DE2110579A1 - Paper mouldings - prepd from shredded paper impregnated with pf or uf resin - Google Patents
Paper mouldings - prepd from shredded paper impregnated with pf or uf resinInfo
- Publication number
- DE2110579A1 DE2110579A1 DE19712110579 DE2110579A DE2110579A1 DE 2110579 A1 DE2110579 A1 DE 2110579A1 DE 19712110579 DE19712110579 DE 19712110579 DE 2110579 A DE2110579 A DE 2110579A DE 2110579 A1 DE2110579 A1 DE 2110579A1
- Authority
- DE
- Germany
- Prior art keywords
- resin
- paper
- weight
- shredded paper
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
Pormkörper und Verfahren zu seiner Herstellung -Die Erfindung betrifft einen Formkörper, insbesondere für Kraftfahrzeuginnenverkleidung Behälter aller Art, Spielzeug, Möbel und Verpakungen. Pormkörper and process for its production -The invention relates a molded body, especially for motor vehicle interior trim containers of all Art, toys, furniture and packaging.
Es ist bereits bekannt, Holzfasern mit wärmehärtendem Bindemittel zu imprägnieren und zu Formkörpern heiß zu verpressen.It is already known to use wood fibers with thermosetting binders to be impregnated and hot-pressed to moldings.
Ein Nachteil derartiger Formkörper besteht darin, daß sie eine relativ große Menge an Harzbindemittel erfordern, die Herstellung der Holzschnitzel selbst relativ aufwendig und teuer ist und die für gleichmäßige Eigenschaften des Formteils erforderliche gleichmäßige Größe der Holzschnitzel nicht einfach zu erreichen ist. Auch ist der Bedarf an Holz schwer zu decken.A disadvantage of such molded bodies is that they are a relatively Requiring large amount of resin binder to make the wood chips themselves is relatively complex and expensive and for uniform properties of the molded part required uniform size of the wood chips is not easy to achieve. The demand for wood is also difficult to meet.
Aufgabe der Erfindung ist es daher, ein billigeres, im Überfluß vorhandenes Material für derartige Formkörper zur Yerfü.gung zu stellen, den erforderlichen Harzgehalt zu verringern und die Gleichmäßigkeit der Eigenschaften des Formkörpers zu verbessern.The object of the invention is therefore to provide a cheaper, abundant one To provide material for such shaped bodies to Yerfü.gung, the necessary Reduce resin content and improve the uniformity of properties of the molded article to improve.
Erfindungsgemäß wird diese Aufgabe gelöst durch einen Formkörper, der aus unter Anwendung von Hitze und Druck verpreßten Papierschnitzeln mit einen Gehalt von 7 bis 40, vorzugsweise 8 bis 20 Cew.-, Phenol-Formaldehydharz oder Harnstoff-Formaldehydharz und gegebenenfalls fl bs 2 Gew. -% Paraffin, bezogen auf trockene Papierschnitzel, besteht und gegebenenfalls auf der Oberfläche eine Dekorfolie aufweist.According to the invention, this object is achieved by a molded body, pressed from using heat and pressure Shredded paper with a content of 7 to 40, preferably 8 to 20 Cew., phenol-formaldehyde resin or urea-formaldehyde resin and optionally fl to 2% by weight paraffin, based on dry shredded paper, and if necessary on the surface a Has decorative film.
Die Papierschnitzel weisen vorzugsweise eine längliche Form auf und haben zweckmäßig ein Verhältnis von Länge zu Breite zwischen 10 und 1,5:1. Besonders geeignet sind Altpapierschnitzel, wie sie beispielsweise bei Anwendung der üblichen Aktenschneider anfallen. Besonders gute Ergebnisse wurden mit Schnitzeln aus Natronpapier erzielt. Es ist aber naturlich ebenso möglich, ungebrauchtes Papier für die Schnitzel herstellung heranzuziehen. Aus Wirtschaftlichkeitsgründen werden jedoch Altpapierschnitzel bevorzugt.The shredded paper preferably has an elongated shape and suitably have a length to width ratio between 10 and 1.5: 1. Particularly scraps of waste paper, such as those used, for example, when the customary ones are used, are suitable File cutter incurred. Particularly good results were achieved with chips made from baking soda paper achieved. It is of course also possible to use unused paper for the schnitzel manufacture to use. For reasons of economy, however, scraps of waste paper are used preferred.
Die Erfindung ist jedoch nicht auf längliche Papierschnitzel beschränkt. Es können an sich Papierschnitzel jeder Form verwendet werden. Längliche Schnitzel weisen jedoch eine überlegene Ziehfähigkeit in der Presse auf.However, the invention is not limited to elongated shredded paper. As such, shredded paper of any shape can be used. Elongated schnitzel however, have superior in-press drawability.
