ES2326585B2 - PHENOLIC STRATIFICATE WITH A METAL OR STEEL SHEET AND PROCEDURE FOR OBTAINING THE SAME. - Google Patents
PHENOLIC STRATIFICATE WITH A METAL OR STEEL SHEET AND PROCEDURE FOR OBTAINING THE SAME. Download PDFInfo
- Publication number
- ES2326585B2 ES2326585B2 ES200900812A ES200900812A ES2326585B2 ES 2326585 B2 ES2326585 B2 ES 2326585B2 ES 200900812 A ES200900812 A ES 200900812A ES 200900812 A ES200900812 A ES 200900812A ES 2326585 B2 ES2326585 B2 ES 2326585B2
- Authority
- ES
- Spain
- Prior art keywords
- metal
- sheet
- phenolic
- base
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Estratificado fenólico con una lámina de metal o acero y procedimiento de obtención del mismo.Phenolic laminate with a sheet of metal or steel and procedure for obtaining it.
Estratificado fenólico compuesto por un base de estratificado de madera sobre la que se fija una lámina metálica o de acero que tiene un espesor de entre 0,1 mm hasta 0,6 mm y sobre la que se ha realizado un grabado. El procedimiento de fabricación consta de las etapas de raspado de la lámina sobre una de las caras, aplicación de una pintura "primer", aplicación de una cola, paso por unos rodillos que ejercen un grabación a la vez que aplican una presión. Gracias a la naturaleza y método de fabricación se consigue un estratificado de elevada resistencia superficial, perfectamente plano ignífugo y que se obtiene en frío y en continuo lo que abarata los costes de obtención.Phenolic stratified consisting of a base of laminated wood on which a metal sheet is fixed or of steel having a thickness of between 0.1 mm to 0.6 mm and about which has been engraved. The manufacturing procedure It consists of the stages of scraping the sheet on one of the faces, application of a "first" paint, application of a glue, I go through rollers that exert a recording while applying a pressure Thanks to the nature and manufacturing method it achieves a high surface resistance laminate, perfectly flat fire retardant and that is obtained in cold and continuous which lowers the cost of obtaining.
Description
Estratificado fenólico con una lámina de metal o acero y procedimiento de obtención del mismo.Phenolic laminate with a sheet of metal or steel and procedure for obtaining it.
Es objeto de la presente invención un estratificado fenólico con una lámina de metal o acero fijada sobre al menos una de sus caras exteriores, así como el procedimiento de fabricación de dicho estratificado.The object of the present invention is a Phenolic laminate with a sheet of metal or steel fixed on at least one of its outer faces, as well as the procedure of manufacture of said laminate.
Caracteriza a la presente invención la especial configuración, y combinación de elementos empleados en la fabricación del estratificado fenólico de manera que permiten obtener un tablero perfectamente plano, que presenta una elevada resistencia superficial, antideslizante e ignífugo.Characterizes the present invention the special configuration, and combination of elements used in the manufacture of the phenolic laminate so as to allow get a perfectly flat board, which has a high surface resistance, non-slip and flame retardant.
Derivado de las etapas del procedimiento de fabricación se consigue un tablero que se fabrica por un procedimiento más rápido y sencillo al realizarse en continuo, que se realiza en frío, por lo que el tablero no ve alterada su resistencia mecánica.Derived from the stages of the procedure manufacturing you get a board that is manufactured by a faster and easier procedure when performed continuously, which it is done cold, so the board is not altered its mechanical strength.
Por lo tanto, la presente invención se circunscribe dentro del ámbito de los estratificados conformados a partir de un estratificado fenólico y de manera particular de entre aquellos que cuentan con una lámina metálica adherida sobre una de sus caras.Therefore, the present invention is circumscribed within the scope of the stratified conformed to from a phenolic stratified and in particular from those that have a metallic sheet attached on one of their faces.
