CN110526666A - 一种高强度隔音泡沫混凝土 - Google Patents
一种高强度隔音泡沫混凝土 Download PDFInfo
- Publication number
- CN110526666A CN110526666A CN201910914492.8A CN201910914492A CN110526666A CN 110526666 A CN110526666 A CN 110526666A CN 201910914492 A CN201910914492 A CN 201910914492A CN 110526666 A CN110526666 A CN 110526666A
- Authority
- CN
- China
- Prior art keywords
- high strength
- foam concrete
- agent
- concrete
- strength sound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高强度隔音泡沫混凝土，由以下成分组成：硅酸盐水泥、粉煤灰、复合起泡剂、脱硫石膏、二氧化硅微粉、萘磺酸盐减水剂、河砂、甲基羟丙基纤维素醚、水玻璃、植物纤维、亚硝酸钙、隔音剂和水。该混凝土方通过加入二氧化硅微粉、水玻璃和亚硝酸钙，可以显著提升混凝土的抗压强度；加入氮掺杂淀粉基活性炭微球材料作为隔音剂，隔音效果非常好，同时加入该改性活性炭微球材料还可以进一步提升混凝土的抗压强度。
Description
技术领域
本发明涉及混凝土技术领域，尤其涉及一种高强度隔音泡沫混凝土。
背景技术
随着经济发展，混凝土的使用量越来越大，泡沫混凝土通常是用机械方法将泡沫剂水溶液制备成泡沫，再将泡沫加入到含硅质材料、钙质材料、水及各种外加剂等组成的料浆中，经混合搅拌、浇注成型、养护而成的一种多孔材料。
目前常规的泡沫混凝土主要关注其隔热性能，对泡沫混凝土的强度和隔音效果关注度不够，尤其是在保证混凝土强度的前提下如何提高隔音效果尚没有有效的办法，故本发明提供了一种高强度隔音泡沫混凝土。
发明内容
基于背景技术存在的技术问题，本发明提出了一种高强度隔音泡沫混凝土。
本发明的技术方案如下：
一种高强度隔音泡沫混凝土，由以下成分组成：硅酸盐水泥、粉煤灰、复合起泡剂、脱硫石膏、二氧化硅微粉、萘磺酸盐减水剂、河砂、甲基羟丙基纤维素醚、水玻璃、植物纤维、亚硝酸钙、隔音剂和水。
优选的，所述的高强度隔音泡沫混凝土，由以下百分比的成分组成：硅酸盐水泥25-33％、粉煤灰15-20％、复合起泡剂3-6％、脱硫石膏1-3％、二氧化硅微粉2-5％、萘磺酸盐减水剂1-3％、河砂10-15％、甲基羟丙基纤维素醚2-5％、水玻璃1-2％、植物纤维2-5％、亚硝酸钙0.5-1％、隔音剂2-4％、水余量。
优选的，所述的硅酸盐水泥为水泥强度等级等于或者高于42.5的硅酸盐水泥。
优选的，所述的复合起泡剂为由烷基聚葡糖苷、季戊四醇硬脂酸酯、双氧水组成。
优选的，所述的河砂为粒径为1-3mm的河砂。
优选的，所述的植物纤维为棉纤维、麻纤维、蚕丝纤维中的任意一种或者多种的任意比的组合。
优选的，所述的植物纤维为纺织行业中天然纤维的边角料。
优选的，所述的隔音剂为氮掺杂淀粉基活性炭微球材料。
进一步优选的，所述的氮掺杂淀粉基活性炭微球材料，直径为5-10μm、比表面积为1000-3000m2/g，含氮量为6-10％。
本发明的有益之处在于：本发明的高强度隔音泡沫混凝土，由以下成分组成：硅酸盐水泥、粉煤灰、复合起泡剂、脱硫石膏、二氧化硅微粉、萘磺酸盐减水剂、河砂、甲基羟丙基纤维素醚、水玻璃、植物纤维、亚硝酸钙、隔音剂和水。该混凝土方通过加入二氧化硅微粉、水玻璃和亚硝酸钙，可以显著提升混凝土的抗压强度；加入氮掺杂淀粉基活性炭微球材料作为隔音剂，隔音效果非常好，同时加入该改性活性炭微球材料还可以进一步提升混凝土的抗压强度。
具体实施方式
实施例1：
一种高强度隔音泡沫混凝土，由以下百分比的成分组成：由以下百分比的成分组成：硅酸盐水泥28％、粉煤灰17％、复合起泡剂5％、脱硫石膏2％、二氧化硅微粉4％、萘磺酸盐减水剂1.5％、河砂12％、甲基羟丙基纤维素醚3％、水玻璃1.5％、植物纤维3％、亚硝酸钙0.8％、隔音剂2.8％、水余量。
所述的硅酸盐水泥为水泥强度等级为42.5的硅酸盐水泥。
所述的复合起泡剂为由烷基聚葡糖苷、季戊四醇硬脂酸酯、双氧水组成。
所述的河砂为粒径为1-3mm的河砂。
