CN109203155A - A kind of preparation method of asepsis environment-protecting wood veneer preservative - Google Patents
A kind of preparation method of asepsis environment-protecting wood veneer preservative Download PDFInfo
- Publication number
- CN109203155A CN109203155A CN201811154539.7A CN201811154539A CN109203155A CN 109203155 A CN109203155 A CN 109203155A CN 201811154539 A CN201811154539 A CN 201811154539A CN 109203155 A CN109203155 A CN 109203155A
- Authority
- CN
- China
- Prior art keywords
- parts
- added
- preservative
- wood veneer
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation methods of asepsis environment-protecting wood veneer preservative, and each raw material is in terms of mass parts, comprising the following steps: A, clean to cloves, rosemary respectively and dry, ball milling obtains Ground Cloves and rosemary powder；B, deionized water is added in blender and is used as bottom water, fatty alcohol polyoxyethylene ether and Lauryl Diethanolamine is added, is dispersed with stirring；C, trimethylborate, butyl carbamate, imidacloprid and Traditional Chinese medicine bacteriostatic agent are sequentially added into blender, are stirred, ultrasonic disperse；D, Ground Cloves and rosemary powder, stirring are added in heating process for heating water bath；E, the mixed solution in step D is cooled to room temperature, ultrasonic disperse, stands, obtains preservative finished product.The present invention has the advantages that environmental friendliness height, concise in technology, at low cost.
Description
Technical field
The present invention relates to wood preservation technical field, especially a kind of preparation side of asepsis environment-protecting wood veneer preservative
Method.
Background technique
The preservative pervasive environments friendliness having currently on the market is poor, has micro toxicity for the human body, especially
It is to directly influence indoor air quality coated in the preservative on the surfacings such as wood veneer, with the development of the times,
The preservative of asepsis environment-protecting is a general orientation of current preservative development, and the preparation side of asepsis environment-protecting wood veneer preservative
Innovation of the law develops at present relatively delays, and existing timber preservative preparation process is relatively complicated, and higher cost, in preparation process
In be easy to produce pollution environment by-product.Therefore, a kind of preparation method of asepsis environment-protecting wood veneer preservative is needed, to make
Standby asepsis environment-protecting wood veneer preservative.
Summary of the invention
The object of the present invention is to provide a kind of preparation methods of asepsis environment-protecting wood veneer preservative.It has environment
Friendliness height, concise in technology, advantage at low cost.
Technical solution of the present invention: a kind of preparation method of asepsis environment-protecting wood veneer preservative, each raw material is with mass parts
Meter, comprising the following steps:
A, respectively cloves, rosemary clean and be dried, with 200-240r/min ball milling 2-3h, obtain Ground Cloves and fan
Repeatedly face powder；
B, 150 parts of deionized waters are added in blender and are used as bottom water, while 5 parts of fatty alcohol polyoxyethylene ether and 7 are added
Part Lauryl Diethanolamine, is heated to 40-46 DEG C, is dispersed with stirring, mixing speed 2200-2600r/min, and when stirring is a length of
30-40min；
C, 40 parts of trimethylborates, 8 parts of butyl carbamates are sequentially added into blender, in 16 parts of imidacloprids and 10 parts
Medicine bacteriostatic agent is heated to 48-52 DEG C after being all added, and stirs 25-35min with the mixing speed of 2500-3000r/min,
Then ultrasonic disperse 15-20min；
D, the mixed solution in step C is poured out to glass container, water is carried out to glass container using 55-60 DEG C of temperature
Bath is heated, and 4 parts of Ground Cloves obtained in step A and 6 parts of rosemary powder is slowly added in heating process, with 2000-2400r/
The mixing speed of min stirs 35-45min；
E, the mixed solution in step D is cooled to room temperature, ultrasonic disperse 5-10min, stand 2-3h, obtain preservative at
Product.
In a kind of preparation method of asepsis environment-protecting wood veneer preservative above-mentioned, 4 parts of Ground Cloves and 6 in the step D
First mixed-powder is added to glass container again after mixing for part rosemary powder.
In a kind of preparation method of asepsis environment-protecting wood veneer preservative above-mentioned, the Traditional Chinese medicine bacteriostatic agent includes micro-nano
Coptis root powder, diatomite and cinnamon oil.
In a kind of preparation method of asepsis environment-protecting wood veneer preservative above-mentioned, the micro-nano coptis root powder, diatom
The weight part ratio of soil and cinnamon oil is 2:5:8.
