CN105819812A - 一种无机保温材料 - Google Patents
一种无机保温材料 Download PDFInfo
- Publication number
- CN105819812A CN105819812A CN201610136395.7A CN201610136395A CN105819812A CN 105819812 A CN105819812 A CN 105819812A CN 201610136395 A CN201610136395 A CN 201610136395A CN 105819812 A CN105819812 A CN 105819812A
- Authority
- CN
- China
- Prior art keywords
- parts
- heat insulation
- insulation material
- inorganic heat
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种无机保温材料。无机保温材料包括玻化微珠、高岭土、改性膨润土、肥皂粉、过氧化铁纳米粉末、岩棉、漂珠、石膏粉、海泡石、抗静电剂、促降解剂、磷酸二氢钾、粉煤灰、火山灰；其中改性膨润土的制备方法为：将膨润土研磨至200目，浸渍于磷酸溶液中，在80℃水浴温度下加热搅拌10‑20min，抽滤去液，用蒸馏水将滤液洗至中性，于150℃下干燥，研磨至200目，即得。本发明配方合理，原料均易获得，成本较低，制备方法简单，制备出来的保温材料无毒无味，绿色环保，保温效果好。
Description
技术领域
本发明涉及一种无机保温材料，属于保温材料领域。
背景技术
无机保温材料具有节能利废、保温隔热、防火防冻、耐老化的优异性能以及低廉的价格等特点，有着广泛的市场需求。目前保温材料多处于单一结构，如岩棉、玻璃纤维、陶瓷纤维等制品属纤维状结构，珍珠岩、陶瓷微珠等属于颗粒微孔结构，这些单一结构的保温材料使用过程中都存在着保温性能因材料结构和施工而大大降低的问题。
申请号为201310014752.9《一种无机保温材料及其制备方法》公开了一种无机保温材料，由二氧化硅气凝胶、可溶性硅酸盐、氧化锡锑、空心玻璃微珠和十二烷基三甲基氯化铵经偶联剂改性后浸润至玻璃纤维毡上得到的。该发明具有良好的抗水性，保温性能好，但是成本高，不适宜大范围的推广应用。
发明内容
本发明的目的在于克服现有技术的不足，提供一种保温效果好的无机保温材料。
本发明是通过以下技术方案来实现的：
一种无机保温材料，以重量百分比计，包括玻化微珠20-50份、高岭土30-60份、改性膨润土5-10份、肥皂粉15-45份、过氧化铁纳米粉末2-7份、岩棉1-6份、漂珠10-20份、石膏粉10-15份、海泡石2-7份、抗静电剂1-5份、促降解剂1-5份、磷酸二氢钾3-8份、粉煤灰2-6份、火山灰40-90份。
所述促降解剂为3-甲基丙烯酰氧基丙基三甲氧基硅烷、月桂醇聚氧乙烯醚和乙二醇的混合物，其中3-甲基丙烯酰氧基丙基三甲氧基硅烷、月桂醇聚氧乙烯醚和乙二醇的混合物分别为15-20份、3-7份和3-7份。
进一步的，玻化微珠、过氧化铁纳米粉末和肥皂粉为200目，高岭土为100目，石膏粉为60目。
进一步的，以重量百分比计，包括玻化微珠30份、高岭土40份、改性膨润土7份、肥皂粉30份、过氧化铁纳米粉末5份、岩棉4份、漂珠15份、石膏粉13份、海泡石5份、抗静电剂4份、促降解剂4份、磷酸二氢钾4份、粉煤灰4份、火山灰60份。
进一步的，改性膨润土的制备方法为：将膨润土研磨至200目，浸渍于磷酸溶液中，在80℃水浴温度下加热搅拌10-20min，抽滤去液，用蒸馏水将滤液洗至中性，于150℃下干燥，研磨至200目，即得。
进一步的，加热搅拌时间为15min。
进一步的，所述抗静电剂为二硫代氨基甲酸的碱金属盐。
本发明的有益效果如下：
本发明采用无机物作为原料，配方合理，且原料均易获得，成本较低，制备方法简单，制备出来的保温材料无毒无味，绿色环保，保温效果好；经过改性的膨润土粒径小、质轻、中空，具有隔热、绝缘和隔音等特性。
制备得到的无机保温材料导热系数为0.01-0.08w/(m.k)，燃烧等级为A级，最高使用温度为1400℃，抗压强度为1.0-1.3MPa，吸水率小于或等于0.1％。
具体实施方式
实施例1
本实施例中，一种无机保温材料，以重量百分比计，包括玻化微珠20份、高岭土60份、改性膨润土5份、肥皂粉45份、过氧化铁纳米粉末2份、岩棉6份、漂珠10份、石膏粉15份、海泡石2份、抗静电剂5份、促降解剂1份、磷酸二氢钾8份、粉煤灰2份、火山灰90份。
其中，玻化微珠、过氧化铁纳米粉末和肥皂粉为200目，高岭土为100目，石膏粉为60目。
所述改性膨润土的制备方法为：将膨润土研磨至200目，浸渍于磷酸溶液中，在80℃水浴温度下加热搅拌20min，抽滤去液，用蒸馏水将滤液洗至中性，于150℃下干燥，研磨至200目，即得。
