DE19501289A1 - Heat sensitive paper for thermal printing - Google Patents
Heat sensitive paper for thermal printingInfo
- Publication number
- DE19501289A1 DE19501289A1 DE1995101289 DE19501289A DE19501289A1 DE 19501289 A1 DE19501289 A1 DE 19501289A1 DE 1995101289 DE1995101289 DE 1995101289 DE 19501289 A DE19501289 A DE 19501289A DE 19501289 A1 DE19501289 A1 DE 19501289A1
- Authority
- DE
- Germany
- Prior art keywords
- heat
- sensitive recording
- recording material
- synthetic fibers
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Ceased
Abstract
Description
Die Erfindung betrifft ein wärmeempfindliches Aufzeichnungsmaterial mit einem Trägermaterial, das auf einer seiner beiden Oberflächen eine wärmeempfindliche, farbbildende Aufzeichnungsschicht aufweist, die einen im wesentlichen farblosen Farbstoffvorläufer, einen bei Erwärmung mit dem Farbstoffvorläufer reagierenden Farbentwickler zur Entwicklung einer Farbe und ein Bindemittel aufweist.The invention relates to a heat sensitive Recording material with a carrier material, the one on one of its two surfaces heat-sensitive, color-forming Recording layer having an im essential colorless dye precursor, one when heated with the dye precursor responsive color developer to develop a Has color and a binder.
Wärmeempfindliche Aufzeichnungsmaterialien der vorstehend angegebenen Art sind seit längerer Zeit aus dem Stand der Technik bekannt und werden überwiegend für die Wiedergabe von empfangenen Fernkopien über das öffentliche Fernsprechnetz (sogenanntes Telefax-Verfahren) eingesetzt. Ein weiterer und zunehmend an Bedeutung gewinnender Einsatzbereich liegt in der Verwendung wärmeempfindlicher Aufzeichnungsmaterialien als Druckträger für den sogenannten Thermodruck. Ein bekannter Anwendungsbereich ist z. B. der Ausdruck von Kassenzetteln durch mit einem Thermodrucker ausgerüstete Registrierkassen an Tankstellen und Supermärkten. Während bei diesem Anwendungsbereich kaum die Gefahr einer Fälschung besteht, mußte in letzter Zeit festgestellt werden, daß mit dem steigenden Einsatz von Thermodruckern bei der Herstellung von Fahrausweisen (Tickets) und Eintrittskarten, die der Einfachheit halber nachfolgend als Ausweise bezeichnet werden, immer häufiger Fälschungen zu beobachten waren.Heat sensitive recording materials of the above type have been for a long time known from the prior art and become mainly for the playback of received Fax copies over the public telephone network (so-called fax procedure) used. On further and increasingly important Area of application lies in the use heat sensitive recording materials as Print media for so-called thermal printing. On known application is z. B. the expression of receipts through with a thermal printer equipped cash registers at petrol stations and Supermarkets. While in this scope there is hardly any risk of counterfeiting have recently been found that with the increasing use of thermal printers at the Production of tickets and tickets Tickets that are for the sake of simplicity hereinafter referred to as ID cards, always counterfeits were more common.
Aus dem DE-93 02 105 U ist ein bahnförmiges Trägermaterial für eine thermosensitive Aufzeichnungsschicht bekannt, das als ein erkennbares Zeichen für eine Qualitätscharakterisierung mit einem Wasserzeichen versehen ist. In dieser Schrift wird auch Bezug genommen auf die EP-0 203 499 A2, in der die Anbringung eines Pseudowasserzeichens offenbart wird, wobei das Papier auf einem Teil der thermosensitiven Oberfläche halbdurchscheinend präpariert wird. Die bekannten Vorschläge stellen darauf ab, dem Anwender die Möglichkeit zur Unterscheidung von Thermopapieren unterschiedlicher Hersteller zu bieten. Sie sind jedoch weniger geeignet, um einem Kontrolleur bei einer Kontrolle von Ausweisen am Eingang zu einer Veranstaltung die Erkennung von Fälschungen zu erleichtern.From DE-93 02 105 U is a web-shaped Backing material for a thermosensitive Recording layer known as a recognizable sign for a Quality characterization with a watermark is provided. In this document reference is also made taken on EP-0 203 499 A2, in which the Attachment of a pseudo watermark disclosed being, the paper on part of the thermosensitive surface semi-translucent is prepared. Make the known suggestions depends on giving the user the opportunity to Differentiation from thermal paper from different manufacturers. you are however less suitable to a controller a control of ID cards at the entrance to a Event to detect counterfeits facilitate.