Compared with prior art, the present invention is with trimethylborate, rosemary powder, Ground Cloves, fatty alcohol polyoxyethylene ether, the moon
Osmanthus base diethanol amine, Traditional Chinese medicine bacteriostatic agent, imidacloprid, butyl carbamate and deionized water are to prepare raw material, first will be in blender
Middle addition water, fatty alcohol polyoxyethylene ether and Lauryl Diethanolamine, form a kind of solution with certain consistency, sequentially add
Trimethylborate, butyl carbamate, imidacloprid and Traditional Chinese medicine bacteriostatic agent, above-mentioned material inherently have good deinsectization sterilization effect
Fruit, preservative set obtained is a variety of a little after being mixed in a certain ratio, and heating is improved mixing speed, made using ultrasonic disperse
Solution mixing is more uniform, then Ground Cloves and rosemary powder is added down to glass container heating water bath in above-mentioned mixed solution, can
So that adding the wood veneer after preservative produced by the present invention increases delicate fragrant, wood veneer is not necessarily to after adding preservative
It stands and carries out dissipating taste for a period of time, can accomplish to produce and sell, finally carry out ultrasonic disperse again, stand to obtain preservative finished product,
Whole preparation process concise in technology, at low cost, raw material of the present invention is environmentally protective, and whole preparation process does not generate pollution environment
By-product, through preservative produced by the present invention be similarly green, asepsis environment-protecting.
To sum up, the present invention has the advantages that environmental friendliness height, concise in technology, at low cost.
Specific embodiment
Below with reference to embodiment, the present invention is further illustrated, but is not intended as the foundation limited the present invention.
Embodiment 1: a kind of preparation method of asepsis environment-protecting wood veneer preservative, each raw material in terms of mass parts, including with
Lower step:
A, respectively cloves, rosemary clean and be dried, with 200r/min ball milling 2h, obtain Ground Cloves and rosemary
Powder；
B, 150 parts of deionized waters are added in blender and are used as bottom water, while 5 parts of fatty alcohol polyoxyethylene ether and 7 are added
Part Lauryl Diethanolamine, is heated to 40 DEG C, is dispersed with stirring, mixing speed 2200r/min, when stirring a length of 30min；
C, 40 parts of trimethylborates, 8 parts of butyl carbamates are sequentially added into blender, in 16 parts of imidacloprids and 10 parts
Medicine bacteriostatic agent is heated to 48 DEG C after being all added, and stirs 25min with the mixing speed of 2500r/min, then ultrasonic disperse
15min；
D, the mixed solution in step C is poured out to glass container, water-bath is carried out to glass container using 55 DEG C of temperature
It heats, 4 parts of Ground Cloves obtained in step A and 6 parts of rosemary powder is slowly added in heating process, with stirring for 2000r/min
Mix speed stirring 35min；
E, the mixed solution in step D is cooled to room temperature, ultrasonic disperse 5min, stands 2h, obtains preservative finished product.
Mixed-powder is first added to glass again after mixing and holds by 4 parts of Ground Cloves and 6 parts of rosemary powder in the step D
Device.
The Traditional Chinese medicine bacteriostatic agent includes micro-nano coptis root powder, diatomite and cinnamon oil.
The weight part ratio of the micro-nano coptis root powder, diatomite and cinnamon oil is 2:5:8.
Embodiment 2: a kind of preparation method of asepsis environment-protecting wood veneer preservative, each raw material in terms of mass parts, including with
Lower step:
A, respectively cloves, rosemary clean and be dried, with 240r/min ball milling 3h, obtain Ground Cloves and rosemary
Powder；
B, 150 parts of deionized waters are added in blender and are used as bottom water, while 5 parts of fatty alcohol polyoxyethylene ether and 7 are added
Part Lauryl Diethanolamine, is heated to 46 DEG C, is dispersed with stirring, mixing speed 2600r/min, when stirring a length of 40min；
C, 40 parts of trimethylborates, 8 parts of butyl carbamates are sequentially added into blender, in 16 parts of imidacloprids and 10 parts
Medicine bacteriostatic agent is heated to 52 DEG C after being all added, and stirs 35min with the mixing speed of 3000r/min, then ultrasonic disperse
20min；
D, the mixed solution in step C is poured out to glass container, water-bath is carried out to glass container using 60 DEG C of temperature
It heats, 4 parts of Ground Cloves obtained in step A and 6 parts of rosemary powder is slowly added in heating process, with stirring for 2400r/min
Mix speed stirring 45min；
E, the mixed solution in step D is cooled to room temperature, ultrasonic disperse 10min, stands 3h, obtains preservative finished product.
Mixed-powder is first added to glass again after mixing and holds by 4 parts of Ground Cloves and 6 parts of rosemary powder in the step D
Device.
The Traditional Chinese medicine bacteriostatic agent includes micro-nano coptis root powder, diatomite and cinnamon oil.
The weight part ratio of the micro-nano coptis root powder, diatomite and cinnamon oil is 2:5:8.
Embodiment 3: a kind of preparation method of asepsis environment-protecting wood veneer preservative, each raw material in terms of mass parts, including with
Lower step:
A, respectively cloves, rosemary clean and be dried, with 220r/min ball milling 2.5h, obtain Ground Cloves and rosemary
Powder；
B, 150 parts of deionized waters are added in blender and are used as bottom water, while 5 parts of fatty alcohol polyoxyethylene ether and 7 are added
Part Lauryl Diethanolamine, is heated to 43 DEG C, is dispersed with stirring, mixing speed 2400r/min, when stirring a length of 35min；
C, 40 parts of trimethylborates, 8 parts of butyl carbamates are sequentially added into blender, in 16 parts of imidacloprids and 10 parts
Medicine bacteriostatic agent is heated to 50 DEG C after being all added, and stirs 30min with the mixing speed of 2800r/min, then ultrasonic disperse
18min；
D, the mixed solution in step C is poured out to glass container, water-bath is carried out to glass container using 57 DEG C of temperature
It heats, 4 parts of Ground Cloves obtained in step A and 6 parts of rosemary powder is slowly added in heating process, with stirring for 2200r/min
Mix speed stirring 40min；
E, the mixed solution in step D is cooled to room temperature, ultrasonic disperse 8min, stands 2.5h, obtains preservative finished product.
