DE19640988C1 - Two-component polyurethane for shaping and smoothing chipboard, etc. edges without a mould - Google Patents

Two-component polyurethane for shaping and smoothing chipboard, etc. edges without a mould

Info

Publication number
DE19640988C1
DE19640988C1 DE1996140988 DE19640988A DE19640988C1 DE 19640988 C1 DE19640988 C1 DE 19640988C1 DE 1996140988 DE1996140988 DE 1996140988 DE 19640988 A DE19640988 A DE 19640988A DE 19640988 C1 DE19640988 C1 DE 19640988C1
Authority
DE
Germany
Prior art keywords
use according
viscosity
component polyurethane
smoothing
polyurethane system
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE1996140988
Other languages
German (de)
Inventor
Lothar Dr Thiele
Hans-Peter Kohlstadt
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Henkel AG and Co KGaA
Original Assignee
Henkel AG and Co KGaA
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Henkel AG and Co KGaA filed Critical Henkel AG and Co KGaA
Priority to DE1996140988 priority Critical patent/DE19640988C1/en
Priority to EP97910390A priority patent/EP0929587A1/en
Priority to PCT/EP1997/005350 priority patent/WO1998015586A1/en
Application granted granted Critical
Publication of DE19640988C1 publication Critical patent/DE19640988C1/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

Disclosed is the use of a two-component polyurethane system for smoothing porous edges of boards, especially chip board, fibre board or plywood. The two-component system is characterized by a high viscosity of 150-350 Pas at 20 DEG C when measured by the Bookfield Viscometer RVT or by the fact that viscosity rises within 5-15 seconds at 20 DEG C to such a high value (thixotropria structure) that less than 0.5mm of a 5mm polyurethane coating does not run from a vertical chip board, fibre board or plywood board. Due to the relatively high viscosity, processing is possible without moulds. At least partial penetration of smoothing agent enables a smooth surface free from pores and holes to be maintained even when the original board size is preserved during subsequent milling and grinding.

Description

Die Erfindung betrifft ein Zweikomponenten-Polyurethan-System zum Glätten von Kanten von Span-, Faser- und Sperrholz-Platten.The invention relates to a two-component polyurethane system for smoothing Edges of chip, fiber and plywood boards.

Eine derartige Verwendung ist bekannt. So wird in der DE 35 11 754 eine reaktionsfähige Masse auf Polyurethanbasis und deren Verwendung zur Herstellung von Beschichtungen im Möbelsektor beschrieben. Dieser Erfindung liegt die Aufgabe zugrunde, die Schnittkanten von Span-, Faser- und Sperrholz- Platten, die in verschiedenen Formen und Stärken hergestellt und auf bestimmte Maße zugeschnitten werden, aus folgenden Gründen zu verschließen:Such use is known. Thus, in DE 35 11 754 a polyurethane-based reactive composition and its use for Production of coatings in the furniture sector described. This invention the task is to determine the cut edges of chip, fiber and plywood Plates made in different shapes and thicknesses and on specific ones Dimensions are cut to close for the following reasons:

  • a) Zur Anpassung des Abschlusses an das Design der Oberfläche,a) to adapt the finish to the design of the surface,
  • b) zum Abdichten gegen Feuchtigkeit,b) for sealing against moisture,
  • c) zum Schutz gegen Ausbrechen von Plattenteilen undc) for protection against breakage of plate parts and
  • d) zur Verhinderung von Beschädigungen und Verletzungen anderer Körper, die gegen die Plattenkante stoßen.d) to prevent damage and injury to other bodies that bump against the plate edge.

Diese Aufgabe wird mit reaktionsfähigen Massen auf Polyurethanbasis gelöst, die ein relativ niedriges Molekulargewicht haben und damit eine niedrige Viskosität. Damit ist der Nachteil verbunden, daß zur Herstellung von Umkantungen der Platten Formen benötigt werden, egal ob nach dem offenen Verfahren oder nach dem geschlossenen Verfahren gearbeitet wird. Damit verbunden sind hohe Kosten aufgrund der speziellen Anfertigung von Formen für den jeweiligen Gegenstand und aufgrund der diskontinuierlichen Herstellung.This object is achieved with reactive polyurethane-based compositions which have a relatively low molecular weight and thus a low viscosity. This has the disadvantage that for the production of Umkantungen the Plate forms are needed, whether after the open procedure or after the closed procedure is worked. This is associated with high Costs due to the special production of molds for each Subject matter and due to the discontinuous production.

Ausgehend von diesem Stand der Technik ergibt sich die Aufgabe, ein einfacheres und kostengünstigeres Verfahren zum Formen und Glätten von Kanten von Span-, Faser- und Sperrholz-Platten bereitzustellen.Based on this prior art, the task results, a simpler and cheaper method of shaping and smoothing To provide edges of chip, fiber and plywood boards.

