DE2600485A1 - Calcium and magnesium carbonates suitable for paper mfr - made by feeding carbon dioxide into aq suspension of calcined dolomite - Google Patents

Calcium and magnesium carbonates suitable for paper mfr - made by feeding carbon dioxide into aq suspension of calcined dolomite

Info

Publication number
DE2600485A1
DE2600485A1 DE19762600485 DE2600485A DE2600485A1 DE 2600485 A1 DE2600485 A1 DE 2600485A1 DE 19762600485 DE19762600485 DE 19762600485 DE 2600485 A DE2600485 A DE 2600485A DE 2600485 A1 DE2600485 A1 DE 2600485A1
Authority
DE
Germany
Prior art keywords
calcium
suspension
magnesium carbonate
magnesium
carbonate
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE19762600485
Other languages
German (de)
Inventor
Reinhard Dipl Ing Feige
Heinz Kendziora
Johann Nenner
Werner Dr Schultze
Roland Dr Thome
Guenter Prof Dr Winkhaus
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Vereinigte Aluminium Werke AG
Original Assignee
Vereinigte Aluminium Werke AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Vereinigte Aluminium Werke AG filed Critical Vereinigte Aluminium Werke AG
Priority to DE19762600485 priority Critical patent/DE2600485A1/en
Priority to DE19762660425 priority patent/DE2660425C2/en
Priority to AT22676A priority patent/AT348489B/en
Priority to NO760148A priority patent/NO141366C/en
Priority to PT64706A priority patent/PT64706B/en
Priority to FI760105A priority patent/FI62656C/en
Priority to IT67117/76A priority patent/IT1066074B/en
Priority to GB2053/76A priority patent/GB1533323A/en
Priority to NL7600557A priority patent/NL7600557A/en
Priority to SE7600550A priority patent/SE418607B/en
Priority to CH74176A priority patent/CH602488A5/xx
Priority to BE2054767A priority patent/BE837744A/en
Priority to FR7602074A priority patent/FR2298512A1/en
Priority to JP13056876A priority patent/JPS5285999A/en
Publication of DE2600485A1 publication Critical patent/DE2600485A1/en
Priority to AT141178A priority patent/AT359462B/en
Priority to NO792804A priority patent/NO154315C/en
Withdrawn legal-status Critical Current

Abstract

Process for mfg. carbonates of calcium and/or magnesium, the novelty being that by heating to 1000-1100 degrees C, dolomite is converted into a mixt. of calcium and magnesium oxides which are suspended in water using 1 pt. wt. of oxides and 20 pts. wt. water and the carbon dioxide is introduced into the suspension to convert the hydroxides into the corresponding carbonates. The initial starting material is pref. natural dolomite calcined in a rotary drum furnace, and the gas fed into the suspension is pref. CO2 or a mixt. of CO2 and N2, esp. the exhaust gas from the drum furnace. Before or during the slaking of the oxides, additional amounts of Ca or Mg oxide, hydroxide or carbonate may be added. Used e.g. for mfr. of basic calcium-magnesium carbonate as a filler or coating for mfg. glossy papers, where the carbonate has a degree of whiteness above 95%.

Description

Verfahren zur Herstellung von Carbonaten Process for the production of carbonates

des Calciums oder/und Magnesiums Die Erfindung betrifft ein Verfahren zur Herstellung von Carbonaten des Calciums oder/und Magnesiums, insbesondere von basischem Magnesiumcarbonat oder basischem Calcium-Magnesium-Carbonat. of calcium and / or magnesium The invention relates to a method for the production of carbonates of calcium and / or magnesium, in particular of basic magnesium carbonate or basic calcium magnesium carbonate.

Derartige Carbonate werden in der Technik zu zahlreichen Zwecken benötigt und nach verschiedenen Verfahren aus geeigneten Ausgangsstoffen gewonnen. Ein leicht und in großen Mengen erhältliches Rohmaterial, das Calcium und Magnesium in Carbonatform enthält, wäre der Dolomit. Der kostengünstigen Gewinnung der Carbonate aus Dolomit steht Jedoch entgegen, daß der Aufschluß schwierig ist. Insbesondere lässt sich Dolomit nur schwer in eine genügend feinteilige Form bringen, wie sie für die Gewinnung und vor allem den Einsatz der Carbonate z. T. erforderlich ist.Such carbonates are required for numerous purposes in industry and obtained from suitable starting materials by various processes. An easy one and raw material available in large quantities, the calcium and magnesium in carbonate form would contain dolomite. The inexpensive extraction of carbonates from dolomite However, this is opposed by the fact that the digestion is difficult. In particular, can It is difficult to bring dolomite into a sufficiently fine-grained form, as it is for extraction and especially the use of carbonates z. T. is required.

