in the art. Typically the resin is a resole resin made with formaldehyde to phenol ratios of greater than 1, typically around 1.5.

The resin may be mixed into the finings as powder or as an aqueous solution.

The iron ore may be any naturally or non-naturally occurring ore, such as haematite, magnetite, or wustite any may contain naturally occurring contaminants.

Typically twin-shaft batching mixers are used to agglomerate the mixture. A roller press is typically used to form the briquettes. Continuous mixers do not typically control the material quantities accurately enough.

PVA may be optionally added from typically 0.1 to 0.2 wt %, especially 0.125% by weight. PVA may be as defined above.

Guar gum may be added together with or instead of PVA at typically 1.05 wt % to 1 wt %, typically 0.5 wt %.

Guar gum is a commercially available galactomannan gum. Typically 5000 cps grade is used.

It should be noted that the term "briquette" includes objects commonly referred to as pellets, rods, pencils, briquettes and slugs. These objects share the common features of being a compacted form of material and are differentiated principally by their size and shape.

The particulate material is typically of a diameter of 4 mm or less. Typically at least 10% by weight of particulate material is capable of passing through a 100 µm sieve prior to forming into a briquette. The presence of the smaller particles of the particulate material improves the packing of the material.

Alkali metal alkyl siliconates are generally known in the art as waterproofing agents, rather than the materials that impart some structural or binding capability. However, a further benefit of using such siliconates is that they impart some waterproofing property to the briquette and import some resilience to the presence of moisture.

Typically the briquette comprises < 15%, < 10% or < 5% by weight of water.

Water content may be reduced by drying as, for example, adding burnt lime (calcium oxide) at up to typically 3%.

The applicant has found that the strength and resilience of the briquette, can be further improved by addition of a suitable cross-linking agent. Suitable cross-linking agents include, for example, glutaraldehydes, for example at 0.01 to 5% w/w.. Sodium hydroxide, for example 0.1% weight/weight, may also be used as a cross-linking agent. Other cross-linkers for PVA include glyoxal, glyoxal resin, PAAE resin (polyamidoamine epichlorohydrine), melamine formaldehydes, organic titanates (e.g. Tizor^™, Du Pont), boric acid, ammonium, zirconium carbonate and glutaric dialdehyde-bis-sodium bisulphate. Typically up to 5% and more typically 3% or 2% by weight of the cross-linking agent is used. This allows, for example, the amount of PVA to be reduced from, for example, 0.8% by weight or 0.5% by weight to, for example, 0.3% by weight or 0.4% by weight PVA. This is a cost effective way of improving the strength of the material.

The water resistance of the briquette may be further improved by, for example, providing a waterproofing agent, such as a layer of waterproofing agent. Waterproofing agent is typically sprayed onto the outer surface of the briquette after the briquette has been formed. Typically waterproofing agents include styrene-acrylate copolymers such as Vinnapas^™ SAF 34 (Wacker Chemie AG, Munich, Germany) which is typically a fine particles dispersion of a styrene acrylate copolymer, typically free from alkyl phenol ethoxylate, optionally this may contain 0.05 to 1% guar gum.

Alternatively the briquettes may be coated by spraying with a layer of bituminous emulsion.

An alternative to spraying of the briquettes with the materials includes, for example, dipping the briquettes in a solution or dispersion of the waterproofing material, or combining the waterproofing material with the particulate material and the binder.

A wetting agent or surfactant, such as a soap solution may be used to assist the wetting of the particulate material. This may be included at up to 1% by weight or 0.5% or 0.1% by weight. The binders crosslinking agent and waterproofing agents may be provided as aqueous solutions prior to use with the particulate material.

Typically, the briquettes comprise the binder, and optionally the cross-linking agent and/or the waterproofing agent where used, the remaining material being the particulate material and any moisture present in the material. Typically at least 70%, at least 80%, at least 90% or at least 95% of the briquette is particulate material as defined above.

The invention also provides a method of producing a briquette according to the invention comprising

1. (i) mixing the particulate material with binders as defined above;
2. (ii) compressing the mixture to form a briquette; and
3. (iii) curing the briquette.

Compressing may, for example, be the use of a mould or alternative, for example, by roller-pressing or extruding the material.

The use of a vacuum may optionally be used to improve the uptake of the binder into the particulate material; however, it has been found by the applicant that this is not typically necessary.

A surfactant may be used to aid in wetting the particulate material.

Once the briquette has been formed it may be sprayed with a further waterproofing agent, for example, as defined above, or dipped in the waterproofing agent.