Die erfindungsgemäße Lösung ist den Patentansprüchen zu entnehmen. Sie besteht im wesentlichen darin, daß das Zweikomponenten-Polyurethansystem pastös ist und eine derart hohe Viskosität hat, daß die Viskosität bei 20°C 150 bis 350 Pa·s beträgt, gemessen mit dem Brookfield-Viskosimeter RVT, oder daß es dünnflüssig ist und die Viskosität innerhalb von 5 bis 15 Sekunden bei 20°C auf einen so hohen Wert ansteigt, daß eine 5 mm dicke PUR-Schicht weniger als 0,5 mm von einer senkrechten Span-, Faser- oder Sperrholz-Platte abläuft, vorzugsweise überhaupt nicht abläuft.The solution according to the invention can be found in the patent claims. you consists essentially in that the two-component polyurethane system is pasty and has such a high viscosity that the viscosity at 20 ° C 150 bis 350 Pa · s, as measured by the Brookfield RVT viscometer, or that it is is viscous and the viscosity within 5 to 15 seconds at 20 ° C on rises so high that a 5 mm thick PUR layer is less than 0.5 mm from a vertical chipboard, fiber or plywood board, preferably does not expire at all.

Die erfindungsgemäßen Zweikomponenten-Polyurethan-Systeme sind also pastös oder sie zeigen ein thixotropes Verhalten unmittelbar nach dem Auftrag. Damit ist eine einfache Beschichtung von Kanten zur Beseitigung von Unebenheiten und Hohlräumen möglich, und zwar ohne Formen. Der Auftrag kann mit einem Transferband oder mit einer Düse erfolgen. Zweckmäßig wird unmittelbar nach dem Auftrag ein Rakel zur Formgebung und Glättung nachgeschaltet. Es ist auch möglich, das Polyurethan durch Spachteln oder durch Streichen aufzutragen mit einer anschließenden Formgebung und Glättung. Die endgültige Formgebung kann auch durch Schleifen, Fräsen oder Schmirgeln erfolgen. Zweckmäßigerweise sollte zum Schleifen die Shore-Härte D des Zweikomponenten-Polyurethan-Systems 65 sein.The two-component polyurethane systems according to the invention are therefore pasty or they show thixotropic behavior immediately after application. This is a simple coating of edges to eliminate bumps and Cavities possible, without forms. The order can with a Transfer tape or with a nozzle. Appropriately becomes immediately after the order a squeegee for shaping and smoothing downstream. It is also possible to apply the polyurethane by trowelling or by brushing with a subsequent shaping and smoothing. The final shape can also be done by grinding, milling or sanding. Conveniently, for grinding the Shore D hardness of Be two-component polyurethane system 65.

Wider Erwarten wird durch die Viskositätserhöhung bzw. Thixotropierung sowohl ein Ablaufen des Glättungsmittels verhindert als auch ein Eindringen des Glättungsmittels in die Poren und Unebenheiten der Kante ermöglicht. Das erfindungsgemäß zu verwendende Glättungsmittel bleibt also nicht als Schicht auf der Kante, sondern dringt in die Vertiefungen ein. Daher entstehen bei dem anschließenden Schleifen oder Fräsen des gehärteten Glättungsmittels keine Löcher, auch wenn man auf die ursprüngliche Dimension abschleift bzw. abfräst.Contrary to expectations, both the viscosity increase and thixotropy a drainage of the smoothing agent prevented as well as penetration of the Smoothing agent in the pores and unevenness of the edge allows. The The smoothing agent to be used according to the invention therefore does not remain as a layer the edge, but penetrates into the wells. Therefore arise in the  subsequent grinding or milling of the hardened smoothing agent no Holes, even if you abraded to the original dimension or milled.

Das erfindungsgemäß zu verwendende Zweikomponenten-Polyurethan-System hat vorzugsweise eine Viskosität von 200 bis 250 Pa·s bei 20°C, gemessen mit dem Brookfield-Viskosimeter RTV.The present invention to use two-component polyurethane system preferably has a viscosity of 200 to 250 Pa · s at 20 ° C, measured with the Brookfield Viscometer RTV.

Dieses pastöse Verhalten kann auf bekannte Art und Weise erhalten werden, z. B. durch Zusatz einer geeigneten Menge an anorganischen Füllstoffen, mit oder ohne organische Beschichtung. Vorzugsweise wird zur Erreichung der gewünschten Viskosität pyrogene Kieselsäure eingesetzt.This pasty behavior can be obtained in a known manner, for. B. by adding a suitable amount of inorganic fillers, with or without organic coating. Preferably, to achieve the desired viscosity fumed silica used.

Als anorganische Füllstoffe eignen sich Carbonate, insbesondere Kalkspat, Kalkstein, Kreide und Magnesium/Calcium-Carbonat-Doppelsalze wie Dolomit, Sulfate wie Barium- und Calciumsulfat, Oxide und Hydroxide wie Aluminiumoxid, Aluminiumoxidhydrate sowie Siliciumdioxid als Quarzmehl oder Kieselgur, Silikate wie Kaolin, Feldspat, Wallostonit, Glimmer, Ton und Talkum, Graphit oder Glasfasern.Suitable inorganic fillers are carbonates, in particular calcite, Limestone, chalk and magnesium / calcium carbonate double salts such as dolomite, Sulfates such as barium and calcium sulfate, oxides and hydroxides such as alumina, Alumina hydrates and silica as quartz or diatomaceous earth, silicates such as kaolin, feldspar, wallostonite, mica, clay and talc, graphite or Glass fibers.

