CN106634038B - 一种活性深蓝染料及其制备方法 - Google Patents
一种活性深蓝染料及其制备方法 Download PDFInfo
- Publication number
- CN106634038B CN106634038B CN201611104713.8A CN201611104713A CN106634038B CN 106634038 B CN106634038 B CN 106634038B CN 201611104713 A CN201611104713 A CN 201611104713A CN 106634038 B CN106634038 B CN 106634038B
- Authority
- CN
- China
- Prior art keywords
- reactive
- dye
- parts
- formula
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种活性深蓝染料及其制备方法，其中活性深蓝染料具有式(I)所示结构，与现有技术相比，本发明的活性深蓝染料单体化合物结构新颖，性能优异，具有良好的色牢度，固色率高，染料稳定，耐洗、耐摩擦、耐日晒度好，与纤维结合稳定性好，成品具有优异的鲜艳度，适于大规模推广应用。
Description
技术领域
本发明属于精细化工领域，具体涉及一种活性染料，特别涉及一种活性深蓝染料及其制备方法和在棉纤维上印染的应用。
背景技术
活性染料色光鲜艳，湿牢度好，但其固色率、耐碱性、耐日晒牢度普遍较低，特别是蓝色系的活性染料如活性深兰M-2GE，其色光不鲜艳，溶解度差，染色的吸尽率低。其结构式如下：
多活性基的活性染料比单活性基活性染料有更高的吸尽率、更好的固色率，同时染料分子与纤维可以形成网状交联结构，使染料更好的与纤维相结合。因此，多活性基的活性染料的合成与开发一直是研究的热点。
发明内容
本发明的目的是提供一种结构新颖、性能优异的活性深蓝染料及其制备方法。该染料具有良好的固色率、色牢度，染色后有很好的稳定性，色光鲜艳，能广泛应用于棉、麻、人造棉等纤维制品的浸染、轧染、喷墨印花等染色工艺，而且生产成本低，可以大规模推广应用。
本发明的另一目的是提供一种上述活性深蓝染料的制备方法。
本发明的第三目的是提供一种上述活性深蓝染料的应用。
本发明的目的可以通过以下措施达到：
一种通式(Ⅰ)所示结构的活性深蓝染料，
其中，
A为具有乙烯基砜基团的单取代或多取代的苯基、萘基或乙基氨甲酰基苯基，其取代基选自氢、-SO3M或C1～3烷基；
D为具有乙烯基砜基团的单取代或多取代的苯基或乙基氨甲酰基苯基，其取代基选自氢、-SO3M或C1～3烷基；
X为卤素；
R1为氢、C1～4烷基或芳基；
R2为氢、C1～4烷基、C1～4烷氧基、-SO3M或芳基；
M为H或碱金属。
在一种方案中，A选自如下基团：
在一种方案中，D选自如下基团：
在一种方案中，R1为甲基、乙基、正丙基、正丁基或苯基。
在一种方案中，R2为氢或-SO3M。
在一种方案中，X为F或Cl。
在一种方案中，M为H、Na或K。
进一步的，本发明优选的通式(Ⅰ)化合物结构如下：
本发明所述式(Ⅰ)的活性深蓝染料，可以以游离酸(即M为H)或优选一碱金属盐(M为Na、K)的形式来制备，在生产需要的情况下，可按常规条件进行酸式和盐式的相互转化，对染料的染色性能没有影响。
