CN100417737C - Alloy, method for preparing the alloy and method for producing jewelry - Google Patents
Alloy, method for preparing the alloy and method for producing jewelry Download PDFInfo
- Publication number
- CN100417737C CN100417737C CNB2006101530405A CN200610153040A CN100417737C CN 100417737 C CN100417737 C CN 100417737C CN B2006101530405 A CNB2006101530405 A CN B2006101530405A CN 200610153040 A CN200610153040 A CN 200610153040A CN 100417737 C CN100417737 C CN 100417737C
- Authority
- CN
- China
- Prior art keywords
- parts
- chain
- platinum
- chain body
- solder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
技术领域 technical field
本发明涉及贵金属加工技术领域，尤其是合金、该合金的制备方法及生产饰品的方法The invention relates to the technical field of precious metal processing, especially alloys, methods for preparing the alloys and methods for producing ornaments
背景技术 Background technique
在贵金属加工领域，饰品在制备过程中要用到大量的焊料，所用焊料占最终产品的30％-40％，如果在制备贵金属饰品中所用焊料的熔点温度与该贵金属链身料的熔点温度相差不大，在焊接时焊料和链身料一起熔化，影响产品后继生产加工，进而影响到饰品的产品质量。In the field of precious metal processing, a large amount of solder is used in the preparation process of jewelry, and the solder used accounts for 30%-40% of the final product. If the melting point temperature of the solder used in the preparation of precious metal jewelry is different from that of the precious metal chain body Not much, the solder and the chain body melt together during welding, which affects the subsequent production and processing of the product, and then affects the product quality of the jewelry.
在现有技术中，铂金饰品的焊料，按重量组分配比为：67份的，15份的钯，18份的银，该焊料的熔点为摄氏温度：900度至950度，铂金的熔点为摄氏温度：1752度，铂金饰品焊料的熔点温度与铂金的熔点温度相差比较大，但铂金饰品的焊料中不含铂，影响到铂金饰品的成色。In the prior art, the solder of platinum ornaments has a ratio of 67 parts by weight, 15 parts of palladium, and 18 parts of silver. The melting point of the solder is 900 to 950 degrees Celsius, and the melting point of platinum is Celsius temperature: 1752 degrees, the melting point temperature of platinum jewelry solder is quite different from that of platinum, but the solder of platinum jewelry does not contain platinum, which affects the fineness of platinum jewelry.
钯金饰品的焊料，按重量组分配比为：60份的钯，36.5份的银，3.5份的黄铜，该焊料的熔点为摄氏温度：1000度至1100度，钯金的熔点为摄氏温度：1550度，钯金饰品焊料的熔点温度与钯金的熔点温度相差很大，但钯金饰品的焊料中钯的含量不是很高，影响到钯金饰品的成色。Solder for palladium jewelry, the distribution ratio by weight is: 60 parts of palladium, 36.5 parts of silver, and 3.5 parts of brass. The melting point of the solder is Celsius: 1000 to 1100 degrees. The melting point of palladium is Celsius : 1550 degrees, the melting point temperature of the palladium jewelry solder is very different from that of palladium, but the content of palladium in the solder of the palladium gold jewelry is not very high, which affects the fineness of the palladium jewelry.
发明内容 Contents of the invention
本发明要解决的问题是提供一种合金、该合金的制备方法及生产饰品的方法，能够在铂金饰品、钯金饰品加工的过程中避免因焊料的熔点与链身料的熔点相差不大及焊料成色偏低而影响饰品的成色、质量。The problem to be solved by the present invention is to provide an alloy, a method for preparing the alloy, and a method for producing jewelry, which can avoid problems caused by the difference between the melting point of the solder and the melting point of the chain material during the processing of platinum jewelry and palladium jewelry. The fineness of solder is low, which affects the fineness and quality of jewelry.
为解决上述技术问题，本发明的目的是通过以下技术方案实现的：In order to solve the problems of the technologies described above, the purpose of the present invention is achieved through the following technical solutions:
一种合金，包括下列重量份数的组分：An alloy comprising the following components in parts by weight:
铂占89.5-90.5份、铟占3份、镓占3份、铜占3.5-4.5份。Platinum accounts for 89.5-90.5 parts, indium accounts for 3 parts, gallium accounts for 3 parts, and copper accounts for 3.5-4.5 parts.
一种合金的制备方法，包括：A method for preparing an alloy, comprising:
按重量组分配比89.5-90.5份的铂、3份的铟、3份的镓、3.5-4.5份的铜，配好后放到熔炼炉进行熔炼。89.5-90.5 parts of platinum, 3 parts of indium, 3 parts of gallium, and 3.5-4.5 parts of copper are distributed according to the weight group, and put into a smelting furnace for smelting after preparation.
可选的，所述熔炼炉的温度为摄氏温度为1000度至1400度的熔炼炉进行熔炼。Optionally, the temperature of the smelting furnace is 1000°C to 1400°C for smelting.
一种生产饰品的方法，包括：A method of producing an ornament, comprising:
(1)按重量组分99.95份的铂进行链身配料；(1) carry out chain body batching by the platinum of weight component 99.95 parts;
(2)按重量组分：89.5-90.5份的铂、3份的铟、3份的镓、3.5-4.5份的铜进行焊料配料；(2) By weight components: 89.5-90.5 parts of platinum, 3 parts of indium, 3 parts of gallium, 3.5-4.5 parts of copper for solder batching;
(3)将链身配料和焊料配料分别熔炼；(3) melting the chain body ingredients and solder ingredients respectively;
(5)对熔炼后链身料拉线；(5) pull the wire on the chain body after smelting;
(5)将拉好的链身线织链；(5) Weave the chain with the pulled chain body thread;
(6)将织链后的链身用拉线后的焊料进行表面焊接；(6) The chain body behind the woven chain is surface-welded with the solder behind the pull wire;
(7)表面焊接后的链身进行表面抛光；(7) The chain body after surface welding is surface polished;
(8)抛光后车花；(8) Car flowers after polishing;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，监测成色并电金。(10) After assembly, the surface is polished, the fineness is monitored and gold is electroplated.
