FR3071420A1 - METHOD OF RECYCLING THE GLUE FOR MAKING A MAROUFLAGE - Google Patents
METHOD OF RECYCLING THE GLUE FOR MAKING A MAROUFLAGE Download PDFInfo
- Publication number
- FR3071420A1 FR3071420A1 FR1758901A FR1758901A FR3071420A1 FR 3071420 A1 FR3071420 A1 FR 3071420A1 FR 1758901 A FR1758901 A FR 1758901A FR 1758901 A FR1758901 A FR 1758901A FR 3071420 A1 FR3071420 A1 FR 3071420A1
- Authority
- FR
- France
- Prior art keywords
- masking layer
- temporary masking
- temporary
- glue
- pieces
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Procédé de dépôt d'un revêtement de décor par aspersion sur une pièce dans lequel, préalablement au dépôt dudit revêtement de décor on dépose sous forme fluide une colle thermofusible et non réticulable sur des zones de la pièce à protéger au cours de l'aspersion, de manière à former une couche de masquage temporaire puis, après avoir aspergé le revêtement de décor sur la surface de la pièce et après le retour de la couche de masquage temporaire sous forme solide et manipulable, on enlève ladite couche de masquage temporaire pour obtenir des morceaux de couche de masquage. On broie les morceaux de couche de masquage temporaire pour former des broyats aptes à être réutilisés pour former une nouvelle couche de masquage temporaire.A process for depositing a decorative coating by spraying on a part in which, prior to the deposition of said decorative coating, a hot-melt and non-crosslinkable adhesive is deposited in fluid form on areas of the part to be protected during the spraying, so as to form a temporary masking layer and after having sprayed the decorative coating on the surface of the workpiece and after the return of the temporary masking layer in solid and manipulable form, said temporary masking layer is removed to obtain pieces of masking layer. The temporary masking layer pieces are ground to form shreds suitable for reuse to form a new temporary masking layer.
Description
[001] L’ invention concerne un procédé de recyclage des produits utilisés pour maroufler des zones spécifiques d’une pièce d’aspect dans le but de masquer ces zones lors de l’aspersion d’un revêtement de décoration tel qu’une peinture.The invention relates to a process for recycling the products used to smooth specific areas of an appearance part with the aim of masking these areas during the spraying of a decorative coating such as a paint.
[002] On entend ici par pièce d’aspect une pièce dont une face est visible de l’extérieur et qui nécessite un traitement particulier. Dans un véhicule automobile, sont considérées comme des pièces d’aspect, des éléments tels qu’un hayon arrière, un becquet avant, une porte latérale, un capot, etc.[002] Here, the term “appearance part” is understood to mean a part of which one face is visible from the outside and which requires special treatment. In a motor vehicle, are considered as appearance parts, elements such as a tailgate, a front spoiler, a side door, a hood, etc.
[003] Il arrive fréquemment que la pièce d’aspect présente une ou plusieurs zones à protéger qui doivent demeurer aussi propres que possible et rester dépourvues de produit aspergé. C’est le cas par exemple des zones de fixation permettant de fixer la pièce d’aspect à une autre pièce par collage, lorsque l’assemblage des deux pièces se fait après le dépôt du revêtement de décoration. La zone de fixation doit rester la plus propre possible avant le dépôt de la colle et ne doit pas recevoir de peinture. C’est aussi le cas des zones de la pièce d’aspect qui doivent rester dépourvues de peinture dans un motif de décoration.It frequently happens that the appearance part has one or more areas to be protected which must remain as clean as possible and remain devoid of sprayed product. This is the case, for example, of the fixing zones allowing the appearance part to be fixed to another part by gluing, when the assembly of the two parts is done after the decorative coating has been deposited. The fixing area must be kept as clean as possible before the adhesive is deposited and must not receive paint. This is also the case for the areas of the appearance room which must remain unpainted in a decoration pattern.
[004] Lors de l’étape du dépôt du revêtement de décor par pulvérisation, les fines gouttelettes de peinture peuvent se déposer sur la zone à protéger, et peuvent même se déposer sur l’autre face de la pièce d’aspect en formant un voile.During the step of depositing the decorative coating by spraying, the fine paint droplets can be deposited on the area to be protected, and can even be deposited on the other face of the appearance part, forming a sail.