Los antecedentes más cercanos al objeto de la
invención son los denominados tableros fenólicos provistos de un
forro de material fenólico. El interior del estratificado está
conformado por una serie de láminas o chapas, de diferentes
maderas, por ejemplo abedul, que están superpuestas intercalándolas
por la dirección de la fibra. Las chapas de madera se encolan con
cola fenólica, que tiene la propiedad de ser resistente al agua,
impidiendo el desencolado del
tablero.The background closest to the object of the invention are the so-called phenolic boards provided with a lining of phenolic material. The interior of the laminate is made up of a series of sheets or veneers, of different woods, for example birch, which are superimposed intercalating them by the direction of the fiber. The veneers are glued with phenolic glue, which has the property of being resistant to water, preventing the decoupling of the
board.
El acabado de la superficie fenólica se realiza con un film fenólico de papel kraft por las dos caras dándole un acabado brillante, que permite su utilización como superficie encofrante lo cual mejora el acabado en las superficies verticales de hormigón.The phenolic surface finish is done with a phenolic film of kraft paper on both sides giving it a glossy finish, which allows its use as a surface formwork which improves the finish on vertical surfaces of concrete.
Las ventajas de estos estratificados fenólicos con forro de material fenólico, es que son reciclables, resistentes al estar formado por una serie de capas de madera contrapuestas entre sí, encoladas y prensadas, y también son resistentes, ligeros y están aislados de la humedad, contando como ventaja adicional que en su uso como tablero para encofrados no deja marcas en el hormigón y ofrece un excelente acabado en el hormigón.The advantages of these phenolic laminates with a lining of phenolic material, it is that they are recyclable, resistant being formed by a series of contrasting layers of wood each other, glued and pressed, and are also resistant, lightweight and are isolated from moisture, counting as an additional advantage that in its use as a formwork board does not leave marks on the concrete and offers an excellent finish in concrete.
No obstante, presenta algunos inconvenientes y características que son susceptibles de ser mejoradas. Por un lado, el procedimiento de fabricación de los estratificados fenólicos con forro de material fenólico, es preciso la aplicación del forro fenólico de una prensa en caliente, lo que impide la fabricación en continuo, además de alterar la resistencia mecánica del estratificado, por lo que no se logra un superficie perfectamente plana.However, it has some drawbacks and features that are likely to be improved. On the one hand, the manufacturing process of phenolic laminates with lining of phenolic material, it is necessary to apply the lining phenolic of a hot press, which prevents manufacturing in continuous, in addition to altering the mechanical resistance of the stratified, so that a perfectly surface is not achieved flat.
Por otro lado, el estratificado obtenido no ofrece una elevada resistencia superficial lo que limita su uso a ciertos casos como el referido de tablero para encofrado.On the other hand, the stratified obtained does not It offers a high surface resistance which limits its use to certain cases such as the formwork board referral.
También sucede que el estratificado fenólico con forro fenólico no es un material ignífugo por lo que limita su campo de actuación a situaciones donde no se tiene que cumplir requisito alguno contra el fuego.It also happens that the phenolic stratified with phenolic lining is not a flame retardant material so it limits your field of action in situations where you do not have to comply any requirement against fire.
Por lo tanto, es objeto de la presente invención mejorar y evitar los inconvenientes anteriormente mencionados mediante un tablero fenólico y procedimiento de obtención del mismo según el juego de reivindicaciones adjunto, que permita la fabricación en continuo, que durante la fabricación no se vea alterada la resistencia estructural del estratificado, que presente una elevada resistencia superficial, y que sea ignífugo.Therefore, it is the subject of the present invention improve and avoid the aforementioned inconveniences by means of a phenolic board and procedure to obtain it according to the attached set of claims, which allows the continuous manufacturing, which during manufacturing is not visible altered the structural strength of the laminate, which presents high surface resistance, and make it flame retardant.