Die Herstellung des erfindungsgemäßen Formkörpers erfolgt so, daß die Papierschnitzel mit einer Harzflotte in der zur Brzielung des gewünschten Harzgehalts erforderlichen Menge behandelt und dann unter den zur Aushärtung des Harzes erforderlichen Bedingungen verpreßt werden. Vorzugsweise wird bei einer Temperatur zwischen 150 und 180°C sowie einem Druck zwischen 50 und 500 kg/cm2 verpreßt Zur Herstellung der harzimprägnierten Papierschnitzel können die trockenen Papierteilchen mit der Harzflotte besprüht oder in sonstiger Weise behandelt werden, beispielsweise durch Eintauchen. Besonders zweckiiiäßig ist ein Aufsprühen der Harzflotte auf die Papierschnitzel in einer Mischtrommel.The molding according to the invention is produced in such a way that the shredded paper with a resin liquor in order to achieve the desired resin content Treated the required amount and then below that required to cure the resin Conditions to be pressed. Preferably at a temperature between 150 and 180 ° C and a pressure between 50 and 500 kg / cm2 for production the resin-impregnated paper shredded the dry paper particles with the Resin liquor sprayed or otherwise treated, for example by Immersion. It is particularly useful to spray the resin liquor onto the shredded paper in a mixing drum.
Die Harzflotte weist vorzugsweise einen Harzgehalt von etwa 6 bis i2 Gew.-% sowie einen Gehalt an emulgiertem Paraffin zwischen 0,5 und 1,5 Gew.-% auf. Auf 100 Gew.-Teile Papierschnitzel werden zweckmäßig 100 bis 150 Gew.-Teile einer derartigen Harzflotte aufgebracht.The resin liquor preferably has a resin content of about 6 to i2% by weight and an emulsified paraffin content between 0.5 and 1.5% by weight on. For 100 parts by weight of shredded paper, it is expedient to add 100 to 150 parts by weight applied to such a resin liquor.
Die mit Harz behandelten Papierschnitzel können unmittelbar nach der Hsrzbehandlung oder zu einem beliebigen späteren Zeitpunkt zum Formkörper verpreßt werden. Als Harze werden alkalisch kondensierte Harze aus Phenol bzw. Harnstoff und Formaldehyd bevorzugt. Derartige Harze sind handelsüblich in Form von etwa 40 bis 50%igen wäßrigen Lösungen.The shredded paper treated with resin can be used immediately after the Resin treatment or pressed at any later point in time to form the molded body will. Alkaline condensed resins made from phenol or urea are used as resins and formaldehyde preferred. Such resins are commercially available in the form of about 40 up to 50% aqueous solutions.
Bei der Herstellung des Forriikörpers selbst werden die imprägnierten Schnitzel zweckmäßig geringfügig unter Bildung einer Matte zusammengepreßt und dann in die Form gegeben. Alternativ hat sich auch ein Einblasen oder Einschütten der Schnitzel in die Pressform als zweckmässig erwiesen.During the manufacture of the molded body itself, the impregnated Schnitzel expediently slightly compressed to form a mat and then put in the form. Alternatively, the Schnitzel in the mold proved to be useful.
Um den erfindungsgemäßen Formkörper verschiedenen Verwendungsarten anzupassen, ist es möglich, die Oberfläche mit einer Dekorfolie zu überziehen. Zweckmäßig werden hierzu ziehfähige Folien, vorzugsweise aus Papier, verwendet, welche auf die Formlingoberfläche gebracht werden können, so daß zugleich mit dem Preßvorgang auch das gewünschte Oberflaehendekor hergestellt werden kann.To the molding according to the invention different types of use adapt, it is possible to cover the surface with a decorative film. Appropriate drawable films, preferably made of paper, are used for this purpose, which on the molding surface can be brought so that at the same time with the pressing process the desired surface decoration can also be produced.
Die erfindungsgemäßen Formkörper sind leicht herstellbar, wetterbeständig und insbesondere wasserbeständig und geräuschdämmend Die Eigenschaften lassen sich durch Wahl von Barzart und Harzmenge weitgehend variieren. Ein Teii des Phenol-Formaldehydharzes bzw. Harnstoff-Formaldehydharzes kann auch durch andere übliche damit verträgliche Harze ersetzt werden.The moldings according to the invention are easy to produce and weatherproof and in particular water-resistant and sound-absorbing The properties can be vary widely by choosing the type of resin and the amount of resin. Part of the phenol-formaldehyde resin or urea-formaldehyde resin can also be compatible with other customary Resins are replaced.