[005] De manière connue et pour résoudre ce problème, avant de peindre la pièce d’aspect, on utilise des rubans adhésifs déposés manuellement par un opérateur. Pour réduire les coûts de cette opération et améliorer la qualité de la protection, il est également connu de déposer sur la zone à protéger une matière fluide formant une couche de masquage temporaire et autrement désigné marouflage. Après l’application et le séchage du revêtement, on enlève la couche de masquage temporaire.In known manner and to resolve this problem, before painting the appearance part, adhesive tapes are used that are manually deposited by an operator. To reduce the costs of this operation and improve the quality of the protection, it is also known to deposit on the area to be protected a fluid material forming a temporary masking layer and otherwise designated masking. After applying and drying the coating, remove the temporary masking layer.
[006] En règle générale, la couche de masquage temporaire est une colle thermofusible (« hot melt » en anglais) qui devient fluide sous l’action de la chaleur et qui peut donc s’appliquer facilement à l’état liquide. Une fois appliquée la colle se solidifie en refroidissant et adhère suffisamment sur la surface de la pièce sans laisser d’interstices par où pourrait pénétrer la peinture, tout en conservant une bonne résistance aux chocs et aux accrochages pouvant survenir pendant la manipulation des pièces au cours du processus de mise en peinture. Au cours de ce processus, la peinture peut recouvrir le marouflage, sans atteindre la zone de la pièce à protéger.Generally, the temporary masking layer is a hot melt adhesive which becomes fluid under the action of heat and which can therefore be easily applied in the liquid state. Once applied, the glue solidifies on cooling and adheres sufficiently to the surface of the part without leaving gaps through which the paint could penetrate, while retaining good resistance to impact and snagging which may occur during the handling of parts during of the painting process. During this process, the paint can cover the masking, without reaching the area of the part to be protected.
[007] Une fois refroidie, la colle peut s’enlever rapidement et facilement du fait de sa souplesse résiduelle et de sa bonne tenue à température ambiante, autorisant de ce fait à retirer le marouflage d’un seul tenant, sans que celui-ci ne se fragmente.Once cooled, the glue can be removed quickly and easily due to its residual flexibility and good resistance at room temperature, thereby allowing the masking to be removed in one piece, without it does not fragment.
[008] L’invention intéresse en particulier le cas dans lequel la colle thermofusible est non réticulable, c’est-à-dire que, en la chauffant à nouveau elle redevient fluide et peut facilement être réutilisée.The invention relates in particular to the case in which the hot-melt adhesive is non-crosslinkable, that is to say that, by heating it again it becomes fluid again and can easily be reused.
[009] Ces colles thermofusibles comprennent en général comme constituant de base des polymères thermoplastiques tels que le polyéthylène, le polypropylène, les polyoléfines et copolymères de ces polyoléfine, les polyamides, les polymères ou copolymères de type acétate de vinyle, ou des copolymères de type EVA auxquels sont rajoutés des additifs et des résines tackifiantes pour ajuster les caractéristiques de collage. A titre d’exemple, la colle polyamide thermofusible est sous forme liquide à partir d’une température de 110°C et redevient solide à une température inférieure à 90°C.These hot-melt adhesives generally comprise, as a basic constituent, thermoplastic polymers such as polyethylene, polypropylene, polyolefins and copolymers of these polyolefins, polyamides, polymers or copolymers of vinyl acetate type, or copolymers of type EVA to which additives and tackifying resins are added to adjust the bonding characteristics. For example, the hot-melt polyamide adhesive is in liquid form from a temperature of 110 ° C and becomes solid again at a temperature below 90 ° C.
[0010] Après avoir détaché le marouflage de la surface de la pièce, il est particulièrement intéressant de recycler la matière en portant, dans un fondoir les morceaux de colle à recycler à une température supérieure à sa température de fusion, de manière à remettre la colle dans un état liquide puis, en utilisant une extrudeuse munie d’une grille, ou d’une plaque à trou, on procède à un filtrage de la colle liquide pour enlever les particules de peinture présentes dans la colle afin de réajuster les propriétés physiques de la colle telles que la densité ou la fluidité. La grille ou la plaque à trou ont une maille de l’ordre de 0,1mm, permettant de retenir les particules dont la taille varie entre 10pm et 300pm.After having detached the masking from the surface of the part, it is particularly advantageous to recycle the material by carrying, in a melter, the pieces of glue to be recycled at a temperature higher than its melting temperature, so as to restore the glue in a liquid state then, using an extruder fitted with a grid, or a plate with a hole, a liquid glue is filtered to remove the paint particles present in the glue in order to readjust the physical properties glue such as density or fluidity. The grid or the plate with a hole has a mesh of the order of 0.1mm, making it possible to retain particles whose size varies between 10pm and 300pm.
