FI69651B - TAPET OCH FOERFARANDE FOER TILLVERKNING AV TAPET - Google Patents
TAPET OCH FOERFARANDE FOER TILLVERKNING AV TAPET Download PDFInfo
- Publication number
- FI69651B FI69651B FI842025A FI842025A FI69651B FI 69651 B FI69651 B FI 69651B FI 842025 A FI842025 A FI 842025A FI 842025 A FI842025 A FI 842025A FI 69651 B FI69651 B FI 69651B
- Authority
- FI
- Finland
- Prior art keywords
- wallpaper
- aluminum
- divalent
- latex
- chloride
- Prior art date
Description
6965169651
Tapetti ja tapetin valmistusmenetelmä - Tapet och förfarande för tillverkning av tapet Tämä keksintö kohdistuu tapettiin, jossa on tapettiraakapaperi-kerros ja sen päällä lateksia ja pigmenttejä sisältävä pigment-tipäällystekerros tapetin painomenetelmiä kuten liima-, silkki-, flekso- ja syväpainomenetelmiä varten.This invention relates to a wallpaper having a wallpaper raw paper layer and a Pigment drip coating layer containing latex and pigments thereon for wallpaper printing methods such as glue, silk, flexographic and gravure printing.
5 Tällaisen tapetin tulee olla riittävän pesunkestävää. Pesunkes-tävyyden toteamisessa käytetään esim. Timberley WPM-kojetta, ja menetelmää B, jossa hankaavana pintana on huopa ja väliaineena kaksiprosenttinen alkalinen saippualiuos. Kohtuullisena vaatimuksena pidetään, että tapettinäytteen tulee kestää kolmekym-10 mentä vetoa ilman, että pinta vioittuu.5 Such wallpaper should be sufficiently washable. For example, a Timberley WPM instrument is used to determine washability, and method B, in which the abrasive surface is a felt and the medium is a 2% alkaline soap solution. It is considered a reasonable requirement that the wallpaper sample should withstand thirty to 10 strokes without damaging the surface.
Pesunkestävyyttä voidaan lisätä lateksin määrää lisäämällä.Washing resistance can be increased by increasing the amount of latex.
Tässä hakemuksessa lateksilla tarkoitetaan tapettipäällysteissä yleensä käytettyjä ns. homo- tai kopolymeerilatekseja, esim. polyvinyyliasetaattihomopolymeeri-, polyvinyyliasetaatti-akry-15 laattikopolymeeri-, etyleeni-vinyyliasetaattikopolymeeri-, styreeni-akrylaattikopolymeeri-, täysakrylaatti- ja styreeni-butadieenilatekseja.In this application, latex refers to the so-called "latex" commonly used in wallpaper coatings. homo- or copolymer latexes, e.g. polyvinyl acetate homopolymer, polyvinyl acetate-acrylate copolymer, ethylene-vinyl acetate copolymer, styrene-acrylate copolymer, full acrylate and styrene-butadiene latex.
Tähänastisessa käytännössä on todettu, että lisäämällä pigment-tipäällystekerrokseen lateksia yli kaksikymmentäviisi painopro-20 senttiä pigmenttien määrästä saavutetaan riittävä tapetin pe-sunkestävyys.In practice to date, it has been found that the addition of latex to the Pigment Coating Layer in excess of twenty-five weight percent of the amount of pigments achieves sufficient wallpaper resistance of the wallpaper.
Lateksin lisääminen kohottaa kuitenkin tapetin valmistuskustannuksia, koska lateksi on kallista.However, the addition of latex increases the cost of making the wallpaper because latex is expensive.