本发明提供了一种活性深蓝染料的制备方法，其包括如下步骤：
(1)、式(Ⅱ)重氮盐与式(Ⅲ)化合物偶合得(Ⅳ)化合物，
(2)、式(Ⅴ)化合物与式(Ⅵ)化合物经缩合反应得式(Ⅶ)化合物；
(3)、式(Ⅷ)化合物与式(Ⅸ)化合物经还原胺化反应得式(X)化合物；
(4)、式(Ⅶ)化合物与式(X)化合物经缩合反应得式(XI)化合物。
(6)、式(XI)重氮化制得重氮盐(XII)与式(Ⅳ)化合物偶合得式(Ⅰ')化合物
(6)、式(Ⅰ')化合物经碱性水解后得式(Ⅰ)化合物
其中，A‘为带有β-硫酸酯乙基砜的单取代或多取代的苯基、萘基或乙基氨甲酰基苯基，A为具有乙烯基砜基团的单取代或多取代的苯基、萘基或乙基氨甲酰基苯基，A‘和A的取代基选自氢、-SO3M或C1～3烷基；D’为带有β-硫酸酯乙基砜的单取代或多取代的苯基或乙基氨甲酰基苯基，D为具有乙烯基砜基团的单取代或多取代的苯基或乙基氨甲酰基苯基，D’和D的取代基选自氢、-SO3M或C1～3烷基；X为卤素；R1为氢、C1～4烷基或芳基；R2为氢、C1～4烷基、C1～4烷氧基、-SO3M或芳基；M为H或碱金属。
在步骤1中，将式(Ⅲ)化合物加到式(Ⅱ)重氮盐中，在温度5-10℃下进行偶合，得(Ⅳ)化合物；步骤(1)具体按照如下方法进行：将式(Ⅲ)化合物加到式(Ⅱ)重氮盐中，温度5-10℃进行偶合，得(Ⅳ)化合物。
在步骤2中，式(Ⅳ)化合物与式(Ⅴ)化合物混合后进行缩合反应，反应中调整pH＝3-5，充分反应后得式(Ⅶ)化合物；步骤(2)具体按照如下方法进行：式(Ⅵ)化合物冰磨打浆，将式(Ⅴ)化合物加入到浆液中，进行缩合反应，该缩合液用小苏打调整pH＝3-5，充分反应后，pH值稳定，料液变清，得式(Ⅶ)化合物。
在步骤3中，式(Ⅷ)化合物与式(Ⅸ)化合物混合，在温度40-80℃下进行催化加氢还原反应，得式(X)化合物；步骤(3)具体按照如下方法进行：式(Ⅷ)化合物与式(Ⅸ)化合物在乙醇中混合，温度40-80℃，催化加氢还原，过滤、蒸干溶剂得式(X)化合物。
在步骤4中，将式(X)化合物加入含式(Ⅵ)化合物料液中，进行缩合反应，反应中调整pH＝3-5，充分反应后得式(XI)化合物；步骤(4)具体按照如下方法进行：将式(X)化合物加入式(Ⅵ)化合物料液中，进行缩合反应，该缩合液用小苏打调整pH＝3-5，充分反应后，pH值稳定，料液变清，得式(XI)化合物。
在步骤5中，式(XI)化合物加入冰水、盐酸和亚硝酸钠，保持温度小于10℃、pH＝1.0±0.2进行重氮化得重氮盐XII；将该重氮盐XII加入到含式(Ⅳ)化合物料液中，调节pH＝6-8、温度5-10℃进行偶合反应，得式(Ⅰ')化合物；步骤(5)具体按照如下方法进行：式(XI)化合物加入冰水和盐酸，打浆均匀后，滴加亚硝酸钠溶液，保持温度小于10℃、pH＝1.0±0.2进行重氮化得重氮盐；将该重氮盐加入到式(Ⅳ)化合物料液中，用小苏打调节pH＝6-8，温度5-10℃进行偶合，得式(Ⅰ')化合物。
在步骤6中，式(Ⅰ')化合物于pH＝9-10、温度40-70℃下进行反应，得式(Ⅰ)化合物。步骤(6)具体按照如下方法进行：式(Ⅰ')化合物再于pH＝9-10，温度40-70℃反应，得式(Ⅰ)化合物，经前标准化加工，喷雾烘干得成品。