[0011] La colle filtrée est refroidie de nouveau pour retrouver l’état solide. On procède alors à la réalisation de granulés de petites tailles, similaires à ceux d’une colle vierge. Puis, les granulés recyclés sont mélangés dans des proportions contrôlées avec les granulés de la colle vierge, et l’ensemble, une fois brassé pour obtenir une bonne homogénéité, est introduit dans le dispositif de marouflage.The filtered glue is cooled again to return to the solid state. We then proceed to the production of small granules, similar to those of a virgin glue. Then, the recycled granules are mixed in controlled proportions with the granules of virgin glue, and the whole, once stirred to obtain good homogeneity, is introduced into the masking device.
[0012] A l’expérience, cette méthode de recyclage présente toutefois quelques inconvénients. En effet, les granulés recyclés ont tendance à se déformer facilement et à se coller entre eux. Ce phénomène est aggravé en raison de l’absence d’agents antimotants enrobant les granulés, lesquels ont été mélangés à la matière lors du passage en phase liquide et ne sont plus présents en surface, comme cela est le cas des granulés de colle vierge. Il en résulte des colmatages des circuits d’alimentation du dispositif de marouflage et des pertes de productivité liées à la nécessité de faire intervenir un opérateur pour remédier à cette interruption de l’alimentation et à l’arrêt de production qui s’en suit.However, experience has shown that this recycling method has some drawbacks. Indeed, recycled granules tend to easily deform and stick to each other. This phenomenon is aggravated due to the absence of anti-motive agents coating the granules, which have been mixed with the material during the transition to the liquid phase and are no longer present on the surface, as is the case with virgin glue granules. This results in blockages in the supply circuits of the masking device and in productivity losses linked to the need to involve an operator to remedy this interruption in the supply and the subsequent production stoppage.
[0013] L’invention a pour objet d’apporter une solution au problème ci-dessus.The object of the invention is to provide a solution to the above problem.
[0014] Selon l’invention, le procédé de dépôt d’un revêtement de décor par aspersion sur une pièce prévoit que, préalablement au dépôt dudit revêtement de décor, on dépose une colle thermofusible non réticulable sous forme fluide sur des zones de la pièce à protéger au cours de l’aspersion de manière à former une couche de masquage temporaire. Puis, après avoir pulvérisé le revêtement de décor sur la surface de la pièce et après le retour de la couche de masquage temporaire sous forme solide et manipulable, on enlève ladite couche de masquage temporaire pour obtenir des morceaux de couche de masquage.According to the invention, the method of depositing a decorative coating by spraying on a part provides that, prior to the deposition of said decorative coating, a non-crosslinkable hot-melt adhesive is deposited in fluid form on areas of the part. to protect during spraying so as to form a temporary masking layer. Then, after having sprayed the decorative coating on the surface of the part and after the return of the temporary masking layer in solid and manipulable form, said temporary masking layer is removed to obtain pieces of masking layer.
[0015] Ce procédé se caractérise en ce qu’on broie les morceaux de couche de masquage temporaire pour former des broyats aptes à être recyclés pour former une nouvelle couche de masquage temporaire.This process is characterized in that the pieces of temporary masking layer are ground to form shredded material capable of being recycled to form a new temporary masking layer.
[0016] Ces broyats ont une taille similaire aux granulés de colle vierge.These shreds have a size similar to the granules of virgin glue.
[0017] A l’expérience il a été possible de constater que la présence de particules de revêtement de décor (i.e ; de peinture) dans la colle modifiait peu les caractéristiques recherchées pour son utilisation comme couche de masquage temporaire. En particulier, le pouvoir couvrant et l’adhésion de la colle sur la surface de la pièce restaient dans des limites tout à fait satisfaisantes. De même, la fluidité et l’aptitude de la colle à s’écouler dans une buse, lorsque la colle recyclée est sous forme liquide, lors du dépôt sur la surface de la pièce en particulier, évoluent lentement, et peuvent facilement être corrigées, en ajustant les proportions de broyats recyclés et de granulés vierges.Experience has shown that the presence of decorative coating particles (i.e. paint) in the glue did little to modify the characteristics sought for its use as a temporary masking layer. In particular, the covering power and the adhesion of the adhesive on the surface of the part remained within entirely satisfactory limits. Likewise, the fluidity and the ability of the glue to flow in a nozzle, when the recycled glue is in liquid form, when deposited on the surface of the part in particular, evolve slowly, and can easily be corrected, by adjusting the proportions of recycled crushed and virgin granules.