Vielä on todettu, että korkeita lateksipitoisuuksia käytettäes-25 sä ei tapetin painomenetelmillä yleensä saavuteta hyvää viiva-terävyyttä eikä tasaista kompaktipintaa, koska painoväri pyrkii helmeilemään, mikä taas johtuu korkean lateksimäärän aiheuttamasta pigmenttipäällystekerroksen imukyvyn huonontumisesta.It has also been found that when using high latex contents, wallpaper printing methods generally do not achieve good line sharpness or a smooth compact surface because the ink tends to bead, which in turn is due to the deterioration of the absorbency of the pigment coating layer caused by the high latex content.
o 69651o 69651
Koska lateksilla on huono opasiteetti, on lateksipitoisuuden ollessa suuri sen vastapainona käytettävä paljon sellaisia pigmenttejä, kuten esim. titaanioksidia, jolla on hyvä opasiteetti. Tällainen pigmentti on kuitenkin kallista.Because latex has poor opacity, when the latex content is high, a lot of pigments such as titanium oxide, which has good opacity, must be used to counterbalance it. However, such a pigment is expensive.
5 Edellä mainittujen haittojen poistamiseksi tämän keksinnön tarkoituksena on tapetin pesunkestävyyden lisääminen jollakin muulla tavalla, kuin lateksia lisäämällä, jolloin lateksin osuutta pigmenttipäällystekerroksessa voitaisiin vähentää. Keksinnön mukaan tämä tavoite saavutetaan siten, että pesunkestä-10 vyyden lisäämiseksi ja lateksin kulutuksen vähentämiseksi pigment tipäällystekerroksen päälle on levitetty kaksi- tai useam-piarvoisten metallien, esim. titaanin, alumiinin, kalsiumin tai magnesiumin epäorgaanisten suolojen vesiliuosta.In order to overcome the above-mentioned disadvantages, the object of the present invention is to increase the washing resistance of the wallpaper in a way other than by adding latex, whereby the proportion of latex in the pigment coating layer could be reduced. According to the invention, this object is achieved by applying an aqueous solution of inorganic salts of divalent or polyvalent metals, e.g. titanium, aluminum, calcium or magnesium, on the Pigment drip coating layer in order to increase the washing resistance and reduce the consumption of latex.
Keksintö perustuu siihen yllättävään havaintoon, että kun ta-15 pettiraakapaperikerroksen päällä olevan, lateksia ja pigmenttejä sisältävän pigmenttipäällystekerroksen, joka on tarkoitettu tapetin painomenetelmiä varten, päälle on ennen painatusta levitetty kaksi- tai useampiarvoisten metallien epäorgaanisten suolojen vesiliuosta, niin tapetin pesunkestävyys huomattavasti 20 lisääntyy, minkä johdosta lateksin osuutta pigmenttipäällyste-kerroksessa voidaan vähentää jopa alle 10 prosenttiin pigmenttien määrästä tapetin pesunkestävyyden silti säilyessä riittävänä. Lateksin osuuden pienentyessä tapetin valmistuskustannukset oleellisesti alenevat, koska lisätyn liuoksen kustannus on 25 huomattavasti pienempi, kuin poisjäävän lateksin ja hyväopasi-teettisen pigmentin kustannus ja sen painettavuusominaisuudet paranevat, niin kuin ylempänä on selitetty.The invention is based on the surprising finding that when an aqueous solution of divalent or more inorganic salts of divalent metals is applied to a layer of pigment coating layer containing latex and pigments for wallpaper printing methods on top of a tufted raw paper layer. as a result, the proportion of latex in the pigment coating layer can be reduced to less than 10% of the amount of pigments while still maintaining the washability of the wallpaper. As the proportion of latex decreases, the cost of manufacturing the wallpaper is substantially reduced because the cost of the added solution is significantly lower than the cost of the latex and the well-opaque pigment and its printability properties are improved, as described above.
Keksinnön erään edullisen toteutusmuodon mukaan kaksi- tai useampiarvoisen metallin suola on alumiinisulfaatti AI2(SO^)3* 30 X H Q 0 , jossa X on 14-18.According to a preferred embodiment of the invention, the salt of the divalent or polyvalent metal is aluminum sulphate Al 2 (SO 2) 3 * 30 X H Q 0, where X is 14-18.