除非另外说明，在说明书和权利要求中使用的“烷基”表示1-20个碳原子的饱和的脂烃基，包括直链和支链基团(本申请书中提到的数字范围，例如“1-20”，是指该基团，此时为烷基，可以含1个碳原子、2个碳原子、3个碳原子等，直至包括20个碳原子)。含1－5个碳原子的烷基称为低级烷基。当低级烷基没有取代基时，称其为未取代的低级烷基。更优选的是，烷基是有1-10个碳原子的中等大小的烷基，例如甲基、乙基、丙基、2-丙基、正丁基、异丁基、叔丁基、戊基等。最好是，烷基为有1-5个碳原子的低级烷基，例如甲基、乙基、丙基、2-丙基、正丁基、异丁基或叔丁基等。烷基可以是取代的或未取代的。
除非另外说明，在说明书和权利要求中使用的“芳基”表示任何从简单芳香环衍生出的官能团或取代基，包括但不限于苯基、邻甲苯基、1-萘基(或α-萘基)、2-萘基等。
本发明公开了一种染料组合物，它以上述的活性深蓝染料为活性组分，辅以染料领域中的助剂。
本发明公开了另一种染料组合物，它以通式(Ⅰ)所示结构的活性深蓝染料和通式(一)所示结构的活性深红染料为主要活性成分，二者之间的质量比为55～95：5～45，
其中，A、D、X、R1、R2的定义如上所述；A1为具有-SO3M或-SO2C2H4OSO3M取代基的单取代或多取代的苯基或萘基；D1为取代或非取代的苯基，其取代基选自氢、-SO3M或C1～3烷基；M为H或碱金属。
在一种优选方案中，该染料组合物中通式(Ⅰ)所示结构的活性深蓝染料和通式(一)所示结构的活性深红染料的质量比为60～90：10～40。
在一种优选方案中，A1选自如下基团：
在一种优选方案中，D1选自如下基团：
在一种优选方案中，M为H、Na或K。
在另一种优选方案中，通式(一)所示结构的活性深红染料具体可选自下述
化合物：
用本发明所述活性深蓝染料以及组合物所制成的染料成品可以以固体颗粒、粉末或溶液存在，含有的电解质盐类，如氯化钠、氯化钾、硫酸钠、硫酸钾以及商业染料中常见的助剂。
本发明所提供的活性深蓝染料以及组合物所制成的染料成品可应用在纤维织品印染中，特别是应用在纤维制品棉、麻或人造棉的浸染、轧染或喷墨印花染色方面的应用。所述纤维制品可以是棉、麻、人造棉等材料。与现有技术相比，本发明的活性深蓝染料单体化合物结构新颖，性能优异，具有良好的色牢度，固色率高，染料稳定，耐洗、耐摩擦、耐日晒度好，与纤维结合稳定性好，成品具有优异的鲜艳度，适于大规模推广应用。
具体实施方式
下面结合具体实施例对本发明进行进一步描述，本发明保护范围包含但不仅限于此实施例：
实施例1：式(Ⅰ-1)化合物的制备
(1)重氮、偶合反应
250ml烧杯中，加入20份(质量份)冰，24.3份30％盐酸，28.1份间位酯，冰磨打浆30min，6.97份亚硝酸钠缓慢加入生成重氮盐，待亚硝酸钠完全加入后再搅拌1h，用氨基磺酸消除微过量的亚硝酸钠；将31.9份H酸加到重氮盐中，加完后继续反应至重氮盐完全消失，同时保持体系温度为0-10℃。
(2)对苯二胺与三聚氟氰一次缩合
1000ml的烧瓶中，加入10.8份对苯二胺、50份的冰水，将13.5份(折百)三聚氟氰加入到对苯二胺中，用小苏打调节pH＝3.5-5.0，保持温度0-10℃，反应4-6h，料液澄清透明，用氨基试剂检测反应终点，保持温度稳定，待二次缩合。
(3)醛与胺的还原胺化