Die Erfindung hat damit die Aufgabe, ein für die Herstellung von Ausweisen geeignetes Aufzeichnungsmaterial zur Verfügung zu stellen, das in verbesserter weise die Erkennung von Fälschungen ermöglicht. Dabei wird von der Überlegung ausgegangen, für die Herstellung der jeweiligen Ausweise ein wärmeempfindliches Aufzeichnungsmaterial einzusetzen, das für einen Kontrolleur deutlich von den Standardqualitäten wärmeempfindlicher Aufzeichnungsmaterialien zu unterscheiden ist und möglichen Fälschern nicht ohne weiteres zur Verfügung steht.The object of the invention is therefore one for Production of ID cards suitable To provide recording material, that in an improved way the detection of Allows forgeries. It is from the Considered the manufacture of the each ID card a heat sensitive To use recording material for a Checker clearly of the standard qualities heat-sensitive recording materials is different and possible counterfeiters is readily available.
Zur Lösung der vorliegenden Aufgabe sieht die Erfindung ein wärmeempfindliches Aufzeichnungsmaterial mit einem Trägermaterial vor, das auf einer seiner Oberflächen eine wärmeempfindliche, farbbildende Aufzeichnungsschicht aufweist, die einen im wesentlichen farblosen Farbstoffvorläufer, einen bei Erwärmung mit dem Farbstoffvorläufer reagierenden Farbentwickler zur Entwicklung einer Farbe und ein Bindemittel enthält und das dadurch gekennzeichnet ist, daß das Trägermaterial ein Streichrohpapier ist, dessen Faserstoffzusammensetzung aus natürlichen Zellulosefasern und - bezogen auf Gesamtfaserstoff - 0,1 bis 0,5 Gew.% farbigen und bei ultravioletter Bestrahlung fluoreszierenden Synthesefasern besteht und die Synthesefasern ein Verhältnis von Faserdicke - ausgedrückt in dtex - : Faserlänge - ausgedrückt in mm - im Bereich von 1 : 0,1 bis 1 : 2 aufweisen. Die dem Faserstoff zugegebenen farbigen Synthesefasern sind infolge der Abdeckung der einen Oberfläche des Trägermaterials mittels der wärmeempfindlichen, farbbildenden Schicht nur schwach wahrnehmbar und beeinträchtigen die Ausbildung eines einwandfreien Druckbildes daher nicht. Rückseitig sind die farbigen Synthesefasern dagegen bereits bei Tageslicht erkennbar und ihre Erkennbarkeit verstärkt sich, insbesondere bei nur schwachem Tageslicht oder bei Dunkelheit unter dem Einfluß von UV-Strahlen. Damit können aus dem erfindungsgemäß hergestellten Aufzeichnungsmaterial hergestellte Ausweise sowohl bei Tageslicht als auch bei Dunkelheit unter Zuhilfenahme einer UV-Quelle leicht erkannt werden und von Fälschungen, die auf üblichen Standardqualitäten mit Hilfe eines Thermodruckers gedruckt sind, unterschieden werden. Der Farbton der Synthesefasern ist an sich nicht kritisch, es ist lediglich darauf zu achten, daß ein ausreichend hoher Kontrast zwischen der Farbe der Synthesefasern und der Rückseite des Aufzeichnungsmaterials resultiert. Als gut geeignet haben sich leuchtende Rot-, Blau-, und Gelbtöne erwiesen. Für die Einfärbung der Synthesefasern sind die üblicherweise zur Einfärbung von Synthesefasern zum Einsatz kommenden Farbstoffsortimente geeignet, sofern sie die im Hauptanspruch an die Eigenschaft der Synthesefasern erhobenen Anforderungen erfüllen. Für Polyamidfasern haben sich Säurefarbstoffe, insbesondere Triphenylmethanfarbstoffe, als gut geeignet erwiesen. Zur Erzeugung einer leuchtend roten Farbe ist der von der Fa. Sandoz-Quinn- Produkte unter der Bezeichnung Sandolan Rhodamin E-BD 400 angebotene Farbstoff besonders geeignet.To solve the present problem, the Invention a heat sensitive Recording material with a carrier material before that one on one of its surfaces heat-sensitive, color-forming Recording layer having an im essential colorless dye precursor, one when heated with the dye precursor responsive color developer to develop a Contains paint and a binding agent and that is characterized in that the carrier material Coating base paper is whose Fiber composition from natural Cellulose fibers and - based on total fiber - 0.1 to 0.5 wt.