CN103184558A - 超细旦涤纶预取向丝的生产方法 - Google Patents
超细旦涤纶预取向丝的生产方法 Download PDFInfo
- Publication number
- CN103184558A CN103184558A CN 201110452117 CN201110452117A CN103184558A CN 103184558 A CN103184558 A CN 103184558A CN 201110452117 CN201110452117 CN 201110452117 CN 201110452117 A CN201110452117 A CN 201110452117A CN 103184558 A CN103184558 A CN 103184558A
- Authority
- CN
- China
- Prior art keywords
- spinning
- production method
- denier polyester
- superfine denier
- oriented yarn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种超细旦涤纶预取向丝的生产方法，包括以下步骤：以PET切片为原料，依次经过预结晶器、干燥塔、螺杆挤压机、过滤器、纺丝箱体、计量泵、纺丝组件、侧吹风、上油和卷绕，所说的干燥温度为160-170摄氏度；所说的组件压力为12-18MPa；所说的纺丝温度为299摄氏度；所说的侧吹风温度为20-24摄氏度，湿度为75%，风速为0.3-0.5m/s；所说的上油率为0.4-0.6%；所说的纺丝速度为2800-3300m/min。本发明的超细旦涤纶预取向丝的生产方法，具有如下技术效果：生产出的超细旦涤纶预取向丝性能良好，质量稳定，线密度为166dtex，断裂强度为2.45cN/dtex，断裂伸长率为107%。
Description
技术领域
本发明涉及一种超细旦涤纶预取向丝的生产方法，属于化纤技术领域。
背景技术
超细旦涤纶预取向丝其制成的织物具有手感柔软、吸湿性好的优点，因此市场应用广泛、前景广阔。
现有的超细旦涤纶预取向丝的生产方法生产出的超细旦涤纶预取向丝产品质量不稳定，导致产量低，成本高。
发明内容
本发明的目的是克服现有技术的不足之处，提供一种超细旦涤纶预取向丝的生产方法。
本发明的超细旦涤纶预取向丝的生产方法，包括以下步骤：以PET切片为原料，依次经过预结晶器、干燥塔、螺杆挤压机、过滤器、纺丝箱体、计量泵、纺丝组件、侧吹风、上油和卷绕，
所说的干燥温度为160-170摄氏度；
所说的组件压力为12-18MPa；
所说的纺丝温度为299摄氏度；
所说的侧吹风温度为20-24摄氏度，湿度为75%，风速为0.3-0.5m/s；
所说的上油率为0.4-0.6%；
所说的纺丝速度为2800-3300m/min。
本发明的超细旦涤纶预取向丝的生产方法，具有如下技术效果：生产出的超细旦涤纶预取向丝性能良好，质量稳定，线密度为166dtex，断裂强度为2.45cN/dtex，断裂伸长率为107%。
具体实施方式
实施例1
本实施例的超细旦涤纶预取向丝的生产方法，包括以下步骤：以PET切片为原料，依次经过预结晶器、干燥塔、螺杆挤压机、过滤器、纺丝箱体、计量泵、纺丝组件、侧吹风、上油和卷绕，所说的干燥温度为160-170摄氏度；所说的组件压力为12-18MPa；所说的纺丝温度为299摄氏度；所说的侧吹风温度为20-24摄氏度，湿度为75%，风速为0.3-0.5m/s；所说的上油率为0.4-0.6%；所说的纺丝速度为2800-3300m/min。
Claims (1)
1.超细旦涤纶预取向丝的生产方法，包括以下步骤：以PET切片为原料，依次经过预结晶器、干燥塔、螺杆挤压机、过滤器、纺丝箱体、计量泵、纺丝组件、侧吹风、上油和卷绕，
其特征在于，
所说的干燥温度为160-170摄氏度；
所说的组件压力为12-18MPa；
所说的纺丝温度为299摄氏度；
所说的侧吹风温度为20-24摄氏度，湿度为75%，风速为0.3-0.5m/s；
所说的上油率为0.4-0.6%；
所说的纺丝速度为2800-3300m/min。