Als anorganischer Füllstoff mit organischer Beschichtung kann Calciumcarbonat mit Stearinsäurebeschichtung eingesetzt werden. Bei den pyrogenen Kieselsäuren sind neben den hydrophilen Produkten mit OH-Gruppen auch hydrophobierte üblich, bei denen OH-Gruppen durch Alkylgruppen ersetzt sind.As inorganic filler with organic coating can calcium carbonate be used with stearic acid coating. At the pyrogenic Silicas are in addition to the hydrophilic products with OH groups also hydrophobicized usual in which OH groups are replaced by alkyl groups.

Vorzugsweise wird die Thixotropie innerhalb von 6 bis 12 Sekunden aufgebaut. Die erfindungsgemäß zu verwendenden zweikomponentigen Polyurethan- Systeme sind erhältlich, wenn die Polyolkomponente eine Mischung von Polyamidaminen mit einem niedermolekularen mehrfunktionellen Amin enthält, wobei es sich um eine Verbindung mit im Mittel etwa 2 Aminogruppen pro Molekül oder um bei Raumtemperatur flüssige Vertreter der homologen Reihe der Alkanolamine handelt. Preferably, the thixotropy is built up within 6 to 12 seconds. The two-component polyurethane to be used according to the invention Systems are available if the polyol component is a mixture of Contains polyamidoamines with a low molecular weight polyfunctional amine, which is a compound having an average of about 2 amino groups per molecule or at room temperature liquid representatives of the homologous series of Alkanolamine is.  

Zu besonders geeigneten, der Polyolkomponente zuzusetzenden Polyamidaminen zählen solche, die durch Umsetzung von oligomerisierten Fettsäuren wie Tricarbonsäuren mit Überschuß von mehrwertigen Aminen erhältlich sind. Als ganz besonders geeignet hat sich ein weichgemachtes Polyamidaminharz auf der Basis von oligomerisierten ungesättigten Fettsäuren gezeigt, dessen mittleres Molekulargewicht ca. 1 200 beträgt, und das der mittleren Zusammensetzung C₇₂H₁₅₀N₉O₃ entspricht; die Viskosität beträgt bei 25°C etwa 3000 Pa·s.To particularly suitable to be added to the polyol component Polyamidoamines include those obtained by reaction of oligomerized Fatty acids such as tricarboxylic acids with excess of polyvalent amines are available. As especially suitable has a plasticized Polyamidoamine resin based on oligomerized unsaturated fatty acids shown, whose average molecular weight is about 1 200, and that of average composition C₇₂H₁₅₀N₉O₃ corresponds; the viscosity is at 25 ° C about 3000 Pa · s.

Diese Harze werden durch Kondensation oder Amidierung von (a) Oligocarbonsäuren aus der Oligomerisation von ungesättigten Fettsäuren mit vorzugsweise mindestens 50 Gew.-% Trimergehalt, bevorzugt einer Zusammensetzung von 0 bis 2% monomere Fettsäuren, 10 bis 50% dimere Fettsäuren und 50 bis 90% trimere Fettsäuren, mit (b) Überschuß eines heterocyclischen Amins der allgemeinen FormelThese resins are formed by condensation or amidation of (a) Oligocarbonsäuren from the oligomerization of unsaturated fatty acids with preferably at least 50% by weight of trimer content, preferably one Composition of 0 to 2% monomeric fatty acids, 10 to 50% dimers Fatty acids and 50 to 90% trimer fatty acids, with (b) excess of one heterocyclic amine of the general formula

erhalten, wobei R eine Alkylaminogruppe oder H, -R′NH₂ ist, wobei R′ eine gesättigte aliphatische Kohlenwasserstoffkette ist, bevorzugt eine -C₂H₄-Gruppe.wherein R is an alkylamino group or H, -R'NH₂, wherein R 'is a saturated aliphatic hydrocarbon chain, preferably a -C₂H₄ group.

Geeignete mehrfunktionelle Amine sind solche, die im Mittel etwa 2 Aminogruppen pro Molekül aufweisen. Hierzu zählen cycloaliphatische Diamine und Diamine auf Basis eines Polyethers, wie z. B. Polyoxypropylen-alpha-omega­ diamin sowie auch flüssige aromatische Diamine.Suitable polyfunctional amines are those which have an average of about 2 Have amino groups per molecule. These include cycloaliphatic diamines and diamines based on a polyether, such as. B. polyoxypropylene-alpha-omega diamine as well as liquid aromatic diamines.

