CN111484816A - 一种环保型水性折边胶及其制备方法 - Google Patents
一种环保型水性折边胶及其制备方法 Download PDFInfo
- Publication number
- CN111484816A CN111484816A CN201911262221.5A CN201911262221A CN111484816A CN 111484816 A CN111484816 A CN 111484816A CN 201911262221 A CN201911262221 A CN 201911262221A CN 111484816 A CN111484816 A CN 111484816A
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- emulsion
- environment
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种环保型水性折边胶，按重量份计，包括以下原料：天然橡胶乳液40‑45份，丙烯酸乳液20‑40份，增粘树脂10‑20份，水10‑20份，氧化锌1‑3份，抗氧剂2‑3份，增稠剂1‑3份。相较于传统的粉胶，本发明产品可以节省3/4的胶水用量，且喷胶所需的人力也较少；本发明的水性喷胶的环保要求符合欧盟标准，完全以水作为溶剂，VOC排量较低，耐热性好；本发明的水性喷胶使用时喷涂均匀、干燥快、初期粘力好，维持时间长，不易爆开；本发明的水性喷胶生产工艺简单，没有中间污染物的排放；本发明中丙烯酸乳液的加入增加了橡胶的粘力，提高了耐老化性，并且降低了成本。
Description
技术领域
本发明涉及一种环保型水性折边胶及其制备方法。
背景技术
在皮鞋生产中，鞋帮(面)周边经削薄后再叠起，并用胶黏剂粘牢，这种胶黏剂称为折边胶。目前市面上主要使用油性喷胶来作为折边胶，油性喷胶中含有机溶剂，导致VOC排放量较高，其中含有很多对人体有害的成分，易挥发进入空气污染环境，同时也影响人们的健康。
目前，市面上也出现了比较环保的水性喷胶，其以水作为溶剂取代有机溶剂，特点是无毒环保，对环境友好，然而一般的水性喷胶来作折边胶使用，粘结效果一般，干燥速度较慢，且耐热性、耐老化性也比较差，影响了皮鞋的生产质量。
发明内容
针对上述现有技术存在的问题，本发明提供一种环保型水性折边胶及其制备方法。
为了实现上述目的，本发明采用的一种环保型水性折边胶，按重量份计，包括以下原料：天然橡胶乳液40-45份，丙烯酸乳液20-40份，增粘树脂10-20份，水10-20份，氧化锌1-3份，抗氧剂2-3份，增稠剂1-3份。
作为优选，所述天然橡胶乳液的固含量为60％。
作为优选，所述丙烯酸乳液的固含量为60％，玻璃化温度在-40℃到-10℃，含有可交联基团。
作为优选，所述增粘树脂采用水性松香树脂、水性改性松香乳液、水性萜烯增粘乳液、水性萜烯酚醛树脂乳液中的一种或几种的混合。
作为优选，所述抗氧剂采用抗氧剂1010。
作为优选，所述水、天然橡胶、丙烯酸乳液与增粘树脂的质量比为1:4:3:2。
作为优选，所述增稠剂采用丙烯酸。
另外，本发明还提供了一种所述环保型水性折边胶的制备方法，包括以下步骤：
(1)分别称取配方量的天然橡胶乳液、丙烯酸乳液、增粘树脂、水、氧化锌、抗氧剂和增稠剂；
(2)将配方量的水先倒入搅拌槽中，并开机搅拌；
(3)将天然橡胶乳液和丙烯酸乳液倒入搅拌槽，搅拌30分钟，待乳液与水混合均匀后，加入氧化锌和抗氧剂；
(4)继续搅拌30分钟后，加入增粘树脂，继续搅拌至混合均匀；
(5)加入增稠剂调节粘度到600-4000mPa·s，即得产品。
与现有技术相比，本发明的有益效果是：
(1)相较于传统的粉胶，本发明产品可以节省3/4的胶水用量，且喷胶所需的人力也较少，该水性喷胶单人即可使用(传统的粉胶使用时需要多人配合上胶)。
(2)本发明的水性喷胶的环保要求符合欧盟标准，完全以水作为溶剂，VOC排量较低，耐热性好。
(3)本发明的水性喷胶使用时喷涂均匀、干燥快、初期粘力好，维持时间长，不易爆开。
(4)本发明的水性喷胶生产工艺简单，没有中间污染物的排放。
(5)本发明中丙烯酸乳液的加入增加了橡胶的粘力，提高了耐老化性，并且降低了成本。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚明了，下面对本发明进行进一步详细说明。但是应该理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限制本发明的范围。
实施例1
一种环保型水性折边胶的制备方法，包括以下步骤：
