CZ284062B6

CZ284062B6 - Carpet structure and process for making the same

Info

Publication number: CZ284062B6
Application number: CZ943328A
Authority: CZ
Inventors: Joseph R. Pacione
Original assignee: Tac-Fast Systems Sa
Priority date: 1992-06-30
Filing date: 1993-06-30
Publication date: 1998-08-12
Also published as: ES2108288T3; HK1002820A1; HU9403834D0; EP0647111B1; DE69313637D1; SK161694A3; NZ254033A; GR3025562T3; RU2104874C1; CA2136210C; PL170948B1; BR9306624A; HU218066B; ATE157521T1; EP0647111A1; JPH07508436A; RU94046352A; AU665664B2; DE69313637T2; AU4554093A

Abstract

A carpet construction having an interposed layer of foam and a loop backing. The foam layer is manufactured with a fabric covering on both of its sides, the bottom covering having loops. A carpet backing is affixed to the foam sandwich using conventional methods. The foam sandwich can be secured to the carpet pile layer at the same time and with the same material that binds and seals the carpet pile layer. Alternatively, the foam sandwich can be manufactured, stored and later attached to the carpet which has previously been pre-coated with a binder.

Description

Vynález se týká konstrukce koberce, obzvláště koberce s použitým instalačním prostředkem háčku a smyčky a způsobu jeho výroby.The invention relates to the construction of a carpet, in particular to a carpet with a hook and loop installation means used, and to a method for its manufacture.

Dosavadní stav technikyBACKGROUND OF THE INVENTION

Jak je známo z US patentu č. 4,822,658, je možné vyrábět koberec, který se má instalovat například jako kobercovina ode zdi ke zdi, s uplatněním systému háčku a smyčky. U tohoto vynálezu se podle výhodného provedení vyrábí koberec se spodním povrchem pokrytým 15 vpodstatě smyčkami a tento koberec se instaluje s doplňkovým páskem, který obsahuje háčky, které jsou prozatímně zakryté. Tyto pásky se uloží na podlahu a podél okrajů v rozestupech, které odpovídají šířce koberce, nebo kdekoli, kde se požaduje dodatečné připevnění koberce k podlaze. Tyto pásky jsou obalené, aby se nepřilepily ke kličkám dříve, než se koberec uloží na místo, ustřihne a přilícuje. Obal pásku se pak strhne, aby se háčky obnažily a koberec přilnul 20 k podlaze.As is known from US Patent No. 4,822,658, it is possible to produce a carpet to be installed, for example, as a wall-to-wall carpet using a hook-and-loop system. In the present invention, according to a preferred embodiment, the carpet is made with a bottom surface substantially covered with loops 15, and the carpet is installed with an additional strip comprising hooks that are provisionally covered. These tapes are laid on the floor and along the edges at intervals that correspond to the width of the carpet or wherever additional carpet attachment to the floor is required. These tapes are wrapped to prevent them from sticking to the loops before the carpet is put in place, cut and aligned. The tape wrapping is then torn off to expose the hooks and the carpet adheres to the floor.

Tento patent také prozrazuje možnost upravené pěnové vrstvy mezi primární vrstvou, která obsahuje prošitá kobercová očka, a spodní smyčkovou podkladovou tkaninou.This patent also discloses the possibility of a modified foam layer between the primary layer comprising the stitched carpet loops and the lower looped backing fabric.

Patent 4,822,658 ukazuje koberec s pěnovou mezilehlou vrstvou. Přímá laminace může vést k dosažení konstrukce koberce, jak je zveřejněno v tomto patentu. Podle takového postupu se spodní smyčková vrstva laminuje na pěnu, zatímco se pěna formuje do vrstvy, takže se pěna vytvrzuje na rubu koberce, což má za následek připevnění podkličkované vrstvy k horní všívané vrstvě koberce s očky.No. 4,822,658 shows a carpet with a foam intermediate layer. Direct lamination may result in the construction of the carpet as disclosed in this patent. According to such a procedure, the lower loop layer is laminated to foam while the foam is formed into a layer such that the foam cures on the back of the carpet, resulting in the attachment of the peg layer to the upper tufted layer of the carpet with loops.

