DE2415652A1 - Self extinguishing safety candle - with wick lower end impregnated with organic polymer checking suction power of wick - Google Patents
Self extinguishing safety candle - with wick lower end impregnated with organic polymer checking suction power of wickInfo
- Publication number
- DE2415652A1 DE2415652A1 DE2415652A DE2415652A DE2415652A1 DE 2415652 A1 DE2415652 A1 DE 2415652A1 DE 2415652 A DE2415652 A DE 2415652A DE 2415652 A DE2415652 A DE 2415652A DE 2415652 A1 DE2415652 A1 DE 2415652A1
- Authority
- DE
- Germany
- Prior art keywords
- wick
- candle
- impregnated
- organic polymer
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
Selbsttätig erlöschende Kerze Gegenstand der Erfindung ist eine selbsttätig erlöschende Kerze, deren Doeht an seinem unteren Ende in der Weise imprägniert ist, daß die Flamme kurz vor dem völligen Abbrennen der Kerze erlischt. Automatically extinguishing candle The subject of the invention is an automatically extinguishing candle, the doeht of which is impregnated at its lower end in such a way, that the flame goes out shortly before the candle burns down completely.
Ohne Aufsicht brennende Kerzen stellen ein nicht unerhebliches Gefahrenmoment dar, sobald die Kerze bis zu ihrem Ende heruntergebrannt ist. Abgesehen davon, daß kostbare Porzellan- oder Glasleuchter zerspringen können, besteht vor allem eine erhebliche Brandgefahr, wenn die Kerze auf einer brennbaren Unterlage befestigt ist oder durch das Umfallen des brennenden Dochtendes benachbarte Trennende Gegenstände in Brand gesetzt werden können.Candles burning without supervision represent a not inconsiderable moment of danger as soon as the candle has burned down to its end. Besides that precious porcelain or glass candlesticks can shatter, there is above all one Significant fire hazard if the candle is attached to a flammable surface or adjacent separating objects due to the burning wick falling over can be set on fire.
Diese Gefahr tritt besonders häufig bei Advents- oder Weihnachtsbaumkerzen auf.This danger occurs particularly often with Advent or Christmas tree candles on.
Aufgabe der Erfindung ist es, eine Kerze zu entwickeln, die selbsttätig vor dem völligen Abbrand erlischt. Diese Aufgabe wird gelöst durch eine Kerze, deren Docht an seinem unteren Ende mit einem die Saugfähigkeit des Dochtes aufhebenden organischen Polymeren imprägniert istfelches bei der Temperatur der geschmolzenen Kerzenmasse ur.schmelzbar und in der Kerzenase unlöslich ist.The object of the invention is to develop a candle that works automatically goes out before it is completely burned off. This task is solved by a candle whose Wick at its lower end with a wick that removes the absorbency of the wick organic polymers is impregnated at the temperature of the melted Candle mass is unmeltable and insoluble in the candle nose.
Als Imprägniermittel eignen sich organische Polymere, die auf das Dochende in gelöster, dispergierter oder geschmolzener Form oder als^Vorkondensate aufgebracht und gegebenenfalls durch eine thermische Nachbehandlung unlösbar und unschmelzbar fixiert werden können. Sie müssen imstande sein, in das Dochtmaterial einzudringen und durch Ausfüllung der Poren und Faserzwischenräume die Saugfähi;:keit des Dochtes aufzuheben. Diese Eigenschaft muß auch in unmittelbarer Nähe der Flamme innerhalb der geschmolzenen Kerzenmasse erhalten bleiben. Das Imprägniermittel soll daher in der geschmolzenen Kerzenmasse unlöslich und entweder unschmelzbar sein oder einen ausreichend hohen Schmelzpunkt oberhalb der Temperatur der geschmolzenen Kerzenmassen in unmittelbarer Flamennäe besitzen. Es nat sich gezeigt, daß der Schmelzpunkt des Imprägniermittels oberhalb von loo° C liegen muß, wenn die gewünschten Eigenschaften erreicht werden sollen.Organic polymers based on the Wick ends in dissolved, dispersed or molten form or as ^ precondensates applied and possibly insoluble and by a thermal aftertreatment infusibly fixed can be. You need to be able to penetrate the wick material and by filling the pores and interstices between the fibers the absorbency of the wick. This property must also be immediate Maintain close proximity to the flame within the melted candle mass. The impregnating agent should therefore be insoluble and either infusible in the melted candle mass be or a sufficiently high melting point above the temperature of the molten Have candle masses in the immediate vicinity of the flame. It has been shown, of course, that the melting point of the impregnating agent must be above 100 ° C if the desired properties should be achieved.