Zu geeigneten aromatischen Diaminen zählen 2,4-Diaminomesitylen, 1,3,5- Triethyl-2,4-diaminobenzol, 1,3,5-Triisopropyl-2,4-diaminobenzol, 4,6-Dimethyl-2- ethyl-1,3-diaminobenzol, 3,5,3′,5′-Tetraethyl-4,4′-diaminodiphenylmethan, 3,5,3′,5,-Tetraisopropyl-4,4′-diaminodiphenylmethan, 3,5-Diethyl-3′,5′-diisopropyl- 4,4′-diaminodiphenylmethan, 1-t-Butyl-3,5-dimethyl-2,4-diaminobenzol, 1-t-Butyl- 3,5-dimethyl-2,6-diaminobenzol oder deren technische Gemische und gegebenenfalls deren Isomere auch in Mischung. Bevorzugt sind trialkylsubstituierte Diaminobenzole, gegebenenfalls in ihren isomeren Mischungen, bei denen die Alkylgruppen vorzugsweise eine Methyl- und 2 Ethylgruppen sind, beispielsweise 1-Methyl-3,5-diethyl-2,4-diaminobenzol und 1- Methyl-3,5-diethyl-2,6-diaminobenzol.Suitable aromatic diamines include 2,4-diaminomesitylene, 1,3,5- Triethyl-2,4-diaminobenzene, 1,3,5-triisopropyl-2,4-diaminobenzene, 4,6-dimethyl-2- ethyl 1,3-diaminobenzene, 3,5,3 ', 5'-tetraethyl-4,4'-diaminodiphenylmethane, 3,5,3 ', 5'-tetraisopropyl-4,4'-diaminodiphenylmethane, 3,5-diethyl-3', 5'-diisopropyl- 4,4'-diaminodiphenylmethane, 1-t-butyl-3,5-dimethyl-2,4-diaminobenzene, 1-t-butyl  3,5-dimethyl-2,6-diaminobenzene or their technical mixtures and optionally their isomers also in a mixture. Preferred are trialkyl substituted diaminobenzenes, optionally in their isomers Mixtures in which the alkyl groups preferably a methyl and 2 Ethyl groups, for example 1-methyl-3,5-diethyl-2,4-diaminobenzene and 1- Methyl-3,5-diethyl-2,6-diaminobenzene.

Die vorstehend genannten Amino-Verbindungen können auch als flüssige Zubereitungen zusammen mit anderen Komponenten eingesetzt werden. Derartige Komponenten können beispielsweise Ester und/oder oligomerisierte bzw. polymerisierte Ester sein. Diese können gegebenenfalls auch NCO-reaktive Hydroxylgruppen enthalten. Beispielhaft seien für derartige Ester z. B. Carbonate bzw. Polycarbonate, insbesondere Propylen-1,2-carbonat, genannt. Die geeigneten Aminzubereitungen bestehen üblicherweise zu einem Drittel bis zur Hälfte aus derartigen Estern. Solche Zubereitungen sind auch kommerziell erhältlich z. B. Baytec 110 von der Firma Bayer.The above-mentioned amino compounds can also be used as liquid Preparations can be used together with other components. Such components may include, for example, esters and / or oligomerized or polymerized esters. These may optionally also NCO-reactive Contain hydroxyl groups. Examples of such esters z. B. Carbonates or polycarbonates, in particular propylene-1,2-carbonate, called. The suitable amine preparations usually consist of one-third to the Half of such esters. Such preparations are also commercial available for. B. Baytec 110 from Bayer.

Es lassen sich aber auch gute Ergebnisse mit Tetramethylethylendiamin erzielen, wie auch mit Vertretern der homologen Reihe der Alkanolamine, sowie die genannten Verbindungen bei Raumtemperatur flüssig sind.But it can also achieve good results with tetramethylethylenediamine, as well as with representatives of the homologous series of alkanolamines, as well as the compounds mentioned are liquid at room temperature.

Zu den geeigneten Polyolen zählen die an sich bekannten Polyole für Zwei- Komponenten-Polyurethansysteme, wie sie beispielsweise in DE 38 27 378 bzw. EP 354 471 beschrieben werden, wobei bevorzugte Polyolkomponenten in den nachfolgenden Beispielen verwendet werden.Suitable polyols include the known polyols for Component polyurethane systems, as described for example in DE 38 27 378 or EP 354 471 are described, wherein preferred polyol components in the following examples are used.

Bevorzugt sind hier Polyester, Polyacetale, Polyether, Polythioether, Polyamide und/oder Polyesteramide, die jeweils im Mittel 2 bis 4 Hydroxylgruppen aufweisen.Preference is given here to polyesters, polyacetals, polyethers, polythioethers, polyamides and / or polyesteramides, each having on average 2 to 4 hydroxyl groups.

Als Polyether seien z. B. die Polymerisationsprodukte des Ethylenoxids, Propylenoxids, Butylenoxids sowie ihre Misch- oder Pfropf­ polymerisationsprodukte sowie die durch Kondensation von mehrwertigen Alkoholen oder Mischungen derselben und die durch Alkoxylierung von mehrwertigen Alkoholen, Aminen, Polyaminen und Aminoalkoholen gewonnenen Polyether genannt. Auch isotaktisches Polypropylenglykol kann Verwendung finden.As a polyether z. B. the polymerization of ethylene oxide, Propylene oxides, butylene oxides and their mixed or graft  polymerization as well as by condensation of polyvalent Alcohols or mixtures thereof and by alkoxylation of obtained from polyhydric alcohols, amines, polyamines and amino alcohols Called polyether. Isotactic polypropylene glycol can also be used Find.

Als Polyacetale kommen z. B. die aus Glykolen wie Diethylenglykol, Triethylenglykol, Hexandiol und Formaldehyd herstellbaren Verbindungen in Frage. Auch durch Polymerisation cyclischer Acetale lassen sich geeignete Polyacetale herstellen.As polyacetals come z. B. from glycols such as diethylene glycol, Triethylene glycol, hexanediol and formaldehyde produced compounds in Question. Also by polymerization of cyclic acetals can be appropriate Produce polyacetals.