% Colored and ultraviolet radiation fluorescent Synthetic fibers exist and the synthetic fibers Ratio of fiber thickness - expressed in dtex - : Fiber length - expressed in mm - in the range of 1: 0.1 to 1: 2. The fiber added colored synthetic fibers are the result the cover of one surface of the Carrier material by means of the heat-sensitive, color-forming layer only slightly perceptible and affect the formation of a flawless Print image therefore not. On the back are the colored synthetic fibers on the other hand Recognizable daylight and its recognizability intensifies, especially when there is only a weak one Daylight or in the dark under the influence of UV rays. So that from the produced according to the invention ID cards produced both in daylight as well as in the dark Using a UV source can be easily recognized and counterfeits that are common Standard qualities with the help of a thermal printer printed, can be distinguished. The shade the synthetic fibers are not critical in themselves, it you just have to make sure that a sufficiently high contrast between the color of the Synthetic fibers and the back of the Recording material results. As well bright red, blue, and Yellows proven. For coloring the Synthetic fibers are usually used for Coloring synthetic fibers for use upcoming dye assortments, provided they which in the main claim to the property of Synthetic fibers meet the requirements raised. Acid dyes for polyamide fibers especially triphenylmethane dyes, as well proven suitable. To produce a luminous red color is that of Sandoz-Quinn Products under the name Sandolan Rhodamine E-BD 400 dye offered particularly suitable.
Vorzugsweise sind Fasern aus Polyamid und Polyester oder eine Mischung dieser beiden Synthesefasersorten geeignet. Die Menge an zugegebenen Synthesefasern beträgt, bezogen auf die Faserstoffzusammensetzung des Streichrohpapiers, vorzugsweise 0,15 bis 0,25 Gew.%.Fibers are preferably made of polyamide and Polyester or a mixture of the two Suitable types of synthetic fibers. The amount of added synthetic fibers is based on the fiber composition of the Coating base paper, preferably 0.15 to 0.25 % By weight.
Gemäß einer weiteren vorzugsweisen Ausführungsform des erfindungsgemäßen Aufzeichnungsmaterials besitzt dieses eine Flächenmasse von 70 bis 140 g/m² und liegt damit höher als die Flächenmassen der für die Herstellung von Fernkopien eingesetzten Standardqualitäten, die eine Flächenmasse von < 70 g/m² aufweisen. Die wärmeempfindliche Schicht an sich ist nicht Gegenstand der vorliegenden Erfindung; es kann hier auf die üblichen Farbbildner und Farbentwickler zurückgegriffen werden, jedoch wird bevorzugt, daß die Schicht in einer Flächenmasse von 3,5 bis 5,5 g/m² aufgetragen wird.According to a further preferred embodiment of the recording material according to the invention it has a basis weight of 70 to 140 g / m² and is therefore higher than the mass per unit area the one for making remote copies used standard qualities that a Have a basis weight of <70 g / m². The heat sensitive layer in itself is not Subject of the present invention; it can here on the usual color formers and Color developers will be resorted to, however preferred that the layer be in a basis weight from 3.5 to 5.5 g / m² is applied.