Erään toisen edullisen toteutusmuodon mukaan kaksi- tai useampiarvoisen metallin suola on titaanikloridi, zirkoniumsulfaat-ti, alumiinikloridi, a1umiininitraatti, sinkkikloridi, sinkki-sulfaatti tai bariumkloridi.According to another preferred embodiment, the salt of the divalent or polyvalent metal is titanium chloride, zirconium sulphate, aluminum chloride, aluminum nitrate, zinc chloride, zinc sulphate or barium chloride.
3 696513 69651
Keksintö kohdistuu myöskin tapetin valmistusmenetelmään, jossa tapettiraakapaperikerros päällystetään lateksia ja pigmenttejä sisältävällä pigmenttipäällystekerroksella tapetin painomenetelmiä, kuten liima-, silkki-, flekso- ja syväpainomenetelmiä 5 varten.The invention also relates to a method of making a wallpaper, in which a raw paper layer of wallpaper is coated with a pigment coating layer containing latex and pigments for wallpaper printing methods such as glue, silk, flexo and gravure printing methods.
Keksinnön mukaiselle menetelmälle on tunnusomaista, että pig-menttipäällystekerroksen päälle pesunkestävyyden lisäämiseksi ja lateksin kulutuksen vähentämiseksi levitetään yhden tai useamman kaksi- tai useampiarvoisen metallin, esim. titaanin, 10 alumiinin, kalsiumin tai magnesiumin epäorgaanisen suolan vesi-liuosta .The process according to the invention is characterized in that an aqueous solution of one or more divalent metals, e.g. titanium, aluminum, calcium or magnesium, inorganic salt is applied to the pigment coating layer in order to increase the washing resistance and reduce the consumption of latex.
Lisäksi voivat tulla kysymykseen niinsanotut kaksoissuolat, joissa kaksi- tai useampiarvoisen metallin suola voi esiintyä yhdenarvoisen metallin suolan kanssa. Tällaisia kaksoissuoloja 15 ovat esim. kalialuna eli kaliniitti, cesiumaluna ja natriumalu-na .In addition, so-called double salts can be used, in which a divalent or polyvalent metal salt can be present together with a monovalent metal salt. Such double salts 15 are, for example, potassium alum, i.e. kalinite, cesium alum and sodium alum.
Levitys voidaan suorittaa esim. teloilla, joita voidaan käyttää erilaisilla paperinvalmistustekniikassa tunnetuilla tavoilla, tai sumuttamalla, jolloin nesteen levityksessä käytetään ilmaa, 20 tai ruiskuttamalla. Myös impregnointia eli upotusmenetelmää voidaan käyttää.The application can be carried out, for example, by rollers, which can be used in various ways known in papermaking technology, or by spraying, in which case air is used in the application of the liquid, or by spraying. Impregnation, i.e. the immersion method, can also be used.
Ennen suolaliuoksen levittämistä pigmenttipäällystekerros kuivataan vähintään kosketuskuivaksi.Prior to application of the saline solution, the pigment coating layer is dried to at least touch dry.
Erään edullisen suoritusmuodon mukaan pigmenttipäällystekerros 25 suolaliuoksen levittämisen jälkeen kuivataan painopaperikosteu-teen.According to a preferred embodiment, the pigment coating layer 25 is applied to the printing paper moisture after application of the brine.
Keksinnön erään edullisen toteutusmuodon mukaan menetelmässä kaksi- tai useampiarvoisen metallin suolana käytetään alumiini-sulfaattia Alg(SO ) ·XH 0, jossa X on 14-18.According to a preferred embodiment of the invention, aluminum sulphate Alg (SO) · XH 0, wherein X is 14-18, is used as the divalent or polyvalent metal salt in the process.