Die erzielten Festgkeitseigenschaften sind trotz Verwendung sehr geringer rengen, besonders bevorzugt 8 bis 1O?', den Eigenschaften von Formteilen, die aus olzschnitzeln bzw. Faser mit einem Gehalt von 15 bis 22 Gew.- % Harz hergestellt werden, mindestens gleichwertig, in vielen Fällen aber überlegen, insbesondere, wenn es auf die Zieheigenschaften beim Verpressen ankommt. Ein besonderer Vorteil der Erfindung ist auch darin zu sehen, daß ein äußerst billiges , in reichlicher Menge zur Verfügung stehendes Abfallprodukt, nämlich Altpapier, verwendet werden kann.The strength properties achieved are very poor in spite of their use narrow, particularly preferably 8 to 10? ', the properties of molded parts that wood chips or fiber with a content of 15 to 22% by weight Resin are produced, at least equivalent, but in many cases superior, especially when it comes to the drawing properties during pressing. A special The advantage of the invention is also to be seen in the fact that an extremely cheap, in abundant Amount of available waste product, namely waste paper, can be used can.
Die folgenden Beispiele erläutern die Erfindung weiter.The following examples further illustrate the invention.
B e i s O i e l 1 In einer Trommel wurden 100 Gew.-Teile Altpapierschnitzel mit einem durchschnittlichen Läne -zu-Breite-Verhältnis von etwa 2 bis 4:1 mit 120 Teilen einer Harzflotte folgender Zusammensetzung besprüht: 100 Gew.-Teile einer handelsüblichen wäßrigen lösung eines Phenol-Formaldehyd-Kondensationsprodukts; Trockengehalt 48%, davon 8% Festharz (Kaurezinleim 250) 12 Gew.-Teile einer 50 %igen Paraffinemulsion 8 Gew.-Teile Wasser Die besprühten Schnitzel wurden getrocknet (Festharzgehalt 8%) unter leichtem Druck zu einer Matte gepreßt und dann evtl. nach Auflegen einer Dekorfolie bei 160°C und 150 kg/cm2 Druck zu einer PKW - Seitenwand-Verkleidung verpresst. Der erhaltene Formkörper war für den beabsichtigten Verwendungszweck gut geeignet und wies insbesondere gute Wetterfestigkeit und Wasserfestigkeit auf.B e i s O i e l 1 100 parts by weight of scraps of waste paper were placed in a drum with an average length-to-width ratio of around 2 to 4: 1 with 120 Parts of a resin liquor sprayed with the following composition: 100 parts by weight of a commercial aqueous solution of a phenol-formaldehyde condensation product; Dry content 48%, of which 8% solid resin (Kaurezinleim 250) 12 parts by weight of a 50% Paraffin emulsion 8 parts by weight of water The sprayed chips were dried (Solid resin content 8%) pressed into a mat under slight pressure and then possibly afterwards Applying a decorative film at 160 ° C and 150 kg / cm2 pressure to a car side wall cladding pressed. The molded article obtained was for the intended use well suited and particularly had good weather resistance and water resistance.
Beispiel 2 100 Gew.-Teile Schnitzel von Natronaltpapier mit einem längeii-Breiten-Verhältnis von 7 bis 10:1 wurden mit 100 Gew.-Teilen einer Harzflotte imprägniert, die folgende Zusammensetzung aufwies: 110 Gew.-Teile einer handelsüblichen wäßrigen Lösung eines Phenol-Pormaldehyd-Kondensatiosprodukts mit einem Festharzgehalt von 8% (Kauresinleim 260) 10 Gew.-Teile einer Oien wäßrigen Wachsemulsion 10 Gew.-Teile Wasser Die imprägnierten Schnitzel wurden getrocknet und in eine mit einer Dekorfolie ausgelegte Form geblasen und bei einem Druck von 150 kg/cm2 und 1600C zu Formteilen verpresst.Example 2 100 parts by weight of chips of old soda paper with a Length to width ratio of 7 to 10: 1 were made with 100 parts by weight of a resin liquor impregnated, the following composition: 110 parts by weight a commercially available aqueous solution of a phenol-formaldehyde condensate product with a solid resin content of 8% (Kauresinleim 260) 10 parts by weight of an aqueous oil Wax emulsion 10 parts by weight of water The impregnated chips were dried and blown into a form lined with a decorative film and at a pressure of 150 kg / cm2 and 1600C pressed into molded parts.
Produkte etwa gleicher Eigenschaften, jedoch mit verminderter Wasserfestigkeit wurden erhalten, wenn anstelle des Phenol-Formaldehydharzes ein handelsübliches Harnstoff-Formaldehydharz verwendet wurde.Products with approximately the same properties, but with reduced water resistance were obtained when, instead of the phenol-formaldehyde resin, a commercially available one Urea-formaldehyde resin was used.
Desgleichen konnte die Wachsemulsion weggelassen werden. In diesem Fall war jedoch eine etwas längere Mischzeit beim Besprühen der Papierschnitzel erforderlich.The wax emulsion could also be omitted. In this The case, however, was a somewhat longer mixing time when spraying the shredded paper necessary.
Claims (7)