1000ml烧瓶中，加入4.4份正丁醛与28.1份间位酯，50份乙醇，1份的镍催化剂，10Mpa、H2、60-80℃还原12h，过滤除去催化剂，蒸干溶剂得仲胺产品。
(4)、仲胺与一缩组分二次缩合
仲胺加入到一缩组分中，将反应液升温至30-40℃，同时用小苏打调节pH＝3.5-5.0，保持温度30-40℃，反应4-6h，料液澄清透明，用氨基试剂检测反应终点。
(5)、二缩组分重氮与偶合组分偶合
二次缩合组分加入20份冰，24.3份30％盐酸，冰磨打浆30min，缓慢加入6.97份亚硝酸钠生成重氮盐，待亚硝酸钠完全加入后再搅拌1h，用氨基磺酸消除微过量的亚硝酸钠；将重氮盐加入到上述一次偶合组分中，加加完后小苏打调节pH＝5.5-8.0，保持pH值、温度为0-10℃继续反应2h，重氮盐完全消失。
(6)二偶组分水解反应
向上述溶液中加入纯碱，调节pH＝9-10，升温至40-70℃，反应8-10h。经标准化加工，喷雾烘干得染料成品。(纯化后，其MS：[M+H]+＝982.07)
实施例2：式(Ⅰ-2)化合物的制备
(1)重氮、偶合反应
250ml烧杯中，加入20份冰，24.3份30％盐酸，28.1份对位酯，冰磨打浆30min，6.97份亚硝酸钠缓慢加入生成重氮盐，待亚硝酸钠完全加入后再搅拌1h，用氨基磺酸消除微过量的亚硝酸钠；将31.9份H酸缓慢滴加到重氮盐中，加完后继续反应2h，重氮盐完全消失，同时保持体系温度为0-10℃。
(2)间苯二胺与三聚氟氰一次缩合
1000ml的烧瓶中，加入10.8份间苯二胺、50份的(质量份)冰水，将13.5份(折百)三聚氟氰加入到间苯二胺中，用小苏打调节pH＝3.5-5.0，保持温度0-10℃，反应4-6h，料液澄清透明，用氨基试剂检测反应终点，保持温度稳定，待二次缩合。
(3)醛与胺的还原胺化
1000ml烧瓶中，加入4.4份正丁醛与28.1份对位酯，50份乙醇，1份的镍催化剂，10MPaH2，60-80℃还原12h，过滤除去催化剂，蒸干溶剂得仲胺产品。
(4)、仲胺与一缩组分二次缩合
仲胺加入到一缩组分中，将反应液升温至30-40℃，同时用小苏打调节pH＝3.5-5.0，保持温度30-40℃，反应4-6h，料液澄清透明，用氨基试剂检测反应终点。
(5)、二缩组分重氮与偶合组分二次偶合
二次缩合组分加入20份冰，24.3份30％盐酸，冰磨打浆30min，缓慢加入6.97份亚硝酸钠生成重氮盐，待亚硝酸钠完全加入后再搅拌1h，用氨基磺酸消除微过量的亚硝酸钠；将重氮盐加入到上述一次偶合组分中，加加完后小苏打调节pH＝5.5-8.0，保持pH值、温度为0-10℃继续反应2h，重氮盐完全消失。
(6)偶合组分水解反应
向上述溶液中加入纯碱，调节pH＝9-10，升温40-70℃，反应8-10h，调整pH＝6.5-7。经标准化加工，喷雾烘干得染料成品。(纯化后，其MS：[M+H]+＝964.12)
其中，M为Na。
实施例3-5：
按照实施例1所述方法，不同的是与H酸偶合的重氮组分、与三聚氯氰的缩合组分、以及还原胺化的胺与醛，采用下表1中等摩尔量的原料化合物进行反应，即可获得本发明所述的式(Ⅰ-3～Ⅰ-5)活性深蓝染料。
其中，M为Na。
实施例6：一种活性深红染料化合物的制备
(1)一次重氮、偶合反应