可选的，所述熔炼后链身料拉线，包括：Optionally, the smelted chain body pull wire includes:
链身按客户的要求规格拉线，焊料按∮0.35毫米规格拉线。The chain body is pulled according to the specification required by the customer, and the solder is drawn according to the specification of ∮0.35mm.
一种合金，包括下列重量份数的组分：An alloy comprising the following components in parts by weight:
钯占97.5-98.5份、铟占0.7-1.2份、镓占0.55-1.55份、铁占0.25份。Palladium accounts for 97.5-98.5 parts, indium accounts for 0.7-1.2 parts, gallium accounts for 0.55-1.55 parts, and iron accounts for 0.25 parts.
一种合金的制备方法，包括：A method for preparing an alloy, comprising:
按重量组分配比97.5.5-98.5份的钯、0.7-1.2份的铟、0.55-1.55份的镓、0.25份的铁，配好后放到熔炼炉进行熔炼。97.5.5-98.5 parts of palladium, 0.7-1.2 parts of indium, 0.55-1.55 parts of gallium, and 0.25 parts of iron are distributed according to the weight group, and put into a smelting furnace for smelting after preparation.
可选的，所述熔炼炉的温度为摄氏温度为800度至1200度的熔炼炉进行熔炼。Optionally, the temperature of the smelting furnace is 800°C to 1200°C for smelting.
一种生产饰品的方法，包括：A method of producing an ornament, comprising:
(1)按重量组分99.95份的钯进行链身用料；(1) carry out chain body material by the palladium of 99.95 parts of weight components;
(2)按重量组分：97.5.5-98.5份的钯、0.7-1.2份的铟、0.55-1.55份的镓、0.25份的铁进行焊料配料；(2) By weight components: 97.5.5-98.5 parts of palladium, 0.7-1.2 parts of indium, 0.55-1.55 parts of gallium, 0.25 parts of iron for solder batching;
(3)将焊料配料熔炼；(3) Melting the solder ingredients;
(4)对链身料不需熔炼直接拉线；(4) The chain body material does not need to be smelted to pull the wire directly;
(5)将拉好的链身线织链；(5) Weave the chain with the pulled chain body thread;
(6)将织链后的链身用拉线后的焊料进行表面焊接；(6) The chain body behind the woven chain is surface-welded with the solder behind the pull wire;
(7)表面焊接后的链身进行表面抛光；(7) The chain body after surface welding is surface polished;
(8)抛光后车花；(8) Car flowers after polishing;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，检测成色并电金。(10) After assembly, the surface is polished, the color is tested and electroplated.
可选的，所述熔炼后链身配料拉线，包括：Optionally, the smelted chain body ingredient pull wire includes:
链身按客户的要求规格拉线，焊料按∮0.35毫米规格拉线。The chain body is pulled according to the specification required by the customer, and the solder is drawn according to the specification of ∮0.35 mm.
本发明通过提供了一种铂金饰品的焊料，按重量份数的组分组成为：按重量组分配比89.5-90.5份的铂、3份的铟、3份的镓、3.5-4.5份的铜，该焊料的熔点温度与铂金的熔点温度相差大，并且该焊料的含铂量较高，在生产铂金饰品时，能保证铂金饰品的成色；The present invention provides a solder for platinum ornaments. The components by weight are: 89.5-90.5 parts by weight of platinum, 3 parts of indium, 3 parts of gallium, and 3.5-4.5 parts of copper. The melting point temperature of the solder is quite different from that of platinum, and the solder has a higher platinum content, which can ensure the fineness of the platinum jewelry when producing platinum jewelry;
本发明还提供了一种钯金饰品的焊料，按重量份数的组分组成为：97.5.5-98.5份的钯、0.7-1.2份的铟、0.55-1.55份的镓、0.25份的铁，该焊料的熔点温度与钯金的熔点温度相差大，并且含钯量较高，在生产钯金饰品时，能保证钯金饰品的成色。The present invention also provides a solder for palladium-gold ornaments, the components in parts by weight are: 97.5.5-98.5 parts of palladium, 0.7-1.2 parts of indium, 0.55-1.55 parts of gallium, 0.25 parts of iron, The melting point temperature of the solder is quite different from that of palladium, and the content of palladium is relatively high, which can ensure the fineness of palladium jewelry when producing palladium jewelry.
具体实施方式 Detailed ways
本发明提供了一种合金、该合金的制备方法及生产饰品的方法，其核心在于，下面分别就该合金为铂金饰品焊料或者钯金饰品焊料时的两种情况列举实施例进行详细说明：The present invention provides an alloy, a method for preparing the alloy, and a method for producing ornaments. The core of the alloy is that the following two situations when the alloy is platinum ornament solder or palladium ornament solder are listed in detail for detailed description:
一、当所述合金为制备铂金饰品的焊料，该合金的制备方法为铂金饰品焊料的制备方法，生产饰品的方法为铂金饰品的生产方法时：One, when described alloy is the solder for preparing platinum jewelry, the preparation method of the alloy is the preparation method of platinum jewelry solder, and when the method for producing jewelry is the production method of platinum jewelry:
(一)铂金饰品的焊料组分，包括如下实施例：(1) The solder component of platinum ornaments, including following examples:
实施例一：所述合金包括下列重量份数的组分：Embodiment 1: The alloy includes the following components in parts by weight:
90份的铂、3份的铟、3份的镓、4份的铜；90 parts platinum, 3 parts indium, 3 parts gallium, 4 parts copper;
实施例二：所述合金包括下列重量份数的组分：Embodiment 2: The alloy includes the following components in parts by weight:
89.5份的铂、3份的铟、3份的镓、4.5份的铜；89.5 parts platinum, 3 parts indium, 3 parts gallium, 4.5 parts copper;
实施例三：所述合金包括下列重量份数的组分：Embodiment three: the alloy comprises the following components in parts by weight:
90.5份的铂、3份的铟、3份的镓、3.5份的铜。90.5 parts platinum, 3 parts indium, 3 parts gallium, 3.5 parts copper.
