DE1803755A1 - Container glass

Info

Publication number: DE1803755A1
Application number: DE19681803755
Authority: DE
Inventors: Siegfried Lehmann; Herwart Pruskel; Manfred Simon; Willi Tenzel
Original assignee: VER VOLKSEIGENER BETR E HAUSHA
Current assignee: VER VOLKSEIGENER BETR E HAUSHA
Priority date: 1968-04-22
Filing date: 1968-10-18
Publication date: 1970-04-16
Also published as: DD69675A3; AT295775B; CS150617B2

Abstract

Glass production process, particularly for vessels, with improved temp. change resistance, leach resistance, mechanical strength and absorption of ultra-violet radiation consists of adding to a glass mass up to 90% powdered non-ferrous cupola slag, in amount up to 90% of constituents for lattice formation and modification. Specif., these are added as colouring raw materials, dependent on furnace atm., and amount of slag addition so as to produce the colours green to olive green, brown to black. The slag consists of SiO2, Sl2O3, CaO, Fe2O3, MgO, R2O (Na2O + K2O) and residual oxides (of Ti, Mn, Cu, Cr).

Description

Verfahren zur Erzeugung von Fab- bis farblosen Gläsern insbesondere Behältergläsern Die Erfindung betrifft ein Verfahren zur Beeinflussung des Glasbildungaprozesses; insbesondere sollen die Baktoren verändert; werden, welche den Schmelzprozeß beschleunigen und die chemischen, physikalischen und mechanischen Parameter des Glases verändern und Leistungssteigerungen bei manueller und maschineller Glasverarbeitung möglich werden.Process for the production of colored to colorless glasses in particular Container glasses The invention relates to a method for influencing the glass formation process; in particular, the bacteria should be changed; which accelerate the melting process and change the chemical, physical and mechanical parameters of the glass and increases in performance for manual and mechanical glass processing are possible will.

Bekannt ist der Einfluß der Scherbenzugabe auf die Verarbeitungseigenschaften des Glases und die Verbreitung der Ansicht, daß bei Verwendung hoher Scherbenanteile das Glas kürzer, viskoser und spröder wird. Dies geschieht bekannterweise mit wachsendem Schmelzalter der Scherben durch die erhöhte Aufnahme von Tonerde aus dem ff.-Material und durch Verlust eines Teiles der flüchtigen Bestandteile wie z.B.The influence of the addition of cullet on the processing properties is known of the glass and the widespread belief that when using a high proportion of cullet the glass becomes shorter, more viscous and more brittle. This is known to happen with growing Melting age of the shards due to the increased absorption of clay from the ff material and by loss of some of the volatile constituents such as e.g.