Es ist bekannt, aus Dolomit dadurch Magnesiumcarbonat herzustellen, daß man Dolomit in konzentrierter kalter Salzsäure löst, die Kieselsäure sowie das Aluminium und das Eisen als Hydroxide abtrennt und das in der klaren Lösung verbliebene Calcium und Magnesium durch Zugabe von Natriumcarbonat in Magnesiumcarbonat überführt. Durch Zusatz von Schwefelsäure zur Lösung kann der Kalk als Sulfat ausgefällt werden. Dieses und ähnliche Verfahren haben jedoch, soweit bekannt wurde, keine größere industrielle Anwendung finden können, weil eine Ruckgewinnung der verwendeten Salzsäure nur mit großem Kostenaufwand möglich ist.It is known to produce magnesium carbonate from dolomite, that one dissolves dolomite in concentrated cold hydrochloric acid, the silica and that Separates aluminum and iron as hydroxides and what remains in the clear solution Calcium and magnesium converted into magnesium carbonate by adding sodium carbonate. By adding sulfuric acid to the solution, the lime can be precipitated as sulfate. However, as far as has been known, this and similar processes have no major ones Can find industrial application because a recovery of the hydrochloric acid used is only possible at great expense.

Der Erfindung liegt die Aufgabe zugrunde, ein großtechnisch durchführbares, billiges Verfahren zur Gewinnung von Calcium-bzw. Magnesiumcarbonat aus Dolomit zu entwickeln, welches keiner Aufschlußchemikalien oder sonstiger Reaktionspartner bedarf.The invention is based on the object of an industrially feasible, cheap process for the production of calcium or. Magnesium carbonate to develop from dolomite, which no digestion chemicals or other reactants requirement.

Diese Aufgabe wird erfindungsgemäß dadurch gelöst, daß man 0 den Dolomit durch Erhitzen auf etwa 1000 bis etwa 1100 C in ein Gemisch von Calciumoxid und Magnesiumoxid umwandelt, das erhaltene Oxidgemisch im Gewichtsverhältnis von wenigstens 20 : 1 in Wasser suspendiert und die dabei in der Suspension gebildeten Hydroxide durch Einleiten von Kohlendioxid in die entsprechenden Carbonate zurückverwandelt.According to the invention, this object is achieved by the fact that the dolomite by heating to about 1000 to about 1100 C in a mixture of calcium oxide and Converts magnesium oxide, the oxide mixture obtained in a weight ratio of at least 20: 1 suspended in water and the hydroxides formed in the suspension converted back into the corresponding carbonates by introducing carbon dioxide.

An diese Behandlung kann sich in an sich bekannter Weise eine Abtrennung evtl. störender Verunreinigungen bzw. die weiter unten beschriebene Aufarbeitung auf die gewünschten Carbonate anschließen.This treatment can be followed by a separation in a manner known per se possibly disruptive impurities or the work-up described below connect to the desired carbonates.

Für die Recarbonisierung können die kohlendioxidhaltigen Abgase der Dolomit-Kalzination verwendet werden, so daß keine besondere Kohlensäure zufuhr erforderlich ist, Jedoch versteht sich, daß auch reines C02 oder ein Kohlendioxid-Stickstoff-Gemisch anderer Herkunft für die Begasung in Betracht kommen. Diese wird vorzugsweise unter intensivem Bewegen der Suspension durchgeführt.The carbon dioxide-containing exhaust gases from the Dolomite calcination can be used so that no special carbonic acid is added However, it goes without saying that pure C02 or a carbon dioxide-nitrogen mixture can also be used other origins can be considered for fumigation. This is preferably under carried out intensive agitation of the suspension.

Die Kalzinierung des Dolomits wird vorzugsweise in einem Drehofen durchgeführt.The calcination of the dolomite is preferably carried out in a rotary kiln carried out.

Wenn auch entsprechend der Zielsetzung der Erfindung in erster Linie natürlicher Dolomit als Ausgangsmaterial einzusetzen ist, so kann die Grundidee des erfindungsgemäßen Verfahrens auch auf synthetische Produkte dolomitähnlicher Beschaffenheit und Zusammensetzung angewandt werden.Albeit primarily in accordance with the aim of the invention If natural dolomite is to be used as the starting material, then the basic idea can be of the method according to the invention also to synthetic products similar to dolomite Nature and composition are applied.