69651 k69651 k
Erään toisen keksinnön mukaisen edullisen suoritusmuodon mukaan menetelmässä kaksi- tai useampiarvoisen metallin suolana käytetään titaanikloridia, zirkoniumsulfaattia, alumiinikloridia, alumiininitraattia, sinkkikloridia, sinkkisulfaattia tai ba-5 riumkloridia.According to another preferred embodiment of the invention, titanium chloride, zirconium sulphate, aluminum chloride, aluminum nitrate, zinc chloride, zinc sulphate or barium chloride are used as the divalent or polyvalent metal salt in the process.
Edelleen keksinnön erään edullisen toteutusmuodon mukaan suolan vesiliuoksen väkevyys on 0,5-10 painoprosenttia.According to a further preferred embodiment of the invention, the concentration of the aqueous salt solution is 0.5 to 10% by weight.
Vielä keksinnön erään edullisen toteutusmuodon mukaan suolan vesiliuoksen väkevyys on noin 5 painoprosenttia.According to another preferred embodiment of the invention, the concentration of the aqueous salt solution is about 5% by weight.
10 Seuraavassa keksintöä valaistaan käytännön esimerkillä: ESIMERKKI 1In the following, the invention is illustrated by a practical example: EXAMPLE 1
Lateksipitoisuuden ja 5% alumiinisulfaattiliuoksella suoritetun jälkikäsittelyn vaikutus pesunkestävyyteenEffect of latex content and after-treatment with 5% aluminum sulphate solution on washing resistance
Pigmenttipäällystekerrosa pigment coating
Lateksi 25.0 15.0 10.0Latex 25.0 15.0 10.0
Pigmenti tPigments t
Titaanioksidi 23.0 16.0 12-0 muut pigmentit 77.0 84.0 88.0Titanium oxide 23.0 16.0 12-0 other pigments 77.0 84.0 88.0
Paksunnosaine CMC 0.3 0.6 1-0Thickener CMC 0.3 0.6 1-0
Pesunkestävyys ei jälkikäsitelty 40 (C) 20 (B) 5 (A) (kestää hankauksia) ------—------Washing resistance not post-treated 40 (C) 20 (B) 5 (A) (abrasion resistant) ------—------
Timberley jälkikäsitelty 150 (D) 100 (D) 40 (OTimberley post - treated 150 (D) 100 (D) 40 (O
IIII
5 69651 ESIMERKKI 25 69651 EXAMPLE 2
Lateksipitoisuuden ja 5% alunaliuoksella K„SO AI (SO ) 2 4 2 4 3 24H^0 suoritetun jälkikäsittelyn vaikutus pesunkestävyyteen PigmenttipäällystekerrosEffect of latex content and post-treatment with 5% alum solution K „SO Al (SO) 2 4 2 4 3 24H ^ 0 on washing resistance Pigment coating layer
Lateksi 25.0 15.0 10.0Latex 25.0 15.0 10.0
Pigmentit 100.0 100.0 100.0Pigments 100.0 100.0 100.0
Paksunnosaine CMC 1.2 1.2 1.2Thickener CMC 1.2 1.2 1.2
Pesunkestävyys ei jälkikäsitelty 40 (C) 25 (B) 15 (A) (kestää hankauk- -—---- siä) Timberley jälkikäsitelty 130 (D) 100 (D) 50 (C) A = pesunkestävyys aivan kehno B = " riittämätön C = " riittävä D = " turhan hyvä (pinta liian suljettu)Washing resistance not post-treated 40 (C) 25 (B) 15 (A) (abrasion-resistant) Timberley post-treated 130 (D) 100 (D) 50 (C) A = washing resistance quite poor B = "insufficient C = "sufficient D =" unnecessarily good (surface too closed)
Pigmenttipäällystekerroksen aineosuudet on laskettu kuivapaino-prosentteina pigmenttien määrästä.The constituents of the pigment coating layer are calculated as a dry weight percentage of the amount of pigments.