Na2O, As203, B203 usw. Mit der Veränderung der Zusammensetzung der Scherben steht auch der Einfluß auf die Erhöhung der Wasser- und Säurebeständigkeit und anderer chemischer und auch physikalischer Eigenschaften im Zusammenhang. Durch sorgfältige Auswahl und Korrektur der Menge der Scherbenzugabe hat man die MögliGhkeit diesem Verdampfungsverlust entgegenzuwirken. Bekannt ist, daß neben der Sprödigkeit eines häufig umgeschmolzenen oder mit hohem ßcherbenzusatz geschmolzenen Glases eine hohe Schlierigkeit zu erwarten ist, welche umso größer wird, Je mehr Bremdscherben unbekannter oder bekannter aber abweichender Zusammensetzung eingesetzt werden müssen, Bekannt ist auch die Verwendung von Hochofenschlacke für die Heratellung bestimmter Emails. Diese Schlacken müssen aber auf Grund ihres hohen Schwefelgehaltes besonders aufbereitet werden. Der Sinsatz ist für die großtechnische Verwendung bei der Glaserzeugung ökonomisch nicht vertretbar, Bei billigeren Gläsern, z.B. Behälterglas, ist es aus ökonomischen Gründen notwendig, Fremdscherben - mit vom Grundglas abweichender oder sogar wechselnder Zusammensetzung - im Gemenge in größeren Posten zu verarbeiten. Dies bedingt einen Einfluß auf die Verarbeitungseigenschaften und zwar hinsichtlich der Viskosität und der Sprödigkeit, es ist aus diesem Grunde eine ständige Nachregulierung der Maschinen, bedingt durch die sich verändernde Viskosität, erforderlich, Dieses wirkt sich leistungsmindern auf den Arbeitsgang der blaschinen aus.Na2O, As203, B203 etc. With the change in the composition of the Shards also have an influence on the increase in water and acid resistance and other chemical and physical properties in connection. By Careful selection and correction of the amount of cullet added is possible to counteract this evaporation loss. It is known that in addition to brittleness a glass that is often remelted or melted with a high amount of cullet a high degree of streakiness is to be expected, which becomes greater, the more Bremdscheben unknown or known but different composition must be used, The use of blast furnace slag for the manufacture of certain products is also known Emails. But these slags have to due to their high sulfur content specially prepared. The set is for large-scale use not economically justifiable in the production of glass. Container glass, it is necessary for economic reasons, foreign shards - with from Base glass of differing or even changing composition - in a batch in larger ones Item to process. This has an influence on the processing properties in terms of viscosity and brittleness, it is for this reason constant readjustment of the machines, due to the changing Viscosity, required, this affects the performance of the work process the blow machines off.

Die Konstanz der Zusammensetzung der eingesetzten scherben ist für das Vermögen des ehnolzggregates, ein einwandfreies Glas zu erzeugen , von Bedeutung.The constancy of the composition of the cullet used is for the ability of the wood aggregate to produce perfect glass is important.

Beim Einsatz der in der Zusammensetzung wechselnden Fremdscherben muß eine entsprechend lange Schmelzzeit zur Erreichung einer vertretbaren Homogenität angesetzt werden, um die Zusammensetzung der Glasmasse durch strömungsbedingte Umwälzung auszugleichen und Scherben extrem fremder Zusammensetzung im eigenen Glasfluß aufzulösen. In der Praxis sind die durch die Scherben verursachten Inhomogenitä ten nicht immer in der Schmelze auszugleichen, die Folge sind Auswirkungen bei der Temperaturwechselbeständigkeit der Gläser, Berstdruckfestigkeit der Glaserzeugnisse und wechselnde hydrolytische Beständigkeit.When using the foreign shards, which change in composition must have a correspondingly long melting time to achieve acceptable homogeneity be set to the composition of the glass mass by flow-induced circulation equalize and dissolve fragments of extremely foreign composition in your own glass flow. In practice, the inhomogeneities caused by the cullet are not always th equalize in the melt, the consequences are effects in the resistance to temperature changes of glasses, burst strength of glass products and changing hydrolytic Resistance.

Neben den Mängeln die durch das ungünstige Einschmelzverhalten der Premdscherben selbst entstehen, treten auch mit den Scherben eingebrachte Verunreinigungen auf, die zu Schmelzschwierigkeiten führen können.In addition to the defects caused by the unfavorable melting behavior of the The fragments themselves arise, and there is also contamination brought in with the fragments which can lead to melting difficulties.

Durch die Erfindung sollen die bei der herkömmlichen Technologie mit dem Einsatz von Scherben auftretenden Nachteile, z.B. Beeinträchtigung der Schmelzleistung der Aggregate, Veränderung der Formbarkeit des Glases durch Inhomogenitäten, Sprödigkeit und Verunreinigungen durch Fremdscherbon, vermindert werden. Der Formbarkeitsbereich soll so verändert werden, daß die Viskositätseigenschaften den Bedingungen der maschinellen Verarbeitung besser angepaßt werden können und Leistungssteigerungen bzw. Erhöhungen des Produktionsvolumens möglich werden.The invention is intended to be used in the conventional technology the disadvantages associated with the use of cullet, e.g. impairment of the melting performance of aggregates, changes in the malleability of the glass due to inhomogeneities, brittleness and contamination by foreign sherds, can be reduced. The malleability area should be changed so that the viscosity properties meet the conditions of the machine Processing can be better adapted and performance increases or increases of the production volume become possible.