Hlavní nevýhodou takového uspořádání je to, že se má k pěnidlu přivést nedokončený koberec, aby se mohla laminace udělat na pěnicí lince, nebo musí případné výrobce koberců investovat do pěnícího strojního vybavení svojí továrny.The main disadvantage of such an arrangement is that an unfinished carpet is to be brought to the foamer so that the lamination can be done on the foaming line, or any carpet manufacturer has to invest in the foaming machinery of his factory.

Dále existuje značné napětí na použitou pěnu, když se připevňuje přímo ke koberci. Bez povlaku, který by dal pěně jakousi rozměrovou stálost, se může nepodložená pěna snadno přestřihnout, přetrhnout nebo se dokonce oddělit.Furthermore, there is considerable stress on the foam used when it is attached directly to the carpet. Without a coating that gives the foam some dimensional stability, the unsupported foam can easily be cut, torn or even detached.

Navíc by bylo u mnoha aplikací nanejvýš žádoucí, kdyby se mohla použít pěna o nižší měrné 40 hmotnosti. Avšak pokud se použije tento postup přímého nanášení pěny na primární vrstvu koberce, je normálně potřebná pěna o vyšší měrné hmotnosti, která by dodala pěně dostatečnou odolnost.Moreover, in many applications it would be highly desirable if a foam having a lower specific gravity of 40 could be used. However, when this method of directly applying foam to the primary carpet layer is used, a higher density foam is normally needed to impart sufficient resistance to the foam.

Některý koberec má podkladovou tkaninu, jako například akční podložení, z polypropylenu nebo 45 z juty na rubu. Přímé připevnění pěny k takovému podložení by mohlo snížit namáhání pěny, avšak pokusy toho dosáhnout způsobovaly problémy vzájemného oddělování vrstev pěny a akčního podložení.Some carpet has a backing fabric, such as an action backing, of polypropylene or 45 of jute on the reverse. Direct attachment of the foam to such a backing could reduce the stress on the foam, but attempts to achieve this have caused problems of separation of the foam layers and the action backing.

Nakonec toto nanášení pěny přímo na primární vrstvu koberce v otevřeném postupu normálně 50 vyžaduje, aby se na pěnu během jejího tuhnutí umístil nějaký povlak nebo smyčková podkladová tkanina, což může vyvolat další nevýhody.Finally, this application of the foam directly to the primary carpet layer in the open process normally requires that a coating or a looped backing fabric be placed on the foam during its setting, which may cause further disadvantages.

Podstata vynálezuSUMMARY OF THE INVENTION

Výše uvedené nedostatky do značné míry odstraňuje a vytvoření zlepšené konstrukce koberce, která zahrnuje vloženou vrstvu pěny a smyčkovou podkladovou tkaninu, řeší konstrukce koberce 5 podle vynálezu, jehož podstata spočívá v tom, že sestává z pěnové vrstvy s látkovými potahy na obou stranách této vrstvy, přičemž spodní látkový potah má smyčky, a tento pěnový sendvič je připevněný k podložení koberce za použití obvyklých postupů. Pěnový sendvič může být připevněný k vlasové vrstvě koberce současně a tímtéž materiálem, který pojí a těsní tuto vlasovou vrstvu koberce, to jest během procesu výroby, nebo se může pěnový sendvič vyrobit, skladovat 10 a připojit ke koberci, který· se předem povleče adhezním prostředkem, v některém následujícím kroku.The aforementioned drawbacks largely eliminate and the formation of an improved carpet structure comprising an intermediate foam layer and a looped backing fabric solves the carpet structure of the present invention, which consists of a foam layer with fabric covers on both sides of the layer, wherein the backing fabric has loops, and the foam sandwich is attached to the carpet backing using conventional techniques. The foam sandwich may be affixed to the pile carpet at the same time and with the same material that binds and seals the pile carpet, i.e. during the manufacturing process, or the foam sandwich may be manufactured, stored 10 and attached to a carpet that is pre-coated with adhesive , in any subsequent step.