(二)铂金饰品焊料的制备方法，包括如下实施例：(2) the preparation method of platinum jewelry solder, comprising following embodiment:
实施例一：按重量组分配比：89.5份的铂、3份的铟、3份的镓、4.5份的铜进行配料，配好后放到摄氏温度为1000度的熔炼炉进行熔炼；Embodiment 1: According to the weight group distribution ratio: 89.5 parts of platinum, 3 parts of indium, 3 parts of gallium, and 4.5 parts of copper are used for batching, and after being prepared, they are put into a smelting furnace with a temperature of 1000 degrees Celsius for smelting;
实施例二：按重量组分配比：90.5份的铂、3份的铟、3份的镓、3.5份的铜进行配料，配好后放到摄氏温度为1400度的熔炼炉进行熔炼；Embodiment 2: According to the weight group distribution ratio: 90.5 parts of platinum, 3 parts of indium, 3 parts of gallium, and 3.5 parts of copper are used for batching, and after being prepared, they are put into a smelting furnace with a temperature of 1400 degrees Celsius for smelting;
实施例三：按重量组分配比：89.5份的铂、3份的铟、3份的镓、4.5份的铜进行配料，配好后放到摄氏温度为1400度的熔炼炉进行熔炼；Embodiment 3: According to the weight group distribution ratio: 89.5 parts of platinum, 3 parts of indium, 3 parts of gallium, and 4.5 parts of copper are used for batching, and after mixing, they are put into a smelting furnace with a temperature of 1400 degrees Celsius for smelting;
实施例四：按重量组分配比：90.5份的铂、3份的铟、3份的镓、3.5份的铜进行配料，配好后放到摄氏温度为1000度的熔炼炉进行熔炼。Embodiment 4: According to the proportion of weight group: 90.5 parts of platinum, 3 parts of indium, 3 parts of gallium, and 3.5 parts of copper are used for batching, and after the preparation, they are put into a melting furnace with a temperature of 1000 degrees Celsius for melting.
实施例五：按重量组分配比：90份的铂、3份的铟、3份的镓、4份的铜进行配料，配好后放到摄氏温度为1000度的熔炼炉进行熔炼；Embodiment 5: according to the weight group distribution ratio: 90 parts of platinum, 3 parts of indium, 3 parts of gallium, and 4 parts of copper are used for batching, and after being prepared, they are put into a smelting furnace with a temperature of 1000 degrees Celsius for smelting;
实施例六：按重量组分配比：90份的铂、3份的铟、3份的镓、4份的铜进行配料，配好后放到摄氏温度为1400度的熔炼炉进行熔炼；Embodiment 6: according to the weight group distribution ratio: 90 parts of platinum, 3 parts of indium, 3 parts of gallium, and 4 parts of copper are used for batching, and after being prepared, they are put into a smelting furnace with a temperature of 1400 degrees Celsius for smelting;
其中，所述熔炼炉的温度也可以为摄氏温度1200度，将上述各种按重量组分配比组成的焊料配好后放入熔炼炉熔炼即可得该合金。Wherein, the temperature of the smelting furnace can also be 1200 degrees centigrade, and the alloy can be obtained by mixing the above-mentioned various solders according to the proportions of weight components and putting them into the smelting furnace for smelting.
(三)生产铂金饰品950的方法，包括如下实施例：(3) the method for producing platinum ornament 950, comprises following embodiment:
实施例一：当焊料按重量组分为：89.5份的铂、3份的铟、3份的镓、4.5份的铜，包括下列步骤：Embodiment 1: When the solder is composed by weight: 89.5 parts of platinum, 3 parts of indium, 3 parts of gallium, and 4.5 parts of copper, the following steps are included:
(1)按重量组分99.95份的铂进行链身用料；(1) carry out chain body material by the platinum of 99.95 parts by weight components;
(2)按重量组分：89.5份的铂、3份的铟、3份的镓、4.5份的铜进行焊料配料；(2) By weight components: 89.5 parts of platinum, 3 parts of indium, 3 parts of gallium, 4.5 parts of copper for solder batching;
(3)将铂金链身配料放到摄氏温度1800度的熔炼炉进行熔炼，将铂金焊料放到摄氏温度1000度的熔炼炉进行熔炼；(3) Put the platinum chain body ingredients into a smelting furnace with a temperature of 1800 degrees Celsius for smelting, and put the platinum solder into a smelting furnace with a temperature of 1000 degrees Celsius for smelting;
(4)将熔炼好的料按要求拉线，链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) Pull the smelted material according to the requirements, the woven wire of the chain body is drawn according to the specifications required by the customer, and the solder is drawn according to the specification of ∮0.35mm;
(5)拉好的链身线用发到机织部织链；(5) The pulled chain body line is sent to the weaving department to weave the chain;
(6)将机织部织好的链身发到链部用所配铂金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with platinum ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，监测成色并电金。(10) After assembly, the surface is polished, the fineness is monitored and gold is electroplated.