Die mit Kohlendioxid behandelte Suspension kann als solche, gegebenenfalls nach Einengung, weiterverwendet werden, oder die gewünschten Carbonate können aus der Suspension abgetrennt werden. Auf diese Weise sind nach dem erfindungsgemäßen Verfahren neben CaCO5 auf einfache Weise vor allem basische Magnesium- oder Calcium-Magnesium-Carbonate zugänglich.The carbon dioxide-treated suspension can be used as such, if appropriate continue to be used after narrowing, or the desired carbonates can be separated from the suspension. In this way, according to the invention In addition to CaCO5, a simple method, especially basic magnesium or calcium-magnesium carbonates accessible.

Verfahren zur Herstellung von gefälltem basischem Magnesium-Carbonat bzw. von Calcium-Carbonat sind zwar bereits bekannt.Process for the production of precipitated basic magnesium carbonate and calcium carbonate are already known.

Unter verschiedenen Bedingungen, z. B. unterschiedlichen Temperaturen, Konzentrationen usw., kann hierzu C02 in Aufschlämmungen von CaO bzw. Ca(OH)2 oder MgO bzw. Mg(OH)2 geleitet werden. Je nach Erfordernis können entsprechende Mischungen der Produkte hergestellt werden. Man benötigt aber getrennte Apparaturen, wenn man - ausgehend von Jeweils reinen Substanzen - auf diese Weise ein basisches Calcium-Magnesium-Carbonat mit einem genau difinierten Calcium-Magnesium-Molverhältnis etwa 1 : 1 herstellen will, das in Form einer stabilen Suspension weitere Verwendung finden soll.Under different conditions, e.g. B. different temperatures, Concentrations etc., this can be done with C02 in slurries of CaO or Ca (OH) 2 or MgO or Mg (OH) 2 are passed. Appropriate mixtures can be used as required of the products are manufactured. But you need separate equipment if you - based on pure substances in each case - in this way a basic calcium-magnesium-carbonate with a precisely defined calcium-magnesium molar ratio of about 1: 1 wants to find further use in the form of a stable suspension.

Nach der Erfindung lassen sich die angestrebten Produkte auf dem scheinbaren Umwege des erfindungsgemä.ßen Verfahrens über die Oxide bzw. Hydroxide hingegen kostengünstig und ohne besonderen Aufwand herstellen. Insbesondere ist es möglich, in einer einzigen Apparatur auf einfache Weise ein Calcium-Magnesium-Carbonat mit definiertem Calcium-Magnesium-Verhältnis herzustellen. Wie weiter unten noch erläutert werden wird, zeichnen sich die Produkte außerdem durch besondere Eigenschaften aus, die sie für bestimmte Produkte wertvoll machen.According to the invention, the desired products can be on the apparent By contrast, detours of the method according to the invention via the oxides or hydroxides Manufacture inexpensively and without special effort. In particular, it is possible a calcium-magnesium-carbonate in a single apparatus in a simple manner to produce a defined calcium-magnesium ratio. As explained below the products are also characterized by special properties, which make them valuable for certain products.

Die Herstellung von basischem Calcium-Magnesium-Carbonat erfolgt erfindungsgemäß dadurch, daß man Dolomit kalziniert, das Produkt ablöscht und in Wasser im Gewichtsverhältnis von 20 - 60 Teilen Wasser auf 1 Teil Oxide suspendiert und die Suspension nach der Begasung mit Kohlendioxid einengt.Basic calcium magnesium carbonate is produced according to the invention by calcining dolomite, quenching the product and putting it in water in a weight ratio from Suspended 20-60 parts of water to 1 part of oxides and the suspension after gassing constricts with carbon dioxide.

Die dabei anfallende Suspension enthält das gewünschte basische Calcium-Magnesium-Carbonat, und zwar in einem definierten Calcium/Magnesium-Verhältnis' das dem ursprünglichen Calcium-Magnesium-Verhältnis in dem eingesetzten Dolomit entspricht. Es ist Jedoch ohne weiteres möglich, dieses Verhältnis zu beeinflussen. Eine Suspension mit abweichendem Calcium-Magnesium-Verhältnis kann z. B. leicht durch Zudosieren von CaO und/oder MgO bzw. Ca(OH)2 und/oder Mg(OH)2 oder gefälltem Calcium- bzw. Magnesiumcarbonat zum Ausgangsstoff oder zu der Suspension vor, während oder nach der C02-Einleitung erhalten werden. Ebenso kann man durch Abtrennen des Calciumcarbonats zu einer Suspension gelangen, die nur noch Magnesium-Carbonat in basischer Form enthält.The resulting suspension contains the desired basic calcium-magnesium-carbonate, in a defined calcium / magnesium ratio 'that of the original Calcium-magnesium ratio in the dolomite used. However, it is it is easily possible to influence this relationship. A suspension with deviating Calcium-magnesium ratio can be e.g. B. easily by adding CaO and / or MgO or Ca (OH) 2 and / or Mg (OH) 2 or precipitated calcium or magnesium carbonate on the starting material or on the suspension before, during or after the introduction of C02 can be obtained. A suspension can also be obtained by separating off the calcium carbonate which only contains magnesium carbonate in basic form.