Toto zlepšení dovoluje, aby se koberec, který obsahuje smyčkovou podkladovou tkaninu, vyrobil na stávajícím strojním vybavení, takže se předem existující, dříve vyrobená pěnová vrstva může 15 připojit pojivém nebo lepidlem krubu koberce při využití běžně dostupného konvenčního strojního zařízení na výrobu koberců.This improvement allows a carpet that comprises a looped backing fabric to be manufactured on existing machinery so that a pre-existing, previously manufactured foam layer can be bonded to the carpet binder or glue using conventional conventional carpet manufacturing machinery.

Kromě toho může výrobce koberců podle požadavků dodržet odlišné tloušťky nebo rozměry pěny pro pozdější připojení k různým vlasovým vrstvám koberce.In addition, the carpet manufacturer can adhere to different foam thicknesses or dimensions for later attachment to different pile carpet layers as desired.

Látkové potahy umístěné na obou stranách předem vyrobené pěnové vrstvy mohou také zvýšit rozměrovou stálost pěny, což dovoluje nižší měrnou hmotnost pěny, která se má použít, a může také u některého výhodného provedení dovolit použít pěny, která se netvaruje během procesu výroby, tedy například plátu pěny.Fabric coatings placed on both sides of the preformed foam layer can also increase the dimensional stability of the foam, allowing a lower density of foam to be used, and may also allow, in some preferred embodiments, the use of foam that does not form during the manufacturing process, e.g. foam.

Tkanina je přitom výhodnější než chemický potah nebo potah z polymeru, protože může pěně propůjčit rozměrovou stálost při současném zajištění určité ohebnosti a ochrany pěny před přetržením a lámáním.The fabric is more advantageous than a chemical or polymer coating, since it can confer dimensional stability to the foam while providing some flexibility and protection of the foam from tearing and breaking.

Podle vynálezu je výhodné, je-li látkový potah horního povrchu tkanina, která může mít chlupatý vnější povrch, jako je vlasová nebo smyčkovitá látka, s odstávajícími vlákny, což bude zlepšovat přilnavost k podložení koberce.According to the invention, it is preferred that the fabric coating of the top surface is a fabric that may have a shaggy outer surface, such as a pile or looped fabric, with standing fibers, which will improve adhesion to the carpet backing.

Zatímco se látkový potah může umístit na pěnu za využití běžných postupů, je u tohoto výhod35 něho provedení žádoucí umístit potah na povrch pěny poté, co byla pěna vytvarována. Toto zabraňuje vsakování pěny do látkového potahu, což je obvykle nežádoucí, zejména vzhledem ke spodnímu potahu pěnové vrstvy, která má smyčky potřebné pro připevnění koberce k podlaze.While the fabric coating can be placed on the foam using conventional techniques, in this advantageous embodiment 35 it is desirable to place the coating on the foam surface after the foam has been formed. This prevents the foam from seeping into the fabric covering, which is usually undesirable, especially with respect to the undercoat of the foam layer having the loops required to secure the carpet to the floor.

S výhodou tedy předložený vynález sestává z konstrukce koberce, zejména laminovaného 40 koberce pro připevnění k podlaze bez jakékoli zvláštní spodní podložky, který obsahuje primární vrstvu, která má vlasové elementy, pokrývající v podstatě první stranu této primární vrstvy, pěnovou vrstvu, která má první látkový potah na horním povrchu této vrstvy a druhý potah, který má obnažené smyčky, na svém spodním povrchu, prostředky pro zajištění prvního a druhého látkového potahu na pěnové vrstvě a adhezní prostředek pro zajištění spodního povrchu prvního 45 látkového potahu pěnové vrstvy na primární vrstvě tak, aby byly vlasové elementy a smyčky obnažené na lícových stranách koberce.Preferably, therefore, the present invention consists of a carpet structure, in particular a laminated carpet 40 for fastening to the floor without any particular backing comprising a primary layer having pile elements substantially covering the first side of the primary layer, a foam layer having a first fabric a coating on the upper surface of the layer and a second coating having the exposed loops on its lower surface, means for securing the first and second fabric coatings on the foam layer and adhesive means for securing the lower surface of the first 45 fabric coatings of the foam layer on the primary layer so the hair elements and loops were exposed on the front of the carpet.