The briquette may then be allowed to cure, for example, for 12, 24 or 48 hours.

Typically the process is carried out at ambient temperatures, for example, 20 to 40°C, 0 to 30°C, 15 to 25°C or 20°C.

The inventors have also found that metal ores, may be made into briquettes using a mixture of fully hydrolysed PVA, partially hydrolysed PVA and a cross linker.

Examples

The invention will now be defined by way of example only, with reference to the following examples and comparative examples:

The Addition of Waterproofing Agent to Coal Dust (comparative)

Sasol coal dust of between 0 and 4 mm diameter particulate size with a 5% moisture content was tested with 0.5% PVA (e.g. Mowiol 47-88) in combination with a number of waterproofing additives. These were Goldcrest, Wacker DP 15, Silres 16 and Wacker DN 3109.

Briquettes of 30 mm size were produced by compressing.

Additionally, a bituminous emulsion was utilised with products. These were originally sprayed on to the briquettes, but it was later found that Silres could be mixed with the PVA and particulate material.

Briquettes that are sprayed with individual additives were allowed to cure for 28 hours and then immersed for 8 hours in water, removed and tested by a drop test.

The best of the waterproofing materials were bituminous emulsion and Wacker SAF 34. The latter is a styrene-acrylate copolymer.

Drop tests were dropped from 2 metres on to a concrete surface and had to survive a minimum of two drops in order to pass the test.

The Combination of Ferrous Fines and PVA and the Silres (comparative)

Samples of ferrous fines, one sourced from the United States and one from South Africa, were tested. The US source was sized at 0-4 mm diameter and the South African source was graded as 0-2 mm, with moisture content at 0.5%. Fines were mixed with PVA 0.5% or less Mowiol 47-88 and Silres BS 16 0.02% in a laboratory Hobart mixer and then briquetted in a pressure briquetting plant.

The material from the United States was subjected to 8-10 tonne pressure produced specimens of approximately 180 gm which appear to be satisfactory. These were in a 40 mm die. The ex. South African material had 3.5% of burnt lime added and mixed vigorously. This survived a satisfactory drop test of 2 metres.

In further tests, the South African ferrous ore was used to study other aspects of the invention.

Trial 1

100 gm of ferrous ore (0.2 mm diameter) was accurately weighed into a mixing bowl. Surfactant was added (a couple of drops of soap solution). This was blended for one minute. A blended binder was prepared, comprising a 10% of 0.5% PVA solution (Mowiol 47-88 with 0.2% weight for weight Silres BS 16). 0.5% by weight of the solution was added to the ferrous ore and mixed for one minute. This was then compacted in a hydraulic press at 8 tonne using a 20 mm die and extruded. Specimens cured for 24 hours were found not to be completely cured with the centre of the specimen not fully cured. After 48 hours the specimen appeared sound

Trial 2

The above experiment was repeated using 0.6% final weight of PVA and hydraulic pressed to 7-8 tonnes with a 20 mm die. After 24 hours the specimen appeared to have been totally cured.

Trial 3

100 gm of ferrous ore was mixed accurately into a bowl. Surfactant was added and mixed for one minute.

A blend of PVA 47-88 was mixed with Silres 16, but 5% of the 10% solution was added and mixed for one minute. This was extruded using a die press of 8 tonne with a 20 mm die. This showed an improvement over trials 1 and 2. This was burned and tested up to 1100°C and proved to be satisfactory.

Trial 4

To above mixed material, the PVA binder was increased to 0.65% and mixed for one minute and extruded at 8 tonnes using a 20 mm die. Examination after extrusion showed the specimen was much stronger and gave a satisfactory solid sound effect. A burn test was satisfactorily completed.

Test 5

0.2 mm iron fines with a moisture content of 3.6% were also found to be successfully bound together using 0.4% PVA 0.02%. This material was successfully extruded using a 12 mm die and then cut into 12 mm lengths. Curing for 48 hours was found to improve the green strength of the material. It is noted that it is possible to reduce the total binder content to 0.35% or alternatively use a higher polymer solution such as 12.5% to reduce the amount of liquid present.

Waterproofing Test using Anthracite Coal from South Africa (comparative)

Powdered anthracite coal (0-4mm) was mixed with a surfactant (0.01% w/w soap solution), sodium hydroxide 0.02% (w/w).

0.2% Silres BS 16 was mixed with the coal. The mixture was then hydraulically pressed using a 20 mm die to form briquettes.