Basisches Magnesiumcarbonat wird nach der Erfindung getrennt von Calciumcarbonat dadurch verhalten, daß man Dolomit kalziniert, das Produkt ablöscht und in Wasser im Gewiohtsverhältnis von etwa 60 Teilen Wasser auf 1 Teil Oxide suspendiert, das ungelöste Calciumcarbonat abfiltriert und die Lösung mit einer Aufheizgeschwindigkeit von mindestens 10 0/min auf Temperaturen zwischen 70 und 800 C erhitzt, bis das basische Magnesiumcarbonat ausgefällt ist.According to the invention, basic magnesium carbonate is separated from calcium carbonate behave by calcining dolomite, extinguishing the product and immersing it in water suspended in a weight ratio of about 60 parts of water to 1 part of oxides, the undissolved calcium carbonate is filtered off and the solution with a heating rate heated from at least 10 0 / min to temperatures between 70 and 800 C until the basic magnesium carbonate is precipitated.

Das in der skizzierten Weise zugängliche basische Magnesiumcarbonat unterscheidet sich eigenartigerweise durch seine Plättchenform von dem basischen Magnesiumcarbonat, welches durch Carbonisierung von gefälltem Mg(OH)2 hergestellt wurde und nadelförmig ist, ebenso wie auch das aus einer Magnesiumsulfatlösung mit Soda ausgefällte basische Magnesium-Carbonat.The basic magnesium carbonate accessible in the manner outlined Strangely enough, it differs from the basic one by its platelet shape Magnesium carbonate, which is produced by carbonizing precipitated Mg (OH) 2 and is needle-shaped, as well as that from a magnesium sulfate solution with Soda precipitated basic magnesium carbonate.

Das Produkt des erfindungsgemäßen Verfahrens zeichnet sich ferner durch einen hohen Shapefaktor von mindestens 1 : 80 aus und ist sehr feinteilig. Es lässt sich beispielsweise in der keramischen Industrie einsetzen.The product of the method according to the invention is also notable has a high shape factor of at least 1:80 and is very finely divided. It can be used, for example, in the ceramics industry.

Auch das erfindungsgemäß erhältliche Calcium-Magnesium-Carbonat ist feinkörnig und überwiegend plättchenförmig. Dieses Produkt bietet sich aufgrund seiner Beschaffenheit zur Verwendung in der Papierindustrie an.The calcium magnesium carbonate obtainable according to the invention is also fine-grained and predominantly platelet-shaped. This product offers itself because of its nature for use in the paper industry.

Es ist bekannt, daß dem Faserbrei bei der Papierherstellung in der Regel Füllstoffe beigemengt werden, um Weiße, Opazität und Glätte des Rohpapiers zu verbessern. Diese Eigenschaften sind wichtig, weil auch beim Streichen der Rohpapieroberfläche mit Pigmenten der Untergrund, besonders nach der Satinage, durchschimmern kann.It is known that the pulp in papermaking in the Usually fillers are added to the whiteness, opacity and smoothness of the base paper to improve. These properties are important because they are also important when painting the surface of the base paper With pigments, the substrate can shimmer through, especially after the glaze.

Der Einsatz von Carbonaten in der Papiermasse hat gerade in den letzten Jahren zunehmend an Bedeutung gewonnen, da die Vorteile der Papierherstellung in basischen Medien gegenüber der in sauren bei weitem überwiegen. Diese liegen nicht nur in der Nutzungsdauer der Anlagenteile einer Papierfabrik (Korrosionen bei saurer Herstellung) und einer Reduzierung des Mahlenergiebedarfs, sondern insbesondere auch in einer Verbesserung der Eigenschaften der auf diese Weise hergestellten Papiere, was beispielsweise die Vergilbungsreigung, Druckeigenschaften und Alterungsbeständigkeit anbelangt. Für die verschiedenartigsten Papiersorten kommen hierbei bisher folgende Füllstoffe in Betracht: Aluminiumsilikat, Magnesiumsilikat, Calciumsulfat, Bariumsulfat, Calciumcarbonat (allerdings nur für bestimmte Papiersorten wie Zigarettenpapiere), Titandioxid, Titandioxid-Bariumsulfat-Gemische, Calciumsilikat, um die bedeutendsten zu nennen.The use of carbonates in paper pulp has just happened in recent years Gained increasing importance over the years as the advantages of papermaking came in alkaline media by far outweigh those in acidic media. These are not only during the useful life of the plant parts of a paper mill (corrosion in the case of acid Production) and a reduction of the grinding energy requirement, but in particular also in an improvement of the properties of the papers produced in this way, what, for example, the tendency to yellowing, printing properties and aging resistance is concerned. So far, the following have been used for the most varied types of paper Fillers under consideration: aluminum silicate, magnesium silicate, calcium sulfate, barium sulfate, Calcium carbonate (but only for certain types of paper such as cigarette papers), Titanium dioxide, titanium dioxide-barium sulfate mixtures, calcium silicate to the most significant to call.