Erfindungsgemäß kann auch eine an sich übliche, ölabsorptive Pigmente enthaltende Zwischenschicht vor Auftrag der wärmeempfindlichen Aufzeichnungsschicht auf das Streichrohpapier aufgetragen werden. According to the invention, a conventional, Intermediate layer containing oil-absorbent pigments before applying the heat sensitive Recording layer on the coating base paper be applied.
Zur Herstellung einer glatten und ebenen Papieroberfläche hat sich bei der Herstellung des Streichrohpapiers unter Zusatz der erfindungsgemäß vorgesehenen Synthesefasern Laubholzzellstoff als besonders geeignet erwiesen, wobei der Anteil des Laubholzzellstoffes bis zu 60 Gew.% - bezogen auf Gesamtfaserstoff - durch Nadelholzzellstoff ersetzt sein kann.To produce a smooth and level Paper surface has been used in the manufacture of the Coating base paper with the addition of the invention provided synthetic fibers hardwood pulp as proven particularly suitable, the proportion of Hardwood pulp up to 60% by weight - based on Total fiber - through softwood pulp can be replaced.
Neben denk vorstehend angegebenen Faserstoffen kann das Streichrohpapier noch weitere nichtfaserige Komponenten enthalten, insbesondere mineralische Füllstoffe, wie z. B. Calciumcarbonat und Talkum, die in einer Menge von insgesamt bis zu 14 Gew.%, bezogen auf die Flächenmasse des Streichrohpapiers, vorliegen können. Zur Retentionsverbesserung können die üblichen Retentionshilfsmittel zugegeben werden und gemäß einer weiteren Ausführungsform wird bevorzugt, daß das Streichrohpapier im Neutralbereich voll geleimt ist. Zur Vermeidung von Problemen bei der Dispergierung der Synthesefasern und um eine ausreichend gleichmäßige Blattbildung sicherzustellen, hat sich gemäß einer weiteren vorzugsweisen Ausführungsform die Einhaltung einer Faserlänge für die einzusetzenden Synthesefasern im Bereich von 3 bis 9 mm als besonders geeignet erwiesen. Geringere Faserlängen führen zu einer nicht ausreichenden Erkennbarkeit, während längere Fasern als 9 mm zu Problemen bei der Faservereinzelung und damit zu einer nicht gleichmäßigen Formierung des Papierblattes führen. In addition to the above-mentioned fibrous materials the base paper still other non-fibrous Contain components, especially mineral ones Fillers such as B. calcium carbonate and talc, in a total amount of up to 14% by weight, based on the mass per unit area of the Coating base paper. For Retention improvement can be the usual Retention aids are added and according to a further embodiment, it is preferred that the coating base paper is full in the neutral area is glued. To avoid problems with the Dispersion of the synthetic fibers and around sufficiently uniform leaf formation has to make sure according to another preferred embodiment compliance with a Fiber length for the synthetic fibers to be used in the range from 3 to 9 mm as particularly suitable proven. Shorter fiber lengths lead to one inadequate recognizability during extended periods Fibers than 9 mm to problems with the Fiber separation and therefore not one lead even formation of the paper sheet.
Bevorzugt werden Synthesefasern mit einer Dicke < 6 dtex eingesetzt, wobei vorzugsweise jedoch eine Faserdicke von 40 dtex nicht überschritten wird. Ganz besonders bevorzugt ist dabei eine Einstellung im Verhältnis von Faserdicke/ Faserlänge im Bereich von 1 : 0,15 bis 1 : 1.Synthetic fibers with a thickness are preferred <6 dtex used, but preferably one Fiber thickness of 40 dtex is not exceeded. One is very particularly preferred Setting in the ratio of fiber thickness / Fiber length in the range of 1: 0.15 to 1: 1.
