[go: up one dir, main page]

CN108084903B - 一种高净化抗污的耐高低温双面遮光胶带 - Google Patents

一种高净化抗污的耐高低温双面遮光胶带 Download PDF

Info

Publication number
CN108084903B
CN108084903B CN201711414198.8A CN201711414198A CN108084903B CN 108084903 B CN108084903 B CN 108084903B CN 201711414198 A CN201711414198 A CN 201711414198A CN 108084903 B CN108084903 B CN 108084903B
Authority
CN
China
Prior art keywords
ether
parts
weight
polyether
ketone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201711414198.8A
Other languages
English (en)
Other versions
CN108084903A (zh
Inventor
王旭辉
邱仕凯
杨旭
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Liumai New Material Technology Co ltd
Original Assignee
Ningbo Liumai New Material Technology Co ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ningbo Liumai New Material Technology Co ltd filed Critical Ningbo Liumai New Material Technology Co ltd
Priority to CN201711414198.8A priority Critical patent/CN108084903B/zh
Publication of CN108084903A publication Critical patent/CN108084903A/zh
Application granted granted Critical
Publication of CN108084903B publication Critical patent/CN108084903B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种高净化抗污的耐高低温双面遮光胶带，由黑磷烯改性遮光PET薄膜、聚醚醚酮改性有机硅压敏胶层、离型层纸组成；其中聚醚醚酮改性有机硅压敏胶层位于黑磷烯改性遮光PET薄膜的两面，离型层纸位于聚醚醚酮改性有机硅压敏胶层的外侧。本发明具有以下优点：首次将具有高紫外光光吸收效率的黑磷烯用于遮光胶带领域，并辅以紫外光吸收剂，本发明能有效的过滤掉紫外光线；本发明具有较高的耐高低温性能；采用聚醚醚酮改性有机硅压敏胶，本发明具有较高的耐老化性能、耐高温性。

Description

一种高净化抗污的耐高低温双面遮光胶带
技术领域
本发明涉及一种遮光胶带，尤其涉及一种高净化抗污的耐高低温双面遮光胶带，属于胶带技术领域。
背景技术