Zweck der Erfindung ist es, durch Veränderung der chemischen und physikalischen Eigenschaften des Glases die Wasser und Säurebeständigkeit und die Absorption von ultraviolettem Licht zu erhöhen; durch Verringerung des Ausdehnungskoeffidienten die Temperaturwechselbeständigkeit und durch Erhöhung der Zugfestigkeit die Berstdruckfestigkeit zu verbessern.The purpose of the invention is to change the chemical and physical Properties of the glass the water and acid resistance and the absorption of to increase ultraviolet light; by reducing the expansion coefficient the resistance to temperature changes and, by increasing the tensile strength, the bursting strength to improve.

Der Erfindung liegt die Aufgabe zugrunde, durch Veränderung der Gemengezusammensetzung die Möglichkeit su schaffen, den Scherbenanteil zu reduzieren. Durch die chemisch- und physi kalischen Eigenschaften der Gemengakomponanten gleichzeitig die Glasfarbe so zu beeinflussen, daß eine erhöhte Absorption von ultraviolettem Licht möglich wird und die für die maschinelle Verarbeitung günstige Viskosität der Glasschmelze und Gleichmäßigkeit in der Homogenität zu erreichen ist. Durch bestimmte Gemengebestandteile den Ausdehnungskoeffizienten und die Zugfestigkeit des Glases im Bin.The invention is based on the object by changing the composition of the batch create the possibility to reduce the amount of broken glass. Due to the chemically and physical properties of the batch components at the same time the color of the glass to influence so that an increased absorption of ultraviolet light is possible and the viscosity of the glass melt, which is favorable for machine processing and uniformity in homogeneity is to be achieved. Through certain batch components the expansion coefficient and the tensile strength of the glass in the bin.

blik auf das Anwendungsgebiet Hohlglas zu verbessern und die Säure- und Wasserbeständigkeit zu erhöhen.to improve the application area of hollow glass and to reduce the acidity and increase water resistance.

Erfindungsgemäß wird die Aufgabe dadurch gelöst, daß man vorzugsweise dem Behälterglasgemenge zerkleinerte Buntmetallschachtofenschlacke, bestehend aus SiO2, Al2O3, CaO, Fe2O3, MgO, R2O (Na2O + K2O) und Restoxyde (von Ti, Mn, Cu, Or) zu Lasten der Scherbenbeigabe zusetzt und die übrigen Gemengebestandteile darauf abstimmt. Der Anteil an Buntmetallschachtofenschlacke kann bis zu 90 % betragen, der übrige q?eil setzt sich aus Netzwerkbildnern und Netzwerkwandlern im bestimmten Verhältnis zusammen.According to the invention the object is achieved in that one preferably Non-ferrous metal shaft furnace slag comminuted from the container glass batch, existing from SiO2, Al2O3, CaO, Fe2O3, MgO, R2O (Na2O + K2O) and residual oxides (from Ti, Mn, Cu, Or) at the expense of adding cullet and adding the other ingredients to the batch votes. The proportion of non-ferrous metal shaft furnace slag can be up to 90%, the remaining part is made up of network formers and network converters in the particular Relationship together.

Claims

Patent claims:

1. A method for producing glass, in particular container glass, with improved thermal shock resistance, leaching resistance, mechanical Strength and absorption of ultraviolet rays, characterized in that in a batch of glass up to 90 / crushed non-ferrous metal shaft toenßschlacke den remaining shares of network formers and network converters added to the who.

2. The method according to claim 1, characterized in that in a batch of glass Crushed non-ferrous metal shaft furnace slag as coloring raw materials, depending on of the furnace atmosphere and the amount of slag added to create the colors grain to olive green, brown to black is added.