CN106752735B - 一种柔性陶瓷涂料组合物 - Google Patents
一种柔性陶瓷涂料组合物 Download PDFInfo
- Publication number
- CN106752735B CN106752735B CN201611056179.8A CN201611056179A CN106752735B CN 106752735 B CN106752735 B CN 106752735B CN 201611056179 A CN201611056179 A CN 201611056179A CN 106752735 B CN106752735 B CN 106752735B
- Authority
- CN
- China
- Prior art keywords
- parts
- component
- phosphate
- sodium
- oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种柔性陶瓷涂料组合物，由A组分和B组分按质量比为A：B＝8：1组成，A组分是磷酸盐；B组分按质量份数由酚醛环氧树脂24‑26份、聚乙烯醇缩丁醛15‑18份、金属氧化物20‑25份、磷酸锌5‑8份、陶瓷粉混合物10‑15份和稀土氧化物15‑18份组成。本发明对原料进行合理配置，这种柔性陶瓷涂料的表面硬度高，在酸碱环境下均有较高的防腐能力。
Description
技术领域
本发明涉及复合材料技术领域，具体涉及一种柔性陶瓷涂料组合物。
背景技术
目前，常规重防腐涂料通常是以锌铝粉为基材的，锌铝粉的基本物理属性决定了常规重防腐涂料涂层耐磨性差。由于酸性腐蚀和碱性腐蚀环境的腐蚀机理不同，常规重防腐涂料一般是利用电化学防腐原理，针对酸性腐蚀或碱性腐蚀其中一种环境设计的。而柔性陶瓷涂料解决常规重防腐涂料的耐磨、耐酸性腐蚀和耐碱性腐蚀性能三者不能兼得的问题。柔性陶瓷涂料是以改性环氧树脂加金红石、刚玉和石英粉等亚微米级陶瓷粉末组合的高端涂料，是难得的既耐磨又耐腐蚀的工程材料。由于是采用金红石、刚玉和石英粉等稳定的金属氧化物和封闭防腐机理，不受环境因素的影响，可以适应酸性和碱性不同环境下的防腐要求。陶瓷涂料在石油机械、化工储罐等石化领域有着广泛的应用前景。
发明内容
针对现有技术的不足，本发明提供了一种柔性陶瓷涂料组合物，这种柔性陶瓷涂料的表面硬度高，在酸碱环境下均有较高的防腐能力。
为实现以上目的，本发明通过以下技术方案予以实现：
一种柔性陶瓷涂料组合物，由A组分和B组分按质量比为A：B＝8：1组成，A组分是磷酸盐；B组分按质量份数由酚醛环氧树脂24-26份、聚乙烯醇缩丁醛15-18份、金属氧化物20-25份、磷酸锌5-8份、陶瓷粉混合物10-15份和稀土氧化物15-18份组成。
所述的B组分按质量份数由酚醛环氧树脂24份、聚乙烯醇缩丁醛15份、金属氧化物20份、磷酸锌5份、陶瓷粉混合物10-15份和稀土氧化物15份组成。
所述的B组分按质量份数由酚醛环氧树脂26份、聚乙烯醇缩丁醛18份、金属氧化物25份、磷酸锌8份、陶瓷粉混合物15份和稀土氧化物18份组成。
所述的B组分按质量份数由酚醛环氧树脂25份、聚乙烯醇缩丁醛16份、金属氧化物23份、磷酸锌6份、陶瓷粉混合物12份和稀土氧化物16份组成。
所述的B组分还设有防锈颜料3-6份。
所述的金属氧化物为氧化铁或氧化钠；或氧化铁与氧化钠混合物。
所述的磷酸盐为磷酸氢钙、磷酸钙、焦磷酸钙、磷酸二氢钾、磷酸氢二钾、酸式焦磷酸钠、磷酸二氢钠、磷酸氢二钠、磷酸钠或焦磷酸钠。
本发明有益效果：本发明当A组分和B组分相遇产生放热反应，使涂层在数分钟内升温4℃—8℃。这种放热反应将基材中的铁、B组分中的金属氧化物、A组分中的磷酸盐形成合金钝化层；该合金钝化层是一种稳定的金属复合物，会随时间增长至约50nm到约2µm；用催化形成非晶体层的方法会激起钢铁自然保护机理。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1：
一种柔性陶瓷涂料组合物，由A组分和B组分按质量比为A：B＝8：1组成，A组分是磷酸盐；所述的B组分按质量份数由酚醛环氧树脂24份、聚乙烯醇缩丁醛15份、金属氧化物20份、磷酸锌5份、陶瓷粉混合物10-15份和稀土氧化物15份组成；所述的B组分还设有防锈颜料3-6份，金属氧化物为氧化铁或氧化钠；或氧化铁与氧化钠混合物，所述的磷酸盐为磷酸氢钙、磷酸钙、焦磷酸钙、磷酸二氢钾、磷酸氢二钾、酸式焦磷酸钠、磷酸二氢钠、磷酸氢二钠、磷酸钠或焦磷酸钠。