(1)称取天然橡胶乳液40份(固含量为60％)、丙烯酸乳液(固含量为60％，玻璃化温度在-40℃到-10℃，含有可交联基团)30份、水性萜烯酚醛树脂乳液20份、水10份、氧化锌1份、抗氧剂1010 2份、丙烯酸乳液增稠剂2份；
(2)将称取的水先倒入搅拌槽中，并开机搅拌；
(3)将称取的天然橡胶乳液和丙烯酸乳液倒入搅拌槽，搅拌30分钟，待乳液与水混合均匀后，加入抗氧剂1010和氧化锌；
(4)继续搅拌30分钟后，加入称取的水性萜烯酚醛树脂乳液，继续搅拌至混合均匀；
(5)加入丙烯酸乳液增稠剂调整粘度到1000mPa·s，取出产品。
实施例2
一种环保型水性折边胶的制备方法，包括以下步骤：
(1)称取天然橡胶乳液40份(固含量为60％)、丙烯酸乳液(固含量为60％，玻璃化温度在-40℃到-10℃，含有可交联基团)33份、水性萜烯酚醛树脂乳液15份、水7份、氧化锌1份、抗氧剂1010 2份、丙烯酸乳液增稠剂2份；
(2)将称取的水先倒入搅拌槽中，并开机搅拌；
(3)将称取的天然橡胶乳液和丙烯酸乳液倒入搅拌槽，搅拌30分钟，待乳液与水混合均匀后，加入抗氧剂1010和氧化锌；
(4)继续搅拌30分钟后，加入称取的水性萜烯酚醛树脂乳液，继续搅拌至混合均匀；
(5)加入丙烯酸乳液增稠剂调整粘度到1000mPa·s，取出产品。
实施例3
一种环保型水性折边胶的制备方法，包括以下步骤：
(1)称取天然橡胶乳液43份、丙烯酸乳液30份、水性松香树脂15份、水7份、氧化锌1份、抗氧剂1010 2份、丙烯酸乳液增稠剂2份；
(2)将称取的水先倒入搅拌槽中，并开机搅拌；
(3)将称取的天然橡胶乳液和丙烯酸乳液倒入搅拌槽，继续搅拌30分钟后，待乳液与水混合均匀，加入抗氧剂1010和氧化锌；
(4)继续搅拌30分钟后，加入称取的水性松香树脂，搅拌至混合均匀；
(5)加入丙烯酸乳液增稠剂调整粘度到1000mPa·s，取出产品。
对上述实施例制得的环保型水性折边胶进行性能测试，并与传统水性喷胶、传统粉胶施胶后起黏时间和黏合性对比，结果如下表1所示。
表1不同折边胶的起黏时间和黏合性对比
| 起黏时间(获得一定粘接强度的时间) | 对PU革的剥离力 | |
| 实施例1 | 50秒 | 30N |
| 实施例2 | 51秒 | 30N |
| 实施例3 | 48秒 | 32N |
| 传统水性喷胶 | 3分钟 | 21N |
| 传统粉胶 | 2分钟 | 15N |
分析表1可知，相较于传统水性喷胶使用的氯丁乳液等，本发明使用了成本更低的丙烯酸乳液，成本大幅度降低。本发明的环保型水性折边胶施胶后起黏时间快于传统的水性喷胶和传统的粉胶，工人们上胶效率提高，并大大的节省工时，提高工作效率。本发明折边胶的粘力明显提高，效率更高，黏性更好，且本发明的环保型水性折边胶以水为溶剂，将胶水对环境的污染降到最低。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换或改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种环保型水性折边胶，其特征在于，按重量份计，包括以下原料：天然橡胶乳液40-45份，丙烯酸乳液20-40份，增粘树脂10-20份，水10-20份，氧化锌1-3份，抗氧剂2-3份，增稠剂1-3份。
2.根据权利要求1所述的一种环保型水性折边胶，其特征在于，所述天然橡胶乳液的固含量为60％。
3.根据权利要求1所述的一种环保型水性折边胶，其特征在于，所述丙烯酸乳液的固含量为60％，玻璃化温度在-40℃到-10℃，含有可交联基团。
4.根据权利要求1所述的一种环保型水性折边胶，其特征在于，所述增粘树脂采用水性松香树脂、水性改性松香乳液、水性萜烯增粘乳液、水性萜烯酚醛树脂乳液中的一种或几种的混合。
5.根据权利要求1所述的一种环保型水性折边胶，其特征在于，所述抗氧剂采用抗氧剂1010。
6.根据权利要求1所述的一种环保型水性折边胶，其特征在于，所述水、天然橡胶、丙烯酸乳液与增粘树脂的质量比为1:4:3:2。
7.根据权利要求1所述的一种环保型水性折边胶，其特征在于，所述增稠剂采用丙烯酸。
8.一种权利要求1-7任一项所述环保型水性折边胶的制备方法，其特征在于，包括以下步骤：
(1)分别称取配方量的天然橡胶乳液、丙烯酸乳液、增粘树脂、水、氧化锌、抗氧剂和增稠剂；
(2)将配方量的水先倒入搅拌槽中，并开机搅拌；
(3)将天然橡胶乳液和丙烯酸乳液倒入搅拌槽，搅拌30分钟，待乳液与水混合均匀后，加入氧化锌和抗氧剂；
(4)继续搅拌30分钟后，加入增粘树脂，继续搅拌至混合均匀；
(5)加入增稠剂调节粘度到600-4000mPa·s，即得产品。