CN101143988A - Water-based flame-retardant fireproof wood paint - Google Patents
Water-based flame-retardant fireproof wood paint Download PDFInfo
- Publication number
- CN101143988A CN101143988A CNA2006101269839A CN200610126983A CN101143988A CN 101143988 A CN101143988 A CN 101143988A CN A2006101269839 A CNA2006101269839 A CN A2006101269839A CN 200610126983 A CN200610126983 A CN 200610126983A CN 101143988 A CN101143988 A CN 101143988A
- Authority
- CN
- China
- Prior art keywords
- water
- flaming
- emulsion
- carpentry paint
- water anti
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a coating, in particular to a water-based flame-retardant fireproof wood lacquer, which comprises a base material, a flame retardant, water, a wetting agent, a film-forming auxiliary agent, a flatting agent, a preservative, a wax emulsion and a thickening agent, wherein the base material is an organic silicon acrylic acid polymer and comprises the following components in percentage by weight: base emulsion: 75-80, flame retardant: 8-15, 4-6 parts of water, and a wetting agent: 0.05-0.2, film-forming assistant: 4-6, leveling agent: 0.1-0.2, preservative: 0.05-0.2, wax emulsion: 1-3, thickening agent: 0.1-0.3, the wood lacquer has good flame retardant effect and good paint decoration effect.
Description
Technical field:
The present invention relates to a kind of coating, is a kind of water anti-flaming carpentry paint specifically.
Background technology
Along with the development of society, paint when playing beauty function, also has provide protection in the widespread use of various fields, has corrosion-resistant, ageing-resistant effect.For example in the application of wood surface, effect attractive in appearance, protection possesses simultaneously.But since wooden be combustible material, therefore paint also is to be made of chemical substances such as resins, when realizing attractive in appearance, preservative activity, is in and lives and the needs of production safety, fire protection flame retarding becomes urgent problem.Along with development of science and technology, fire retardant is brought into use in every field, and the especially application in paint, but because the effect of the chemistry of fire retardant own and physical attribute has influence on the effect such as bright and clean, anticorrosion of paint.Therefore how to make paint promptly reach the effect of fire-retardant fireproof, do not influence the decoration of paint, effect such as anticorrosion again, become the technical problem that need improve constantly.
Goal of the invention:
The present invention aims to provide a kind of water anti-flaming carpentry paint, has flame retardant efficiency, and does not influence the paint decorative effect.
Summary of the invention:
In order to realize the purpose of this invention, water anti-flaming carpentry paint of the present invention is achieved by the following scheme:
A kind of water anti-flaming carpentry paint is characterized in that comprising base-material, fire retardant, water, wetting agent, film coalescence aid, flow agent, sanitas, wax emulsion, thickening material, and described base-material is the acid-organosilicon crylic acid polymkeric substance, and its composition component ratio is:
Matrix emulsion: 75-80
Fire retardant: 8-15
Water: 4-6
Wetting agent: 0.05-0.2
Film coalescence aid: 4-6
Flow agent: 0.1-0.2
Sanitas: 0.05-0.2
Wax emulsion: 1-3
Thickening material: 0.1-0.3
Aforesaid water anti-flaming carpentry paint is characterized in that, described base-material is a pure-acrylic emulsion.
Aforesaid water anti-flaming carpentry paint is characterized in that, described base-material is an aqueous polyurethane emulsion.
Aforesaid water anti-flaming carpentry paint is characterized in that, described base-material is a water-borne acrylic resin.
Aforesaid water anti-flaming carpentry paint is characterized in that, described base-material is an aqueous polyurethane dispersion.
Aforesaid water anti-flaming carpentry paint is characterized in that, described base-material is the aqueous acrylamide polyaminoester emulsion.
Aforesaid water anti-flaming carpentry paint is characterized in that, described film coalescence aid is one or more in butyl glycol ether, 12 methyl alcohol of alcohol ester, the propylene glycol propyl ether.
The production method of aforesaid water anti-flaming carpentry paint obtains by physical method mixing, stirring, impurity elimination.
Embodiment:
Below in conjunction with example the embodiment of this invention is described, but does not do restriction this summary of the invention.
Embodiment 1:
A kind of water anti-flaming carpentry paint is formed by following material combination, and acid-organosilicon crylic acid polymkeric substance, fire retardant, water, wetting agent, film coalescence aid, flow agent, sanitas, wax emulsion, thickening material, described base-material are that its ingredient components ratio is:
Acid-organosilicon crylic acid polymkeric substance: 77
Fire retardant: 12
Water: 4
Wetting agent: 0.1
Film coalescence aid (butyl glycol ether): 4.5
Flow agent: 0.15
Sanitas: 0.1
Wax emulsion: 1
Thickening material: 0.15
The production method of this water anti-flaming carpentry paint is:
With starting dispersator in the acid-organosilicon crylic acid polymer emulsion adding stirred pot, under the speed that Revolution Per Minute 600 changes, add the wax emulsion, stirred 20 minutes, slowly adding fire retardant, stirred 15 minutes.Slowly add entry and film coalescence aid then, sanitas, flow agent, wetting agent stirred 20 minutes, added thickening material afterwards and stirred 20-30 minute.Last filtering and impurity removing gets final product.