250ml烧杯中，加入20份冰，24.3份30％盐酸，36.1份磺化对位酯，冰磨打浆30min，缓慢加入6.97份亚硝酸钠生成重氮盐，待亚硝酸钠完全加入后再搅拌1h，用氨基磺酸消除微过量的亚硝酸钠；将重氮盐缓慢滴加到23.9份J酸中，边滴加边用小苏打调节pH＝3-5，加加完后继续反应2h，同时保持体系温度为0-10℃，重氮盐完全消失。
(2)酰氯与对苯二胺缩合
1000ml的烧瓶中，加入50份的(质量份)冰水，10.8份(折百)对苯二胺打浆1h，滴加23.2份4-(2-氯乙基砜基)丁酰氯，用小苏打调节pH＝3.5-5.0，保持温度0-10℃，反应4-6h，料液澄清透明，保持温度稳定，待重氮。
(3)二次重氮、偶合反应
在上述缩合液中加入20份冰，24.3份30％盐酸，缓慢加入6.97份亚硝酸钠生成重氮盐，待亚硝酸钠完全加入后再搅拌1h，用氨基磺酸消除微过量的亚硝酸钠；将重氮盐缓慢滴加到一次重氮偶合组分中，边滴加边用小苏打调节pH＝5.5-8.0，加加完后继续反应2h，重氮盐完全消失，同时保持体系温度为0-10℃，经标准化加工，喷雾烘干得染料成品。(纯化后，其MS：[M+H]+＝968.96)
实施例7：一种活性深红染料化合物的制备
(1)一次重氮、偶合反应
250ml烧杯中，加入20份(质量份)冰，24.3份30％盐酸，28.1份间位酯，冰磨打浆30min，6.97份亚硝酸钠缓慢加入生成重氮盐，待亚硝酸钠完全加入后再搅拌1h，用氨基磺酸消除微过量的亚硝酸钠；将重氮盐缓慢滴加到23.9份J酸中，边滴加边用小苏打调节pH＝3-5加加完后继续反应2h，重氮盐完全消失，同时保持体系温度为0-10℃。
(2)酰氯与间苯二胺缩合
1000ml的烧瓶中，加入50份的冰水，10.8份(折百)间苯二胺打浆1h，23.2份4-(2-氯乙基砜基)丁酰氯，用小苏打调节pH＝3.5-5.0，保持温度0-10℃，反应4-6h，料液澄清透明，保持温度稳定，待重氮。
(3)二次重氮、偶合反应
在上述缩合液中加入20份冰，24.3份30％盐酸，缓慢加入6.97份亚硝酸钠生成重氮盐，待亚硝酸钠完全加入后再搅拌1h，用氨基磺酸消除微过量的亚硝酸钠；将重氮盐缓慢滴加到一次偶合组分中，边滴加边用小苏打调节pH＝5.5-8.0，加加完后继续反应2h，重氮盐完全消失，同时保持体系温度为0-10℃，经标准化加工，喷雾烘干得染料成品。(纯化后，其MS：[M+H]+＝890.02)
实施例8：一种活性深红染料化合物的制备
(1)一次重氮、偶合反应
250ml烧杯中，加入20份冰，24.3份30％盐酸，41份6-羟乙基砜基硫酸酯-2-萘胺-1-磺酸冰磨打浆50min，缓慢加入6.97份亚硝酸钠生成重氮盐，待亚硝酸钠完全加入后再搅拌1h，用氨基磺酸消除微过量的亚硝酸钠；将重氮盐缓慢滴加到23.9份J酸中，边滴加边用小苏打调节pH＝3-5，加加完后继续反应2h，重氮盐完全消失，同时保持体系温度为0-10℃。
(2)酰氯与对苯二胺缩合
1000ml的烧瓶中，加入50份的(质量份)冰水，10.8份(折百)对苯二胺打浆1h，滴加23.2份4-(2-氯乙基砜基)丁酰氯，用小苏打调节pH＝3.5-5.0，保持温度0-10℃，反应4-6h，料液澄清透明，保持温度稳定，待重氮偶合。
(3)二次重氮、偶合反应