其中，所述步骤(3)也可以为：将铂金链身料放到摄氏温度1800度的熔炼炉进行熔炼，将铂金焊料放到摄氏温度1200度的熔炼炉进行熔炼；Wherein, the step (3) can also be: putting the platinum chain body into a melting furnace with a temperature of 1800 degrees Celsius for melting, and putting the platinum solder into a melting furnace with a temperature of 1200 degrees Celsius for melting;
至此，完成了铂金950饰品的生产。So far, the production of platinum 950 jewelry has been completed.
实施例二：当焊料按重量组分为：90.5份的铂、3份的铟、3份的镓、3.5份的铜，包括下列步骤：Embodiment 2: When the solder is composed by weight: 90.5 parts of platinum, 3 parts of indium, 3 parts of gallium, and 3.5 parts of copper, the following steps are included:
(1)按重量组分99.95份的铂进行链身用料；(1) carry out chain body material by the platinum of 99.95 parts by weight components;
(2)按重量组分：90.5份的铂、3份的铟、3份的镓、3.5份的铜进行焊料配料；(2) By weight components: 90.5 parts of platinum, 3 parts of indium, 3 parts of gallium, 3.5 parts of copper for solder batching;
(3)将铂金链身配料放到摄氏温度1800度的熔炼炉进行熔炼，将铂金焊料放到摄氏温度1400度的熔炼炉进行熔炼；(3) Put the platinum chain body ingredients into a smelting furnace with a temperature of 1800 degrees Celsius for smelting, and put the platinum solder into a smelting furnace with a temperature of 1400 degrees Celsius for smelting;
(4)将熔炼好的料按要求拉线，链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) Pull the smelted material according to the requirements, the woven wire of the chain body is drawn according to the specifications required by the customer, and the solder is drawn according to the specification of ∮0.35mm;
(5)拉好的链身用机织线发到机织部织链；(5) The pulled chain body is sent to the weaving department with a woven thread to weave the chain;
(6)将机织部织好的链身发到链部用所配铂金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with platinum ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，监测成色并电金。(10) After assembly, the surface is polished, the fineness is monitored and gold is electroplated.
至此，完成了铂金950饰品的生产。So far, the production of platinum 950 jewelry has been completed.
其中，所述步骤(3)也可以为：将铂金链身配料放到摄氏温度1800度的熔炼炉进行熔炼，将铂金焊料放到摄氏温度1200度的熔炼炉进行熔炼；Wherein, the step (3) can also be: putting the platinum chain body ingredients into a melting furnace with a temperature of 1800 degrees Celsius for melting, and putting the platinum solder into a melting furnace with a temperature of 1200 degrees Celsius for melting;
实施例三：当焊料按重量组分为：89.5份的铂、3份的铟、3份的镓、4.5份的铜，包括下列步骤：Embodiment three: when the solder is composed by weight: 89.5 parts of platinum, 3 parts of indium, 3 parts of gallium, and 4.5 parts of copper, the following steps are included:
(1)按重量组分99.95份的铂进行链身用料；(1) carry out chain body material by the platinum of 99.95 parts by weight components;
(2)按重量组分：89.5份的铂、3份的铟、3份的镓、4.5份的铜进行焊料配料；(2) By weight components: 89.5 parts of platinum, 3 parts of indium, 3 parts of gallium, 4.5 parts of copper for solder batching;
(3)将铂金链身配料放到摄氏温度1800度的熔炼炉进行熔炼，将铂金焊料放到摄氏温度1400度的熔炼炉进行熔炼；(3) Put the platinum chain body ingredients into a smelting furnace with a temperature of 1800 degrees Celsius for smelting, and put the platinum solder into a smelting furnace with a temperature of 1400 degrees Celsius for smelting;
(4)将熔炼好的料按要求拉线，链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) Pull the smelted material according to the requirements, the woven wire of the chain body is drawn according to the specifications required by the customer, and the solder is drawn according to the specification of ∮0.35mm;
(5)拉好的链身用机织线发到机织部织链；(5) The pulled chain body is sent to the weaving department with a woven thread to weave the chain;
(6)将机织部织好的链身发到链部用所配铂金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with platinum ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，监测成色并电金。(10) After assembly, the surface is polished, the fineness is monitored and gold is electroplated.
至此，完成了铂金950饰品的生产。So far, the production of platinum 950 jewelry has been completed.
实施例四：当焊料按重量组分为：90.5份的铂、3份的铟、3份的镓、3.5份的铜，包括下列步骤：Embodiment 4: When the solder is composed by weight: 90.5 parts of platinum, 3 parts of indium, 3 parts of gallium, and 3.5 parts of copper, the following steps are included:
(1)按重量组分99.95份的铂进行链身用料；(1) carry out chain body material by the platinum of 99.95 parts by weight components;
(2)按重量组分：90.5份的铂、3份的铟、3份的镓、3.5份的铜进行焊料配料；(2) By weight components: 90.5 parts of platinum, 3 parts of indium, 3 parts of gallium, 3.5 parts of copper for solder batching;
(3)将铂金链身配料放到摄氏温度1800度的熔炼炉进行熔炼，将铂金焊料放到摄氏温度1000度的熔炼炉进行熔炼；(3) Put the platinum chain body ingredients into a smelting furnace with a temperature of 1800 degrees Celsius for smelting, and put the platinum solder into a smelting furnace with a temperature of 1000 degrees Celsius for smelting;
(4)将熔炼好的料按要求拉线，链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) Pull the smelted material according to the requirements, the woven wire of the chain body is drawn according to the specifications required by the customer, and the solder is drawn according to the specification of ∮0.35mm;
(5)拉好的链身用机织线发到机织部织链；(5) The pulled chain body is sent to the weaving department with a woven thread to weave the chain;
(6)将机织部织好的链身发到链部用所配铂金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with platinum ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，监测成色并电金。(10) After assembly, the surface is polished, the fineness is monitored and gold is electroplated.