Unter den Polythioethern seien insbesondere die Kondensationsprodukte von Thiodiglykol mit sich selbst und/oder mit anderen Glykolen, Dicarbonsäuren, Formaldehyd, Aminocarbonsäuren oder Aminoalkoholen angeführt. Je nach den Co-Komponenten handelt es sich bei den Produkten um Polythioether, Polythiomischether, Polythioetherester, Polythioetheresteramide. Derartige Polyhdydroxylverbindungen können auch in alkylierter Form bzw. in Mischung mit Alkylierungsmitteln angewandt werden.Among the polythioethers are in particular the condensation products of Thiodiglycol with itself and / or with other glycols, dicarboxylic acids, Formaldehyde, aminocarboxylic acids or amino alcohols listed. Depending on the Co-components, the products are polythioethers, Polythiomischether, Polythioetherester, Polythioetheresteramide. such Polyhydroxyl compounds can also be in alkylated form or in admixture with Alkylating agents are used.

Zu den Polyestern, Polyesteramiden und Polyamiden zählen die aus mehrwertigen gesättigten und ungesättigten Carbonsäuren bzw. deren Anhydriden und mehrwertigen gesättigten und ungesättigten Alkoholen, Aminoalkoholen, Diaminen, Polyaminen und ihren Mischungen gewonnenen, überwiegend linearen Kondensate, sowie z. B. Polyterphthalate oder Polycarbonate. Auch Polyester aus Lactonen, z. B. Caprolacton oder aus Hydroxycarbonsäuren sind verwendbar. Die Polyester können Hydroxyl- oder Carboxylendgruppen aufweisen. Zu ihrem Aufbau können als Alkoholkomponente auch höhermolekulare Polymerisate oder Kondensate, wie z. B. Polyether, Polyacetale, Polyoxymethylene (mit)verwendet werden. Among the polyesters, polyester amides and polyamides include the polyvalent saturated and unsaturated carboxylic acids or their Anhydrides and polyhydric saturated and unsaturated alcohols, Amino alcohols, diamines, polyamines and their mixtures, predominantly linear condensates, and z. As polyphthalphthalates or Polycarbonates. Also, polyester from lactones, z. B. caprolactone or from Hydroxycarboxylic acids are useful. The polyesters can be hydroxyl or Have carboxyl end groups. To their construction can as alcohol component also higher molecular weight polymers or condensates, such as. Polyether, Polyacetals, polyoxymethylenes (with) are used.  

Auch bereits Urethan- oder Harnstoffgruppen enthaltende Polyhydroxylverbindungen sowie gegebenenfalls modifizierte natürliche Polyole wie Rizinusöl sind verwendbar. Grundsätzlich kommen auch Polyhydroxylverbindungen, welche basische Stickstoffatome aufweisen, in Frage, z. B. polyalkoxylierte primäre Amine oder Polyester bzw. Polythioether, welche Alkyl-diethanolamin einkondensiert enthalten. Weiterhin eingesetzt werden können Polyole, die durch vollständige oder teilweise Ringöffnung epoxidierter Triglyceride mit primären oder sekundären Hydroxylverbindungen erzeugt werden können, beispielsweise das Umsetzungsprodukt von epoxidiertem Sojaöl mit Methanol.Also already containing urethane or urea groups Polyhydroxyl compounds and optionally modified natural polyols like castor oil are usable. Basically, too Polyhydroxyl compounds which have basic nitrogen atoms, in question z. As polyalkoxylated primary amines or polyesters or polythioethers, which Alkyl diethanolamine condensed contained. Continue to be used may be polyols epoxidized by complete or partial ring opening Triglycerides are produced with primary or secondary hydroxyl compounds can, for example, the reaction product of epoxidized soybean oil with Methanol.

In die Polyolkomponente können auch Feststoffe eingearbeitet sein, die nicht als physikalische Thixotropierungsmittel wirken, sondern andere Funktionen ausüben, z. B. Trocknungsmittel, Pigmente, Streckmittel, Füllstoffe, Dispersionshilfsmittel.In the polyol component and solids may be incorporated, not as act physical thixotropic agents, but perform other functions, z. As drying agents, pigments, extenders, fillers, dispersion aids.

Als Isocyanatkomponente sind solche geeignet, die ebenfalls zur Verwendung in Zwei-Komponenten-Polyurethansystemen an sich bekannt sind und beispielsweise in DE 38 27 378 beschrieben werden. So sind praktisch alle flüssigen mehrfunktionellen Isocyanate, insbesondere Roh-MDI (technisch hergestelltes 4,4′-Diphenylmethandiisocyanat) mit einer Funktionalität von 2,4 bis 2,7 sowie Toluylendiisocyanat (TDI), Tetramethylxyloldiisocyanat (TMXDI) und/oder Isophorondiisocyanat (IDPI) geeignet.Suitable isocyanate components are those which are also suitable for use in Two-component polyurethane systems are known per se and For example, be described in DE 38 27 378. That's practically all liquid polyfunctional isocyanates, especially crude MDI (technically prepared 4,4'-diphenylmethane diisocyanate) having a functionality of 2.4 to 2.7 and tolylene diisocyanate (TDI), tetramethylxylene diisocyanate (TMXDI) and / or isophorone diisocyanate (IDPI).