Als "unschmelzbart' im Sinne der Erfindung werden auch solche Imprägniermittel verstanden, die lediglich erweichen, wobei die Viskosität aber so hoch bleibt, daß ein Aufsteigen im brennenden Docht verhindert wird.Such impregnating agents are also considered to be "infusible" for the purposes of the invention understood that only soften, but the viscosity remains so high that a rise in the burning wick is prevented.
Es hat sich gezeigt, daß Imprägnierungen allein mit anorganischen Salzen diese Bedingungen nicht erfüllen können, da durch die Kristallisation der Salze die Porosität des Dochtes nicht genügend aufgehoben wird.It has been shown that impregnations only with inorganic Salts cannot meet these conditions because of the crystallization of the Salt will not sufficiently break the porosity of the wick.
Geeignete Imprägniermittel im Sinne der Erfindung, die in geschmolzener Form oder als härtbare Vorkondensate auf das Dochtmaterial aufgebracht werden können, sind z.B. thermoplastische Polymere, wie Polyäthylen, Polypropylen, Polyvinylchlorid, Polyvinylacetat, Poly-(meth)-acrylsäureester, sowie deren Copolymere, wie sie z.B. als Schmelzkleber in der Verklebungstechnik verbreitete Anwendung finden, ferner Harnstoff- und Melaminharze, Phenoplaste u. dgl.. Die Polymeren werden als Pulver oder Granulat oder als Folie auf das Dochtende aufgebracht und durch Temperatureinwirkung eingeschmolzen bzw. gehärtet.Suitable impregnating agents for the purposes of the invention, which are in molten Can be applied to the wick material in the form or as hardenable precondensates, are e.g. thermoplastic polymers such as polyethylene, polypropylene, polyvinyl chloride, Polyvinyl acetate, poly (meth) acrylic acid esters, and their copolymers, as e.g. also find widespread use as hot melt adhesives in bonding technology Urea and melamine resins, phenoplasts and the like .. The polymers are supplied as powders or granules or as a film applied to the end of the wick and by the action of temperature melted down or hardened.
Weiterhin sind solche Polymere geeignet, die in Form von wäßrigen oder organischen Lösungen oder Dispersionen auf das Dochtmaterial aufgetragen werden können und dieses in ausreichend kurzer Zeit durchdringen und ausfüllen. Beispiele hierfür sind wäßrige oder organische Lösungen oder Dispersionen von Polyvinylacetat, Poly-(meth)-acrylsäureestern, Harnstoff- oder Melaminharzen,-Polyvinylchlorid, Kautschuk, Polychloropren, Butadien-Acrylnitril-Mischpolymerisaten, Silikonen oder von natürlichen Polymeren, wie Eiweiß, Stärke, Harze, Gummen und dgl. Gegebenenfalls empfiehlt sich auch hier eine zusätzliche thermische Nachbehandlung zur besseren Härtung oder Fixierung.Furthermore, those polymers are suitable in the form of aqueous or organic solutions or dispersions are applied to the wick material can and penetrate and fill this in a sufficiently short time. Examples these are aqueous or organic solutions or dispersions of polyvinyl acetate, Poly (meth) acrylic acid esters, urea or melamine resins, polyvinyl chloride, rubber, Polychloroprene, butadiene-acrylonitrile copolymers, silicones or natural ones Polymers, such as egg white, starch, resins, gums and the like. If necessary, it is recommended Here, too, an additional thermal post-treatment for better hardening or fixing.