随着科学技术的不断发展，电子产品的不断微型化，在产品的制作过程中，胶带扮演着重要的角色，对胶带的要求也越来越高，普通的胶带已满足不了市场的需求，尤其遮光方面的性能欠佳。
由于液晶显示器具有以下优点：零辐射，低耗能，散热小，纤薄轻巧，精确还原图像，画面稳定不闪烁，屏幕调节方便等，因此现在的绝大多数数码产品的显示结构都采用液晶显示。但是，液晶显示的亮度和对比度都不是很好，因为液晶体本身不发光，需要液晶板背后的发光管提供光源，如果屏蔽的不好会发生露光，从而影响液晶显示的对比度和亮度，而为了防止漏光的发生，同时固定液晶面板端部以及防止尘土进入，通常采用遮光胶带来固定液晶屏。
中国专利CN201511028549.2公开一种含APCF层偏光片用双面遮光胶带及其制备方法，包括重工型具有UV活性的丙烯酸胶黏剂组合物由以下组分及其质量份数组成：低聚物和丙烯酸酯单体共聚形成的共聚物100份，光引发剂4～10份，第一交联剂0.5～0.8份，增韧剂1～2份；还涉及应用有该胶黏剂组合物的含APFC层偏光用双面遮光胶带及其制备方法。该发明中的双面遮光胶带不仅能永久固定液晶显示屏和背光模组，且对含APCF层偏光片48小时内再剥离时200倍显微镜下观察无残胶、无损坏，该胶带制备方法简单，应用本发明中的胶带能显著降低新型偏光片使用过程中的不良率，提高重工作业的效率。
发明内容
为克服现有技术的缺点和不足，本发明旨在提供一种高净化抗污的耐高低温双面遮光胶带。
一种高净化抗污的耐高低温双面遮光胶带，由黑磷烯改性遮光PET薄膜、聚醚醚酮改性有机硅压敏胶层、离型层纸组成；其中聚醚醚酮改性有机硅压敏胶层位于黑磷烯改性遮光PET薄膜的两面，离型层纸位于聚醚醚酮改性有机硅压敏胶层的外侧。
所述的黑磷烯改性遮光PET薄膜，由以下步骤制得：准确称取PET聚酯切片25～35重量份、钛酸酯偶联剂3～6重量份、乙烯基MQ硅树脂10～20重量份、黑磷烯5～10重量份、紫外线吸收剂4～8重量份、有机溶剂10～20重量份加入到反应装置中，搅拌分散均匀，然后加热至100～120℃，回流反应3～5h，然后通过冷却热溶液法结晶，干燥结晶物，即得到改性遮光PET粗产品；在300～400℃、500～700r/min的双螺杆机转速的条件下，将改性遮光PET粗产品投入双螺杆机搅拌熔融2～4h，经挤出机将将产物挤出，得到片材，再同时双向拉伸片材，得黑磷烯改性遮光PET薄膜。
所述的聚醚醚酮改性有机硅压敏胶层，由聚醚醚酮改性有机硅压敏胶组成，所述的聚醚醚酮改性有机硅压敏胶，由以下步骤制得：(1)活性聚醚醚酮的制备：将10重量份聚醚醚酮粉体分批次加入至2～5重量份浓硫酸中，冰水浴中反应0.5～2h，然后移至室温继续反应2～4h，反应结束后，经过滤水洗至中性，然后经乙醇洗涤、真空干燥得活性聚醚醚酮；(2)改性有机硅压敏胶的制备：将活性聚醚醚酮10～15重量份、乙烯基MQ硅树脂2～10重量份、多羟基聚硅氧烷8～15重量份、107硅橡胶10～20重量份、10～20重量份稀释剂、2～5重量份黑色浆加入到反应装置中搅拌分散均匀，然后升温至120℃～135℃，向其中缓慢加入1～4份100ppm铂催化剂，然后保温反应10～30min，然后加入0.02～0.2份阻聚剂，同时冷却至室温，即得到所述的聚醚醚酮改性有机硅压敏胶。
所述的黑磷烯改性遮光PET薄膜的厚度为30～60μm，所述的聚醚醚酮改性有机硅压敏胶层厚度为3～6μm。
所述的钛酸酯偶联剂为异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯、钛酸四丁酯、异丙基三(二辛基磷酸酰氧基)钛酸酯、双(二辛氧基焦磷酸酯基)乙撑钛酸酯、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯、钛酸四异丙酯、单烷氧基脂肪酸钛酸酯偶联剂中的至少一种。