所述的植物纤维为棉纤维的边角料。
所述的隔音剂为氮掺杂淀粉基活性炭微球材料。
所述的氮掺杂淀粉基活性炭微球材料，直径为5-10μm、比表面积为1000-3000m2/g，含氮量为6-10％。
实施例2：
一种高强度隔音泡沫混凝土，由以下百分比的成分组成：由以下百分比的成分组成：硅酸盐水泥33％、粉煤灰15％、复合起泡剂6％、脱硫石膏1％、二氧化硅微粉5％、萘磺酸盐减水剂1％、河砂15％、甲基羟丙基纤维素醚2％、水玻璃2％、植物纤维2％、亚硝酸钙1％、隔音剂2％、水余量。
所述的硅酸盐水泥为水泥强度等级为42.5R的硅酸盐水泥。
所述的复合起泡剂为由烷基聚葡糖苷、季戊四醇硬脂酸酯、双氧水组成。
所述的河砂为粒径为1-3mm的河砂。
所述的植物纤维为棉纤维、麻纤维、蚕丝纤维混合纤维的边角料。
所述的隔音剂为氮掺杂淀粉基活性炭微球材料。
所述的氮掺杂淀粉基活性炭微球材料，直径为5-10μm、比表面积为1000-3000m2/g，含氮量为6-10％。
实施例3：
一种高强度隔音泡沫混凝土，由以下百分比的成分组成：由以下百分比的成分组成：硅酸盐水泥25％、粉煤灰20％、复合起泡剂3％、脱硫石膏3％、二氧化硅微粉2％、萘磺酸盐减水剂3％、河砂10％、甲基羟丙基纤维素醚5％、水玻璃1％、植物纤维5％、亚硝酸钙0.5％、隔音剂4％、水余量。
所述的硅酸盐水泥为水泥强度等级为42.5的硅酸盐水泥。
所述的复合起泡剂为由烷基聚葡糖苷、季戊四醇硬脂酸酯、双氧水组成。
所述的河砂为粒径为1-3mm的河砂。
所述的植物纤维为棉纤维和麻纤维混合纤维的边角料。
所述的隔音剂为氮掺杂淀粉基活性炭微球材料。
所述的氮掺杂淀粉基活性炭微球材料，直径为5-10μm、比表面积为1000-3000m2/g，含氮量为6-10％。
对比例1
将实施例1中的氮掺杂淀粉基活性炭微球材料替换为常规的活性炭材料，其余配比不变。
对比例2
将实施例1中的氮掺杂淀粉基活性炭微球材料去除，其余配比不变。
以下对实施例1-3和对比例1-2的样品进行性能测试，得到如下测试结果，具体测试结果见表1。
表1：样品的性能测试结果：
| 实施例1 | 实施例2 | 实施例3 | 对比例1 | 对比例2 | |
| 密度(kg/m<sup>3</sup>) | 315 | 318 | 312 | 315 | 332 |
| 28d抗压强度(MPa) | 7.82 | 7.78 | 7.71 | 3.19 | 2.85 |
| 隔音系数(dB) | 97 | 94 | 99 | 67 | 46 |
由以上测试数据可以知道，采用本发明的高强度隔音泡沫混凝土加入氮掺杂淀粉基活性炭微球材料，可以显著提升混凝土的抗压强度以及隔音效果。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (9)
1.一种高强度隔音泡沫混凝土，其特征在于，由以下成分组成：硅酸盐水泥、粉煤灰、复合起泡剂、脱硫石膏、二氧化硅微粉、萘磺酸盐减水剂、河砂、甲基羟丙基纤维素醚、水玻璃、植物纤维、亚硝酸钙、隔音剂和水。
2.如权利要求1所述的高强度隔音泡沫混凝土，其特征在于，由以下百分比的成分组成：硅酸盐水泥 25-33%、粉煤灰 15-20%、复合起泡剂 3-6%、脱硫石膏 1-3%、二氧化硅微粉2-5%、萘磺酸盐减水剂 1-3%、河砂 10-15%、甲基羟丙基纤维素醚 2-5%、水玻璃 1-2%、植物纤维 2-5%、亚硝酸钙 0.5-1%、隔音剂 2-4%、水 余量。
3.如权利要求1所述的高强度隔音泡沫混凝土，其特征在于，所述的硅酸盐水泥为水泥强度等级等于或者高于42.5的硅酸盐水泥。
4.如权利要求1所述的高强度隔音泡沫混凝土，其特征在于，所述的复合起泡剂为由烷基聚葡糖苷、季戊四醇硬脂酸酯、双氧水组成。
5.如权利要求1所述的高强度隔音泡沫混凝土，其特征在于，所述的河砂为粒径为1-3mm的河砂。
6.权利要求1所述的高强度隔音泡沫混凝土，其特征在于，所述的植物纤维为棉纤维、麻纤维、蚕丝纤维中的任意一种或者多种的任意比的组合。
7.如权利要求1所述的高强度隔音泡沫混凝土，其特征在于，所述的植物纤维为纺织行业中天然纤维的边角料。
8.如权利要求1所述的高强度隔音泡沫混凝土，其特征在于，所述的隔音剂为氮掺杂淀粉基活性炭微球材料。
9.如权利要求8所述的高强度隔音泡沫混凝土，其特征在于，所述的氮掺杂淀粉基活性炭微球材料，直径为5-10μm、比表面积为1000-3000m2/g，含氮量为6-10％。