Das Verhältnis von niedermolekularen mehrfunktionellen Aminen zu Polyamidamin beträgt von etwa 10 : 1 bis 2 : 3 Gewichtsteile. Wenn auch dieses Verhältnis nicht überaus kritisch zu sein scheint, werden bei den genannten Methyl-diethyl-diaminobenzolen-Gewichtsverhältnissen von etwa 2 : 1 bis 4 : 1 bevorzugt.The ratio of low molecular weight polyfunctional amines too Polyamidoamine is from about 10: 1 to 2: 3 parts by weight. If so, too Ratio does not seem to be overly critical, are mentioned in the Methyl diethyl diaminobenzene weight ratios of about 2: 1 to 4: 1 prefers.

Der Anteil der Kombination von Aminen an der Polyolkomponente beträgt 1 bis 10 Gew.-%, vorzugsweise 2 bis 6 Gew.-%, insbesondere 3 bis 5 Gew.-%. The proportion of the combination of amines in the polyol component is 1 to 10 Wt .-%, preferably 2 to 6 wt .-%, in particular 3 to 5 wt .-%.  

Vorzugsweise werden die mehrfunktionellen Amine und das Polyamidamin der Polyolkomponenten vor der Umsetzung mit der Isocyanatkomponente zugegeben. Üblicherweise wird die Polyolkomponente samt den Zusätzen unmittelbar vor der Applikation mit der Isocyanatkomponente innig vermengt.Preferably, the polyfunctional amines and the polyamidoamine are the Polyol components added before the reaction with the isocyanate component. Usually, the polyol component together with the additives immediately before Application intimately mixed with the isocyanate component.

Eine geeignete Polylolkomponente enthält z. B.:
15 bis 100 Gew.-% Polyol
0 bis 85 Gew.-% Füllstoff
0 bis 8 Gew.-% Trockenmittel wie Zeolith
0 bis 2 Gew.-% Verdickungsmittel (auch zur Verhinderung der Sedimentation)
0 bis 2 Gew.-% sonstige Hilfsstoffe wie z. B. Farbstoffe oder Katalysatoren
1 bis 10 Gew.-%, insbesondere 3 bis 5 Gew.-% erfindungsgemäßes Thixotropiermittel.A suitable polylol component contains z. B .:
15 to 100% by weight of polyol
0 to 85 wt .-% filler
0 to 8 wt .-% desiccant such as zeolite
0 to 2 wt .-% thickener (also to prevent sedimentation)
0 to 2 wt .-% of other auxiliaries such. As dyes or catalysts
1 to 10 wt .-%, in particular 3 to 5 wt .-% of thixotropic agent according to the invention.

Das geeignete Verhältnis von Polyolkomponente zu Isocyanatkomponente läßt sich am besten durch das stöchiometrische Verhältnis von NCO-reaktiven zu NCO-Gruppen angeben. Dieses Verhältnis liegt im Bereich von 3 : 2 bis 2 : 3, insbesondere im Bereich von 1 : 1 bis 3 : 4. Optimal ist ein Überschuß an NCO- Gruppen von etwa 10 bis 30%.The appropriate ratio of polyol component to isocyanate component leaves best by the stoichiometric ratio of NCO-reactive to Specify NCO groups. This ratio is in the range of 3: 2 to 2: 3, in particular in the range from 1: 1 to 3: 4. Optimal is an excess of NCO- Groups of about 10 to 30%.

Die Verwendung dieser pastösen oder thixotropen Zweikomponenten- Polyurethan-Systeme bringt mehrere Vorteile mit sich im Vergleich zu den flüssigen der DE 35 11 754:The use of these pasty or thixotropic two-component Polyurethane systems brings several advantages compared to the ones liquid of DE 35 11 754:

  • - Es wird ein problemloses Arbeiten ohne Formen ermöglicht.- It is a trouble-free working without forms possible.
  • - Das Glättungsmittel ist so standfest, daß es auch bei senkrechter Verarbeitung nicht abläuft, z. B. auf die Ober- oder Unterseite der Platte.- The smoothing agent is so stable that it is also in vertical Processing does not expire, eg. B. on the top or bottom of the plate.
  • - Auch nach dem Schleifen auf die ursprüngliche Dimension wird eine loch- und porenfreie Oberfläche durch zumindest partielles Einbringen des Glättungsmittels erhalten. Flüssige Glättungsmittel fordern dagegen häufig zwei Beschichtungsgänge wegen des Penetrationseffektes in das Plattenmaterial.- Even after sanding to the original dimension becomes a hole and non-porous surface by at least partially introducing the Obtained smoothing agent. Liquid smoothing agents, on the other hand, often require it two coating courses because of the penetration effect in the Board material.

Es können also zahlreiche Kanten und Oberflächen von porösem Holz- und Nicht- Holzwerkstoffen sicher geglättet und versiegelt werden. Hierzu zählen insbesondere Span-, Faser- und Sperrholz-Platten. Aber auch Mineralfaserplatten, mineralisch gebundene Faserplatten und Gipsplatten können so vergütet werden. Die erfindungsgemäße Verwendung läßt sich sowohl diskontinuierlich; z. B. in der Werkstatt eines Tischlers oder auf der Baustelle; als auch kontinuierlich anwenden, z. B. bei der industriellen Verarbeitung solcher Platten in der Möbelindustrie.Thus, numerous edges and surfaces of porous wood and non-wood Wood materials are smoothed and sealed securely. Which includes in particular chip, fiber and plywood boards. But also Mineral fiber boards, mineral-bonded fiberboard and gypsum boards can so be compensated. The use according to the invention can be both discontinuous; z. In the workshop of a carpenter or on the construction site; when also apply continuously, for. B. in industrial processing such Plates in the furniture industry.