所述的乙烯基MQ硅树脂的乙烯基百分含量为1.2％～3.0％，M∶Q值为0.5～0.8∶1。
所述的紫外线吸收剂为2，2’-硫代双(4-叔辛基酚氧基)镍、三(1，2，2，6.6-五甲哌啶基)亚磷酸酯、2，4-二羟基二苯甲酮、邻羟基苯甲酸苯酯、2-(2’-羟基-5’-甲基苯基)苯并三氮唑、2-羟基-4-正辛氧基二苯甲酮中的至少一种；所述的有机溶剂为乙二醇二甲醚、乙二醇二丁醚、丁醚、甲苯、二甲苯、丙酮、环己酮中的至少一种。
所述的聚醚醚酮粉体的粒径为100～500目；所述的多羟基聚硅氧烷的粘度为60～300mPa·s，羟基百分含量为3％～8％；所述的107硅橡胶粘度为2000～20000mPa·s；所述的稀释剂为二甲基聚硅氧烷，粘度为10～30mPa·s。
所述铂催化剂是处理后的氯铂酸、乙醇改性的氯铂酸、氯铂酸-烯烃络合物、氯铂酸-烯烃硅氧烷络合物、氯铂酸-二乙烯基四甲基二硅氧烷络合物中的至少一种；所述阻聚剂为1-乙炔基-环己醇、3-甲基-1-戊烯-3-醇、苯并三唑中的至少一种。
相对于现有技术，本发明具有以下优点：(1)以黑磷烯改性遮光PET薄膜为遮光膜，首次将具有高紫外光光吸收效率的黑磷烯用于遮光胶带领域，并辅以紫外光吸收剂，本发明能有效的过滤掉紫外光线；(2)所述的黑磷烯改性遮光PET薄膜、聚醚醚酮改性有机硅压敏胶在制备过程中，均加入适用温度范围在-60℃至+350℃温度环境下使用、耐高低温性能优异的乙烯基MQ硅树脂，本发明具有较高的耐高低温性能；(3)首次公开采用聚醚醚酮改性有机硅压敏胶，本发明具有较高的耐老化性能、耐高温性。
具体实施方式
实施例1
一种高净化抗污的耐高低温双面遮光胶带，由黑磷烯改性遮光PET薄膜A、聚醚醚酮改性有机硅压敏胶层D、离型层纸组成；其中聚醚醚酮改性有机硅压敏胶层D位于黑磷烯改性遮光PET薄膜A的两面，离型层纸位于聚醚醚酮改性有机硅压敏胶层D的外侧。其中，黑磷烯改性遮光PET薄膜A的厚度为30μm，所述的聚醚醚酮改性有机硅压敏胶层厚度为4μm。
本实施例中黑磷烯改性遮光PET薄膜A的制备方法，由以下步骤制得：准确称取PET聚酯切片25重量份、异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯6重量份、乙烯基MQ硅树脂(乙烯基百分含量为1.3％，M∶Q值为0.7)10重量份、黑磷烯10重量份、2，4-二羟基二苯甲酮4重量份、乙二醇二丁醚20重量份加入到反应装置中，搅拌分散均匀，然后加热至100℃，回流反应5h，然后通过冷却热溶液法结晶，干燥结晶物，即得到改性遮光PET粗产品；在300℃、700r/min的双螺杆机转速的条件下，将改性遮光PET粗产品投入双螺杆机搅拌熔融2h，经挤出机将将产物挤出，得到片材，再同时双向拉伸片材，得黑磷烯改性遮光PET薄膜A。
本实施例中聚醚醚酮改性有机硅压敏胶层D，由聚醚醚酮改性有机硅压敏胶d组成，所述的聚醚醚酮改性有机硅压敏胶d，由以下步骤制得：(1)活性聚醚醚酮的制备：将10重量份聚醚醚酮粉体分批次加入至5重量份浓硫酸中，冰水浴中反应0.5h，然后移至室温继续反应2h，反应结束后，经过滤水洗至中性，然后经乙醇洗涤、真空干燥得活性聚醚醚酮；(2)改性有机硅压敏胶的制备：将活性聚醚醚酮15重量份、乙烯基MQ硅树脂(乙烯基百分含量为1.3％，M∶Q值为0.7)2重量份、多羟基聚硅氧烷(粘度为300mPa·s，羟基百分含量为3％)15重量份、107硅橡胶(粘度为2000mPa·s)20重量份、10重量份二甲基聚硅氧烷(粘度为30mPa·s)、2重量份黑色浆加入到反应装置中搅拌分散均匀，然后升温至135℃，向其中缓慢加入1份100ppm乙醇改性的氯铂酸，然后保温反应10min，然后加入0.2份3-甲基-1-戊烯-3-醇，同时冷却至室温，即得到所述的聚醚醚酮改性有机硅压敏胶d。