至此，完成了铂金950饰品的生产。So far, the production of platinum 950 jewelry has been completed.
实施例五：当焊料按重量组分为：90份的铂、3份的铟、3份的镓、4份的铜，包括下列步骤：Embodiment five: when the solder is composed by weight: 90 parts of platinum, 3 parts of indium, 3 parts of gallium, and 4 parts of copper, the following steps are included:
(1)按重量组分99.95份的铂进行链身用料；(1) carry out chain body material by the platinum of 99.95 parts by weight components;
(2)按重量组分：90份的铂、3份的铟、3份的镓、4份的铜进行焊料配料；(2) By weight components: 90 parts of platinum, 3 parts of indium, 3 parts of gallium, 4 parts of copper for solder batching;
(3)将铂金链身配料放到摄氏温度1800度的熔炼炉进行熔炼，将铂金焊料放到摄氏温度1000度的熔炼炉进行熔炼；(3) Put the platinum chain body ingredients into a smelting furnace with a temperature of 1800 degrees Celsius for smelting, and put the platinum solder into a smelting furnace with a temperature of 1000 degrees Celsius for smelting;
(4)将熔炼好的料按要求拉线，链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) Pull the smelted material according to the requirements, the woven wire of the chain body is drawn according to the specifications required by the customer, and the solder is drawn according to the specification of ∮0.35 mm;
(5)拉好的链身用机织线发到机织部织链；(5) The pulled chain body is sent to the weaving department with a woven thread to weave the chain;
(6)将机织部织好的链身发到链部用所配铂金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with platinum ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，监测成色并电金。(10) After assembly, the surface is polished, the fineness is monitored and gold is electroplated.
至此，完成了铂金950饰品的生产。So far, the production of platinum 950 jewelry has been completed.
实施例六：当焊料按重量组分为：90份的铂、3份的铟、3份的镓、4份的铜，包括下列步骤：Embodiment 6: When the solder is composed by weight: 90 parts of platinum, 3 parts of indium, 3 parts of gallium, and 4 parts of copper, the following steps are included:
(1)按重量组分99.95份的铂进行链身用料；(1) carry out chain body material by the platinum of 99.95 parts by weight components;
(2)按重量组分：90份的铂、3份的铟、3份的镓、4份的铜进行焊料配料；(2) By weight components: 90 parts of platinum, 3 parts of indium, 3 parts of gallium, 4 parts of copper for solder batching;
(3)将铂金链身配料放到摄氏温度1800度的熔炼炉进行熔炼，将铂金焊料放到摄氏温度1400度的熔炼炉进行熔炼；(3) Put the platinum chain body ingredients into a smelting furnace with a temperature of 1800 degrees Celsius for smelting, and put the platinum solder into a smelting furnace with a temperature of 1400 degrees Celsius for smelting;
(4)将熔炼好的料按要求拉线，链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) Pull the smelted material according to the requirements, the woven wire of the chain body is drawn according to the specifications required by the customer, and the solder is drawn according to the specification of ∮0.35mm;
(5)拉好的链身用机织线发到机织部织链；(5) The pulled chain body is sent to the weaving department with a woven thread to weave the chain;
(6)将机织部织好的链身发到链部用所配铂金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with platinum ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊固并上扣组装；(9) Cut off the two ends according to the required length, weld and fasten the assembly;
(10)组装好后表面打磨，监测成色并电金。(10) After assembly, the surface is polished, the fineness is monitored and gold is electroplated.
至此，完成了铂金950饰品的生产。So far, the production of platinum 950 jewelry has been completed.
其中，所述步骤(3)也可以为：将铂金链身配料放到摄氏温度1800度的熔炼炉进行熔炼，将铂金焊料放到摄氏温度1200度的熔炼炉进行熔炼；Wherein, the step (3) can also be: putting the platinum chain body ingredients into a melting furnace with a temperature of 1800 degrees Celsius for melting, and putting the platinum solder into a melting furnace with a temperature of 1200 degrees Celsius for melting;
其中，所述熔炼炉的温度稍高于合金的温度，比如，铂金的熔点为1752度，熔炼炉的温度为1800度。Wherein, the temperature of the melting furnace is slightly higher than the temperature of the alloy, for example, the melting point of platinum is 1752 degrees, and the temperature of the melting furnace is 1800 degrees.
其中，所述机织部织好的链，环与环之间需要用焊线进行表面焊接，所述焊料熔点的温度与铂金熔点的温度相差较大，在焊接的过程中焊料不会和铂金链身一起熔化，这样可以保证后继产品生产加工；并且，焊料中所含铂金重量组分配比的比重高，这样不会可以保证铂金饰品中铂的含量较高，从而保证饰品的成色。Wherein, the chain woven by the woven part needs to be welded on the surface with a welding wire between the rings. The temperature of the melting point of the solder is quite different from the melting point of platinum, and the solder will not mix with the platinum during the welding process. The chain body is melted together, which can ensure the production and processing of subsequent products; moreover, the proportion of platinum weight components contained in the solder is high, which will not ensure the high content of platinum in the platinum jewelry, thereby ensuring the fineness of the jewelry.