La invención de estratificado fenólico con una lámina de metal y/o acero fijada sobre una de sus caras consta de una base conformada por estratificado base fenólico realizado a base de al menos una chapa o tablero de madera, en el que las chapas de madera se encolan con cola fenólica y sobre la que se fija una lámina metálica.The invention of phenolic laminate with a sheet of metal and / or steel fixed on one of its faces consists of a base formed by stratified phenolic base made with base of at least one veneer or wooden board, in which the veneers of wood is glued with phenolic glue and on which a metal foil
La esencia de la invención no reside solamente en la disposición de una lámina metálica sobre una de las caras de un tablero o de un estratificado base, sino en la naturaleza, dimensiones y procedimiento empleado para la fijación de dicha lámina metálica.The essence of the invention does not only reside in the arrangement of a metal sheet on one of the faces of a board or a laminated base, but in nature, dimensions and procedure used to fix said metal foil
La lámina metálica presenta un espesor de entre 0,1 mm a 0,6 mm, por lo que perfectamente puede ser denominada como "film" metálico. La lámina es metálica o incluso de acero.The metal sheet has a thickness between 0.1 mm to 0.6 mm, so it can perfectly be referred to as metallic "film". The sheet is metallic or even steel.
\newpage\ newpage
El procedimiento de fijación de la lámina metálica sobre el tablero base o estratificado base consta de las siguientes etapas:The sheet fixation procedure metal on the base board or laminated base consists of the following stages:
- \bullet?
- Una vez dispuesta la lámina metálica o de acero en una bobina se procede al raspado de la lámina metálica por una de sus caras, en concreto por la cara que queda fijada sobre la base.Once the sheet is arranged metal or steel in a coil is scraped off the sheet metal on one of its faces, specifically on the face that is fixed on the base.
- \bullet?
- Seguidamente por la misma cara sobre la que se ha procedido al raspado previo, se procede a la aplicación de una pintura "primer", que es un promotor que mejora la adherencia y puede usarse sobre superficies ferrosas y no ferrosasNext on the same face on which the previous scraping has been carried out, the application of a "first" paint, which is a promoter that improves adhesion and can be used on ferrous surfaces and not ferrous
- \bullet?
- A continuación se procede a la aplicación sobre dicha cara en la que se ha aplicado la pintura "primer" a aplicar una cola formada por un poliuretano de dos componentes o por una cola "PUR"Then proceed to the application on said face in which the paint has been applied "first" to apply a glue formed by a polyurethane of two components or by a "PUR" queue
- \bullet?
- Seguidamente se hace pasar el conjunto de la base y lámina dispuesta sobre la base sobre un conjunto de rodillo(s) grabador(es) que proceden a realizar una impresión bajo relieve sobre la lámina metálica, mediante el paso y aplicación de una presión adecuada al grosor de la lámina metálica.Then the assembly of the base and sheet arranged on the base on a set of engraver roller (s) that proceed to make an impression under relief on the metallic sheet, by passing and applying a suitable pressure to the thickness of The metal sheet.
\vskip1.000000\baselineskip\ vskip1.000000 \ baselineskip
La fijación final de la lámina metálica o de acero sobre la base de madera se realiza por adherencia gracias al empleo de una cola, y por el grabado realizado por los rodillos grabadores al aplicar una presión sobre la superficie del conjunto.Final fixing of the metal sheet or steel on the wooden base is made by adhesion thanks to the use of a glue, and the engraving made by the rollers engravers when applying a pressure on the surface of the set.
Gracias a las etapas de fabricación expuestas se consigue un tablero fenólico sobre el que se fija sobre al menos una de sus caras una lámina metálica, donde el procedimiento de fabricación se realiza en continuo, sin necesidad de someter a altas temperaturas el conjunto que podrían alterar la resistencia mecánica del conjunto, y donde el estratificado final es perfectamente plano obtenido en continuo.Thanks to the manufacturing stages exposed, get a phenolic board that is fixed on at least one of its faces a metal sheet, where the procedure of manufacturing is carried out continuously, without the need to submit to high temperatures the set that could alter the resistance mechanics of the set, and where the final laminate is perfectly flat obtained continuously.
Los rodillos de grabado, ejercerán una presión determinada sobre el conjunto de base y lámina metálica o de acero. La presión dependerá del grosor de la lámina metálica o de acero, así cuanto más gruesa sea dicha lámina mayor será la presión a ejercer y viceversa.Engraving rollers will exert pressure determined on the base and metal or steel sheet assembly. The pressure will depend on the thickness of the metal or steel sheet, thus, the thicker said sheet, the greater the pressure at exercise and vice versa.