实施例2
一种高净化抗污的耐高低温双面遮光胶带，由黑磷烯改性遮光PET薄膜B、聚醚醚酮改性有机硅压敏胶层E、离型层纸组成；其中聚醚醚酮改性有机硅压敏胶层E位于黑磷烯改性遮光PET薄膜B的两面，离型层纸位于聚醚醚酮改性有机硅压敏胶层E的外侧。其中，黑磷烯改性遮光PET薄膜的厚度为50μm，所述的聚醚醚酮改性有机硅压敏胶层厚度为6μm。
本实施例中黑磷烯改性遮光PET薄膜B的制备方法，由以下步骤制得：准确称取PET聚酯切片35重量份、异丙基三(二辛基磷酸酰氧基)钛酸酯3重量份、乙烯基MQ硅树脂20重量份(乙烯基百分含量为1.6％，M∶Q值为0.8)、黑磷烯5重量份、邻羟基苯甲酸苯酯8重量份、甲苯10重量份加入到反应装置中，搅拌分散均匀，然后加热至120℃，回流反应3h，然后通过冷却热溶液法结晶，干燥结晶物，即得到改性遮光PET粗产品；在400℃、500r/min的双螺杆机转速的条件下，将改性遮光PET粗产品投入双螺杆机搅拌熔融2h，经挤出机将将产物挤出，得到片材，再同时双向拉伸片材，得黑磷烯改性遮光PET薄膜B。
本实施例中聚醚醚酮改性有机硅压敏胶层E，由聚醚醚酮改性有机硅压敏胶e组成，所述的聚醚醚酮改性有机硅压敏胶e，由以下步骤制得：(1)活性聚醚醚酮的制备：将10重量份聚醚醚酮粉体分批次加入至2重量份浓硫酸中，冰水浴中反应2h，然后移至室温继续反应4h，反应结束后，经过滤水洗至中性，然后经乙醇洗涤、真空干燥得活性聚醚醚酮；(2)改性有机硅压敏胶的制备：将活性聚醚醚酮10重量份、乙烯基MQ硅树脂10重量份(乙烯基百分含量为1.6％，M∶Q值为0.8)、多羟基聚硅氧烷(粘度为60mPa·s、羟基百分含量为6％)8重量份、107硅橡胶(粘度为20000mPa·s)10重量份、20重量份二甲基聚硅氧烷(粘度为10mPa·s)、5重量份黑色浆加入到反应装置中搅拌分散均匀，然后升温至120℃，向其中缓慢加入2份100ppm氯铂酸-烯烃络合物，然后保温反应30min，然后加入0.02份1-乙炔基-环己醇，同时冷却至室温，即得到所述的聚醚醚酮改性有机硅压敏胶e。
实施例3
一种高净化抗污的耐高低温双面遮光胶带，由黑磷烯改性遮光PET薄膜C、聚醚醚酮改性有机硅压敏胶层F、离型层纸组成；其中聚醚醚酮改性有机硅压敏胶层F位于黑磷烯改性遮光PET薄膜C的两面，离型层纸位于聚醚醚酮改性有机硅压敏胶层F的外侧。其中，黑磷烯改性遮光PET薄膜的厚度为60μm，所述的聚醚醚酮改性有机硅压敏胶层厚度为4.5μm。
本实施例中黑磷烯改性遮光PET薄膜C的制备方法，由以下步骤制得：准确称取PET聚酯切片28重量份、四异丙基二(二辛基亚磷酸酰氧基)钛酸酯5重量份、乙烯基MQ硅树脂(乙烯基百分含量为1.8％，M∶Q值为0.7)14重量份、黑磷烯7重量份、三(1，2，2，6.6-五甲哌啶基)亚磷酸酯5重量份、环己酮13重量份加入到反应装置中，搅拌分散均匀，然后加热至115℃，回流反应4h，然后通过冷却热溶液法结晶，干燥结晶物，即得到改性遮光PET粗产品；在360℃、600r/min的双螺杆机转速的条件下，将改性遮光PET粗产品投入双螺杆机搅拌熔融3h，经挤出机将将产物挤出，得到片材，再同时双向拉伸片材，得黑磷烯改性遮光PET薄膜C。