二、当所述合金为制备铂金饰品的焊料，该合金的制备方法为铂金饰品焊料的制备方法，生产饰品的方法为铂金饰品的生产方法时：2. When the alloy is a solder for preparing platinum ornaments, the preparation method of the alloy is a method for preparing solder for platinum ornaments, and the method for producing ornaments is a production method for platinum ornaments:
(一)钯金饰品的焊料组分，包括如下实施例：(1) The solder component of the palladium-gold ornament, including following examples:
实施例一：所述合金包括下列重量份数的组分：Embodiment 1: The alloy includes the following components in parts by weight:
98份的钯、0.9份的铟、0.85份的镓、0.25份的铁。98 parts of palladium, 0.9 parts of indium, 0.85 parts of gallium, 0.25 parts of iron.
实施例二：所述合金包括下列重量份数的组分：Embodiment 2: The alloy includes the following components in parts by weight:
98.5份的钯、0.7份的铟、0.55份的镓、0.25份的铁。98.5 parts of palladium, 0.7 parts of indium, 0.55 parts of gallium, 0.25 parts of iron.
实施例三：所述合金包括下列重量份数的组分：Embodiment three: the alloy comprises the following components in parts by weight:
97.5份的钯、1.2份的铟、1.05份的镓、0.25份的铁。97.5 parts of palladium, 1.2 parts of indium, 1.05 parts of gallium, 0.25 parts of iron.
(二)钯金饰品焊料的制备方法，包括如下实施例：(2) the preparation method of palladium-gold ornament solder, comprising following embodiment:
实施例一：按重量组分配比：97.5份的钯、1.2份的铟、1.05份的镓、0.25份的铁进行配料，配好后放到摄氏温度为800度的熔炼炉进行熔炼；Embodiment 1: According to the weight group distribution ratio: 97.5 parts of palladium, 1.2 parts of indium, 1.05 parts of gallium, and 0.25 parts of iron are used for batching, and after being prepared, they are put into a smelting furnace with a temperature of 800 degrees Celsius for smelting;
实施例二：按重量组分配比：98.5份的钯、0.7份的铟、0.55份的镓、0.25份的铁进行配料，配好后放到摄氏温度为800度熔炼炉进行熔炼；Embodiment 2: According to the weight group distribution ratio: 98.5 parts of palladium, 0.7 parts of indium, 0.55 parts of gallium, and 0.25 parts of iron are used for batching, and after being prepared, they are put into a smelting furnace with a temperature of 800 degrees Celsius for smelting;
实施例三：按重量组分配比：97.5份的钯、1.2份的铟、1.05份的镓、0.25份的铁进行配料，配好后放到摄氏温度为1200的熔炼炉进行熔炼；Embodiment 3: According to the weight group distribution ratio: 97.5 parts of palladium, 1.2 parts of indium, 1.05 parts of gallium, and 0.25 parts of iron are used for batching, and after the preparation, they are put into a smelting furnace with a temperature of 1200 degrees Celsius for smelting;
实施例四：按重量组分配比：98.5份的钯、0.7份的铟、0.55份的镓、0.25份的铁进行配料，配好后放到摄氏温度为1200熔炼炉进行熔炼；Embodiment 4: According to the weight group distribution ratio: 98.5 parts of palladium, 0.7 parts of indium, 0.55 parts of gallium, and 0.25 parts of iron are used for batching, and after the preparation is completed, the temperature is 1200 degrees Celsius for smelting in a smelting furnace;
实施例五：按重量组分配比：98份的钯、0.9份的铟、0.85份的镓、0.25份的铁进行配料，配好后放到摄氏温度为1000熔炼炉进行熔炼；Embodiment 5: according to weight group distribution ratio: 98 parts of palladium, 0.9 parts of indium, 0.85 parts of gallium, 0.25 parts of iron are used for batching, and after being prepared, they are put into a smelting furnace with a temperature of 1000 degrees Celsius for smelting;
实施例六：按重量组分配比：98份的钯、0.9份的铟、0.85份的镓、0.25份的铁进行配料，配好后放到摄氏温度为1000熔炼炉进行熔炼；Embodiment 6: According to the weight group distribution ratio: 98 parts of palladium, 0.9 parts of indium, 0.85 parts of gallium, and 0.25 parts of iron are used for batching, and after the preparation, they are put into a smelting furnace with a temperature of 1000 degrees Celsius for smelting;
其中，所述熔炼炉的温度也可以为摄氏温度1050度，将上述各种按重量组分配比组成的焊料配好后放入熔炼炉熔炼即可得该合金。Wherein, the temperature of the smelting furnace can also be 1050 degrees centigrade, and the alloy can be obtained by mixing the above-mentioned various solders according to the weight component ratio and putting them into the smelting furnace for smelting.
(三)生产钯金饰品950的方法，包括如下实施例：(3) the method for producing palladium gold ornament 950, comprises following embodiment:
实施例一：当焊料按重量组分为：97.5份的钯、1.2份的铟、1.05份的镓、0.25份的铁，包括下列步骤：Embodiment 1: When the solder is composed by weight: 97.5 parts of palladium, 1.2 parts of indium, 1.05 parts of gallium, and 0.25 parts of iron, the following steps are included:
(1)按重量组分99.95份的钯进行链身用料；(1) carry out chain body material by the palladium of 99.95 parts of weight components;
(2)按重量组分：97.5份的钯、1.2份的铟、1.05份的镓、0.25份的铁进行焊料配料；(2) Components by weight: 97.5 parts of palladium, 1.2 parts of indium, 1.05 parts of gallium, 0.25 parts of iron for solder batching;
(3)将钯金链身直接用来拉线，将钯金焊料放到摄氏温度800度的熔炼炉进行熔炼；(3) Use the palladium chain body directly to pull the wire, and put the palladium solder into a melting furnace with a temperature of 800 degrees Celsius for melting;
(4)链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) The woven wire of the chain body is drawn according to the specification required by the customer, and the solder is drawn according to the specification of ∮0.35 mm;
(5)拉好的链身用机织线发到机织部织链；(5) The pulled chain body is sent to the weaving department with a woven thread to weave the chain;
(6)将机织部织好的链身发到链部用所配钯金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with the palladium ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，检测成色并电金。(10) After assembly, the surface is polished, the color is tested and electroplated.