Zur Verbesserung der Benetzungsfähigkeit und Eindringgeschwindigkeit derartiger Lösungen oder Dispersionen können Netzmittel, wie höhere Fettalkoholsulfate, Alkylsulfonate, Alkylbenzolsulfonate, SulfobernsteinsSureester, Alkylenoxidaddukte an höhere Fettalkohole und Fettsäuren oder dgl. zugesetzt werden. Als organische Lösungsmittel kommen Benzine, halogenierte Kohlenwasserstoffe, Alkohole, Glykole, Ketone oder dgl. in Betracht, doch werden wäßrige Lösungen oder Dispersionen aus praktischen Gründen bevorzugt.To improve the wettability and penetration speed such solutions or dispersions may include wetting agents such as higher fatty alcohol sulfates, Alkyl sulfonates, alkylbenzenesulfonates, sulfosuccinic acid esters, alkylene oxide adducts to higher fatty alcohols and fatty acids or the like. Be added. As organic Solvents come benzines, halogenated hydrocarbons, alcohols, glycols, Ketones or the like are possible, but aqueous solutions or dispersions are made preferred for practical reasons.
Zur Herabsetzung der Brennbarkeit oder zur Verbilligung können den Polymeren weiterhin anorganische Füllstoffe, wie Metallsalze, -oxide oderhydroxide, beispielsweise, Zinkchlorid oder Aluminiumchlorid, Kieselsäure, Silikate oder dgl. zugesetzt werden.To reduce the flammability or to make it cheaper, the Polymers furthermore inorganic fillers, such as metal salts, oxides or hydroxides, for example, zinc chloride or aluminum chloride, silica, silicates or the like. can be added.
Die Imprägnierung erfolgt am Dochtende in einer Länge von etwa o,5 bis 2 cm, vorzugsweise etwa 1 cm. Dadurch wird ein sicheres Erlöschen der Flamme vor dem vollständigen Abbrennen der Kerze erreicht.The impregnation takes place at the end of the wick in a length of about 0.5 to 2 cm, preferably about 1 cm. This will safely extinguish the flame reached before the candle burns down completely.
Die Imprägnierung kann ohne Schwierigkeiten bei der Kerzenherstellung nach dem Tauch- oder Gießverfahren aufgebracht werden. Sie erfolgt beispielsweise durch Eintauchen der geschnittenen Dochte in eine Lösung oder Dispersion des Imprägniermittels oder während des Gießvorganges an der Gießmaschine unmittelbar vor dem Einziehen des Dochtes in die Gießform. Im letzteren Falle kann das Aufschmelzen eines thermoplastischen Polymeren in Folien- oder Pulverform besonders vorteilhaft sein. Bei der Herstellung der Kerzen im Gießverfahren ist darauf zu achten, daß das Imprägniermittel den Docht nicht verformt oder verhärtet, damit das Einziehen in die Gießform keine Schwierigkeiten bereitet.The impregnation can be done without any difficulties in candle making can be applied by dipping or pouring. It takes place, for example by dipping the cut Wicks into a solution or dispersion of the impregnating agent or directly on the casting machine during the casting process before pulling the wick into the mold. In the latter case, the melting can take place a thermoplastic polymer in film or powder form is particularly advantageous be. When manufacturing the candles in the casting process, it is important to ensure that the impregnating agent does not deform or harden the wick so that it can be drawn in in the mold does not cause any difficulties.
Vorzugsweise werden aus diesem Grunde thermoplastische Polymere, wie Polypropylen, Polyvinylchlorid, Polyvinylacetat, Poly(meth)acrylate, Kautschuk, Polychloropren, Butadien-Acrylnitril-Mischpolymere oder Silikone als Lösungen, Dispersionen,oder in Pulver- oder Folienform verwendet.For this reason, thermoplastic polymers such as Polypropylene, polyvinyl chloride, polyvinyl acetate, poly (meth) acrylate, rubber, Polychloroprene, butadiene-acrylonitrile copolymers or silicones as solutions, dispersions, or used in powder or foil form.
Zur Markierung des imprägnierten Abschnittes kann das Imprägniermittel einen Farbstoffzusatz erhalten. Dieser Farbstoffzusatz sollte in der geschmolzenen Kerzenmasse unlöslich sein, um Verfärbungen des unteren Kerzabschnittes zu vermeiden.The impregnating agent can be used to mark the impregnated section receive a dye additive. This dye additive should be in the melted Candle mass must be insoluble in order to avoid discoloration of the lower part of the candle.