[0018] Ce procédé permet également de s’affranchir d’un nouveau passage de la colle dans un fondoir à haute température et d’éviter de chauffer la colle inutilement. Cela permet de plus de réduire la consommation d’énergie et de simplifier le processus de fabrication.This process also makes it possible to dispense with a new passage of the glue in a melter at high temperature and to avoid unnecessarily heating the glue. This further reduces energy consumption and simplifies the manufacturing process.
[0019] Le dispositif selon l'invention peut aussi comprendre isolément, ou en combinaison, les caractéristiques énoncées ci-après dans la description qui suit.The device according to the invention can also comprise, in isolation, or in combination, the characteristics set out below in the description which follows.
[0020] Afin de conserver une bonne homogénéité des broyats on peut également faire passer lesdits broyats sur un premier tamis pour retenir les broyats de trop grande taille.In order to maintain good homogeneity of the comminuted products, it is also possible to pass said comminuted products through a first sieve to retain the comminuted products which are too large.
[0021] Le premier tamis comporte une grille dont la maille est comprise entre 4mm et 5mm.The first sieve has a grid whose mesh is between 4mm and 5mm.
[0022] Il en résulte que les broyats ont une taille comprise entre 0,2 mm et 5 mm en moyenne, équivalente à la taille des granulés vierges.It follows that the comminuted products have a size between 0.2 mm and 5 mm on average, equivalent to the size of the virgin granules.
[0023] Il peut s’avérer également utile de faire passer les broyats sur un second tamis pour éliminer les particules fines et faciliter la mise en œuvre de la colle. En effet, après avoir terminé l’opération de broyage, les fines particules de peinture peuvent se détacher de la surface des broyats et faire évoluer les caractéristiques de la colle.It can also be useful to pass the ground material through a second screen to remove fine particles and facilitate the implementation of the glue. Indeed, after having finished the grinding operation, the fine particles of paint can detach from the surface of the ground material and cause the characteristics of the adhesive to change.
[0024] Ces particules présentent également l’inconvénient de se répandre dans l’atmosphère et de boucher les filtres à air utilisés sur les moyens de transfert ou d’alimentation par aspiration des granulés, tout en présentant de surcroît un danger pour les opérateurs.These particles also have the disadvantage of spreading in the atmosphere and clogging the air filters used on the means of transfer or feed by suction of the granules, while also presenting a danger for operators.
[0025] Le second tamis comporte une grille dont la maille est comprise entre 0,2mm et 0,5mm. Ce tamis peut utilement être un tamis vibrant de manière à favoriser le passage des matières.The second sieve has a grid whose mesh is between 0.2mm and 0.5mm. This screen can usefully be a vibrating screen so as to promote the passage of materials.
[0026] Pour favoriser l’écoulement de la colle pendant l’opération de marouflage on dépose ladite couche de masquage temporaire sous forme fluide à l’aide d’un pistolet muni d’une buse dont le diamètre est compris entre 1mm et 3mm.To promote the flow of the glue during the masking operation, said temporary masking layer is deposited in fluid form using a gun provided with a nozzle whose diameter is between 1mm and 3mm.
[0027] Ce pistolet est alimenté par un fondoir apte à délivrer la colle sous forme liquide et sous pression.This gun is fed by a melter capable of delivering the adhesive in liquid form and under pressure.
[0028] Il peut alors s’avérer utile de disposer des moyens de filtration, en aval du fondoir, pour éliminer les particules de peinture de taille importante. Ces moyens peuvent être formés par une cartouche filtrante ou une plaque à trou dont la maille ou dont le diamètre des trous est compris entre 0,1mm et 0,2mm.It can then be useful to have filtration means, downstream of the melter, to remove large paint particles. These means can be formed by a filter cartridge or a hole plate whose mesh or whose hole diameter is between 0.1mm and 0.2mm.
[0029] Les broyats peuvent alors être mélangés avec des granulés vierges selon des proportions prédéterminées pour former la colle utilisée lors du processus de réalisation de marouflage au cours de laquelle on forme la couche de masquage temporaire.The ground material can then be mixed with virgin granules in predetermined proportions to form the glue used during the process of production of masking during which the temporary masking layer is formed.