Um die Druckqualität eines Papieres zu steigern, sind insbesondere die Gleichmäßigkeit seiner Oberfläche, Glätte, Glanz, Opazität, Weiße, Lackierfähigkeit und Druckfarbenaufnahme ausschlaggebend. Diese Eigenschaften werden erreicht-bzw. verbesser, wenn das Rohpapier anschließend mit insbesondere Weißpigmenten gestrichen wird, die man in Form eines Breies bzw.In order to increase the print quality of a paper, are in particular the evenness of its surface, smoothness, gloss, opacity, whiteness, paintability and ink absorption are decisive. These properties are achieved or. Better if the base paper is then coated with white pigments in particular which is in the form of a porridge or

einer Suspension in der Papierstreichanlage auf das Papier aufbringt.a suspension in the paper coating system on the paper.

An das Pigment werden dabei folgende Anforderungen gestellt: Hohe Reinheit, geringe Teilchengröße, hohe Weiße und Opazität, hoher Berechnungsindex, hohe spez. Oberfläche, hoher Shape-Faktor, gute Dispergierbarkeit und günstiges rheologisches Verhalten und selbstverständlich gute Druckfarbenaufnahme.The following requirements are made of the pigment: High Purity, small particle size, high whiteness and opacity, high refractive index, high spec. Surface, high shape factor, good dispersibility and inexpensive rheological behavior and of course good ink absorption.

Diese Eigenschaften werden weitgehend durch folgende Pigmente und entsprechende Kombinationen untereinander erreicht, da nicht alle diese Substanzen für sich allein die gestellten Anforderungen gleich gut erfüllen: Kaoline, Calciumcarbonate, Satinweiß, Titandioxid, Blancfixe.These properties are largely due to the following pigments and corresponding combinations with one another are achieved, since not all of these substances meet the requirements equally well on their own: kaolins, calcium carbonates, Satin white, titanium dioxide, blancfixe.

Es hat sich nun gezeigt, daß ein gefälltes feinkörniges, überwiegend plättchenförmiges basisches Calcium-Magnesium-Carbonat, wie es nach dem Verfahren der Erfindung erhältlich ist, sich hervorragend als Masse-Zusatz und/oder als Streichpigment zur Herstellung von glänzenden Papieren eignet.It has now been shown that a precipitated fine-grained, predominantly platelet-shaped basic calcium magnesium carbonate, as it is after the process the invention is obtainable, is excellent as a mass additive and / or as a coating pigment suitable for the production of glossy papers.

Die Teilchen führen insbesondere dann zu einem sehr hohen Glanz des gestrichenen Papiers nach dem Trocknen, wenn diese plättchenförmig vorliegen. Der Vergleich zu einem mit Kaolin oder Satinweiß gestrichenen Papier zeigte hinsichtlieh Glanz eine verbesserte Qualität. Weitere Vorteile bei Verwendung des gefällten basischen Calcium-Magnesium-Carbonats liegen in der verbesserten Opazität und zugleich in der höheren Weiße des behandelten Papiers.In particular, the particles then lead to a very high gloss of the coated paper after drying, if they are in flake form. Of the A comparison with a paper coated with kaolin or satin white showed this Shine an improved quality. Further advantages of using the precipitated basic Calcium Magnesium Carbonate lie in the improved opacity and at the same time in the higher whiteness of the treated paper.

Bei einer vorteilhaften Ausführungsform der Erfindung beträgt die Feinheit des Calcium-Magnesium-Carbonats 100 % <l 1 /um.In an advantageous embodiment of the invention, the Fineness of the calcium magnesium carbonate 100% <l 1 / um.

Weiterhin ist es zweckmäßig, wenn die spezifische Oberfläche des Calcium-Magnesium-Carbonats in der Größenordnung von 2 20 m2/g liegt.It is also useful if the specific surface area of the calcium magnesium carbonate is of the order of 2 20 m2 / g.

Ferner ist von Vorteils wenn das basische Calcium-Magnesium-Carbonat einen Weißgrad > 95 % aufweist.It is also advantageous if the basic calcium magnesium carbonate has a whiteness> 95%.