至此，完成了钯金950饰品的生产。So far, the production of palladium 950 jewelry has been completed.
其中，所述步骤(3)也可以为：将钯金焊料放到摄氏温度1000度的熔炼炉进行熔炼；Wherein, the step (3) can also be: putting the palladium-gold solder into a smelting furnace with a temperature of 1000 degrees Celsius for smelting;
实施例二：当焊料按重量组分为：98.5份的钯、0.7份的铟、0.55份的镓、0.25份的铁，包括下列步骤：Embodiment two: when the solder is composed by weight: 98.5 parts of palladium, 0.7 parts of indium, 0.55 parts of gallium, 0.25 parts of iron, comprising the following steps:
(1)按重量组分99.95份的铂进行链身用料；(1) carry out chain body material by the platinum of 99.95 parts by weight components;
(2)按重量组分：98.5份的钯、0.7份的铟、0.55份的镓、0.25份的铁进行焊料配料；(2) Components by weight: 98.5 parts of palladium, 0.7 parts of indium, 0.55 parts of gallium, 0.25 parts of iron for solder batching;
(3)将钯金链身用料不需要熔炼直接拉线，将钯金焊料放到摄氏温度1200度的熔炼炉进行熔炼；(3) The material used for the palladium chain body does not need to be smelted to directly pull the wire, and the palladium solder is put into a smelting furnace with a temperature of 1200 degrees Celsius for smelting;
(4)链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) The woven wire of the chain body is drawn according to the specification required by the customer, and the solder is drawn according to the specification of ∮0.35 mm;
(5)拉好的链身用机织线发到机织部织链；(5) The pulled chain body is sent to the weaving department with a woven thread to weave the chain;
(6)将机织部织好的链身发到链部用所配钯金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with the palladium ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，检测成色并电金。(10) After assembly, the surface is polished, the color is tested and electroplated.
至此，完成了钯金950饰品的生产。So far, the production of palladium 950 jewelry has been completed.
其中，所述步骤(3)也可以为：将钯金焊料放到摄氏温度1100度的熔炼炉进行熔炼；Wherein, the step (3) can also be: putting the palladium-gold solder into a smelting furnace with a temperature of 1100 degrees Celsius for smelting;
实施例三：当焊料按重量组分为：97.5份的钯、1.2份的铟、1.05份的镓、0.25份的铁，包括下列步骤：Embodiment three: when the solder is composed by weight: 97.5 parts of palladium, 1.2 parts of indium, 1.05 parts of gallium, and 0.25 parts of iron, the following steps are included:
(1)按重量组分99.95份的铂进行链身配料；(1) carry out chain body batching by the platinum of weight component 99.95 parts;
(2)按重量组分：97.5份的钯、1.2份的铟、1.05份的镓、0.25份的铁进行焊料配料；(2) Components by weight: 97.5 parts of palladium, 1.2 parts of indium, 1.05 parts of gallium, 0.25 parts of iron for solder batching;
(3)将钯金链身用料不需要熔炼直接拉线，将钯金焊料放到摄氏温度1100度的熔炼炉进行熔炼；(3) The material used for the palladium chain body does not need to be smelted to directly pull the wire, and the palladium solder is put into a smelting furnace with a temperature of 1100 degrees Celsius for smelting;
(4)将熔炼好的料按要求拉线，链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) Pull the smelted material according to the requirements, the woven wire of the chain body is drawn according to the specifications required by the customer, and the solder is drawn according to the specification of ∮0.35 mm;
(5)拉好的链身用机织线发到机织部织链；(5) The pulled chain body is sent to the weaving department with a woven thread to weave the chain;
(6)将机织部织好的链身发到链部用所配钯金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with the palladium ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，检测成色并电金。(10) After assembly, the surface is polished, the color is tested and electroplated.
至此，完成了钯金950饰品的生产。So far, the production of palladium 950 jewelry has been completed.
实施例四：当焊料按重量组分为：98.5份的钯、0.7份的铟、0.55份的镓、0.25份的铁，包括下列步骤：Embodiment 4: When the solder is composed by weight: 98.5 parts of palladium, 0.7 parts of indium, 0.55 parts of gallium, and 0.25 parts of iron, the following steps are included:
(1)按重量组分99.95份的铂进行链身用料；(1) carry out chain body material by the platinum of 99.95 parts by weight components;
(2)按重量组分：98.5份的钯、0.7份的铟、0.55份的镓、0.25份的铁进行焊料配料；(2) Components by weight: 98.5 parts of palladium, 0.7 parts of indium, 0.55 parts of gallium, 0.25 parts of iron for solder batching;
(3)将钯金链身用料不需要熔炼直接拉线，将钯金焊料放到摄氏温度1200度的熔炼炉进行熔炼；(3) The material used for the palladium chain body does not need to be smelted to directly pull the wire, and the palladium solder is put into a smelting furnace with a temperature of 1200 degrees Celsius for smelting;
(4)链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) The woven wire of the chain body is drawn according to the specification required by the customer, and the solder is drawn according to the specification of ∮0.35 mm;
(5)拉好的链身用机织线发到机织部织链；(5) The pulled chain body is sent to the weaving department with a woven thread to weave the chain;
(6)将机织部织好的链身发到链部用所配钯金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with the palladium ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，检测成色并电金。(10) After assembly, the surface is polished, the color is tested and electroplated.
至此，完成了钯金950饰品的生产。So far, the production of palladium 950 jewelry has been completed.
