GB191211799A - A Method of Producing Volumetrically Permanent Artificial Stone Compounds. - Google Patents
A Method of Producing Volumetrically Permanent Artificial Stone Compounds.Info
- Publication number
- GB191211799A GB191211799A GB191211799DA GB191211799A GB 191211799 A GB191211799 A GB 191211799A GB 191211799D A GB191211799D A GB 191211799DA GB 191211799 A GB191211799 A GB 191211799A
- Authority
- GB
- United Kingdom
- Prior art keywords
- artificial stone
- dolomite
- volumetrically
- producing
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
11,799. Billwiller, J. May 17. Plastic compositions containing fibres:-Dolomite, calcined at a temperature at which the carbon dioxide is driven off onlv from the magnesium carbonate, that is at about 850‹ C., is mixed with a solution of waterglass to make a mortar for the manufacture of artificial stone. Should the calcined dolomite contain more than 5 per cent of caustic lime, this lime is hydrated by the addition of water. Small quantities of gypsum and clay may be added to the dolomite, and also fibrous materials such as sawdust, asbestos, or cork meal. The artificial stone is hardened by impregnating the surface with a solution of an alkaline phosphate.
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| GB191211799T | 1912-05-17 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| GB191211799A true GB191211799A (en) | 1913-01-23 |
Family
ID=32572140
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| GB191211799D Expired GB191211799A (en) | 1912-05-17 | 1912-05-17 | A Method of Producing Volumetrically Permanent Artificial Stone Compounds. |
Country Status (1)
| Country | Link |
|---|---|
| GB (1) | GB191211799A (en) |
Cited By (2)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| EP0467165A1 (en) * | 1990-07-06 | 1992-01-22 | Walhalla-Kalk Entwicklungs- und Vertriebsgesellschaft mbH | Solids suspensions stable against sedimentation and process for their preparation |
| EP2958856B1 (en) | 2013-02-19 | 2019-08-28 | S.A. Lhoist Recherche Et Developpement | Method for the dry slaking of calcium oxides and magnesium from calcomagnesian compounds |
-
1912
- 1912-05-17 GB GB191211799D patent/GB191211799A/en not_active Expired
Cited By (2)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| EP0467165A1 (en) * | 1990-07-06 | 1992-01-22 | Walhalla-Kalk Entwicklungs- und Vertriebsgesellschaft mbH | Solids suspensions stable against sedimentation and process for their preparation |
| EP2958856B1 (en) | 2013-02-19 | 2019-08-28 | S.A. Lhoist Recherche Et Developpement | Method for the dry slaking of calcium oxides and magnesium from calcomagnesian compounds |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| AP2001002159A0 (en) | Inorganic cementitous material. | |
| EA199800429A1 (en) | CAPABILITY-COMPOSITION AND USE | |
| KR101806161B1 (en) | Binder agent with high-calcium | |
| KR101324548B1 (en) | Cement composition using cement admixtures for enhancing compressive strength | |
| KR850003373A (en) | Manufacturing method of coal ash hardened body | |
| GB191211799A (en) | A Method of Producing Volumetrically Permanent Artificial Stone Compounds. | |
| KR101825463B1 (en) | Stabilization agents for improving soft ground using steel-making slag having passed through a sorting step and recycled resources | |
| JP2008247642A (en) | Inorganic composite cured product and method for producing the same | |
| KR102685350B1 (en) | Tetrapod Manufacturing Method using Carbon dioxide Capture | |
| KR20200047489A (en) | Room temperature curing non-cement composition for light weight block | |
| GB531469A (en) | Improvements in or relating to the manufacture of cellular masses suitable for building purposes | |
| US1782460A (en) | Method of manufacturing porous building materials | |
| GB2017076A (en) | Fiber reinforced composition | |
| KR102685341B1 (en) | Tetrapot composition using carbon dioxide collector material | |
| KR890001995B1 (en) | Manufacturing method of building materials using briquettes | |
| GB627532A (en) | Improvements in or relating to constructional materials | |
| KR20250095074A (en) | Mortar composition using steelmaking slag-based carbon dioxide capture material | |
| GB191416560A (en) | Process for the Production of an Improved Gypsum Cement. | |
| GB190611366A (en) | Cement for Brushes and the like. | |
| GB191417829A (en) | A Method for the Manufacture of Magnesian Cement. | |
| US366609A (en) | Composition of brick | |
| KR20250017859A (en) | Eco cement composition | |
| GB368742A (en) | Improvements in the manufacture and production of cellular building materials | |
| GB191309792A (en) | An Improved Composition for Covering Floors, Walls, and other Surfaces. | |
| GB220677A (en) | Improvements in or relating to the treatment of wood or similar bodies to be used as an aggregate with or as a re-inforcement for calcareous cement |