[0030] Ces proportions peuvent aller de 0% à 100% de la colle utilisée pour réaliser la couche de masquage temporaire.These proportions can range from 0% to 100% of the adhesive used to make the temporary masking layer.
[0031] Toutefois, on veillera à ce que la viscosité dynamique (μ) à 190°C des broyats reste dans des limites prédéfinies permettant la mise en œuvre industrielle de la colle. La mesure de la viscosité s’effectue de manière classique à l’aide d’un viscosimètre Brookfield, selon les standards ASTM.However, it will be ensured that the dynamic viscosity (μ) at 190 ° C. of the comminuted material remains within predefined limits allowing the industrial use of the glue. The viscosity measurement is carried out in a conventional manner using a Brookfield viscometer, according to ASTM standards.
[0032] Et, lorsque la viscosité des broyats augmente, en raison de l’augmentation de la concentration de particules fines de peinture, et dépasse les limites recommandées, il est possible de réintroduire des granulés vierges pour ramener la viscosité de la colle dans les valeurs limites énoncées ci-dessus. On ajuste alors la proportion de granulés vierge et de broyats de sorte que la viscosité dynamique (μ) à 190°C de la colle servant à former la couche de masquage temporaire reste comprise entre des limites prédéfinies.And, when the viscosity of the ground material increases, due to the increase in the concentration of fine paint particles, and exceeds the recommended limits, it is possible to reintroduce virgin granules to reduce the viscosity of the adhesive in the limit values stated above. The proportion of virgin granules and ground materials is then adjusted so that the dynamic viscosity (μ) at 190 ° C. of the adhesive used to form the temporary masking layer remains between predefined limits.
[0033] A titre d’exemple, pour une colle de type polyamide il convient que la viscosité dynamique (μ) reste comprise entre 1,5 Pa.s et 2,5 Pa.s. Le dépôt de la colle sous forme liquide, comprenant des broyats et des granulés vierges, s’effectue alors de manière connue à une température comprise entre 140°C et 220°C.For example, for a polyamide type adhesive, the dynamic viscosity (μ) should remain between 1.5 Pa.s and 2.5 Pa.s. The deposition of the adhesive in liquid form, comprising ground materials and virgin granules, is then carried out in a known manner at a temperature between 140 ° C and 220 ° C.
[0034] Lorsque la couche de masquage temporaire redevient solide et manipulable, il est alors possible d’enlever la couche de masquage temporaire en décollant le film formé par ladite couche. On entend ici par manipulable, le fait que la couche de masquage est à une température suffisamment basse pour redevenir solide mais reste encore suffisamment souple pour se détacher sans se rompre en formant des morceaux d’un seul tenant.When the temporary masking layer becomes solid and easy to handle, it is then possible to remove the temporary masking layer by peeling off the film formed by said layer. The term “manipulable” is understood here to mean that the masking layer is at a temperature low enough to become solid again but is still flexible enough to come off without breaking, forming pieces in one piece.
[0035] A titre d’exemple, pour une colle de type polyamide, cette opération peut intervenir dans les quinze minutes suivant le dépôt de la colle liquide.For example, for a polyamide type glue, this operation can take place within fifteen minutes of depositing the liquid glue.
[0036] Toutefois, pour que le procédé de broyage soit efficace il est préférable, après avoir enlevé la couche de marouflage, de laisser les morceaux de masquage temporaire revenir à la température ambiante pour qu’ils soient plus durs et plus cassants, de sorte que les morceaux puissent se rompre plus facilement pour former des broyats de petite taille. La température ambiante est assimilée à la température de l’atelier dans lequel on met en œuvre le procédé, et peut utilement être comprise entre 18°C et 35°C.However, for the grinding process to be effective, it is preferable, after removing the masking layer, to allow the temporary masking pieces to return to room temperature so that they are harder and more brittle, so that the pieces can break more easily to form small shreds. The ambient temperature is assimilated to the temperature of the workshop in which the process is implemented, and can usefully be between 18 ° C and 35 ° C.
[0037] Les alternatives de mise en œuvre de l’invention décrites ci-dessus n’ont aucun caractère limitatif et peuvent faire l’objet de variantes, sans se départir de l’objet de l’invention tel que revendiqué.The implementation alternatives of the invention described above are in no way limiting and may be subject to variants, without departing from the subject of the invention as claimed.
Claims (10)