En general, la presión que hay que ejercer sobre una superficie de madera para producir un grabado sobre la misma es de unos 700 Kg/m^{3}, mientras que para producir el hundimiento de una zona de un metal la presión que hay que ejercer es de unos 2000 Kg/m^{3}.In general, the pressure to be exerted on a wooden surface to produce an engraving on it It is about 700 Kg / m 3, while to produce the sinking in a zone of a metal the pressure to be exerted is about 2000 Kg / m 3.
Complementariamente, la superficie metálica o de acero puede someterse a una etapa de anodizado, que busca evitar la corrosión por ejemplo de un metal como el Aluminio, o también busca una función decorativa.In addition, the metal surface or steel can undergo an anodizing stage, which seeks to avoid the corrosion for example of a metal such as aluminum, or also seeks A decorative function.
Gracias a esta configuración y procedimiento de fabricación se obtienen un tablero que es perfectamente plano, que es antideslizante, que ofrece una elevada resistencia superficial, es ignífugo, pudiendo utilizarse como elemento constructivo o por ejemplo forrado del interior y suelo de un vagón de tren, la cabina de transporte de un camión.Thanks to this configuration and procedure of manufacturing you get a board that is perfectly flat, which It is non-slip, offering high surface resistance, It is flame retardant, and can be used as a construction element or by lined example of the interior and floor of a train car, the cabin of transport of a truck.
\vskip1.000000\baselineskip\ vskip1.000000 \ baselineskip
Para complementar la descripción que seguidamente se va a realizar y con objeto de ayudar a una mejor comprensión de sus características, se acompaña a la presente memoria descriptiva, de un juego de planos en cuyas figuras, de forma ilustrativa y no limitativa, se representan los detalles más significativos de la invención.To complement the description that then it will be done and in order to help a better understanding of its characteristics, is accompanied by this descriptive memory, of a set of planes in whose figures, of illustrative and non-limiting, the details are represented significant of the invention.
En la figura 1 se muestran las diferentes etapas que son necesarias para la obtención del estratificado fenólico con una capa de metal o acero.The different stages are shown in Figure 1 which are necessary to obtain the phenolic laminate With a layer of metal or steel.
La figura 2 muestra una representación del estrafificado fenólico con una lámina de metal o acero objeto de la invención.Figure 2 shows a representation of the Phenolic laminate with a sheet of metal or steel that is the object of the invention.
\vskip1.000000\baselineskip\ vskip1.000000 \ baselineskip
A la vista de las figuras se describe seguidamente un modo de realización preferente de la invención propuesta.In view of the figures described then a preferred embodiment of the invention proposal.
En la figura 1, podemos observar una bobina (2) sobre la que hay enrollada en continuo una lámina metálica o de acero (7) que tendrá un espesor de entre 0,1 mm y 0,6 mm, por lo que perfectamente dicha lámina puede ser denominada como "film".In figure 1, we can see a coil (2) on which there is continuously rolled a metal sheet or steel (7) that will have a thickness of between 0.1 mm and 0.6 mm, so that perfectly said sheet can be referred to as "film".
El primer tratamiento a que se somete a dicha lámina (7) es a un raspado (3) por la cara en la que se va a fijar a una base de madera (1); donde la base (1) bien está formada por un tablero o por un estratificado fenólico. Seguidamente sobre la misma cara sobre la que se ha realizado el raspado (3) se procede a la aplicación de una pintura "primer" (4), para a continuación aplicar una cola (5) para la adhesión.The first treatment to be submitted to said sheet (7) is scraped (3) by the face on which it is to be fixed to a wooden base (1); where the base (1) is well formed by a board or by a phenolic stratified. Then on the same face on which the scraping has been performed (3) proceeds to the application of a "first" paint (4), then apply a glue (5) for adhesion.