Die Verwendung des wärmeempfindlichen Aufzeichnungsmaterials ist an keinen besonderen Verwendungsbereich gebunden, jedoch ist die Verwendung zur Herstellung von mittels Thermodruck hergestellten Fahrausweisen und Eintrittskarten ein besonders bevorzugtes Einsatzgebiet.The use of the heat sensitive Recording material is not special at all Scope of use is bound, however Use for the production of by means of thermal printing manufactured tickets and tickets a particularly preferred area of application.
Das nachfolgende Beispiel erläutert die Erfindung.The following example explains the invention.
0,2 Gew.-Teile leuchtend rot angefärbter Polyamidfasern von 6,7 dtex und einer Faserlänge von 6 mm werden einem Faserstoff, der aus 49,8 Gew.-Teilen eines auf 30 Grad Schopper-Riegler angemahlenen Laubholzzellstoff und 50 Gew.% auf 45 Grad Schopper-Riegler angemahlenem Nadelholzzellstoff besteht, zugegeben. Der fertigen Fasermischung werden noch 1,5 Gew.-Teile Talkum und 10 Gew.-Teile Calciumcarbonat, bezogen auf 100 Gew.-Teile Faserstoffmischung, 0,2 Gew.- Teile eines Retentionshilfsmittels sowie 1 Gew.- Teil einer Harzdispersion zur Einstellung einer Volleimung zugegeben. 0.2 parts by weight bright red Polyamide fibers of 6.7 dtex and a fiber length of 6 mm are a fibrous material made from 49.8 Parts by weight of a Schopper-Riegler at 30 degrees ground hardwood pulp and 50% by weight to 45 Degree Schopper-Riegler ground Coniferous wood pulp is added. Of the The finished fiber mixture is still 1.5 parts by weight Talc and 10 parts by weight of calcium carbonate per 100 parts by weight of fiber mixture, 0.2 parts by weight Parts of a retention aid and 1 part by weight Part of a resin dispersion to adjust Full glue added.
Auf einer Langsiebpapiermaschine wird aus der vorstehend angegebenen Stoffmischung ein Streichrohpapier mit einer Flächenmasse von 72 g/m² hergestellt und auf einer Rakelstreichmaschine mit einer Beschichtungsmasse zur Ausbildung einer an sich üblichen wärmeempfindlichen Aufzeichnungsschicht einer Flächenmasse von 4,5 g/m² versehen. Nach Behandlung auf einem Satinierkalander liegt ein wärmeempfindliches Aufzeichnungsmaterial vor, das auf der der wärmeempfindlichen Aufzeichnungsschicht gegenüberliegenden Seite bereits bei Tageslicht deutlich erkennbare rote Fasern zeigt. Unter Einwirkung von UV-Strahlung intensiviert sich die rote Farbe.On a Fourdrinier paper machine, the a mixture of substances specified above Coating base paper with a basis weight of 72 g / m² manufactured and on a Doctor coater with a coating compound to form a conventional one heat sensitive recording layer of a Surface weight of 4.5 g / m². To Treatment on a calendering calender is on heat-sensitive recording material before on that of the heat sensitive Opposite side of the recording layer already clearly recognizable red in daylight Fibers shows. Under the influence of UV radiation the red color intensifies.
Claims (7)
0,1 bis 0,5 Gew.% Synthesefasern, Rest Laubholzzellstoff besteht und, der Laubholzzellstoff bis zu 60 Gew.% - bezogen auf Gesamtfaserstoff - durch Nadelholzzellstoff ersetzt sein kann.6. Heat-sensitive recording material according to one of claims 1 to 5, characterized in that the fibrous composition of the coating base paper from:
0.1 to 0.5% by weight of synthetic fibers, the rest is hardwood pulp and the hardwood pulp can be replaced by softwood pulp up to 60% by weight, based on the total fiber pulp.