Eine vorteilhafte Ausführungsform besteht in der Verwendung plättchenförmig gestalteter Calcium-Magnesium-Carbonatteilchen mit einem Shape-Faktor, der um eine Zehnerpotenz größer als bei Kaolin ist.An advantageous embodiment consists in the use of flakes designed calcium-magnesium-carbonate particles with a shape factor that is one Power of ten is greater than that of kaolin.

Die Erfindung ist im nachstehenden anhand von Ausführungsbeispielen näher erläutert.The invention is described below on the basis of exemplary embodiments explained in more detail.

Beispiel 1 0 Dolomit wird in einem Drehofen auf etwa 1100 C erhitzt, wodurch ein CaO-MgO-Gemisch erhalten wird. Dieses Oxidgemisch wird mit Wasser etwa im Gewichtsverhältnis 1 : 20 gelöscht und bei gleichzeitigem intensiven Durchmischen mit den im Drehofen entstandenen gereinigten Abgasen zu einem basischen Calcium-Magnesium-Carbonat recarbonisiert. Die danach etwa 8 % Feststoff enthaltene Suspension wird über eine Zentrifuge eingeengt oder bei Durchgang durch eine Filterpresse konzentriert. Nach Zugabe eines Dispergiermittels wird eine stabile Suspension erhalten.Example 1 0 dolomite is heated in a rotary kiln to around 1100 C, whereby a CaO-MgO mixture is obtained. This oxide mixture is mixed with water approximately deleted in a weight ratio of 1:20 and with simultaneous intensive mixing with the cleaned exhaust gases produced in the rotary kiln to form a basic calcium-magnesium-carbonate recarbonized. The suspension then contained about 8% solids is via a Centrifuge concentrated or concentrated on passage through a filter press. To A stable suspension is obtained by adding a dispersant.

Beispiel 2 Ein durch Brennen von Dolomit erhaltenes CaO-MgO-Gemisch wird nach Zugabe von 5 ffi Ca0 gelöscht. Die Recarbonisierung des Ca0 ùnd MgO erfolgt während des Umpumpens mit einer Umwälzpumpe durch Zugabe von CO2> wobei eine besonders gute Absorption erfolgt. Nach Einengung der Suspension über eine Filterpresse wird durch Zugabe von Dispergiermittel eine stabile Suspension erhalten.Example 2 A CaO-MgO mixture obtained by burning dolomite is quenched after adding 5 ffi Ca0. The Ca0 and MgO are re-carbonised while pumping with a circulation pump by adding CO2> whereby a particularly good absorption takes place. After the suspension has been concentrated using a filter press a stable suspension is obtained by adding dispersing agent.

In beiden Beispielen fällt dabei das basische Calcium-Magnesium-Carbonat zum überwiegenden Teil in plättchenförmiger Struktur an.In both examples the basic calcium-magnesium-carbonate falls predominantly in a platelet-shaped structure.

Beispiel 3 Zur Gewinnung von basischem Magnesiumoarbonat geht man im einzelnen wie folgt vor: Zunächst wird Dolomit auf Temperaturen von etwa 10000 C erhitzt, wobei Kohlendioxid entweicht und ein Gemisch von CaO mit MgO zurückbleibt. Nach dem Löschen wird in die Suspension nach Verdünnung auf etwa 1 T. CaO/MgO : 60 T. Wasser bei Temperaturen < 500 C Kohlendioxid eingeleitet, wobei CaCO5 ausfällt. Mit Hilfe von Zentrifugen oder Filtern wird dann das gefällte CaCO) abgetrennt und auf diese Weise aus der Suspension ein Filtrat verhalten, aus dem durch Erhitzen auf 70 bis 8o0C mit einer Aufheizgeschwindigkeit von mindestens 10°/min ein plättchenförmpges basisches Magnesiumcarbonat mit hohem Shapefaktor ausfällt. Das Produkt kann dann aus der Suspension durch eine mechanische und/oder thermische Entwässerung o.ä. nach dem Trocknen gewonnen werden.Example 3 Basic magnesium carbonate is obtained in detail as follows: First, dolomite is heated to temperatures of about 10,000 C heated, carbon dioxide escapes and a mixture of CaO with MgO remains. After extinguishing, after dilution to about 1 T. CaO / MgO, the following is added to the suspension: 60 T. water introduced at temperatures <500 C carbon dioxide, whereby CaCO5 precipitates. With the help of centrifuges or filters, the precipitated CaCO2 is then separated off and In this way from the suspension a filtrate behave, from which by heating a platelet-shaped pges to 70 to 8o0C with a heating rate of at least 10 ° / min basic magnesium carbonate with a high shape factor precipitates. The product can then from the suspension by mechanical and / or thermal dewatering or the like. can be obtained after drying.