With the absence of PVOH, the briquettes appear to be too dry and appear to lack mechanical strength. The addition of PVOH at 5% weight for weight produced a briquette which appeared to be sound and passed a 2 metre drop test.

This was repeated for Silres plus PVA plus glutaraldehyde as a cross-linker 0.02% (w/w). This was observed to improve the strength of the material.

Bitumen emulsion sprayed onto the briquette was observed to improve the waterproofing of the material.

Coal and Ferrous Oxide (comparative)

The addition of up to 15% of particulate ferrous oxide containing material to coal, in combination with 0.5% PVOH and 0.2% Silres was found to improve the strength of the briquettes as tested by drop testing.

The use of fully and partially saponified PVA with cross linker (comparative) Test 1 Material:

• Ferromanganese silicate slag- brittle with a significant metallic content. Lab processed to -4mm size and minimum 20% passing 0.063mm
• Source- Kazakhstan

Blend:

• Ferromanganese Silicate slag
• 0.25% w/w of fully saponified polyvinyl alcohol in a 10%solution
• 0.25% w/w of partially saponified polyvinyl alcohol in a 10%solution
• Glutaraldehyde crosslinker 0.02% w/w
• 1% w/w water
• Mix was pressed 9 tonnes, 30mm diameter

Satisfactory specimens produced in respect of cold cure strength.

Specimens were placed in a muffle furnace at normal atmosphere up to 1100c for 2 hours. Specimens were very hard when cooled.

Effect of crosslinkers on PVA Test 1 Material to be agglomerated:

Un-beneficated iron ore (haematite) quarry fines - 4mm size. Contains silica and other minerals. Source- India

Blend: Quarry Fines

• 0.5% w/w of partially saponified polyvinyl alcohol in a 10% solution.
• Glutaraldehyde crosslinker 0.02% w/w
• 3% w/w water
• Mix was pressed 9 tonnes, 30mm diameter

Satisfactory specimens produced in respect of cold cure strength. End user testing showed retained strength after heating in a reducing atmosphere to 600 and 950c was marginal.

Test 2 Material to be agglomerated:

Un-beneficated iron ore (haematite) quarry fines -4mm size. Contains silica and other minerals. Source - India

Blend:

• 100% Quarry Fines
• 0.455% of polyvinyl alcohol in a 12.5%solution
• Sodium Hydroxide xlinker@0.02%
• 3% water
• Mix was pressed 9tonnes, 30mm diameter

Satisfactory specimens produced in respect of cold cure strength. Retained strength after heating in a reducing atmosphere to 600 and 950c was satisfactory:

Test results

Test 3

Test 2 was successfully up-scaled on a briquetting plant, 45mm pillow briquettes demonstrated the same properties as the lab specimens

Agglomeration of fine mineral wastes using polysaccharide binder (comparative) Test 1 Material to be agglomerated:

• Very fine (+40% -0.063mm) dust, dry condition, arc furnace fines (EAF)
• Source: South Africa COREX

Blend: EAF

• 0.5% w/w of polyvinyl alcohol in a 10% solution
• Crosslinker glutaraldehyde 0.02% w/w
• 3% water

This binder was found to be incompatible with the dust, the PVOH dropped out of solution, due to alkalinity and/or trace elements such as boron in the EAF dust. Agglomeration not possible

Test 2 Material to be agglomerated:

• Very fine (+40% -0.063mm) dust, dry condition.
• Source: South Africa COREX

Blend:

• 100% EAF dust (SA)
• 0.6% of organic, anionic polysaccharide binder
• 0.02% of glutaraldehyde
• 2% added water
• Mix for 30s, press 10 tonnes on 30x30mm specimens.

The mix achieved satisfactory specimens which achieved the following properties:

• Heat to 950c in air 1hour: retained strength, pass 2x 2m drop test
• Heat to 950c in a reduced atmosphere 2 hours - as above.

Heat from 600-1100c in a reducing atmosphere - 8 hours. Very hard specimens in region of 2.5MpA compressive strength.

Test 3 Material to be agglomerated:

Iron-bearing fine dust from wet collectors on a direct reduced iron plant "DRI sludge"

Blend

• DRI Sludge 100%
• 0.5% of anionic polysaccharide in 10% solution
• 0.02% of glutaraldehyde
• 3% added water
• 30mm specimens visually Satisfactory (10t load).Failed drop test.

Binder increased to 7% - drop test satisfactory - cracking started on 3^rd drop.

