CN107163906A - 服装标签用胶水及其制备方法 - Google Patents
服装标签用胶水及其制备方法 Download PDFInfo
- Publication number
- CN107163906A CN107163906A CN201710447179.9A CN201710447179A CN107163906A CN 107163906 A CN107163906 A CN 107163906A CN 201710447179 A CN201710447179 A CN 201710447179A CN 107163906 A CN107163906 A CN 107163906A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- organosilicon
- label
- curing agent
- platinum catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种服装标签用胶水，由如下原料制成：铂催化剂0.5‑0.7质量份；有机硅95‑105质量份；UV固化剂2‑4质量份。本发明胶水内聚力高，标签从服装布料上剥离后，不容易留下残胶，并且由于有机硅为惰性材料，制成的胶水耐温性强，布料不容易产生色变。
Description
技术领域
本发明属于标签用胶水技术领域，尤其涉及一种服装标签用胶水及其制备方法。
背景技术
服装标签通常通过胶水粘附于服装上(如尺码贴)。
目前，服装标签常用的丙烯酸压敏胶水内聚力不足，在标签剥离后容易在服装上留下残胶，并且耐温性不强，在高温下容易在服装上产生色变。
发明内容
基于此，针对上述技术问题，提供一种服装标签用胶水及其制备方法。
为解决上述技术问题，本发明采用如下技术方案：
一种服装标签用胶水，由如下原料制成：
铂催化剂 0.5-0.7质量份；
有机硅 95-105质量份；
UV固化剂 2-4质量份。
所述铂催化剂为0.6质量份，所述有机硅为100质量份，所述UV固化剂为2-4质量份。
本方案还涉及一种服装标签用胶水的制备方法，包括：
将铂催化剂以及UV固化剂加入有机硅中，三者配比为：
铂催化剂 0.5-0.7质量份；
有机硅 95-105质量份；
UV固化剂 2-4质量份；
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间10-20分钟。
所述铂催化剂为0.6质量份，所述有机硅为100质量份，所述UV固化剂为2-4质量份。
本发明胶水内聚力高，标签从服装布料上剥离后，不容易留下残胶，并且由于有机硅为惰性材料，制成的胶水耐温性强，布料不容易产生色变。
具体实施方式
一种服装标签用胶水，由如下原料制成：
铂催化剂 0.5-0.7质量份；
有机硅 95-105质量份；
UV固化剂 2-4质量份。
其制备过程如下：
按上述配比将铂催化剂以及UV固化剂加入有机硅中。
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间10-20分钟。
本发明胶水粘合性能佳、内聚力高，移除性能优秀，标签从服装布料上剥离后，不会留下残胶，并且由于有机硅为惰性材料，制成的胶水耐温性强，布料不会产生色变。
较佳的，铂催化剂为0.6质量份，有机硅为100质量份，UV固化剂为2-4质量份，制成的胶水内聚力、耐温性更佳。
通过如下实验对上述性能进行验证：
在温度60-80℃、湿度60-80％的环境下，在多种常用服装的布料上通过本发明的胶水贴上标签(如尺码贴)，并用5kg的重物压在标签上7天，7天后将标签从服装布料上剥离，实验结果见表1：
表1
实施例1
本实施例为一种服装标签用胶水，由如下原料制成：
铂催化剂 0.5质量份；
有机硅 105质量份；
UV固化剂 2质量份。
其制备过程如下：
按上述配比将铂催化剂以及UV固化剂加入有机硅中。
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间10分钟。
实施例2
本实施例为一种服装标签用胶水，由如下原料制成：
铂催化剂 0.7质量份；
有机硅 95质量份；
UV固化剂 4质量份。
其制备过程如下：
按上述配比将铂催化剂以及UV固化剂加入有机硅中。
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间20分钟。
实施例3
本实施例为一种服装标签用胶水，由如下原料制成：
铂催化剂 0.6质量份；
有机硅 100质量份；
UV固化剂 3质量份。
其制备过程如下：
按上述配比将铂催化剂以及UV固化剂加入有机硅中。
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间15分钟。
但是，本技术领域中的普通技术人员应当认识到，以上的实施例仅是用来说明本发明，而并非用作为对本发明的限定，只要在本发明的实质精神范围内，对以上所述实施例的变化、变型都将落在本发明的权利要求书范围内。
Claims (4)
1.一种服装标签用胶水，其特征在于，由如下原料制成：
铂催化剂0.5-0.7质量份；
有机硅95-105质量份；
UV固化剂2-4质量份。
2.根据权利要求1所述的一种服装标签用胶水，其特征在于，所述铂催化剂为0.6质量份，所述有机硅为100质量份，所述UV固化剂为2-4质量份。
3.一种服装标签用胶水的制备方法，其特征在于，包括：
将铂催化剂以及UV固化剂加入有机硅中，三者配比为：
铂催化剂0.5-0.7质量份；
有机硅95-105质量份；
UV固化剂2-4质量份；
通过搅拌机对加入铂催化剂以及UV固化剂的有机硅进行搅拌，搅拌速度在30秒内从300转/秒提升至3000转/秒，搅拌时间10-20分钟。
4.根据权利要求3所述的一种服装标签用胶水的制备方法，其特征在于，所述铂催化剂为0.6质量份，所述有机硅为100质量份，所述UV固化剂为2-4质量份。