Claims (9)

Patentansprüche Verfahren zur Herstellung von Carbonaten des Calciums oder/und Magnesiums, dadurch gekennzeichnet, daß man den Dolomit durch Erhitzen auf etwa 1000 bis etwa 1100 cc in ein Gemisch von Calciumoxid und Magnesiumoxid umwandelt, das erhaltene Oxidgemisch im Gewichtsverhältnis von wenigstens 20 eilen Wasser auf 1 Peil Oxide in Wasser suspendiert und die dabei in der Suspension gebildeten Hydroxide durch Einleiten von Kohlendioxid in die entsprechenden Carbonate zurückverwandelt.Process for the production of carbonates of calcium and / or magnesium, characterized in that the dolomite is heated to about 1000 to about 1100 cc in a mixture of calcium oxide and magnesium oxide converts, the oxide mixture obtained in a weight ratio of at least 20 hurry Suspended water to 1 Peil Oxide in water and the thereby formed in the suspension Hydroxides are converted back into the corresponding carbonates by introducing carbon dioxide. 2. Verfahren nach Anspruch 1, dadurch gekennzeichnet. daß natürlicher Dolomit als Ausgangsmaterial verwendet wird.2. The method according to claim 1, characterized. that more natural Dolomite is used as the starting material. 3. Verfahren nach Anspruch 1 oder 2, dadurch gekennzeichnet. daß die Kalzinierung des Dolomits in einem Drehofen durchgeführt wird.3. The method according to claim 1 or 2, characterized. that the Calcination of the dolomite is carried out in a rotary kiln. 4. Verfahren nach Anspruch 1 - 3, dadurch gekennzeichnet, daß zur Wiederbegasung reines C02 oder C02-N2-Gemische, insbesondere die Abgase aus dem Drehofen verwendet werden.4. The method according to claim 1-3, characterized in that for Re-gassing of pure C02 or C02-N2 mixtures, especially the exhaust gases from the Rotary kiln can be used. 5. Verfahren zur Herstellung von basischem Calcium-Magnesium-Carbonat nach einem der Ansprüche 1 - 4, dadurch gekennzeichnet, daß man Dolomit kalziniert, das Produkt ablöscht und in Wasser im Gewichtsverhältnis von 20 - 60 Teilen Wasser auf 1 Teil Oxide suspendiert und die Suspension nach der Begasung mit Kohlendioxid einengt.5. Process for the production of basic calcium magnesium carbonate according to one of claims 1 - 4, characterized in that dolomite is calcined, the product extinguishes and in water in a weight ratio of 20-60 parts of water suspended to 1 part of oxides and the suspension after fumigation with carbon dioxide constricts. 6. Verfahren nach Anspruch 1 - 5, dadurch gekennzeichnet, daß die nach dem Löschen erhaltene Suspension über Zentrifugen oder Filterpressen eingeengt wird.6. The method according to claim 1-5, characterized in that the suspension obtained after extinguishing concentrated using centrifuges or filter presses will. 7. Verfahren nach Anspruch 1 - 6, dadurch gekennzeichnet, daß dem Ausgangsstoff zusätzlich gefälltes Calciumcarbonat und/oder Magnesiumcarbonat beigemischt werden. 7. The method according to claim 1-6, characterized in that the Starting material additionally precipitated calcium carbonate and / or magnesium carbonate are added will. 8. Verfahren nach Anspruch 1 - 7, dadurch gekennzeichnet, daß vor oder während des Löschens CaO und/oder MgO und/oder Ca(OH)2 und/oder Mg(OH)2 und/oder CaCO und/oder MgCO5 5 beigegeben werden. 8. The method according to claim 1-7, characterized in that before or during the extinguishing CaO and / or MgO and / or Ca (OH) 2 and / or Mg (OH) 2 and / or CaCO and / or MgCO5 5 are added. 9. Verfahren nach Anspruch 1 - 8, dadurch gekennzeichnet, daß durch Zugabe eines Dispergiermittels nach der Einengung der Suspension über Zentrifugen oder Filterpressen in Mischern eine stabile Suspension mit hohem Feststoffgehalt hergestellt wird. 9. The method according to claim 1-8, characterized in that by Addition of a dispersant after the suspension has been concentrated using centrifuges or filter presses in mixers a stable suspension with a high solids content will be produced. 