Temperature test in a reducing atmosphere at 1000c- satisfactory

Test 4 Material: fines from iron oxide pellet feed to direct reduction plant

• 100% oxide
• 0.6% of anionic polysaccharide 10%solution
• Glutaraldehyde @ 0.02%
• 3% water
• Unsatisfactory - fail drop test

Test 5 Material: fines from iron oxide pellet feed to direct reduction plant

• 100% oxide
• 0.6% of anionic polysaccharide 10%solution
• 0.3% of A in 10% solution
• Glutaraldehyde @ 0.02%
• 3% water
• Unsatisfactory - fail drop test

Further test results are as follows:

Results of pellets post- reaction in DRI plant without coating material:

Sample No	1	3	10
ccs kN	1.16	3.6	1.74
% Total Fe	86.3	86.6	87.1
% Metallisation	94.2	90.3	93.9

Iron Ore Fines

Iron ore fines were agglomerated with binder using a twin-shaft batching mixer at a minimum speed of 45 rpm. A roller press was used to form the briquettes.

Mixture 1 (comparative)

4.0% of an aqueous phenol formaldehyde resin of the RESOL type and 30-40% solids was added to mined iron ore fines with grading of 0-4mm. This was mixed and cylinder briquettes were produced at a pressure of 8tonnes.

Mixture 2

A phenol formaldehyde resin of a resol type in a methanol carrier and having a sold content of 30-50% was emulsified as follows: 500ml of a 30% solution of PVOH grade 4/80 was stirred at 450rpm. 500ml of the resin was added slowly. Then 2ml of a 10% solution of PVOH was added. The emulsion was verified by microscopy and remained stable for over 5 days @25C.

The emulsion was diluted with water at 4:1 and 5% was mixed into mined iron ore fines. This was mixed and cylinder briquettes were produced at a pressure of 8tonnes.

Mixture 3 (comparative)

A Phenol formaldehyde resin of RESOL type in powder form was blended with guar gum powder of grade 5000cps. The ratio was 30parts resin to 1 part gum. An aqueous solution was produced at by adding 300g to 1 Litre of water whilst stirring. 5% was mixed into mined iron ore fines .This was mixed and cylinder briquettes were produced at a pressure of 8 tonnes.

Mixture 4 (comparative)

A 1% solution of guar gum powder of grade 5000cps was produced. To this, 30% of A Phenol formaldehyde resin of RESOL type in powder form was added, whilst stirring. 5% was mixed into mined iron ore fines. This was mixed and cylinder briquettes were produced at a pressure of 8 tonnes.

Equipment for Reduction-disintegration testing

Briquettes were placed on ceramic plinths in the centre of the heating zone and subjected to the gas flow. A maximum of 4 briquettes at a time could be tested (100-150g).

A tumbler drum, of the specification ISO 4696-2 was loaned from BSL for the tests. Variable speed twin rollers were used to roll the drum, calibrated to 30 RPM.

Test Procedure RDI test:

• Tube temperature 550+/-10 C
• Time in reduction zone 30mins
• Gas conditions 70% Nitrogen/30% Carbon Dioxide at approx. 300Litres/hour Time Cooling - 1 hour in ceramic box
• Tumbler- 300 revolutions at 30rpm / 900 revolutions at 30rpm

Results: Reduction Degradation Index

mix No	Result RDI	Result Strength	Comments
10	6.5 kN	good
14	5kN	good
63	6.5kN	Poor
12	7kN	good

Superfine iron residues for tailing ponds/wash systems (comparative) Analysis by XRF gave the following Fe contents (as Fe₂O₃):

• Sub 20 microns 55.7%
• 150-20 microns 89.2%

These were agglomerated by twin-shaft batching mixer and formed into briquettes as described above.

Specification

Briquettes should have a strength of 150kg/cm and withstand 30 Drops with max 10% loss

Summary of Work

32mm diameter cylinders were produced with different blend ratios and tested at the DTS laboratory, Stockton on Tees, UK

Binder was added as powders to a wet iron slurry, typically composed of the following:

Anionic Polyacrylamide	8 parts
Guar gum	1 part
Calcium oxide	3 parts

Mixing was by a high speed and high shear mixer

Results size less than 20 mic

Ref no	Added Moisture	Binder (wt %)	Strength kN	No. Drops, 2m
77/15a	12	BSL539→Phenol formaldehyde resole resin	4.1	3
77/15b	12	BSL200→Polyacrylamide (anionic)	nd	1
77/15c	12	BSL139→Phenol formaldehyde resin	0.7	0
80/15a	20	BSL203→ Polyacrylamide	nd	7
80/15b	20	BSL203→ Polyacrylamide	1.5	15
80/15c	15	BSL201→Polyacrylamide	2.2	15
80/15d	20	BSL201→ Polyacrylamide	3.3	30+
80/15e	20	BSLCSF→Inorganic cement and silica fumed blend	1.55	0
80/15f	20	BSL150→Sodium carboxylate solution	1.3	2