Podle vynálezu je výhodné, zahmuje-li konstrukce koberce primární vrstvu, která má vlasové elementy všívané do této vrstvy a skrze tuto vrstvu, které v podstatě pokrývají první stranu 50 primární vrstvy, pěnovou vrstvu, která má první látkový potah, s obnaženými vlákny vyčnívajícími z horního povrchu této vrstvy a druhý látkový potah, který ukazuje smyčky na spodním povrchu této vrstvy a adhezní prostředek jednak pro zajištění prvního látkového potahu pěnové vrstvy na primární vrstvě tak, aby byla vyčnívající vlákna horního povrchu prvního potahu avšívaná očka vlasových elementů, sahající skrze primární vrstvu zajištěná k sobě, atak, abyAccording to the invention, it is preferred that the carpet structure comprises a primary layer having hair elements tufted into and through the layer which substantially cover the first side 50 of the primary layer, a foam layer having a first fabric coating with exposed fibers protruding from an upper fabric surface and a second fabric covering showing loops on the lower surface of the layer and an adhesive means for securing the first fabric coating of the foam layer on the primary layer such that the upper fiber surface of the first coating protruding; secured together, attack to

- 2 I byly vlasové elementy a smyčky spodního povrchu pěnové vrstvy obnažené na protějších lícových stranách laminace koberce.The hair elements and loops of the lower surface of the foam layer were exposed on opposite faces of the carpet lamination.

Přehled obrázků na výkresechOverview of the drawings

Některá tělesná vytvoření vynálezu jsou popsaná s poukazem na připojené výkresy, na kterých je na obr. 1 nárys řezu výhodného provedení laminovaného koberce podle vynálezu před instalací pěnové vrstvy na podložení koberce, a na obr. 2 nárys řezu tohoto výhodného provedení laminovaného koberce, u kterého jsou již pěnová vrstva a podložení koberce připojené k sobě.Some embodiments of the invention are described with reference to the accompanying drawings, in which Fig. 1 is a cross-sectional front view of a preferred embodiment of a laminated carpet according to the invention prior to installation of a foam layer on a carpet backing; the foam layer and the carpet backing are already joined together.

Příklady provedení vynálezuDETAILED DESCRIPTION OF THE INVENTION

Pokud se týká výkresů, představuje obrázek 1 běžné provedení koberce z polypropylenu nebo jiného běžného materiálu, který tvoří primární vrstvu 1, obsahující vlasové elementy 3 příze zajehlené skrze podložení do formy prošitých oček 5.Referring to the drawings, Figure 1 represents a conventional embodiment of a carpet of polypropylene or other conventional material that forms a primary layer 1 comprising the pile elements 3 of yarn needled through the backing in the form of stitched stitches 5.

Je ukázána také pěnová vrstva 7. Taková pěnová vrstva 7 může být tvořena jakýmkoli konvenčním prostředkem, jako je chemicky foukaný, pěněný nebo předem vy robený plát, nebo některým dalším prostředkem, který by vyvolával nezbytnou objemovou pružnost, pevnost ve střihu a pevnost v tahu. U tohoto výhodného provedení je k pěnové vrstvě 7 připevněný tkaný nebo netkaný smyčkovitý první a druhý látkový potah 9 a 11 poté, co se vrstva 7 vyrobí, za použití pojiv, laminace natavením nebo ultrazvukem či nějakým dalším způsobem, který vytváří dostatečnou pevnost při vrstveném odtrhávání bez nepatřičného vsakování do smyčkového látkového potahu a zajišťuje tak vysoký stupeň ohebnosti.A foam layer 7 is also shown. Such a foam layer 7 may be formed by any conventional means, such as a chemically blown, foamed or preformed sheet, or any other means that would produce the necessary volumetric elasticity, shear strength and tensile strength. In this preferred embodiment, a woven or nonwoven looped first and second fabric coverings 9 and 11 are attached to the foam layer 7 after the layer 7 has been manufactured, using binders, melting or ultrasonic lamination, or any other method that provides sufficient layered tear strength. without undue infiltration into the loop fabric coating and ensures a high degree of flexibility.