Finalmente el conjunto formado por la base (1) y la lámina metálica (7) se hacen pasar por un conjunto grabador (6), que pudiera estar formado en una posible forma de realización por un par de rodillos que aplican una presión y donde al menos uno de los rodillos está moleteado realizando un grabado por hundimiento sobre la cara en la que se ha dispuesto la lámina metálica.Finally the set formed by the base (1) and the metal sheet (7) is impersonated (6), which could be formed in a possible embodiment by a pair of rollers that apply a pressure and where at least one of the rollers is knurled making an engraving by sinking on the face on which the sheet has been arranged metallic
Gracias a la aplicación de la presión sobre el conjunto se consigue, por un lado la fijación de la adherencia entre lámina y base, y por otro lado, el hundimiento de la lámina metálica por grabado en la base de madera.Thanks to the application of pressure on the set is achieved, on the one hand fixing the adhesion between sheet and base, and on the other hand, the sinking of the sheet Metal by engraving on the wooden base.
La cola empleada para el pegado de la lámina metálica o de acero (7) sobre la base de madera es una cola que está conformada por un poliuretano de dos componentes o una cola "PUR".The glue used for bonding the sheet metallic or steel (7) on the wooden base is a tail that It is made up of a two-component polyurethane or a glue "PUR".
En la figura 2 se observa los elementos de que consta el estratificado fenólico, donde se distingue la base de madera (1) conformada por una una serie de tableros (9) encolados entre sí y sobre el que se ha fijado una lámina de metal o de acero (7) mediante una cola y por presión, presentando la lámina (7) un moleteado (8) o una serie de resaltes en su cara exterior.Figure 2 shows the elements that consists of the phenolic stratified, where the basis of wood (1) consisting of a series of boards (9) glued each other and on which a sheet of metal or steel has been fixed (7) by means of a glue and by pressure, the sheet (7) presenting a knurled (8) or a series of projections on its outer face.
Derivado de la naturaleza del objeto de la invención y del procedimiento de fabricación se consigue un estratificado que ofrece una elevada resistencia superficie, antideslizante, que es ignífugo y que puede fabricarse en frío, por lo que no se altera la resistencia mecánica del estratificado y se fabrica en continuo, que es más rápido y económico.Derived from the nature of the object of the invention and of the manufacturing process a stratified that offers a high surface resistance, non-slip, which is flame retardant and can be manufactured cold, by what does not alter the mechanical resistance of the laminate and it manufactures continuously, which is faster and cheaper.
No altera la esencialidad de esta invención variaciones en materiales, forma, tamaño y disposición de los elementos componentes, descritos de manera no limitativa, bastando ésta para su reproducción por un experto.It does not alter the essentiality of this invention variations in materials, shape, size and arrangement of component elements, described in a non-limiting manner, sufficient This one for reproduction by an expert.
Claims (7)
- --
- Raspado (3) de una lámina metálica o de acero (7) bobinada en una bobina (2), raspado que se hace sobre una de las caras de la lámina (7), en concreto por la cara que queda fijada sobre la base.Scraping (3) of a metal sheet or steel (7) wound in a coil (2), scraped on a of the faces of the sheet (7), specifically for the face that remains fixed on the base.
- --
- Seguidamente por la misma cara sobre la que se ha procedido al raspado anterior, se procede a la aplicación (4) de una pintura "primer", que es un promotor que mejora la adherencia y puede usarse sobre superficies no ferrosasThen on the same face on the that the previous scraping has been carried out, the application is carried out (4) of a "first" paint, which is a promoter that improves the adhesion and can be used on non-ferrous surfaces
- --
- A continuación se procede a la aplicación sobre dicha cara en la que se ha aplicado la pintura "primer" a aplicar (5) una colaTO then the application is carried out on said face in which "first" paint has been applied to apply (5) a tail
- --
- pasar el conjunto de la base y lámina dispuesta sobre la base sobre un conjunto de rodillo(s) grabador(es) (6) que proceden a realizar una impresión bajo relieve sobre la lámina metálica, mediante el paso y aplicación de una presión adecuada al grosor de la lámina metálica.happen the base and sheet assembly arranged on the base on a set of engraver roller (s) (6) that proceed to make an impression under relief on the metallic sheet, by passing and applying a suitable pressure to the thickness of The metal sheet.