Particle size 150-20 microns

Ref no	Added Moisture	Binder (wt %)	Strength kN	No. Drops, 2m
78/15A	10	BSL539→Phenol formaldehyde resole resin	0.5	0
78/15B	10	BSL203→ Polyacrylamide	1.3	10
81/15	10	BSL203→ Polyacrylamide	1.5	8
82/15	15	BSL201→ Polyacrylamide	3.2	18
84/15	15	BSL201→ Polyacrylamide	3.9	+30 (20mm pellet)

80/15 d and 84/15 were upscaled to an extrusion pilot plant, number of drops +40.

Low grade coke (lignin based coke) (comparative)

A formulation for cold binding a low grade coke breeze which meets high temperature resistance, attrition resistance and cold handling strength

Agglomeration was carried out using a batching mixer of a minimum speed of 45 rpm.

• 35% wt of a 1% gum solution was added to the coke, the grade of gum preferred is 5000cps technical. This was used to fill at least some of the pores in the coke.
• To this was added 1% of Styrene acrylic emulsion and mixed to make the coke bind.
• 8% wt of rapid hardening cement was added to give strength and heat resistance to the briquette.
• Further treatment is required after the briquette process.
• A roller press was used so that the water/cement ratio is not affected on extrusion. Briquettes were left to cure for a few days, dependent on temperature. Ideally temperature was raised to 25 C, without too much handling of briquettes.

Further treatment

• A 1:4 solution of the styrene acrylic emulsion was prepared and the briquettes passed through the solution, e.g. by a dipping trough on a conveyor belt run. This adds around 1% raw chemical. This was allowed to dry. This adds resistance to abrasion and water resistance.

Test results on lab prepared samples

Test	Result
Density	-
Compressive strength	1.45kN
Water abs.	21%
Compressive str after Water	1.33kN
Hot compressive strength	0.62kN
Abrasion	90
Drop test	98.5

This shows that coke briquettes using poor quality coke can be produced which meet the necessary standards for use in, for example, furnaces.

Claims (18)

1. A briquette comprising:

   (i) a particulate metal ore; and

   (ii) a binder comprising partially saponified polyvinyl alcohol and 0.5 wt% to 1.5 wt% phenol formaldehyde resin.
2. A briquette according to claim 1, wherein the metal ore is iron-ore.
3. A briquette according to claim 1 or claim 2, wherein the resin is a resole phenol formaldehyde resin.
4. A briquette according to any preceding claim, wherein the binder comprises 0.1 to 0.2 wt% polyvinyl alcohol.
5. A briquette according to any preceding claim, wherein the binder comprises 0.05 wt% to 1 wt% guar gum.
6. A briquette according to any preceding claim, wherein the particulate material has a particle size of 4 mm diameter or less.
7. A briquette according to claim 6, wherein at least 10% by weight of the particulate material is capable of passing through a 100 µm sieve prior to forming into a briquette.
8. A briquette according to any preceding claim, additionally comprising a waterproofing agent, combined with the particulate material or as a layer on the external surface of the briquette.
9. A briquette according to any preceding claim, wherein the waterproofing agent comprises a styrene-acrylate copolymer or a bitumen emulsion.
10. A briquette according to any preceding claim, having a moisture content of <15% by weight.
11. A method for producing a briquette according to any preceding claim comprising:

    (i) mixing the particulate, with the binder;

    (ii) compressing the mixture to form a briquette; and

    (iii) curing the briquette.
12. A method according to claim 11, wherein mixing comprises twin-shaft batching mixers to agglomerate the mixture.
13. A method according to claim 11 or claim 12, wherein the compression comprises a roller press to form briquettes.
14. A method according to claims 11 to 13, wherein the particulate has a moisture content of <15% by weight.
15. A method according to claims 11 to 14, comprising the step of mixing a crosslinking agent with the particulate prior to curing.
16. A method according to claims 11 to 15, wherein the briquette is coated with a waterproofing agent.
17. A method according to claim 16, wherein the waterproofing agent is sprayed on to the briquette.
18. A method according to claims 16 or 17, wherein the waterproofing agent comprises a styrene-acrylate copolymer or a bitumen emulsion.