Avšak v některých případech je možné, i když to není obvykle výhodné, umístit první respektive druhý látkový potah 9, 11 na pěnovou vrstvu 7 během jejího tvarování nebo tuhnutí. V tomto případě nebudou přednosti řízení tloušťky a neprosakování potahu adekvátní konstrukci koberce, u které se nejprve tvářela pěnová vrstva 7, avšak ještě zde budou výhody pocházející z odděleného potahování a výroby vrstvy 7, jak bylo popsáno dříve.However, in some cases it is possible, although not usually preferred, to place the first and second fabric coatings 9, 11 on the foam layer 7 during its shaping or solidification. In this case, the advantages of controlling the thickness and leakage of the covering will not be adequate to the carpet construction in which the foam layer 7 was first formed, but still there will be advantages derived from separate coating and production of the layer 7, as previously described.

Umístění potahu na pěnovou vrstvu 7 předtím, než tato ztuhla, má nevýhody v tom, že je smyčková tkanina prosáklá do míry, která je nevýhodná, a pokud vrstva 7 ztvrdne kolem i ve smyčkové tkanině, může se vytvořit efekt zprkenatění.Placing the coating on the foam layer 7 before it has solidified has the disadvantage that the loop fabric is soaked to an extent that is disadvantageous, and if the layer 7 hardens around even in the loop fabric, a sintering effect can be created.

Infiltrace, která se může vyskytnout, může také zničit nebo překážet všem nebo některým ze smyček látkových potahů 9, 11 v plnění jejich funkce, jak byla určená, a to díky ztrátě jejich směrového pohybu. Dále tento způsob laminace během procesu výroby snižuje možnost zmenšit váhu smyčkové tkaniny rozvolněním počtu smyček. Rozvolnění počtu smyček pro snížení hmotnosti smyčkové tkaniny může způsobit další pronikání tekuté pěny, což by mohlo způsobit ronění tekuté pěny na druhou stranu smyčkové tkaniny atak eliminovat použití některých nebo všech smyček.The infiltration that may occur may also destroy or interfere with all or some of the loops of the fabric coatings 9, 11 in performing their function as determined, due to the loss of their directional movement. Furthermore, this lamination method during the manufacturing process reduces the possibility of reducing the weight of the loop fabric by loosening the number of loops. Loosening the number of loops to reduce the weight of the loop fabric may cause further penetration of the liquid foam, which could cause the liquid foam to flutter on the other side of the loop fabric and thus eliminate the use of some or all of the loops.

U vrstvy smyček je výhodné mít zachovanou schopnost roztahovat se do délky i do šířky. Rozvolněnější počet smyček a menší průnik pěny do vrstvy smyček může dovolit vrstvě smyček pracovat. To může umožnit, aby se kompletní kobercový výrobek se svojí připěněnou vloženou pěnovou poduškou sbaloval jednodušeji a byl ohebnější.In the loop layer, it is advantageous to have the ability to extend in length and width. A looser number of loops and less penetration of foam into the loop layer may allow the loop layer to operate. This may allow the complete carpet product with its foamed insert foam cushion to fold more easily and be more flexible.