Embodiment 2:
A kind of water anti-flaming carpentry paint, form by following material combination, acid-organosilicon crylic acid polymkeric substance, fire retardant, water, wetting agent, film coalescence aid, flow agent, sanitas, wax emulsion, thickening material, described base-material are aqueous polyurethane emulsion, and its composition component ratio is:
Aqueous polyurethane emulsion: 77
Fire retardant: 12
Water: 4
Wetting agent: 0.1
Film coalescence aid (propylene glycol propyl ether): 4.5
Flow agent: 0.15
Sanitas: 0.1
Wax emulsion: 1
Thickening material: 0.15
The production method of this water anti-flaming carpentry paint is:
Aqueous polyurethane emulsion added start dispersator in the stirred pot, under the speed that Revolution Per Minute 500-800 changes, add the wax emulsion, stirred 20 minutes,, stirred 15 minutes at slow adding fire retardant.Slowly add entry and film coalescence aid then, sanitas, flow agent, wetting agent stirred 20 minutes, added thickening material afterwards and stirred 20-30 minute.Last filtering and impurity removing gets final product.
Embodiment 3:
A kind of water anti-flaming carpentry paint is formed by following material combination, and acid-organosilicon crylic acid polymkeric substance, fire retardant, water, wetting agent, film coalescence aid, flow agent, sanitas, wax emulsion, thickening material, described base-material are that its ingredient components ratio is:
Water-borne acrylic resin: 78
Fire retardant: 9
Water: 5.5
Wetting agent: 0.1
Film coalescence aid (12 methyl alcohol of alcohol ester): 5
Flow agent: 0.2
Sanitas: 0.1
Wax emulsion: 2
Thickening material: 0.1
The production method of this water anti-flaming carpentry paint is:
With starting dispersator in the water-borne acrylic resin emulsion adding stirred pot, under the speed that Revolution Per Minute 500-800 changes, add the wax emulsion, stirred 20 minutes, slowly adding fire retardant, stirred 15 minutes.Slowly add entry and film coalescence aid then, sanitas, flow agent, wetting agent stirred 20 minutes, added thickening material afterwards and stirred 20-30 minute.Last filtering and impurity removing gets final product.
Embodiment 4:
A kind of water anti-flaming carpentry paint is formed by following material combination, and acid-organosilicon crylic acid polymkeric substance, fire retardant, water, wetting agent, film coalescence aid, flow agent, sanitas, wax emulsion, thickening material, described base-material are that its ingredient components ratio is:
Aqueous polyurethane dispersion: 78
Fire retardant: 9
Water: 5.5
Wetting agent: 0.1
Film coalescence aid (butyl glycol ether): 5
Flow agent: 0.2
Sanitas: 0.1
Wax emulsion: 2
Thickening material: 0.1
The production method of this water anti-flaming carpentry paint is:
With starting dispersator in the aqueous polyurethane dispersion emulsion adding stirred pot, under the speed that Revolution Per Minute 500-800 changes, add the wax emulsion, stirred 20 minutes, slowly adding fire retardant, stirred 15 minutes.Slowly add entry and film coalescence aid then, sanitas, flow agent, wetting agent stirred 20 minutes, added thickening material afterwards and stirred 20-30 minute.Last filtering and impurity removing gets final product.
Embodiment 5:
A kind of water anti-flaming carpentry paint is formed by following material combination, and acid-organosilicon crylic acid polymkeric substance, fire retardant, water, wetting agent, film coalescence aid, flow agent, sanitas, wax emulsion, thickening material, described base-material are that its ingredient components ratio is:
Aqueous acrylamide polyaminoester emulsion: 75
Fire retardant: 14
Water: 4.5
Wetting agent: 0.2
Film coalescence aid (butyl glycol ether): 4
Flow agent: 0.2
Sanitas: 0.2
Wax emulsion: 1.6
Thickening material: 0.3
The production method of this water anti-flaming carpentry paint is:
With starting dispersator in the aqueous acrylamide polyaminoester emulsion adding stirred pot, under the speed that Revolution Per Minute 500-800 changes, add the wax emulsion, stirred 20 minutes, slowly adding fire retardant, stirred 15 minutes.Slowly add entry and film coalescence aid then, sanitas, flow agent, wetting agent stirred 20 minutes, added thickening material afterwards and stirred 20-30 minute.Last filtering and impurity removing gets final product.
Claims (8)
1. a water anti-flaming carpentry paint is characterized in that comprising base-material, fire retardant, water, wetting agent, film coalescence aid, flow agent, sanitas, wax emulsion, thickening material, and described base-material is the acid-organosilicon crylic acid polymkeric substance, and its composition component ratio is:
Base-material emulsion: 75-80
Fire retardant: 8-15
Water: 4-6
Wetting agent: 0.05-0.2
Film coalescence aid: 4-6
Flow agent: 0.1-0.2
Sanitas: 0.05-0.2
Wax emulsion: 1-3
Thickening material: 0.1-0.3.
2. water anti-flaming carpentry paint according to claim 1 is characterized in that, described base-material is a pure-acrylic emulsion.
3. water anti-flaming carpentry paint according to claim 1 is characterized in that, described base-material is an aqueous polyurethane emulsion.
4. water anti-flaming carpentry paint according to claim 1 is characterized in that, described base-material is a water-borne acrylic resin.
5. water anti-flaming carpentry paint according to claim 1 is characterized in that, described base-material is an aqueous polyurethane dispersion.
6. water anti-flaming carpentry paint according to claim 1 is characterized in that, described base-material is the aqueous acrylamide polyaminoester emulsion.
7. water anti-flaming carpentry paint according to claim 1 is characterized in that, described film coalescence aid is one or more in butyl glycol ether, 12 methyl alcohol of alcohol ester, the propylene glycol propyl ether.
8. the production method of water anti-flaming carpentry paint according to claim 1 is characterized in that, obtains by physical method mixing, stirring, impurity elimination.