Die Erfindung wird nun anhand von Beispielen im einzelnen beschrieben:The invention will now be described in detail by way of examples:

Beispiel 1example 1 Harzkomponenteresin component Masseanteile in %Mass shares in% Polypropylenglykol, Mm 400|8,00Polypropylene glycol, Mm 400 | 8,00 Rizinusölcastor oil 21,0021,00 Na-Al-Silikat in Rizinusöl (50%)Na Al silicate in castor oil (50%) 4,004.00 Calciumcarbonatcalcium carbonate 41,9941,99 Calciumcarbonat, gecoatetCalcium carbonate, coated 25,0025,00 Dibutylzinndilauratdibutyltindilaurate 0,010.01 Härterkomponente @hardener component @ Diphenylmethan-4,4′-diisocyanat (Roh-MDI)Diphenylmethane-4,4'-diisocyanate (crude MDI) 100100 Mischungsverhältnis Harz: HärterMixing ratio of resin: hardener 6 : 16: 1 Topfzeitpot life 11 min11 min Mischviskositätmixed viscosity 230 000 mPa·s230,000 mPa · s

Beispiel 2Example 2 Harzkomponenteresin component Massenanteile in %Mass shares in% Polypropylenglykol, Mm 1000|7,00Polypropylene glycol, Mm 1000 | 7.00 trifunktionelles Polypropylenglykol, Mm 450trifunctional polypropylene glycol, Mm 450 36,5036,50 Rizinusölcastor oil 23,4823.48 Na-Al-Silikat in RizinusölNa Al silicate in castor oil 4,504.50 Calciumcarbonatcalcium carbonate 20,0020.00 aromatisches Diamingemisch aus . . .aromatic diamine mixture. , , 5,505.50 Polyaminoamidpolyaminoamide 2,002.00 Schichtsilikatphyllosilicate 1,001.00 Dibutylzinndilauratdibutyltindilaurate 0,020.02 Härterkomponente @hardener component @ Diphenylmethan-4,4′-diisocyanat (Roh-MDI)Diphenylmethane-4,4'-diisocyanate (crude MDI) 100100 Mischungsverhältnis Harz : HärterMixing ratio of resin: hardener 10 : 610: 6 Topfzeitpot life 5 min5 min ThixotropieaufbauThixotropieaufbau nach 10 safter 10 s

Beide Produkte wurden nach Mischung in Zweikomponentenanlagen über eine 20 mm breite Schlitzdüse auf Möbelspanplatten mit 20 mm Kantenbreite aufgetragen. Die Dicke der Polyurethan-Schicht betrug 1 mm. Es erfolgte die Beschichtung der Kanten in einem Schritt, d. h. unmittelbar nach Auftragen auf eine Kante wird die Platte um 90°C gedreht und anschließend die nächste Kante beschichtet. Hierbei bleibt der 1 mm dicke Auftrag erhalten. Die Beschichtungsmasse läuft also nicht von der Spanplatte ab. Das PU wurde ausgehärtet, indem-die beschichteten Platten durch einen Heizkanal mit 130°C geführt wurden. Both products were mixed after mixing in two-component systems 20 mm wide slot nozzle on furniture boards with 20 mm edge width applied. The thickness of the polyurethane layer was 1 mm. It took place the Coating the edges in one step, d. H. immediately after application one edge is turned the plate by 90 ° C and then the next edge coated. Here, the 1 mm thick order remains. The Coating compound does not run off the chipboard. The PU was Hardened by placing the coated plates through a heating channel at 130 ° C were led.  

Nach Schleifen der Platten entsteht eine glatte Kante mit planer Oberfläche, die nach Kaschieren mit Möbelfolie im Membranpreßverfahren keine Unebenheiten aufweist. Des weiteren wird durch die hohe Temperaturbeständigkeit der Polyurethan-Schicht ein Folienrückzug auch bei Lagerung bei 120°C ausgeschlossen.After sanding the panels creates a smooth edge with a flat surface, the after laminating with furniture foil in Membranpreßverfahren no bumps having. Furthermore, the high temperature resistance of the Polyurethane layer a film retraction even when stored at 120 ° C. locked out.

Claims (12)