- J CZ 284062 B6- J CZ 284062 B6

Průběžný způsob ukládání pěny během jejího připevňování kvlákennému odložení koberce navíc nevytváří nejúčinnější formu řízení rozměrů pěny. Poněvadž přímá laminace nevyžaduje výrobu pěny současně s jejím připevněním krubu koberce, je obtížné řídit přesný rozměr nebo výšku pěny během tohoto procesu.Moreover, the continuous method of storing the foam during its attachment to the fibrous matting of the carpet does not constitute the most effective form of controlling the dimensions of the foam. Since direct lamination does not require the production of foam at the same time as its attachment to the carpet neck, it is difficult to control the exact size or height of the foam during this process.

Nicméně se může hlavních výhod vynálezu dosáhnout pokrytím pěny tkaninou na obou jejích stranách, jak je popsáno, a pro některé výrobce to s jejich stávajícím strojním vybavením může být zpočátku jednodušší, když přidávají tento potah během tuhnutí pěny, a to i přes další nevýhody.However, the main advantages of the invention can be achieved by covering the foam on both sides of the fabric as described, and for some manufacturers this with their existing machinery may initially be simpler when adding this coating during the foam solidification, despite other disadvantages.

S výhodou je smyčková tkanina druhého látkového potahu 11 uzavřená smyčka, čímž je míněno, že se smyčky pevně usadí do smyčkového podložení buď lepidlem, použitým pro připojení potahu k pěnové vrstvě 7, který se používá ve formě smyčkového materiálu, nebo podle nevýhodného provedení, infiltrací pěny do tkaniny. Bylo zjištěno, že ideální je pletenina, zejména osnovní nebo trikotový úplet proto, že má vhodný stupeň uzavření smyčky v tkanině. Takový osnovní nebo trikotový úplet se s výhodou použije pro obě smyčkové vrstvy prvního i druhého látkového potahu 9, 11, avšak může se také použít tkaný nebo jiný materiál. Výraz tkanina znamená nějaký tkaný, netkaný nebo slisovaný materiál z přírodních nebo umělých vláken.Preferably, the loop fabric of the second fabric coating 11 is a closed loop, meaning that the loops are firmly seated in the loop backing either by the adhesive used to attach the coating to the foam layer 7, which is used as a loop material, or foam into fabric. It has been found that a knit, especially a warp or leotard knit, is ideal because it has a suitable degree of loop closure in the fabric. Such a warp or tricot knit is preferably used for both the loop layers of the first and second fabric coatings 9, 11, but woven or other material may also be used. The term fabric means any woven, nonwoven or pressed material of natural or man-made fibers.

Vrstvy smyček prvního a druhého látkového potahu 9 a 11 nemusejí být z téhož materiálu, ani nemusejí mít stejnou pevnost. Vrstva smyček prvního látkového potahu 9 je méně kritická a s výhodou má smyčky nebo odstávající vlákna, která napomáhají přilnutí k prošitým očkům 5 podložení. Vhodných potahů, které mají požadovanou pevnost, ohebnost a schopnost přilnout k pěné, je mnoho.The loop layers of the first and second fabric coatings 9 and 11 need not be of the same material, nor do they have the same strength. The loop layer of the first fabric coating 9 is less critical and preferably has loops or protruding fibers to assist adhesion to the stitched loops 5 of the backing. Suitable coatings having the required strength, flexibility and adhesion properties are numerous.

Jak bylo dříve uvedeno, je první látkový potah 9 s výhodou pletenina nebo jiný materiál s uzavřenou smyčkou, avšak samozřejmě by to mohla být i látka, která má spíše odstávající vlákna než smyčky, což je například mnoho jehlovaných materiálů nebo plst či další druhy smyčkovitých tkanin, ve kterých nejsou smyčky držené na místě pevně. Navrhuje se proto, aby odstávající vlákna vyplňov ala primární vrstvu £ koberce a napomáhala v přilnutí pěnové vrstvy 7 k primární vrstvě £ koberce. Normálně bude mít koberec podložení z polypropylenu, avšak vynález by fungoval stejně dobře i s kobercem bez zřetelného podložení, u kterého tvoří primární vrstvu £ osnova a útek koberce.As mentioned earlier, the first fabric coating 9 is preferably knit or other closed loop material, but of course it could also be a fabric that has more outgoing fibers than loops, such as many needles or felt or other types of loop fabric in which the loops are not held firmly in place. It is therefore proposed that the outgoing fibers fill the primary layer 6 of the carpet and assist in adhering the foam layer 7 to the primary layer 6 of the carpet. Normally, the carpet will have a polypropylene backing, but the invention would work equally well with a carpet without a distinct backing in which the warp and weft of the carpet form the primary layer.