本实施例中聚醚醚酮改性有机硅压敏胶层F，由聚醚醚酮改性有机硅压敏胶f组成，所述的聚醚醚酮改性有机硅压敏胶f，由以下步骤制得：(1)活性聚醚醚酮的制备：将10重量份聚醚醚酮粉体分批次加入至4重量份浓硫酸中，冰水浴中反应1h，然后移至室温继续反应3h，反应结束后，经过滤水洗至中性，然后经乙醇洗涤、真空干燥得活性聚醚醚酮；(2)改性有机硅压敏胶的制备：将活性聚醚醚酮12重量份、乙烯基MQ硅树脂(乙烯基百分含量为1.8％，M∶Q值为0.7)6重量份、多羟基聚硅氧烷(粘度为120mPa·s，羟基百分含量为4％)10重量份、107硅橡胶(粘度为8000mPa·s)14重量份、14重量份二甲基聚硅氧烷(粘度为20mPa·s)、4重量份黑色浆加入到反应装置中搅拌分散均匀，然后升温至120℃，向其中缓慢加入4份100ppm铂氯铂酸-二乙烯基四甲基二硅氧烷络合物，然后保温反应18min，然后加入0.1份阻聚剂，同时冷却至室温，即得到所述的聚醚醚酮改性有机硅压敏胶f。
性能检测：实施例1、实施例2、实施例3中高净化抗污的耐高低温双面遮光胶带的检测数据如下：
Figure BSA0000156190700000071
Figure BSA0000156190700000081

Claims (1)

1.一种高净化抗污的耐高低温双面遮光胶带，其特征在于，由黑磷烯改性遮光PET薄膜、聚醚醚酮改性有机硅压敏胶层、离型层纸组成；其中聚醚醚酮改性有机硅压敏胶层位于黑磷烯改性遮光PET薄膜的两面，离型层纸位于聚醚醚酮改性有机硅压敏胶层的外侧；
其中，所述的黑磷烯改性遮光PET薄膜，由以下步骤制得：准确称取PET聚酯切片25重量份、异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯6重量份、乙烯基MQ硅树脂10重量份、黑磷烯10重量份、2，4-二羟基二苯甲酮4重量份、乙二醇二丁醚20重量份加入到反应装置中，搅拌分散均匀，然后加热至100℃，回流反应5h，然后通过冷却热溶液法结晶，干燥结晶物，即得到改性遮光PET粗产品；在300℃、700r/min的双螺杆机转速的条件下，将改性遮光PET粗产品投入双螺杆机搅拌熔融2h，经挤出机将产物挤出，得到片材，再同时双向拉伸片材，得黑磷烯改性遮光PET薄膜；其中，所述乙烯基MQ硅树脂中乙烯基百分含量为1.3％，M∶Q值为0.7；
所述的聚醚醚酮改性有机硅压敏胶层，由聚醚醚酮改性有机硅压敏胶组成，所述的聚醚醚酮改性有机硅压敏胶，由以下步骤制得：(1)活性聚醚醚酮的制备：将10重量份聚醚醚酮粉体分批次加入至5重量份浓硫酸中， 冰水浴中反应0.5h，然后移至室温继续反应2h，反应结束后，经过滤水洗至中性，然后经乙醇洗涤、真空干燥得活性聚醚醚酮；(2)改性有机硅压敏胶的制备：将活性聚醚醚酮15重量份、乙烯基MQ硅树脂2重量份、多羟基聚硅氧烷15重量份、粘度为2000mPa·s的107硅橡胶20重量份、粘度为30mPa·s的二甲基聚硅氧烷10重量份、黑色浆2重量份加入到反应装置中搅拌分散均匀，然后升温至135℃，向其中缓慢加入1份100ppm乙醇改性的氯铂酸，然后保温反应10min，然后加入0.2份3-甲基-1-戊烯-3-醇，同时冷却至室温，即得到所述的聚醚醚酮改性有机硅压敏胶，其中，所述乙烯基MQ硅树脂中乙烯基百分含量为1.3％，M∶Q值为0.7，所述多羟基聚硅氧烷的粘度为300mPa·s，羟基百分含量为3％。
CN201711414198.8A 2017-12-16 2017-12-16 一种高净化抗污的耐高低温双面遮光胶带 Active CN108084903B (zh)