1. Verwendung eines Zweikomponenten-Polyurethan-Systems zur Formgebung und Glättung von Kanten von Span-, Faser- und Sperrholz-Platten, dadurch gekennzeichnet, daß das Zweikomponenten-Polyurethan-System pastös ist und eine derart hohe Viskosität hat, daß die Viskosität bei 20°C 150 bis 350 Pa·s beträgt, gemessen mit dem Brookfield-Viskosimeter RVT, oder daß es dünnflüssig ist und die Viskosität innerhalb von 5 bis 15 Sekunden bei 20°C auf einen so hohen Wert ansteigt, daß eine 5 mm dicke PUR-Schicht weniger als 0,5 mm von einer senkrechten Span-, Faser- oder Sperrholz- Platte abläuft.1. Use of a two-component polyurethane system for shaping and smoothing edges of particleboard, fibreboard and plywood boards, characterized in that the two-component polyurethane system is pasty and has such a high viscosity that the viscosity at 20 ° C is 150 to 350 Pa · s, measured with the Brookfield RVT viscometer, or that it is low-viscosity and the viscosity rises within 5 to 15 seconds at 20 ° C to such a high value that a 5 mm thick PUR Layer runs less than 0.5 mm from a vertical chip, fiber or plywood board. 2. Verwendung nach Anspruch 1, gekennzeichnet durch eine Viskosität des pastösen Zweikomponenten-Polyurethan-Systems von 200 bis 250 Pa·s.2. Use according to claim 1, characterized by a viscosity of pasty two-component polyurethane system from 200 to 250 Pa · s. 3. Verwendung nach Anspruch 1, gekennzeichnet durch einen Viskositätsanstieg (Thixotropieaufbau) innerhalb von 6 bis 12 Sekunden.3. Use according to claim 1, characterized by a Viscosity increase (Thixotropieaufbau) within 6 to 12 seconds. 4. Verwendung nach Anspruch 1 oder 3, dadurch gekennzeichnet, daß die Polyolkomponente eine Mischung von Polyamidamin und niedermolekularen mehrfunktionellen Aminen enthält, wobei es sich bei den niedermolekularen mehrfunktionellen Aminen um Verbindungen mit im Mittel etwa 2 Aminogruppen pro Molekül oder um bei Raumtemperatur flüssige Vertreter der homologen Reihe der Alkanolamine handelt.4. Use according to claim 1 or 3, characterized in that the Polyol component a mixture of polyamidoamine and low molecular weight contains polyfunctional amines, wherein it is the low molecular weight polyfunctional amines to compounds with an average of about 2 Amino groups per molecule or liquid at room temperature representatives the homologous series of alkanolamines. 5. Verwendung nach Anspruch 4, dadurch gekennzeichnet, daß das Gewichtsverhältnis von Amin zu Polyamidamin von 10 : 1 bis 2 : 3 Gewichtsteile beträgt. 5. Use according to claim 4, characterized in that the Weight ratio of amine to polyamidoamine from 10: 1 to 2: 3 Parts by weight.   6. Verwendung nach Anspruch 4, dadurch gekennzeichnet, daß der Anteil der Kombination mehrfunktionelles Amin und Polyamidamin an der Polyolkomponente 1 bis 10 Gew.-%, vorzugsweise 2 bis 6 Gew.-%, insbesondere 3 bis 5 Gew.-%, beträgt.6. Use according to claim 4, characterized in that the proportion of Combination of polyfunctional amine and polyamidoamine at the Polyol component 1 to 10% by weight, preferably 2 to 6% by weight, in particular 3 to 5 wt .-%, is. 7. Verwendung nach Anspruch 4, dadurch gekennzeichnet, daß es sich um ein mehrfunktionelles Amin mit dem Mittel etwa 2 Aminogruppen pro Molekül handelt.7. Use according to claim 4, characterized in that it is a polyfunctional amine having the average of about 2 amino groups per molecule is. 8. Verwendung nach Anspruch 7, dadurch gekennzeichnet, daß das mehrfunktionelle Amin ein cycloaliphatisches Diamin oder ein Diamin auf Basis von Polyether wie Polyoxypropylen-alpha-omega-diamin ist.8. Use according to claim 7, characterized in that the polyfunctional amine, a cycloaliphatic diamine or a diamine Basis of polyether such as polyoxypropylene-alpha-omega-diamine. 9. Verwendung nach Anspruch 4, dadurch gekennzeichnet, daß das Polyamidamin ein Polyamidamin auf der Basis von oligomerisierter Fettsäure, insbesondere Trimerfettsäure ist.9. Use according to claim 4, characterized in that the Polyamidoamine a polyamidoamine based on oligomerized fatty acid, in particular trimer fatty acid. 10. Verwendung nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß das pastöse Verhalten des Zweikomponenten-Polyurethan-Systems durch Zusatz eines geeigneten Gehalts an mindestens einem anorganischen Füllstoff, mit oder ohne organische Beschichtung, insbesondere durch Zusatz pyrogener Kieselsäure erhalten wird.10. Use according to claim 1 or 2, characterized in that the pasty behavior of the two-component polyurethane system by addition a suitable content of at least one inorganic filler, with or without organic coating, in particular by adding pyrogenic Silica is obtained. 11. Verwendung nach Anspruch 1, dadurch gekennzeichnet, daß die Formgebung und Glättung des Zweikomponenten-Polyurethan-Systems unmittelbar nach Auftrag mit einem Rakel erfolgt.11. Use according to claim 1, characterized in that the Shaping and smoothing of the two-component polyurethane system immediately after application with a squeegee. 12. Verwendung nach Anspruch 1, dadurch gekennzeichnet, daß bei Formgebung und Glättung durch Schleifen die Shore Härte D des Zweikomponenten-Polyurethan-Systems 65 sein muß.12. Use according to claim 1, characterized in that at Shaping and smoothing by grinding the Shore hardness D of Two-component polyurethane system 65 must be.
DE1996140988 1996-10-04 1996-10-04 Two-component polyurethane for shaping and smoothing chipboard, etc. edges without a mould Expired - Fee Related DE19640988C1 (en)