U tělesného vytvoření podle obrázku 1 se může pěnový materiál dopravovat a skladovat jednodušeji, když byl předtím na obou stranách potažený smyčkovou tkaninou prvního a druhého látkového potahu 9, 11, než pokud potažený není. Nepotažená pěna se párá, trhá a špiní snadněji a není tak vhodná pro manipulaci, přepravování a skladování. Smyčkový potah po obou stranách pěny dodává navíc pěně značně zvýšenou pevnost ve střihu a v tahu při současném zachování a možná dokonce zlepšení přirozené pružnosti pěny.In the embodiment of Figure 1, the foam material can be transported and stored more easily if it has been previously coated on both sides with a loop fabric of the first and second fabric coatings 9, 11 than if it is not coated. Uncoated foam mats, tears and stains more easily and is thus not suitable for handling, transport and storage. In addition, the loop coating on both sides of the foam gives the foam a considerably increased shear and tensile strength while maintaining and possibly even improving the natural flexibility of the foam.

Výhodná konstrukce využívá plát pěny, protože s plátem pěny je řízení šířky a tloušťky jednodušší než u jiných způsobů výroby pěny.The preferred design utilizes a foam sheet because with the foam sheet, width and thickness control is easier than other foam manufacturing methods.

Obrázek 2 představuje koberec s pěnovou vrstvou 7, usazenou na podložení koberce. Pěnová vrstva 7 se může ukládat za použití běžných pracovních postupů při využití nějakého adhezního prostředku 13, jako pojivá nebo lepidla. Pokud se použije smyčkovitá tkanina, je výhodné, pronikne-li lepidlo aspojí-li smyčkový materiál prvního látkového potahu 9 a prošitá očka 5 koberce k sobě.Figure 2 shows a carpet with a foam layer 7 mounted on a carpet backing. The foam layer 7 may be deposited using conventional techniques using an adhesive 13, such as a binder or an adhesive. If a loop fabric is used, it is preferred that the adhesive penetrates and the loop material of the first fabric cover 9 and the stitched eyelets 5 of the carpet bond together.

Toto pojivo se může nanášet za využití běžného strojního zařízení na výrobu koberců buď v jednosledovém systému, při kterém koná používané pojivo práci zalití prošitého spoje i sekundární laminace podložení předem vyrobené potažené pěnové vrstvy 7, nebo na konci linky či v nespřaženém systému dodatečné laminace, čímž se vyztužuje běžné primární podložení seThis binder can be applied using conventional carpet manufacturing machinery either in a one-time system in which the used binder performs the work of embedding the stitched joint and the secondary lamination of the pre-coated foam layer backing 7, or reinforces the normal primary underlay

-4 I skrze prošitou přízí za využití vhodného povlaku, například povlaku dotykem, lepicího pojivá pro laminování předem zhotoveného plátového pěnového sendviče. Výsledný výrobek může mít zvýšenou rozměrovou stálost, lepší provázání všitých ok a větší ohebnost.Even through the stitched yarn using a suitable coating, for example a touch coating, an adhesive binder for laminating a preformed sheet foam sandwich. The resulting product can have increased dimensional stability, better sewing of stitches and greater flexibility.

Tento koberec se může vy rábět jako rozměrově ohraničené kusy nebo v rolích pro pokládání ode zdi ke zdi. Nicméně tento vynález představuje největší přínos u instalace ode zdi ke zdi, kde rozměrová stálost dlouhých okrajů koberce a obtíže s instalací představují markantnější problémy.This carpet can be cut as dimensionally limited pieces or in rolls for laying from wall to wall. However, the present invention represents the greatest benefit in wall-to-wall installation, where the dimensional stability of the long edges of the carpet and the difficulty in installing present significant problems.