Pigmenttipäällystekerroksessa esiintyvän paksunnosaineen tarkoituksena on parantaa pigmenttipäällystekerroksen tasoittu-5 vuutta. Paksunnosaineena käytetään nykyään tavallisimmin vesiliukoista CMC-ainetta, eli karboksimetyy1ise1luloosaa. Tämän aineen ominaisuuksiin kuuluu vielä, että se pyrkii huonontamaan tapetin pesunkesto-ominaisuuksia.The purpose of the thickener present in the pigment coating layer is to improve the smoothness of the pigment coating layer. Today, the most commonly used thickener is a water-soluble CMC substance, i.e. carboxymethylcellulose. Another property of this material is that it tends to degrade the washing resistance properties of the wallpaper.
Esimerkissä 1 on käytetty 5¾ alumiinisulfaattiliuosta ja esi-10 merkissä 2 5% alunaliuosta. Laboratoriokokeissa on todettu,että 69651 6 jo 0,5% väkevyydellä keksinnön mukainen vaikutus alkaa näkyä.Example 1 uses a 5¾ aluminum sulfate solution and Example 10 a 5% alum solution. It has been found in laboratory experiments that at 69651 6 already at a concentration of 0.5% the effect according to the invention begins to show.
Jo 2% väkevyydellä vaikutus on selvästi havaittavissa. Vaikutuksen optimi eri tekijät huomioonottaen saavutetaan noin 5% liuoksella. Jos väkevyyttä siitä lisätään, vaikutus lateksin 5 määrään kasvaa hitaasti. Yli 10% väkevyydellä alkaa ilmetä haittavaikutuksia, esim. käsitellystä pinnasta tulee kirjava.Even at a concentration of 2%, the effect is clearly noticeable. The optimum effect, taking into account various factors, is achieved with a solution of about 5%. If the concentration of it is increased, the effect on the amount of latex 5 increases slowly. At concentrations above 10%, adverse effects begin to occur, e.g., the treated surface becomes mottled.
Esimerkkitaulukoista havaitaan, että keksinnön mukaista menetelmää käyttämällä lateksin osuus pigmenttipäällystekerroksessa on voitu alentaa 25%:sta 10%:iin tapetin pesunkesto-ominaisuuk-10 sien säilyessä silti riittävän hyvinä. Titaanioksidin osuus pigmenttien kokonaismäärästä on voitu alentaa 23%:sta 12%:iin (Esimerkki 1). Samalla ovat tapetin valmistuskustannukset alentuneet ja pigmenttipäällystekerroksen painettavuusominaisuudet parantuneet. Keksinnön etuna voidaan pitää myöskin sitä, että 15 lateksin osuuden erittäin huomattavasta alenemisesta johtuen paksunnosainetta voidaan huoletta käyttää riittävästi hyvän tasoittumisen aikaansaamiseksi pigmenttipäällystekerrokselle.It can be seen from the example tables that by using the method according to the invention it has been possible to reduce the proportion of latex in the pigment coating layer from 25% to 10%, while still maintaining the washing resistance properties of the wallpaper sufficiently good. The proportion of titanium oxide in the total amount of pigments has been reduced from 23% to 12% (Example 1). At the same time, the manufacturing cost of the wallpaper has been reduced and the printability properties of the pigment coating layer have been improved. It can also be considered an advantage of the invention that, due to the very considerable reduction in the proportion of latex, the thickener can be safely used sufficiently to provide a good leveling for the pigment coating layer.
Alentuneesta lateksipitoisuudesta syntyy vielä seuraavat edut:The reduced latex content also has the following benefits:
Ennen keksinnön mukaista käsittelyä syntyvä pigmenttipäällys-20 tetty hylkypaperi hajoaa helposti ja voidaan siten helposti palauttaa paperinvalmistusjärjestelmään.The pigment-coated waste paper formed prior to the treatment according to the invention decomposes easily and can thus be easily returned to the papermaking system.
Päällystyksessä käytettyjen laitteiden puhdistus helpottuu. Jäteveden biologinen hapen kulutus (B0D) vähenee.Equipment used for coating is easier to clean. The biological oxygen demand (B0D) of wastewater is reduced.
nof
Claims (11)