10. Verfahren nach einem der Ansprüche 1 bis 4 zur Herstellung von basischem Magnesiumcarbonat, dadurch gekennzeichnet, daß man Dolomit kalziniert, das Produkt ablöscht und in Wasser im Gewichtsverhältnis von etwa 60 Teilen Wasser auf 1 Teil Oxide suspendiert, das ungelöste Calciumcarbonat abfiltriert und die Lösung mit einer Aufheizgeschwindigkeit von mindestens 10 O/min auf Temperaturen zwischen 70 und 80 0" erhitzt, bis das basische Magnesiumcarbonat ausgefällt ist.10. The method according to any one of claims 1 to 4 for the production of basic magnesium carbonate, characterized in that dolomite is calcined, the product extinguishes and in water in the weight ratio of about 60 parts of water suspended to 1 part of oxides, the undissolved calcium carbonate filtered off and the Solution with a heating rate of at least 10 O / min to temperatures between 70 and 80 0 "heated until the basic magnesium carbonate has precipitated. 11. Verfahren nach Anspruch 10, dadurch gekennzeichnet, daß vor dem Einleiten von Kohlendioxid die Suspension auf 1 T. CaO/MgO : 60 T. Wasser verdünnt wird.11. The method according to claim 10, characterized in that before Introducing carbon dioxide, dilute the suspension to 1 part of CaO / MgO: 60 parts of water will. 12. Verfahren nach einem der Ansprüche 10 oder 11, dadurch gekennzeichnet, daß zum Ausfällen von CaCO Kohlendioxid 5 bei Temperaturen a: 50 oC eingeleitet wird.12. The method according to any one of claims 10 or 11, characterized in that that initiated the precipitation of CaCO carbon dioxide 5 at temperatures a: 50 oC will. 15. Verfahren nach einem der Ansprüche 10 oder 11, dadurch gekennzeichnet, daß das Calciumcarbonat aus der Suspension abgetrennt wird.15. The method according to any one of claims 10 or 11, characterized in that that the calcium carbonate is separated from the suspension. 14. Verfahren nach einem der Ansprüche 10 - 13, dadurch gekennzeichnet, daß nach Ausfällen des basischen MgCO5 dieses durch Einengen der Suspension z;B. durch Zentrifugieren angereichert wird.14. The method according to any one of claims 10-13, characterized in that that after the basic MgCO5 has precipitated, this can be achieved by concentrating the suspension, for example. is enriched by centrifugation. 15. Verfahren nach einem der Ansprüche 10 - 14, dadurch gekennzeichnet, daß basisches MgCO) nach dem Abfiltrieren getrocknet wird.15. The method according to any one of claims 10-14, characterized in that that basic MgCO) is dried after filtering off. 16. Verwendung eines gefällten basischen überwiegend plättchenförmigen Calcium-Magnesium-Carbonats als Füllstoff und/oder Streichpigment zur Herstellung von glänzenden Papieren in der Papierindustrie.16. Use of a precipitated basic, predominantly platelet-shaped Calcium magnesium carbonate as a filler and / or coating pigment for production of glossy papers in the paper industry. 17. Verwendung eines Calcium-Magnesium-Carbonats nach Anspruch 16, dadurch gekennzeichnet, daß die Feinheit des Calcium-Magnesium-Carbonats 100 ffi 4 l /um beträgt.17. Use of a calcium-magnesium carbonate according to claim 16, characterized in that the fineness of the calcium-magnesium carbonate 100 ffi 4 l / µm. 18. Verwendung eines Calcium-Magnesium-Carbonats nach Anspruch 16 oder 17, dadurch gekennzeichnet, daß die spezifische Oberfläche des Calcium-Magnesium-Carbonats in der Größenordnung von 20 m2/g liegt.18. Use of a calcium-magnesium carbonate according to claim 16 or 17, characterized in that the specific surface of the calcium-magnesium carbonate is of the order of 20 m2 / g. 19. Verwendung eines Calcium-Magnesium-Carbonats nach einem der Ansprüche 17 - 18, dadurch gekennzeichnet, daß plättchenförmig gestaltete Calcium-Magnesium-Carbonatteilchen mit einem Shape-Faktor eingesetzt werden, der um eine Zehnerpotenz größer als bei Kaolin ist.19. Use of a calcium-magnesium carbonate according to one of the claims 17-18, characterized in that calcium-magnesium-carbonate particles of platelet shape can be used with a shape factor that is a power of ten greater than Kaolin is. 20. Verwendung eines Calcium-Magnesium-Carbonats nach einem der Ansprüche 17 - 19, dadurch gekennzeichnet, daß das basische Calcium-Magnesium-Carbonat einen WeiBgrad > 95 % aufweist.20. Use of a calcium-magnesium carbonate according to one of the claims 17-19, characterized in that the basic calcium-magnesium carbonate a Whiteness> 95%.
DE19762600485 1975-01-21 1976-01-08 Calcium and magnesium carbonates suitable for paper mfr - made by feeding carbon dioxide into aq suspension of calcined dolomite Withdrawn DE2600485A1 (en)