实施例五：当焊料按重量组分：98份的钯、0.9份的铟、0.85份的镓、0.25份的铁，包括下列步骤：Embodiment five: when the solder is composed by weight: 98 parts of palladium, 0.9 parts of indium, 0.85 parts of gallium, 0.25 parts of iron, comprising the following steps:
(1)按重量组分99.95份的铂进行链身配料；(1) carry out chain body batching by the platinum of weight component 99.95 parts;
(2)按重量组分：98份的钯、0.9份的铟、0.85份的镓、0.25份的铁进行焊料配料；(2) Components by weight: 98 parts of palladium, 0.9 parts of indium, 0.85 parts of gallium, 0.25 parts of iron for solder batching;
(3)将钯金链身用料不需要熔炼直接拉线，将钯金焊料放到摄氏温度800度的熔炼炉进行熔炼；(3) The material used for the palladium chain body does not need to be smelted to directly pull the wire, and the palladium solder is put into a smelting furnace with a temperature of 800 degrees Celsius for smelting;
(4)链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) The woven wire of the chain body is drawn according to the specification required by the customer, and the solder is drawn according to the specification of ∮0.35 mm;
(5)拉好的链身用机织线发到机织部织链；(5) The pulled chain body is sent to the weaving department with a woven thread to weave the chain;
(6)将机织部织好的链身发到链部用所配钯金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with the palladium ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，检测成色并电金。(10) After assembly, the surface is polished, the color is tested and electroplated.
至此，完成了钯金950饰品的生产。So far, the production of palladium 950 jewelry has been completed.
实施例六：当焊料按重量组分：98份的钯、0.9份的铟、0.85份的镓、0.25份的铁，包括下列步骤：Embodiment six: when the solder is composed by weight: 98 parts of palladium, 0.9 parts of indium, 0.85 parts of gallium, and 0.25 parts of iron, the following steps are included:
(1)按重量组分99.95份的铂进行链身用料；(1) carry out chain body material by the platinum of 99.95 parts by weight components;
(2)按重量组分：98份的钯、0.9份的铟、0.85份的镓、0.25份的铁进行焊料配料；(2) Components by weight: 98 parts of palladium, 0.9 parts of indium, 0.85 parts of gallium, 0.25 parts of iron for solder batching;
(3)钯金链身用料不需要熔炼直接拉线，将钯金焊料放到摄氏温度1200度的熔炼炉进行熔炼；(3) The material used for the palladium chain body does not need to be smelted and directly pulled, and the palladium solder is put into a melting furnace at a temperature of 1200 degrees Celsius for melting;
(4)链身机织线按客户要求规格拉线，焊料按∮0.35毫米规格拉线；(4) The woven wire of the chain body is drawn according to the specification required by the customer, and the solder is drawn according to the specification of ∮0.35 mm;
(5)拉好的链身用机织线发到机织部织链；(5) The pulled chain body is sent to the weaving department with a woven thread to weave the chain;
(6)将机织部织好的链身发到链部用所配钯金∮0.35毫米焊线表面焊接；(6) Send the chain body woven by the weaving part to the chain part for surface welding with the palladium ∮ 0.35 mm welding wire;
(7)焊接好的半成品用磁力抛光机进行表面抛光；(7) The welded semi-finished products are surface polished with a magnetic polishing machine;
(8)半成品经抛光后车花；(8) Semi-finished products are polished and turned into car flowers;
(9)按要求长度剪断两头焊圈并上扣组装；(9) Cut off the welding rings at both ends according to the required length and buckle up for assembly;
(10)组装好后表面打磨，检测成色并电金。(10) After assembly, the surface is polished, the color is tested and electroplated.
至此，完成了钯金950饰品的生产。So far, the production of palladium 950 jewelry has been completed.
可选的，步骤(3)也可以为：将钯金焊料放到摄氏温度1000度的熔炼炉进行熔炼；Optionally, step (3) can also be: putting palladium-gold solder into a smelting furnace at a temperature of 1000 degrees Celsius for melting;
其中，所述熔炼炉的温度稍高于合金的熔点。Wherein, the temperature of the melting furnace is slightly higher than the melting point of the alloy.
其中，所述机织部织好的链，环与环之间需要用焊线进行表面焊接，所述钯金焊料熔点的温度与钯金熔点的温度相差大，所以在焊接的过程中焊料不会和钯金链身一起熔化，这样可以保证后继产品加工；并且，焊料中所含钯金重量组分配比的比重高，这样不会可以保证钯金饰品中铂的含量较高，从而保证饰品的成色。Wherein, the chain woven by the woven part needs to be surface-welded with a welding wire between the rings, and the temperature difference between the melting point of the palladium-gold solder and the melting point of the palladium-gold solder is large, so the solder is not in the process of welding. It will melt together with the palladium chain body, which can ensure the processing of subsequent products; moreover, the proportion of palladium weight components contained in the solder is high, so that it will not be able to ensure a high content of platinum in the palladium jewelry, so as to ensure the quality of the jewelry. fineness.
以上对本发明所提供的一种合金、该合金的制备方法及生产饰品的方法进行了详细介绍，本文中应用了具体个例对本发明的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本发明的方法及其核心思想；同时，对于本领域的一般技术人员，依据本发明的思想，在具体实施方式及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。A kind of alloy provided by the present invention, the preparation method of the alloy and the method for producing ornaments have been introduced in detail above. The principles and implementation methods of the present invention have been explained by using specific examples in this paper. The description of the above examples is only used To help understand the method of the present invention and its core idea; at the same time, for those of ordinary skill in the art, according to the idea of the present invention, there will be changes in the specific implementation and scope of application. In summary, this specification The content should not be construed as a limitation of the invention.
Claims (10)