Claims

A construction of a carpet, in particular a laminated carpet, for attachment to a floor without a separate backing having a primary layer with pile elements covering the first side of the primary layer and loops on the bottom surface, the pile elements and loops being exposed on opposite faces of the carpet and between them is a foam layer, characterized in that the foam layer (7) has a first fabric coating (9) on the upper surface and a second fabric coating (11) on the lower surface and having exposed loops, wherein both the first and the second fabric-coating (9). 9, 11) is secured to the foam layer (7) by the securing means, while the upper surface of the first fabric covering (9) of the foam layer (7) is attached to the primary layer (1) by the adhesive means (13).

Carpet construction according to claim 1, characterized in that the exposed loops cover the lower surface of the foam layer (7).

Carpet construction according to claim 2, characterized in that the exposed loops of the second fabric cover (11) are locked into the fabric of the cover (11).

The carpet structure of claim 3, the cover (11) being a knitted fabric.

The carpet structure of claim 3, the cover (11) being a woven fabric.

characterized in that the second cloth is characterized by the second cloth

Carpet construction according to claim 3, characterized in that the cover (9) is a fabric with exposed outgoing fibers.

that the first cloth

Carpet construction according to claim 6, characterized in that the first fabric coating (9) is attached to the primary layer (1) by an adhesive applied to the entire surface of the second side of the primary layer (1) and soaked into the protruding fibers of the first fabric coating (9). ).

Carpet construction according to claim 7, characterized in that the protruding fibers of the first fabric covering (9) are loops interlocked in the fabric of the covering (9).

Carpet construction according to claim 2, characterized in that the loops of the second fabric covering (11) are anchored in the foam layer (7) by the rigid foam of the layer (7) itself.

Carpet construction according to claim 9, characterized in that the first fabric cover (9) has exposed loops protruding upwardly from its upper surface and the loops are bound to the cover (9) and firmly clamped by the solidified foam layer (7).

The carpet structure of claim 2, having a uniform cross-section.

Carpet construction according to claim 3, characterized in that the fabric coverings (9,

11) are attached to the surface of the foam layer (7) by foam penetrating the fabric of the coverings (9, 11).

Carpet construction according to claim 12, characterized in that the foam layer (7) consists of a pre-fabricated foam sheet.

Carpet construction according to claim 12, characterized in that the foam layer (7) is a chemically blown layer.

Carpet construction according to claims 1 to 14, characterized in that the pile elements (3) are tufted into and through the primary layer (1), while the exposed fibers of the first fabric covering (9) of the foam layer (7) are sewn. protruding from the upper surface of the layer (7) and the adhesive means (13) for securing the first fabric coating (9) of the foam layer (7) on the primary layer (1) such that the fibers of the upper surface of the first fabric coating (9) are exposed and stitched The eyelets (5) that extend through the primary layer (1) are held firmly together, the adhesive means.

Carpet construction according to claim 15, characterized in that the second fabric covering (11) is adhered to the surface of the foam layer (7) by foam penetrating into the second fabric covering (11).

The carpet structure of claim 16, wherein the first fabric cover (9) is adhered to the surface of the foam layer (7) by foam penetrating into the cover.

Method for forming a carpet structure according to claims 1 to 17, characterized in that a foam sandwich is produced having a foam layer (7) in the center to which two outer fabric coverings (9, 11) are attached, at least one of of these coatings (9, 11) having loops over their entire surface, a pile of carpet having a exposed carpet pile is made on one surface, whereupon the foam sandwich is attached to the pile layer such that the carpet pile and loops are exposed on opposite faces carpets.

The method according to claim 18, characterized in that, in order to prevent substantial penetration of the foam into the fabric coatings (9, 11), an additional basic solidification of the foam is carried out before the coatings are fixed.