在上述缩合液中加入20份冰，24.3份30％盐酸，缓慢加入6.97份亚硝酸钠生成重氮盐，待亚硝酸钠完全加入后再搅拌1h，用氨基磺酸消除微过量的亚硝酸钠；将重氮盐缓慢滴加到一次重氮偶合组分中，边滴加边用小苏打调节pH＝5.5-8.0，加加完后继续反应2h，重氮盐完全消失，同时保持体系温度为0-10℃，经标准化加工，喷雾烘干得染料成品。(纯化后，其MS：[M+H]+＝1041.97)
实施例9：
采用本发明实施例4制得的活性深蓝染料85份、实施例7制得的活性深红染料15份进行复配制成偏兰光的一种棕黑色活性染料。
实施例10：
采用本发明实施例1制得的活性深蓝染料80份、实施例6制得的活性深红染料20份进行复配制成偏红光的一种棕黑色活性染料。
实施例11：
采用本发明实施例5制得的活性深蓝染料70份、实施例8制得的活性深红染料30份进行复配制成偏兰光的一种棕色活性染料。
实施例12：
采用本发明实施例1制得的活性深蓝染料65份、实施例6制得的活性深红染料35份进行复配制成偏红光的一种棕色活性染料。
实施例13：
采用本发明实施例4制得的活性深蓝染料60份、实施例7制得的活性深红染料40份进行复配制成偏红光的一种红棕色活性染料。
实施例14：
采用本发明实施例5制得的活性深蓝染料60份、实施例8制得的活性深红染料40份进行复配制成偏红光的一种红棕色活性染料。
染色实施例1：
取2g根据实施例1-6得到活性深蓝染料与元明粉配成330ml染液。在恒温下将棉布浸染一段时间后，加入一定量的纯碱固色一段时间，再进行水洗、皂洗、干燥。分别按GB/T3920-2008、GB/T 3922-1995和GB/T 3921-2008中的方法测试其耐摩擦色牢度、耐日晒牢度、耐水洗牢度，同时与同类型的M-2GE兰、Supra Navy Blue 3GF作对比，结果如表2，从结果可以看出，本发明提供的活性深蓝染料，各项牢度性能优良，染料吸尽率固色率高、用水用盐量少、染色温度不高节能，适于生产推广。
表2染色实施例性能比较
染色深度：3％
从结果可以看出，本发明实施例1、2提供的活性深蓝染料染色温度为40℃，染色的浴比为1：5比M-2GE兰、Supra Navy Blue 3GF的染色浴比1：20小75％，大大节约染色用水量达75％；同时固色温度下降20℃，节约能耗30％以上；
实施例3、4提供的活性深蓝染料染色温度为60℃，染色的浴比为1：8比M-2GE兰、Supra Navy Blue 3GF的染色浴比1：20小60％，大大节约染色用水量60％；实施例5染色的浴比为1：5比M-2GE兰、Supra Navy Blue 3GF的染色浴比1：20小75％，大大节约染色用水量达75％；
实施例1-5提供的活性深蓝染料染色的吸尽率为92-96％比M-2GE兰、Supra NavyBlue 3GF80-82％高12-20％，活性深蓝固色率为85-90％比M-2GE兰、Supra Navy Blue 3GF的71％和68％高20-35％，大大减少染色废水40％；
实施例1-5提供的活性深蓝染料染色各项牢度性能优良，特别是摩擦牢度(干)比M-2GE兰、Supra Navy Blue 3GF提高1-2级，摩擦牢度(湿)比M-2GE兰、Supra Navy Blue3GF提高1-2级，耐日晒牢度比M-2GE兰、Supra Navy Blue 3GF提高2-3级，水洗牢度比M-2GE兰、Supra Navy Blue 3GF提高1-2级。
染色实施例2：