所述的B组分按质量份数由酚醛环氧树脂26份、聚乙烯醇缩丁醛18份、金属氧化物25份、磷酸锌8份、陶瓷粉混合物15份和稀土氧化物18份组成。
所述的B组分按质量份数由酚醛环氧树脂25份、聚乙烯醇缩丁醛16份、金属氧化物23份、磷酸锌6份、陶瓷粉混合物12份和稀土氧化物16份组成。
实施例2：
一种柔性陶瓷涂料组合物，由A组分和B组分按质量比为A：B＝8：1组成，A组分是磷酸盐；所述的B组分按质量份数由酚醛环氧树脂26份、聚乙烯醇缩丁醛18份、金属氧化物25份、磷酸锌8份、陶瓷粉混合物15份和稀土氧化物18份组成；所述的B组分还设有防锈颜料3-6份，金属氧化物为氧化铁或氧化钠；或氧化铁与氧化钠混合物，所述的磷酸盐为磷酸氢钙、磷酸钙、焦磷酸钙、磷酸二氢钾、磷酸氢二钾、酸式焦磷酸钠、磷酸二氢钠、磷酸氢二钠、磷酸钠或焦磷酸钠。
所述的B组分按质量份数由酚醛环氧树脂25份、聚乙烯醇缩丁醛16份、金属氧化物23份、磷酸锌6份、陶瓷粉混合物12份和稀土氧化物16份组成。
实施例3：
一种柔性陶瓷涂料组合物，由A组分和B组分按质量比为A：B＝8：1组成，A组分是磷酸盐；所述的B组分按质量份数由酚醛环氧树脂25份、聚乙烯醇缩丁醛16份、金属氧化物23份、磷酸锌6份、陶瓷粉混合物12份和稀土氧化物16份组成；所述的B组分还设有防锈颜料3-6份，金属氧化物为氧化铁或氧化钠；或氧化铁与氧化钠混合物，所述的磷酸盐为磷酸氢钙、磷酸钙、焦磷酸钙、磷酸二氢钾、磷酸氢二钾、酸式焦磷酸钠、磷酸二氢钠、磷酸氢二钠、磷酸钠或焦磷酸钠。
本发明当A组分和B组分相遇产生放热反应，使涂层在数分钟内升温4℃—8℃。这种放热反应将基材中的铁、B组分中的金属氧化物、A组分中的磷酸盐形成合金钝化层；该合金钝化层是一种稳定的金属复合物，会随时间增长至约50nm到约2µm；用催化形成非晶体层的方法会激起钢铁自然保护机理，涂料喷涂到基材上发生两种反应：金属（铁）和酸之间的反应（形成惰性层，保护金属不受腐蚀）。酸和基体之间的反应（形成陶瓷层，保护惰性层不损坏并提供自修复性能）。在放大到6500倍的电镜下可以明显看出，基材与合金钝化层之间是极其致密的。
需要说明的是，在本文中，诸如第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。在没有更多限制的情况下，由语句“包括一个……”限定的要素，并不排除在包括所述要素的过程、方法、物品或者设备中还存在另外的相同要素。
以上实施例仅用以说明本发明的技术方案，而非对其限制；尽管参照前述实施例对本发明进行了详细的说明，本领域的普通技术人员应当理解：其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换；而这些修改或者替换，并不使相应技术方案的本质脱离本发明各实施例技术方案的精神和范围。
Claims (6)
1.一种柔性陶瓷涂料组合物，其特征在于：由A组分和B组分按质量比为A：B＝8：1组成，A组分是磷酸盐；B组分按质量份数由酚醛环氧树脂24-26份、聚乙烯醇缩丁醛15-18份、氧化铁或氧化钠或氧化铁与氧化钠混合物20-25份、磷酸锌5-8份、陶瓷粉混合物10-15份和稀土氧化物15-18份组成。
2.如权利要求1所述的柔性陶瓷涂料组合物，其特征在于，所述的B组分按质量份数由酚醛环氧树脂24份、聚乙烯醇缩丁醛15份、氧化铁或氧化钠或氧化铁与氧化钠混合物20份、磷酸锌5份、陶瓷粉混合物10-15份和稀土氧化物15份组成。
3.如权利要求1所述的柔性陶瓷涂料组合物，其特征在于，所述的B组分按质量份数由酚醛环氧树脂26份、聚乙烯醇缩丁醛18份、氧化铁或氧化钠或氧化铁与氧化钠混合物25份、磷酸锌8份、陶瓷粉混合物15份和稀土氧化物18份组成。
4.如权利要求1所述的柔性陶瓷涂料组合物，其特征在于，所述的B组分按质量份数由酚醛环氧树脂25份、聚乙烯醇缩丁醛16份、氧化铁或氧化钠或氧化铁与氧化钠混合物23份、磷酸锌6份、陶瓷粉混合物12份和稀土氧化物16份组成。
5.如权利要求1所述的柔性陶瓷涂料组合物，其特征在于，所述的B组分还设有防锈颜料3-6份。
6.如权利要求1所述的柔性陶瓷涂料组合物，其特征在于，所述的磷酸盐为磷酸氢钙、磷酸钙、焦磷酸钙、磷酸二氢钾、磷酸氢二钾、酸式焦磷酸钠、磷酸二氢钠、磷酸氢二钠、磷酸钠或焦磷酸钠。