ES317653A1 - A procedure for making steel plate thick with great strength to the traction. (Machine-translation by Google Translate, not legally binding) - Google Patents

A procedure for making steel plate thick with great strength to the traction. (Machine-translation by Google Translate, not legally binding)

Info

Publication number
ES317653A1
ES317653A1 ES0317653A ES317653A ES317653A1 ES 317653 A1 ES317653 A1 ES 317653A1 ES 0317653 A ES0317653 A ES 0317653A ES 317653 A ES317653 A ES 317653A ES 317653 A1 ES317653 A1 ES 317653A1
Authority
ES
Spain
Prior art keywords
translation
machine
legally binding
google translate
traction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
ES0317653A
Other languages
Spanish (es)
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inland Steel Co
Original Assignee
Inland Steel Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US398626A external-priority patent/US3378360A/en
Application filed by Inland Steel Co filed Critical Inland Steel Co
Publication of ES317653A1 publication Critical patent/ES317653A1/en
Expired legal-status Critical Current

Abstract

A process for making thin tensile steel sheet of high tensile strength comprising heating thin, thin carbon steel sheet having a carbon content of from about 0.03 wt% to about 0.25 wt% until a temperature at least above the critical point A1 so as to at least partially austenitize the steel and uniformly cool the sheet uniformly from said temperature to obtain a microstructure consisting at least partially of martensite. (Machine-translation by Google Translate, not legally binding)
ES0317653A 1964-09-23 1965-09-21 A procedure for making steel plate thick with great strength to the traction. (Machine-translation by Google Translate, not legally binding) Expired ES317653A1 (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US398626A US3378360A (en) 1964-09-23 1964-09-23 Martensitic steel
US45358865A 1965-05-06 1965-05-06

Publications (1)

Publication Number Publication Date
ES317653A1 true ES317653A1 (en) 1966-03-16

Family

ID=27016311

Family Applications (1)

Application Number Title Priority Date Filing Date
ES0317653A Expired ES317653A1 (en) 1964-09-23 1965-09-21 A procedure for making steel plate thick with great strength to the traction. (Machine-translation by Google Translate, not legally binding)

Country Status (9)

Country Link
BE (1) BE670020A (en)
CH (1) CH469810A (en)
DE (1) DE1483247C3 (en)
DK (1) DK136911B (en)
ES (1) ES317653A1 (en)
GB (1) GB1057530A (en)
IL (1) IL24356A (en)
LU (1) LU49520A1 (en)
NL (1) NL151440B (en)

Families Citing this family (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS56150135A (en) * 1980-01-18 1981-11-20 British Steel Corp Binary steel
JPS579831A (en) * 1980-05-21 1982-01-19 British Steel Corp Steel production
NL8500658A (en) * 1985-03-08 1986-10-01 Hoogovens Groep Bv METHOD FOR MANUFACTURING DUAL PHASE PACKING SAMPLE
CN100370054C (en) * 2001-06-15 2008-02-20 新日本制铁株式会社 High-strength steel plates coated with aluminum alloy systems and high-strength automotive parts with excellent heat resistance and corrosion resistance after painting
JP4825882B2 (en) * 2009-02-03 2011-11-30 トヨタ自動車株式会社 High-strength quenched molded body and method for producing the same
DE102011056846B4 (en) 2011-12-22 2014-05-28 Thyssenkrupp Rasselstein Gmbh Method for producing a tear-open lid and use of a steel sheet provided with a protective layer for producing a tear-open lid
DE102011056847B4 (en) 2011-12-22 2014-04-10 Thyssenkrupp Rasselstein Gmbh Steel sheet for use as a packaging steel and process for the production of a packaging steel
JP6211581B2 (en) 2012-03-30 2017-10-11 タタ、スティール、アイモイデン、ベスローテン、フェンノートシャップＴａｔａ Ｓｔｅｅｌ Ｉｊｍｕｉｄｅｎ Ｂｖ Method for producing recovery annealed steel substrate for packaging applications and packaged steel products produced thereby
DE102013101847B3 (en) 2013-02-25 2014-03-27 Thyssenkrupp Rasselstein Gmbh Method for producing a corrosion-resistant steel sheet

Also Published As

Publication number Publication date
DK136911B (en) 1977-12-12
DE1483247C3 (en) 1981-02-26
LU49520A1 (en) 1966-03-23
CH469810A (en) 1969-03-15
DE1483247A1 (en) 1969-03-20
NL6512364A (en) 1966-03-24
NL151440B (en) 1976-11-15
GB1057530A (en) 1967-02-01
DE1483247B2 (en) 1980-06-19
IL24356A (en) 1969-08-27
DK136911C (en) 1978-05-22
BE670020A (en) 1966-03-23

Similar Documents

Publication Publication Date Title
ES317653A1 (en) A procedure for making steel plate thick with great strength to the traction. (Machine-translation by Google Translate, not legally binding)
ES329953A1 (en) A procedure for the treatment of a mixture of symmetrical and asymmetric diclorotetrafluorethane. (Machine-translation by Google Translate, not legally binding)
GB973489A (en) Improvements in or relating to martensitic-stainless steels
ES295155A1 (en) A procedure for the preparation of a resinant composition very resistant to impact (Machine-translation by Google Translate, not legally binding)
JPS52119412A (en) Steel material having excellent temper brittleness resistance and high temperature strength
ES315241A1 (en) A basic procedure for the production of steel. (Machine-translation by Google Translate, not legally binding)
ES237339A1 (en) Procedure for the preparation of iron directly from minerals. (Machine-translation by Google Translate, not legally binding)
SU635153A1 (en) Steel
JPS5229418A (en) Heat resisting steel
ES294930A1 (en) METHOD OF PRODUCTION OF DEEPLY HARDENED STEEL ELEMENTS
JPS5262121A (en) Process for improving toughness of boron steel
ES382962A1 (en) Procedure for the thermal treatment of nickel steel. (Machine-translation by Google Translate, not legally binding)
JPS5329218A (en) Production of ultralow carbon, 80 kg/mm2 high tensile steel plate
ES370816A1 (en) A PROCEDURE TO DEGASSIFY A BETA-LA-CTONA POLYMER.
JPS52135808A (en) Furnace cooling in batch type furnace
JPS5270912A (en) Equipment for heat treatment of high tensile steel material
GB768455A (en) Improvements in the manufacture of spheroidal graphite cast iron
Shellenberger et al. An Effective Method for Controlling a Blast Furnace.(Retroactive Coverage)
ES275466A1 (en) Improvements in or relating to alloy steels
ES249049A1 (en) Procedure for obtaining steel molded to manganese of austenic structure (Machine-translation by Google Translate, not legally binding)
JPS5311811A (en) Carburizing method for molten steel
JPS525612A (en) Process for regulating the temperature of blowinout at a converter
ES333612A1 (en) PROCEDURE TO IMPROVE THE ELASTIC LIMIT TO TENACITY RATIO OF A STEEL.
GB648242A (en) Graphitic alloy steels and nitrided products made therefrom
GB1065899A (en) Improvements in or relating to martensitic,age hardening stainless steel