取2g根据实施例9-14得到的棕黑色、红棕色活性染料与元明粉配成330ml染液。在恒温下将棉布浸染一段时间后，加入一定量的纯碱固色一段时间，再进行水洗、皂洗、干燥。分别按GB/T 3920-2008、GB/T 3922-1995和GB/T 3921-2008中的方法测试其耐摩擦色牢度、耐日晒牢度、耐水洗牢度，同时与同类型的棕黑色、红棕色活性染料作对比，结果如表2，从结果可以看出，本发明提供的棕黑色、红棕色活性染料，各项牢度性能优良，染色用水用盐量少、溶解度、吸尽率、固色率高，适于推广生产。
表3染色实施例(棕黑色活性染料)性能比较
染色深度：3％
从结果可以看出，本发明实施例9、10提供的棕黑色活性染料染色的浴比为1：5比活性黑M‐2R、活性灰M‐4R的染色浴比1：20小75％，大大节约染色用水量达75％；
实施例9、10提供的棕黑色活性染料染色的吸尽率为92-94％比活性黑M‐2R、活性灰M‐4R高12-18％，固色率为88-90％比活性黑M‐2R、活性灰M‐4R的60％和65％高35-50％，大大减少染色废水35-50％；
实施例9、10提供的棕黑色活性染料染色各项牢度性能优良，特别是摩擦牢度(干)比活性黑M‐2R、活性灰M‐4R提高1-2级，摩擦牢度(湿)比活性黑M‐2R、活性灰M‐4R提高1-2级，耐日晒牢度比活性黑M‐2R、活性灰M‐4R提高2级，水洗牢度比活性黑M‐2R、活性灰M‐4R提高2级。
表4染色实施例(棕色、红棕色活性染料)性能比较
染色深度：3％
从结果可以看出，本发明实施例11-14提供的棕色、红棕色活性染料染色的浴比为1：5比活性红棕K-B3R、活性棕K-GR的染色浴比1：20小75％，大大节约染色用水量达75％；
实施例11-14提供的棕色、红棕色活性染料染色的吸尽率为92-96％比活性红棕K-B3R、活性棕K-GR的80％高15-20％，固色率为82-90％比活性红棕K-B3R、活性棕K-GR的60％和54％高35-67％，大大减少染色废水35-67％；
实施例11-14提供的棕色、红棕色活性染料染色各项牢度性能优良，特别是摩擦牢度(干)比活性红棕K-B3R、活性棕K-GR提高1-2级，摩擦牢度(湿)比活性红棕K-B3R、活性棕K-GR提高1-2级，耐日晒牢度比活性红棕K-B3R、活性棕K-GR提高2级，水洗牢度比活性红棕K-B3R、活性棕K-GR提高2级。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (5)
1.一类活性深蓝染料，其选自下述化合物：
其中，M为Na。
2.权利要求1所述的活性深蓝染料在纤维织品印染中的应用。
3.权利要求1所述的活性深蓝染料在纤维制品棉、麻或人造棉的浸染、轧染或喷墨印花染色方面的应用。
4.一种染料组合物，它以权利要求1所述的活性深蓝染料和通式(一)所示结构的活性深红染料为主要活性成分，二者之间的质量比为55～95：5～45，
其中，
A1为具有-SO3M或-SO2C2H4OSO3M取代基的单取代或多取代的苯基或萘基；
D1为取代或非取代的苯基，其取代基选自-SO3M或C1～3烷基，
M为Na。
5.根据权利要求4所述的染料组合物，其中权利要求1所述的活性深蓝染料和通式(一)所示结构的活性深红染料的质量比为60～90：10～40；其中，A1选自如下基团：
D1选自如下基团：