Mixed-powder is first added to glass again after mixing and holds by 4 parts of Ground Cloves and 6 parts of rosemary powder in the step D
Device.
The Traditional Chinese medicine bacteriostatic agent includes micro-nano coptis root powder, diatomite and cinnamon oil.
The weight part ratio of the micro-nano coptis root powder, diatomite and cinnamon oil is 2:5:8.
The present invention with trimethylborate, rosemary powder, Ground Cloves, fatty alcohol polyoxyethylene ether, Lauryl Diethanolamine, in
Medicine bacteriostatic agent, imidacloprid, butyl carbamate and deionized water are to prepare raw material, and water, fatty alcohol will first be added in blender
Polyoxyethylene ether and Lauryl Diethanolamine form a kind of solution with certain consistency, sequentially add trimethylborate, amino
Butyl formate, imidacloprid and Traditional Chinese medicine bacteriostatic agent, above-mentioned material inherently have good deinsectization bactericidal effect, mix by a certain percentage
Preservative set obtained is a variety of a little after conjunction, and heating improves mixing speed, keeps solution mixing more equal using ultrasonic disperse
It is even, then Ground Cloves and rosemary powder is added down to glass container heating water bath in above-mentioned mixed solution, the addition present invention can be made
Wood veneer after preservative obtained increases delicate fragrant, wood veneer after add preservative without stand for a period of time into
The scattered taste of row can be accomplished to produce and sell, finally carry out ultrasonic disperse again, stand to obtain preservative finished product, whole preparation process work
Skill is succinct, at low cost, and raw material of the present invention is environmentally protective, and whole preparation process does not generate the by-product of pollution environment, through this
It invents preservative obtained and is similarly green, asepsis environment-protecting.
A kind of wood veneer preservative of asepsis environment-protecting, comprises the following components in parts by weight: trimethylborate, 40 parts, fan
Repeatedly face powder, 6 parts, Ground Cloves, 4 parts, fatty alcohol polyoxyethylene ether, 5 parts, Lauryl Diethanolamine, 7 parts, Traditional Chinese medicine bacteriostatic agent, 10
Part, imidacloprid, 16 parts, butyl carbamate, 8 parts, deionized water, 150 parts.
The Traditional Chinese medicine bacteriostatic agent includes micro-nano coptis root powder, diatomite and cinnamon oil.
The weight part ratio of the micro-nano coptis root powder, diatomite and cinnamon oil is 2:5:8.
Claims (4)
1. a kind of preparation method of asepsis environment-protecting wood veneer preservative, which is characterized in that each raw material in terms of mass parts, including with
Lower step:
A, respectively cloves, rosemary clean and be dried, with 200-240r/min ball milling 2-3h, obtain Ground Cloves and rosemary
Powder；
B, 150 parts of deionized waters are added in blender and are used as bottom water, while 5 parts of fatty alcohol polyoxyethylene ether and 7 parts months are added
Osmanthus base diethanol amine, is heated to 40-46 DEG C, is dispersed with stirring, mixing speed 2200-2600r/min, when stirring a length of 30-
40min；
C, 40 parts of trimethylborates, 8 parts of butyl carbamates, 16 parts of imidacloprids and 10 parts of Chinese medicine suppressions are sequentially added into blender
Microbial inoculum is heated to 48-52 DEG C after being all added, and stirs 25-35min with the mixing speed of 2500-3000r/min, then
Ultrasonic disperse 15-20min；
D, the mixed solution in step C is poured out to glass container, water-bath is carried out to glass container using 55-60 DEG C of temperature and is added
Heat is slowly added to 4 parts of Ground Cloves obtained in step A and 6 parts of rosemary powder in heating process, with 2000-2400r/min's
Mixing speed stirs 35-45min；
E, the mixed solution in step D is cooled to room temperature, ultrasonic disperse 5-10min, stands 2-3h, obtains preservative finished product.
2. a kind of preparation method of asepsis environment-protecting wood veneer preservative according to claim 1, it is characterised in that: described
First mixed-powder is added to glass container again after mixing for 4 parts of Ground Cloves and 6 parts of rosemary powder in step D.
3. a kind of preparation method of asepsis environment-protecting wood veneer preservative according to claim 1, it is characterised in that: described
Traditional Chinese medicine bacteriostatic agent includes micro-nano coptis root powder, diatomite and cinnamon oil.
4. a kind of preparation method of asepsis environment-protecting wood veneer preservative according to claim 3, it is characterised in that: described
The weight part ratio of micro-nano coptis root powder, diatomite and cinnamon oil is 2:5:8.