实施例2
本实施例中，一种无机保温材料，以重量百分比计，包括玻化微珠30份、高岭土40份、改性膨润土7份、肥皂粉30份、过氧化铁纳米粉末5份、岩棉4份、漂珠15份、石膏粉13份、海泡石5份、抗静电剂4份、促降解剂4份、磷酸二氢钾4份、粉煤灰4份、火山灰60份。
其中，玻化微珠、过氧化铁纳米粉末和肥皂粉为200目，高岭土为100目，石膏粉为60目。
所述改性膨润土的制备方法为：将膨润土研磨至200目，浸渍于磷酸溶液中，在80℃水浴温度下加热搅拌15min，抽滤去液，用蒸馏水将滤液洗至中性，于150℃下干燥，研磨至200目，即得。
实施例3
本实施例中，一种无机保温材料，其特征在于，以重量百分比计，包括玻化微珠50份、高岭土30份、改性膨润土10份、肥皂粉15份、过氧化铁纳米粉末7份、岩棉1份、漂珠20份、石膏粉10份、海泡石7份、抗静电剂1份、促降解剂5份、磷酸二氢钾3份、粉煤灰6份、火山灰40份。
其中，玻化微珠、过氧化铁纳米粉末和肥皂粉为200目，高岭土为100目，石膏粉为60目。
所述改性膨润土的制备方法为：将膨润土研磨至200目，浸渍于磷酸溶液中，在80℃水浴温度下加热搅拌10min，抽滤去液，用蒸馏水将滤液洗至中性，于150℃下干燥，研磨至200目，即得。
对比例1
一种无机保温材料，以重量百分比计，包括玻化微珠10份、高岭土70份、膨润土1份、肥皂粉10份、过氧化铁纳米粉末10份、岩棉12份、漂珠3份、石膏粉20份、海泡石1份、抗静电剂10份、促降解剂8份、磷酸二氢钾14份、粉煤灰10份、火山灰20份。
其中，玻化微珠、过氧化铁纳米粉末和肥皂粉为200目，高岭土为100目，石膏粉为60目。
所述改性膨润土的制备方法为：将膨润土研磨至200目，浸渍于磷酸溶液中，在80℃水浴温度下加热搅拌20min，抽滤去液，用蒸馏水将滤液洗至中性，于150℃下干燥，研磨至200目，即得。
对比例1与实施例1、2、3相比，是各原料的组成不同，所以没有实施例1、2、3的效果，但是仍然比一般的保温材料性能好，抗压强度高，吸水率低。
对比例2
一种无机保温材料，以重量百分比计，包括玻化微珠20份、高岭土60份、膨润土5份、肥皂粉45份、过氧化铁纳米粉末2份、岩棉6份、漂珠10份、石膏粉15份、海泡石2份、抗静电剂5份、促降解剂1份、磷酸二氢钾8份、粉煤灰2份、火山灰90份。
其中，玻化微珠、过氧化铁纳米粉末和肥皂粉为200目，高岭土为100目，石膏粉为60目。
对比例2与实施例1不同在于膨润土没有经过改性。
各实施例与对比例得到的保温材料的性能见下表：
| 导热系数 | 燃烧等级 | 最高使用温度 | 抗压强度 | 吸水率 | |
| 实施例1 | 0.02w/(m.k) | A级 | 1200℃ | 1.0MPa | 0.08％ |
| 实施例2 | 0.01w/(m.k) | A级 | 1400℃ | 1.3MPa | 0.10％ |
| 实施例3 | 0.08w/(m.k) | A级 | 1200℃ | 0.8MPa | 0.08％ |
| 对比例1 | 0.14w/(m.k) | B级 | 800℃ | 0.5MPa | 0.12％ |
| 对比例2 | 0.18w/(m.k) | B级 | 800℃ | 0.5MPa | 0.09％ |
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是说明本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (6)
1.一种无机保温材料，其特征在于，以重量百分比计，包括玻化微珠20-50份、高岭土30-60份、改性膨润土5-10份、肥皂粉15-45份、过氧化铁纳米粉末2-7份、岩棉1-6份、漂珠10-20份、石膏粉10-15份、海泡石2-7份、抗静电剂1-5份、促降解剂1-5份、磷酸二氢钾3-8份、粉煤灰2-6份、火山灰40-90份。
2.根据权利要求1所述的一种无机保温材料，其特征在于，玻化微珠、过氧化铁纳米粉末和肥皂粉为200目，高岭土为100目，石膏粉为60目。
3.根据权利要求1所述的一种无机保温材料，其特征在于，以重量百分比计，包括玻化微珠30份、高岭土40份、改性膨润土7份、肥皂粉30份、过氧化铁纳米粉末5份、岩棉4份、漂珠15份、石膏粉13份、海泡石5份、抗静电剂4份、促降解剂4份、磷酸二氢钾4份、粉煤灰4份、火山灰60份。
4.根据权利要求1所述的一种无机保温材料，其特征在于，改性膨润土的制备方法为：将膨润土研磨至200目，浸渍于磷酸溶液中，在80℃水浴温度下加热搅拌10-20min，抽滤去液，用蒸馏水将滤液洗至中性，于150℃下干燥，研磨至200目，即得。
5.根据权利要求4所述的一种无机保温材料，其特征在于，加热搅拌时间为15min。
6.根据权利要求1所述的一种无机保温材料，其特征在于，所述抗静电剂为二硫代氨基甲酸的碱金属盐。