Geeignete Farbstoffe sind z. B. organische oder anorganisnhe Pigmentfarben; jedoch lassen sich auch lipoidlösliche Farbstoffe verwenden, wenn sie von der Imprägnierungsmasse ausreichend gebunden werden.Suitable dyes are e.g. B. organic or inorganic pigment colors; however, lipoid-soluble dyes can also be used if they are removed from the impregnation mass be adequately bound.
Die Erfindung läßt sich auf alle Arten von Kerzen aus Paraffinen, Stearinen, Wachsen oder deren Mischungen anwenden. Sie ist nicht an das Herstellungsverfahren für die Kerzen gebunden, obwohl sie sich insbesondere für das Tauch-und das Gießverfahren eignet.The invention can be applied to all types of candles made from paraffins, Use stearins, waxes or their mixtures. She is not involved in the manufacturing process tied for the candles, although they are particularly suitable for the dipping and the pouring process suitable.
Beispiel 1 Ein Flachdocht der Stärke 3 x 12 mm wird ca. 3 cm vom unteren Ende über eine Länge von ca. 1 cm mit einer Dispersion von Polyvinylacetat (50 %ig) imprägniert und getrocknet. Eine mit diesem Docht hergestellte Stearinkompositionskerze von 24 mm Durchmesser brennt bis zur imprägnierten Zone völlig gleichmäßig ab, dann verkleinert sich die Flamme rasch, um nach wenigen Minuten zu erlöschen.Example 1 A flat wick with a thickness of 3 x 12 mm is approx. 3 cm from the bottom End over a length of approx. 1 cm with a dispersion of polyvinyl acetate (50%) impregnated and dried. A stearin composition candle made with this wick with a diameter of 24 mm burns completely evenly up to the impregnated zone, then the flame shrinks quickly to go out after a few minutes.
Beispiel 2 Wie unter Beispiel 1 beschrieben, wird ein Docht mit einer handelsüblichen Butylkautschuklösung in Benzin imprägniert.Example 2 As described in Example 1, a wick with a commercial butyl rubber solution impregnated in gasoline.
Die Flamme erlischt mit Sicherheit beim Erreichen der imprägnierten Zone.The flame will certainly go out when it reaches the impregnated Zone.
Beispiel 3 Vor dem Einziehen in die Gießmaschine wird an die vorgesehenen Dochtenden über eine Zuführvorrichtung eine 1 cm breite Polypropylenfolie von 0,1 mm Stärke angelegt und durch Anpressen einer geheizten etallfläche eingeschmolzen. Durch geeignete Anpassung der Preßform an den Dochtdurchmesser wird vermieden, daß der Docht verformt wird und beim Einziehen des Dochtendes durch die Führung der Gießform Schwierigkeiten auftreten.Example 3 Before it is drawn into the casting machine, the intended Wick ends a 1 cm wide polypropylene film of 0.1 via a feeder mm thick and melted down by pressing a heated metal surface. By suitable adaptation of the mold to the wick diameter, it is avoided that the wick is deformed and when the wick end is drawn in by the guidance of the Mold difficulties arise.
Beispiel 4 Es wird wie in Beispiel 3 gearbeitet, lediglich mit dem Unterschied, daß anstelle der Folie eine wäßrige Dispersion von Polyvinylacetat (50 %ig),oder eines Melamin-Formaldehyd-Harzes (60 %ig), oder eines Polyvinylchlorid-Plastisols in Dioctylphthalat (40 %ig) zur Imprägnierung der vorgesehenen Dochtenden verwendet wird. Nach dem Aufbringen der Imprägnierung wird ca. 20 Sekunden auf 200°C erhitzt.Example 4 The procedure is as in Example 3, only with the The difference is that instead of the film, an aqueous dispersion of polyvinyl acetate (50%), or a melamine-formaldehyde resin (60%), or a polyvinyl chloride plastisol in dioctyl phthalate (40%) used to impregnate the intended wick ends will. After the impregnation has been applied, the mixture is heated to 200 ° C for approx. 20 seconds.
Auch hiermit wird ein einwandfreies Ergebnis erhalten, ohne daß Störungen beim Einziehen des Dochtes in die Gießform entstehen.This also gives a perfect result without disturbances arise when the wick is drawn into the mold.
Claims (6)