CN1277887C - Method for producing fibee reinforced composite board - Google Patents
Method for producing fibee reinforced composite board Download PDFInfo
- Publication number
- CN1277887C CN1277887C CN 00122907 CN00122907A CN1277887C CN 1277887 C CN1277887 C CN 1277887C CN 00122907 CN00122907 CN 00122907 CN 00122907 A CN00122907 A CN 00122907A CN 1277887 C CN1277887 C CN 1277887C
- Authority
- CN
- China
- Prior art keywords
- add
- reinforced composite
- composite board
- water
- industrial residue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides a method for producing a fiber reinforced composite board. The present invention has an essential technical scheme that (1) plant fiber materials and industrial waste fine materials are mixed in the proportion 1: 0.3 to 0.8; (2) adhesives are added; (3) materials are paved in a mold net for forming board blanks; (4) the board blanks are pressed and shaped. Compared with the prior art, the present invention has the advantages of thermal insulation, light weight, etc. Thereby, the present invention is suitable for buildings.
Description
The present invention relates to the manufacture method of a kind of wallboard for building, particularly dead meal and the industrial residue material with plant is that main raw material is processed into, and has the manufacture method of the structural sheeting of insulated fire, water-proof function.
Present structural sheeting, all by concrete prefabricated one-tenth, the advantage of concrete prefabricated board is: intensity is big.Shortcoming is: load is heavy; Heat-insulating property is poor; Need use a large amount of cement aborning, and cement belongs to pollutent.
The object of the present invention is to provide a kind of manufacture method of fibee reinforced composite board for building, it can avoid the deficiency of concrete prefabricated board.
The object of the present invention is achieved like this: it is to process as main raw material with dead meal of plant and industrial residue, and its practice is:
1, the dead meal of plant being separated into diameter is 0.1-0.5mm, long fibrous for 2-5mm, and its water ratio is controlled at 3-8%.
2, industrial residue processing is broken into 50-80 order granular powder.
3, in Vegetrable fibre material: the ratio of industrial residue powder=1: 0.3-0.8, with the two mixing and mix evenly.
4, in above-mentioned steps 1 or 3 to Vegetrable fibre material prevent fires, water-fast and mildew-resistant handles.
5, add binding agent, add-on is the 10-25% of whole material.
6, install lay wire (the nylon grid does not have anti-grid, woven wire etc.).
7, under the 80-150 temperature, unit pressure suppresses at 0.15-0.4Mpa, becomes the wallboard in band lay wire cavity.
Know after testing, with the wallboard that the present invention makes, its thermal conductivity is 1/10th of a common brick, the wallboard made from the present invention, when thickness is 75cm, its heat insulation effect is equivalent to 4 times of the thick common brick of 240cm, and under equal volume, the weight of the wallboard that the present invention makes is 1/10th of common brick, therefore, the wallboard that the present invention makes is compared with common brick, has good heat insulating, intensity height, characteristics such as free from environmental pollution, and it will become the substitute of traditional materials for wall.
Below provide three embodiment and further specify the present invention:
Embodiment one:
Farm crop straw, bar, straw fiber φ 0.3mm, long 3mm: industrial residue flyash=1: 0.3, add mineral binder bond, add-on is 25% of a whole material, mix does not evenly have conglomeration, controls total water ratio 18%, and does fire prevention, water-fast and mildew-resistant processing.Install lay wire, core rod, the fiber material of mixing evenly is paved into slab.80 ℃ of temperature, unit pressure 0.25Mpa compacting down forms.
Embodiment two:
With wood working tankage fiber (wood shavings, sawdust) the φ 0.2mm after performing fire prevention, water-fast and mildew-resistant and handling, long 2mm: industrial residue slag granular powder=1: 0.4, add organic binder bond, add-on is 10% of a whole material, mix even no conglomeration, install lay wire, core rod, the fiber material that mixes is evenly mated formation into slab, 150 ℃ of temperature, unit pressure 0.35Mpa compacting down forms.
Embodiment three:
With the farm crop straw fiber material φ 0.3mm after performing fire prevention, water-fast and mildew-resistant and handling, long 3mm: industrial residue perlite (or vermiculite) mine tailing=1: 0.6,16% the organic and inorganic binder mixture (organic binder bond: mineral binder bond=1: 0.1) that adds whole material, 120 ℃ of temperature, unit pressure 0.15Mpa compacting forms.
Claims (4)
1, a kind of manufacture method of fibee reinforced composite board is characterized in that:
(1) dead meal of plant being separated into diameter is 0.1-0.5mm, long fibrous for 2-5mm, and its water ratio is controlled at 3-8%;
(2) industrial residue processing is broken into 50-80 order granular powder;
(3) in Vegetrable fibre material: the ratio of industrial residue powder=1: 0.3-0.8, with the two mixing and mix evenly;
(4) in above-mentioned steps 1 or 3 to Vegetrable fibre material prevent fires, water-fast and mildew-resistant handles;
(5) add binding agent, add-on is the 10-25% of whole material;
(6) install lay wire;
(7) under 80-150 ℃, 0.15-0.4Mpa, be pressed into the wallboard that has the lay wire hole.
2, according to the manufacture method of the described fibee reinforced composite board of claim 1, it is characterized in that: diameter is farm crop straw, bar, the straw fiber of 0.3mm, long 3mm: industrial residue flyash=1: 0.3, add mineral binder bond, add-on is 25% of a whole material, and mix does not evenly have conglomeration, controls total water ratio 18%, and do fire prevention, water-fast and mildew-resistant is handled, install lay wire, core rod, the fiber material of mixing evenly is paved into slab, under 80 ℃, 0.25Mpa, suppress forming.
3, according to the manufacture method of the described fibee reinforced composite board of claim 1, it is characterized in that: the diameter after will performing fire prevention, water-fast and mildew-resistant and handling is 0.2mm, long 2mm wood working tankage fiber: industrial residue slag granular powder=1: 0.4, add organic binder bond, add-on is 10% of a whole material, mix even no conglomeration, install lay wire, core rod, the fiber material that mixes is evenly mated formation into slab, under 150 ℃, 0.35MPa, suppress forming.
4, according to the manufacture method of the described fibee reinforced composite board of claim 1, it is characterized in that: will perform fire prevention, diameter after water-fast and mildew-resistant is handled is 0.3mm, long 3mm farm crop straw fiber material: industrial residue perlite tailing=1: 0.6,16% the organic and inorganic binder mixture that adds whole material, organic binder bond wherein: mineral binder bond=1: 0.1, under 120 ℃, 0.15Mpa, suppress forming.